TY  - JOUR
A1  - Wolf-Brandstetter, C
A1  - Beutner, R
A1  - Hess, R
A1  - Bierbaum, S
A1  - Wagner, K
A1  - Scharnweber, D
A1  - Gbureck, U
A1  - Moseke, C
T1  - Multifunctional calcium phosphate based coatings on titanium implants with integrated trace elements
JF  - Biomedical Materials
N2  - For decades, the main focus of titanium implants developed to restore bone functionality was on improved osseointegration. Additional antimicrobial properties have now become desirable, due to the risk that rising antibiotic resistance poses for implant-associated infections. To this end, the trace elements of copper and zinc were integrated into calcium phosphate based coatings by electrochemically assisted deposition. In addition to their antimicrobial activity, zinc is reported to attract bone progenitor cells through chemotaxis and thus increase osteogenic differentiation, and copper to stimulate angiogenesis. Quantities of up to 68.9 ± 0.1 μg cm\(^{-2}\) of copper and 56.6 ± 0.4 μg cm\(^{-2}\) of zinc were deposited; co-deposition of both ions did not influence the amount of zinc but slightly increased the amount of copper in the coatings. The release of deposited copper and zinc species was negligible in serum-free simulated body fluid. In protein-containing solutions, a burst release of up to 10 μg ml\(^{-1}\) was observed for copper, while zinc was released continuously for up to 14 days. The presence of zinc was beneficial for adhesion and growth of human mesenchymal stromal cells in a concentration-dependent manner, but cytotoxic effects were already visible for coatings with an intermediate copper content. However, co-deposited zinc could somewhat alleviate the adverse effects of copper. Antimicrobial tests with E. coli revealed a decrease in adherent bacteria on brushite without copper or zinc of 60%, but if the coating contained both ions there was almost no bacterial adhesion after 12 h. Coatings with high zinc content and intermediate copper content had the overall best multifunctional properties.
KW  - coating
KW  - titanium
KW  - implant
KW  - pro-angiogenic
KW  - osteogenic
KW  - antimicrobial
Y1  - 2020
U6  - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-254085
VL  - 15
IS  - 2
ER  - 
TY  - THES
A1  - Wenninger, Florian
T1  - Modifikation von Titanoberflächen mittels elektrochemischer Abscheidung von Magnesiumphosphaten
N2  - In der vorliegenden Arbeit ist es gelungen, die experimentellen Parameter für eine erfolgreiche elektrochemische Abscheidung sowohl von Struvit (MgNH4PO4 • 6H2O) als auch Newberyit (MgHPO4 • 3H2O) auf durch Sandstrahlen aufgeraute Titanproben zu ermitteln. Welche der beiden Phasen auf den Titanoberflächen abgeschieden wurde, hing dabei hauptsächlich von der jeweiligen Elektrolytzusammensetzung ab. Bei der Elektrodeposition selbst erwiesen sich eine Elektrolyttemperatur von 50 °C und Stromdichten von etwa 79 – 105 mA/cm2 als optimal, um geschlossene Schichten von hinreichender Dicke reproduzierbar herzustellen. Es zeigte sich, dass die für die jeweiligen Abscheidungsprodukte optimierten Parameter (79 mA/cm2 für Struvit und 105,3 mA/cm2 für Newberyit) zu deutlich unterschiedlichen Massenabscheidungen (4,4 mg/cm2 für Struvit und 0,6 mg/cm2 für Newberyit bei einer Beschichtungsdauer von 15 min) führten. Das Monohydrat Dittmarit (MgNH4PO4 • H2O) ließ sich nicht direkt abscheiden, konnte aber durch Dampfsterilisation von zuvor erzeugten Struvitschichten in einem Autoklaven erzeugt werden.
Um das Verhalten der Oberflächenmodifikationen in einer in-vivo-Umgebung zu simulieren, wurden die Beschichtungen für eine maximale Dauer von 14 Tagen in Simulated Body Fluid (SBF), Dulbecco's Modified Eagle Medium (DMEM) und in fötalem Kälberserum (FCS) eingelagert. In bestimmten Zeitabständen wurden eingelagerte Proben ihrem Medium entnommen, getrocknet und die Schichten mit Hilfe der Röntgendiffraktometrie und der Rasterelektronen-mikroskopie hinsichtlich ihrer kristallographischen und morphologischen Eigenschaften charakterisiert. Dabei zeigten die drei Magnesiumphosphate jeweils unterschiedliches Degradationsverhalten in den verschiedenen Einlagerungsmedien. Struvit wandelte sich nach 14 Tagen in DMEM teilweise, in FCS größtenteils und in SBF vollständig zu Bobierrit (Mg3(PO4)2 • 8H2O) um. Ein ähnliches Verhalten zeigte sich bei Dittmarit, allerdings kam es hier in allen Medien zur Bildung einer weiteren Phase (Tri-Magnesium-Di-Phosphat-5-Hydrat, Mg3(PO4)2 • 5H2O), in FCS bildete sich zusätzlich noch Di-Magnesiumphosphathydroxid-4-Hydrat (Mg2PO4OH • 4H2O). Die Newberyit-Schichten hingegen zeigten keinerlei Phasenumwandlungen, lösten sich aber in den Einlagerungsversuchen teilweise auf.
Diese Ergebnisse zeigen, dass elektrochemisch erzeugte Beschichtungen auf Magnesiumphosphatbasis durchaus vielversprechend im Hinblick auf die funktionelle Modifikation metallischer Implantatoberflächen sind. Neben den literaturbekannten positiven Eigenschaften der Magnesiumphosphate (gute Zytokompatibilität, hohe Löslichkeit und mechanische Festigkeit) ist für zukünftige Forschungen vor allem das in dieser Arbeit untersuchte Degradationsverhalten von Interesse. Die in fast allen untersuchten Kombinationen aus Schichtmodifikation und Einlagerungsmedium auftretenden Phasenumwandlungen weisen auf durch die physiologische Umgebung hervorgerufene Resorptionsprozesse hin, die wiederum in vivo die Osteointegration des Implantats unterstützen könnten.
Ein weiterer Aspekt zukünftiger Untersuchungen ist die mögliche Beladung der biokompatiblen Schichten mit bioaktiven Substanzen (antibakterielle oder osteointegrative Wirkstoffe sowie Metallionen zur Unterstützung bzw. Steuerung biologischer Prozesse im implantatnahen Bereich). Hier könnten die unterschiedlichen Degradationsmechanismen der verschiedenen untersuchten Magnesiumphosphat-Modifikationen die Grundlage für kontrollierte und maßgeschneiderte Freisetzungskinetiken liefern.
KW  - Magnesiumphosphate
KW  - Titan
KW  - Galvanische Abscheidung
KW  - Struvit
KW  - Degradation
KW  - elektrochemische Abscheidung
KW  - electrochemical deposition
KW  - titanium
KW  - magnesium phosphate
KW  - struvite
Y1  - 2013
U6  - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-85557
ER  - 
TY  - THES
A1  - Tebbe, David
T1  - Funktionalisierung von Titan(dioxid)oberflächen mit kovalent gebundenem und in Depots eingebrachtem Wirkstoff für den Blutkontakt
T1  - Functionalization of titanium surfaces with covalently attached and embedded drug for blood contact
N2  - Ziel der vorliegenden Arbeit war die Funktionalisierung von Titanoberflächen mit dem Glycosaminoglycan Heparin, um bei Kontakt des Werkstoffs mit Blut die Gerinnungskaskade nicht auszulösen und das Material für Stents (Gefäßstützen) im arteriellen System einsetzbar zu machen. Für die Modifizierungen wurden als Modell der oxidierten Titanoberfläche sowohl oxidierte cp-Titanplättchen als auch TiO2-Pulver verwendet. Heparin kam zum Einsatz, da es sowohl die Hämostase (Blutgerinnung) als auch die Proliferation (Überwucherung) mit glatten Muskelzellen unterdrückt und somit eine Restenose (Wiederverengung) des in die verengte Arterie eingebrachten Stents verhindert. Die kovalente Immobilisierung des Wirkstoffs erfolgte über bifunktionale Spacer (Haftvermittlermoleküle). Spacer waren 3-(Trimethoxysilyl)-propylamin (APMS), N-(2-Aminoethyl)-3-aminopropyltrimethoxysilan (Diamino-APMS) und N1-[3-(Trimethoxysilyl)-propyl]diethylen¬triamin (Triamino-APMS). Der qualitative und quantitative Nachweis der Funktionalisierung von TiO2 mit Haftvermittler bzw. Heparin erfolgte durch schwingungsspektroskopische Methoden, komplexometrische Farbreaktionen sowie der Bestimmung des Zetapotentials im Elektrolytkontakt. Durch die Anbindung von APMS, Di- und Triamino-APMS stieg das Zetapotential von ca. -26 mV auf positive Werte zwischen +41 und +45 mV. Ein Absinken des Zetapotentials belegte die erfolgreiche Anbindung von Heparin (Werte zwischen -39 und -37 mV) an die verschiedenen Haftvermittler, ebenso wie das Vorhandensein der symmetrischen SO3-Valenzschwingung bei 1040 cm-1. Der quantitative Nachweis der immobilisierten Aminogruppen über die Ninhydrinreaktion ergab für die TiO2-Pulver Werte zwischen 17-20 NH2/nm2, wobei die dichteste Funktionalisierung mit APMS und die niedrigste mit Triamino-APMS erzielt werden konnte. Alle Werte lagen im Bereich von Multilayern, da ein Monolayer aus ca. 2 3 NH2/nm2 besteht. Die immobilisierte Menge an Heparin war bei Verwendung von APMS am größten (53.3±3.6 ng/cm2) und bei Triamino-APMS am geringsten (32.1±5.7 ng/cm2). Die biologische Wirksamkeit des gebundenen Heparins wurde über das chromogene Substrat ChromozymTH® bestimmt und verblieb bei Anbindung an den Spacer mit der größten Moleküllänge (Triamino-APMS) mit ca. 70% am wirksamsten. Neben der kovalenten Anbindung des Wirkstoffs an Spacer zielte diese Arbeit auf die Entwicklung von organisch modifizierten, porösen SiO2-Wirkstoffdepots (P-MA-PS; Poly-methacryl¬oxy¬propylpolysilsesquioxane) für Heparin ab, die sowohl als Volumenwerkstoffe als auch zur Modifikation von Titan(dioxid)oberflächen anwendbar wären. Die Matrices wurden ausgehend von MAS (Methacryl¬oxypropyl¬trimethoxysilan) über den Sol-Gel Prozeß anorganisch und anschließend über photochemische Polymerisation zusätzlich organisch vernetzt. Die Quantifizierung des Polymerisationsgrads erfolgte über die Signalintensität der methacrylischen C=C-Doppelbindung bei 1635 cm-1 durch Integration einer Gauß-Funktion. Über den Polymerisationsgrad der organischen Matrix zwischen 0-71% konnte die Freisetzungskinetik von Heparin je nach therapeutischer Anforderung eingestellt werden. Es konnte gezeigt werden, daß hohe Wirkstoff-Beladungen und niedrige Polymerisationsgrade mit einer schnelleren Freisetzung des Heparins korrelierten, die aufgrund der Endlichkeit des Wirkstoffs im Depot einer Kinetik 1. Ordnung unterlag. Die kumulativ freigesetzten Wirkstoffmengen verhielten sich hierbei proportional zur Wurzel aus der Freisetzungszeit, was dem Higuchi-Modell zur Wirkstofffreisetzung aus porösen Matrices mit einem rein Diffusions-kontrollierten Mechanismus entsprach. Die durch Hydrolyse bedingte Degradation der anorganischen Matrix, die UV-VIS-spektroskopisch bei λ = 220 nm gemessen wurde, folgte einer Kinetik pseudo-0. Ordnung. Da das freigesetzte Heparin seine biologische Wirksamkeit beibehielt, sind P-MA-PS Matrices interessant für klinische Anwendungen, wie z.B. für die Beschichtung von Gefäßstützen, die im Blutkontakt stehen.
N2  - Aim of this work was the functionalization of titanium surfaces with the glycosaminoglycane heparin to improve the surface hemocompatibility for an application in the field of coronary stenting. Surface modification was performed using both TiO2 powder and titanium sheets as substrates imitating the (oxidized) surface of titanium implants. The substrates were modified with heparin to prevent side effects like blood coagulation and neointimal proliferation after implantation, which can both lead to restenosis of the acute artery closure. Surfaces can be modified either by covalent bonding of the drug to the metal by a silane spacer or by embedding the active agent into a polymer matrix for the controlled release over a certain period of time. Covalent attachment of heparin to titanium metal and TiO2 powder was carried out using the coupling agents 3-(Trimethoxysilyl)-propylamine (APMS), N-[3-(Trimethoxysilyl)-propyl]-ethylenediamine (Diamino-APMS) and N1-[3-(Trimethoxysilyl)-propyl]-diethylenetriamine (Triamino-APMS). Additionally, the influence of primary accomplished TiO2 films on the density of surface bound spacer was determined. Therefore, polished titanium substrates were covered with thin (< 2 µm) TiO2 layers by means of thermal/anodic oxidation, physical vapor deposition (PVD) or the sol-gel process and were then modified with the different spacer molecules, respectively. Aim was a correlation between the composition/topography of the TiO2 layers and the amount of bound spacer molecules. At this, two tendencies could be observed. Firstly, the density of surface bound spacer was generally highest for APMS (115-212 nmol/cm2) and lowest for Triamino-APMS (102-176 nmol/cm2), which was due to that smaller molecules underlie less intermolecular sterical hindrance onto surfaces. And secondly, on TiO2 surfaces with a higher roughness and therewith a higher specific surface area more spacer molecules could be immobilized (in the sequence: PVD > heat treated > anodized > sol-gel). The amount of surface bound coupling agent and heparin was quantified photometrically by the ninhydrin reaction and the toluidine-blue test. The biological potency of heparin was determined photometrically by the chromogenic substrate Chromozym TH and fibrinogen adsorption on the modified surfaces was investigated using the QCM-D (Quartz Crystal Microbalance with Dissipation Monitoring) technique. Zeta-potential measurements confirmed the successful coupling reaction; the zeta-potential of the unmodified anatase surface (approx. -26 mV) shifted into the positive range (> +40 mV) after silanisation. Binding of heparin resulted in a strongly negatively charged surface with zeta-potentials of approx. 39 mV. The successful heparinization could also be followed using RAMAN-spectroscopy by the occurrence of the peak at 1040 cm-1 (S=O vibration) caused by the drug. The amount of covalently attached primary amino groups on TiO2 powder was the highest for APMS (20 NH2/nm2) and decreased for Di- and Triamino-APMS (19 & 17 NH2/nm2). The hereby accomplished aminosilane layers were all in the range of multilayers since a monolayer is approx. 2 3 NH2/nm2. On the APMS spacer, the greatest amount of 53.3±3.6 ng/cm2 heparin was immobilized compared to Di- and Triamino-APMS (41.2±6.9 & 32.1±5.7 ng/cm2). The retaining biological activity of heparin was found to be the highest (70%) for the covalent attachment with Triamino-APMS as coupling agent due to the long chain of this spacer molecule and therefore the highest mobility of the drug. Moreover, this work aimed to investigate the use of an organically modified porous silica matrix (Poly(methacryloxypropyl)-poly(silsesquioxane); P-MA-PS) as a release system for heparin. The matrices were obtained from the precursor methacryloxypropyltrimethoxysilane (MAS) via the sol-gel process under acidic conditions following photochemical polymerization and cross-linking of the organic matrix. Modulation of the polymerization degree of the organic matrix in the range 0-71% allowed to adjust the release kinetics of heparin according to therapeutic needs. It was demonstrated that higher drug loads and a decreasing polymerization degree resulted in a faster release profile of heparin, which followed a square root of time kinetic according to the Higuchi model. The hydrolytic degradation of the xerogel was found to follow a zero-order kinetic whereas the heparin concentration did not show an influence on the degradation rate of the anorganic matrix. Since the released heparin retained its biological activity, P-MA-PS matrices may be interesting for clinical application, for instance as coating on drug eluting coronary stents.
KW  - Heparin
KW  - Titan
KW  - Oberfläche
KW  - Blutkontakt
KW  - Stent
KW  - Heparin
KW  - Titan
KW  - Oberfläche
KW  - Blutkontakt
KW  - Stent
KW  - heparin
KW  - titanium
KW  - surface
KW  - blood-contact
KW  - stent
Y1  - 2008
U6  - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-26579
ER  - 
TY  - JOUR
A1  - Holst, Alexandra Ioana
A1  - Holst, Stefan
A1  - Hirschfelder, Ursula
A1  - von Seckendorff, Volker
T1  - Retrieval analysis of different orthodontic brackets: the applicability of electron microprobe techniques for determining material heterogeneities and corrosive potential
JF  - Journal of applied oral science
N2  - Objective: The objective of this study was to investigate the applicability of microanalytical methods with high spatial resolution to the characterization of the composition and corrosion behavior of two bracket systems. 
Material and methods: The surfaces of six nickel-free brackets and six nickel-containing brackets were examined for signs of corrosion and qualitative surface analysis using an electron probe microanalyzer (EPMA), prior to bonding to patient's tooth surfaces and four months after clinical use. The surfaces were characterized qualitatively by secondary electron (SE) images and back scattered electron (BSE) images in both compositional and topographical mode. Qualitative and quantitative wavelength-dispersive analyses were performed for different elements, and by utilizing qualitative analysis the relative concentration of selected elements was mapped two-dimensionally. The absolute concentration of the elements was determined in specially prepared brackets by quantitative analysis using pure element standards for calibration and calculating correction-factors (ZAF). 
Results: Clear differences were observed between the different bracket types. The nickel-containing stainless steel brackets consist of two separate pieces joined by a brazing alloy. Compositional analysis revealed two different alloy compositions, and reaction zones on both sides of the brazing alloy. The nickel-free bracket was a single piece with only slight variation in element concentration, but had a significantly rougher surface. After clinical use, no corrosive phenomena were detectable with the methods applied. Traces of intraoral wear at the contact areas between the bracket slot and the arch wire were verified. Conclusion: Electron probe microanalysis is a valuable tool for the characterization of element distribution and quantitative analysis for corrosion studies.
KW  - orthodontic brackets
KW  - dental casting alloys
KW  - metallurgical characterization
KW  - galvanic corrosion
KW  - surface analysis
KW  - nickel release
KW  - archwires
KW  - titanium
KW  - fluoride
KW  - biocompatibility
KW  - appliances
KW  - electron probe microanalysis
KW  - nickel
Y1  - 2012
U6  - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-130415
VL  - 20
IS  - 4
ER  - 
TY  - JOUR
A1  - Goettel, James T.
A1  - Gao, Haopeng
A1  - Dotzauer, Simon
A1  - Braunschweig, Holger
T1  - \(^{Me}\)CAAC=N\(^{-}\): A Cyclic (Alkyl)(Amino)Carbene Imino Ligand
JF  - Chemistry – A European Journal
N2  - A cyclic (alkyl)(amino)carbene (CAAC) has been shown to react with a covalent azide similar to the Staudinger reaction. The reaction of \(^{Me}\)CAAC with trimethylsilyl azide afforded the N‐silylated 2‐iminopyrrolidine (\(^{Me}\)CAAC=NSiMe\(_{3}\)), which was fully characterized. This compound undergoes hydrolysis to afford the 2‐iminopyrrolidine and trimethylsiloxane which co‐crystallize as a hydrogen‐bonded adduct. The N‐silylated 2‐iminopyrrolidine was used to transfer the novel pyrrolidine‐2‐iminato ligand onto both main‐group and transition‐metal centers. The reaction of the tetrabromodiborane bis(dimethyl sulfide) adduct with two equivalents of \(^{Me}\)CAAC=NSiMe\(_{3}\) afforded the disubstituted diborane. The reaction of \(^{Me}\)CAAC=NSiMe\(_{3}\) with TiCl\(_{4}\) and CpTiCl\(_{3}\) afforded \(^{Me}\)CAAC=NTiCl\(_{3}\) and \(^{Me}\)CAAC=NTiCl\(_{2}\)Cp, respectively.
KW  - boron
KW  - carbenes
KW  - imide ligands
KW  - nitrogen ligands
KW  - titanium
Y1  - 2020
U6  - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-212662
VL  - 26
IS  - 5
ER  - 
TY  - JOUR
A1  - Föhrenbacher, Steffen A.
A1  - Krahfuss, Mirjam J.
A1  - Zapf, Ludwig
A1  - Friedrich, Alexandra
A1  - Ignat'ev, Nikolai V.
A1  - Finze, Maik
A1  - Radius, Udo
T1  - Tris(pentafluoroethyl)difluorophosphorane: a versatile fluoride acceptor for transition metal chemistry
JF  - Chemistry Europe
N2  - Fluoride abstraction from different types of transition metal fluoride complexes [L\(_n\)MF] (M=Ti, Ni, Cu) by the Lewis acid tris(pentafluoroethyl)difluorophosphorane (C\(_2\)F\(_5\))\(_3\)PF\(_2\) to yield cationic transition metal complexes with the tris(pentafluoroethyl)trifluorophosphate counterion (FAP anion, [(C\(_2\)F\(_5\))\(_3\)PF\(_3\)]\(^-\)) is reported. (C\(_2\)F\(_5\))\(_3\)PF\(_2\) reacted with trans-[Ni(iPr\(_2\)Im)\(_2\)(Ar\(^F\))F] (iPr2Im=1,3-diisopropylimidazolin-2-ylidene; Ar\(^F\)=C\(_6\)F\(_5\), 1 a; 4-CF\(_3\)-C\(_6\)F\(_4\), 1 b; 4-C\(_6\)F\(_5\)-C\(_6\)F\(_4\), 1 c) through fluoride transfer to form the complex salts trans-[Ni(iPr\(_2\)Im)\(_2\)(solv)(Ar\(^F\))]FAP (2 a-c[solv]; solv=Et\(_2\)O, CH\(_2\)Cl\(_2\), THF) depending on the reaction medium. In the presence of stronger Lewis bases such as carbenes or PPh\(_3\), solvent coordination was suppressed and the complexes trans-[Ni(iPr\(_2\)Im)\(_2\)(PPh\(_3\))(C\(_6\)F\(_5\))]FAP (trans-2 a[PPh\(_3\)]) and cis-[Ni(iPr\(_2\)Im)\(_2\)(Dipp\(_2\)Im)(C\(_6\)F\(_5\))]FAP (cis-2 a[Dipp\(_2\)Im]) (Dipp\(_2\)Im=1,3-bis(2,6-diisopropylphenyl)imidazolin-2-ylidene) were isolated. Fluoride abstraction from [(Dipp\(_2\)Im)CuF] (3) in CH\(_2\)Cl\(_2\) or 1,2-difluorobenzene led to the isolation of [{(Dipp\(_2\)Im)Cu}\(_2\)]\(^2\)\(^+\)2 FAP\(^-\) (4). Subsequent reaction of 4 with PPh\(_3\) and different carbenes resulted in the complexes [(Dipp\(_2\)Im)Cu(LB)]FAP (5 a–e, LB=Lewis base). In the presence of C6Me6, fluoride transfer afforded [(Dipp\(_2\)Im)Cu(C\(_6\)Me\(_6\))]FAP (5 f), which serves as a source of [(Dipp\(_2\)Im)Cu)]\(^+\). Fluoride abstraction of [Cp\(_2\)TiF\(_2\)] (7) resulted in the formation of dinuclear [FCp\(_2\)Ti(μ-F)TiCp\(_2\)F]FAP (8) (Cp=η\(^5\)-C\(_5\)H\(_5\)) with one terminal fluoride ligand at each titanium atom and an additional bridging fluoride ligand.
KW  - inorganic chemistry
KW  - copper
KW  - nickel
KW  - phosphoranes
KW  - titanium
KW  - weakly coordinating anions
Y1  - 2021
U6  - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-256665
VL  - 27
IS  - 10
ER  -