@article{SeifertGrollWeichholdetal.2021,
  author    = {Seifert, Annika and Groll, J{\"u}rgen and Weichhold, Jan and Boehm, Anne V. and M{\"u}ller, Frank A. and Gbureck, Uwe},
  title     = {Phase Conversion of Ice-Templated α-Tricalcium Phosphate Scaffolds into Low-Temperature Calcium Phosphates with Anisotropic Open Porosity},
  series = {Advanced Engineering Materials},
  volume    = {23},
  journal   = {Advanced Engineering Materials},
  number    = {5},
  doi       = {10.1002/adem.202001417},
  url       = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-256311},
  year      = {2021},
  abstract  = {The current study aims to extend the material platform for anisotropically structured calcium phosphates to low-temperature phases such as calcium-deficient hydroxyapatite (CDHA) or the secondary phosphates monetite and brushite. This is achieved by the phase conversion of highly porous α-tricalcium phosphate (α-TCP) scaffolds fabricated by ice-templating into the aforementioned phases by hydrothermal treatment or incubation in phosphoric acid. Prior to these steps, α-TCP scaffolds are either sintered for 8 h at 1400 °C or remain in their original state. Both nonsintered and sintered α-TCP specimens are converted into CDHA by hydrothermal treatment, while a transformation into monetite and brushite is achieved by incubation in phosphoric acid. Hydrothermal treatment for 72 h at 175 °C increases the porosity in nonsintered samples from 85\% to 88\% and from 75\% to 88\% in the sintered ones. An increase in the specific surface area from (1.102 ± 0.005) to (9.17 ± 0.01) m2 g-1 and from (0.190 ± 0.004) to (2.809 ± 0.002) m2 g-1 due to the phase conversion is visible for both the nonsintered and sintered samples. Compressive strength of the nonsintered samples increases significantly from (0.76 ± 0.11) to (5.29 ± 0.94) MPa due to incubation in phosphoric acid.},
  language  = {en}
}