@article{KadeBakirciTandonetal.2022,
  author    = {Kade, Juliane C. and Bakirci, Ezgi and Tandon, Biranche and Gorgol, Danila and Mrlik, Miroslav and Luxenhofer, Robert and Dalton, Paul D.},
  title     = {The Impact of Including Carbonyl Iron Particles on the Melt Electrowriting Process},
  series = {Macromolecular Materials and Engineering},
  volume    = {307},
  journal   = {Macromolecular Materials and Engineering},
  number    = {12},
  issn      = {1438-7492},
  doi       = {10.1002/mame.202200478},
  url       = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-318482},
  year      = {2022},
  abstract  = {Melt electrowriting, a high-resolution additive manufacturing technique, is used in this study to process a magnetic polymer-based blend for the first time. Carbonyl iron (CI) particles homogenously distribute into poly(vinylidene fluoride) (PVDF) melts to result in well-defined, highly porous structures or scaffolds comprised of fibers ranging from 30 to 50 µm in diameter. This study observes that CI particle incorporation is possible up to 30 wt\% without nozzle clogging, albeit that the highest concentration results in heterogeneous fiber morphologies. In contrast, the direct writing of homogeneous PVDF fibers with up to 15 wt\% CI is possible. The fibers can be readily displaced using magnets at concentrations of 1 wt\% and above. Combined with good viability of L929 CC1 cells using Live/Dead imaging on scaffolds for all CI concentrations indicates that these formulations have potential for the usage in stimuli-responsive applications such as 4D printing.},
  language  = {en}
}
@article{BoehmTandonHrynevichetal.2022,
  author    = {B{\"o}hm, Christoph and Tandon, Biranche and Hrynevich, Andrei and Teßmar, J{\"o}rg and Dalton, Paul D.},
  title     = {Processing of Poly(lactic-co-glycolic acid) Microfibers via Melt Electrowriting},
  series = {Macromolecular Chemistry and Physics},
  volume    = {223},
  journal   = {Macromolecular Chemistry and Physics},
  number    = {5},
  doi       = {10.1002/macp.202100417},
  url       = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-318444},
  year      = {2022},
  abstract  = {Polymers sensitive to thermal degradation include poly(lactic-co-glycolic acid) (PLGA), which is not yet processed via melt electrowriting (MEW). After an initial period of instability where mean fiber diameters increase from 20.56 to 27.37 µm in 3.5 h, processing stabilizes through to 24 h. The jet speed, determined using critical translation speed measurements, also reduces slightly in this 3.5 h period from 500 to 433 mm min\(^{-1}\) but generally remains constant. Acetyl triethyl citrate (ATEC) as an additive decreases the glass transition temperature of PLGA from 49 to 4 °C, and the printed ATEC/PLGA fibers exhibits elastomeric behavior upon handling. Fiber bundles tested in cyclic mechanical testing display increased elasticity with increasing ATEC concentration. The processing temperature of PLGA also reduces from 165 to 143 °C with increase in ATEC concentration. This initial window of unstable direct writing seen with neat PLGA can also be impacted through the addition of 10-wt\% ATEC, producing fiber diameters of 14.13 ± 1.69 µm for the first 3.5 h of heating. The investigation shows that the initial changes to the PLGA direct-writing outcomes seen in the first 3.5 h are temporary and that longer times result in a more stable MEW process.},
  language  = {en}
}
@article{BoehmStahlhutWeichholdetal.2022,
  author    = {B{\"o}hm, Christoph and Stahlhut, Philipp and Weichhold, Jan and Hrynevich, Andrei and Teßmar, J{\"o}rg and Dalton, Paul D.},
  title     = {The Multiweek Thermal Stability of Medical-Grade Poly(ε-caprolactone) During Melt Electrowriting},
  series = {Small},
  volume    = {18},
  journal   = {Small},
  number    = {3},
  doi       = {10.1002/smll.202104193},
  url       = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-257741},
  year      = {2022},
  abstract  = {Melt electrowriting (MEW) is a high-resolution additive manufacturing technology that places unique constraints on the processing of thermally degradable polymers. With a single nozzle, MEW operates at low throughput and in this study, medical-grade poly(ε-caprolactone) (PCL) is heated for 25 d at three different temperatures (75, 85, and 95 °C), collecting daily samples. There is an initial increase in the fiber diameter and decrease in the jet speed over the first 5 d, then the MEW process remains stable for the 75 and 85 °C groups. When the collector speed is fixed to a value at least 10\% above the jet speed, the diameter remains constant for 25 d at 75 °C and only increases with time for 85 and 95 °C. Fiber fusion at increased layer height is observed for 85 and 95 °C, while the surface morphology of single fibers remain similar for all temperatures. The properties of the prints are assessed with no observable changes in the degree of crystallinity or the Young's modulus, while the yield strength decreases in later phases only for 95 °C. After the initial 5-d period, the MEW processing of PCL at 75 °C is extraordinarily stable with overall fiber diameters averaging 13.5 ± 1.0 µm over the entire 25-d period.},
  language  = {en}
}