@phdthesis{Niklaus2022, author = {Niklaus, Lukas}, title = {Electrochromic systems based on metallopolymers and metal oxides: towards neutral tint and near-infrared transmission modulation}, doi = {10.25972/OPUS-25855}, url = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-258554}, school = {Universit{\"a}t W{\"u}rzburg}, year = {2022}, abstract = {While the field of electrochromic (EC) materials and devices (ECDs) continues to advance in terms of color palette and understanding the underlying mechanism, several scientific and technological challenges need to be addressed by optimizing the materials and understanding the electrochemical interplay of these materials in full cells. The main issue here is to further improve the EC profile for color neutrality and cycling stability in order to commercialize dimmable EC products. The transparent conductive substrates used in this work (FTO and ultra-thin ITO glass) have high visible light transmittance (τv > 85\%) and low sheet resistance (< 25 Ω·sq-1). In addition, the Li+-containing gel electrolyte has sufficient ionic conductivity (2.8·10-4 S·cm-1 at 25 °C), so the investigated ECDs could achieve a fast response (required ionic conductivity is between 10-3 and 10-7 S·cm-1). This work shows that the combination of cathodically-coloring Fe-MEPE with anodically-coloring non-stoichiometric nickel oxide (Ni1-xO) electrodes (prepared by the National Institute of Chemistry in Ljubljana, Slovenia) can be used in neutral-coloring type III ECDs. The Fe-MEPE/Ni1-xO ECD with the underbalanced CE (ECD1-1, 2: 1) and the balanced configuration (ECD1-2, 1: 1) are both nearly neutrally-colored (ECD1-1: a* = -6.7, b* = 8.8; ECD1-2: a* = -9.0, b* = 10.1) in the bright state with a τv of almost 70\%. Due to the overbalancing of the CE (ECD1-3, 1:3), a deviation (a* = -2.8, b* = 19.9) from the neutral coloration occurred here. The balanced as well as the overbalanced ECD configurations show high electrochemical cycling stability (over 1,000 potentiostatic switching cycles). In general, the overbalanced configuration offers the advantage of a smaller operating voltage range (-1 V ↔ 2.5 V to -1 V ↔ 1.5 V), i.e., avoiding possible electrochemical degradation of the EC materials, electrolyte, or conductive layers. By using a Li RE in the full cell, insights into the optimal matching of electrochemical and optical properties between the two electrodes are obtained to achieve more stable ECDs. Thereby, the redox potentials of both EC electrodes (Fe-MEPE and Ni1-xO) can be measured during operation. The incomplete decolorization of ECD1-1 can be explained by the measured electrode potentials (below the required 4 V vs. Li/Li+), excluding side reactions and degradation at both electrodes. The results demonstrate the importance of using balanced and (slightly) overbalanced ECD configurations with complementary-coloring EC electrodes to achieve high cycling stability and fast switching at low operating voltages. Therefore, this three-electrode configuration provides an excellent method for in situ electrochemical characterization of the individual EC electrodes to better understand the redox processes during device operation and to further improve the optical contrast and cycle stability of ECDs. The Fe-MEPE/Ni1-xO combination was tested on flexible ultrathin ITO glass (ECD1-4). Here, by applying a low voltage of -1 V ↔ 2.5 V, the MEPE/Ni1-xO ECDs can be reversibly switched from a colored (L* = 35.6, a* = 19.4, b* = -26.7) to a nearly colorless (L* = 78.5, a* = -14.0, b* = 21.3) state. This is accompanied by a change in τv from 6\% to 53\%. The ECDs exhibit fast response and good cycling stability (5\% loss of optical contrast over 100 switching cycles). To further improve color neutrality and cycling stability, ECDs combining Fe-MEPE and mixed metal oxides as ion storage layers were investigated. Titanium manganese oxide (TMO, Fraunhofer IST) and titanium vanadium oxide (TiVOx, EControl-Glas GmbH \& Co. KG) electrodes are compared for use as optically-passive ion storage layers. TiVOx with a maximum charge density of approx. 27 mC·cm-2 and a coloration efficiency of η = 2 cm·C-1 at 584 nm shows a color change from yellow to light gray at 2 V vs. Ag/AgCl, while the slightly anodically-coloring Ti-rich TMO (10.5 mC·cm-², η584 nm = -4 cm·C-1) switches from light yellow to colorless at -2.5 V vs. Ag/AgCl. These materials show only a slight change in τv value from 85\% to 75\% and from 72\% to 81\%, respectively, thus reaching the requirements for highly transmissive optical-passive ion storage layers. The ECDs with Fe-MEPE in combination with TiVOx (ECD2-1) and TMO-1 (ECD2-2) are blue-purple in the dark state (0 V) and turn colorless by applying a voltage of 1.5 V, changing the τv value from 28\% to 69\% and from 21\% to 57\% in 3 s and 13 s, respectively. The ECDs show fast responses and high cyclability over more than 100 cycles. In the last section, the simplification of cell architecture by using redox mediators shows that different redox mediators (KHCF(III), Fc-PF6, Fc-BF4, and TMTU) can be used in type II ECDs (4 instead of 5 layers) consisting of Fe-MEPE or Ni1-xO thin film electrodes. The combination of KHCF(III) with Fe-MEPE has a low cycling stability due to the electrochemical formation of Prussian blue (PB). This side reaction is undesirable as it decreases the optical contrast. It can be avoided by using Fc+- (ECD3-5/6) or TMTU-based (ECD3-7) redox mediators, which exhibit reversible redox behavior. A high τv value of 72\% is obtained for the use of TMTU. Low concentrations (<0.1 M) of redox mediators decrease the cell voltage for complete switching without affecting the optical properties of the ECDs. The redox couple TMTU/TMFDS2+ (molar ratio of 1:0.1 in 1 M LiClO4/PC as electrolyte) works well in combination with Ni1-xO electrodes (ECD3-10), with a change in τv value from 38\% (colored at 2 V, L* = 67.1, a* = 3.9, b* = 17.2) to 70\% at (decolored at -2 V, L* = 86.6, a* = -0.6, b* = 17.2). This result implies that incorporating redox mediators into the electrolyte is an effective means to simplify the cell assembly and color neutrality can be obtained with one optically active WE and a color-neutral redox mediator. Moreover, the combination of Ni1-xO and the colorless TMTU/TMFDS2+ redox mediator is a potential candidate to obtain neutrally colored ECDs. It is shown that the lab-sized FTO- and ultra-thin ITO-glass-based ECDs are very attractive for energy-efficient EC applications, e.g., in architectural or automotive glazing, aircraft, ships, home appliances and displays. To monitor the EC performance and to prevent diverging electrode potentials during the switching process, the studied three-electrode configuration can help to extend the cycle stability as well as to improve the charge balancing of dimmable applications. The studied ECDs display a route towards neutral tint, e.g., EC active Ni1-xO, optically-inactive mixed metal oxides, and colorless redox mediators. Nevertheless, color neutrality should be further improved to meet the requirements for industrial applications. For future work, a scale-up process from lab-sized (few cm²) to prototype (few m²) ECDs will be necessary.}, subject = {Elektrochromie}, language = {en} }