TY - THES A1 - Kade, Juliane Carolin T1 - Expanding the Processability of Polymers for a High-Resolution 3D Printing Technology T1 - Erweiterung der Verarbeitbarkeit von Polymeren für eine hochauflösende 3D-Drucktechnologie N2 - This thesis identifies how the printing conditions for a high-resolution additive manufacturing technique, melt electrowriting (MEW), needs to be adjusted to process electroactive polymers (EAPs) into microfibers. Using EAPs based on poly(vinylidene difluoride) (PVDF), their ability to be MEW-processed is studied and expands the list of processable materials for this technology. N2 - Im Rahmen dieser Arbeit wird melt electrowriting (MEW), eine hochauflösende additive Fertigungstechnik, zur Herstellung von Polymerfasern im unteren Mikrometerbereich eingesetzt. Neue Materialien, hauptsächlich elektroaktive Polymere (EAPs) auf Basis von Poly(vinylidendifluorid) (PVDF), werden hinsichtlich ihrer Druckbarkeit untersucht, um die Liste der prozessierbaren Materialien für diese Technologie zu erweitern. KW - Polymere KW - Melt electrowriting KW - Biofabrication KW - 3D-Druck KW - 3D Printing KW - Polymers Y1 - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-270057 ER - TY - THES A1 - Hauptstein, Niklas T1 - Site directed molecular design and performances of Interferon-α2a and Interleukin-4 bioconjugates with PEG alternative polymers T1 - Seitenspezifisches molekulares Design und Eigenschaften von Interferon-α2a und Interleukin-4 Biokonjugaten mit PEG alternativen Polymeren N2 - Serum half-life elongation as well as the immobilization of small proteins like cytokines is still one of the key challenges for biologics. This accounts also for cytokines, which often have a molecular weight between 5 and 40 kDa and are therefore prone to elimination by renal filtration and sinusoidal lining cells. To solve this problem biologics are often conjugated to poly(ethylene glycol) (PEG), which is the gold standard for the so called PEGylation. PEG is a synthetic, non-biodegradable polymer for increasing the hydrodynamic radius of the conjugated protein to modulate their pharmacokinetic performance and prolong their therapeutic outcome. Though the benefits of PEGylation are significant, they also come with a prize, which is a loss in bioactivity due to steric hindrance and most often the usage of heterogeneous bioconjugation chemistries. While PEG is a safe excipient in most cases, an increasing number of PEG related side-effects, such as immunological responses like hypersensitivity and accelerated blood clearance upon repetitive exposure occur, which highlights the need for PEG alternative polymers, that can replace PEG in such cases. Another promising method to significantly prolong the residence time of biologics is to immobilize them at a desired location. To achieve this, the transglutaminase (TG) Factor XIIIa (FXIIIa), which is an important human enzyme during blood coagulation can be used. FXIIIa can recognize specific peptide sequences that contain a lysine as substrates and link them covalently to another peptide sequence, that contains a glutamine, forming an isopeptide bond. This mechanism can be used to link modified proteins, which have a N- or C-terminal incorporated signal peptide by mutation, to the extracellular matrix (ECM) of tissues. Additionally, both above-described methods can be combined. By artificially introducing a TG recognition sequence, it is possible to attach an azide group containing peptide site-specifically to the TG, recognition sequence. This allows the creation of a site-selective reactive site at the proteins N- or C-terminus, which can then be targeted by cyclooctyne functionalized polymers, just like amber codon functionalized proteins. This thesis has focused on the two cytokines human Interferon-α2a (IFN-α2a) and human, as well as murine Interleukin-4 (IL-4) as model proteins to investigate the above-described challenges. IFN-α2a has been chosen as a model protein because it is an approved drug since 1986 in systemic applications against some viral infections, as well as several types of cancer. Furthermore, IFN-α2 is also approved in three PEGylated forms, which have different molecular weights and use different conjugation techniques for polymer attachment. This turns it into an ideal candidate to compare new polymers against the gold standard PEG. Interleukin-4 (IL-4) has been chosen as the second model protein due to its similar size and biopotency. This allows to compare found trends from IFN-α2a with another bioconjugate platform and distinguish between IFN-α2a specific, or general trends. Furthermore, IL-4 is a promising candidate for clinical applications as it is a potent anti-inflammatory protein, which polarizes macrophages from the pro-inflammatory M1 state into the anti-inflammatory M2 state. N2 - Die Verlängerung der Serum-Halbwertszeit sowie die Immobilisierung kleiner Proteine wie Zytokine ist nach wie vor eine der größten Herausforderungen für Biologika. Dies gilt auch für Zytokine, die häufig ein Molekulargewicht zwischen 5 und 40 kDa haben und daher leicht durch die Nierenfiltration und sinusoidale Endothelzellen eliminiert werden können. Um dieses Problem zu lösen, werden Biologika häufig an Poly(ethylenglykol) (PEG) konjugiert, das den Goldstandard für die so genannte PEGylierung darstellt. PEG ist ein synthetisches, biologisch nicht abbaubares Polymer, das den hydrodynamischen Radius des konjugierten Proteins vergrößert, um die pharmakokinetische Leistung zu modulieren und die therapeutische Wirkung zu verlängern. Obwohl die Vorteile der PEGylierung beträchtlich sind, haben sie auch ihren Preis, nämlich einen Verlust an Bioaktivität aufgrund sterischer Hindernisse und meist die Verwendung heterogener Biokonjugationstechniken. Obwohl PEG in den meisten Fällen ein sicherer Hilfsstoff ist, treten immer mehr PEG-bedingte Nebenwirkungen auf, wie z. B. immunologische Reaktionen wie Überempfindlichkeit und beschleunigter Abbau bei wiederholter Exposition, was den Bedarf an alternativen PEG-Polymeren unterstreicht, die PEG in solchen Fällen ersetzen können. Eine weitere vielversprechende Methode, um die Verweildauer von Biologika deutlich zu verlängern, besteht darin, sie an einem gewünschten Ort zu immobilisieren. Dazu kann die Transglutaminase (TG) Faktor XIIIa (FXIIIa) verwendet werden, die ein wichtiges menschliches Enzym bei der Blutgerinnung ist. FXIIIa kann bestimmte Peptidsequenzen, die ein Lysin enthalten, als Substrate erkennen und sie kovalent an eine andere Peptidsequenz, die ein Glutamin enthält, binden, wobei eine Isopeptidbindung entsteht. Dieser Mechanismus kann benutzt werden um modifizierte Proteine, welche durch Mutation ein N- oder C-terminal eingebautes Signalpeptid besitzen, mit der extrazellularen Gewebematrix (ECM) zu verknüpfen. Diese Arbeit konzentriert sich auf die beiden Zytokine humanes Interferon-α2a (IFN-α2a) und humanes sowie murines Interleukin-4 (IL-4) als Modellproteine, um die oben beschriebenen Herausforderungen zu untersuchen. IFN-α2a wurde als Modellprotein ausgewählt, weil es seit 1986 ein zugelassenes Medikament für die systemische Anwendung gegen einige Virusinfektionen und verschiedene Krebsarten ist. Darüber hinaus ist IFN-α2 auch in drei PEGylierten Formen zugelassen, die unterschiedliche Molekulargewichte haben und verschiedene Konjugationstechniken für die Polymeranbindung verwenden. Dies macht es zu einem idealen Kandidaten für den Vergleich neuer Polymere mit dem Goldstandard PEG. Interleukin-4 (IL-4) wurde als zweites Modellprotein gewählt, da es eine ähnliche Größe und Biopotenz aufweist. Dies ermöglicht es, die von IFN-α2a gefundenen Trends mit einer anderen Biokonjugat-Plattform zu vergleichen und zwischen IFN-α2a-spezifischen und allgemeinen Trends zu unterscheiden. Darüber hinaus ist IL-4 ein vielversprechender Kandidat für klinische Anwendungen, da es ein starkes entzündungshemmendes Protein ist, das Makrophagen vom entzündungsfördernden M1-Zustand in den entzündungshemmenden M2-Zustand polarisiert. KW - Cytokine KW - Interferon KW - Konjugation KW - Polymere KW - Interleukin 4 KW - Bioconjugate KW - Polyglycerol KW - poly(2-ethyl-2-oxazoline) KW - Polyethylenglykole Y1 - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-296911 ER - TY - THES A1 - Selby, Joshua T1 - Design and Chiroptical Properties of Chirally Substituted Indolenine Squaraine Mono-, Oligo-, and Polymers T1 - Design und chiroptische Eigenschaften von chiral substituierten Indolenin-Squarain-Mono-, Oligo- und Polymeren N2 - A series of monomeric chirally substituted indolenine squaraine monomers were successfully synthesized and utilized for the construction of various oligo- and polymers, in order to study their chiroptical properties in terms of exciton chirality. The quaternary carbon atom at the 3-position of the indolenine subunit, as well as the alkyl side chain attached to the indolenine nitrogen were selected as the most suitable site for chiral functionalization. For the C(3)-chiral derivatives, two synthetic routes depending on the desired substitution at the stereogenic center were established. The chiral side chains were prepared via Evans asymmetric alkylation where the resulting branching point at the 2 position constituted the chiral center. While the chiral substitution only had minor effects on the linear optical properties and geometric structure of the chromophore, all compounds exhibited a distinct and measurable CD signal that correlated with the distance of the chiral center to the central chromophore. Polymers bearing chiral side chains exhibited a solvent- and temperature-dependent helix-coil equilibrium, which was influenced by the type of side chain used. CD spectroscopy revealed the helical conformation to possess a preferred twist sense, and temperature-dependent measurements showed the degree of homohelicity to be nearly complete in certain cases. Furthermore, a CPL signal was able to be obtained for the helical conformer of one polymer. Various (co)oligo- and polymers comprising the C(3)-chiral monomers only displayed a solvent-independent J-type absorption behavior and thus did not form helical conformations in solution. CD spectroscopy revealed a solvent-dependent adoption of quasi-enantiomeric conformers, which was elucidated by quantum chemical TDDFT calculations. N2 - Eine Reihe von monomeren, chiral substituierten Indolenin-Squarain-Monomeren wurde erfolgreich synthetisiert und für die Konstruktion verschiedener Oligo- und Polymere verwendet, um ihre chiroptischen Eigenschaften in Bezug auf die Exzitonenchiralität zu untersuchen. Als geeignete Stelle für die chirale Funktionalisierung wurden das quartäre Kohlenstoffatom an der 3-Position der Indolenineinheit sowie die an den Indolenin- Stickstoff gebundene Alkylseitenkette ausgewählt. Für die C(3)-chiralen Derivate wurden je nach gewünschter Substitution am stereogenen Zentrum zwei Synthesrouten etabliert. Die chiralen Seitenketten wurden über eine asymmetrische Evans-Alkylierung synthetisiert, wobei der resultierende Verzweigungspunkt an der 2-Position das chirale Zentrum darstellte. Während die chirale Substitution nur geringe Auswirkungen auf die linearen optischen Eigenschaften und die geometrische Struktur des Chromophors hatte, zeigten alle Verbindungen ein deutliches und messbares CD-Signal, das mit dem Abstand des chiralen Zentrums zum zentralen Chromophor korrelierte. Polymere mit chiralen Seitenketten zeigten ein lösungsmittel- und temperaturabhängiges Helix-Knäuel-Gleichgewicht, das durch die Art der verwendeten Seitenkette beeinflusst wurde. Durch CD Spektroskopie konnte gezeigt werden, dass die helikale Konformation einen bevorzugten Drehsinn besitzt. Temperaturabhängige CD Messungen zeigten, dass der Grad der Homohelizität in bestimmten Fällen nahezu vollständig ist. Weiterhin konnte für das helikale Konformer eines Polymers ein CPL-Signal erhalten werden. Verschiedene (Co)oligo- und Polymere bestehend aus den C(3)-chiralen Monomere zeigten nur ein lösungsmittelunabhängiges J- Typ Absorptionsverhalten und bildeten daher in Lösung keine helikalen Konformationen. CD-Spektroskopie zeigte eine lösungsmittelabhängige Annahme von quasi-enantiomeren Konformationen, was durch quantenchemische TDDFT-Rechnungen aufgeklärt wurde. KW - Squaraine KW - Oligomere KW - Polymere KW - Chiralität KW - Chemische Synthese KW - Asymmetrische Synthese KW - CD-Spektroskopie KW - Helix-Knäuel-Umwandlung KW - J- and H-Aggregate KW - Asymmetric synthesis KW - Helix-Coil-Transition KW - J- and H-Aggregates KW - Circular dichroism Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-282067 ER - TY - THES A1 - Macher, Sven T1 - On the Effects of Moisture on Polymer-Based Electrochromic Devices T1 - Über die Auswirkung von Feuchtigkeit auf Polymer-basierte Elektrochrome Elemente N2 - The present work builds on a conjugated electrochromic polymer with a highly transmissive and colorless bright state and its application in electrochromic devices. The main body of this work focuses on the investigation of the influence of moisture on electrochromic devices and solutions to overcome possible degradation of these devices due to moisture ingress. Firstly, a series of EDOT derivatives with a terminal double bond in the lateral sidechain to potentially achieve a highly transmissive and fully colorless bright state was investigated. All of the EDOT derivatives were electrochemically polymerized and characterized by means of (in-situ) spectroelectrochemistry. The results highlight the dramatic influence of the terminal double bond on the improved visible light transmittance and color neutrality in the bright state. After detailed evaluation and comparison, the best performing compound, which contains a hexenyl sidechain (PEDOT-EthC6), was scaled-up by changing the deposition technique from an electrochemical to a chemical in-situ polymerization process on a R2R-pilot line in an industrially relevant environment. The R2R-processed PEDOTEthC6 half-cells were characterized in detail and provide enhanced electrochromic properties in terms of visible light transmittance and color neutrality in the bright state as well as short response times, improved contrast ratio, coloration efficiency and cycling stability (10 000 cycles).[21] In a second step, the novel PEDOT-EthC6 electrochromic polymer was combined with a Prussian Blue counter electrode and a solid polymer electrolyte to form an all-solid-sate ECDs based on complementary switching electrodes and PET-ITO as flexible substrates. The fabricated ECDs were optically and spectroelectrochemically characterized. Excellent functionality of the S2S-processed flexible ECDs was maintained throughout 10 000 switching cycles under laboratory conditions. The ECDs offer enhanced electrochromic properties in terms of visible light transmittance change and color neutrality in the bright state as well as contrast ratio, coloration efficiency, cycling stability and fast response times. Furthermore, the final device assembly was transferred from a S2S-process to a continuous R2R-lamination process.[238] In a third step, the PEDOT-EthC6/PB-based ECDs were submitted to conscious environmental aging tests. The emphasis of the research presented in this work, was mainly put at the influence of moisture and possible failure mechanisms regarding the PEDOT-EthC6/PB based ECDs. An intense brown coloration of the electrodes was observed while cycling the ECDs in humid atmospheres (90% rH) as a major degradation phenomenon. The brown coloration and a thereby accompanied loss of conductivity of the PET-ITO substrates was related to significant degradation of the ITO layers, inserted as the conductive layers in the flexible ECDs. A dissolution of the ITO thin films and formation of metallic indium particles on the surface of the ITO layers was observed that harmed the cycling stability enormously. The conductive layers of the aged ECDs were investigated by XRD, UV-Vis, SEM and spectroelectrochemical measurements and validated the supposed irreversible reduction of the ITO layers.[279] In the absence of reasonable alternatives to PET-ITO for flexible (R2R-processed) ECDs, it is also important to investigate measures to avoid the degradation of ECDs. This is primarily associated with the avoidance of appropriate electrode potentials necessary for ITO reduction in humid atmospheres. As an intrinsic action point, the electrode potentials were investigated via electrochemical measurements in a three-electrode setup of an all-solid-state ECD. Extensive knowledge on the electrode potentials allowed the voltage-induced degradation of the ITO in flexible ECDs to be avoided through the implementation of an unbalanced electrode configuration (charge density ratio of working and counter electrode). It was possible to narrow the overall operational voltage window to an extent in which irreversible ITO reduction no longer occurs. The unbalanced electrode configuration lead to an improved cycling stability without harming other characteristics such as response time and light transmittance change and allows ECD operation in the presence of humidity.[279] The avoidance of the mentioned degradation phenomena is further associated with appropriate sealing methods and materials as well as appropriate electrode and device fabrication processes. Since a variety of sealing materials is commercially available, due to the commercial launch of organic photovoltaic (OPV) and light emitting diodes (OLEDs), the focus in the present work was put to water-free electrode fabrication. As an extrinsic action point, a novel preparation method of a nanoscale PEDOT-EthC6 dispersion based on organic solvents is presented here in a final step. The water-free processing method gives access to straightforward printing and coating processes on flexible PET-ITO substrates and thus represents a promising and simplified alternative to the established PEDOT:PSS. The resulting nano-PEDOT-EthC6 thin films exhibit enhanced color neutrality and transmissivity in the bright state and are comparable to the properties of the in-situ polymerized PEDOT-EthC6 thin films.[280] N2 - Die vorliegende Arbeit beruht auf einem konjugierten elektrochromen Polymer mit hochtransmissivem und farblosem Hellzustand sowie dessen Anwendung in elektrochromen Elementen. Der Hauptteil die-ser Arbeit konzentriert sich auf den Einfluss von Feuchtigkeit auf elektrochrome Elemente sowie Lösun-gen, um einer möglichen Degradation dieser Systeme aufgrund der Einwirkung von Feuchtigkeit entge-genzuwirken. In einem ersten Schritt wurde eine Reihe von EDOT-Derivaten mit terminalen Doppelbindung in einer lateralen Seitenkette untersucht, um einen hochtransmissiven und vollständig farblosen Hellzustand zu erreichen. Alle EDOT-Derivate wurden elektrochemisch polymerisiert und mittels (in-situ) spektroelekt-rochemischer Messungen charakterisiert. Die Ergebnisse unterstreichen den dramatischen Einfluss der terminalen Doppelbindung auf die verbesserte Transmission und Farbneutralität im Hellzustand. Nach einer detaillierten Bewertung und entsprechendem Vergleich wurden die Dünnschichten der Verbin-dung mit den besten Eigenschaften, welche eine Hexenylseitenkette (PEDOT-EthC6) enthält, hochska-liert. Dazu wurde die elektrochemische Abscheidung durch einen chemischen in-situ-Polymerisationsprozess ersetzt. Dies ermöglicht die Abscheidung elektrochromer Dünnschichten im großen Maßstab auf einer R2R-Beschichtungsanlage. Die mittels R2RBeschichtung abgeschiedenen PE-DOT-EthC6-Dünnschichten wurden daraufhin detailliert charakterisiert und zeigen verbesserte elektro-chrome Eigenschaften hinsichtlich visueller Transmission und Farbneutralität im Hellzustand, kurze Schaltzeiten, ein verbessertes Kontrastverhältnis sowie verbesserte Färbeeffizienz und Zyklenstabilität (10 000 Zyklen).[21] Im zweiten Schritt wurden PEDOT-EthC6-Halbzellen mit Preußisch Blau-Gegenelektroden und einem festen Polymerelektrolyten kombiniert und ein Festkörper- ECD auf Basis koplementär-färbender Elekt-roden und flexiblen PET-ITO-Substraten realisiert. Die hergestellten ECDs wurden optisch und (spektro-)elektrochemisch charakterisiert. Die Funktionalität der S2S-assemblierten flexiblen ECDs wurde über 10 000 Schaltzyklen unter Laborbedingungen getestet. Die ECDs bieten verbesserte elektrochrome Eigenschaften hinsichtlich der visuellen Transmission und Farbneutralität im Hellzustand sowie des Kon-trastverhältnisses, der Färbeeffizienz, Zyklenstabilität und Schaltzeit. Darüber hinaus wurde die S2S-Laminierung der ECDs in einen kontinuierlichen R2R-Laminierprozess übertragen.[238] Dann wurden die PEDOT-EthC6/PB-basierten ECDs kontrollierten Alterungstests unterzogen. Der Schwerpunkt dieser Arbeit lag hauptsächlich auf dem Einfluss von Feuchtigkeit und den daraus resultie-renden Degradationsmechanismen des PEDOT-EthC6/PB-Systems. Während die ECDs in feuchter At-mosphäre (90 % rH) zyklisiert wurden, konnte eine intensive Braunfärbung der Elektroden beobachtet werden. Die braune Färbung und ein damit einhergehender Verlust der Leitfähigkeit wurde auf eine signifikante Degradation der ITO-Schichten zurückgeführt, die als leitfähige Schichten in den flexiblen ECDs Verwendung fanden. Die Auflösung der ITO-Dünnschichten sowie die Bildung von metallischen Indiumpartikeln auf der Oberfläche der ITO-Schichten wurde beobachtet und als Ursache für die ver-minderte Zyklenstabilität herangezogen. Die leitfähigen Schichten der gealterten ECDs wurden durch XRD-, UV-Vis-, REM- und (spektro-) elektrochemische Messungen untersucht und die vermutete irre-versible Reduktion der ITO- Schichten bestätigt.[279] Mangels Alternativen zu PET-ITO für flexible (R2R-prozessierte) ECDs ist es wichtig, Maßnahmen zur Vermeidung der Degradation von ECDs zu untersuchen. Dies ist in erster Linie mit der Vermeidung ge-eigneter Elektrodenpotentiale verbunden, die für die Reduktion von ITO in feuchter Atmosphäre erfor-derlich sind. Als intrinsische Maßnahme wurden die Elektrodenpotentiale durch elektrochemische Mes-sungen in einem Drei-Elektroden-Aufbau eines Festkörper-ECD untersucht. Aufgrund der umfassende Kenntnis der Elektrodenpotentiale konnte die spannungsinduzierte Degradation der enthaltenen ITO-Schichten durch die Implementierung einer unbalancierten Elektrodenkonfiguration (Ladungsdichte-verhältnis von Arbeits- und Gegenelektrode) vermieden werden. Es war dadurch möglich, das gesamte Spannungsfenster zum Betrieb des ECD so weit einzuschränken, dass keine irreversible ITO-Reduktion mehr auftrat. Die unbalancierte Elektrodenkonfiguration führt zu einer verbesserten Zyklenstabilität, ohne andere Eigenschaften wie Schaltzeit oder visuellen Transmissionshub zu beeinträchtigen und er-möglicht daher den Betrieb von ECDs auch in feuchter Atmosphäre.[279] Die Vermeidung der genannten Degradationsphänomene ist ferner mit geeigneten Versiegelungsver-fahren und -materialien sowie geeigneten Elektroden- und Assemblierungsverfahren möglich. Da auf-grund der kommerziellen Einführung von organischer Photovoltaik (OPV) und organischer Leuchtdio-den (OLEDs) eine Vielzahl von Versiegelungsmaterialien kommerziell erhältlich ist, lag der Schwerpunkt der vorliegenden Arbeit auf der Herstellung wasserfreier Elektroden. Als extrinsische Maßnahme wurde in einem letzten Schritt eine neuartige Herstellungsmethode für eine nanoskaligen PEDOT-EthC6-Dispersion auf Basis organischer Lösungsmittel entwickelt. Die wasserfreie Verarbeitungsmethode er-möglicht einfache Druck- und Beschichtungsprozesse auf flexiblen PET-ITO-Substraten und stellt somit eine vielversprechende und vereinfachte Alternative zu etabliertem PEDOT:PSS dar. Die resultierenden PEDOT-EthC6-Schichten zeigen im Hellzustand ebenfalls eine verbesserte Farbneutralität sowie visuelle Transmission und sind vergleichbar mit den Eigenschaften der in-situ-polymerisierten PEDOT-EthC6-Schichten.[280] KW - Elektrochromie KW - conjugated electrochromic polymers KW - electrochromic device KW - Elektrochemie KW - Polymere Y1 - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-242407 ER - TY - THES A1 - Nahm, Daniel T1 - Poly(2-oxazine) Based Biomaterial Inks for the Additive Manufacturing of Microperiodic Hydrogel Scaffolds T1 - Poly(2-oxazine) Basierte Biomaterialtinten für die Additive Fertigung von Mikroperiodischen Hydrogelstrukturen N2 - The aim of this thesis was the preparation of a biomaterial ink for the fabrication of chemically crosslinked hydrogel scaffolds with low micron sized features using melt electrowriting (MEW). By developing a functional polymeric material based on 2-alkyl-2-oxazine (Ozi) and 2-alkyl-2-oxazoline (Ox) homo- and copolymers in combination with Diels-Alder (DA)-based dynamic covalent chemistry, it was possible to achieve this goal. This marks an important step for the additive manufacturing technique melt electrowriting (MEW), as soft and hydrophilic structures become available for the first time. The use of dynamic covalent chemistry is a very elegant and efficient method for consolidating covalent crosslinking with melt processing. It was shown that the high chemical versatility of the Ox and Ozi chemistry offers great potential to control the processing parameters. The established platform offers straight forward potential for modification with biological cues and fluorescent markers. This is essential for advanced biological applications. The physical properties of the material are readily controlled and the potential for 4D-printing was highlighted as well. The developed hydrogel architectures are excellent candidates for 3D cell culture applications. In particular, the low internal strength of some of the scaffolds in combination with the tendency of such constructs to collapse into thin strings could be interesting for the cultivation of muscle or nerve cells. In this context it was also possible to show that MEW printed hydrogel scaffolds can withstand the aspiration and ejection through a cannula. This allows the application as scaffolds for the minimally invasive delivery of implants or functional tissue equivalent structures to various locations in the human body. N2 - Das Ziel dieses Projekts war die Herstellung einer Biomaterialtinte, welche die Herstellung chemisch vernetzter, mikrostrukturierter Hydrogelgerüste mittels Melt Electrowriting (MEW) ermöglicht. Die Verwendung von speziell auf den schmelzbasierten 3D Druck angepassten polyoxazinbasierten Polymeren und die Anwendung von dynamisch kovalenter Chemie ermöglichte es, dieses Ziel zu erreichen. Dies ist ein wichtiger Schritt für die aufstrebende, additive Fertigungstechnologie MEW, da nun erstmals weiche und hydrophile Strukturen erzeugt werden können. Speziell die Verwendung der dynamischen Diels-Alder (DA) Chemie ist ein effizienter Weg, die Fertigung von kovalent vernetzten Strukturen mit der Schmelzprozessierung zu vereinen. Es wurde weiterhin gezeigt, dass die hier etablierte Materialplattform die Möglichkeit zur Modifikation mit biologischen und chemischen Signalen bietet. Dies ist besonders für biologische Anwendungen unerlässlich. Die physikalisch-chemischen Eigenschaften des Materials lassen sich leicht auf potentielle Anwendungen anpassen und das Potential für den 4D Druck wurde ebenfalls hervorgehoben. Alles in Allem legt diese Arbeit den Grundstein für eine Vielzahl von verschiedenen Anwendungen sowohl in der Biomedizin als auch in anderen Bereichen. KW - Polymere KW - Ringöffnungspolymerisation KW - Biomaterial KW - 3D-Druck KW - biofabrication KW - poly(2-oxazoline)s KW - poly(2-oxazine)s KW - ring-opening polymerization Y1 - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-245987 ER - TY - THES A1 - Liebscher [geb. Blöhbaum], Julia T1 - Side chain functional poly(2-oxazoline)s for biomedical applications T1 - Seitenkettenfunktionalisierte Poly(2-oxazoline) für biomedizinische Anwendungen N2 - The aim of the thesis was to develop water soluble poly(2-oxazoline) (POx) copolymers with new side group functionalities, which can be used for the formation of hydrogels in biomedical applications and for the development of peptide-polymer conjugates. First, random copolymers of the monomer MeOx or EtOx with ButEnOx and EtOx with DecEnOx were synthesized and characterized. The vinyl functionality brought into the copolymer by the monomers ButEnOx and DecEnOx would later serve for post-polymerization functionalization. The synthesized copolymers were further functionalized with thiols via post-polymerization functionalization using a newly developed synthesis protocol or with a protected catechol molecule for hydrogel formation. For the formation of peptide-polymer conjugates, a cyclic thioester, namely thiolactone acrylamide and an azlactone precursor, whose synthesis was newly developed, were attached to the side chain of P(EtOx-co-ButEnOx) copolymers. The application of the functionalized thiol copolymers as hydrogels using thiol-ene chemistry for cross-linking was demonstrated. The swelling behavior and mechanical properties were characterized. The hydrophilicity of the network as well as the cross-linking density strongly influenced the swelling behavior and the mechanical strength of the hydrogels. All hydrogels showed good cell viability results. The hydrogel networks based on MeOx and EtOx were loaded with two dyes, fluorescein and methylene blue. It was observed that the uptake of the more hydrophilic dye fluorescein depended more on the ability of the hydrogel to swell. In contrast, the uptake of the more hydrophobic dye methylene blue was less dependent on the swelling degree, but much more on the hydrophilicity of the network. For the potential application as cartilage glue, (biohybrid) hydrogels were synthesized based on the catechol-functionalized copolymers, with and without additional fibrinogen, using sodium periodate as the oxidizing agent. The system allowed for degradation due to the incorporated ester linkages at the cross-linking points. The swelling behavior as well as the mechanical properties were characterized. As expected, hydrogels with higher degrees of cross-linking showed less swelling and higher elastic modulus. The addition of fibrinogen however increased the elasticity of the network, which can be favorable for the intended application as a cartilage glue. Biological evaluation clearly demonstrated the advantage of degradable ester links in the hydrogel network, where chondrocytes were able to bridge the artificial gap in contrast to hydrogels without any ester motifs. Lastly, different ways to form peptide-polymer conjugates were presented. Peptides were attached with the thiol of the terminal cysteine group to the vinyl side chain of P(EtOx-co-ButEnOx) copolymers by radical thiol-ene chemistry. Another approach was to use a cyclic thioester, thiolactone, or an azlactone functionality to bind a model peptide via native chemical ligation. The two latter named strategies to bind peptides to POx side chains are especially interesting as one and in the case of thiolactone two free thiols are still present at the binding site after the reaction, which can, for example, be used for further thiol-ene cross-linking to form POx hydrogels. In summary, side functional poly(oxazoline) copolymers show great potential for numerous biomedical applications. The various side chain functionalities can be introduced by an appropriate monomer or by post-polymerization functionalization, as demonstrated. By their multi-functionality, hydrogel characteristics, such as cross-linking degree and mechanical strength, can be fine-tuned and adjusted depending on the application in the human body. In addition, the presented chemoselective and orthogonal reaction strategies can be used in the future to synthesize polymer conjugates, which can, for example, be used in drug delivery or in tissue regeneration. N2 - Das Ziel der Arbeit war es, wasserlösliche Poly(2-oxazolin) (POx) Copolymere mit neuen Seitenkettenfunktionalitäten zu entwickeln, welche zur Synthese von Hydrogelen für biomedizinische Anwendungen und zur Entwicklung von Peptid-Polymer Konjugaten genutzt werden können. Zunächst wurden Copolymere aus den Monomeren MeOx oder EtOx mit ButEnOx und EtOx mit DecEnOx synthetisiert und anschließend charakterisiert. Die Monomere wurden statistisch miteinander copolymerisiert, indem sie zusammen zum Start der Reaktion in das Reaktionsgefäß gegeben wurden. Die Vinyl Funktionalität, die durch die Monomere ButEnOx und DecEnOx eingebracht wurde, kann später zur nachträglichen Funktionalisierung am Polymer verwendet werden. Die synthetisierten Copolymere wurden weiterhin mit Thiolen oder mit funktionellen Catecholgruppen ausgestattet, um Hydrogele herzustellen. Um Peptid-Polymer Konjugate zu bilden, wurden zyklische Thioester, genauer Thiolacton acrylamid und ein Azlacton Präkursor, dessen Synthese neu entwickelt wurde, an die Seitenkette von P(EtOx-co-ButEnOx) Copolymere angebunden. Im Folgenden wurde die Anwendung der thiol funktionalisierten Copolymere als Hydrogele, welche mittels radikalischer Thiol-ene Chemie vernetzt wurden, präsentiert. Das Quellverhalten und die mechanischen Eigenschaften wurden analysiert. Sowohl die Hydrophilie des Netzwerkes als auch die Vernetzungsdichte beeinflusste das Quellverhalten und die mechanische Festigkeit stark. Alle Hydrogele zeigten gute Zellverträglichkeit. Die Hydrogele basierend auf MeOx und EtOx wurden außerdem mit den Farbstoffen Fluorescein und Methylenblau beladen. Es wurde beobachtet, dass von den beiden Farbstoffen die Aufnahme des hydrophileren Farbstoffs Fluorescein stärker vom Quellungsgrad des Hydrogels abhing. Hingegen war die Aufnahme des hydrophoberen Farbstoffs Methylenblau weniger davon abhängig wie sehr das Hydrogel quellen konnte, sondern stärker von der Hydrophilie des Hydrogel-Netzwerkes. Um die potenzielle Anwendung als Knorpelkleber zu testen, wurden (biohybrid) Hydrogele basierend auf Catechol-funktionalisiertem Copolymeren mit und ohne zusätzliches Fibrinogen und dem Oxidationsmittel Natriumperiodat hergestellt. Das System war durch die eingebauten Ester Vernetzungspunkte abbaubar. Das Quellverhalten und die mechanischen Eigenschaften wurden charakterisiert. Wie zu erwarten, zeigten Hydrogele mit stärkerer Vernetzung eine geringe Quellung und einen höheren elastischen Modulus. Die Zugabe von Fibrinogen jedoch erhöhte die Elastizität des Netzwerkes, welches förderlich für die avisierte Anwendung als Knorpelkleber sein kann. Die biologische Auswertung zeigte, dass die Ester-haltigen, abbaubaren Vernetzungspunkte von großem Vorteil sind. Die Chondrozyten konnten ohne Probleme den Defektspalt überbrücken, was nicht möglich war, sobald keine Ester Funktionalitäten im Hydrogel eingebunden waren. Zuletzt wurden verschiedene Möglichkeiten Peptid-Polymer Konjugate zu synthetisieren präsentiert. Zum einen wurden Peptide mit der Thiolgruppe des endständigen Cysteins an die Vinyl Seitenkette der P(EtOx-co-ButEnOx) Copolymere mittels radikalischer Thiol-en Chemie angebunden. Des Weiteren wurde ein zyklischer Thioester, das Thiolacton, und eine Azlacton Funktionalität verwendet, um ein Modell Peptid mittels nativer chemischer Ligation zu binden. Die zwei zuletzt genannten Strategien, um Peptide an Polymere zu binden, sind besonders interessant, da hier ein beziehungsweise im Fall der Thiolacton Funktionalität zwei freie Thiole an der Bindungsstelle nach der Reaktion entstehen. Diese könnten genutzt werden, um zum Beispiel über Thiol-en Chemie Peptid-haltige Hydrogele herzustellen. Zusammenfassend zeigen seitenkettenfunktionale Poly(oxazolin) Copolymere ein großes Potenzial für biomedizinische Anwendungen. Die vielen verschiedenen Seitenkettenfunktionalitäten können durch das passende Monomer oder durch Post-Polymerisationsfunktionalisierung eingebracht werden, wie in dieser Arbeit gezeigt. Durch ihre Multifunktionalität können Hydrogel Charakteristika, wie der Vernetzungsgrad und die mechanische Festigkeit, fein eingestellt und angepasst werden, je nach Anwendungsbereich im menschlichen Körper. Die entwickelten chemoselektiven und orthogonalen Reaktionswege können in der Zukunft genutzt werden, um Polymer Konjugate zu synthetisieren, welche zum Beispiel für das Drug Delivery oder im Bereich der Geweberegneration zum Einsatz kommen. KW - Polymere KW - Ringöffnungspolymerisation KW - Hydrogel KW - hydrogel KW - poly(2-oxazoline)s KW - ring-opening polymerization KW - polymer-peptide-conjugate KW - thiol-ene KW - Dihydrooxazole Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-203960 ER - TY - THES A1 - Lübtow, Michael M. T1 - Structure-property relationships in poly(2-oxazoline)/poly(2-oxazine) based drug formulations T1 - Struktur-Eigenschafts-Beziehungen in Poly(2-oxazolin)/Poly(2-oxazin) basierten Wirkstoffformulierungen N2 - According to estimates, more than 40% of all new chemical entities developed in pharmaceutical industry are practically insoluble in water. Naturally, the demand for excipients which increase the water solubility and thus, the bioavailability of such hydrophobic drugs is enormous. Poly(2-oxazoline)s (POx) are currently intensively discussed as highly versatile class of biomaterials. Although selected POx based micellar drug formulations exhibit extraordinarily high drug loadings > 50 wt.% enabling high anti-tumor efficacies in vivo, the formulation of other hydrophobic compounds has failed. This casts doubt on the general understanding in which a hydrophobic active pharmaceutical ingredient is dissolved rather unspecifically in the hydrophobic core of the micelles following the fundamental concept of “like dissolves like”. Therefore, a closer look at the interactions between all components within a formulation becomes increasingly important. To do so, a large vehicle platform was synthesized, loaded with various hydrophobic drugs of different structure, and the formulations subsequently characterized with conventional and less conventional techniques. The obtained in-depth insights helped to develop a more thorough understanding about the interaction of polymer and incorporated API finally revealing morphologies deviating from a classical core/shell structure. During these studies, the scarcely investigated polymer class of poly(2-oxazine)s (POzi) was found as promising drug-delivery vehicle for hydrophobic drugs. Apart from this fundamental research, the anti-tumor efficacy of the two APIs curcumin and atorvastatin has been studied in more detail. To increase the scope of POx and POzi based formulations designed for intravenous administration, a curcumin loaded hydrogel was developed as injectable drug-depot. N2 - Schätzungen zufolge sind mehr als 40% aller „new chemical entities“, welche in der pharmazeutischen Industrie entwickelt werden, wasserunlöslich. Aus diesem Grund ist der Bedarf an Zusatzstoffen, welche die Wasserlöslichkeit und dadurch die Bioverfügbarkeit erhöhen, enorm. Poly(2-oxazolin)e (POx) werden derzeitig intensiv als vielseitig einsetzbare Biomaterialien untersucht. Obwohl bestimmte POx basierte, mizellare Wirkstoffformulierungen außergewöhnlich hohe Beladungskapazitäten > 50 Gew.% aufwiesen und dadurch ausgeprägte anti-Tumor Effektivität in vivo ermöglichten, schlug die Formulierung anderer hydrophober Stoffe fehl. Dies lässt Zweifel an dem altbewährten Konzept aufkommen, in welchem hydrophobe Arzneistoffe mehr oder weniger unspezifisch im hydrophoben Kern einer Mizelle gelöst werden. Aus diesem Grund ist ein genauerer Blick auf die Interaktionen zwischen allen Bestandteilen einer Formulierung vonnöten. Deshalb wurde eine große Polymerplattform synthetisiert, mit verschiedenen hydrophoben Wirkstoffen unterschiedlicher Struktur beladen und die Formulierungen im Anschluss mit herkömmlichen und weniger herkömmlichen Methoden charakterisiert. Die daraus erhaltenen Einblicke ermöglichten es ein umfassenderes Verständnis über die Interaktionen von Polymer und Wirkstoff zu entwickeln. Innerhalb dieser Studien wurden Aggregate charakterisiert, welche von einer klassischen Kern/Schale Morphologie abwichen. Des Weiteren konnte die kaum erforschte Polymerklasse der Poly(2-oxazin)e (POzi) als vielversprechende Wirkstoffträgerplattform für hydrophobe Wirkstoffe charakterisiert werden. Von dieser Grundlagenforschung abgesehen, wurde die anti-Tumor Effektivität von Curcumin und Atorvastatin Nanoformulierungen untersucht. Um den Anwendungsbereich der POx und POzi basierten Wirkstoffformulierungen, welche für intravenöse Verabreichung entwickelt wurden, zu erweitern, wurde ein Curcumin beladenes Hydrogel als injizierbares Wirkstoffdepot entwickelt. KW - Polymere KW - Nanomedizin KW - Wirkstoff-Träger-System KW - Ringöffnungspolymerisation KW - Hydrogel KW - Drug-Polymer Interactions KW - Poly(2-oxazoline) KW - Poly(2-oxazine) Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-193387 ER - TY - THES A1 - Lorson, Thomas T1 - Novel Poly(2-oxazoline) Based Bioinks T1 - Neuartige Poly(2-oxazolin) Basierte Biotinten N2 - Motivated by the great potential which is offered by the combination of additive manufacturing and tissue engineering, a novel polymeric bioink platform based on poly(2 oxazoline)s was developed which might help to further advance the young and upcoming field of biofabrication. In the present thesis, the synthesis as well as the characteristics of several diblock copolymers consisting of POx and POzi have been investigated with a special focus on their suitability as bioinks. In general, the copolymerization of 2-oxazolines and 2-oxazines bearing different alkyl side chains was demonstrated to yield polymers in good agreement with the degree of polymerization aimed for and moderate to low dispersities. For every diblock copolymer synthesized during the present study, a more or less pronounced dependency of the dynamic viscosity on temperature could be demonstrated. Diblock copolymers comprising a hydrophilic PMeOx block and a thermoresponsive PnPrOzi block showed temperature induced gelation above a degree of polymerization of 50 and a polymer concentration of 20 wt%. Such a behavior has never been described before for copolymers solely consisting of poly(cyclic imino ether)s. Physically cross linked hydrogels based on POx b POzi copolymers exhibit reverse thermal gelation properties like described for solutions of PNiPAAm and Pluronic F127. However, by applying SANS, DLS, and SLS it could be demonstrated that the underlying gel formation mechanism is different for POx b POzi based hydrogels. It appears that polymersomes with low polydispersity are formed already at very low polymer concentrations of 6 mg/L. Increasing the polymer concentration resulted in the formation of a bicontinuous sponge like structure which might be formed due to the merger of several vesicles. For longer polymer chains a phase transition into a gyroid structure was postulated and corresponds well with the observed rheological data. Stable hydrogels with an unusually high mechanical strength (G’ ~ 4 kPa) have been formed above TGel which could be adjusted over a range of 20 °C by changing the degree of polymerization if maintaining the symmetric polymer architecture. Variations of the chain ends revealed only a minor influence on TGel whereas the influence of the solvent should not be neglected as shown by a comparison of cell culture medium and MilliQ water. Rotationally as well as oscillatory rheological measurements revealed a high suitability for printing as POx b POzi based hydrogels exhibit strong shear thinning behavior in combination with outstanding recovery properties after high shear stress. Cell viability assays (WST-1) of PMeOx b PnPrOzi copolymers against NIH 3T3 fibroblasts and HaCat cells indicated that the polymers were well tolerated by the cells as no dose-dependent cytotoxicity could be observed after 24 h at non-gelling concentrations up to 100 g/L. In summary, copolymers consisting of POx and POzi significantly increased the accessible range of properties of POx based materials. In particular thermogelation of aqueous solutions of diblock copolymers comprising PMeOx and PnPrOzi was never described before for any copolymer consisting solely of POx or POzi. In combination with other characteristics, e.g. very good cytocompatibility at high polymer concentrations and comparably high mechanical strength, the formed hydrogels could be successfully used for 3D bioprinting. Although the results appear promising and the developed hydrogel is a serious bioink candidate, competition is tough and it remains an open question which system or systems will be used in the future. N2 - Motiviert durch das große Potential, das die Kombination aus additiver Fertigung und künstlicher Geweberegeneration bietet, wurde eine neuartige polymerbasierte Biotintenplattform auf Basis von Poly(2 oxazolin)en entwickelt. Diese soll zukünftig dazu beitragen das noch junge, aber aufstrebende Forschungsfeld der Biofabrikation weiterzuentwickeln. In der vorliegenden Arbeit wurden die Synthese sowie die Eigenschaften von mehreren Diblock Copolymeren, bestehend aus POx und POzi, untersucht, wobei der Hauptfokus auf deren Eignung als Biotinte lag. Grundsätzlich konnte gezeigt werden, dass Copolymere, bestehend aus 2 Oxazolinen und 2 Oxazinen, die unterschiedliche Alkylseitenketten besitzen, synthetisiert werden können. Dabei lagen die ermittelten Polymerisationsgrade nahe am zuvor errechneten Wert. Die Polymere wiesen mittlere bis niedrigere Dispersitäten auf. Für jedes der im Rahmen der vorliegenden Arbeit synthetisierten Diblock Copolymere konnte eine mehr oder weniger starke Abhängigkeit der dynamischen Viskosität von der Temperatur gezeigt werden. Allerdings ist es nicht möglich, aus den thermischen Eigenschaften des Bulkmaterials Rückschlüsse auf das temperaturabhängige Verhalten in Lösung zu ziehen. Diblock Copolymere mit einem hydrophilen PMeOx Block und einem thermoresponsiven PnPrOzi Block bildeten oberhalb einer Kettenlänge von 50 Einheiten und einer Polymerkonzentration von 20 Gew% ein physikalisches Gel. Solch ein Verhalten wurde bisher noch nicht für Copolymere, die ausschließlich auf POx oder seinen höheren Homologen basieren, beschrieben. Physikalische Hydrogele, basierend auf POx b POzi Copolymeren, weisen eine umgekehrte thermische Gelierung wie auch wässrige Lösungen von PNiPAAm und Pluronic F127 auf. Allerdings konnte durch die komplementäre Verwendung von SANS, DLS und SLS gezeigt werden, dass sich der zugrundeliegende Gelbildungsmechanismus für POx b POzi basierte Hydrogele deutlich von den beiden zuvor genannten unterscheidet. Es wird davon ausgegangen, dass sich zunächst bei einer sehr geringen Polymerkonzentration von 6 mg/L Vesikel mit geringer Polydispersität ausbilden. Eine Erhöhung der Konzentration resultiert in der Ausbildung eines bikontinuierlichen Netzwerks mit schwammartiger Struktur. Dieses bildet sich vermutlich durch die Fusion mehrerer Vesikel. Des Weiteren wird für höhere Polymerisationsgrade ein Phasenübergang zu einer gyroidalen Struktur postuliert der sich sehr gut mit den gewonnenen rheologischen Daten deckt. Stabile Hydrogele mit außergewöhnlich hoher mechanischer Stärke (G‘ ≈ 4kPa) bildeten sich oberhalb der Tgel, die über eine Temperaturspanne von 20 °C durch Änderung des Polymerisationsgrades eingestellt werden konnte. Veränderung der Kettenenden zeigten nur einen geringen Einfluss auf die TGel, wobei der Einfluss des verwendeten Lösemittels nicht unterschätzt werden sollte. Dies konnte durch den direkten Vergleich von MilliQ Wasser und Zellkulturmedium gezeigt werden. Rheologische Untersuchungen, die sowohl im rotierenden als auch im oszillierenden Modus durchgeführt wurden, zeigten eine gute Eignung der POx b POzi basierten Hydrogele für Extrusion basierte Druckverfahren. Insbesondere aufgrund des stark ausgeprägten scherverdünnenden Verhaltens und der ausgezeichneten Strukturerholung nach hoher Scherbelastung sollten gute Druckergebnisse erzielbar sein. Zellviabilität-Assays (WST-1) von PMeOx b PnPrOzi Copolymeren an NIH 3T3 Fibroblasten und HaCat-Zellen zeigten, dass die Polymere bei Konzentrationen von bis zu 100 g/L und Inkubationszeiten von 24 h keine dosisabhängige Zytotoxizität besitzen. Zusammenfassend kann festgehalten werden, dass die Copolymerisation von POx und POzi den verfügbaren Eigenschaftsbereich von POx basierten Materialien deutlich vergrößert hat. Insbesondere die temperaturinduzierte Gelierung von wässrigen Polymerlösungen wurde noch nie zuvor für ein anderes Copolymer auf Basis von POx und POzi beschrieben. Aufgrund ihrer herausragenden Eigenschaften, wozu unter anderem eine sehr gute Zytokompatibilität bei hohen Polymerkonzentrationen und eine vergleichsweise hohe mechanische Festigkeit zählen, konnten die entwickelten Hydrogele erfolgreich für den 3D Biodruck verwendet werden. Obwohl die beschriebenen Ergebnisse sehr vielversprechend sind und die entwickelte Hydrogelplattform folglich als ernstzunehmender Biotintenkandidat angesehen werden sollte, ist die Konkurrenz sehr groß und es bleibt abzuwarten, welche Tinte bzw. Tinten in Zukunft zum Einsatz kommen. KW - Polymere KW - Ringöffnungspolymerisation KW - Lichtstreuung KW - Biomaterial KW - 3D-Druck KW - Poly(2-oxazolin)e KW - poly(2-oxazoline)s KW - Biofabrikation KW - biofabrication KW - Biotinten KW - bioinks KW - Hydrogel KW - hydrogel KW - Ringöffnungspolymerisation KW - ring-opening polymerization Y1 - 2019 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-180514 ER - TY - THES A1 - Munzert, Stefanie Martina T1 - Coordination of dynamic metallosupramolecular polymers (MEPEs) T1 - Koordination von dynamischen metallosupramolekularen Polyelektrolyten (MEPE) N2 - Several transition metal ions, like Fe2+, Co2+, Ni2+, and Zn2+ complex to the ditopic ligand 1,4-bis(2,2’:6’,2’’-terpyridin-4’-yl)benzene. Due to the high association constant, metal ion induced self-assembly of Fe2+, Co2+, and Ni2+ leads to extended, rigid-rod like metallo-supramolecular coordination polyelectrolytes (MEPEs) even in aqueous solution. Here, the kinetics of coordination and the kinetics of growth of MEPEs are presented. The species in solutions are analyzed by stopped-flow fluorescence spectroscopy, light scattering, viscometry and cryogenic transmission electron microscopy. At near-stoichiometric amounts of the reactants, high molar masses are obtained, which follow the order Ni-MEPE ~ Co-MEPE < Fe-MEPE. Furthermore, a way is presented to adjust the average molar mass, chain-length and viscosity of MEPEs using the monotopic chain stopper 4’-(phenyl)-2,2’:6’,2’’-terpyridine. N2 - Verschiedene Übergangsmetallionen, wie Fe2+, Co2+, Ni2+ und Zn2+ komplexieren an den ditopen Liganden 1,4-Bis(2,2’:6’,2”-terpyridin-4’-yl)benzen. Aufgrund der hohen Bindungskonstanten, führt die metallinduzierte Selbstassemblierung von Fe2+, Co2+ und Ni2+ zu ausgedehnten, stäbchenförmigen metallosupramolekularen Polyelektrolyten (MEPE) in wässriger Lösung. In dieser Arbeit wird die Kinetik der Koordination sowie die Kinetik des Wachstums der MEPE aufgezeigt. Die Spezies in Lösung werden anhand von Stopped-flow-Fluoreszenzspektroskopie, Lichtstreuung, Viskosimetrie und Kryo-Transmittionselektronenmikroskopie analysiert. Bei nahezu stöchiometrischen Mengen der Reaktanden werden hohe molare Massen beobachtet. Dabei gilt: Ni-MEPE ~ Co-MEPE < Fe-MEPE. Außerdem wird ein Verfahren beschrieben, mit welchem die mittlere Molmasse, Kettenlänge und Viskosität der MEPE durch Nutzung des monotopen Kettenstoppers 4’-(Phenyl)-2,2’:6’,2’’-terpyridin eingestellt werden kann. KW - Supramolekulare Chemie KW - supramolecular chemistry KW - Polymere Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-160650 ER - TY - THES A1 - Namal, Imge T1 - Fabrication and Optical and Electronic Characterization of Conjugated Polymer-Stabilized Semiconducting Single-Wall Carbon Nanotubes in Dispersions and Thin Films T1 - Herstellung und Optische- und Elektronische- Charakterisierung von konjugierten Polymer-stabilisierten halbleitenden Kohlenstoffnanoröhren in Dispersionen und dünnen Filmen N2 - In order to shrink the size of semiconductor devices and improve their efficiency at the same time, silicon-based semiconductor devices have been engineered, until the material almost reaches its performance limits. As the candidate to be used next in semiconducting devices, single-wall carbon nanotubes show a great potential due to their promise of increased device efficiency and their high charge carrier mobilities in the nanometer size active areas. However, there are material based problems to overcome in order to imply SWNTs in the semiconductor devices. SWNTs tend to aggregate in bundles and it is not trivial to obtain an electronically or chirally homogeneous SWNT dispersion and when it is done, a homogeneous thin film needs to be produced with a technique that is practical, easy and scalable. This work was aimed to solve both of these problems. In the first part of this study, six different polymers, containing fluorene or carbazole as the rigid part and bipyridine, bithiophene or biphenyl as the accompanying copolymer unit, were used to selectively disperse semiconducting SWNTs. With the data obtained from absorption and photoluminescence spectroscopy of the corresponding dispersions, it was found out that the rigid part of the copolymer plays a primary role in determining its dispersion efficiency and electronic sorting ability. Within the two tested units, carbazole has a higher π electron density. Due to increased π−π interactions, carbazole containing copolymers have higher dispersion efficiency. However, the electronic sorting ability of fluorene containing polymers is superior. Chiral selection of the polymers in the dispersion is not directly foreseeable from the selection of backbone units. At the end, obtaining a monochiral dispersion is found to be highly dependent on the used raw material in combination to the preferred polymer. Next, one of the best performing polymers due to high chirality enrichment and electronic sorting ability was chosen in order to disperse SWNTs. Thin films of varying thickness between 18 ± 5 to 755o±o5 nm were prepared using vacuum filtration wet transfer method in order to analyze them optically and electronically. The scalability and efficiency of the integrated thin film production method were shown using optical, topographical and electronic measurements. The relative photoluminescence quantum yield of the radiative decay from the SWNT thin films was found to be constant for the thickness scale. Constant roughness on the film surface and linearly increasing concentration of SWNTs were also supporting the scalability of this thin film production method. Electronic measurements on bottom gate top contact transistors have shown an increasing charge carrier mobility for linear and saturation regimes. This was caused by the missing normalization of the mobility for the thickness of the active layer. This emphasizes the importance of considering this dimension for comparison of different field effect transistor mobilities. N2 - Um die Verkleinerung in Halbleiterbauelementen zu erreichen und gleichzeitig ihre Effizienz zu verbessern, wurden Halbleiterbauelemente auf Siliziumbasis entwickelt, bis das Material seine Leistungsgrenzen nahezu erreicht hat. Als zukünftiger Kandidat, der in halbleitenden Geräten Verwendung finden wird, zeigen einwandige Kohlenstoff−Nanoröhren ein großes Potenzial für eine erhöhte Geräteeffizienz. Grund dafür sind ihre hohen Ladungsträger−Mobilitäten in den ein paar Nanometergroßen aktiven Flächen. Allerdings gibt es materialbasierte Probleme zu überwinden um SWNTs in den Halbleiterbauelementen zu implizieren. SWNTs neigen dazu in Bündeln zu aggregieren. Eine Herausforderung ist zudem eine elektronische oder chiral homogene Kohlenstoffnanorohr−Dispersion zu erhalten. Ein weiteres Problem ist, aus diesen Kohlenstoffnanorohr−Dispersion einen homogenen Dünn−Film mit einer Technik herzustellen die praktisch, einfach und skalierbar ist. Diese Arbeit zielte darauf ab, diese beiden Probleme zu lösen. Im ersten Teil dieser Arbeit wurden sechs verschiedene Polymere, die Fluoren oder Carbazol als starren Teil und Bipyridin, Bithiophen oder Biphenyl als begleitende Copolymereinheit enthielten, verwendet um selektiv halbleitende SWNTs zu dispergieren. Mit den aus der Absorptions− und Photolumineszenzspektroskopie erhaltenen Daten der entsprechenden Dispersionen wurde herausgefunden, dass der starre Teil des Copolymers eine primäre Rolle bei der Bestimmung seiner Dispersionseffizienz und der elektronischen Sortierfähigkeit spielt. Innerhalb der beiden getesteten Einheiten hat Carbazol eine höhere π−Elektronendichte. Aufgrund erhöhter π−π Wechselwirkungen haben Carbazol−haltige Copolymere eine höhere Dispersionseffizienz. Die elektronische Selektivität von fluorenhaltigen Polymeren ist gegenüber Carbazol enthaltenden Polymeren höher. Die chirale Selektivität der Polymere in der Dispersion ist nicht direkt vor der Auswahl der Grundgerüsteinheiten vorhersehbar. Am Ende wird das Erhalten einer monochiralen Dispersion im hohen Maße von den verwendeten Rohmaterialien in Kombination mit dem bevorzugten Polymer abhängig gemacht. Im nächsten Schritt wurde ein Polymer ausgewählt der durch eine hohe Chiralitätanreicherung besticht und zudem eine gute elektronische Sortierfähigkeit besitzt, um SWNTs zu dispergieren. Dünnfilme unterschiedlicher Dicke, zwischen 18 ± 5 bis 755 ± 5 nm, wurden unter der Verwendung eines Vakuumfiltrations−Nassübertragungsverfahrens hergestellt um sie daraufhin optisch und elektronisch zu analysieren. Die Skalierbarkeit und Effizienz des integrierten Dünnschichtherstellungsverfahrens wurde anhand optischer, topographischer und elektronischer Messungen gezeigt. Die relative Photolumineszenzquantenausbeute des Strahlungsabfalls aus den SWNT−Dünnfilmen wurde für den Dickenmaßstab konstant gehalten. Eine konstante Rauigkeit auf der Filmoberfläche und eine linear zunehmende Konzentration von SWNTs unterstützten auch die Skalierbarkeit dieses Dünnfilmherstellungsverfahrens. Elektronische Messungen am „bottom gate – top contact Transistoren“ zeigten eine zunehmende Ladungsträgermobilität für Linear− und Sättigungsregionen. Dies wurde durch die fehlende Normalisierung der Ladungsträgermobilität für die Dicke der aktiven Schicht verursacht. Betrachtet man die Wichtigkeit, diese Dimension für den Vergleich verschiedener Feldeffekttransistor− Mobilitäten zu betrachten, so deutet diese Feststellung auch darauf hin, dass es eine Skalierung in der Dicke in Bezug auf die berechneten Mobilitäten für die Feldeffekttransistoren gibt. KW - single-wall carbon nanotubes KW - semiconductor devices KW - optical spectroscopy KW - polymer KW - Field effect transistor KW - Feldeffekttransistor KW - Optische Spektroskopie KW - Polymere KW - Halbleiter KW - Kohlenstoff-Nanoröhre Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-162393 ER -