TY - THES A1 - Al-Baidhani, Mohammed T1 - Spectroscopy as a tool to investigate the high energy optical properties of nanostructured magnetically doped topological insulator T1 - Spektroskopie als Methode zur Untersuchung der optischen Eigenschaften nanostrukturierter, magnetisch dotierter Topologischer Isolatoren bei hohen Energien N2 - In this dissertation the electronic and high-energy optical properties of thin nanoscale films of the magnetic topological insulator (MTI) (V,Cr)y(BixSb1-x)2-yTe3 are studied by means of X-ray photoelectron spectroscopy (XPS) and electron energy-loss spectroscopy (EELS). Magnetic topological insulators are presently of broad interest as the combination of ferromagnetism and spin-orbit coupling in these materials leads to a new topological phase, the quantum anomalous Hall state (QAHS), with dissipation less conduction channels. Determining and controlling the physical properties of these complex materials is therefore desirable for a fundamental understanding of the QAHS and for their possible application in spintronics. EELS can directly probe the electron energy-loss function of a material from which one can obtain the complex dynamic dielectric function by means of the Kramers-Kronig transformation and the Drude-Lindhard model of plasmon oscillations. The XPS core-level spectra in (V,Cr)y(BixSb1-x)2-yTe3 are analyzed in detail with regards to inelastic background contributions. It is shown that the spectra can be accurately described based on the electron energy-loss function obtained from an independent EELS measurement. This allows for a comprehensive and quantitative analysis of the XPS data, which will facilitate future core-level spectroscopy studies in this class of topological materials. From the EELS data, furthermore, the bulk and surface optical properties were estimated, and compared to ab initio calculations based on density functional theory (DFT) performed in the GW approximation for Sb2Te3. The experimental results show a good agreement with the calculated complex dielectric function and the calculated energy-loss function. The positions of the main plasmon modes reported here are expected to be generally similar in other materials in this class of nanoscale TI films. Hence, the present work introduces EELS as a powerful method to access the high-energy optical properties of TI thin films. Based on the presented results it will be interesting to explore more systematically the effects of stoichiometry, magnetic doping, film thickness and surface morphology on the electron-loss function, potentially leading to a better understanding of the complex interplay of structural, electronic, magnetic and optical properties in MTI nanostructures. N2 - Die vorliegende Dissertation beschäftigt sich mit den elektronischen und hochen- ergetischen optischen Eigenschaften von auf der Nanoskala dünnen Filmen des magnetischen topologischen Isolators (MTI) (V,Cr)y(BixSb1−x)2−yTe3 mithilfe von Röntgenphotoelektronenspektroskopie (engl.: X-ray photoelectron spectroscopy, XPS), sowie Elektronenenergieverlustspektroskopie (engl.: electron energy-loss spectroscopy, EELS). Magnetische topologische Isolatoren sind gegenwärtig von großem Interesse, da die Kombination von Ferromagnetismus und Spin-Bahn- Kopplung in diesen Materialien zu einer neuen topologischen Phase führt, der Quanten-Anomalen-Hall-Phase (engl.: quantum anomalous Hall state, QAHS), die sich durch verlustfreie Leitungskanäle auszeichnet. Bestimmung und Kontrolle der physikalischen Eigenschaften dieser komplexen Materialien ist somit erstrebenswert für ein fundamentales Verständnis des QAHS sowie für Anwendungen in der Spin- tronik. EELS erlaubt die direkte Untersuchung der Elektronenenergieverlustfunk- tion eines Materials, aus der man, mithilfe der Kramers-Kronig-Transformation und des Drude-Lindhard-Modells von Plasmonenoszillationen, die komplexe dynamis- che dielektrische Funktion des Materials erhält. In den XPS-Spektren der Rumpfniveaus in (V,Cr)y(BixSb1−x)2−yTe3 wird detail- liert insbesondere der Beitrag des inelastischen Untergrunds analysiert. Es kann gezeigt werden, dass, basierend auf der in einem unabhängigen EELS-Experiment gewonnenen Elektronenenergieverlustfunktion, die Rumpfniveauspektren präzise beschrieben werden können. Dies erlaubt eine umfangreiche und quantitative Anal- yse der Daten, was zukünftige Rumpfniveaustudien dieser Klasse topologischer Materialien erleichtern wird. Die mit EELS gewonnenen Daten ermöglichen weiter- hin eine Abschätzung der optischen Eigenschaften von Volumen und Oberfläche der Materialien, die in der vorliegenden Arbeit mit ab initio Berechnungen aus der Literatur für Sb2Te3 verglichen werden, welche auf Basis der Dichtefunktionaltheo- rie (DFT) in GW-näherung durchgeführt wurden. Die experimentellen Ergebnisse zeigen gute Übereinstimmungen mit der berechneten komplexen dielektrischen Funktion, sowie mit der Energieverlustfunktion. Es wird erwartet, dass die hier beschriebenen Positionen der Hauptplasmonenmoden im Allgemeinen ähnlich zu denen anderer Materialien dieser Klasse auf der Nanoskala dünner topologischer Isolatoren sind. Somit stellt die vorliegende Arbeit das EELS Experiment als eine mächtige Methode vor, die einen Zugang zu den hochenergetischen optischen Eigen- schaften dünner TIs schafft. Basierend auf den hier vorgestellten Ergebnissen bleibt es interessant sein die Auswirkungen von Stöchiometrie, magnetischer Dotierung, Filmdicke, sowie Oberflächenmorphologie auf die Energieverlustfunktion system- atischer zu untersuchen, um damit ein besseres Verständnis für das komplexe Zusammenspiel aus strukturellen, elektronischen und optischen Eigenschaften in MTI-Nanostrukturen zu erlangen. KW - spectroscopy KW - XPS KW - REELS KW - topological insulator KW - QAHE KW - Topologischer Isolator KW - Optische Eigenschaft KW - Elektronenspektroskopie Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-157221 ER - TY - THES A1 - Keller, Dirk T1 - Optische Eigenschaften ZnSe-basierter zweidimensionaler Elektronengase und ihre Wechselwirkung mit magnetischen Ionen T1 - ZnSe-based QWs with a two-dimensional electron gas: Optical properties and interaction with magnetic ions N2 - In dieser Arbeit wurden nichtmagnetische und semimagnetische ZnSe-basierte Quantentröge untersucht. Im Mittelpunkt des Interesses standen hierbei vor allem die Modifikation der optischen Spektren mit einer zunehmenden Modulationsdotierung der Strukturen und der Einfluss von Spinflip-Streuungen der freien Band-Elektronen an den Mn-Ionen auf die Magnetisierung und somit die Zeeman-Aufspaltung der Strukturen. Als experimentelle Methoden wurden Photolumineszenz (PL), Photolumineszenzanregung (PLE) und Reflexionsmessungen verwendet, die in Magnetfeldern von bis zu B=48 T und bei Temperaturen im Bereich von 1.6 K bis 70 K durchgeführt wurden. Darüber hinaus wurde die Abhängigkeit der Spin-Gitter-Relaxationszeit der Mn-Ionen von der Mn-Konzentration und der Elektronengasdichte in den Quantentrögen durch zeitaufgelöste Lumineszenzmessungen untersucht. Der Einfluss eines Gradienten in der s/p-d-Austauschwechselwirkung auf die Diffusion der Ladungsträger bildet einen weiteren Schwerpunkt dieser Arbeit. Als experimentelle Methode wurde hierbei ortsaufgelöste Lumineszenz verwendet. N2 - In the present work, nonmagnetic and semimagnetic ZnSe based quantum wells were studied. The thesis was focussed on the modification of optical spectra with an increasing modulation-doping of the structures. Further emphasis was placed on the influence of the spinflip scattering of the free carriers and the Mn ions on the magnetization and thus the giant Zeeman splitting of the structures. As experimental methods, photoluminescence spectroscopy (PL), photoluminescence excitation spectroscopy (PLE) and reflection measurements were used and were performed in magnetic fields up to B=48 T and at temperatures within the range of 1.6 K to 70 K. In addition, the dependence of the spin-lattice relaxation time of the Mn ions on the Mn concentration and the electron density was examined by time-resolved luminescence spectroscopy. The influence of a gradient in the s/p-d-exchange interaction on the diffusion of carriers was studied by spatially resolved luminescence spectroscopy. KW - Zinkselenid KW - Dimension 2 KW - Elektronengas KW - Optische Eigenschaft KW - Manganselenide KW - Quantenwell KW - Elektronenstreuung KW - Spin flip KW - Manganion KW - Quantentrog KW - Magneto-optische Eigenschaften KW - 2DEG KW - Exziton KW - Spinflip-Streuung KW - quantum wells KW - magneto-optical properties KW - 2DEG KW - excitons KW - spinflip scattering Y1 - 2004 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-14774 ER - TY - THES A1 - Wagner, Joachim T1 - Optische Charakterisierung von II-VI-Halbleiter-Oberflächen in Kombination mit First-Principles-Rechnungen T1 - Optical Characterisation of II-VI Semiconductor Surfaces in Combination with First Principles Calculations N2 - In dieser Arbeit sind Methoden der optischen Spektroskopie, insbesondere die Ramanspektroskopie (RS) und die Reflexions-Anisotropie-Spektroskopie (RAS), angewandt worden, um die Oberflächen von II-VI Halbleitern zu charakterisieren. Für die experimentellen Untersuchungen wurde eine eigens für diesen Zweck entwickelte UHV-Optikkammer benutzt. Diese einzigartige Möglichkeit, II-VI Halbleiterproben aus einer state-of-the-art MBE-Anlage mit einer UHV-Optikanlage zu kombinieren hat gezeigt, dass optische Spektroskopie sehr gut dafür geeignet ist, strukturelle Eigenschaften, z.B. Rekonstruktionen, und chemische Bindungen an Oberflächen, sowie die damit verbundene Schwingungsdynamik zu analysieren. Neben den experimentellen Arbeiten wurden u. a. first principles Rechnungen mittels der Dichtefunktionaltheorie im Rahmen der Lokalen-Dichte-Approximation durchgeführt. Damit konnten für die Oberflächen einerseits ihre geometrischen Eigenschaften, d.h die atomare Anordnung der Oberflächenatome, und andererseits auch ihre Dynamik, d.h. die Schwingungsfrequenzen und die Auslenkungsmuster der an der Rekonstruktion beteiligten Atome der Oberfläche und der oberflächennahen Schichten, im Rahmen der Frozen-Phonon-Näherung bestimmt werden. Die Kombination von experimenteller und theoretischer Vibrationsbestimmung von Oberflächen bietet also, neben den klassischen Oberflächen-Analysemethoden wie RHEED, LEED, XPS, Auger und SXRD, ein zusätzliches Werkzeug zur Charakterisierung von Oberflächen. Da die Frozen-Phonon-Näherung nicht elementarer Bestandteil des hier benutzten DFT-Programmcodes fhi96md ist, wurde diese Erweiterung im Rahmen dieser Arbeit durchgeführt. Die theoretische Berechnung von Schwingungsfrequenzen mit dynamischen Matrizen ist in einem Unterkapitel dargestellt. Die so berechneten Schwingungsfrequenzen für verschiedene Oberflächen-Rekonstruktionen konnten erfolgreich am Beispiel der reinen BeTe(100)-Oberfläche mit den experimentell mit der UHV-Ramanspektroskopie beobachteten Frequenzen verglichen werden. So gelang erstmalig die optische identifizierung von rekonstruktionsinduzierten Eigenschwingungen einer Oberfläche. Nach detaillierter Kenntnis der BeTe(100)-Oberfläche wurde die Ramanspektroskopie als Sonde benutzt, um die Entwicklung der BeTe-Oberfläche bei unterschiedlichen Behandlungen (Modifikation) zu verfolgen. Dabei dienten die früheren Ergebnisse als Referenzpunkte, um die modifizierten Spektren zu erklären. Zusätzlich wurde ein Konzept zur Passivierung der Te-reichen BeTe(100)-Oberfläche entwickelt, um diese Proben ohne einen technisch aufwendigen UHV-Transportbehälter über grössere Entfernungen transportieren zu können (z.B. zu Experimenten an einem Synchrotron). Mit der RAS wurden auch die Oberflächen von weiteren Gruppe II-Telluriden, nämlich die Te-reiche (2x1) CdTe(100)-Oberfläche, die Te-reiche (2x1) MnTe(100)-Oberfläche und die Hg-reiche c(2x2) HgTe(100)-Oberfläche untersucht. Schließlich wurde der Wachstumsstart von CdSe auf der BeTe(100)-Oberfläche im Bereich weniger Monolagen (1-5 ML) CdSe analysiert, wobei die hohe Empfindlichkeit der Ramanspektroskopie bereits den Nachweis einer Monolage CdSe erlaubte. N2 - In this thesis optical spectroscopy, especially Raman spectroscopy (RS) and reflection anisotropy spectroscopy (RAS), was used for characterisation of II-VI-semiconductor surfaces. For the experimental studies a specially designed UHV-optical chamber was applied. The unique combination of a state of the art molecular beam epitaxy (MBE) facility with this UHV-optical chamber distinctly proved that optical spectroscopy is a powerfull tool for analyzing the structural properties (e.g. reconstructions) and the chemical bindings at a surface, as well as its dynamical properties. Beside the experimental activities, first principles calculations within the framework of density functional theory (DFT) and local density approximation (LDA) were performed. Therefore the geometrical, statical properties (e.g. atomic positions) of the surface and near-surface atoms could be determined. Additionally, their dynamical properties (e.g. displacement patterns and vibrational frequencies) were calculated with the frozen phonon approximation. This combination of experimental and theoretical determination of the surface dynamics offers an additional tool for surface characterisation beside the classical methods for surface analysis like RHEED, LEED, XPS, Auger and SXRD. Because frozen phonon calculations do not constitute an integral part of the available DFT programm code fhi96md, the extension was performed as a part of this thesis. The theoretical calculation of vibration frequencies with dynamical matrices is described in one of the subsections. The frequencies calculated in this way for different surface reconstructions were successfully compared with the experimentally observed frequencies in the case of pure BeTe(100) surfaces. Thus, the first optical identification of reconstruction-induced surface eigenvibration modes was realized. After this detailed knowledge of the BeTe(100) surface Raman spectroscopy was used as a probe to track the changes of the BeTe surface under different modifications. In doing so the previous result on the pure BeTe surfaces served as references to explain the modified spectra. Besides a concept for passivation of the tellurium rich BeTe(100) surface was developed to ease the transport to far away laboratories without using extensive UHV facilities. Additionally the surfaces of further group II-tellurides (e.g. Te-rich (2x1) CdTe(100), Te-rich (2x1) MnTe(100) and Hg-rich c(2x2) HgTe) has been investigated with the RAS. Finally the start of the CdSe growth on the BeTe(100) surface was analyzed in the region of 1-5 monolayers of CdSe. Within these experiments a high sensitivity for detecting even one monolayer of CdSe was achieved by Raman spectroscopy. KW - Zwei-Sechs-Halbleiter KW - Halbleiteroberfläche KW - Optische Eigenschaft KW - optisch KW - spektroskopie KW - Halbleiter KW - Oberfläche KW - DFT KW - optical KW - spectroscopy KW - semiconductor KW - surface KW - DFT Y1 - 2003 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-8722 ER -