@phdthesis{Boehm2023,
  author    = {B{\"o}hm, Christoph},
  title     = {Thermal Stability of the Polyesters PCL and PLGA during Melt Electrowriting},
  doi       = {10.25972/OPUS-30613},
  url       = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-306139},
  school      = {Universit{\"a}t W{\"u}rzburg},
  year      = {2023},
  abstract  = {The focus of this thesis was to investigate how PCL and PLGA react to the heat exposure that comes with the MEW process over a defined timespan. To assess the thermal stability of PCL during MEW over 25 d, an automated collection of fibers has been used to determine the CTS on each day of heating for three different temperatures. PCL is exceptionally stable over 25 d at 75 °C, whereas for 85 °C and 95 °C a slight upward trend during the last 10 d could be observed, which is an indication for thermal degradation. Same trend could be observed for diameter of fibers produced at a fixed collector speed. For all temperatures, CTS during the first 5 d decreased due to inhomogeneities of the melt. Physical analysis of the fibers by XRD and mechanical testing showed no significant changes. To investigate the chemical details of the thermal durability, PCL was artificially aged over 25 d at 75 °C, 85 °C and 95 °C. Data from GPC analysis and rheology revealed that PCL is degrading steadily at all three temperatures. Combined with GC-MS analysis, two different mechanisms for degradation could be observed: random chain scission and unzipping. Additional GPC experiment using a mixture of PCL and a fluorescence labelled PCL showed that PCL was undergoing ester interchange reactions, which could explain its thermal stability. PLGA was established successfully as material for MEW. GPC results revealed that PLGA degraded heavily in the one-hour preheating period. To reduce the processing temperature, ATEC was blended with PLGA in three mixtures. This slowed down degradation and a processing window of 6 h could be established. Mechanical testing with fibers produced with PLGA and all three blends was performed. PLGA was very brittle, whereas the blends showed an elastic behavior. This could be explained by ester interchange reactions that formed a loosely crosslinked network with ATEC.},
  subject      = {Degradation},
  language  = {en}
}
@article{BoehmStahlhutWeichholdetal.2022,
  author    = {B{\"o}hm, Christoph and Stahlhut, Philipp and Weichhold, Jan and Hrynevich, Andrei and Teßmar, J{\"o}rg and Dalton, Paul D.},
  title     = {The Multiweek Thermal Stability of Medical-Grade Poly(ε-caprolactone) During Melt Electrowriting},
  series = {Small},
  volume    = {18},
  journal   = {Small},
  number    = {3},
  doi       = {10.1002/smll.202104193},
  url       = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-257741},
  year      = {2022},
  abstract  = {Melt electrowriting (MEW) is a high-resolution additive manufacturing technology that places unique constraints on the processing of thermally degradable polymers. With a single nozzle, MEW operates at low throughput and in this study, medical-grade poly(ε-caprolactone) (PCL) is heated for 25 d at three different temperatures (75, 85, and 95 °C), collecting daily samples. There is an initial increase in the fiber diameter and decrease in the jet speed over the first 5 d, then the MEW process remains stable for the 75 and 85 °C groups. When the collector speed is fixed to a value at least 10\% above the jet speed, the diameter remains constant for 25 d at 75 °C and only increases with time for 85 and 95 °C. Fiber fusion at increased layer height is observed for 85 and 95 °C, while the surface morphology of single fibers remain similar for all temperatures. The properties of the prints are assessed with no observable changes in the degree of crystallinity or the Young's modulus, while the yield strength decreases in later phases only for 95 °C. After the initial 5-d period, the MEW processing of PCL at 75 °C is extraordinarily stable with overall fiber diameters averaging 13.5 ± 1.0 µm over the entire 25-d period.},
  language  = {en}
}