TY  - THES
A1  - Götzendörfer, Stefan
T1  - Synthesis of Copper-Based Transparent Conductive Oxides with Delafossite Structure via Sol-Gel Processing
T1  - Synthese von Kupfer-basierten transparenten leitfähigen Oxiden mit Delafossit-Struktur über das Sol-Gel-Verfahren
N2  - Starting off with solubility experiments of possible precursors, the present study reveals the whole development of a sol gel processing route for transparent p type semiconductive thin films with delafossite structure right to the fabrication of functional p-n junctions. The versatile sol formulation could successfully be modified for several oxide compositions, enabling the synthesis of CuAlO2, CuCrO2, CuMnO2, CuFeO2 and more. Although several differences in the sintering behaviour of powders and thin films could be observed, the powder experiments significantly contributed to the clearification of the intricate phase development during thermal annealing and also to optimization of the annealing sequence for thin film processing. Two different ternary systems turned out to be the most promising candidates for p-TCO application: Copper aluminum oxide for its high optical transmittance and copper chromium oxide for its low synthesis temperature, which allowed thin film deposition on low-cost borosilicate substrates. In order to combine the advantages of these two systems, the quaternary oxide composition CuAl1-xCrxO2 was investigated. With a higher optical transmittance than CuCrO2, a lower synthesis temperature than CuAlO2 and a lower resistivity than both parent systems, the optimum composition of the quaternary oxide is reached for x = 0.50. Compared to physical vapour deposition techniques, the undoped thin films presented here still need to make up some deficites in their optoelectronic performance. Although the best sol-gel samples are able to compete with RF sputtered samples or sampes deposited by PLD in transmittance, their resistivity is almost two orders of magnitude higher. The most probable reasons for this are the characteristic imperfections of sol-gel thin films like porosity and small crystallite size, which create barriers like grain boundaries and bottlenecks like barely connected particles. By additional effort such shortcomings can be repelled to a certain extend, but nevertheless the density of undoped sol-gel material always stays behind its pendants processed by physical vapour deposition.[246] Furthermore, such additional endeavour is likely to annihilate the advantage of sol-gel technique in processing costs. Extrinsic doping is a common method to decrease the resistivity of delafossite materials. Partially replacing the trivalent cations by divalent ones creates additional holes and thus generates additional charge carriers for p-type semiconductivity. This can improve the conductivity of delafossites by up to three orders of magnitude. Due to the compositorial flexibility of sol-gel processing, dopants could be introduced easily in this study by soluble precursors. However, improving the conductivity of CuAlO2 and CuAl0.5Cr0.5O2 via this method failed. Actually, this seems to be due to the fact that instead of being incorporated into the delafossite phase the dopant ions form intransparent phase impurities like spinels, which interfere with optical transmittance of the thin films. On the contrary, doping had a positive effect on the conductivity and the optical transmittance of copper chromium oxide, with magnesium being the most effective dopant. The resistivity could be decreased by more than three orders of magnitude, but in order to achieve this, much higher Mg concentrations than by other thin film deposition methods were necessary. This indicates a low doping efficiency in sol gel processed thin films, but also the ability of sol gel processing to incorporate more magnesium into the oxide than any other processing method. The extensive substitution of the chromium ions also increases the optical transmittance and allows sol gel processed thin films to draw level with thin films deposited by sputtering methods or PLD. Finally, the applicability of the delafossite thin films was proven by the asymmetric current voltage characteristics of heterojunctions between ITO and the delafossites. Shunting problems of the metallic contacts, on the other hand, reveal structural deficites of the delafossites, which should be the subject of further investigations.
N2  - Ausgehend von Versuchen zur Löslichkeit möglicher Ausgangsstoffe zeigt die vorliegende Studie die komplette Entwicklung einer Sol-Gel-Route für die Synthese transparenter p-halbleitfähiger Dünnschichten mit Delafossitstruktur bis hin zur Herstellung funktionstüchtiger p-n-Übergänge. Die vielseitige Solrezeptur konnte erfolgreich für mehrere Oxidzusammensetzungen abgewandelt werden, was die Synthese von CuAlO2, CuCrO2, CuMnO2, CuFeO2 und weiteren Mischoxiden ermöglichte. Obwohl einige Unterschiede im Sinterverhalten von Pulvern und Dünnschichten beobachtet werden konnten, trugen die Pulverversuche erheblich zur Aufklärung der komplizierten Phasenentwicklung während der thermischen Behandlung und auch zur Optimierung der Kalzinierungsschritte bei der Dünnschichtherstellung bei. Zwei der ternären Oxide erwiesen sich als die vielversprechendsten Kandidaten für die Anwendung als p-halbleitfähiges transparentes Oxid: Kupfer-Aluminium-Oxid aufgrund seiner hohen optischen Transparenz und Kupfer-Chrom-Oxid aufgrund seiner niedrigen Synthesetemperatur, die die Abscheidung von Dünnschichten auf kostengünstigen Borosilicatglas-Substraten ermöglicht. Um die Vorteile dieser beiden Systeme zu vereinen, wurde die quaternäre Oxidzusammensetzung CuAl1-xCrxO2 untersucht. Mit einer höheren optischen Transmission als CuCrO2, einer niedrigeren Synthesetemperatur als CuAlO2 und einem geringeren spezifischen Widerstand als die beiden Muttersysteme wird die optimale Zusammensetzung dieses quaternären Oxids bei x = 0,50 erreicht. Im Vergleich zu Methoden der physikalischen Gasphasenabscheidung müssen die hier vorgestellten undotierten Dünnschichten noch einige Defizite bei ihren optoelektronischen Eigenschaften aufholen. Obschon die besten Sol-Gel-Proben in puncto Transparenz mit Proben, die über Radiofrequenz-Kathodenzerstäubung oder Laserstrahlverdampfen hergestellt wurden, mithalten können, liegt ihr spezifischer Widerstand um zwei Größenordnungen höher. Die wahrscheinlichste Ursache hierfür sind die charakteristischen Unvollkommenheiten von Sol-Gel-Dünnschichten wie Porosität und geringe Kristallitgröße, die den Stromfluss durch Hindernisse wie Korngrenzen und Engpässe wie schlecht verknüpfte Partikel behindern. Durch zusätzlichen Aufwand können derartige Unzulänglichkeiten in gewissem Maße zurückgedrängt werden, doch nichtsdestotrotz liegt die Dichte von undotiertem Sol-Gel-Material immer unter der von vergleichbaren Proben, die über physikalische Gasphasenabscheidung hergestellt wurden.[246] Zudem ist es wahrscheinlich, dass solche zusätzlichen Anstrengungen die Vorteile des Sol-Gel-Verfahrens bei den Herstellungskosten zunichte machen. Extrinsische Dotierung ist ein gängiger Weg, um den spezifischen Widerstand von Delafossit-Materialien abzusenken. Teilweiser Austausch der dreiwertigen Kationen durch zweiwertige erzeugt zusätzliche Löcher und stellt so zusätzliche Ladungsträger für die p-Halbleitung bereit. Dies kann die Leitfähigkeit von Delafossiten um bis zu drei Größenordnungen erhöhen. Dank der stofflichen Flexibilität des Sol-Gel-Verfahrens konnten in dieser Studie Dotanden sehr leicht in Form von löslichen Vorstufen eingebracht werden. Jedoch scheiterten die Versuche, die Leitfähigkeit von CuAlO2 und CuAl0,5Cr0,5O2 auf diesem Wege zu verbessern. Dies scheint darauf zurückzuführen zu sein, dass die Dotanden nicht in die Delafossitphase eingebaut werden, sondern intransparente Fremdphasen wie Spinelle bilden, die die optische Transmission der Dünnschichten beeinträchtigen. Im Gegensatz dazu wirkte sich die Dotierung positiv auf die Leitfähigkeit und die optische Transmission von Kupfer-Chrom-Oxid aus, wobei Magnesium als Dotant die besten Resultate lieferte. Der spezifische Widerstand konnte so um mehr als drei Größenordnungen verringert werden, doch wurden hierfür deutlich höhere Magnesiumkonzentrationen benötigt als bei anderen Beschichtungsverfahren. Einerseits weist dies auf eine geringe Dotiereffizienz in den über das Sol-Gel-Verfahren hergestellten Proben hin, andererseits zeigt dies aber auch, dass über das Sol-Gel-Verfahren wesentlich mehr Magnesium in die Oxidschichten eingebracht werden kann als über jedes andere Verfahren. Der beträchtliche Ersatz der Chromionen erhöht auch die optische Transmission und ermöglicht es den Sol-Gel-Proben, zu den Dünnschichten aufzuschließen, die durch Kathodenzerstäuben oder Laserstrahlverdampfen hergestellt wurden. Schließlich wurde das Anwendungspotential der Delafossit-Dünnschichten durch die asymmetrischen Strom-Spannungs-Kennlinien von p-n-Übergängen zwischen Delafossit und Indium-Zinn-Oxid belegt. Andererseits machen die Kurzschlussprobleme bei der metallischen Kontaktierung die strukturellen Defizite der Delafossite deutlich. Dies sollte zum Gegenstand weiterführender Untersuchungen werden.
KW  - Transparent-leitendes Oxid
KW  - p-Halbleiter
KW  - Sol-Gel-Verfahren
KW  - Beschichtung
KW  - pn-Übergang
KW  - Delafossit
KW  - Kupfer-Chrom-Oxid
KW  - Kupfer-Aluminium-Oxid
KW  - Delafossite
KW  - Copper-Chromium-Oxide
KW  - Copper-Aluminum-Oxide
Y1  - 2010
U6  - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-51601
ER  - 
TY  - THES
A1  - Declerck, Pélagie
T1  - Synthesis and technological processing of hybrid organic-inorganic materials for photonic applications
T1  - Synthese und technische Prozesse von organisch-anorganischen Hybridmaterialien für photonische Anwendungen
N2  - Im Rahmen dieser Doktorarbeit wurden neue UV-strukturierbare organisch-anorganische hybride Polymere für photonische Anwendungen mit einem hohem Brechungsindex und der Möglichkeit, sie durch Ein- bzw. Zwei-Photonen-Polymerisation zu strukturieren, entwickelt. Die Materialien wurden in Bezug auf ihre chemische Struktur, ihre optischen Eigenschaften, und ihrer Fähigkeit, durch 1PP und 2PP strukturierbar zu sein, untersucht. Besonders mit 2PP konnte man mit diesen neuartigen hybriden Materialien 3D-Strukturen erzeugen. ie Hydrolyse und Polykondensationsreaktionen wurden mit · Organo-Alkoxysilanen und Titanalkoxiden, modifiziert mit und ohne komplexierende Liganden und · Organo-Alkoxysilanen, Titanalkoxiden und Organophosphorsäure als Precrusoren durchgeführt. Primäres Ziel dieser Arbeit war es, den Brechungsindex von ORMOCER®en, die auf der Basis von Organo-Alkoxysilan-Precursoren ohne Heteroelemente synthetisiert werden, zu vergrößern. Die chemische Struktur der synthetisierten Materialien und somit mit ihr die Parameter, die den Brechungsindex beeinflussen, wurden eingehend untersucht. Insbesondere die Synthese-Parameter, wie das Einsetzen der Titanalkoxide und ihrer Konzentration, der Organo-Alkoxysilane, die Katalysator-Konzentration, die verwendeten Lösungsmittel und auch die Verfahrensparameter für eine spätere Strukturierung durch lithographische Verfahren, wie die UV-Bestrahlungsdosis, die Initiator-Konzentration und der Entwickler, wurden untersucht.
N2  - In the framework of this thesis, new UV-patternable organic-inorganic hybrid polymers with higher refractive indices than reported in the literature for photonic applications were developed and studied with respect to their chemical structure, their optical properties, and their ability of being patterned by 1PP and 2PP. Particularly with 2PP, one could create 3D structures using the novel hybrid materials. The materials were prepared from hydrolysis and polycondensation reactions of · organo-alkoxysilanes and titanium alkoxide precursors, modified with and without CL and organo-alkoxysilanes precursors, and · organo-alkoxysilanes, titanium alkoxide and organophosphorus precursors. The major scope of this work was to increase the refractive index of ORMCER® materials based on only organo-alkoxysilanes. Thus, the parameters which influence the refractive index were investigated thoroughly. In particular, the synthesis parameters such as the introduction of titanium alkoxide and its concentration, the organo-alkoxysilanes, the catalyst concentration, the solvent used, but, also the processing parameters such as, the UV exposure dose, initiator concentration, and developer were investigated.
KW  - Brechzahl
KW  - Ormocer
KW  - Photonischer Kristall
KW  - Sol-Gel-Verfahren
KW  - Photolithographie
KW  - Titan
KW  - refractive index
KW  - Ormocer
KW  - sol-gel
KW  - photonic crystal
Y1  - 2010
U6  - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-56053
ER  - 
TY  - THES
A1  - Bockmeyer, Matthias
T1  - Structure and Densification of Thin Films Prepared From Soluble Precursor Powders by Sol-Gel Processing
T1  - Struktur und Verdichtung von dünnen Schichten hergestellt über das Sol-Gel Verfahren unter Verwendung löslicher Vorstufenpulver
N2  - The main focus of this work was to get a deeper understanding of the relationship between the structure of sol-gel films, their densification and their macroscopic cracking. First of all titania was chosen as model system. Therefore a synthesis route starting from the preparation of long-term stable amorphous redissoluble precursor powders based on acetylacetone as chelate ligand was utilized. The solubility and stability of the powders in various solvents can be determined by chemical synthesis and technological parameters. When dissolved in a solvent mixture of ethanol and 1,5-pentanediol, thin films can be easily prepared by dip-coating technique. Thereby the quality of the titania films enormously depends on the calcinations temperature and the solvent mixture is used. In order to investigate the influence of different solvents and solvent mixtures on the microstructure and densification of the precursors, the coating solutions were stripped off (sol powder) and analyzed as function of annealing temperature. It was pointed out that a high densification rate caused by the addition of 1,5-pentanediol, results in dense microstructure with trapped residual carbon. These impurities can retard the phase transformation of anatase to rutile. The analysis of so-called “film powders” scraped off multiple dip-coated substrates provides valuable information on the effect of air moisture and unidirectional densification during drying and aging on the structure of thin films. The high surface-to-volume ratio and access to air moisture determine the chemical composition of the as-prepared film, which controls shrinkage, crystallization and defect structure of the coatings. Further it was shown, that drying as a thin film results in the formation of closed pores and much denser microstructure than the respective sol powder. Without the addition of 1,5-pentanediol all –OEt moieties undergo hydrolysis reactions, which causes the formation of a rigid network. The presence of 1,5-pentanediol retards this hydrolysis reactions and provides some network plasticity. Generally the microstructure of thin films is comparatively close to the microstructure of the film powders. The addition of 1,5-pentandiol prevents hydrolysis and condensation reactions as like in the film powders. However even at 700 °C, thin films never transform to rutile, which was attributed to the tensile stresses in thin films. In thin films and in film powders as well a comparable amount of closed pores are formed during annealing. Further it was shown that most of the thin sol-gel films investigated form a dense crust on their tops during annealing. This explains why crack free films exhibit only closed pores. However, when cracks appear during thin film shrinkage in the coating, this crust is burst, which generates open porosity. The defect density in the coatings was determined by an automated analysis of surface images. The crack formation and quantity can be directly referred to tensile stresses in the coatings, which arise from hydrolysis and condensation during thin film drying and aging. Therefore when 1,5-pentanediol is added to the sol, thin film cracking was avoided, because hydrolysis and condensation reactions are retarded, which preserves a higher network flexibility. Furthermore the crack formation was significantly influenced by the atmospheric humidity that was used during the coating process, which was explained by different drying and condensation rates. Under certain chemical starting conditions water soluble precursor powders can be also obtained. In general the observations made with the water based coating solutions are mostly in agreement with the former results based on ethanol based coating solutions. For example the high surface-to-volume ratio of film powders compared to sol powders also significantly enhances film drying and densification. The addition of 1,5-pentanediol also clearly contributes to their densification behavior and phase evolution. As seen before in the case of ethanol based coatings, 1,5-pentanediol enhances the stability towards hydrolysis and condensation reactions and preserves some network plasticity. Therefore coatings prepared without the addition of 1,5-pentanediol already form cracks during film drying and aging because of tensile stresses. Thus, the addition of 1,5-pentanediol results in a reduction/prevention of crack formation. Nevertheless some differences were observed, i.e. the critical single coating film thickness of ethanol based coatings is nearly twice that of water based coatings. This was explained by the different surface tensions of the basis solvents, which during thin film drying causes significantly higher capillary forces and tensile stresses in water based coatings. When acetylacetone is replaced by triethanolamine as chelating ligand for titanium also re-dissolvable precursor powders can be synthesized. The film powders combine a high hydrolytic stability of the precursor with sufficient intermediate network flexibility. The different type of organics changes the drying and densification behavior: i.e. in contrast to film powders obtained from acetylacetone based precursor powders the structure of triethanolamine based film powders is unaffected by the thin film drying process. This high hydrolytic stability and plasticity of this precursor allows the preparation of defect free coatings up to single film thickness of 300 nm. However triethanolamine based thin films present at intermediary annealing temperatures a distinctively different microstructure compared to acetylacetone based films. The general validity of the conclusions was proved on the basis of zirconia coatings that were also prepared by the use of re-dissolvable precursor powders. In principle all conclusions concerning the interconnection of precursor chemistry, film formation, densification and structure were transferable to the respective zirconia coatings. Differences mainly arise only from differential material properties i.e. bulk density. Finally, it has been pointed out that the findings obtained on the densification behavior of thinsol-gel films are also a valuable tool for improved explanations of other important scientific questions concerning sol-gel films, i.e. scratch resistance of sol-gel coatings, fiber -bridging and – degradation of sol-gel coated fibers.
N2  - Grundsätzlich war es Ziel der vorliegenden Arbeit, die Zusammenhänge zwischen Struktur von Sol-Gel Schichten, ihrer Verdichtung und der Entstehung von makroskopischen Rissen besser verstehen zu können. Als Modelsystem wurde hierfür Titanoxid ausgewählt. Hierzu wurde von einer Syntheseroute basierend auf der Verwendung von langzeitstabilen amorphenre-dispergierbaren Vorstufenpulvern mit Acetylaceton als Chelatligand ausgegangen. Die Löslichkeit und Stabilität der Pulver in verschiedenen Lösungsmitteln lässt sich über die chemische Synthese bzw. technologischen Parameter einstellen. Wenn die Pulver in einem Lösungsmittelgemisch aus Ethanol und 1,5-Pentandiol gelöst werden, lassen sich mittels Tauchbeschichtungsverfahren einfach dünne Schichten herstellen. Die Qualität der Titanoxidschichten hängt dabei entscheidend von der verwendeten Pyrolysetemperatur und der Menge an verwendetem 1,5- Pentandiol ab. Um den Einfluss von verschiedenen Lösungsmitteln und Lösungsmittelgemischen auf die Mikrostruktur und Verdichtung der Vorstufen zu untersuchen, wurden die Sole am Rotationsverdampfer eingeengt (Sol-Pulver) und in Abhängigkeit von der Behandlungstemperatur analysiert. Dabei stellte sich heraus, dass eine hohe Verdichtungsrate verursacht durch den Zusatz von 1,5-Pentandiol, in einer dichten Mikrostruktur mit eingeschlossenem Rest-Kohlenstoff resultiert. Diese Kohlenstoff-Rückstände können die Phasenumwandlung von Anatas zu Rutil hemmen. Die Analyse der so genannten „Film-Pulver“, welche von mehrfach tauchbeschichteten Substraten abgekratzt worden sind, ermöglicht den Zugang zu entscheidenden Informationen über den Einfluss der Luftfeuchtigkeit und der unidirektionalen Verdichtung, während der Film-Trocknung und –Alterung, auf die Struktur der dünnen Schichten. Es zeigte sich, dass das große Oberfläche zu Volumen Verhältnis und der Kontakt mit Luftfeuchtigkeit die chemische Zusammensetzung der frisch hergestellten Schichten bestimmen. Diese wiederum steuert die Schichtschrumpfung, Kristallisation und Defektstruktur der Schichten. Ferner konnte dargestellt werden, dass die Trocknung als dünner Film zu der Entstehung von geschlossenen Poren und zu einer deutlich dichteren Mikrostruktur als die der entsprechenden Sol-Pulver führt. Ohne den Zusatz an 1,5-Pentandiol kommt es zur Hydrolyse der –OEt Gruppen, was die Bildung eines rigiden Netzwerks bewirkt. 1,5-Pentandiol als Zusatz hemmt diese Hydrolysereaktionen und bedingt damit eine gewisse Plastizität des Netzwerkes. Im Großen und Ganzen ist die Mikrostruktur der dünnen Schichten mit der Struktur der Film-Pulver gut vergleichbar. Durch den Zusatz an 1,5-Pentandiol werden in den Schichten die Hydrolyse und Kondensationsreaktionen ebenso gehemmt wie in den entsprechenden Film-Pulvern. Allerdings bei den dünnen Schichten ist auch bei 700 °C keine Phasenumwandlung zu beobachten, was auf Zugspannung in den dünnen Filmen zurückzuführen ist. Während der Calcinierung kommt es sowohl in dünne Schichten wie als auch in den Film-Pulvern zur Ausbildung von geschlossenen Poren. Ferner wurde gezeigt, dass die meisten untersuchten dünnen Schichten während der Pyrolyse auf ihrer Oberfläche eine dichte Kruste ausbilden. Dies erklärt warum rissfreie Schichten nur geschlossene Poren aufweisen. Allerdings wenn Risse während der Schichtschrumpfung in der Schicht auftreten, wird diese Kruste durchbrochen, was zur Bildung von offener Porosität führt. Die Defektdichte in den Schichten wurde mittels einer automatisierten Bildanalyse der Oberfläche bestimmt. Die Riss-Bildung und Riss-Häufigkeit kann dabei direkt mit der Entstehung von Zugspannung, durch Hydrolyse und Kondensation während der Schicht-Trocknung und –Alterung, in Zusammenhang gebracht werden. Durch die Zugabe von 1,5-Pentandiol konnte die Rissentstehung verhindert werden, da Hydrolyse und Kondensations-Reaktionen gehemmt werden, was eine höhere Flexibilität des Netzwerkes erhält. Weiterhin wurde die Rissentstehung signifikant durch die herrschende Luftfeuchtigkeit während es Beschichtungsprozesses beeinflusst, was mit unterschiedlichen Hydrolyse- und Kondensations-Raten zu erklären ist. Unter Verwendung bestimmter chemische Syntheseparameter, können ebenso wasserlösliche Vorstufenpulver erhalten werden. Grundsätzlich sind die Untersuchungen an den hieraus resultierenden wässrigen Solen und Schichten in guter Übereinstimmung mit den vorherigen Untersuchungen an ethanolischen Beschichtungssystemen. So zum Beispiel, beschleunigt ebenso das große Oberfläche zu Volumen Verhältnis der Film-Pulver deutlich die Film-Trocknung und –Verdichtung, im Vergleich zu den Sol-Pulvern. Auch beeinflusst ein Zusatz an 1,5-Pentandiol eindeutig das Verdichtungsverhalten und die Phasenentwicklung. Wie schon bereits im Fall der Ethanol basierenden Beschichtungen festgestellt worden ist, erhöht 1,5-Pentandiol die Beständigkeit hinsichtlich Hydrolyse und Kondensationsreaktionen und erhält hiermit eine gewisse Netzwerkplastizität. Deshalb bilden Filme die ohne einen Zusatz an 1,5-Pentandiol hergestellt worden sind, aufgrund von Zugspannung, schon während der Film-Trocknung und -Alterung Risse aus. Durch einen Zusatz von 1,5-Pentandiol kann dagegen die Entstehung von Rissen vermindert bzw. vermieden werden. Allerdings zeigten sich auch einige Unterschiede: So ist zum Beispiel die erreichbare Einzelschichtdicke der ethanolischen Beschichtungssystemen nahezu doppelt so groß wie die der wässrigen Beschichtungssysteme. Dies wurde mit der unterschiedlichen Oberflächenspannung des Basislösungsmittels erklärt, welche während der Schichttrocknung deutlich höhere Kapillarkräfte und Zugspannung in wässrigen Filmen erzeugt. Wird Acetylaceton gegen Triethanolamin als Chelatligand für Titan ausgetauscht, so können ebenso re-dispergierbare Vorstufenpulver hergestellt werden. Die Film-Pulver kombinieren hohe hydrolytische Stabilität der Vorstufe mit einer ausreichenden intermediären Netzwerkflexibilität. Der andere Komplexbildner verändert entscheidend das Trocknungs- und Verdichtungs-Verhalten: so z.B. wird die die Struktur von Film-Pulvern basierend auf Triethanolamin nicht entscheidend durch die Trocknung als dünne Schicht beeinflusst, im Gegensatz zu Film-Pulvern hergestellt von Vorstufenpulvern mit Acetylacetone als Chelatligand. Diese hohe hydrolytische Stabilität und Plastizität der Vorstufe ermöglicht die Herstellung von defektfreien Beschichtungen bis hin zu einer Einzelschichtdicke von 300 nm. Dennoch unterscheidet sich bei intermediären Pyrolysetemperaturen die Mikrostruktur der Triethanolamin basierenden Schichten deutlich von der auf Acetylaceton basierenden Schichtsystemen. Die Allgemeingültigkeit der Schlussfolgerungen wurde anhand Zirkonoxidbeschichtungen, welche ebenfalls unter Verwendung von löslichen Vorstufenpulvern hergestellt worden sind, überprüft. Grundsätzlich zeigte sich hierbei, dass alle Schlüsse hinsichtlich der Zusammenhänge der Vorstufenchemie, Film-Bildung, -Verdichtung und –Struktur auf die entsprechenden Zirkonoxidbeschichtungen übertragbar sind. Unterschiede ergeben sich nur aus unterschiedlichen Materialeigenschaften wie z.B. der makroskopischen Dichte. Letztlich wurde dargestellt, dass die Erkenntnisse hinsichtlich des Verdichtungsverhalten der Sol-Gel Schichten die Grundlage für die Aufklärung vieler anderer wichtiger wissenschaftlich Fragestellungen hinsichtlich Sol-Gel Beschichtungen bilden, wie z.B. der Kratzfestigkeit von Sol-Gel Schichten, Faser-Verbrückung und -Schädigung von Sol-Gel beschichten Fasern.
KW  - Sol-Gel-Verfahren
KW  - Dünne Schicht
KW  - Titan
KW  - Titandioxid
KW  - Dünnfilm
KW  - thin film
KW  - sol-gel
KW  - titania
Y1  - 2007
U6  - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-24577
ER  - 
TY  - THES
A1  - Klukowska, Anna
T1  - Switching hybrid polymers with physically and covalently entrapped organic photochromes
T1  - Schaltbare Hybridpolymere mit physikalisch eingebetteten und kovalent angebundenen organischen Photochromen
N2  - The aim of this work was to test and tailor new sol gel derived hybrid polymer coatings for the incorporation of photochromic spirooxazines and chromenes. The development and optimisation of work was performed via two different routes (dye and matrix ones), that led to photochromic multi-layer coating systems with coloration depth and photostabilities comparable to commercially available products. Hybrid sol-gel derived polymers were found to be suitable host materials for photochromic dyes. Matrix properties and the type of entrapment heavily influence the photochromic activity, as well as the degradation rate and the kinetics of incorporated dyes. Dyes incorporated within more polar and rigid matrices were found to show slower kinetics and higher coloration but associated with faster photodegradation. On the other hand, hosts with less polar sites, low residual water concentration and low rigidity are preferable in terms of photostability. Significant differences were found for physically incorporated and covalently grafted chromophores. Using silylated dyes that can participate in the sol-gel process, the photodegradation rate of the whole system can be decreased as compared to the physically entrapped systems. The higher photostability and slower kinetics for covalently bonded photochromes is probably due to sterical hindrance. Addition of proper stabilisers increases the photostability: The employment of UV light stabilisers, excited state quenchers and HALS was found to be beneficial but not sufficient. Besides the presence of stabilisers, also the reduction of oxygen migration into the coating (by a hard top coat and an inorganic anti reflective coating) strongly increases stability of photochromes. Finally, it was found that the separation of photochromes within two (or more) different layers leads to a further improvement of the coloration and fatigue behaviour of the whole coating stack, presumably by preventing the contact of dye molecules with excited states of other molecules or their degradation products. These latter findings are considered to pave the way for stable photochromic coatings based on hybrid polymers. Future development should be directed towards more photostable yellow and red switching dyes. The results of the present investigations should help to choose the most suitable molecular environments for the tested photochromes in terms of photostability, kinetics and activity, which is considered relevant with respect to potential applications, in particular in the ophthalmic sector. Furthermore, the interesting combination of properties of this type of materials offers a large potential with regard to many applications, such as coatings for sunglasses, radiation protectors, filters, sunroofs, reversible markings, printing applications and smart textiles.
N2  - Das Ziel dieser Arbeit war es, neue, über das Sol Gel Verfahren hergestellte Beschichtungsmaterialien zu entwickeln, die als Matrices für photochrome Spirooxazine und Chromene geeignet sind. Die Entwicklungs- und Optimierungsarbeit erfolgte über zwei Routen (Farbstoff- und Matrix-Rout) und führte zu komplexen photochromen Mehrschichtaufbauten, deren Einfärbungs und Photostabilitätseigenschaften mit kommerziell erhältlichen Produkten vergleichbar sind. Über das Sol-Gel Verfahren hergestellte hybride Polymere stellen geeignete Wirtsmaterialien für photochrome Farbstoffen dar. Die Eigenschaften der Matrix und die Einbauweise beeinflussen sowohl die photochrome Aktivität, als auch die Degradationsgeschwindigkeit und Kinetik der eingebauten Farbstoffe. Farbstoffe integriert in rigide Matrices höherer Polarität zeigen geringere Schaltgeschwindigkeit und stärkere Einfärbung, jedoch verknüpft mit höherer Degradationsgeschwindigkeit. Andererseits Matrixmaterialien mit eher unpolarem Charakter, niedriger Konzentration an Restwasser, und niedriger Rigidität sind zu bevorzugen, wenn gute Photostabilität erreicht werden soll. Wesentliche Unterschiede bestehen zwischen chemisch angebundenen und physikalisch eingebauten Farbstoffen. Durch den Einsatz von silylierten Farbstoffen, die am Sol Gel-Prozess partizipieren können, kann eine Verringerung der Photodegradationsgeschwindigkeit im Vergleich zu physikalisch eingebauten Farbstoffen erreicht werden. Höhere Photostabilität und langsamere Schaltkinetikt sind vermutlich auf sterische Hinderung zurückzuführen. Der Zusatz geeigneter Stabilisatoren erhöht die Photostabilität: Der Einsatz von UV Stabilisatoren, Excited State Quenchern und HALS ist vorteilhaft aber nicht ausreichend. Neben der Präsenz von Stabilisatoren, führt auch die Verringerung der Sauerstoffpermeation (durch eine harte Deckschicht und eine reflexionsmindernde PVD Beschichtung) zu einer Stabilitätserhöhung. Schließlich wurde gefunden, dass die räumliche Trennung der Farbstoffe in zwei (oder mehr) unabhängigen Schichten ebenfalls die Färbetiefe und Photoresistenz der Beschichtungen erhöhte, vermutlich dadurch, dass der Kontakt von Farbstoffmolekülen mit angeregten Zuständen anderer Moleküle oder ihren Degradationsprodukten verhindert oder zumindest eingeschränkt wird. Diese Befunde können den Weg für stabile photochrome Beschichtungen auf de Basis von Hybridpolymeren ebnen. Weiterer Optimierungsbedarf wird in den bisher erzielbaren Farbtönen gesehen. Zukünftige Entwicklungen sollten sich auf photostabilere gelb und rot schaltende Farbstoffe konzentrieren. Die Ergebnisse der vorgelegten Untersuchungen können bei der Auswahl der am besten geeigneten, molekularen Umgebung für erprobte Photochrome in Bezug auf Photostabilität, Kinetik und Aktivität helfen. Dies ist von großer Bedeutung im Hinblick auf mögliche Anwendung vor allem im ophthalmischen Bereich. Darüber hinaus bergen die interessante Eigenschaftskombinationen dieser Art von Materialien großes Potential für ein weites Feld möglicher Anwendungen (Sonnenbrillen, Strahlungsschutz, Filter, Sonnendächer, schaltbare Markierungen, Druck, Textilien).
KW  - Metallorganische Polymere
KW  - Sol-Gel-Verfahren
KW  - Spirooxazine
KW  - Photochrome Verbindungen
KW  - Photochromie
KW  - Sol-Gel
KW  - Hybridpolymere
KW  - Ophthalmik
KW  - Spirooxazine
KW  - photochromism
KW  - sol-gel
KW  - hybrid polymers
KW  - ophthalmic
KW  - spirooxazine
Y1  - 2004
U6  - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-11721
ER  -