@phdthesis{MeiningergebChrist2018,
  author    = {Meininger [geb. Christ], Susanne},
  title     = {Processing of calcium and magnesium phosphate cements for bone substitution},
  url       = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-169126},
  school      = {Universit{\"a}t W{\"u}rzburg},
  year      = {2018},
  abstract  = {The main focus of this thesis was the processing of different calcium and magnesium phosphate cements together with an optimization of mechanical and biological properties. Therefore, different manufacturing techniques like 3D powder printing and centrifugally casting were employed for the fabrication of reinforced or biomedically improved implants. One of the main problems during 3D powder printing is the low green strength of many materials, especially when they are only physically bonded and do not undergo a setting reaction. Such materials need post-treatments like sintering to exhibit their full mechanical performance. However, the green bodies have to be removed from the printer requiring a certain stability. With the help of fiber reinforcement, the green strength of printed gypsum samples could be increased by the addition of polymeric and glass fibers within the printing process. The results showed that fiber reinforcement during 3D powder printing is possible and opens up diverse opportunities to enhance the damage tolerance of green bodies as well as directly printed samples. The transfer to biomedically relevant materials like calcium and magnesium phosphate cements and biocompatible fibers would be the next step towards reinforced patient-specific implants. In a second approach, centrifugally casting derived from construction industries was established for the fabrication of hollow bioceramic cylinders. The aim was the replacement of the diaphysis of long bones, which exhibit a tubular structure with a high density of cortical bone on the fringe. By centrifugation, cement slurries with and without additives could be fabricated to tubes. As a first establishment, the processing parameters regarding the material (e.g. cement composition) as well as the set-up (e.g. rotation times) had to be optimized for each system. In respect of mechanics, such tubes can keep up with 3D powder printed tubes, although the mechanical performance of 3D printed tubes is strongly dependent on printing directions. Additionally, some material compositions like dual setting systems cannot be fabricated by 3D powder printing. Therefore, a transfer of such techniques to centrifugally casting enabled the fabrication of tubular structures with an extremely high damage tolerance due to high deformation ability. A similar effect was achieved by fiber (mesh) addition, as already shown for 3D powder printing. Another possibility of centrifugally casting is the combination of different materials resulting in graded structures to adjust implant degradation or bone formation. This became especially apparent for the incorporation of the antibiotic vancomycin, which is used for the treatment of bacterial implant infections. A long-term release could be achieved by the entrapment of the drug between magnesium phosphate cement layers. Therefore, the release of the drug could be regulated by the degradation of the outer shell, which supports the release into an acidic bacterial environment. The centrifugally casting technique exhibited to be a versatile tool for numerous materials and applications including the fabrication of non-centrosymmetric patient-specific implants for the reconstruction of human long bones. The third project aimed to manufacture strontium-substituted magnesium phosphate implants with improved biological behavior by 3D powder printing. As the promoting effect of strontium on bone formation and the inhibitory impact on bone resorption is already well investigated, the incorporation of strontium into a degradable magnesium phosphate cement promised a fast integration and replacement of the implant. Porous structures were obtained with a high pore interconnectivity that is favorable for cell invasion and bone ingrowth. Despite the porosity, the mechanical performance was comparable to pure magnesium phosphate cement with a high reliability of the printed samples as quantitatively determined by Weibull statistics. However, the biological testing was impeded by the high degradation rate and the relating ion release. The high release of phosphate ions into surrounding media and the detachment of cement particles from the surface inhibited osteoblast growth and activity. To distinguish those two effects, a direct and indirect cell seeding is always required for degradable materials. Furthermore, the high phosphate release compared to the strontium release has to be managed during degradation such that the adverse effect of phosphate ions does not overwhelm the bone promoting effect of the strontium ions. The manufacturing techniques presented in this thesis together with the material property improvement offer a diverse tool box for the fabrication of patient-specific implants. This includes not just the individual implant shape but also the application like bone growth promotion, damage tolerance and local drug delivery. Therefore, this can act as the basis for further research on specific medical indications.},
  subject      = {Calciumphosphate},
  language  = {en}
}
@phdthesis{Roedel2019,
  author    = {R{\"o}del, Michaela},
  title     = {Development of Dual Setting Cement Systems as Composite Biomaterials with Ductile Properties},
  doi       = {10.25972/OPUS-18277},
  url       = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-182776},
  school      = {Universit{\"a}t W{\"u}rzburg},
  year      = {2019},
  abstract  = {Synthetic bone replacement materials have their application in non-load bearing defects with the function of (re-)construction or substitution of bone. This tissue itself represents a biological composite material based on mineralized collagen fibrils and combines the mechanical strength of the mineral with the ductility of the organic matrix. By mimicking these outstanding properties with polymer-cement-composites, an imitation of bone is feasible. A promising approach for such replacement materials are dual setting systems, which are generated by dissolution-precipitation reaction with cement setting in parallel to polymerization and gelation of the organic phase forming a coherent hydrogel network. Hereby, the high brittleness of the pure inorganic network was shifted to a more ductile and elastic behavior. The aim of this thesis was focused on the development of different dual setting systems to modify pure calcium phosphate cements' (CPCs') mechanical performance by incorporation of a hydrogel matrix. A dual setting system based on hydroxyapatite (HA) and cross-linked 2-hydroxyethyl methacrylate (HEMA) via radical polymerization was advanced by homogenous incorporation of a degradable cross-linker composed of poly(ethylene glycol) (PEG) as well as poly(lactic acid) (PLA) with reactive terminal methacrylate functionalities (PEG-PLLA-DMA). By integration of this high molecular weight structure in the HEMA-hydrogel network, a significant increase in energy absorption (toughness) under 4-point bending testing was observed. An addition of only 10 wt\% hydrogel precursor (referred to the liquid phase) resulted in a duplication of stress over a period of 8 days. Additionally, the calculated elasticity was positively affected and up to six times higher compared to pure HA. With a constantly applied force during compressive strength testing, a deformation and thus strain levels of about 10 \% were reached immediately after preparation. For higher degradability, the system was modified in a second approach regarding organic as well as inorganic phase. The latter component was changed by brushite forming cement that is resorbable in vivo due to solubility processes. This CPC was combined with a hydrogel based on PEG-PLLA-DMA and other dimethacrylated PEGs with different molecular weights and concentrations. Hereby, new reaction conditions were created including a shift to acidic conditions. On this ground, the challenge was to find a new radical initiator system. Suitable candidates were ascorbic acid and hydrogen peroxide. that started the polymerization and successful gelation in this environment. These highly flexible dual set composites showed a very high ductility with an overall low strength compared to HA-based models. After removal of the applied force during compressive strength testing, a complete shape recovery was observed for the samples containing the highest polymeric amount (50 wt\%) of PEG-PLLA-DMA. Regarding phase distribution in the constructs, a homogenously incorporated hydrogel network was demonstrated in a decalcifying study with ethylenediaminetetraacetic acid. Intact, coherent hydrogels remained after dissolution of the inorganic phase via calcium ion complexation. In a third approach, the synthetic hydrogel matrix of the previously described system was replaced by the natural biopolymer gelatin. Simultaneously to brushite formation, physical as well as chemical cross-linking by the compound genipin was performed in the dual setting materials. Thanks to the incorporation of gelatin, elasticity increased significantly, in which concentrations up to 10.0 w/v\% resulted in a certain cohesion of samples after compressive strength testing. They did not dissociate in little pieces but remained intact cuboid specimens though having cracks or fissures. Furthermore, the drug release of two active pharmaceutical ingredients (vancomycin and rifampicin) was investigated over a time frame of 5 weeks. The release exponent was determined according to Korsmeyer-Peppas with n = 0.5 which corresponds to the drug liberation model of Higuchi. A sustained release was observed for the antibiotic vancomycin encapsulated in composites with a gelatin concentration of 10.0 w/v\% and a powder-to-liquid ratio of 2.5 g/mL. With respect to these developments of different dual setting systems, three novel approaches were successfully established by polymerization of monomers and cross-linking of precursors forming an incorporated, homogenous hydrogel matrix in a calcium phosphate network. All studies showed an essential transfer of mechanical performance in direction of flexibility and bendability.},
  subject      = {Calciumphosphate},
  language  = {en}
}
@phdthesis{Spatz2013,
  author    = {Spatz, Kerstin},
  title     = {Mechanische und rheologische Eigenschaften von Calciumphosphat-Zementen},
  url       = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-124860},
  school      = {Universit{\"a}t W{\"u}rzburg},
  year      = {2013},
  abstract  = {Zur Erh{\"o}hung der mechanischen Stabilit{\"a}t mineralischer Knochenzemente aus Calciumorthophosphaten (CPC) wurde in einem TTCP/DCPA-System das Zementedukt TTCP mit verschiedenen biokompatiblen Oxiden (SiO2, TiO2, ZrO2) w{\"a}hrend des Herstellungsprozesses dotiert. Dies f{\"u}hrte zur Bildung von Calciummetallaten und einer Herabsetzung der L{\"o}slichkeit der TTCP-Komponente des Zements. Gegen{\"u}ber einem oxidfreien Zement konnte die Druckfestigkeit von 65 MPa auf 80 MPa (SiO2) bzw. 100 MPa (TiO2) gesteigert werden. In einem zweiten Ansatz zur Verbesserung der Injizierbarkeit wurden die Wechselwirkungen der Partikeloberfl{\"a}chen mit der fl{\"u}ssigen Zementphase betrachtet. Durch biokompatible Additive sollte eine repulsive elektrostatische Wechselwirkung eingestellt werden, um Partikelagglomerate effektiv zu dispergieren und eine verfl{\"u}ssigende Wirkung zu erreichen. Die Injizierbarkeit eines TTCP/DCPA-Zements durch eine Kan{\"u}le mit 800 µm Durchmesser konnte durch die Verwendung von 500 mM tri-Natriumzitrat-L{\"o}sung aufgrund einer deutlichen Herabsetzung der Viskosit{\"a}t der Zementpaste signifikant gesteigert werden (>95\%, P/L 3,3/1, Kraftaufwand 20 N). Abschließend wurde der Einfluss der Partikelgr{\"o}ßenverteilung auf die Festigkeit und Injizierbarkeit einer auf monomodaler Partikelgr{\"o}ßenverteilung basierten Zementmatrix untersucht. Hierzu wurden einem mechanisch aktivierten a-TCP-System unreaktive, feink{\"o}rnige F{\"u}llstoffpopulationen (TiO2, CaHPO4, CaCO3) zugesetzt und systematisch deren Effekt in Verbindung mit einer Partikelaufladung durch tri-Natriumzitrat auf die rheologischen und mechanischen Eigenschaften untersucht. Erst die Kombination einer bimodalen Partikelgr{\"o}ßenverteilung mit tri-Natriumzitrat-L{\"o}sung f{\"u}hrte zu einer starken Erniedrigung der Viskosit{\"a}t, damit zur nahezu vollst{\"a}ndigen Injizierbarkeit der Zemente und einer teilweise signifikanten Steigerung der mechanischen Festigkeiten (z.B. 72 MPa reiner a-TCP-Zement auf 142 MPa mit Zusatz von CaHPO4).},
  subject      = {Biomaterial},
  language  = {de}
}
@phdthesis{SchamelgebGeffers2017,
  author    = {Schamel [geb. Geffers], Martha},
  title     = {Novel dual setting approaches for mechanically reinforced mineral biocements},
  url       = {http://nbn-resolving.de/urn:nbn:de:bvb:20-opus-154946},
  school      = {Universit{\"a}t W{\"u}rzburg},
  year      = {2017},
  abstract  = {Calcium phosphate biocements are inherently brittle materials due to their ceramic nature. Hence, currently applied cement formulations are only indicated for non-load bearing application sites. An approach to reduce cement brittleness is based on the use of cement - polymer composites, which combine the flexibility of a polymeric phase with the hardness and compression strength of a cement matrix. Here, a relatively new strategy is the use of "dual-setting" cements, in which the polymeric phase is simultaneously build up from monomers or prepolymers during cement setting. This approach largely maintains basic properties of the fresh paste such as rheology or setting time. Previous works on such dual setting cements were dealing with a radical polymerization reaction to create the polymeric network. This type of reaction requires the addition of a suitable initiator system (e.g. a tertiary amine in conjunction with ammonium peroxosulfate), which are often cytotoxic and may interfere with the cement setting conditions. The current thesis dealt with alternative strategies, in which the cross-linking and gelation of the second (polymeric or inorganic) cement phase is initiated by the chemical conditions of the setting reaction such that no additional initiator has to be added to the cement paste. In a first approach a six armed star molecule functionalized with isocyanate groups as reactive termini (NCO-sP(EO-stat-PO)) was used to build up a hydrogel matrix, which was then subsequently mineralized with hydroxyapatite nanocrystals following the hydrolysis of incorporated -tricalcium phosphate particles. The stimulus to initiate hydrogel cross-linking are water molecules, which subsequently hydrolyzed isocyanate groups to amines, which then cross-linked with unreacted isocyanate to form urea-bonds. Here, it was possible to show the advantages features of a dual setting system in comparison to the simple combination of hydrogels with unreactive filler particles. By the formation of the cement matrix within the hydrogel a strength improvement by the factor of 30 could be observed. Furthermore, by applying a dual setting system higher mineral concentrations are realizable. The mechanical properties such as elasticity, compression strength and E-modulus of a composite with 30 wt\% NCO-sP(EO-stat-PO) were found to be similar to the properties of cancellous bone. With the motivation to develop a dual setting and resorbable cement, a brushite (CaHPO4·2H2O) forming cement was modified with a second inorganic silica based precursor. The latter was obtained by pre-hydrolysing tetraethyl orthosilicate (TEOS) under acidic conditions. This silica precursor was mixed with a cement powder composed of ß-tricalcium phosphate and monocalcium phosphate, whereas cement setting occurred by a dissolution-precipitation process to form a matrix of brushite. Simultaneously, the increase of the pH during setting from initially 1-2 to values > 4 initiated the condensation reaction of the hydrolysed TEOS. This resulted in an interpenetrating phase composite material in which the micropores of the cement were filled with the nanoporous silica gel. This resulted in a higher density and a compressive strength of 24 MPa, which is approximately 5-10 times higher than the CPC reference at the same powder to liquid ratio. The microporous character of the composites also altered the release of vancomycin as a model drug, whereby in contrast to the quantitative release from the CPC reference, approx. 25 \% of the immobilised drug remained in the composite matrix. It was also observed, that a variation of the TEOS content in the composite enabled a control over cement phase composition to form either brushite, anhydrous monetite or a biphasic mixture of both. Cytocompatibility tests revealed that composites with the highest silicate content showed an increased cell proliferation compared to the silica-free brushite reference. Proliferation was found to be similar to a hydroxyapatite reference with a significant higher activity per cell. Mechanistically, the improved biological response could not be attributed to the released silicate ions, but to a decreased release of phosphate and adsorption of magnesium ions from the cell culture medium. Finally, an investigated dual setting cement system was based on the combination of a brushite forming cement powder with an aqueous silk fibroin solution. Here, changes of both ion concentration and pH during cement setting were shown to build up an interpenetrating fibroin - brushite composite with combined properties of the elastic polymer and the rigid cement. Mechanistically, the low pH of the cement paste (2) as well as the free Ca2+ ions during setting resulted in a conformation change of the dissolved fibroin from random coil to ß-sheet structure. This leads to a rapid gelation and contraction of the fibroin phase with a self-densifying effect on the cement paste. The set composites showed typical ductile fracture behavior under dry testing conditions and a high elasticity under wet conditions with a mechanical strength nearly an order of magnitude higher than the fibroin free cement reference. Cell number and activity against MG63 cells were strongly increased on silk fibroin cement composite surfaces at later time points, which could be again attributed to a decreased ion release and adsorption compared to the fibroin free cements. This in turn slowed down the in vitro degradation of the CPC phase in such composites.},
  subject      = {Calciumphosphate},
  language  = {en}
}