@phdthesis{Shan2022, author = {Shan, Junwen}, title = {Tailoring Hyaluronic Acid and Gelatin for Bioprinting}, doi = {10.25972/OPUS-29825}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-298256}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2022}, abstract = {In the field of biofabrication, biopolymer-based hydrogels are often used as bulk materials with defined structures or as bioinks. Despite their excellent biocompatibility, biopolymers need chemical modification to fulfill mechanical stability. In this thesis, the primary alcohol of hyaluronic acid was oxidized using TEMPO/TCC oxidation to generate aldehyde groups without ring-opening mechanism of glycol cleavage using sodium periodate. For crosslinking reaction of the aldehyde groups, adipic acid dihydrazide was used as bivalent crosslinker for Schiff Base chemistry. This hydrogel system with fast and reversible crosslinking mechanism was used successfully as bulk hydrogel for chondrogenic differentiation with human mesenchymal stem cells (hMSC). Gelatin was modified with pentenoic acid for crosslinking reaction via light controllable thiol-ene reaction, using thiolated 4-arm sPEG as multivalent crosslinker. Due to preservation of the thermo responsive property of gelatin by avoiding chain degradation during modification reaction, this gelatin-based hydrogel system was successfully processed via 3D printing with low polymer concentration. Good cell viability was achieved using hMSC in various concentrations after 3D bioprinting and chondrogenic differentiation showed promising results.}, subject = {Hydrogel}, language = {en} } @phdthesis{Smolan2022, author = {Smolan, Willi}, title = {Linear Multifunctional PEG-Alternatives for Bioconjugation and Hydrogel Formation}, doi = {10.25972/OPUS-27873}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-278734}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2022}, abstract = {The objective of this thesis was the synthesis and characterisation of two linear multifunctional PEG-alternatives for bioconjugation and hydrogel formation: i) Hydrophilic acrylate based copolymers containing peptide binding units and ii) hydrophilic polyether based copolymers containing different functional groups for a physical crosslinking. In section 3.1 the successful synthesis of water soluble and linear acrylate based polymers containing oligo(ethylene glycol) methyl ether acrylate with either linear thioester functional 2-hydroxyethyl acrylate, thiolactone acrylamide, or vinyl azlactone via the living radical polymerisation technique Reversible Addition Fragmentation Chain Transfer (RAFT) and via free-radical polymerisation is described. The obtained polymers were characterized via GPC, 1H NMR, IR and RAMAN spectroscopy. The RAFT end group was found to be difficult to remove from these short polymer chains and accordingly underwent the undesired side reaction aminolysis with the peptide during the conjugation studies. Besides that, polymers without RAFT end groups did not show any binding of the peptide at the thioester groups, which can be improved in future by using higher reactant concentrations and higher amount of binding units at the polymer. Polymers containing the highly reactive azlactone group showed a peptide binding of 19 \%, but unfortunately this function also underwent spontaneous hydrolysis before the peptide could even be bound. In all cases, oligo(ethylene glycol) methyl ether acrylate was used with a relatively high molecular weight (Mn = 480 Da) was used, which eventually was efficiently shielding the introduced binding units from the added peptide. In future, a shorter monomer with Mn = 300 Da or less or hydrophilic N,N'-dialkyl acrylamide based polymers with less steric hindrance could be used to improve this bioconjugation system. Additionally, the amount of monomers containing peptide binding units in the polymer can be increased and have an additional spacer to achieve higher loading efficiency. The water soluble, linear and short polyether based polymers, so called polyglycidols, were successfully synthesized and modified as described in section 3.2. The obtained polymers were characterized using GPC, 1H NMR, 31P{1H} NMR, IR, and RAMAN spectroscopy. The allyl groups which were present up to 20 \% were used for radical induced thiol-ene chemistry for the introduction of functional groups intended for the formation of the physically crosslinking hydrogels. For the positively charged polymers, first a chloride group had to be introduced for the subsequent nucleophilic substitution with the imidazolium compound. There, degrees of modifications were found in the range 40-97 \% due to the repulsion forces of the charges, decreased concentration of active chloride groups, and limiting solution concentrations of the polymer for this reaction. For the negatively charged polymers, first a protected phosphonamide moiety was introduced with a deprotection step afterwards showing 100 \% conversion for all reactions. Preliminary hydrogel tests did not show a formation of a three-dimensional network of the polymer chains which was attributed to the short backbone length of the used polymers, but the gained knowledge about the synthetic routes for the modification of the polymer was successfully transferred to longer linear polyglycidols. The same applies to the introduction of electron rich and electron poor compounds showing π-π stacking interactions by UV-vis spectroscopy. Finally, long linear polyglycidyl ethers were synthesised successfully up to molecular weights of Mn ~ 30 kDa in section 3.3, which was also proven by GPC, 1H NMR, IR and RAMAN spectroscopy. This applies to the homopolymerisation of ethoxyethyl glycidyl ether, allyl glycidyl ether and their copolymerisation with an amount of the allyl compound ~ 10 \%. Attempts for higher molecular weights up to 100 kDa showed an uncontrolled polymerisation behaviour and eventually can be improved in future by choosing a lower initiation temperature. Also, the allyl side groups were modified via radical induced thiol-ene chemistry to obtain positively charged functionalities via imidazolium moieties (85 \%) and negatively charged functionalities via phosphonamide moieties (100 \%) with quantitative degree of modifications. Hydrogel tests have still shown a remaining solution by using long linear polyglycidols carrying negative charges with long/short linear polyglycidols carrying positive charges. The addition of calcium chloride led to a precipitate of the polymer instead of a three-dimensional network formation representing a too high concentration of ions and therefore shielding water molecules with prevention from dissolving the polymer. These systems can be improved by tuning the polymers structure like longer polymer chains, longer spacer between polymer backbone and charge, and higher amount of functional groups. The objective of the thesis was partly reached containing detailed investigated synthetic routes for the design and characterisation of functional polymers which could be used in future with improvements for bioconjugation and hydrogel formation tests.}, subject = {Wasserl{\"o}sliche Polymere}, language = {en} } @phdthesis{Loeblein2021, author = {L{\"o}blein, Jochen}, title = {Development of Dynamic Self-Initiated Photografting and Photopolymerization}, doi = {10.25972/OPUS-25182}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-251828}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2021}, abstract = {After examining suitable parameters for a newly designed system, dynamic SIPGP could be developed. For the first time, SIPGP was performed while applying a constant flow of monomer solution through the reaction system. This added a new parameter: the flow rate (rfl). Accordingly, this parameter was examined, comparing dynamic to static SIPGP. It could be shown, that by applying higher rfl to the system, the contact angle increases, which indicates a slower coating. The flow patterns inside the reactor were then modelled and calculated. These calculations indicated, that, due to higher flow velocities, the contact angle on the coated samples would be lower on the sides of the sample and higher in the middle. This finding was verified by contact angle measurements. The influence of dynamic SIPGP on the temperature inside the reaction chamber during the reaction was examined by temperature sensors inside the reactor. This showed, that the constant flow of monomer solution can be utilized to decrease the warming of the reaction solution during the reaction. Finally it was shown, that dynamic SIPGP can decrease the formation of bulk polymer on the sample, which is forming during the reaction. This enables SIPGP to fabricate more homogeneous coatings by applying a constant monomer flow.}, subject = {Hydrogel}, language = {en} } @phdthesis{Schmidt2021, author = {Schmidt, Stefanie}, title = {Cartilage Tissue Engineering - Comparison of Articular Cartilage Progenitor Cells and Mesenchymal Stromal Cells in Agarose and Hyaluronic Acid-Based Hydrogels}, doi = {10.25972/OPUS-25171}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-251719}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2021}, abstract = {Articular cartilage damage caused by sports accidents, trauma or gradual wear and tear can lead to degeneration and the development of osteoarthritis because cartilage tissue has only limited capacity for intrinsic healing. Osteoarthritis causes reduction of mobility and chronic pain and is one of the leading causes of disability in the elderly population. Current clinical treatment options can reduce pain and restore mobility for some time, but the formed repair tissue has mostly inferior functionality compared to healthy articular cartilage and does not last long-term. Articular cartilage tissue engineering is a promising approach for the improvement of the quality of cartilage repair tissue and regeneration. In this thesis, a promising new cell type for articular cartilage tissue engineering, the so-called articular cartilage progenitor cell (ACPC), was investigated for the first time in the two different hydrogels agarose and HA-SH/P(AGE-co-G) in comparison to mesenchymal stromal cells (MSCs). In agarose, ACPCs´ and MSCs´ chondrogenic capacity was investigated under normoxic (21 \% oxygen) and hypoxic (2 \% oxygen) conditions in monoculture constructs and in zonally layered co-culture constructs with ACPCs in the upper layer and MSCs in the lower layer. In the newly developed hyaluronic acid (HA)-based hydrogel HA-SH/P(AGE-co-G), chondrogenesis of ACPCs and MSCs was also evaluated in monoculture constructs and in zonally layered co-culture constructs like in agarose hydrogel. Additionally, the contribution of the bioactive molecule hyaluronic acid to chondrogenic gene expression of MSCs was investigated in 2D monolayer, 3D pellet and HA-SH hydrogel culture. It was shown that both ACPCs and MSCs could chondrogenically differentiate in agarose and HA-SH/P(AGE-co-G) hydrogels. In agarose hydrogel, ACPCs produced a more articular cartilage-like tissue than MSCs that contained more glycosaminoglycan (GAG), less type I collagen and only little alkaline phosphatase (ALP) activity. Hypoxic conditions did not increase extracellular matrix (ECM) production of ACPCs and MSCs significantly but improved the quality of the neo-cartilage tissue produced by MSCs. The creation of zonal agarose constructs with ACPCs in the upper layer and MSCs in the lower layer led to an ECM production in zonal hydrogels that lay in general in between the ECM production of non-zonal ACPC and MSC hydrogels. Even though zonal co-culture of ACPCs and MSCs did not increase ECM production, the two cell types influenced each other and, for example, modulated the staining intensities of type II and type I collagen in comparison to non-zonal constructs under normoxic and hypoxic conditions. In HA-SH/P(AGE-co-G) hydrogel, MSCs produced more ECM than ACPCs, but the ECM was limited to the pericellular region for both cell types. Zonal HASH/P(AGE-co-G) hydrogels resulted in a native-like zonal distribution of ECM as MSCs in the lower zone produced more ECM than ACPCs in the upper zone. It appeared that chondrogenesis of ACPCs was supported by hydrogels without biological attachment sites such as agarose, and that chondrogenesis of MSCs benefited from hydrogels with biological cues like HA. As HA is an attractive material for cartilage tissue engineering, and the HA-based hydrogel HA-SH/P(AGE-co-G) appeared to be beneficial for MSC chondrogenic differentiation, the contribution of HA to chondrogenic gene expression of MSCs was investigated. An upregulation of chondrogenic gene expression was found in 2D monolayer and 3D pellet culture of MSCs in response to HA supplementation, while gene expression of osteogenic and adipogenic transcription factors was not upregulated. MSCs, encapsulated in a HA-based hydrogel, showed upregulation of gene expression for chondrogenic, osteogenic and adipogenic differentiation markers as well as for stemness markers. In a 3D bioprinting process, using the HA-based hydrogel, gene expression levels of MSCs mostly did not change. Nevertheless, expression of three tested genes (COL2A1, SOX2, CD168) was downregulated in printed in comparison to cast constructs, underscoring the importance of closely monitoring cellular behaviour during and after the printing process. In summary, it was confirmed that ACPCs are a promising cell source for articular cartilage engineering with advantages over MSCs when they were cultured in a suitable hydrogel like agarose. The performance of the cells was strongly dependent on the hydrogel environment they were cultured in. The different chondrogenic performance of ACPCs and MSCs in agarose and HA-SH/P(AGE-co-G) hydrogels highlighted the importance of choosing suitable hydrogels for the different cell types used in articular cartilage tissue engineering. Hydrogels with high polymer content, such as the investigated HA-SH/P(AGE-co-G) hydrogels, can limit ECM distribution to the pericellular area and should be developed further towards less polymer content, leading to more homogenous ECM distribution of the cultured cells. The influence of HA on chondrogenic gene expression and on the balance between differentiation and maintenance of stemness in MSCs was demonstrated. More studies should be performed in the future to further elucidate the signalling functions of HA and the effects of 3D bioprinting in HA-based hydrogels. Taken together, the results of this thesis expand the knowledge in the area of articular cartilage engineering with regard to the rational combination of cell types and hydrogel materials and open up new possible approaches to the regeneration of articular cartilage tissue.}, subject = {Hyaliner Knorpel}, language = {en} } @phdthesis{Haschke2021, author = {Haschke, Sebastian}, title = {Untersuchung Thiol-En vernetzter Gelatine Hydrogele und Vergleich mit Alginat-Gelatine in Bezug auf das in vitro Zellverhalten von Fibroblasten}, doi = {10.25972/OPUS-24872}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-248727}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2021}, abstract = {Hydrogele stehen als Material f{\"u}r den 3D-Biodruck zunehmend im Fokus aktueller Forschung, da sie aufgrund ihrer wasserhaltigen Struktur optimale Voraussetzungen f{\"u}r Anwendungen der Zellkultur aufweisen. Durch die Verarbeitung solcher Biotinten mittels additiver Fertigungstechniken der Biofabrikation erhofft man sich besch{\"a}digtes oder krankes Gewebe zu heilen oder zu ersetzen. Allerdings wird der Fortschritt in diesem Bereich durch einen Mangel an geeigneten Materialien gebremst, weshalb die Entwicklung neuer Biotinten von zentraler Bedeutung ist. Das Polymer GelAGE ist ein am Lehrstuhl f{\"u}r Funktionswerkstoffe der Medizin und Zahnheilkunde der Universit{\"a}t W{\"u}rzburg synthetisiertes Hydrogelsystem. Zu diesem {\"u}ber eine Thiol-En Reaktion vernetzenden Material stehen systematische Untersuchungen der f{\"u}r die in vitro Zellkultur relevanten Eigenschaften noch aus. Das Ziel dieser Arbeit war daher die biologische Evaluation von GelAGE und der Vergleich mit der Biotinte Alginat-Gelatine. Zu diesem Zweck wurden L929-Zellen f{\"u}r 7 Tage in verschiedenen Hydrogelzusammensetzungen in vitro kultiviert. Um die zytokompatiblen Eigenschaften in den verschiedenen Versuchsgruppen zu untersuchen, wurden die Proben mittels der in vitro Testverfahren Live/Dead F{\"a}rbung, DNA-Assay, CCK-8-Assay und Phalloidin-F{\"a}rbung analysiert. Im Rahmen dieser Arbeit konnte ein Herstellungsprotokoll f{\"u}r das Material GelAGE etabliert werden, welches eine Grundlage f{\"u}r die Durchf{\"u}hrung weiterer biologischer Experimente bietet. Das Resultat der biologischen Untersuchungen war, dass das Polymer GelAGE als zytokompatibel bewertet werden kann, es jedoch nicht die Qualit{\"a}t des Alginat-Gelatine Hydrogelsystems aufweist. Allerdings konnten die Eigenschaften der GelAGE Proben teilweise durch eine Modifikation mit Humanem Pl{\"a}ttchenlysat verbessert werden. Des Weiteren konnten deutliche Unterschiede in der Zell-Material- Interaktion zwischen den verschiedenen GelAGE Varianten nachgewiesen werden.}, subject = {Hydrogel}, language = {de} } @phdthesis{Bernuth2020, author = {Bernuth, Silvia}, title = {Bioaktiv funktionalisierbare Hyalurons{\"a}ure-Polyglycidol-Hydrogele unter Verwendung von ASCs aus dem Fettgewebe zur Rekonstruktion von Weichgewebsdefekten}, doi = {10.25972/OPUS-21424}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-214248}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2020}, abstract = {In der Plastischen Chirurgie erfordert die Rekonstruktion von {\"a}sthetisch anspruchsvollen Bereichen in vielen F{\"a}llen die Wiederherstellung von subkutanem Fettgewebe. Neben chirurgischen Rekonstruktionen k{\"o}nnte das Tissue Engineering von Fettgewebe einen wertvollen Beitrag leisten. Jedoch bringt es vielschichtige Herausforderungen mit sich und ist zum aktuellen Zeitpunkt nur limitiert m{\"o}glich. Ein Ansatz ist die Schaffung einer Tr{\"a}germatrix zur Besiedelung und Differenzierung von Stammzellen. Auf dieser Basis sollten in der vorliegenden Arbeit zwei Teilbereiche untersucht werden. In dem ersten Teilbereich erfolgten Untersuchungen verschiedener Gewinnungsmethoden von ASCs aus dem subkutanen Fettgewebe bezogen auf ihr Effizienz. Die untersuchten Liposuktionstechniken zeigten eine deutlich h{\"o}here Effizienz gegen{\"u}ber der mechanischen Gewinnungsmethode bezogen auf die gewonnene Zellzahl. In den Viabilit{\"a}tsuntersuchungen zeigte sich eine {\"a}hnliche Tendenz. ASCs aller drei Gewinnungsmethoden proliferierten durchaus gleich gut, jedoch zeigten die histologischen und quantitativen Adipogeneseuntersuchungen tendenziell mehr Lipidbildung bei den Liposuktionstechniken. Das {\"u}bergeordnete Ziel des zweiten Abschnittes dieser Arbeit war es eine Tr{\"a}germatrix auf Hyalurons{\"a}ure-Basis mit dem vielseitig modifizierbarem Crosslinker Polyglycidol zu untersuchen, sie mit mesenchymalen Stammzellen aus dem Fettgewebe zu besiedeln und diese adipogen zu differenzieren. Des Weiteren erfolgten erste Versuche die Hydrogele mit funktionellen Gruppen zu modifizieren um eine Verbesserung der Adh{\"a}sion der Zellen im Hydrogel zu erreichen. Die unmodifizierten Hydrogele waren zu jeder Zeit stabil in ihrer Form und zeigten nach Besiedelung mit ASCs eine gleichm{\"a}ßige Verteilung der Zellen im Gel. Auch ließ sich die Adipogenese histologisch visualisieren und biochemisch best{\"a}tigen. Die inkorporierten Peptide brachten eine peptidabh{\"a}ngige und konzentrationsabh{\"a}ngige Ver{\"a}nderung der Zellverteilung im Hydrogel. Eine Steigerung der Funktionalit{\"a}t der Zellen bezogen auf das {\"U}berleben und die Adipogenese konnte in diesen ersten Versuchen noch nicht gezeigt werden. Generell zeigt sich eine Eignung der hyalurons{\"a}urebasierten mit Polyglycidol-verlinkten Hydrogele f{\"u}r das Tissue Engineering von Fettgewebe. Weitere Untersuchungen bez{\"u}glich der Modifikation der Hydrogele mit adh{\"a}siven und adipogenen funktionellen Gruppen bietet sich daher an und k{\"o}nnte ein fettgewebs{\"a}hnliches Umgebungsmilieu hervorbringen.}, subject = {Hyalurons{\"a}ure}, language = {de} } @phdthesis{LiebschergebBloehbaum2020, author = {Liebscher [geb. Bl{\"o}hbaum], Julia}, title = {Side chain functional poly(2-oxazoline)s for biomedical applications}, doi = {10.25972/OPUS-20396}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-203960}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2020}, abstract = {The aim of the thesis was to develop water soluble poly(2-oxazoline) (POx) copolymers with new side group functionalities, which can be used for the formation of hydrogels in biomedical applications and for the development of peptide-polymer conjugates. First, random copolymers of the monomer MeOx or EtOx with ButEnOx and EtOx with DecEnOx were synthesized and characterized. The vinyl functionality brought into the copolymer by the monomers ButEnOx and DecEnOx would later serve for post-polymerization functionalization. The synthesized copolymers were further functionalized with thiols via post-polymerization functionalization using a newly developed synthesis protocol or with a protected catechol molecule for hydrogel formation. For the formation of peptide-polymer conjugates, a cyclic thioester, namely thiolactone acrylamide and an azlactone precursor, whose synthesis was newly developed, were attached to the side chain of P(EtOx-co-ButEnOx) copolymers. The application of the functionalized thiol copolymers as hydrogels using thiol-ene chemistry for cross-linking was demonstrated. The swelling behavior and mechanical properties were characterized. The hydrophilicity of the network as well as the cross-linking density strongly influenced the swelling behavior and the mechanical strength of the hydrogels. All hydrogels showed good cell viability results. The hydrogel networks based on MeOx and EtOx were loaded with two dyes, fluorescein and methylene blue. It was observed that the uptake of the more hydrophilic dye fluorescein depended more on the ability of the hydrogel to swell. In contrast, the uptake of the more hydrophobic dye methylene blue was less dependent on the swelling degree, but much more on the hydrophilicity of the network. For the potential application as cartilage glue, (biohybrid) hydrogels were synthesized based on the catechol-functionalized copolymers, with and without additional fibrinogen, using sodium periodate as the oxidizing agent. The system allowed for degradation due to the incorporated ester linkages at the cross-linking points. The swelling behavior as well as the mechanical properties were characterized. As expected, hydrogels with higher degrees of cross-linking showed less swelling and higher elastic modulus. The addition of fibrinogen however increased the elasticity of the network, which can be favorable for the intended application as a cartilage glue. Biological evaluation clearly demonstrated the advantage of degradable ester links in the hydrogel network, where chondrocytes were able to bridge the artificial gap in contrast to hydrogels without any ester motifs. Lastly, different ways to form peptide-polymer conjugates were presented. Peptides were attached with the thiol of the terminal cysteine group to the vinyl side chain of P(EtOx-co-ButEnOx) copolymers by radical thiol-ene chemistry. Another approach was to use a cyclic thioester, thiolactone, or an azlactone functionality to bind a model peptide via native chemical ligation. The two latter named strategies to bind peptides to POx side chains are especially interesting as one and in the case of thiolactone two free thiols are still present at the binding site after the reaction, which can, for example, be used for further thiol-ene cross-linking to form POx hydrogels. In summary, side functional poly(oxazoline) copolymers show great potential for numerous biomedical applications. The various side chain functionalities can be introduced by an appropriate monomer or by post-polymerization functionalization, as demonstrated. By their multi-functionality, hydrogel characteristics, such as cross-linking degree and mechanical strength, can be fine-tuned and adjusted depending on the application in the human body. In addition, the presented chemoselective and orthogonal reaction strategies can be used in the future to synthesize polymer conjugates, which can, for example, be used in drug delivery or in tissue regeneration.}, subject = {Polymere}, language = {en} } @phdthesis{Luebtow2020, author = {L{\"u}btow, Michael M.}, title = {Structure-property relationships in poly(2-oxazoline)/poly(2-oxazine) based drug formulations}, doi = {10.25972/OPUS-19338}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-193387}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2020}, abstract = {According to estimates, more than 40\% of all new chemical entities developed in pharmaceutical industry are practically insoluble in water. Naturally, the demand for excipients which increase the water solubility and thus, the bioavailability of such hydrophobic drugs is enormous. Poly(2-oxazoline)s (POx) are currently intensively discussed as highly versatile class of biomaterials. Although selected POx based micellar drug formulations exhibit extraordinarily high drug loadings > 50 wt.\% enabling high anti-tumor efficacies in vivo, the formulation of other hydrophobic compounds has failed. This casts doubt on the general understanding in which a hydrophobic active pharmaceutical ingredient is dissolved rather unspecifically in the hydrophobic core of the micelles following the fundamental concept of "like dissolves like". Therefore, a closer look at the interactions between all components within a formulation becomes increasingly important. To do so, a large vehicle platform was synthesized, loaded with various hydrophobic drugs of different structure, and the formulations subsequently characterized with conventional and less conventional techniques. The obtained in-depth insights helped to develop a more thorough understanding about the interaction of polymer and incorporated API finally revealing morphologies deviating from a classical core/shell structure. During these studies, the scarcely investigated polymer class of poly(2-oxazine)s (POzi) was found as promising drug-delivery vehicle for hydrophobic drugs. Apart from this fundamental research, the anti-tumor efficacy of the two APIs curcumin and atorvastatin has been studied in more detail. To increase the scope of POx and POzi based formulations designed for intravenous administration, a curcumin loaded hydrogel was developed as injectable drug-depot.}, subject = {Polymere}, language = {en} } @phdthesis{Bertlein2019, author = {Bertlein, Sarah}, title = {Hydrogels as Biofunctional Coatings and Thiol-Ene Clickable Bioinks for Biofabrication}, doi = {10.25972/OPUS-17422}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-174225}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2019}, abstract = {Ziel dieser Arbeit war die Entwicklung von funktionalisierbaren Hydrogel Beschichtungen f{\"u}r Schmelz-elektrogeschriebene PCL Ger{\"u}ste und von Bio-druckbaren Hydrogelen f{\"u}r die Biofabrikation. Hydrogel Beschichtungen von Schmelz-elektrogeschriebenen Konstrukten erm{\"o}glichten die Kontrolle der Oberfl{\"a}chen-Hydrophilie und damit Zell-Material Interaktionsstudien in minimal Protein-adh{\"a}siven Umgebungen. Zu diesem Zweck wurde ein hydrophiles sternf{\"o}rmiges vernetzbares Polymer verwendet und eine Optimierung der Beschichtungsbedingungen durchgef{\"u}hrt. Außerdem boten neu entwickelte photosensitive Konstrukte eine Zeit- und pH-unabh{\"a}ngige Biofunktionalisierung. Bio-druckbare Hydrogele f{\"u}r die Biofabrikation basierten auf der Allyl-Funktionalisierung von Gelatine (GelAGE) und modifizierten Hyalurons{\"a}ure-Produkten, die das Hydrogel-Vernetzen mittels Thiol-En Click Chemie erm{\"o}glichen. Die Optimierung der GelAGE Hydrogel-Eigenschaften wurde durch eine detaillierte Analyse der Syntheseparameter, variierender En:SH Verh{\"a}ltnisse, unterschiedlicher Vernetzungsmolek{\"u}le und Photoinitiatoren erreicht. Die Homogenit{\"a}t der Thiol-En Netzwerke wurde mit denen der freien radikalischen Polymerisation verglichen und die Verwendbarkeit von GelAGE als Bio-Tinte f{\"u}r den Extrusions-basierten Bio-Druck wurde untersucht. Es wurde angenommen, dass reine Hyalurons{\"a}ure-basierte Bio-Tinten eine Beibehaltung der mechanischen und rheologischen Eigenschaften, der Zellviabilit{\"a}t und der Prozessierbarkeit erm{\"o}glichen trotz geringerem Polymer- und Thiol-Anteil der Hydrogele. Hydrogel-Beschichtungen: Hoch definierte PCL Ger{\"u}ste wurden mittels MEW hergestellt und anschließend mit sechs armigen sternf{\"o}rmigen vernetzbaren Polymeren (sP(EO-stat-PO)) beschichtet. Die Vernetzung wird durch die w{\"a}ssrig-induzierte Hydrolyse reaktiver Isocyanatgruppen (NCO) von sP(EO-stat-PO) bedingt. Diese Beschichtung erh{\"o}hte die Oberfl{\"a}chen-Hydrophilie und stellte eine Plattform f{\"u}r weitere Biofunktionalisierungen, in minimal Protein-adh{\"a}siven Umgebungen, dar. Nicht nur das Beschichtungsprotokoll wurde hinsichtlich der sP(EO-stat-PO) Konzentrationen und der Beschichtungsdauern optimiert, sondern auch Vorbehandlungen der Ger{\"u}ste wurden entwickelt. Diese waren essentiell um die finale Hydrophilie von sP(EO-stat-PO) beschichteten Ger{\"u}ste so zu erh{\"o}hen, dass unspezifische Protein-Adh{\"a}sionen vollst{\"a}ndig unterbunden wurden. Die sP(EO-stat-PO) Schichtdicke, von ungef{\"a}hr 100 nm, erm{\"o}glicht generell in vitro Studien nicht nur in Abh{\"a}ngigkeit der Ger{\"u}st-Biofunktionalisierung, sondern auch in Abh{\"a}ngigkeit der Ger{\"u}st-Architektur durchzuf{\"u}hren. Das Ausmaß der Hydrogel-Beschichtung wurde mittels einer indirekten Quantifizierung der NCO-Hydrolyse-Produkte ermittelt. Kenntnis {\"u}ber die NCO-Hydrolyse-Kinetik erm{\"o}glichte ein Gleichgewicht zwischen ausreichend beschichteten Ger{\"u}sten und der Pr{\"a}senz der NCO-Gruppen herzustellen, welche f{\"u}r die anschließenden Biofunktionalisierungen genutzt wurden. Diese Zeit- und pH-abh{\"a}ngige Biofunktionalisierung war jedoch nur f{\"u}r kleine Biomolek{\"u}le m{\"o}glich. Um diese Beschr{\"a}nkung zu umgehen und auch hochmolekulare Biomolek{\"u}le kovalent anzubinden, wurde ein anderer Reaktionsweg entwickelt. Dieser basierte auf der Photolyse von Diazirin-Gruppen und erm{\"o}glichte eine Zeit- und pH-unabh{\"a}ngige Biofunktionalisierung der Ger{\"u}ste mit Streptavidin und Kollagen Typ I. Die Fibrillen bildende Eigenschaft von Kollagen wurde genutzt um auf den Ger{\"u}sten verschiedene Kollagen-Konformationen zu erhalten und eine erste in vitro Studie best{\"a}tigte die Anwendbarkeit f{\"u}r Zell-Material Interaktionsstudien. Die hier entwickelten Ger{\"u}ste k{\"o}nnten verwendet werden um tiefere Einblicke in die Grundlagen der zellul{\"a}ren Wahrnehmung zu erhalten. Insbesondere die Komplexit{\"a}t mit der Zellen z.B. Kollagen wahrnehmen bleibt weiterhin kl{\"a}rungsbed{\"u}rftig. Hierf{\"u}r k{\"o}nnten diverse Hierarchien von Kollagen-{\"a}hnlichen Konformationen an die Ger{\"u}ste gebunden werden, z.B. Gelatine oder Kollagen-abgeleitete Peptidsequenzen. Dann k{\"o}nnte die Aktivierung der DDR-Rezeptoren in Abh{\"a}ngigkeit der Komplexit{\"a}t der angebundenen Substanzen bestimmt werden. Aufgrund der starken Streptavidin-Biotin Bindung k{\"o}nnten Streptavidin funktionalisierte Ger{\"u}ste eine vielseitige Plattform f{\"u}r die Immobilisierung von jeglichen biotinylierten Molek{\"u}len darstellen. Gelatine-basierte Bio-Tinten: Zuerst wurden die GelAGE-Produkte hinsichtlich der Molekulargewichts-Verteilung und der Integrit{\"a}t der Aminos{\"a}uren-Zusammensetzung synthetisiert. Eine detailliert Studie, mit variierenden molaren Edukt-Verh{\"a}ltnissen und Synthese-Zeitspannen, wurde durchgef{\"u}hrt und implizierte, dass der Gelatine Abbau am deutlichsten f{\"u}r stark alkalische Synthesebedingungen mit langen Reaktionszeiten war. Gelatine beinhaltet mehrere funktionalisierbare Gruppen und anhand diverser Model-Substanzen und Analysen wurde die vorrangige Amingruppen-Funktionalisierung ermittelt. Die Homogenit{\"a}t des GelAGE-Polymernetzwerkes, im Vergleich zu frei radikalisch polymerisierten GelMA-Hydrogelen, wurde best{\"a}tigt. Eine ausf{\"u}hrliche Analyse der Hydrogel-Zusammensetzungen mit variierenden funktionellen Gruppen Verh{\"a}ltnissen und UV- oder Vis-Licht induzierbaren Photoinitiatoren wurde durchgef{\"u}hrt. Die UV-Initiator Konzentration ist aufgrund der Zell-Toxizit{\"a}t und der potenziellen zellul{\"a}ren DNA-Besch{\"a}digung durch UV-Bestrahlung eingeschr{\"a}nkt. Das Zell-kompatiblere Vis-Initiator System hingegen erm{\"o}glichte, durch die kontrollierte Photoinitiator-Konzentration bei konstanten En:SH Verh{\"a}ltnissen und Polymeranteilen, die Einstellung der mechanischen Eigenschaften {\"u}ber eine große Spanne hinweg. Die Flexibilit{\"a}t der GelAGE Bio-Tinte f{\"u}r unterschiedliche additive Fertigungstechniken konnte, durch Ausnutzung des temperaturabh{\"a}ngigen Gelierungsverhaltens unterschiedlich stark degradierter GelAGE Produkte, f{\"u}r Stereolithographie und Extrusions-basiertem Druck bewiesen werden. Außerdem wurde die Viabilit{\"a}t zellbeladener GelAGE Konstrukte bewiesen, die mittels Extrusions-basiertem Bio-Druck erhalten wurden. Die Verwendung diverser multifunktioneller und makromolekularer Thiol-Vernetzungsmolek{\"u}le erm{\"o}glichte eine Verbesserung der mechanischen und rheologischen Eigenschaften und ebenso der Prozessierbarkeit. Verglichen mit dem kleinen bis-Thiol-funktionellen Vernetzungsmolek{\"u}l waren geringere Thiol-Vernetzer-Konzentrationen notwendig um bessere mechanische Festigkeiten und physikochemische Eigenschaften der Hydrogele zu erhalten. Der Extrusions-basierte Bio-Druck unterschiedlicher eingekapselter Zellen verdeutlichte die Notwendigkeit der individuellen Optimierung von Zell-beladenen Hydrogel-Formulierungen. Nicht nur die Zellviabilit{\"a}t von eingekapselten Zellen in Extrusions-basierten biogedruckten Konstrukten sollte bewertet werden, sondern auch andere Parameter wie die Zellmorphologie oder die Kollagen- oder Glykosaminoglykan-Produktion, da diese einige der essentiellen Voraussetzungen f{\"u}r die Verwendung in Knorpel Tissue Engineering Konzepten darstellen. Außerdem sollten diese Studien auf die stereolithographischen Ans{\"a}tze erweitert werden und letztlich w{\"a}re die Flexibilit{\"a}t und Zellkompatibilit{\"a}t der Formulierungen mit makromolekularen Vernetzern von Interesse. Makromolekulare Vernetzer erm{\"o}glichten die Reduktion des Polymeranteils und des Thiol-Gehalts und k{\"o}nnen, insbesondere in Kombination mit dem Zell-kompatibleren Vis-Initiator-System, voraussichtlich zu einer gesteigerten Zellkompatibilit{\"a}t beitragen, was zu kl{\"a}ren bleibt. Hyalurons{\"a}ure-basierte Bio-Tinten: Unterschiedliche Hyalurons{\"a}ure-Produkte (HA) wurden synthetisiert, sodass diese En- (HAPA) oder Thiol-Funktionalit{\"a}ten (LHASH) beinhalteten, um reine HA Thiol-En vernetzte Hydrogele zu erhalten. In Abh{\"a}ngigkeit des Molekulargewichts der HA-Produkte, der Polymeranteile und des En:SH Verh{\"a}ltnisses, konnte eine große Spanne an mechanischen Festigkeiten abgedeckt werden. Aufgrund der hohen Viskosit{\"a}t war allerdings im Falle von hochmolekularen HA (HHAPA) Produkt-L{\"o}sungen (HHAPA + LHASH) die Handhabbarkeit auf 5.0 wt.-\% beschr{\"a}nkt. Die Verwendung der gleichen HA Thiol-Komponenten (LHASH) erm{\"o}glichte Hybrid-Hydrogele, mit HA und GelAGE, mit reinen HA-Hydrogelen zu vergleichen. Obwohl der Polymeranteil von HHAPA + LHASH Hydrogelen signifikant geringer war, als im Vergleich zu Hybrid-Hydrogelen (GelAGE + LHASH), wurden f{\"u}r gleiche En:SH Verh{\"a}ltnisse {\"a}hnliche mechanische und physikochemische Eigenschaften reiner HA-Hydrogele bestimmt. Aufgrund der geringen Viskosit{\"a}t niedermolekularer HA L{\"o}sungen (LHAPA + LHASH) konnten diese nicht f{\"u}r den Extrusions-basierten Druck verwendet werden. Das nicht temperaturabh{\"a}ngige HHAPA + LHASH System hingegen konnte mit nur einem Viertel des Polymeranteils der Hybrid Formulierungen gedruckt werden. Im Vergleich zu der Hybrid Bio-Tinte wurde angenommen, dass das hoch viskose Verhalten von HHAPA + LHASH L{\"o}sungen, der geringere Polymeranteil, der geringere Druck f{\"u}r das Drucken und eine demzufolge geringere Scherspannung, maßgeblich zu der hohen Zellviabilit{\"a}t in Extrusions-basiert-biogedruckten Konstrukten beisteuerten. Die niedrigmolekulare HA Formulierung (LHAPA + LHASH) konnte zwar nicht f{\"u}r den Extrusions-basierten Druck verwendet werden, allerdings besitzt dieses System Potential f{\"u}r andere additive Fertigungstechniken wie z.B. der Stereolithographie. Um dieses System weiterzuentwickeln w{\"a}re, analog zu dem GelAGE System, eine detailliertere Studie zu den Funktionen eingekapselter Zellen hilfreich. Außerdem sollte die Initiierung dieses Systems mit dem Vis-Initiator untersucht werden.}, subject = {Biomaterial}, language = {en} } @phdthesis{Roedel2019, author = {R{\"o}del, Michaela}, title = {Development of Dual Setting Cement Systems as Composite Biomaterials with Ductile Properties}, doi = {10.25972/OPUS-18277}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-182776}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2019}, abstract = {Synthetic bone replacement materials have their application in non-load bearing defects with the function of (re-)construction or substitution of bone. This tissue itself represents a biological composite material based on mineralized collagen fibrils and combines the mechanical strength of the mineral with the ductility of the organic matrix. By mimicking these outstanding properties with polymer-cement-composites, an imitation of bone is feasible. A promising approach for such replacement materials are dual setting systems, which are generated by dissolution-precipitation reaction with cement setting in parallel to polymerization and gelation of the organic phase forming a coherent hydrogel network. Hereby, the high brittleness of the pure inorganic network was shifted to a more ductile and elastic behavior. The aim of this thesis was focused on the development of different dual setting systems to modify pure calcium phosphate cements' (CPCs') mechanical performance by incorporation of a hydrogel matrix. A dual setting system based on hydroxyapatite (HA) and cross-linked 2-hydroxyethyl methacrylate (HEMA) via radical polymerization was advanced by homogenous incorporation of a degradable cross-linker composed of poly(ethylene glycol) (PEG) as well as poly(lactic acid) (PLA) with reactive terminal methacrylate functionalities (PEG-PLLA-DMA). By integration of this high molecular weight structure in the HEMA-hydrogel network, a significant increase in energy absorption (toughness) under 4-point bending testing was observed. An addition of only 10 wt\% hydrogel precursor (referred to the liquid phase) resulted in a duplication of stress over a period of 8 days. Additionally, the calculated elasticity was positively affected and up to six times higher compared to pure HA. With a constantly applied force during compressive strength testing, a deformation and thus strain levels of about 10 \% were reached immediately after preparation. For higher degradability, the system was modified in a second approach regarding organic as well as inorganic phase. The latter component was changed by brushite forming cement that is resorbable in vivo due to solubility processes. This CPC was combined with a hydrogel based on PEG-PLLA-DMA and other dimethacrylated PEGs with different molecular weights and concentrations. Hereby, new reaction conditions were created including a shift to acidic conditions. On this ground, the challenge was to find a new radical initiator system. Suitable candidates were ascorbic acid and hydrogen peroxide. that started the polymerization and successful gelation in this environment. These highly flexible dual set composites showed a very high ductility with an overall low strength compared to HA-based models. After removal of the applied force during compressive strength testing, a complete shape recovery was observed for the samples containing the highest polymeric amount (50 wt\%) of PEG-PLLA-DMA. Regarding phase distribution in the constructs, a homogenously incorporated hydrogel network was demonstrated in a decalcifying study with ethylenediaminetetraacetic acid. Intact, coherent hydrogels remained after dissolution of the inorganic phase via calcium ion complexation. In a third approach, the synthetic hydrogel matrix of the previously described system was replaced by the natural biopolymer gelatin. Simultaneously to brushite formation, physical as well as chemical cross-linking by the compound genipin was performed in the dual setting materials. Thanks to the incorporation of gelatin, elasticity increased significantly, in which concentrations up to 10.0 w/v\% resulted in a certain cohesion of samples after compressive strength testing. They did not dissociate in little pieces but remained intact cuboid specimens though having cracks or fissures. Furthermore, the drug release of two active pharmaceutical ingredients (vancomycin and rifampicin) was investigated over a time frame of 5 weeks. The release exponent was determined according to Korsmeyer-Peppas with n = 0.5 which corresponds to the drug liberation model of Higuchi. A sustained release was observed for the antibiotic vancomycin encapsulated in composites with a gelatin concentration of 10.0 w/v\% and a powder-to-liquid ratio of 2.5 g/mL. With respect to these developments of different dual setting systems, three novel approaches were successfully established by polymerization of monomers and cross-linking of precursors forming an incorporated, homogenous hydrogel matrix in a calcium phosphate network. All studies showed an essential transfer of mechanical performance in direction of flexibility and bendability.}, subject = {Calciumphosphate}, language = {en} } @phdthesis{Lorson2019, author = {Lorson, Thomas}, title = {Novel Poly(2-oxazoline) Based Bioinks}, doi = {10.25972/OPUS-18051}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-180514}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2019}, abstract = {Motivated by the great potential which is offered by the combination of additive manufacturing and tissue engineering, a novel polymeric bioink platform based on poly(2 oxazoline)s was developed which might help to further advance the young and upcoming field of biofabrication. In the present thesis, the synthesis as well as the characteristics of several diblock copolymers consisting of POx and POzi have been investigated with a special focus on their suitability as bioinks. In general, the copolymerization of 2-oxazolines and 2-oxazines bearing different alkyl side chains was demonstrated to yield polymers in good agreement with the degree of polymerization aimed for and moderate to low dispersities. For every diblock copolymer synthesized during the present study, a more or less pronounced dependency of the dynamic viscosity on temperature could be demonstrated. Diblock copolymers comprising a hydrophilic PMeOx block and a thermoresponsive PnPrOzi block showed temperature induced gelation above a degree of polymerization of 50 and a polymer concentration of 20 wt\%. Such a behavior has never been described before for copolymers solely consisting of poly(cyclic imino ether)s. Physically cross linked hydrogels based on POx b POzi copolymers exhibit reverse thermal gelation properties like described for solutions of PNiPAAm and Pluronic F127. However, by applying SANS, DLS, and SLS it could be demonstrated that the underlying gel formation mechanism is different for POx b POzi based hydrogels. It appears that polymersomes with low polydispersity are formed already at very low polymer concentrations of 6 mg/L. Increasing the polymer concentration resulted in the formation of a bicontinuous sponge like structure which might be formed due to the merger of several vesicles. For longer polymer chains a phase transition into a gyroid structure was postulated and corresponds well with the observed rheological data. Stable hydrogels with an unusually high mechanical strength (G' ~ 4 kPa) have been formed above TGel which could be adjusted over a range of 20 °C by changing the degree of polymerization if maintaining the symmetric polymer architecture. Variations of the chain ends revealed only a minor influence on TGel whereas the influence of the solvent should not be neglected as shown by a comparison of cell culture medium and MilliQ water. Rotationally as well as oscillatory rheological measurements revealed a high suitability for printing as POx b POzi based hydrogels exhibit strong shear thinning behavior in combination with outstanding recovery properties after high shear stress. Cell viability assays (WST-1) of PMeOx b PnPrOzi copolymers against NIH 3T3 fibroblasts and HaCat cells indicated that the polymers were well tolerated by the cells as no dose-dependent cytotoxicity could be observed after 24 h at non-gelling concentrations up to 100 g/L. In summary, copolymers consisting of POx and POzi significantly increased the accessible range of properties of POx based materials. In particular thermogelation of aqueous solutions of diblock copolymers comprising PMeOx and PnPrOzi was never described before for any copolymer consisting solely of POx or POzi. In combination with other characteristics, e.g. very good cytocompatibility at high polymer concentrations and comparably high mechanical strength, the formed hydrogels could be successfully used for 3D bioprinting. Although the results appear promising and the developed hydrogel is a serious bioink candidate, competition is tough and it remains an open question which system or systems will be used in the future.}, subject = {Polymere}, language = {en} } @phdthesis{SchaefergebStichler2019, author = {Sch{\"a}fer [geb. Stichler], Simone}, title = {Thiol-ene Cross-linked Poly(glycidol) / Hyaluronic Acid Based Hydrogels for 3D Bioprinting}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-174713}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2019}, abstract = {The aim of the work was the development of thiol-ene cross-linked hydrogels based on functionalized poly(glycidol)s (PG) and hyaluronic acid (HA) for extrusion based 3D bioprinting. Additionally, the functionalization of the synthesized PG with peptides and the suitability of these polymers for physically cross-linked gels were investigated, in a proof of principle study in order to demonstrate the versatile use of PG polymers in hydrogel development. First, the precursor polymers of the different hydrogel systems were synthesized. For thiol-ene cross-linked hydogels, linear allyl-functionalized PG (P(AGE-co-G)) and three different thiol-(SH-)functionalized polymers, ester-containing PG-SH (PG SHec), ester-free PG-SH (PG-SHef) and HA-SH were synthesized and analysed, The degree of functionalization of these polymers was adjustable. For physically cross-linked hydrogels, peptide-functionalized PG (P(peptide-co-G)), was synthesized through polymer analogue thiol-ene modification of P(AGE-co-G). Subsequently, thiol-ene cross-linked hydrogels were prepared with the synthesized thiol- and allyl-functionalized polymers. Depending on the origin of the used polymers, two different systems were obtained: on the one hand synthetic hydrogels consisting of PG-SHec/ef and P(AGE-co-G) and on the other hand hybrid gels, consisting of HA-SH and P(AGE-co-G). In synthetic gels, the degradability of the gels was determined by the applied PG-SH. The use of PG-SHec resulted in hydrolytically degradable hydrogels, whereas the cross-linking with PG-SHef resulted in non-degradable gels. The physical properties of these different hydrogel systems were determined by swelling, mechanical and diffusion studies and subsequently compared among each other. In swelling studies the differences of degradable and non-degradable synthetic hydrogels as well as the differences of synthetic compared to hybrid hydrogels were demonstrated. Next, the stiffness and the swelling ratios (SR) of the established hydrogel systems were examined in dependency of different parameters, such as incubation time, polymer concentration and UV irradiation. In general, these measurements revealed the same trends for synthetic and hybrid hydrogels: an increased polymer concentration as well as prolonged UV irradiation led to an increased network density. Moreover, it was demonstrated that the incorporation of additional non-bound HMW HA hampered the hydrogel cross-linking resulting in gels with decreased stiffness and increased SR. This effect was strongly dependent on the amount of additional HMW HA. The diffusion of different molecular weight fluorescein isothiocyanate-dextran (FITC-dextran) through hybrid hydrogels (with/without HMW HA) gave information about the mesh size of these gels. The smallest FITC-dextran (4 kDa) completely diffused through both hydrogel systems within the first week, whereas only 55 \% of 40 kDa and 5-10 \% HMW FITC-dextrans (500 kDa and 2 MDa) could diffuse through the networks. The applicability of synthetic and hybrid hydrogels for cartilage regeneration purpose was investigated through by biological examinations. It was proven that both gels support the survival of embedded human mesenchymal stromal cells (hMSCs) (21/28 d in vitro culture), however, the chondrogenic differentiation was significantly improved in hybrid hydrogels compared to synthetic gels. The addition of non-bound HMW HA resulted in a slightly less distinct chondrogenesis. Lastly the printability of the established hydrogel systems was examined. Therefore, the viscoelastic properties of the hydrogel solutions were adjusted by incorporation of non-bound HMW HA. Both systems could be successfully printed with high resolution and high shape fidelity. The introduction of the double printing approach with reinforcing PCL allowed printing of hydrogel solutions with lower viscosities. As a consequence, the amount of additional HMW HA necessary for printing could be reduced allowing successful printing of hybrid hydrogel solutions with embedded cells. It was demonstrated that the integrated cells survived the printing process with high viability measured after 21 d. Moreover, by this reinforcing technique, robust hydrogel-containing constructs were fabricated. In addition to thiol-ene cross-linked hydrogels, hydrogel cross-linking via ionic interactions was investigated with a hybrid hydrogel based on HMW HA and peptide-functionalized PG. Rheological measurements revealed an increase in the viscosity of a 2 wt.\% HMW HA solution by the addition of peptide-functionalized PG. The increase in viscosity could be attributed to the ionic interactions between the positively charge PG and the negatively charge HMW HA. In conclusion, throughout this thesis thiol-ene chemistry and PG were introduced as promising cross-linking reaction and polymer precursor for the field of biofabrication. Furthermore, the differences of hybrid and synthetic hydrogels as well as chemically and physically cross-linked hydrogels were demonstrated. Moreover, the double printing approach was demonstrated to be a promising tool for the fabrication of robust hydrogel-containing constructs. It opens the possibility of printing hydrogels that were not printable yet, due to too low viscosities.}, subject = {Hyalurons{\"a}ure}, language = {en} } @phdthesis{Boeck2018, author = {B{\"o}ck, Thomas}, title = {Multifunctional Hyaluronic Acid / Poly(glycidol) Hydrogels for Cartilage Regeneration Using Mesenchymal Stromal Cells}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-155345}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2018}, abstract = {Improved treatment options for the degenerative joint disease osteoarthritis (OA) are of major interest, since OA is one of the main sources of disability, pain, and socioeconomic burden worldwide [202]. According to epidemiological data, already 27 million people suffer from OA in the US [23]. Moreover, the WHO expects OA to be the fourth most common cause of disability in 2020 [203], illustrating the need for effective and long-lasting therapy options of severe cartilage defects. Despite numerous clinically available products for the treatment of cartilage defects [62], the development of more cartilage-specific materials is still at the beginning. Hyaluronic acid (HA) is a major component of the cartilaginous extracellular matrix (ECM) and inherently creates a cell-friendly niche by providing cell attachment and migration sites. Furthermore, it is known that the functional groups of HA are well suited for chemical modification. These characteristics render HA an attractive material for hydrogel-based tissue engineering approaches. Poly(glycidol) (PG) as chemical crosslinker basically features similar chemical characteristics as the widely used poly(ethylene glycol) (PEG), but provides additional side groups at each repeating unit that can be further chemically functionalized. With the introduction of PG as multifunctional crosslinker for HA gels, a higher cross-linking density and, accordingly, a greater potential for biomimetic functionalization may be achieved. However, despite the mentioned potential benefits, PG has not been used for cartilage regeneration approaches so far. The initial aim of the study was to set up and optimize a HA-based hydrogel for the chondrogenic differentiation of mesenchymal stromal cells (MSCs), using different amounts and variations of cross-linkers. Therefore, the hydrogel composition was optimized by the utilization of different PEG diacrylate (PEGDA) concentrations to cross-link thiol-modified HA (Glycosil, HA-SH) via Michael addition. We aimed to generate volumestable scaffolds that simultaneously enable a maximum of ECM deposition. Histological and biochemical analysis showed 0.4\% PEGDA as the most suitable concentration for these requirements (Section 5.1.2). In order to evaluate the impact of a differently designed cross-linker on MSC chondrogenesis, HA-SH was cross-linked with PEGTA (0.6\%) and compared to PEGDA (0.4\%) in a next step. Following this, acrylated PG (PG-Acr) as multifunctional cross-linker alternative to acrylated PEG was evaluated. It provides around five times more functional groups when utilized in PG-Acr (0.6\%) HA-SH hydrogels compared to PEGTA (0.6\%) HA-SH hydrogels, thus enabling higher degrees of biomimetic functionalization. Determination of cartilage-specific ECM components showed no substantial differences between both cross-linkers while the deposition of cartilaginous matrix appeared more homogeneous in HA-SH PG-Acr gels. Taken together, we were able to successfully increase the possibilities for biomimetic functionalization in the developed HA-SH hydrogel system by the introduction of PG-Acr as cross-linker without negatively affecting MSC chondrogenesis (Section 5.1.3). The next part of this thesis focused extensively on the biomimetic functionalization of PG-Acr (0.6\%) cross-linked HA-SH hydrogels. Here, either biomimetic peptides or a chondrogenic growth factor were covalently bound into the hydrogels. Interestingly, the incorporation of a N-cadherin mimetic (HAV), a collagen type II binding (KLER), or a cell adhesion-mediating peptide (RGD) yielded no improvement of MSC chondrogenesis. For instance, the covalent binding of 2.5mM HAV changed morphology of cell nuclei and reduced GAG production while the incorporation of 1.0mM RGD impaired collagen production. These findings may be attributed to the already supportive conditions of the employed HA-based hydrogels for chondrogenic differentiation. Most of the previous studies reporting positive peptide effects on chondrogenesis have been carried out in less supportive PEG hydrogels or in significantly stiffer MeHA-based hydrogels [99, 101, 160]. Thus, the incorporation of peptides may be more important under unfavorable conditions while inert gel systems may be useful for studying single peptide effects (Section 5.2.1). The chondrogenic factor transforming growth factor beta 1 (TGF-b1) served as an example for growth factor binding to PG-Acr. The utilization of covalently bound TGF-b1 may thereby help overcome the need for repeated administration of TGF-b1 in in vivo applications, which may be an advantage for potential clinical application. Thus, the effect of covalently incorporated TGF-b1 was compared to the effect of the same amount of TGF-b1 without covalent binding (100nM TGF-b1) on MSC chondrogenesis. It was successfully demonstrated that covalent incorporation of TGF-b1 had a significant positive effect in a dose-dependent manner. Chondrogenesis of MSCs in hydrogels with covalently bound TGF-b1 showed enhanced levels of chondrogenesis compared to hydrogels into which TGF-b1 was merely mixed, as shown by stronger staining for GAGs, total collagen, aggrecan and collagen type II. Biochemical evaluation of GAG and collagen amounts, as well as Western blot analysis confirmed the histological results. Furthermore, the positive effect of covalently bound TGF-b1 was shown by increased expression of chondrogenic marker genes COL2A1, ACAN and SOX9. In summary, covalent growth factor incorporation utilizing PG-Acr as cross-linker demonstrated significant positive effects on chondrogenic differentiation of MSCs (Section 5.2.2). In general, PG-Acr cross-linked HA hydrogels generated by Michael addition represent a versatile hydrogel platform due to their high degree of acrylate functionality. These hydrogels may further offer the opportunity to combine several biological modifications, such as the incorporation of biomimetic peptides together with growth factors, within one cell carrier. A proof-of-principle experiment demonstrated the suitability of pure PG gels for studying single peptide effects. Here, the hydrogels were generated by the utilization of thiol-ene-click reaction. In this setting, without the supportive background of hyaluronic acid, MSCs showed enhanced chondrogenic differentiation in response to the incorporation of 1.0mM HAV. This was demonstrated by staining for GAGs, the cartilage-specific ECM molecules aggrecan and type II collagen, and by increased GAG and total collagen amounts shown by biochemical analysis. Thus, pure PG gels exhibit the potential to study the effects and interplay of peptides and growth factors in a highly modifiable, bioinert hydrogel environment. The last section of the thesis was carried out as part of the EU project HydroZONES that aims to develop and generate zonal constructs. The importance of zonal organization has attracted increased attention in the last years [127, 128], however, it is still underrepresented in tissue engineering approaches so far. Thus, the feasibility of zonal distribution of cells in a scaffold combining two differently composed hydrogels was investigated. A HA-SH(FMZ) containing bottom layer was generated and a pure PG top layer was subsequently cast on top of it, utilizing both times thiol-ene-click reaction. Indeed, stable, hierarchical constructs were generated that allowed encapsulated MSCs to differentiate chondrogenically in both zones as shown by staining for GAGs and collagen type II, and by quantification of GAG amount. Thus, the feasibility of differently composed zonal hydrogels utilizing PG as a main component was successfully demonstrated (Section 5.4). With the first-time utilization and evaluation of PG-Acr as versatile multifunctional cross-linker for the preparation of Michael addition-generated HA-SH hydrogels in the context of cartilage tissue engineering, a highly modifiable HA-based hydrogel system was introduced. It may be used in future studies as an easily applicable and versatile toolbox for the generation of biomimetically functionalized hydrogels for cell-based cartilage regeneration. The introduction of reinforcement structures to enhance mechanical resistance may thereby further increase the potential of this system for clinical applications. Additionally, it was also demonstrated that thiol-ene clickable hydrogels can be used for the generation of cell-laden, pure PG gels or for the generation of more complex, coherent zonal constructs. Furthermore, thiol-ene clickable PG hydrogels have already been further modified and successfully been used in 3D bioprinting experiments [204]. 3D bioprinting, as part of the evolving biofabrication field [205], offers the possibilities to generate complex and hierarchical structures, and to exactly position defined layers, yet at the same time alters the requirements for the utilized hydrogels [159, 206-209]. Since a robust chondrogenesis of MSCs was demonstrated in the thiol-ene clickable hydrogel systems, they may serve as a basis for the development of hydrogels as so called bioinks which may be utilized in more sophisticated biofabrication processes.}, subject = {Hyalurons{\"a}ure}, language = {en} } @phdthesis{Schoenwaelder2016, author = {Sch{\"o}nw{\"a}lder, Sina Maria Siglinde}, title = {Entwicklung und Charakterisierung von Gelatine-basierten Hydrogelen und PLGA-basierten Janus-Partikeln}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-142636}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2016}, abstract = {Zusammenfassung In der Regenerativen Medizin sind polymerbasierte Biomaterialien von großer Bedeutung f{\"u}r die Entwicklung und Anwendung verbesserter bzw. neuer Therapien. Die Erforschung der Oberfl{\"a}cheneigenschaften von Biomaterialien, welche als Implantate eingesetzt werden, ist eine grundlegende Voraussetzung f{\"u}r deren erfolgreichen Einsatz. Die Protein-Oberfl{\"a}chen- Interaktion geschieht initial, sobald ein Implantat mit K{\"o}rperfl{\"u}ssigkeiten oder mit Gewebe in Kontakt kommt, und tr{\"a}gt maßgeblich zur direkten Wechselwirkung von Implantat und umgebenden Zellen bei. Dieser Prozess wird in der vorliegenden Arbeit an Gelatine untersucht. Daher bestand ein Ziel darin, stabile, nanometerd{\"u}nne Gelatineoberfl{\"a}chen herzustellen und darauf die Adsorption von humanen Plasmaproteinen und bakteriellen Proteinen zu analysieren. Die Abscheidung der Gelatinefilme in variabler Schichtdicke auf zuvor mit PPX-Amin modifizierten Oberfl{\"a}chen wurde unter Verwendung eines Rotationsbeschichters durchgef{\"u}hrt. Um stabile Hydrogelfilme zu erhalten, wurden die Amingruppen der disaggregierten Gelatinefibrillen untereinander und mit denen der Amin-Modifizierung durch ein biokompatibles Diisocyanat quervernetzt. Dieser Prozess lieferte einen reproduzierbaren und chemisch stabilen Gelatinefilm, welcher durch die substratunabh{\"a}ngige Amin-Modifizierung kovalent auf unterschiedlichste Oberfl{\"a}chen aufgebracht werden konnte. Die durch den Herstellungsprozess pr{\"a}zise eingestellte Schichtdicke (Nano- bzw. Mikrometermaßstab) wurde mittels Ellipsometrie und Rasterkraftmikroskopie ermittelt. Die ebenso bestimmte Rauheit war unabh{\"a}ngig von der Schichtdicke sehr gering. Gelatinefilme, die auf funktionalisierte und strukturierte Proben aufgebracht wurden, konnten durch Elektronenmikroskopie dargestellt werden. Mit Hilfe der Infrarot-Reflexions-Absorptions-Spektroskopie wurden die Gelatinefilme im Hinblick auf ihre Stabilit{\"a}t chemisch charakterisiert. Zur Quantifizierung der Adsorption humaner Plasmaproteine (Einzelproteinl{\"o}sungen) und komplexer Proteingemische aus steril filtrierten Kultur{\"u}berst{\"a}nden des humanpathogenen Bakteriums Pseudomonas aeruginosa wurde die Quarzkristall-Mikrowaage mit Dissipations{\"u}berwachung eingesetzt. Hiermit konnte nicht nur die adsorbierte Menge an Proteinen auf dem Gelatinehydrogel bzw. Referenzoberfl{\"a}chen (Gold, PPX-Amin, Titan), sondern auch die viskoelastischen Eigenschaften des adsorbierten Proteinfilms bestimmt werden. Allgemein adsorbierte auf dem Gelatinehydrogel eine geringere Proteinmasse im Vergleich zu den Referenzoberfl{\"a}chen. Circa ein Viertel der adsorbierten Proteine migrierte in die Poren des gequollenen Gels und ver{\"a}nderte dessen viskoelastische Eigenschaften. Durch anschließende MALDI-ToF/MS- und MS/MS-Analyse konnten die bakteriellen Proteine auf den untersuchten Oberfl{\"a}chen identifiziert und untereinander verglichen werden. Hierbei zeigten sich nur geringf{\"u}gige Unterschiede in der Proteinzusammensetzung. Zudem wurde eine Sekund{\"a}rionenmassenspektrometrie mit Flugzeitanalyse an reinen Gelatinefilmen und an mit humanen Plasmaproteinen beladenen Gelatinefilmen durchgef{\"u}hrt. Durch eine anschließende multivariante Datenanalyse konnte zwischen den untersuchten Proben eindeutig differenziert werden. Dieser Ansatz erm{\"o}glicht es, die Adsorption von unterschiedlichen Proteinen auf proteinbasierten Oberfl{\"a}chen markierungsfrei zu untersuchen und kann zur Aufkl{\"a}rung der in vivo-Situation beitragen. Dar{\"u}ber hinaus bietet dieser Untersuchungsansatz neue Perspektiven f{\"u}r die Gestaltung und das schnelle und effiziente Screening von unterschiedlichen Proteinzusammensetzungen. Biomaterialien k{\"o}nnen jedoch nicht nur als Implantate oder Implantatbeschichtungen eingesetzt werden. Im Bereich des drug delivery und der Depotarzneimittel sind biologisch abbaubare Polymere, aufgrund ihrer variablen Eigenschaften, von großem Interesse. Die Behandlung von bakteriellen und fungalen Pneumonien stellt insbesondere bei Menschen mit Vorerkrankungen wie Cystische Fibrose oder prim{\"a}re Ziliendyskinesie eine große Herausforderung dar. Oral oder intraven{\"o}s applizierte Wirkstoffe erreichen die Erreger aufgrund der erh{\"o}hten Z{\"a}higkeit des Bronchialsekretes oft nicht in ausreichender Konzentration. Daher besteht ein weiteres Ziel der vorliegenden Arbeit darin, mittels electrohydrodynamic cojetting mikrometergroße, inhalierbare, wirkstoffbeladene Partikel mit zwei Kompartimenten (Janus-Partikel) herzustellen und deren Eignung f{\"u}r die therapeutische Anwendung bei Lungeninfektionen zu untersuchen. Durch das in dieser Arbeit entwickelte L{\"o}sungsmittelsystem k{\"o}nnen Janus-Partikel aus biologisch abbaubaren Co-Polymeren der Polymilchs{\"a}ure (Poly(lactid-co-glycolid), PLGA) hergestellt und mit verschiedenen Wirkstoffen beladen werden. Darunter befinden sich ein Antibiotikum (Aztreonam, AZT), ein Antimykotikum (Itraconazol, ICZ), ein Mukolytikum (Acetylcystein, ACC) und ein Antiphlogistikum (Ibuprofen, IBU). Die Freisetzung der eingelagerten Wirkstoffe, mit Ausnahme von ICZ, konnte unter physiologischen Bedingungen mittels Dialyse und anschließender Hochleistungsfl{\"u}ssigkeitschromatographie gemessen werden. Die Freisetzungsrate wird von der Kettenl{\"a}nge des Polymers beeinflusst, wobei eine k{\"u}rzere Kettenl{\"a}nge zu einer schnelleren Freisetzung f{\"u}hrt. Das in die Partikel eingelagerte Antimykotikum zeigte in vitro eine gute Wirksamkeit gegen Aspergillus nidulans. Durch das Einlagern von ICZ in die Partikel ist es m{\"o}glich diesen schlecht wasserl{\"o}slichen Wirkstoff in eine f{\"u}r Patienten zug{\"a}ngliche und wirksame Applikationsform zu bringen. In Interaktion mit P. aeruginosa erzielten die mit Antibiotikum beladenen Partikel in vitro bessere Ergebnisse als der Wirkstoff in L{\"o}sung, was sich in einem in vivo-Infektionsmodell mit der Wachsmotte Galleria mellonella best{\"a}tigte. AZT-beladene Partikel hatten gegen{\"u}ber einer identischen Wirkstoffmenge in L{\"o}sung eine 27,5\% bessere {\"U}berlebensrate der Wachsmotten zur Folge. Des Weiteren hatten die Partikel keinen messbaren negativen Einfluss auf die Wachsmotten. Dreidimensionale Atemwegsschleimhautmodelle, hergestellt mit Methoden des Tissue Engineerings, bildeten die Basis f{\"u}r Untersuchungen der Partikel in Interaktion mit humanen Atemwegszellen. Die Untersuchung von Apoptose- und Entz{\"u}ndungsmarkern im {\"U}berstand der 3D-Modelle zeigte diesbez{\"u}glich keinen negativen Einfluss der Partikel auf die humanen Zellen. Diese gut charakterisierten und standardisierten in vitro-Testsysteme machen es m{\"o}glich, Medikamentenuntersuchungen an menschlichen Zellen durchzuf{\"u}hren. Hinsichtlich der histologischen Architektur und funktionellen Eigenschaften der 3D-Modelle konnte eine hohe in vitro-/in vivo-Korrelation zu menschlichem Gewebe festgestellt werden. Humane Mucine auf den 3D-Modellen dienten zur Untersuchung der schleiml{\"o}senden Wirkung von ACC-beladenen Partikeln. Standen diese in r{\"a}umlichem Kontakt zu den Mucinen, wurde deren Z{\"a}higkeit durch das freigesetzte ACC herabgesetzt, was qualitativ mittels histologischen Methoden best{\"a}tigt werden konnte. Die in dieser Arbeit entwickelten Herstellungsprotokolle dienen als Grundlage und k{\"o}nnen f{\"u}r die Synthese {\"a}hnlicher Systeme, basierend auf anderen Polymeren und Wirkstoffen, modifiziert werden. Gelatine und PLGA erwiesen sich als vielseitig einsetzbare Werkstoffe und bieten eine breite Anwendungsvielfalt in der Regenerativen Medizin, was die erzielten Resultate bekr{\"a}ftigen.}, subject = {Gelatine}, language = {de} } @phdthesis{RamosTirado2015, author = {Ramos Tirado, Mario}, title = {Stammzellbasierte Behandlungsstrategien zur Stimmlippenaugmentation und laryngealen Defektrekonstruktion}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-117528}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2015}, abstract = {Der Kehlkopf ist ein stimmerzeugendes knorpelhaltiges Organ und spielt eine wichtige Rolle in der Atemfunktion und beim aspirationsfreien Schluckakt. Funktionsst{\"o}rungen des Kehlkopfs wie Stimmbandl{\"a}hmungen werden durch Sch{\"a}digungen des Kehlkopfnervs nach operativen Eingriffen und Halsverletzungen hervorgerufen. Des Weiteren f{\"u}hren durch Traumen, Teil- und komplette Resektionen verursachte Substanzdefekte des Kehlkopfs zu Funktionsverlusten. Die hierf{\"u}r notwendigen und komplexen Rekonstruktionen werden durch das schlechte Regenerationspotential von Knorpelgewebe eingeschr{\"a}nkt und k{\"o}nnen nur bedingt durch synthetische Ersatzmaterialen oder k{\"o}rpereigenes Ersatzgewebe bewerkstelligt werden. Ist es m{\"o}glich, mit Hilfe des Tissue Engineerings aus k{\"o}rpereigenen Stammzellen und biokompatiblen Tr{\"a}germaterialien implantierbares Knorpelersatzgewebe herzustellen, welches zur dauerhaften Wiederherstellung der Kehlkopffunktionen eingesetzt werden kann? Die zus{\"a}tzliche Markierung von Stammzellen mit superparamagnetischen Eisenoxidnanopartikeln (VSOP) als Zellmarker bietet die M{\"o}glichkeit der Detektion und der Verfolgung der Zellen mittels nicht-invasiver Nachweismethoden nach deren Implantation. Ist die Verwendung dieser Nanopartikel ohne negative Folgen f{\"u}r die Stammzellen m{\"o}glich und sind diese f{\"u}r den Einsatz in der Laryngologie geeignet? Fettgewebsstammzellen (ASC) wurden aus humanem Liposuktionsmaterial und Kaninchen-Nackenfett isoliert und expandiert. Die Zellen wurden in Hydrogelkombinationen aus Kollagen Typ-I, Agarose, Fibrin und Hyalurons{\"a}ure eingebettet und mit den chondrogenen Wachstumsfaktoren TGF-β3, BMP-6 und IGF-I {\"u}ber 14 Tage differenziert. Anschließend wurden diese Zell-Hydrogelkonstrukte bez{\"u}glich Morphologie, extrazellul{\"a}rer Matrixanreicherung und knorpelspezifischer Genexpression histologisch, immunhistochemisch und molekularbiologisch analysiert. In einem weiteren Schritt wurden die Integration der Zell-Hydrogelkonstrukte in natives Knorpelgewebe sowie die Defektdeckung in einem in vitro- und einem in vivo-Knorpeldefektmodell mit vor- und nicht-vordifferenzierten Zell-Hydrogelkonstrukten untersucht. Die Analyse m{\"o}glicher zyto- und genotoxischer Effekte von VSOP sowie des Einflusses der Markierung von ASC mit VSOP auf die Proliferation, Migration und das Multidifferenzierungspotential erfolgte nach der Markierung der Zellen mit unterschiedlichen VSOP-Konzentrationen. Außerdem wurden VSOP-markierte ASC in Kaninchenstimmlippen injiziert und die Nachweisbarkeit dieser Zellen im Injektionsareal histologisch und mittels Magnetresonanztomographie (MRT) untersucht. Nach 14-t{\"a}giger chondrogener Differenzierung wurde in den Zell-Hydrogelkonstrukten eine knorpel{\"a}hnliche Morphologie, die Anreicherung knorpelspezifischer Matrixproteine und die Expression chondrogener Markergene nachgewiesen. Die Kombination der chondrogenen Wachstumsfaktoren zeigte keinen verst{\"a}rkenden Einfluss auf die Chondrogenese von ASC. Hydrogele aus Kollagen Typ I und Hyalurons{\"a}ure wiesen die st{\"a}rkste extrazellul{\"a}re Matrixanreicherung auf. Bei den agarosefreien Hydrogelen war eine ausgepr{\"a}gte Gelschrumpfung auff{\"a}llig. In den beiden Knorpeldefektmodellen konnte weder eine Integration der Zell-Hydrogelkonstrukte in den Nativknorpel noch eine vollst{\"a}ndige Defektdeckung nachgewiesen werden. Nach der Markierung von ASC mit VSOP zeigte sich bei der h{\"o}chsten Konzentration von 1,5 mM eine genotoxische Wirkung. Zytotoxische Effekte sowie Einfl{\"u}sse der Markierung auf die Proliferation, Migration und das Multidifferenzierungspotential von ASC waren nicht nachweisbar. VSOP-markierte ASC konnten nach deren Injektion in Kaninchenstimmlippen im Injektionsareal nur vereinzelt mittels MRT und histologisch nachgewiesen werden. Es ist m{\"o}glich, mit Hilfe des Tissue Engineerings aus k{\"o}rpereigenen Stammzellen und biokompatiblen Tr{\"a}germaterialien implantierbares knorpel{\"a}hnliches Gewebe herzustellen. Dabei beg{\"u}nstigen agarosefreie Tr{\"a}germaterialien die chondrogene Differenzierung von ASC. Diese k{\"o}nnte durch die jeweilige Erh{\"o}hung der Zelldichte und Wachstumsfaktorkonzentrationen sowie die Verl{\"a}ngerung der Induktionszeit verst{\"a}rkt werden. Eine m{\"o}gliche klinische Anwendung dieser knorpel{\"a}hnlichen Gewebe in der Laryngologie ist jedoch durch deren Schrumpfung wie auch mangelnde Integration und Defektdeckung noch weit entfernt. Aufgrund ihrer genotoxischen Wirkung kann eine Verwendung von VSOP als Zellmarker auch unterhalb von 1,5 mM ohne negative Folgen f{\"u}r den Organismus nicht sicher ausgeschlossen werden. Der inhomogene Gewebekontrast im Kehlkopf, die schlechte Aufl{\"o}sung im MRT und die geringe Gr{\"o}ße von VSOP erschweren die Nachweisbarkeit und Verfolgung markierter Zellen mittels MRT. Daher sind andere nicht-invasive Nachweismethoden f{\"u}r die Verwendung von VSOP im Kehlkopf zu evaluieren. Der m{\"o}glichen Anwendung dieser knorpel{\"a}hnlichen Gewebe und VSOP in der rekonstruktiven Laryngologie muss eine erfolgreiche Optimierung und ausf{\"u}hrliche positive Validierung in klinischen Tests vorausgehen.}, subject = {Tissue Engineering}, language = {de} } @phdthesis{Beer2011, author = {Beer, Meike Vanessa}, title = {Correlation of ligand density with cell behavior on bioactive hydrogel layers}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-74454}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2011}, abstract = {Diese Arbeit besch{\"a}ftigte sich mit der Quantifizierung von Zelladh{\"a}sion vermittelnden Liganden in und auf d{\"u}nnen Hydrogelschichten, die zur Oberfl{\"a}chenmodifizierung auf Biomaterialien aufgebracht wurden. Das bereits etablierte und gut charakterisierte inerte NCO-sP(EO-stat-PO) Hydrogelsystem, das eine einfache und reproduzierbare Bioaktivierung mit Peptiden erlaubt, wurde als Basis f{\"u}r diese Arbeit verwendet. Diese Hydrogele k{\"o}nnen auf zwei Weisen funktionalisiert werden. Liganden k{\"o}nnen entweder mit der Prepolymerl{\"o}sung vor der Beschichtung gemischt (Einmischmethode) oder frische Hydrogelschichten mit einer Ligandenl{\"o}sung inkubiert werden (Inkubationsmethode). Der erste Teil dieser in drei Hauptteile unterteilten Arbeit, besch{\"a}ftigte sich mit der Konzentrationsbestimmung der Liganden in der gesamten Tiefe der Hydrogelschicht, w{\"a}hrend sich der zweite Teil auf die oberfl{\"a}chensensitive Quantifizierung von Zelladh{\"a}sion vermittelnden Molek{\"u}len an der biologischen Grenzfl{\"a}che konzentrierte. Die Ergebnisse wurden mit Zelladh{\"a}sionskinetiken verglichen. Der dritte Teil dieser Arbeit besch{\"a}ftigte sich mit der biochemischen als auch strukturellen Nachahmung der komplexen Extrazellul{\"a}rmatrix (ECM). Das ECM Protein Fibronektin (FN) wurde {\"u}ber Zucker-Lektin Anbindung pr{\"a}sentiert und Zellverhalten auf diesen biomimetischen Oberfl{\"a}chen untersucht. Ebenfalls wurde Zellverhalten in einer dreidimensionalen Faserumgebung mit identischer Oberfl{\"a}chenchemie wie in den beiden ersten Teilen dieser Arbeit untersucht und mit der Peptidkonzentration korreliert. Insgesamt, war die Hauptfragestellung in dieser Arbeit 'Wie viel?', d.h. einerseits die Ermittlung der maximalen, als auch der f{\"u}r Zelladh{\"a}sion optimalen Ligandendichte. Im ersten praktischen Teil der vorliegenden Arbeit (Klassische Quantifizierung) wurden Liganden in der gesamten Hydrogelschicht, als auch speziell in oberen Bereichen der Schichten quantifiziert. Die Untersuchung der Hydrogelschichten in Wellplatten und auf Glas funktionalisiert mit GRGDS und 125I-YRGDS erfolgte in Kapitel 3 mittels Radioaktivmessung. Wurden Hydrogelschichten mittels Inkubationsmethode funktionalisiert, konnte eine S{\"a}ttigung mit Liganden bei etwa 600 µg/mL ermittelt werden. Mittels Einmischmethode funktionalisierte Hydrogele erreichten keine maximale Ligandenkonzentration in den Schichten, mit dem Verh{\"a}ltnis 2/1 als maximales verwendetes Verh{\"a}ltnis. H{\"o}here Liganden zu Prepolymer Verh{\"a}ltnisse als 2/1 wurden jedoch nicht verwendet, um eine ausreichende Vernetzung der Hydrogele nicht zu gef{\"a}hrden. Zur Detektion mittels R{\"o}ntgenphotoelektronenspektroskopie (XPS) und Flugzeit-Sekund{\"a}rionen-Massen-spektrometrie (TOF-SIMS) (Kapitel 4) wurden eine fluorierte Aminos{\"a}ure und ein iodiertes Peptid mit den Prepolymeren in molaren Verh{\"a}ltnissen von 1/2, 1/1 und 2/1 gemischt. Beide Methoden ermittelten eine maximale Ligandenkonzentration bei Verh{\"a}ltnissen von 1/1. Zus{\"a}tzliche Liganden (2/1) f{\"u}hrten zu keiner vermehrten Anbindung. Wesentlich im Zusammenhang mit der Ligandenquantifizierung auf Biomaterialien ist, diese an der Oberfl{\"a}che, die f{\"u}r Zellen zug{\"a}nglich ist, durchzuf{\"u}hren. Im zweiten Teil dieser Arbeit (Oberfl{\"a}chensensitive Quantifizierung) kamen daher Methoden zum Einsatz, die Liganden ausschließlich auf der Oberfl{\"a}che quantifizierten. Zur Detektion mit Oberfl{\"a}chenplasmon-resonanz (SPR) und akustischer Oberfl{\"a}chenwellentechnologie (SAW) in Kapitel 5 musste die Standardbeschichtung der Hydrogele von Glas und Silikon auf Cystamin funktionalisierte Goldoberfl{\"a}chen {\"u}bertragen werden. Mittels Ellipsometrie und Rasterkraftmikroskopie (AFM) konnte nur eine d{\"u}nne und inhomogene Hydrogelbeschichtung nachgewiesen werden. Dennoch zeigten SPR und SAW die Unterbindung von Serum und Streptavidin (SA) Adsorption auf nicht funktionalisierten Schichten, jedoch eine spezifische und konzentrationsabh{\"a}ngige SA Bindung auf Hydrogelschichten, die mit Biocytin und GRGDSK-biotin funktionalisiert wurden. Die Ligandenquantifizierung mittels Enzymgekoppeltem Immunadsorptionstest (ELISA) und Enzymgekoppelten Lektinadsorptionstest (ELLA) (Kapitel 6) wurde auf Hydrogelschichten in Wellplatten und auf Glas angewendet, die mit verschiedenen Liganden mittels Inkubation und Einmischung funktionalisiert wurden. Das Modellmolek{\"u}l Biocytin, das biotinylierte Peptid GRGDSK-biotin, das ECM Protein Fibronektin (FN), als auch die Modellzucker N-Acetyl-glukosamin (GlcNAc) und N-Acetyllaktosamin (LacNAc) konnten spezifisch in verschiedenen Konzentrationen nachgewiesen werden. Beispielhaft seien hier Schichten auf Glas genannt, die mittels Einmischmethode mit GRGDSK-biotin funktionalisiert wurden, da diese zum Vergleich in Kapitel 8 herangezogen wurden. Auf diesen Oberfl{\"a}chen wurde eine maximale Peptidkonzentration auf der Oberfl{\"a}che bei einem Peptid zu Prepolymer Verh{\"a}ltnis von 1/5 ermittelt. Neben diesen verschiedenen Quantifzierungsmethoden ist die in vitro Analyse mit Zellen nicht zu vernachl{\"a}ssigen (Kapitel 7). Hierzu wurden Hydrogele auf Glas aufgebracht und mit GRGDS mittels Einmischmethode funktionalisiert. Durch Z{\"a}hlen adh{\"a}renter prim{\"a}rer humaner dermaler Fibroblasten (HDF) auf Mikroskopbildern wurde eine maximale Zelladh{\"a}sion bei dem Peptid zu Prepolymer Verh{\"a}ltnis von 1/5 festgestellt. Hingegen wurde ein Verh{\"a}ltnis von 1/2 f{\"u}r optimale Zelladh{\"a}sion ermittelt, wenn Zellen zur Quantifizierung von den Hydrogelen abgel{\"o}st und im CASY® Zellz{\"a}hler quantifiziert wurden. Zus{\"a}tzlich wurde die Zellvitalit{\"a}t durch Messung intrazellul{\"a}rer Enzymaktivit{\"a}ten gemessen, jedoch konnte kein Zusammenhang zwischen Zellvitalit{\"a}t und GRGDS Konzentration hergestellt werden. Adh{\"a}rente HDFs waren in allen F{\"a}llen vital, unabh{\"a}ngig von der Ligandenkonzentration auf der Oberfl{\"a}che. Auch die Mausfibroblasten Zelllinie NIH L929 wurde auf Hydrogelen mit verschiedenen GRGDS zu Prepolymer Verh{\"a}ltnissen durch Z{\"a}hlen adh{\"a}renter Zellen auf Mikroskopbildern untersucht. Diese im Verh{\"a}ltnis zu HDFs wesentlich kleineren Mauszellen ben{\"o}tigten h{\"o}here GRGDS Konzentrationen (2/1) f{\"u}r maximale Zelladh{\"a}sion. Nach der Ligandenquantifizierung in Kapitel 3 bis 7, wurden diese Ergebnisse in Kapitel 8 miteinander verglichen. Hierzu wurden Messungen auf Hydrogelschichten verwendet, die mittels Einmischmethode funktionalisiert wurden. W{\"a}hrend die Quantifizierung mittels Radioaktivmessung in der gesamten Tiefe der Hydrogelschichten keine maximale Ligandenkonzentration ermitteln konnte, war in den oberen Bereichen der Schicht ein Maximum an Liganden bei 1/1 festzustellen (XPS, TOF-SIMS). SPR und SAW wurden zum Vergleich nicht herangezogen, da die Beschichtung auf Gold erst optimiert werden muss. Oberfl{\"a}chensensitive Quantifizierung mittels ELISA und Zelladh{\"a}sion, die lediglich die sterisch zug{\"a}nglichen Liganden auf einer Oberfl{\"a}che nachweisen, ergaben {\"u}bereinstimmend eine optimale Ligandenkonzentration f{\"u}r SA Bindung und Zelladh{\"a}sion bei einem Peptid zu Prepolymer Verh{\"a}ltnis von 1/5. Dies unterstreicht, wie wichtig der Vergleich der Methoden, als auch die Verwendung von oberfl{\"a}chensensitiven Methoden ist. Der dritten Teil dieser Arbeit besch{\"a}ftigte sich mit der biochemischen und strukturellen Nachahmung der komplexen extrazellul{\"a}ren Umgebung (Advanced ECM engineering), ein wichtiger Aspekt in der Biomaterialforschung, da zum gr{\"o}ßten Teil zwei-dimensionale Biomaterialien zum Einsatz kommen, die direkt mit Liganden kovalent funktionalisiert werden. Die ECM ist jedoch um ein Vielfaches komplexer und die bestm{\"o}gliche Nachahmung ist Voraussetzung f{\"u}r eine bessere Akzeptanz durch Zellen und Gewebe. In Kapitel 9 wurde eine M{\"o}glichkeit aufgezeigt, das ECM Protein FN nicht-kovalent {\"u}ber Zucker-Lektinbindungen zu immobilisieren. Ein Schichtaufbau von Hydrogel, dem darauf durch Mikrokontakt-druckverfahren (MCP) kovalent gebundenen Zucker Poly-N-Acetyllaktosamin (polyLacNAc) und den darauf nicht-kovalent gebundenen Galektin His6CGL2 und FN, konnte mit Fluoreszenzf{\"a}rbung elegant nachgewiesen werden. Optimale Konzentrationen f{\"u}r den Schichtaufbau wurden mittels ELLA/ELISA auf Hydrogelschichten ermittelt, die durch Inkubation mit dem Zucker funktionalisiert wurden. Nur der komplette Schichtaufbau konnte zufriedenstellende HDF Adh{\"a}sion vermitteln und im Vergleich zu Zellkulturpolystyrol (TCPS) Oberfl{\"a}chen konnten HDFs auf dem biomimetischen Schichtaufbau schneller adh{\"a}rieren und spreiten. Zudem wurde die Umorganisierung von auf Glas adsorbiertem FN, auf NCO-sP(EO-stat-PO) kovalent gebundenem FN und biomimetisch {\"u}ber polyLAcNAc-His6CGL2 gebundenem FN durch HDFs verglichen. Nur auf den biomimetischen Oberfl{\"a}chen schien eine Umorganisation durch die Zellen m{\"o}glich, wie sie auch in der ECM zu finden ist. Diese biomimetische und flexible Pr{\"a}sentation eines Proteins erwies sich als vielversprechende M{\"o}glichkeit eine biomimetischere Oberfl{\"a}che f{\"u}r Zellen zu schaffen, die eine optimale Biokompatibilit{\"a}t erm{\"o}glichen k{\"o}nnte. Auch die strukturelle Nachahmung der ECM ist eine vielversprechende Strategie zum Nachbau der ECM. In Kapitel 10 wurde ein Einschrittverfahren zur Herstellung synthetischer, bioaktiver und degradierbarer Faserkonstrukte durch Elektrospinnen zur Nachahmung der ECM pr{\"a}sentiert. In diesem System wurden durch Zugabe von NCO-sP(EO-stat-PO) als reaktives Additiv zu Poly(D,L-laktid-co-Glycolid) (PLGA) Fasern hergestellt, die mit einer ultrad{\"u}nnen, inerten Hydrogelschicht versehen waren. Es konnte gezeigt werden, dass durch die Verwendung von NCO-sP(EO-stat-PO) als Additiv die Adsorption von Rinderserumalbumin (BSA) im Vergleich zu PLGA um 99,2\% reduziert, die Adh{\"a}sion von HDFs verhindert und die Adh{\"a}sion von humanen mesenchymalen Stammzellen (MSC) minimiert werden konnten. Spezifische Bioaktivierung wurde durch Zugabe von Peptidsequenzen zur Spinl{\"o}sung erreicht, welche kovalent in die Hydrogelschicht eingebunden werden konnten und kontrollierte Zell-Faser Interaktionen erm{\"o}glichten, Um die spezifische Zelladh{\"a}sion an solchen inerten Fasern zu erzielen, wurde GRGDS kovalent auf der Faseroberfl{\"a}che gebunden. Dies erfolgte durch Zugabe des Peptids zur Polymerl{\"o}sung vor dem Elektrospinnen. Als Negativkontrolle wurde die Peptidsequenz GRGES an die Faseroberfl{\"a}che gebunden, welche durch Zellen nicht erkannt wird. W{\"a}hrend die Verhinderung unspezifischer Proteinadsorption f{\"u}r die Peptidmodifizierten Fasern erhalten blieb, konnten HDFs lediglich auf den mit GRGDS Peptid modifizierten Fasern adh{\"a}rieren, proliferieren und nach zwei Wochen eine konfluente Zellschicht aus vitalen Zellen bilden. Zus{\"a}tzlich konnten MSCs auf GRGDS funktionalisierten Fasern adh{\"a}rieren. Liganden konnten auf Fasern quantifiziert werden, indem die ELISA Technik aus Kapitel 6 auf Faseroberfl{\"a}chen transferiert wurde. Um das Potential der biochemischen und strukturellen Nachbildung der ECM aufzuzeigen, wurden beide Ans{\"a}tze miteinander kombiniert. Die Immobilisierung von polyLacNAc auf die Hydrogelfasern durch Inkubation und der Schichtaufbau mit His6CGL2 und FN resultierte in HDF Adh{\"a}sion.}, subject = {Hydrogel}, language = {en} } @phdthesis{Noeth2010, author = {N{\"o}th, Alexia Irmgard}, title = {Rekonstruktion von Gelenkknorpeldefekten mit einer Kollagen I Hydrogel Matrix - klinische Ergebnisse einer Fallseriestudie}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-52630}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2010}, abstract = {F{\"u}r die Rekonstruktion von Gelenkknorpeldefekten des Kniegelenkes in Folge eines Traumas oder einer Osteochondrosis dissecans (OD) stehen verschiedene operative Verfahren zur Verf{\"u}gung. Die Autologe Chondrozytentransplantation (ACT) hat sich als zuverl{\"a}ssiges Rekonstruktionsverfahren erwiesen. In der vorliegenden Arbeit wurde eine prospektive Fallseriestudie f{\"u}r eine neue Form der ACT mit einem Kollagen I Hydrogel (CaReS-Technologie) durchgef{\"u}hrt. Die Vorteile der Technologie liegen zum Einen darin, dass sich die Zellen homogen im Gel verteilen und zum Anderen, dass die Zellen unmittelbar nach dem Herausl{\"o}sen aus dem Gelenkknorpel in das Gel eingebracht werden und dadurch eine geringere Dedifferenzierung der Chondrozyten stattfindet. Von M{\"a}rz 2003 bis Ende 2006 wurden 29 Patienten in die Studie eingeschlossen. Die Ein- und Ausschlusskriterien erf{\"u}llten die Kriterien der Arbeitsgruppe ACT und Tissue Engineering der Deutschen Gesellschaft f{\"u}r Orthop{\"a}die und Unfallchirurgie. Die Eingangs- und Nachuntersuchungsb{\"o}gen wurden an die IKDC Form 2000 angelehnt. Insgesamt zeigte sich ein signifikanter Anstieg des IKDC Scores im mittleren follow-up von 30,7 Monaten von 47,3 auf 74,9 bei den 29 Patienten. Bei Aufschl{\"u}sselung der Patienten bzgl. Diagnose, Defektgr{\"o}ße, Lokalisation und Defektanzahl zeigte sich bei den Behandlungsgruppen OD, Trauma/degenerativ, > 4 cm2, mediale Femurkondyle und Einzeldefekte eine signifikante Zunahme des IKDC Scores im zeitlichen Verlauf. Der postoperative Schmerz zeigte einhergehend mit dem Anstieg des IKDC Scores eine signifikante Abnahme der Schmerzintensit{\"a}t in den Behandlungsgruppen OD, Trauma/degenerativ, > 4 cm2, mediale Femurkondyle und Einzeldefekte. Nachgewiesen wurde ebenfalls ein Anstieg des SF36 Scores, der den gegenw{\"a}rtigen Gesundheitszustand sowohl k{\"o}rperlich als auch psychisch beurteilt. Zusammen mit einer globalen Patientenzufriedenheit von 80\% und einem IKDC Funktionsstatus von I und II bei 77\% der Patienten spiegeln die gewonnenen Daten die Ergebnisse der klassischen ACT bzw. anderer matrixgekoppelten Verfahren wieder. Die CaReS-Technologie stellt somit ein gleichwertiges Verfahren zu den bisher auf dem Markt befindlichen Techniken der ACT dar.}, subject = {Gelenkknorpel}, language = {de} } @phdthesis{Heymer2008, author = {Heymer, Andrea}, title = {Chondrogenic differentiation of human mesenchymal stem cells and articular cartilage reconstruction}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-29448}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2008}, abstract = {Articular cartilage defects are still one of the major challenges in orthopedic and trauma surgery. Today, autologous chondrocyte transplantation (ACT), as a cell-based therapy, is an established procedure. However, one major limitation of this technique is the loss of the chondrogenic phenotype during expansion. Human mesenchymal stem cells (hMSCs) have an extensive proliferation potential and the capacity to differentiate into chondrocytes when maintained under specific conditions. They are therefore considered as candidate cells for tissue engineering approaches of functional cartilage tissue substitutes. First in this study, hMSCs were embedded in a collagen type I hydrogel to evaluate the cartilaginous construct in vitro. HMSC collagen hydrogels cultivated in different culture media showed always a marked contraction, most pronounced in chondrogenic differentiation medium supplemented with TGF-ß1. After stimulation with chondrogenic factors (dexamethasone and TGF-ß1) hMSCs were able to undergo chondrogenesis when embedded in the collagen type I hydrogel, as evaluated by the temporal induction of cartilage-specific gene expression. Furthermore, the cells showed a chondrocyte-like appearance and were homogeneously distributed within a proteoglycan- and collagen type II-rich extracellular matrix, except a small area in the center of the constructs. In this study, chondrogenic differentiation could not be realized with every hMSC preparation. With the improvement of the culture conditions, e.g. the use of a different FBS lot in the gel fabrication process, a higher amount of cartilage-specific matrix deposition could be achieved. Nevertheless, the large variations in the differentiation capacity display the high donor-to-donor variability influencing the development of a cartilaginous construct. Taken together, the results demonstrate that the collagen type I hydrogel is a suitable carrier matrix for hMSC-based cartilage regeneration therapies which present a promising future alternative to ACT. Second, to further improve the quality of tissue-engineered cartilaginous constructs, mechanical stimulation in specific bioreactor systems are often employed. In this study, the effects of mechanical loading on hMSC differentiation have been examined. HMSC collagen hydrogels were cultured in a defined chondrogenic differentiation medium without TGF-ß1 and subjected to a combined mechanical stimulation protocol, consisting of perfusion and cyclic uniaxial compression. Bioreactor cultivation neither affected overall cell viability nor the cell number in collagen hydrogels. Compared with non-loaded controls, mechanical loading promoted the gene expression of COMP and biglycan and induced an up-regulation of matrix metalloproteinase 3. These results circumstantiate that hMSCs are sensitive to mechanical forces, but their differentiation to chondrocytes could not be induced. Further studies are needed to identify the specific metabolic pathways which are altered by mechanical stimulation. Third, for the development of new cell-based therapies for articular cartilage repair, a reliable cell monitoring technique is required to track the cells in vivo non-invasively and repeatedly. This study aimed at analyzing systematically the performance and biological impact of a simple and efficient labeling protocol for hMSCs. Very small superparamagnetic iron oxide particles (VSOPs) were used as magnetic resonance (MR) contrast agent. Iron uptake was confirmed histologically with prussian blue staining and quantified by mass spectrometry. Compared with unlabeled cells, VSOP-labeling did neither influence significantly the viability nor the proliferation potential of hMSCs. Furthermore, iron incorporation did not affect the differentiation capacity of hMSCs. The efficiency of the labeling protocol was assessed with high resolution MR imaging at 11.7 Tesla. VSOP-labeled hMSCs were visualized in a collagen type I hydrogel indicated by distinct hypointense spots in the MR images, resulting from an iron specific loss of signal intensity. This was confirmed by prussian blue staining. In summary, this labeling technique has great potential to visualize hMSCs and track their migration after transplantation for articular cartilage repair with MR imaging.}, subject = {Gelenkknorpel}, language = {en} } @phdthesis{Rackwitz2007, author = {Rackwitz, Lars}, title = {In-vitro-Untersuchungen zur chondrogenen Differenzierung von humanen mesenchymalen Stammzellen in einem Kollagen I Hydrogel f{\"u}r den Gelenkknorpelersatz}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-22547}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2007}, abstract = {No abstract available}, language = {de} } @phdthesis{Grassmann2003, author = {Graßmann, Olaf}, title = {Biomimetische Materialabscheidung in funktionalisierten Hydrogelmatrices}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-6521}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2003}, abstract = {In Analogie zu nat{\"u}rlichen Proteinger{\"u}sten wurden poly-Acrylamid-Hydrogele mit polaren funktionellen Gruppen modifiziert, die in der Biomineralisation eine wichtige Rolle spielen. Durch gezielte Variation der Synthesebedingungen ist es m{\"o}glich, Art, Gehalt und r{\"a}umliche Anordnung der ionischen Funktionalit{\"a}ten in den Copolymernetzwerken einzustellen. Die Hydrogele wurden in einer Doppeldiffusionsanordnung zur Mineralisation von CaCO3 eingesetzt und die Ergebnisse mit Gelatinegel als nat{\"u}rlichem Reaktionsmedium verglichen. Entgegen der urspr{\"u}nglichen Erwartungen konnten in Gelatinegel keine Hinweise auf molekular-chemische Wechselwirkungen zwischen dem Proteinnetzwerk und den Mineralisationsprodukten nachgewiesen werden. Im Verlauf der Kristallisation wird die organische Matrix lediglich passiv inkorporiert. Allerdings bewirkt die heterogene Verteilung in den hantel{\"a}hnlichen Kompositpartikeln die Auff{\"a}cherung der Wachstumsfronten, so daß sich im Verlauf des Kristallwachstums eine Zwillingsstruktur der makroskopischen Produkte ausbildet. Der Netzwerkeffekt der organischen Matrix wird jedoch von dem lokalen chemischen Milieu in dem Gelk{\"o}rper {\"u}berlagert. Die {\"A}hnlichkeit der Produkte mit nat{\"u}rlichen Biomineralen weist darauf hin, daß auch Biomineralisationsprozesse lediglich Folge eines unspezifischen chemischen Milieus sein k{\"o}nnen. Deutliche Analogien zu nat{\"u}rlichen Biomineralisationsprodukten wurden bei der Materialabscheidung in unfunktionalisierten poly-Acrylamid-Hydrogelen beobachtet. Die oktaedrische Form der Mineralisationsprodukte ist untypisch f{\"u}r Calcit und kennzeichnet einen spezifischen Kristallisationsmechanismus. Obwohl die Aggregate aus zahlreichen rhomboedrischen Calcit-Bausteinen zusammengef{\"u}gt sind, weisen die makroskopischen Produkte eine gest{\"o}rte einkristalline Struktur auf. Das große Mosaik der R{\"o}ntgenbeugungsmaxima ist auf die Fehlorientierung koh{\"a}rent streuender Bereiche zur{\"u}ckzuf{\"u}hren. Basierend auf den Untersuchungsergebnissen wurde ein Aggregationsmodell postuliert: Die simultane orientierte Verwachsung rhomboedrischer Untereinheiten sowie das Fl{\"a}chenwachstum dieser Bausteine f{\"u}hrt zu der oktaedrischen Morphologie der Aggregate. Die prinzipielle Analogie der Mineralisationsprodukte mit vielen Biomineralen richtet den Blick auf die Frage, inwieweit alleine die physikalische Struktur extrazellul{\"a}rer Matrices eine wichtige Rolle bei der Biomineralisation spielt. Die Ergebnisse der Mineralisationsversuche in Sulfonat-funktionalisierten Hydrogelen untermauern den dominanten Effekt der Netzwerkstruktur. Die stark polaren funktionellen Gruppen modifizieren lediglich die Morphologie der Aggregate, f{\"u}hren aber nicht zu einer grundlegenden Ver{\"a}nderung der Nukleation und des Wachstumsmechanismus. Demgegen{\"u}ber zeigt sich in Carboxylat-funktionalisiertem poly-Acrylamid eine deutlich erh{\"o}hte Keimdichte und eine intermedi{\"a}re Stabilisierung von Vaterit. Dieser spezifische Einfluß der Carboxylatgruppen auf die Keimbildung relativiert das oft f{\"u}r Biomineralisationsvorg{\"a}nge postulierte ionotrope Nukleationsmodell und unterstreicht die Notwendigkeit einer stereochemischen Verwandtschaft zwischen den organischen Funktionalit{\"a}ten und der entstehenden Kristallphase. Besonders deutlich wird die Bedeutung der Carboxylatgruppen bei der Mineralisation in Gelmatrices, die mit poly-L-Aspartat versetzt wurden. Die Wirkungsweise des Gelatinegels sowie der Kompartimenteffekt des poly-Acrylamid wird durch die Wechselwirkung des Additivs mit der anorganischen Phase {\"u}berkompensiert: Im Verlauf der Doppeldiffusion entstehen in den untersuchten Hydrogelen Vaterit-Agglomerate, die permanent stabilisiert sind. Da die Kristallisationsmechanismen der reinen Gelmatrices rhomboedrische Calcit-Keimkristalle voraussetzen, werden die Netzwerkeffekte durch die Bildung sph{\"a}rischer Vaterit-Partikel außer Kraft gesetzt. M{\"o}glicherweise beruht auch die Morphogenese nat{\"u}rlicher Biomineralisationsprodukte auf einem Wechselspiel des physikalischen Netzwerkeffekts einer extrazellul{\"a}ren Matrix und der Wirkungsweise modifikationsselektiver Makromolek{\"u}le. In den unterschiedlichen Hydrogelmatrices sind, trotz einheitlicher Versuchsbedingungen, drei grunds{\"a}tzlich verschiedene Kristallisationsmechanismen des Calcits wirksam: In Gelatinegel kommt es zu lagenweisem Wachstum, die oktaedrischen Produkte aus poly-Acrylamid gehen auf die Aggregation vorgeformter Untereinheiten zur{\"u}ck und in Carboxylat-funktionalisierten Netzwerken entstehen sph{\"a}rolithische Kristalle. Diese Ergebnisse belegen auf anschauliche Weise eine Wechselwirkung der organischen Matrix mit der anorganischen Phase. In nat{\"u}rlichen Systemen wird dieser Effekt durch komplexe genetische und zellul{\"a}re Prozesse gesteuert, die sich in-vitro nicht simulieren lassen. Allerdings weisen die Analogien der Mineralisationsversuche mit nat{\"u}rlichen Biomineralisationsprozessen auf vergleichbare Prinzipien hin. Demzufolge k{\"o}nnen die Mechanismen der Biomineralisation verh{\"a}ltnism{\"a}ßig trivial sein, allein die biologische Reproduzierbarkeit der Materialabscheidung setzt ein hohes Maß an genetischer Steuerung voraus. Von einer weiterf{\"u}hrenden Untersuchung der Mechanismen, die der Biomineralisation zugrunde liegen, sind wesentliche Impulse f{\"u}r eine biomimetische Materialsynthese zu erwarten. Wie die spezifische Wechselwirkung der Carboxylatgruppen mit der Kristallphase nahelegt, sollten die molekular-chemischen Effekte polarer funktioneller Gruppen im Mittelpunkt des Interesses stehen. F{\"u}r ein besseres Gesamtverst{\"a}ndnis muß daher eine Br{\"u}cke zwischen der "mesoskopischen" Wirkung gelartiger Medien und entsprechenden Vorg{\"a}ngen auf atomarer Skala geschlagen werden. Die atomaren Mechanismen bei der Kristallisation von CaCO3 in Gegenwart verschiedener Additive werden in einem Partnerprojekt an der Universit{\"a}t M{\"u}nster untersucht [Set03]. Die Zusammenf{\"u}hrung dieser beiden Sichtweisen l{\"a}ßt ein tiefgreifendes Verst{\"a}ndnis der allgemeinen Prinzipien der Biomineralisation erwarten.}, subject = {Hydrogel}, language = {de} }