TY - THES A1 - Lorson, Thomas T1 - Novel Poly(2-oxazoline) Based Bioinks T1 - Neuartige Poly(2-oxazolin) Basierte Biotinten N2 - Motivated by the great potential which is offered by the combination of additive manufacturing and tissue engineering, a novel polymeric bioink platform based on poly(2 oxazoline)s was developed which might help to further advance the young and upcoming field of biofabrication. In the present thesis, the synthesis as well as the characteristics of several diblock copolymers consisting of POx and POzi have been investigated with a special focus on their suitability as bioinks. In general, the copolymerization of 2-oxazolines and 2-oxazines bearing different alkyl side chains was demonstrated to yield polymers in good agreement with the degree of polymerization aimed for and moderate to low dispersities. For every diblock copolymer synthesized during the present study, a more or less pronounced dependency of the dynamic viscosity on temperature could be demonstrated. Diblock copolymers comprising a hydrophilic PMeOx block and a thermoresponsive PnPrOzi block showed temperature induced gelation above a degree of polymerization of 50 and a polymer concentration of 20 wt%. Such a behavior has never been described before for copolymers solely consisting of poly(cyclic imino ether)s. Physically cross linked hydrogels based on POx b POzi copolymers exhibit reverse thermal gelation properties like described for solutions of PNiPAAm and Pluronic F127. However, by applying SANS, DLS, and SLS it could be demonstrated that the underlying gel formation mechanism is different for POx b POzi based hydrogels. It appears that polymersomes with low polydispersity are formed already at very low polymer concentrations of 6 mg/L. Increasing the polymer concentration resulted in the formation of a bicontinuous sponge like structure which might be formed due to the merger of several vesicles. For longer polymer chains a phase transition into a gyroid structure was postulated and corresponds well with the observed rheological data. Stable hydrogels with an unusually high mechanical strength (G’ ~ 4 kPa) have been formed above TGel which could be adjusted over a range of 20 °C by changing the degree of polymerization if maintaining the symmetric polymer architecture. Variations of the chain ends revealed only a minor influence on TGel whereas the influence of the solvent should not be neglected as shown by a comparison of cell culture medium and MilliQ water. Rotationally as well as oscillatory rheological measurements revealed a high suitability for printing as POx b POzi based hydrogels exhibit strong shear thinning behavior in combination with outstanding recovery properties after high shear stress. Cell viability assays (WST-1) of PMeOx b PnPrOzi copolymers against NIH 3T3 fibroblasts and HaCat cells indicated that the polymers were well tolerated by the cells as no dose-dependent cytotoxicity could be observed after 24 h at non-gelling concentrations up to 100 g/L. In summary, copolymers consisting of POx and POzi significantly increased the accessible range of properties of POx based materials. In particular thermogelation of aqueous solutions of diblock copolymers comprising PMeOx and PnPrOzi was never described before for any copolymer consisting solely of POx or POzi. In combination with other characteristics, e.g. very good cytocompatibility at high polymer concentrations and comparably high mechanical strength, the formed hydrogels could be successfully used for 3D bioprinting. Although the results appear promising and the developed hydrogel is a serious bioink candidate, competition is tough and it remains an open question which system or systems will be used in the future. N2 - Motiviert durch das große Potential, das die Kombination aus additiver Fertigung und künstlicher Geweberegeneration bietet, wurde eine neuartige polymerbasierte Biotintenplattform auf Basis von Poly(2 oxazolin)en entwickelt. Diese soll zukünftig dazu beitragen das noch junge, aber aufstrebende Forschungsfeld der Biofabrikation weiterzuentwickeln. In der vorliegenden Arbeit wurden die Synthese sowie die Eigenschaften von mehreren Diblock Copolymeren, bestehend aus POx und POzi, untersucht, wobei der Hauptfokus auf deren Eignung als Biotinte lag. Grundsätzlich konnte gezeigt werden, dass Copolymere, bestehend aus 2 Oxazolinen und 2 Oxazinen, die unterschiedliche Alkylseitenketten besitzen, synthetisiert werden können. Dabei lagen die ermittelten Polymerisationsgrade nahe am zuvor errechneten Wert. Die Polymere wiesen mittlere bis niedrigere Dispersitäten auf. Für jedes der im Rahmen der vorliegenden Arbeit synthetisierten Diblock Copolymere konnte eine mehr oder weniger starke Abhängigkeit der dynamischen Viskosität von der Temperatur gezeigt werden. Allerdings ist es nicht möglich, aus den thermischen Eigenschaften des Bulkmaterials Rückschlüsse auf das temperaturabhängige Verhalten in Lösung zu ziehen. Diblock Copolymere mit einem hydrophilen PMeOx Block und einem thermoresponsiven PnPrOzi Block bildeten oberhalb einer Kettenlänge von 50 Einheiten und einer Polymerkonzentration von 20 Gew% ein physikalisches Gel. Solch ein Verhalten wurde bisher noch nicht für Copolymere, die ausschließlich auf POx oder seinen höheren Homologen basieren, beschrieben. Physikalische Hydrogele, basierend auf POx b POzi Copolymeren, weisen eine umgekehrte thermische Gelierung wie auch wässrige Lösungen von PNiPAAm und Pluronic F127 auf. Allerdings konnte durch die komplementäre Verwendung von SANS, DLS und SLS gezeigt werden, dass sich der zugrundeliegende Gelbildungsmechanismus für POx b POzi basierte Hydrogele deutlich von den beiden zuvor genannten unterscheidet. Es wird davon ausgegangen, dass sich zunächst bei einer sehr geringen Polymerkonzentration von 6 mg/L Vesikel mit geringer Polydispersität ausbilden. Eine Erhöhung der Konzentration resultiert in der Ausbildung eines bikontinuierlichen Netzwerks mit schwammartiger Struktur. Dieses bildet sich vermutlich durch die Fusion mehrerer Vesikel. Des Weiteren wird für höhere Polymerisationsgrade ein Phasenübergang zu einer gyroidalen Struktur postuliert der sich sehr gut mit den gewonnenen rheologischen Daten deckt. Stabile Hydrogele mit außergewöhnlich hoher mechanischer Stärke (G‘ ≈ 4kPa) bildeten sich oberhalb der Tgel, die über eine Temperaturspanne von 20 °C durch Änderung des Polymerisationsgrades eingestellt werden konnte. Veränderung der Kettenenden zeigten nur einen geringen Einfluss auf die TGel, wobei der Einfluss des verwendeten Lösemittels nicht unterschätzt werden sollte. Dies konnte durch den direkten Vergleich von MilliQ Wasser und Zellkulturmedium gezeigt werden. Rheologische Untersuchungen, die sowohl im rotierenden als auch im oszillierenden Modus durchgeführt wurden, zeigten eine gute Eignung der POx b POzi basierten Hydrogele für Extrusion basierte Druckverfahren. Insbesondere aufgrund des stark ausgeprägten scherverdünnenden Verhaltens und der ausgezeichneten Strukturerholung nach hoher Scherbelastung sollten gute Druckergebnisse erzielbar sein. Zellviabilität-Assays (WST-1) von PMeOx b PnPrOzi Copolymeren an NIH 3T3 Fibroblasten und HaCat-Zellen zeigten, dass die Polymere bei Konzentrationen von bis zu 100 g/L und Inkubationszeiten von 24 h keine dosisabhängige Zytotoxizität besitzen. Zusammenfassend kann festgehalten werden, dass die Copolymerisation von POx und POzi den verfügbaren Eigenschaftsbereich von POx basierten Materialien deutlich vergrößert hat. Insbesondere die temperaturinduzierte Gelierung von wässrigen Polymerlösungen wurde noch nie zuvor für ein anderes Copolymer auf Basis von POx und POzi beschrieben. Aufgrund ihrer herausragenden Eigenschaften, wozu unter anderem eine sehr gute Zytokompatibilität bei hohen Polymerkonzentrationen und eine vergleichsweise hohe mechanische Festigkeit zählen, konnten die entwickelten Hydrogele erfolgreich für den 3D Biodruck verwendet werden. Obwohl die beschriebenen Ergebnisse sehr vielversprechend sind und die entwickelte Hydrogelplattform folglich als ernstzunehmender Biotintenkandidat angesehen werden sollte, ist die Konkurrenz sehr groß und es bleibt abzuwarten, welche Tinte bzw. Tinten in Zukunft zum Einsatz kommen. KW - Polymere KW - Ringöffnungspolymerisation KW - Lichtstreuung KW - Biomaterial KW - 3D-Druck KW - Poly(2-oxazolin)e KW - poly(2-oxazoline)s KW - Biofabrikation KW - biofabrication KW - Biotinten KW - bioinks KW - Hydrogel KW - hydrogel KW - Ringöffnungspolymerisation KW - ring-opening polymerization Y1 - 2019 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-180514 ER - TY - THES A1 - Ulbricht, Juliane T1 - Insights into Polymer Biodegradation - Investigations on oxidative, hydrolytic and enzymatic Pathways T1 - Einblicke in die Bioabbaubarkeit von Polymeren - Untersuchungen zu oxidativen, hydrolytischen und enzymatischen Abbauwegen N2 - The present work aims towards the investigation of polymer degradation under biologically relevant conditions. In order to assess a potential degradation of polymers of interest for biomedical applications in vivo and associated effects on living tissue, representatives of poly(2-oxazoline)s and polypeptoids as well as poly(ethylene glycol) and poly(N-vinylpyrrolidone) for reference purposes are examined regarding their stability under oxidative and hydrolytic conditions as well as towards enzymatic degradation. The polymers investigated in the framework of this thesis are generally considered to be non-biodegradable. Both poly(ethylene glycol) and poly(N-vinylpyrrolidone) are or were applied intensively in vivo provoking seriously harmful side effects like fatal blood poisoning from the oxidation of poly(ethylene glycol) chain ends or poly(N-vinylpyrrolidone) storage disease. Poly(2-alkyl-2-oxazoline)s and polypeptoids, both promising polymeric biomaterials for a wide variety of in vivo applications, are not clinically applied yet but undergo thorough investigations. However, comprising amide bonds within the backbone or the appending side chain, poly(2-alkyl-2-oxazoline)s and polypeptoids potentially offer a higher susceptibility towards (bio-)degradation. Representing the three most impactful initiators of degradation in vivo, the present study is focused on polymer deterioration by oxidative species, hydrolytic conditions and enzymes. Oxidative species are generated in a variety of processes in vivo, both on purpose and as an unintentional by-product. Previous investigations revealed the susceptibility of poly(ethylene glycol), poly(N-vinylpyrrolidone), poly(2-alkyl-2-oxazoline)s and polypeptoids to deterioration by hydroxyl radicals deriving from hydrogen peroxide and copper ions. The obtained data confirm previous results of an apparent degradation rate increasing with increasing chain length due to self-inhibitory end group effects for all investigated polymer species. Although the exact concentrations of oxidative species in vivo are very controversial, with respect to their great variety and wide distribution the investigated polymers are likely prone to oxidative deterioration to some extent, with rates, mechanisms and degradation products strongly depending on the respective reactive species, polymer structure and chain length. Like blood, most tissues of the human body benefit from a slightly alkaline pH value. Nevertheless, specific areas like the human stomach or tumor tissues possess acidic conditions potentially capable to cleave amide bonds comprised by poly(2-alkyl-2-oxazoline)s and polypeptoids. Unlike the hydrolysis of poly(2-alkyl-2-oxazoline)s resulting in side chain cleavage, the hydrolysis of polypeptoids induces backbone scission decreasing the polymer chain length tremendously and releasing, if performed exhaustively, the respective amino acids. Hydrolysis of polysarcosine is monitored by quantification of the released sarcosine via 1H-NMR spectroscopy and determination of the residual Mw via GPC. Its cyclic dimer sarcosine anhydride is formed as an intermediate product in this process via cyclization of unstable linear dimers of sarcosine. Modification and degradation of bio(macro)molecules is an essential part of human metabolism. Polymers bearing amide bonds and showing a great similarity to natural occurring and widely distributed polypeptides, like poly(2-alkyl-2-oxazoline)s and polypeptoids, bear the potential of an enzymatic biodegradability by (more or less specific) peptidases. Just like the acidic hydrolysis described previously, peptidase activity would result in the cleavage of polymer amide bonds. The aim of the present thesis was to evaluate the stability of poly(2-alkyl-2-oxazoline)s and polypeptoids as well as poly(ethylene glycol) for the sake of reference under circumstances resembling in vivo conditions as closely as possible. Initial experiments focused on the degradation of dye-labeled upon incubation with homogenates of freshly harvested rat liver and kidney. However, although the obtained results are promising for the most part, they are considered rather unreliable and non-reproducible for various reasons. More conclusive data are attained from the incubation of non-labeled polymers in freshly laid chicken eggs. While no evidence for an enzymatic digestion of poly(ethylene glycol) in chicken egg white is found and deterioration of poly(2-methyl-2-oxazoline) upon incubation apparently derives from non-enzymatic hydrolysis, incubated polysarcosine samples reveal distinct elugram patterns depending on the respective C- and N-terminal end groups indicating both exopeptidase and endopeptidase activity. It has to be kept in mind though, that an enzymatic digestibility of polysarcosine does not necessarily imply the digestion of polypeptoids bearing longer side chains by peptidases as well, which should be investigated in further studies. N2 - Die vorgestellte Arbeit befasst sich mit der Untersuchung des Abbauverhaltens von Polymeren unter biologisch relevanten Bedingungen. Vertreter der Poly(2-alkyl-2-oxazolin)e und Polypeptoide sowie Polyethylenglycol und Poly(N-vinylpyrrolidon) als Referenzpolymere werden im Hinblick auf ihre Stabilität unter oxidativen und hydrolytischen Bedingungen sowie gegen enzymatische Verdauung untersucht, um Rückschlüsse auf ihren potentiellen Abbau in vivo ziehen und die damit verbundenen Auswirkungen auf lebendes Gewebe abschätzen zu können. Poly(2-alkyl-2-oxazolin)e und Polypeptoide, zwei vielversprechende, jedoch noch wenig untersuchte Polymerklassen, sind als Biomaterialien für eine Vielzahl von in vivo Anwendungen interessant, werden aber bisher nicht kommerziell eingesetzt. Wie auch Polyethylenglycol und Poly(N-vinylpyrrolidon) werden Poly(2-alkyl-2-oxazolin)e und Polypeptoide als nicht bioabbaubar angesehen, was in Anbetracht der im Polymerrückgrat bzw. der davon abgehenden Seitenkette enthaltenen Amidbindungen kritisch zu hinterfragen ist. Reaktive Sauerstoff- und Stickstoffspezies werden in vivo in einer Vielzahl von Prozessen gezielt oder auch als unerwünschtes Nebenprodukt gebildet. Vorangegangene Untersuchungen konnten bereits die Anfälligkeit von Polyethylenglycol, Poly(N-vinylpyrrolidon), Poly(2-alkyl-2-oxazolin)en und Polypeptoiden für Modifikationen durch in situ durch Reaktion von Wasserstoffperoxid und Kupferionen gebildete Hydroxylradikale zeigen. Desweiteren wiesen die Resultate auf eine starke Abhängigkeit der scheinbaren Abbaurate von der Polymerkettenlänge hin. Die erhaltenen Daten bestätigen die früheren Ergebnisse zum Anstieg der scheinbaren Abbaurate mit steigender Kettenlänge durch selbstinhibitorische Endgruppeneffekte für alle untersuchten Polymerspezies. Die tatsächlichen Konzentrationen reaktiver Sauerstoffspezies in vivo werden kontrovers diskutiert, hinsichtlich ihrer großen Vielfalt und breiten Verteilung im Körper ist es jedoch durchaus wahrscheinlich, dass die untersuchten Polymere in vivo in unterschiedlichem Maße dem oxidativen Abbau unterliegen. Dabei sind nicht nur die Abbauraten, sondern auch der Mechanismus und die entsprechend gebildeten Abbauprodukte von der Art der reaktiven Spezies, der Polymerstruktur und der entsprechenden Kettenlänge abhängig. Blut und die meisten Gewebe des menschlichen Körpers sind auf einen leicht alkalischen pH-Wert angewiesen. Dennoch weisen spezifische Regionen wie den Magen oder Tumorgewebe ein saures Milieu auf, welches eventuell in der Lage ist, Amidbindungen, wie sie in Poly(2-alkyl-2-oxazolin)en und Polypeptoiden enthalten sind, zu spalten. Im Gegensatz zur Hydrolyse von Poly(2-alkyl-2-oxazolin)en, welche in Abspaltung der Seitenkette resultiert, kommt es bei der Hydrolyse von Polypeptoiden zur Spaltung des Polymerrückgrates, welche mit einer drastischen Verringerung der Kettenlänge und, mit fortschreitender Hydrolyse, mit der Freisetzung der entsprechenden Aminosäure einhergeht. Die Hydrolyse von Polysarkosin wird durch Quantifizierung des freigesetzten Sarkosins via 1H-NMR Spektroskopie sowie durch Bestimmung des Mw via GPC verfolgt. Dabei zeigt sich, dass sich das zyklische Dimer Sarkosinanhydrid als Zwischenprodukt der Hydrolyse durch Zyklisierung instabiler linearer Dimere bildet. Die Modifikation und der Abbau von Bio(makro)molekülen sind essentieller Bestandteil des menschlichen Metabolismus. Polymere, die wie die Poly(2-alkyl-2-oxazolin)e und Polypeptoide Amidbindungen und damit große Ähnlichkeit zu den natürlich vorkommenden und weit verbreiteten Polypeptiden aufweisen, bergen das Potential einer möglichen Bioabbaubarkeit durch Peptidasen. Ziel der vorliegenden Arbeit war die Evaluierung der Stabilität von Poly(2-alkyl-2-oxazolin)en und Polypeptoiden sowie Polyethylenglycol als Referenzpolymer ohne Amidbindungen unter Bedingungen, welche den in vivo vorliegenden Verhältnisse möglichst ähnlich sind. In ersten Experimenten liegt der Schwerpunkt auf der Inkubation Farbstoff-markierter Polymere in Homogenaten von frisch entnommenen Rattenlebern und -nieren. Obwohl die erhaltenen Ergebnisse zum Großteil vielversprechend sind, bestehen aus einer Vielzahl von Gründen Zweifel an ihrer Zuverlässigkeit und Reproduzierbarkeit. Die Inkubation von nicht marktierten Polymeren in frisch gelegten Hühnereiern liefert aussagekräftigere Ergebnisse. Es sind keine Hinweise auf einen enzymatischen Abbau von Polyethylenglycol in Hühnereiweiß ersichtlich. Abweichungen der Elugramme des Poly(2-methyl-2-oxazolin)s deuten auf eine Modifikation während der Inkubation hin, die jedoch vermutlich nicht enzymatischen Ursprungs ist. Im Gegensatz dazu zeigen die Polysarkosin-Proben in Abhängigkeit der entsprechenden C- und N-terminalen Gruppen charakteristische Elugrammmodifikationen, welche auf die Aktivität von Exo- und Endopeptidasen hindeuten. KW - Biologischer Abbau KW - Polymere KW - Bioabbaubarkeit KW - Polyethylenglycol KW - Polypeptoide KW - Poly(2-oxazolin)e KW - Biodegradability KW - Polyethylene glycol KW - Polypeptoids KW - Poly(2-oxazoline)s Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-158683 ER -