T1  - Tooth discoloration induced by apical plugs with hydraulic calcium silicate-based cements in teeth with open apices-a 2-year in vitro study
T2  - Clinical Oral Investigations
N2  - Objectives
To assess tooth discoloration induced by different hydraulic calcium silicate-based cements (HCSCs), including effects of blood and placement method.
Materials and methods
Eighty bovine teeth cut to a length of 18 mm (crown 8 mm, root 10 mm) were randomly assigned to 10 groups (n = 8), receiving orthograde apical plug treatment (APT). Apical plugs were 4 mm in length and made of ProRoot MTA (Dentsply), Medcem MTA (Medcem), TotalFill BC RRM Fast Set Putty (Brasseler), or Medcem Medical Portland Cement (Medcem) plus bismuth oxide (Bi2O3) with and without bovine blood. Further, orthograde (with or without preoperative adhesive coronal dentin sealing) and retrograde APT were compared. Teeth were obturated with gutta-percha and sealer, sealed with composite and stored in distilled water. Tooth color was measured on apical plug, gutta-percha/sealer, and crown surface before treatment versus 24 h, 1, 3, 6, 12, and 24 months after treatment by spectrophotometry. Color difference (ΔE) values were calculated and analyzed by Shapiro-Wilk test, ANOVA with post hoc tests, Friedman test, t test, and post hoc tests with Bonferroni correction (α = .05).
Results
Tooth discoloration occurred in all groups with no significant differences between HCSCs (p > .05). After 24 months, color changes were prominent on roots but insignificant on crowns. Blood contamination induced a significantly decreased luminescence (p < .05). Blood had a stronger impact on tooth color than Bi2O3. No relevant effects of retrograde placement (p > .05) or preoperative dentin sealing (p > .05) were detected.
Conclusions
Apical plugs of the tested HCSCs cause discoloration of bovine roots, but not discoloration of bovine tooth crowns within a 24-month period.
Clinical relevance
APT should be performed carefully while avoiding direct contact with the coronal dentin, and in that case no aesthetic impairments occur.
KW  - dentin sealing
KW  - mineral trioxide aggregate
KW  - Portland cement
KW  - tooth discoloration
KW  - spectrophotometer
KW  - blood contamination
Y1  - 2022
UR  - https://opus.bibliothek.uni-wuerzburg.de/frontdoor/index/index/docId/26885
UR  - https://nbn-resolving.org/urn:nbn:de:bvb:20-opus-268856
SN  - 1436-3771
VL  - 26
IS  - 1
ER  -