TY - THES A1 - Meininger, Markus T1 - Calcium hydroxide as antibacterial implant coating T1 - Calciumhydroxid als antibaterielle Implantatbeschichtung N2 - In modern medicine hip and knee joint replacement are common surgical procedures. However, about 11 % of hip implants and about 7 % of knee implants need re-operations. The comparison of implant registers revealed two major indications for re-operations: aseptic loosening and implant infections, that both severely impact the patients’ health and are an economic burden for the health care system. To address these problems, a calcium hydroxide coating on titanium was investigated in this thesis. Calcium hydroxide is a well-known antibacterial agent and used with success in dentistry. The coatings were applied with electrochemically assisted deposition, a versatile tool that combines easiness of process with the ability to coat complex geometries homogeneously. The pH-gradient during coating was investigated and showed the surface confinement of the coating process. Surface pre-treatment altered the surface morphology and chemistry of the titanium substrates and was shown to affect the morphology of the calcium hydroxide coatings. The influence of the coating parameters stirring speed and current pulsing were examined in various configurations and combinations and could also affect the surface morphology. A change in surface morphology results in a changed adhesion and behavior of cells and bacteria. Thus, the parameters surface pre-treatment, stirring speed and current pulsing presented a toolset for tailoring cellular response and antibacterial properties. Microbiological tests with S. aureus and S. epidermidis were performed to test the time-dependent antibacterial activity of the calcium hydroxide coatings. A reduction of both strains could be achieved for 13 h, which makes calcium hydroxide a promising antibacterial coating. To give insight into biofilm growth, a protocol for biofilm staining was investigated on titanium disks with S. aureus and S. epidermidis. Biofilm growth could be detected after 5 days of bacterial incubation, which was much earlier than the 3 weeks that are currently assumed in medical treatment. Thus, it should be considered to treat infections as if a biofilm were present from day 5 on. The ephemeral antibacterial properties of calcium hydroxide were further enhanced and prolonged with the addition of silver and copper ions. Both ionic modifications significantly enhanced the bactericidal potential. The copper modification showed higher antibacterial effects than the silver modification and had a higher cytocompatibility which was comparable to the pure calcium hydroxide coating. Thus, copper ions are an auspicious option to enhance the antibacterial properties. Calcium hydroxide coatings presented in this thesis have promising antibacterial properties and can easily be applied to complex geometries, thus they are a step in fighting aseptic loosening and implant infections. N2 - Der Fortschritt in der modernen Medizin ist so weit, dass Hüft- und Kniegelenkersatz mit Implantaten heutzutage Standardoperationen sind. Allerdings kommt es in circa 11 % des Hüftgelenkersatzes und 7 % des Kniegelenkersatzes zu nicht zufriedenstellenden Ergebnissen und Revisionen sind nötig. Der Vergleich von Implantationsregistern zeigte zwei Hauptindikatoren für Revisionen: aseptische Lockerung und Implantatinfektionen, welche die Gesundheit der Patienten stark beeinträchtigen und eine wirtschaftliche Belastung für das Gesundheitssystem darstellen. Um diese Probleme anzugehen, wurde Calciumhydroxid auf Titan als Beschichtung aufge- bracht und in dieser Arbeit untersucht. Calciumhydroxid ist ein bekanntes antibakterielles Material und wird erfolgreich in der Zahnheilkunde eingesetzt. Die Beschichtungen wurden mit elektrochemisch gestützter Abscheidung aufgebracht, da diese Methode einen einfachen Prozess mit der Möglichkeit vereint, komplexe Geometrien homogen zu beschichten. In dieser Arbeit wurde der pH-Gradient während der Beschichtung untersucht und zeig- te die Beschränkung des Beschichtungsprozesses auf die direkte Oberfläche der Probe. Eine Vorbehandlung der Titansubstrate veränderte die Morphologie und die Chemie der Oberflä- chen und dadurch auch die Morphologie der Calciumhydroxidbeschichtung. Der Einfluss der Beschichtungsparameter Rührgeschwindigkeit und Pulsen des Stroms wurden in zahlreichen Konfigurationen und Kombinationen getestet und konnte ebenfalls die Oberflächenmorphologie verändern. Die Oberflächenmorphologie wiederum beeinflusst die Adhäsion und das Verhalten von Zellen und Bakterien. Deshalb sind die Parameter Oberflächenvorbehandlung, Rührge- schwindigkeit und Pulsen des Stroms ein Instrument für das Einstellen einer angepassten Zellantwort und der antibakteriellen Eigenschaften. Mikrobiologische Tests mit S. aureus und S. epidermidis wurden unternommen, um die Zeitabhängigkeit der antibakteriellen Aktivität auf Calciumhydroxidbeschichtungen zu bestimmen. Eine Reduktion beider Stämme konnte nach 13 h erreicht werden, was Calciumhydroxid zu einer erfolgversprechenden antibakteriellen Beschichtung macht. Um einen Einblick in das Wachstum von Biofilmen zu geben, wurde ein Protokoll zur Biofilm- Färbung auf Titanplättchen mit S. aureus und S. epidermidis entwickelt. Biofilm-Wachstum konnte nach 5 Tagen Bakterien-Inkubation detektiert werden, was sehr viel früher war als die 3 Wochen, die aktuell bei der Behandlung von Implantatinfektionen angenommen werden. Folglich muss schon nach 5 Tagen darüber nachgedacht werden, Behandlungsmethoden gegen einen Biofilm anzuwenden. Die kurzzeitigen antibakteriellen Eigenschaften von Calciumhydroxid konnten durch den Zusatz von Silber- und Kupferionen weiter verbessert und verlängert werden. Beide Ionen erhöhten die antibakterielle Wirkung signifikant. Die Kupfermodifikation zeigte dabei einen größeren antibakteriellen Effekt als die Silbermodifikation und war gleichzeitig besser zell- verträglich. Die Zytokompatibilität der Kupfermodifikation lag auf dem Niveau der reinen Calciumhydroxidbeschichtungen. Deshalb sind Kupferionen eine vielversprechende Möglichkeit für eine weitere Verbesserung der antibakteriellen Eigenschaften. Die in dieser Arbeit vorgestellten Calciumhydroxidbeschichtungen haben ein großes Potential als antibakterielle Oberflächen und können sehr leicht auch auf komplizierte Geometrien aufgebracht werden. Deshalb können sie ein entscheidender Baustein bei der Vermeidung von aseptischer Lockerung und Implantatinfektionen sein. KW - Calciumhydroxid KW - Implantat KW - Beschichtung KW - antibakteriell KW - antibacterial KW - implant KW - coating KW - calciumhydroxide Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-261122 ER - TY - JOUR A1 - El-Hawary, Seham S. A1 - Sayed, Ahmed M. A1 - Mohammed, Rabab A1 - Hassan, Hossam M. A1 - Rateb, Mostafa E. A1 - Amin, Elham A1 - Mohammed, Tarek A. A1 - El-Mesery, Mohamed A1 - Bin Muhsinah, Abdullatif A1 - Alsayari, Abdulrhman A1 - Wajant, Harald A1 - Anany, Mohamed A. A1 - Abdelmohsen, Usama Ramadan T1 - Bioactive brominated oxindole alkaloids from the Red Sea sponge Callyspongia siphonella JF - Marine Drugs N2 - In the present study, LC-HRESIMS-assisted dereplication along with bioactivity-guided isolation led to targeting two brominated oxindole alkaloids (compounds 1 and 2) which probably play a key role in the previously reported antibacterial, antibiofilm, and cytotoxicity of Callyspongia siphonella crude extracts. Both metabolites showed potent antibacterial activity against Gram-positive bacteria, Staphylococcus aureus (minimum inhibitory concentration (MIC) = 8 and 4 µg/mL) and Bacillus subtilis (MIC = 16 and 4 µg/mL), respectively. Furthermore, they displayed moderate biofilm inhibitory activity in Pseudomonas aeruginosa (49.32% and 41.76% inhibition, respectively), and moderate in vitro antitrypanosomal activity (13.47 and 10.27 µM, respectively). In addition, they revealed a strong cytotoxic effect toward different human cancer cell lines, supposedly through induction of necrosis. This study sheds light on the possible role of these metabolites (compounds 1 and 2) in keeping fouling organisms away from the sponge outer surface, and the possible applications of these defensive molecules in the development of new anti-infective agents. KW - Callyspongia siphonella KW - LC-HRESIMS KW - metabolomic profiling KW - oxindole alkaloids KW - tisindoline KW - antibacterial KW - antibiofilm KW - antitrypanosomal KW - anticancer Y1 - 2019 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-201485 VL - 17 IS - 8 ER - TY - JOUR A1 - Espina, Laura A1 - Pagán, Rafael A1 - López, Daniel A1 - García-Gonzalo, Diego T1 - Individual Constituents from Essential Oils Inhibit Biofilm Mass Production by Multi-Drug Resistant Staphylococcus aureus JF - Molecules N2 - Biofilm formation by Staphylococcus aureus represents a problem in both the medical field and the food industry, because the biofilm structure provides protection to embedded cells and it strongly attaches to surfaces. This circumstance is leading to many research programs seeking new alternatives to control biofilm formation by this pathogen. In this study we show that a potent inhibition of biofilm mass production can be achieved in community-associated methicillin-resistant S. aureus (CA-MRSA) and methicillin-sensitive strains using plant compounds, such as individual constituents (ICs) of essential oils (carvacrol, citral, and (+)-limonene). The Crystal Violet staining technique was used to evaluate biofilm mass formation during 40 h of incubation. Carvacrol is the most effective IC, abrogating biofilm formation in all strains tested, while CA-MRSA was the most sensitive phenotype to any of the ICs tested. Inhibition of planktonic cells by ICs during initial growth stages could partially explain the inhibition of biofilm formation. Overall, our results show the potential of EOs to prevent biofilm formation, especially in strains that exhibit resistance to other antimicrobials. As these compounds are food additives generally recognized as safe, their anti-biofilm properties may lead to important new applications, such as sanitizers, in the food industry or in clinical settings. KW - Listeria monocytogenes KW - carvacrol KW - strains KW - essential oils KW - anti-biofilm KW - bacterial biofilms KW - food industry KW - antibacterial KW - inactivation KW - components KW - citrus KW - biofilms KW - Staphylococcus aureus KW - (+)-limonene KW - citral Y1 - 2015 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-151845 VL - 20 SP - 11357 EP - 11372 ER - TY - THES A1 - Hösl, Daniel T1 - In vitro- Untersuchungen zur Biokompatibilität und antibakteriellen Wirksamkeit von silber-dotierten Tricalciumphosphat-Zementen T1 - In vitro- studies on the biocompatibility and antibacterial activity of silver-doped tricalcium phosphate cements N2 - Gegenstand der vorliegenden Arbeit war die Modifikation von Hydroxylapatit- und Bruschit-Zementen mit 1 % Silber. Ziel war es, den Zementen eine antibakterielle Wirksamkeit bei gleichzeitiger Biokompatibilität ohne Beeinträchtigung ihrer mechanischen Eigenschaften zu verleihen. Durch Mischung von silberdotiertem β-TCP mit Calcium-bis-dihydrogenphosphat Monohydrat (MCPM) bzw. von silberdotiertem α-TCP mit einer 2,5%-Na2HPO4-Lösung entstanden Zementformulierungen, deren Silberfreisetzung, Druckfestigkeit, Abbindezeit sowie Phasenzusammensetzung bestimmt wurde. Desweiteren wurden in vitro-Untersuchungen zur Evaluation der Zytotoxizität mittels Osteoblasten sowie der antibakteriellen Eigenschaften mittels Staph. aureus und Staph. epidermidis durchgeführt. Bei der massenspektrometrischen Analyse der Auslagerungsmedien legte Ag-Bruschit im LB-Medium mit kumulativ 184,5 µg nach 7 Tagen das höchste Freisetzungsverhalten im Vergleich zu Ag-Hydroxylapatit mit 36,8 µg an den Tag; außerdem konnte gezeigt werden, dass sich das molare Verhältnis von Ag+/Ca2+ von theoretisch 1 % bereits bei der Herstellung von Ag+-dotiertem α- bzw. β-TCP auf je 0,78 % reduziert hatte. Die Untersuchung der Phasenzusammensetzung der Zemente wies auf die für die Zemente charakteristischen Beugungsmuster hin. Peaks, die auf Silber hinweisen würden, konnten nicht nachgewiesen werden. Betrachtet man die Druckfestigkeit, konnte der silberdotierte Bruschit-Zement eine leichte Steigerung um 5,1 MPa auf 19,8 MPa erfahren, während der Ag-Hydroxylapatit-Zement nahezu eine Halbierung seiner Festigkeit um 18,5 MPa auf 22,7 MPa erfahren musste. Bei der Auswertung der Versuchsergebnisse wies Ag-Bruschit einen signifikanten bakteriziden Effekt auf, führte aber auch zu einer Reduktion der Osteoblasten auf dieser Oberfläche. Ag-Hydroxylapatit zeigte hingegen nur eine geringe Wirkung gegen die Bakterien, während die Verbindung in dieser in vitro-Studie eher biokompatibel auf die Zellen wirkte. Die in dieser Arbeit modifizierten Zemente sind aufgrund ihrer nicht einheitlichen Ergebnisse hinsichtlich der antibakteriellen Wirksamkeit sowie der wünschenswerten Biokompatibilität für den Einsatz als Knochenersatzmaterial noch nicht geeignet. Die von Ag-Bruschit freigesetzte bakterizide Silbermenge ist für eukaryotische Zellen zu hoch, sodass in weiterführenden Studien diese Freisetzung begrenzt werden müsste. N2 - The present work was the modification of hydroxyapatite and brushite cements with 1% silver. The aim was to give the cement an anti-bacterial activity simultaneously with a biocompatibility without compromising their mechanical properties. Cement formulations, of which the release of silver ions, compressive strength, setting time and phase composition were determined, emerged by mixing silver-doped β-TCP with calcium bis-dihydrogen phosphate monohydrate (MCPM) or by silver-doped α-TCP with a 2.5% Na2HPO4 solution. Furthermore, in vitro- studies were performed to evaluate the cytotoxicity by osteoblasts, and the antibacterial properties using Staph. aureus and Staph. epidermidis. In the mass spectrometric analysis of the outsourcing media, Ag brushite in LB-medium with cumulative 184.5 µg after 7 days, demonstrated the highest release behavior as compared to Ag-hydroxyapatite with 36.8 µg; it also could be shown that the molar ratio of Ag+/ Ca2+ of theoretically 1% had already reduced to 0.78% in the production of Ag+-doped α- and β-TCP. The investigation of the phase composition of the cements showed the characteristic diffraction pattern for these cements. Peaks, which would indicate silver, could not be detected. Considering the compressive strength, the silver-doped brushite cement had shown a slight increase of 5.1 MPa to 19.8 MPa, while the Ag-hydroxyapatite cement had experienced a near halving of its strength of 18.5 MPa to 22.7 MPa. When evaluating the test results, Ag-brushite presented a significant bactericidal effect, but also led to a reduction of osteoblasts on the surface. Ag-hydroxyapatite offered a little effect against the bacteria, while the compound in this in vitro- study had more biocompatible to the cells. The modified cements in this study are, due to their non-uniform results in terms of antibacterial efficacy as well as the desirable biocompatibility, not suitable for the use as a bone substitute material. The release of Ag-brushite bactericidal amount of silver for eukaryotic cells is too high, so this release should be limited in further studies. KW - Bruschit KW - Hydroxylapatit KW - Silber KW - Biokompatibilität KW - antibakteriell KW - Tricalciumphosphat KW - Knochenzement KW - brushite KW - hydroxyapatite KW - silver KW - biocompatibility KW - antibacterial Y1 - 2010 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-52383 ER -