TY - THES A1 - Müller, Andreas T1 - Towards functional oxide heterostructures T1 - Funktionelle oxidische Heterostrukturen N2 - Oxide heterostructures attract a lot of attention as they display a vast range of physical phenomena like conductivity, magnetism, or even superconductivity. In most cases, these effects are caused by electron correlations and are therefore interesting for studying fundamental physics, but also in view of future applications. This thesis deals with the growth and characterization of several prototypical oxide heterostructures. Fe3O4 is highly ranked as a possible spin electrode in the field of spintronics. A suitable semiconductor for spin injection in combination with Fe3O4 is ZnO due to its oxide character and a sufficiently long spin coherence length. Fe3O4 has been grown successfully on ZnO using pulsed laser deposition and molecular beam epitaxy by choosing the oxygen partial pressure adequately. Here, a pressure variation during growth reduces an FeO-like interface layer. Fe3O4 films grow in an island-like growth mode and are structurally nearly fully relaxed, exhibiting the same lattice constants as the bulk materials. Despite the presence of a slight oxygen off-stoichiometry, indications of the Verwey transition hint at high-quality film properties. The overall magnetization of the films is reduced compared to bulk Fe3O4 and a slow magnetization behavior is observed, most probably due to defects like anti-phase boundaries originating from the initial island growth. LaAlO3/SrTiO3 heterostructures exhibit a conducting interface above a critical film thickness, which is most likely explained by an electronic reconstruction. In the corresponding model, the potential built-up owing to the polar LaAlO3 overlayer is compensated by a charge transfer from the film surface to the interface. The properties of these heterostructures strongly depend on the growth parameters. It is shown for the first time, that it is mainly the total pressure which determines the macroscopic sample properties, while it is the oxygen partial pressure which controls the amount of charge carriers near the interface. Oxygen-vacancy-mediated conductivity is found for too low oxygen pressures. A too high total pressure, however, destroys interface conductivity, most probably due to a change of the growth kinetics. Post-oxidation leads to a metastable state removing the arbitrariness in controlling the electronic interface properties by the oxygen pressure during growth. LaVO3/SrTiO3 heterostructures exhibit similar behavior compared to LaAlO3/SrTiO3 when it comes to a thickness-dependent metal-insulator transition. But in contrast to LaAlO3, LaVO3 is a Mott insulator exhibiting strong electron correlations. Films have been grown by pulsed laser deposition. Layer-by-layer growth and a phase-pure pervoskite lattice structure is observed, indicating good structural quality of the film and the interface. An electron-rich layer is found near the interface on the LaVO3 side for conducting LaVO3/SrTiO3. This could be explained by an electronic reconstruction within the film. The electrostatic doping results in a band-filling-controlled metal-insulator transition without suffering from chemical impurities, which is unavoidable in conventional doping experiments. N2 - Oxidische Heterostrukturen besitzen verschiedenste physikalische Eigenschaften wie Leitfähigkeit, Magnetisums oder sogar Supraleitung. Diese Effekte, die meist von elektronischen Korrelationen verursacht werden, zu verstehen und ihren fundamentalen Ursprung zu erklären, machen diese Materialsysteme ebenso interessant wie ihr zukünftiges Anwendungspotential. Diese Arbeit beschäftigt sich mit verschiedenen prototypischen Schichtsystemen. Fe3O4 könnte zukünftig als Spinelektrode im Bereich der Spintronik dienen. ZnO ist ein Halbleiter, der durch seinen oxidischen Charakter und einer hinreichenden Spinkohärenzlänge gut zur Spininjektion geeignet ist. Das Wachstum von Fe3O4 auf ZnO wurde erfolgreich mittels gepulster Laserdeposition und Molekularstrahlepitaxie durchgeführt. Dabei ist der Sauerstoffpartialdruck entscheidend und eine Variation des Drucks während des Wachstums wirkt der Bildung einer FeO-artigen Grenzschicht entgegen. Die Filme wachsen inselartig und ihre Gitterstruktur ist fast vollständig relaxiert. Trotz einer Sauerstofffehlstöchiometrie wird die hohe Qualität der Filme durch einen Verwey-Phasenübergang bestätigt. Im Vergleich zu Einkristallen ist die Magnetisierung der Filme reduziert. Durch das Inselwachstum verursachte Antiphasengrenzen könnten zu dieser Reduzierung führen. Die leitfähige Grenzschicht, die in LaAlO3/SrTiO3 Heterostrukturen ab einer bestimmten LaAlO3 Filmdicke auftritt, kann höchstwahrscheinlich durch eine elektronische Rekonstruktion erklärt werden. Im entsprechenden Modell wird der Aufbau eines elektrischen Potentials auf Grund der Polarität des LaAlO3 Films durch eine Ladungsumordnung kompensiert. Die Eigenschaften dieser Heterostruktur sind jedoch von den Wachstumsparametern abhängig. Diese Studie zeigt erstmals, dass die makroskopischen Eigenschaften maßgeblich vom Gesamtdruck, die Anzahl der Ladungsträger dagegen stark vom Sauerstoffpartialdruck während des Wachstums abhängen. Leitfähigkeit auf Grund von Sauerstofffehlstellen wurde für sehr kleine Sauerstoffpartialdrücke beobachtet. Ein zu hoher Gesamtdruck hingegen verhindert die Leitfähigkeit der Grenzschicht. Dies ist vermutlich durch eine Änderung der Wachstumskinematik erklärbar. Ein Nachoxidieren der Proben führt überdies zu einem metastabilen Zustand, der die Vergleichbarkeit von Proben verschiedener Arbeitsgruppen gewährleistet. LaVO3/SrTiO3 zeigt ähnliches Verhalten wie LaAlO3/SrTiO3 und Leitfähigkeit tritt ab einer gewissen LaVO3 Schichtdicke auf. Im Gegensatz zu LaAlO3 ist LaVO3 ein Mottisolator, dass heißt, Korrelationseffekte spielen eine Rolle. LaVO3/SrTiO3 wurde mittels gepulster Laserdeposition hergestellt, Phasenreinheit und die strukturellen Eigenschaften mit verschiedenen Methoden überprüft. Zusätzliche Elektronen wurden für leitfähige Proben auf der LaVO3-Seite der Grenzfläche nachgewiesen. Eine Erklärung hierfür wäre eine elektronische Rekonstruktion im Film selbst. Dieses elektrostatische Dotieren führt zu einem bandfüllungsinduzierten Mott-Phasenübergang, der nicht durch chemische Verunreinigungen, die in konventionellen Dotierexperimenten unvermeidbar sind, beeinflusst ist. KW - Oxide KW - Epitaxieschicht KW - Heterostruktur KW - Physikalische Eigenschaft KW - Heterostrukturen KW - Oxid KW - Wachstum KW - MBE KW - PLD KW - Fe3O4 KW - LaAlO3 KW - LaVO3 KW - heterostructures KW - oxide KW - growth KW - MBE KW - PLD KW - Fe3O4 KW - LaAlO3 KW - LaVO3 KW - Röntgen-Photoelektronenspektroskopie KW - Photoelektronenspektroskopie KW - Kristallwachstum KW - Impulslaserbeschichten KW - Molekularstrahlepitaxie Y1 - 2012 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-72478 ER - TY - THES A1 - Paul, Markus Christian T1 - Molecular beam epitaxy and properties of magnetite thin films on semiconducting substrates T1 - Molekularstrahlepitaxie und Eigenschaften dünner Magnetitfilme auf Halbleitersubstraten N2 - The present thesis is concerned with molecular beam epitaxy of magnetite (Fe3O4) thin films on semiconducting substrates and the characterization of their structural, chemical, electronic, and magnetic properties. Magnetite films could successfully be grown on ZnO substrates with high structural quality and atomically abrupt interfaces. The films are structurally almost completely relaxed exhibiting nearly the same in-plane and out-of-plane lattice constants as in the bulk material. Films are phase-pure and show only small deviations from the ideal stoichiometry at the surface and in some cases at the interface. Growth proceeds via wetting layer plus island mode and results in a domain structure of the films. Upon coalescence of growing islands twin-boundaries (rotational twinning) and anti-phase boundaries are formed. The overall magnetization is nearly bulk-like, but shows a slower approach to saturation, which can be ascribed to the reduced magnetization at anti-phase boundaries. However, the surface magnetization which was probed by x-ray magnetic circular dichroism was significantly decreased and is ascribed to a magnetically inactive layer at the surface. Such a reduced surface magnetization was also observed for films grown on InAs and GaAs. Magnetite could also be grown with nearly ideal iron-oxygen stoichiometry on InAs substrates. However, interfacial reactions of InAs with oxygen occur and result in arsenic oxides and indium enrichment. The grown films are of polycrystalline nature. For the fabrication of Fe3O4/GaAs films, a postoxidation of epitaxial Fe films on GaAs was applied. Growth proceeds by a transformation of the topmost Fe layers into magnetite. Depending on specific growth conditions, an Fe layer of different thickness remains at the interface. The structural properties are improved in comparison with films on InAs, and the resulting films are well oriented along [001] in growth direction. The magnetic properties are influenced by the presence of the Fe interface layer as well. The saturation magnetization is increased and the approach to saturation is faster than for films on the other substrates. We argue that this is connected to a decreased density of anti-phase boundaries because of the special growth method. Interface phases, viz. arsenic and gallium oxides, are quantified and different growth conditions are compared with respect to the interface composition. N2 - Die vorliegende Arbeit beschäftigt sich mit der Molekularstrahlepitaxie von dünnen Magnetitfilmen (Fe3O4) auf Halbleitersubstraten und der Charakterisierung ihrer strukturellen, chemischen, elektronischen und magnetischen Eigenschaften. Magnetitfilme konnten auf ZnO Substraten mit hoher struktureller Qualität und scharfen Grenzflächen durch Kodeposition von Eisen und Sauerstoff gewachsen werden. Die Filme sind strukturell nahezu vollständig relaxiert und weisen innerhalb und außerhalb der Wachstumsebene annähernd die Gitterkonstante von Einkristallen auf. Weiterhin sind die hergestellten Proben phasenrein und zeigen nur an der Oberfläche und in einigen Fällen an der Grenzfläche allenfalls kleine Abweichungen von der idealen Stöchiometrie. Das Wachstum erfolgt im Stranski-Krastanov-Modus und resultiert in einer Domänenstruktur der Filme. Beim Zusammenwachsen der Inseln entstehen Antiphasengrenzen und Zwillingsgrenzen. Die Volumenmagnetisierung der Filme ist annähernd gleich der eines Einkristalls, jedoch ist das Einmündungsverhalten in die Sättigung aufgrund von reduzierter Magnetisierung an Antiphasengrenzen deutlich langsamer. Dagegen ist die Oberflächenmagnetisierung, welche mit der Methode des Röntgenzirkulardichroismus untersucht wurde, erheblich reduziert, was auf eine magnetisch inaktive Schicht an der Oberfläche schließen lässt. Diese Reduzierung der Oberflächenmagnetisierung wurde auch für Filme, die auf InAs oder GaAs deponiert wurden, beobachtet. Ebenfalls konnte Magnetit mit nahezu idealem Eisen-Sauerstoff-Verhältnis auf InAs gewachsen werden. Bei diesem Substrat treten jedoch Grenzflächenreaktionen des Indiumarsenids mit Sauerstoff auf, die eine Arsenoxidphase und eine Indiumanreicherung bewirken. Die Filme wachsen hier nur polykristallin. Für die Herstellung von Fe3O4/GaAs-Filmen wurde die Methode der Nachoxidation von epitaktischen Eisenfilmen benutzt. Das Wachstum läuft dabei durch Transformation der obersten Lagen des Eisenfilms zu Magnetit ab. Abhängig von den genauen angewandten Wachstumsbedingungen bleibt dabei eine Eisenschicht unterschiedlicher Dicke an der Grenzfläche übrig. Die strukturellen Eigenschaften sind im Vergleich zu Filmen auf InAs verbessert und die Proben sind gut entlang der [001]-Richtung orientiert. Die magnetischen Eigenschaften werden ebenfalls durch die Eisen-Grenzflächenschicht beeinflusst. Die Sättigungsmagnetisierung ist erhöht und tritt bei niedrigeren Magnetfeldern auf. Dieses Verhalten ist offenbar mit einer geringeren Dichte an Antiphasengrenzen aufgrund des andersartigen Wachstumsmechanismus verknüpft. Auftretende Grenzflächenphasen wurden quantifiziert und unterschiedliche Wachstumsbedingungen im Hinblick auf die Grenzflächenzusammensetzung verglichen. KW - Molekularstrahlepitaxie KW - Dünne Schicht KW - Magnetit KW - Physikalische Eigenschaft KW - Halbleitersubstrat KW - Photoelektronenspektroskopie KW - Röntgenabsorption KW - Röntgenbeugung KW - Elektronenbeugung KW - molecular beam epitaxy KW - photoelectron spectroscopy KW - x-ray magnetic circular dichroism KW - magnetic oxide KW - thin film Y1 - 2010 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-56044 ER -