TY - THES A1 - Bach, Peter T1 - Growth and characterization of NiMnSb-based heterostructures T1 - Wachstum und Charaktersisierung von NiMnSb-basierenden Heterostrukturen N2 - In this work heterostructures based on the half-Heusler alloy NiMnSb have been fabricated and characterized. NiMnSb is a member of the half-metallic ferromagnets, which exhibit an electron spin-polarization of 100% at the Fermi-level. For fabrication of these structures InP substrates with surface orientations of (001),(111)A and (111)B have been used. The small lattice mismatch of NiMnSb to InP allows for pseudomorphic layers, the (111) orientation additionally makes the formation of a half-metallic interface possible. For the growth on InP(001), procedures for the substrate preparation, growth of the lattice matched (In,Ga)As buffer layer and of the NiMnSb layer have been developed. The effect of flux-ratios and substrate temperatures on the MBE growth of the buffer as well as of the NiMnSb layer have been investigated and the optimum conditions have been pointed out. NiMnSb grows in the layer-by-layer Frank-van der Merwe growth mode, which can be seen by the intensity oscillations of the RHEED specular spot during growth. RHEED and LEED measurements show a flat surface and a well-defined surface reconstruction. High resolution x-ray measurements support this statement, additionally they show a high crystalline quality. Measurements of the lateral and the vertical lattice constant of NiMnSb films on (001) oriented substrates show that layers above a thickness of 20nm exhibit a pseudomorphic as well as a relaxed part in the same layer. Whereas layers around 40nm show partly relaxed partitions, these partitions are totally relaxed for layers above 100nm. However, even these layers still have a pseudomorphic part. Depth-dependent x-ray diffraction experiments prove that the relaxed part of the samples is always on top of the pseudomorphic part. The formation and propagation of defects in these layers has been investigated by TEM. The defects nucleate early during growth and spread until they form a defect network at a thickness of about 40nm. These defects are not typical misfit dislocations but rather antiphase boundaries which evolve in the Mn/Sb sublattice of the NiMnSb system. Dependent on the thickness of the NiMnSb films different magnetic anisotropies can be found. For layers up to 15nm and above 25nm a clear uniaxial anisotropy can be determined, while the layers with thicknesses in between show a fourfold anisotropy. Notably the easy axis for the thin layers is perpendicular to the easy axis observed for the thick layers. Thin NiMnSb layers show a very good magnetic homogeneity, as can be seen by the very small FMR linewidth of 20Oe at 24GHz. However, the increase of the linewidth with increasing thickness shows that the extrinsic damping gets larger for thicker samples which is a clear indication for magnetic inhomogeneities introduced by crystalline defects. Also, the magnetic moment of thick NiMnSb is reduced compared to the theoretically expected value. If a antiferromagnetic material is deposited on top of the NiMnSb, a clear exchange biasing of the NiMnSb layer can be observed. In a further step the epitaxial layers of the semiconductor ZnTe have been grown on these NiMnSb layers, which enables the fabrication of NiMnSb/ZnTe/NiMnSb TMR structures. These heterostructures are single crystalline and exhibit a low surface and interface roughness as measured by x-ray reflectivity. Magnetic measurements of the hysteresis curves prove that both NiMnSb layers in these heterostructures can switch separately, which is a necessary requirement for TMR applications. If a NiMn antiferromagnet is deposited on top of this structure, the upper NiMnSb layer is exchange biased by the antiferromagnet, while the lower one is left unaffected. Furthermore the growth of NiMnSb on (111) oriented substrates has been investigated. For these experiments, InP substrates with a surface orientation of (111)A and (111)B were used, which were miscut by 1 to 2° from the exact orientation to allow for smoother surfaces during growth. Both the (In, Ga)As buffer as well as the NiMnSb layer show well defined surface reconstructions during growth. X-ray diffraction experiments prove the single crystalline structure of the samples. However, neither for the growth on (111)A nor on (111)B a perfectly smooth surface could be obtained during growth, which can be attributed to the formation of pyramid-like facets evolving as a result of the atomic configuration at the surface. A similar relaxation behavior as NiMnSb layers on (001) oriented InP could not be observed. RHEED and x-ray diffraction measurements show that above a thickness of about 10nm the NiMnSb layer begins to relax, but remnants of pseudomorphic parts could not be found. Magnetic measurements show that the misorientation of the substrate crystal has a strong influence on the magnetic anisotropies of NiMnSb(111) samples. In all cases a uniaxial anisotropy could be observed. The easy axis is always aligned parallel to the direction of the miscut of the substrate. N2 - Im Rahmen dieser Arbeit wurden Heterostrukturen basierend auf dem Halb-Heusler Material NiMnSb hergestellt und charakterisiert. NiMnSb ist ein Mitglied der halbmetallischen Ferromagnete, die sich durch eine 100% Spinpolarisation an der Fermikante auszeichnen. Zur Herstellung der Strukturen wurden InP Substrate der Orientierungen (001), (111)A und (111) B verwendet. Die geringe Gitterfehlanpassung von NiMnSb an InP erlaubt pseudomorphe Strukturen, die (111) Orientierung ermöglicht zusätzlich die Entstehung eines halb-metallischen Interfaces. Für das Wachstum auf InP(001) wurden Prozeduren für die Substratvorbereitung, die Herstellung des gitterangepassten (In, Ga)As und des NiMnSb entwickelt. Sowohl der Einfluss der Flussverhältnisse als auch der Substrattemperatur wurden erforscht und die optimalen Parameter ermittelt. NiMnSb wächst im Frank-van der Merwe Modus, der sich durch Oszillationen des Spekularreflexes bei RHEED Messungen auszeichnet. Untersuchungen der Oberfläche mittels LEED zeigen eine wohldefinierte Rekonstruktion sowie eine niedrige Oberflächenrauhigkeit. Hochauflösende Röntgenbeugungsexperimente unterstützen diese Aussage, zusätzliche zeigen sie eine hohe kristalline Qualität der Schichten. Messungen der NiMnSb Gitterkonstante in lateraler sowie vertikaler Richtung zeigen, dass in allen Schichten dicker als 20 nm sowohl pseudomorphe als auch relaxierte Teilbereiche existieren. Während Schichten um 40 nm teilrelaxierte Bereiche aufweisen, sind diese Bereiche bei Schichten über 100 nm vollständig relaxiert. Tiefenabhängige Röntgenbeugungsexperimente beweisen, dass der relaxierte Teil der NiMnSb Schicht immer über dem pseudomorphen Teil liegt. Die Ausbreitung von Kristalldefekten wurde durch TEM untersucht. Dabei zeigte sich, dass diese Defekte schon sehr bald während des Wachstums entstehen und sich immer weiter ausbreiten, bis sie bei einer Dicke von etwa 40 nm überlappen. Bei diesen Defekten handelt es sich nicht um typische Versetzungen, die aufgrund der Gitterfehlanpassung entstehen, sondern sehr wahrscheinlich um Antiphasen Grenzen die sich im Mn/Sb Untergitter des NiMnSb ausbilden. Zusätzlich zur hohen kristallinen Qualität der NiMnSb Schichten zeigen auch magnetische Messungen eine hohe Homogenität. Die Curie-Temperatur liegt erwartungsgemäß weit über Raumtemperatur. Die Schichten zeigen verschiedene Anisotropien abhängig von der Dicke der Schicht, uniaxiale Anisotropien wurden für Schichten dünner als 15 bzw. dicker als 25 nm beobachtet, dazwischen bildet sich eine Vierfach-Anisotropie aus. Mit steigender Dicke konnte auch eine Abnahme der magnetischen Homogenität beobachtet werden, was auf die Zunahme der Defektdichte bei dickeren Schichten zurückgeführt werden kann. Scheidet man auf dem NiMnSb-Ferromagneten einen Antiferromagneten bestehend aus NiMn ab, so kann der „Exchange Bias“ Effekt beobachtet werden. Auf diese NiMnSb Schichten wurde in einem weiteren Schritt der Halbleiter ZnTe epitaktisch gewachsen, wodurch die Herstellung von NiMnSb/ZnTe/NiMnSb TMR Strukturen ermöglicht wurde. Diese Schichten sind einkristallin und zeichnen sich durch kleine Oberflächen- und Grenzflächenrauhigkeiten aus. Magnetische Messungen dieser Heterostrukturen zeigen, dass beide ferromagnetische Schichten separat schalten können, eine der Grundvoraussetzung für die Beobachtung des TMR Effekts. Bringt man auf diese Strukturen einen Antiferromagneten auf, so kann eine „Exchange Bias“ Wechselwirkung mit der oberen NiMnSb-Schicht beobachtet werden, während die untere unbeeinträchtigt bleibt. In einem weiteren Teil der Arbeit wurde das Wachstum von NiMnSb auf (111) orientierten Substraten untersucht. Dazu wurden InP Kristalle der Orientierung (111)A und (111)B verwendet, die um 1-2° von der exakten Orientierung abweichen, um ein glatteres Wachstum zu ermöglichen. Sowohl die (In,Ga)As als auch NiMnSb-Schichten zeigen wohldefinierte Rekonstruktionen während des Wachstums. Röntgenbeugungsexperimente zeigen die einkristalline Struktur der Proben. Weder für das Wachstum auf InP(111)A noch auf InP(111)B konnte jedoch perfekt glatte Oberflächen während des Wachstums erzielt werden, was auf die Entstehung von pyramidenartigen Facetten aufgrund der Atomkonfiguration an der (111) Oberfläche zurückgeführt werden kann. Ein ähnliches Relaxationsverhalten wie für NiMnSb Schichten auf InP(001) konnte nicht beobachtet werden. Schichten oberhalb einer Dicke von ca. 10 nm beginnen während des Wachstums komplett zu relaxieren, was durch RHEED und Röntgenbeugungsexperimente belegt wurde. Magnetische Messungen ergaben, dass sich die Fehlorientierung der Substratkristalle stark auf das Anisotropieverhalten der NiMnSb(111) Proben auswirkt. In allen Fällen konnte eine uniaxiale Anisotropie beobachtet werden, die sich jeweils senkrecht zur Richtung der Fehlorientierung befindet. KW - Nickelverbindungen KW - Manganverbindungen KW - Antimonverbindungen KW - Heterostruktur KW - Halbmetalle KW - Spintronic KW - MBE KW - halfmetals KW - spintronics KW - MBE Y1 - 2006 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-17771 ER - TY - THES A1 - Bach, Lars T1 - Neuartige nanostrukturierte Halbleiterlaser und Mikroringresonatoren auf InP-Basis für Wellenlängenmultiplexsysteme in der optischen Nachrichtenübertragung T1 - New types of nanostructured semiconductor lasers and micro ring resonators based on InP for dense wavelength division multiplexing systems in optical telecommunication applications N2 - Zusammenfassung Diese Arbeit beschäftigt sich mit der Herstellung und Untersuchung von neuartigen nanostrukturierten Halbleiterbauelementen. Es wird gezeigt, dass durch den Einsatz von optischer und hochauflösender Elektronenstrahl- und Ionenstrahllithographie verschiedene optoelektronische Bauelemente (Laser und Filter) definiert werden können. Die Kombination dieser Definitionsprozesse mit speziellen nass- und trockenchemischen Ätzverfahren erlaubt die Herstellung von Bauelementen mit sehr hoher Genauigkeit, Reproduzierbarkeit und monolithischer Integrationsfähigkeit mit verschiedensten Geometrien und Bereichen innerhalb der Bauelemente. Die Grundlagen zum Verständnis der Funktionsweise und der Hochfrequenzeigenschaften der einzelnen Resonatorarten, Gitterstrukturen und der Laser mit diesen Gitterstrukturen sind in Kapitel 2 zusammen gefasst. Nach einer kurzen Abhandlung des Laserprinzips und des Aufbaus einer Laserdiode, werden die statischen und dynamischen Kenngrößen und Prozesse in den Lasern ausführlich vorgestellt. Besonderes Augenmerk gilt dabei den dynamischen Grundlagen und der Erläuterung eines zusätzlichen Wechselwirkungsprinzips, genannt „Detuned Loading“, im Laser und die sich daraus ergebenden neuen Eigenschaften. Die Auswirkungen der Resonatorgeometrien und Gitterstrukturen auf die spektralen Eigenschaften der Laser sind Bestandteil des zweiten Teiles von Kapitel 2. In Kapitel 3 werden die technologischen Prozesse zur Herstellung der verschiedensten präsentierten Bauelemente im Detail vorgestellt. Die Vorstellung der Charakterisierungsmethoden und der verwendeten Messplätze schließen dieses Kapitel ab. Kapitel 4 beschäftigt sich ausschließlich mit den elektrischen und spektralen Eigenschaften der einzel- und gekoppelten Quadrat-Resonator-Lasern. Kapitel 5 beschäftigt sich mit monomodige DFB- oder DBR-Lasern für Wellenlängenmultiplexsysteme im Wellenlängenbereich um 1.55 µm, als Einzelkomponenten oder in Arrays, die eine exakt einstellbarere Wellenlänge und hoher Modenstabilität aufweisen. Durch die Verwendung des DBR-Prinzips kann eine signifikante Verbesserung der statischen und dynamischen Eigenschaften gegenüber dem DFB-Prinzip erreicht werden. Die Verbesserungen der statischen Eigenschaften beruhen hauptsächlich auf der räumlichen Trennung von Verstärkungs- und Gitterbereich im Fall des DBR-Lasers und der damit verbundenen Erhöhung der Reflexion des Rückfacettenbereiches. Die Trennung bewirkt eine Reduktion der Absorption im Verstärkungsbereich, keine gitterimplantationsbedingten Erhöhung der internen Absorption wie im DFB-Fall, und damit eine Erhöhung der Effizienz was sich wiederum in einer geringern Wärmeproduktion äußert. Aufgrund der aufgeführten Ursachen ist es möglich durch Größenoptimierung der jeweiligen Bereiche Schwellenströme von 8 mA, Effizienzen von 0.375 W/A, Ausgangsleistungen bis zu 70 mW, Betriebsbereiche bis zum 12fachen des Schwellenstromes, Verschiebungen der Wellenlänge mit dem Betriebsstrom von 0.01 nm/mA, eine thermische Belastbarkeiten bis zu 120°C und Seitenmodenunterdrückungen bis zu 67 dB durch das DBR-Laserprinzip zu realisieren. In Kapitel 6 wird ein neues Konzept eines hochfrequenzoptimierten Lasers vorgestellt. Das Prinzip des „Detuned Loading“ ist sehr sensitiv auf die Phasenlage der umlaufenden Welle im Laser und auf die Lage der Hauptmode auf der Reflexionsfunktion des Gitters. Da eine Phasenänderung von 2einer Längenänderung von einigen 100 nm entspricht und dies außerhalb der Herstellungstoleranz liegt, ist eine gezielte Kontrolle dieses Prinzips im DBR-Laser nicht möglich. Dies führte zu einer Weiterentwicklung des DBR-Lasers in einem Laser der einer Phasenkontrolle ermöglicht, genannt CCIG-Laser. Dieser Laser besteht aus einer Lasersektion, einer zentralen Gittersektion und einer angeschlossenen Phasensektion. Durch Strominjektion in die Phasensektion ist es möglich über eine Änderung des Brechungsindexes eine gezielte Einstellung der Phasenlage zu gewährleisten. Die Phasensektion hat keine Auswirkungen auf die statischen elektrischen und spektralen Eigenschaften der Laser. Diese sind sehr gut mit denen der DBR-Laser vergleichbar. Damit war es möglich durch einen CCIG-Laser mit Sektionsgrößen von 500 µm für jede Sektion eine Steigerung der Bandbreite auf einen Rekordwert von 37 GHz, dass entspricht einem Steigerungsfaktor von 4.5 gegenüber Fabry-Perot-Lasern gleicher Länge, zu steigern. N2 - Summary This dissertation occupies with the fabrication and investigation of new types ofnanostructured semiconductor devices. It will be shown that the use of high resolution e-beam and focused ion beam technologies enables the fabrication of several types of optoelectronic devices (laser and filter). The combination of these methods with specific wet- and drychemical etching procedures allows the fabrication of devices with high accuracy, reproducibility and the potential of monolithic integration. The theoretical background for a better understanding of the functionality and the high frequency properties of the several resonator types, grating structures and lasers with these gratings will be given in chapter 2. After a short explanation of the laser principle and the geometry of a laser diode the static and dynamic parameters and processes inside the lasers will be explained. The main focus of this chapter is the explanation of the detuned loading principle in the lasers. This principle is responsible for the new dynamic properties of these lasers. In the second part of chapter 2 the affects of the resonator geometries and grating structures at the spectral properties will be discussed. The technological processes for the fabrication of the several-presented devices will be discussed in detail in chapter 3. Also the measurement methods and setups will be presented in this chapter. Exclusive in chapter 4 the spectral and electrical properties of the single- and coupled squareresonator lasers will be shown. The specific analysis of the geometrical parameters (width, radius) allows a reduction of the size of these lasers down to diameters of D = 30 µm. The square like geometry of these lasers with the four 45° facets results in 8 singularities at the corners of these facets. The content of chapter 5 are the single mode emitting DFB- and DBR-lasers for dense wavelength division multiplexing systems at the 1.55 µm wavelength region. These lasers have a high potential as single devices or in arrays. Based at the in fabrication technology presented in chapter 3 these types of lasers were fabricated at InGaAsP/InP quantum well and InGaAlAs/InAs/InP quantum dash laser structures. Using the FIB technology a wavelength tuning of the emission wavelength over a 100 nm wide wavelength region could be obtained. The DBR-principle leads to a significant improvement of the static and dynamic properties in comparison to the DFB-principle. The enhancement of the static properties results in the separation of the gain- a grating-section and the higher reflectivity of this section. Further this separation leads to a reduction of the absorption inside the gain-section due to the absent of the grating like in the DFB case. A lower absorption results in a higher efficiency and this leads to a lower heat production. Using all these effects it is possible to fabricate DBR-lasers with threshold currents of 8 mA, efficiencies of 0.375 W/A, output powers of more than 70 mW, side mode suppression ratios up to 67 dB and a three times thermal stability. Due to the fact that lasers are key components for telecommunication applications their dynamic properties are of major importance. To get access to the high frequency properties small signal measurements are necessary. Out of these measurements the resonance frequency and the modulation bandwidth can be determined. DBR-lasers show resonance frequencies up to 14 GHz and modulation bandwidths up to 22.5 GHz, which is a rise of 2.5 in comparison to Fabry-Perot-lasers. In chapter 6 the detuned loading principle will be presented in a new type of laser called “CCIG-laser “ (coupled cavity injected grating). This laser consists of three sections: the gain-, the grating- and the phase-section. Due to the fact that this principle is very sensitive to the phase conditions of the waves at the facets a phase section was added. By current injection in this section the phase conditions can be controlled by a variation of the refractive index via the injected current. The spectral and electrical properties of the CCIG-laser are the same like the DBR-laser. Due to the complexity of the CCIG-laser exist a lot of cavities inside of them, which are correlated to the current level of each section. These cavities are of major importance because of the position of the photon-photon-resonance depended on them. For an increase of the modulation bandwidth the three current levels must optimized. The exact influence of each section at the bandwidth will be given in detail in chapter 6. With the CCIG-laser it was able to increase the modulation bandwidth by a factor of 4.5 in comparison to Fabry-Perot-lasers. The best value was 37 GHz which is the highest value world wide up today on InP. KW - Halbleiterlaser KW - Nanostrukturiertes Material KW - Ringresonator KW - DFB-Laser KW - DBR-Laser KW - CCIG-Laser KW - FIB KW - optoelektronische Bauelemente KW - DFB-laser KW - DBR-laser KW - CCIG-laser KW - FIB KW - optoelectronic devices Y1 - 2004 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-9474 ER - TY - THES A1 - Auth, Michael Tilman T1 - Quantitative Electron Paramagnetic Resonance Studies of Charge Transfer in Organic Semiconductors T1 - Quantitative Elektron Paramagnetische Resonanz Untersuchungen von Ladungstransfer Prozessen in Organischen Halbleitern N2 - In the present work we investigated various charge transfer processes, as they appear in the versatile world of organic semiconductors by probing the spin states of the corresponding charge carrier species via electron paramagnetic resonance (EPR) spectroscopy. All studied material systems are carbon-based compounds, either belonging to the group of polymers, fullerenes, or single-wall carbon nanotubes (SWNTs). In the first instance, we addressed the change of the open circuit voltage (Voc) with the fullerene blend stoichiometry in fullerene-based solar cells for organic photovoltaics (OPV). The voltage depends strongly on the energy separation between the lowest unoccupied molecular orbital (LUMO) of the donor and the highest occupied molecular orbital (HOMO) of the acceptor. By exploiting the Gaussian distribution of the charge carriers in a two-level system, and thus also their spins in the EPR experiment, it could be shown that the LUMOs get closer by a few to a few hundred meV when going from pure fullerene materials to a fullerene mixture. The reason for this strong energetic effect is likely the formation of a fullerene alloy. Further, we investigated the chemical doping mechanism of SWNTs with a (6,5)-chirality and their behaviour under optical excitation. In order to determine the unintentional (pre)-doping of SWNTs, EPR spectra of the raw material as well as after different purification steps were recorded. This facilitated the determination of nanotube defects and atmospheric p-doping as the causes of the measured EPR signals. In order to deliberately transfer additional charge carriers to the nanotubes, we added the redox-active substance AuCl3 where we determined an associated doping-yield of (1.5±0.2)%. In addition, a statistical occupation model was developed which can be used to simulate the distribution of EPR active, i.e. unpaired and localised charge carriers on the nanotubes. Finally, we investigated the charge transfer behaviour of (6,5)-SWNTs together with the polymer P3HT and the fullerene PC60BM after optical excitation. N2 - Die vorliegende Arbeit untersuchte mit Hilfe der Elektron Paramagnetischen Resonanz Spektroskopie (EPR) die Ladungsträgerspins bei Ladungstransfer-Prozessen in organischen Halbleitern. Insbesondere wurden hier verschiedene Kohlenstoffverbindungen betrachtet, welche zur Gruppe der Polymere, Fullerene, oder Kohlenstoff-Nanoröhren gehören. Zu Beginn gingen wir auf die Veränderung der Leerlaufspannung in Fulleren Solarzellen für organische photovoltaic (OPV) ein, welche mit der Fulleren Stöchiometry variiert. Die Leerlaufspannung ist entscheidend für das Ladungsstransfer-Verhalten nach erfolgreicher optischer Anregung. Sie hängt stark vom Energieabstand des niedrigsten unbesetzten Molekülorbitals (engl. LUMO) des Donators zum höchsten besetzten Molekülorbital (engl. HOMO) des Akzeptors ab. Hierbei wurde die Gaußsche Verteilungs-Statistik der Ladungsträger, und damit auch deren Spins, in einem zwei Niveau System im EPR Experiment ausgenutzt. Es konnte gezeigt werden, dass sich deren Abstand um wenige bis hin zu wenigen Hundert meV annähert wenn man vom reinen Fulleren Material zu einem Fulleren Gemisch übergeht. Die Ursache für diesen starken energetischen Effekt ist wahrscheinlich die Bildung einer Fulleren-Legierung. Des weiteren betrachteten wir speziell einwandige Kohlenstoff-Nanoröhren der Chiralität (6,5). Untersucht wurde zunächst die chemische Dotierung dieser Systeme und anschließend ihr Verhalten bei optischer Anregung. Um zunächst die ungewünschte (vor)-Dotierung der Nanoröhren zu ermitteln, wurden EPR Spektren in unbehandelter Form, als auch nach unterschiedlichen Aufreinigungsschritten aufgenommen. Dies ermöglichte die Bestimmung von Nanorohr-Defekten und atmosphärischer p-Dotierung als Ursache für das gemessene EPR Signal. Um bewusst zusätzliche Ladungsträger auf die Nanoröhren zu übertragen gaben wir die redox-aktive Substanz AuCl3 hinzu, wo wir eine zugehörige Dotiereffizienz von (1,5±0,2)% ermittelten. Darüber hinaus wurde ein statistisches Modell erarbeitet welches die Verteilung von EPR aktiven, d.h. ungepaarten und lokalisierten Ladungsträgern auf den Nanoröhren simulieren kann. Zum Abschluss betrachteten wir das Ladungstransfer-Verhalten von (6,5)-Nanoröhren zusammen mit dem Polymer P3HT und dem Fulleren PC60BM nach optischer Anregung. KW - Organische Halbleiter KW - EPR Spektroskopie KW - Dotierung KW - Ladungstransfer KW - organic semiconductor KW - carbon nanotube KW - epr spectroskopy KW - doping KW - quantitative epr KW - charge transfer KW - organic photovoltaic KW - spin Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-189513 ER - TY - THES A1 - Aulbach, Julian T1 - Gold-Induced Atomic Wires on Terraced Silicon Surfaces: Formation and Interactions of Silicon Spin Chains T1 - Goldinduzierte Nanodrähte auf gestuften Silizium Oberflächen: Ausbildung und Wechselwirkung von Siliziumspinketten N2 - Atomic nanowires formed by self-assembled growth on semiconducting surfaces represent a feasible physical realization of quasi-1D electron systems and can be used to study fascinating 1D quantum phenomena. The system in the focus of this thesis, Si(553)-Au, is generated by Au adsorption onto a stepped silicon surface. It features two different chain types, interspersed with each other: A Au chain on the terrace, and a honeycomb chain of graphitic silicon located at the step edge. The silicon atoms at the exposed edges of the latter are predicted to be spin-polarized and charge-ordered [1], leading to an ordered array of local magnetic moments referred to as ``spin chains''. The present thesis puts this spin chain proposal to an experimental test. A detailed scanning tunneling microscopy (STM) and scanning tunneling spectroscopy (STS) scrutiny reveals a distinct unoccupied density of states (DOS) feature localized at every third Si step-edge atom, which aligns perfectly with the density functional theory (DFT) prediction. This finding provides strong evidence for the formation of spin chains at the Si(553)-Au step edges, and simultaneously rules out the interpretation of previous studies which attributed the x3 step-edge superstructure to a Peierls instability. To study the formation of spin chains in further detail, an additional member of the so-called Si(hhk)-Au family -- Si(775)-Au -- is analyzed. Based on DFT modeling (performed by S.C. Erwin, Naval Research Laboratory, USA) and detailed STM and STS experiments, a new structure model for this surface is developed, and the absence of spin chains at the Si(775)-Au step edges is demonstrated. The different step-edge charge distributions of all known Si(hhk)-Au surfaces are traced back to an electron transfer between the terrace and the step edge. Accordingly, an unintentional structure defect should create a localized spin at the Si(775)-Au step edge. This prediction is verified experimentally, and suggest that surface chemistry can be used to create and destroy Si spin chains. Having clarified why spin chains form on some Si(hhk)-Au surfaces but not on others, various interaction effects of the Si(553)-Au spin chains are inspected. A collaborative analysis by SPA-LEED (M. Horn-von Hoegen group, University of Duisburg-Essen, Germany), DFT (S.C. Erwin), and STM reveals strong lateral coupling between adjacent spin chains, bearing interesting implications for their magnetic ordering. The centered geometry uncovered leads to magnetic frustration, and may stabilize a 2D quantum spin liquid. Moreover, a complex interplay between neighboring Au and Si chains is detected. Specifically, the interaction is found effectively ``one-way'', i.e., the Si step edges respond to the Au chains but not vice versa. This unidirectional effect breaks the parity of the Si chains, and creates two different configurations of step edges with opposite directionality. In addition to the static properties of the Si(553)-Au surface mentioned above, the occurrence of solitons in both wire types is witnessed in real space by means of high-resolution STM imaging. The solitons are found to interact with one another such that both move in a coupled fashion along the chains. Likewise, STM experiments as a function of the tunneling current suggest an excitation of solitons along the step edge by the STM tunneling tip. Solitons are also found to play an essential role in the temperature-dependent behavior of the Si(553)-Au step edges. It is an accepted fact that the distinct x3 superstructure of the Si(553)-Au step edges vanishes upon heating to room temperature. As a first step in exploring this transition in detail over a large temperature range, a previously undetected, occupied electronic state associated with the localized step-edge spins is identified by means of angle-resolved photoemission spectroscopy (ARPES). A tracking of this state as a function of temperature reveals an order-disorder-type transition. Complementary STM experiments attribute the origin of this transition to local, thermally activated spin site hops, which correspond to soliton-anitsoliton pairs. Finally, a manipulation of the Si(553)-Au atomic wire array is achieved by the stepwise adsorption of potassium atoms. This does not only increase the filling of the Au-induced surface bands culminating in a metal-insulator transition (MIT), but also modifies the Si step-edge charge distribution, as indicated by STM and ARPES experiments. [1] S. C. Erwin and F. Himpsel, Intrinsic magnetism at silicon surfaces, Nat. Commun. 1, 58 (2010). N2 - Durch Selbstorganisation erzeugte atomare Nanodrähte auf Halbleiteroberflächen erlauben die experimentelle Realisierung quasi-eindimensionaler Elektronensysteme und ermöglichen so die Untersuchung faszinierender eindimensionaler Quantenphänomene. Das Nanodrahtsystem im Zentrum dieser Arbeit [Si(553)-Au] lässt sich durch Adsorption von Goldatomen auf eine gestufte Siliziumoberfläche herstellen. Es besteht aus zwei unterschiedlichen, alternierend angeordneten Kettenarten. Auf jeder Terrasse befindet sich eine Goldkette, während die Stufenkanten aus einer graphitartigen Honigwabenstruktur aus Silizium aufgebaut sind. Für die Stufenkantenatome der Siliziumhonigwabenkette wurde eine Ladungsordnung mit vollständiger Spin-Polarisation jedes dritten Stufenkantenatoms vorhergesagt [1]. Dies entspricht einer regelmäßigen Anordnung von lokalen magnetischen Momenten, die als ``Spinketten'' bezeichnet werden. Die vorliegende Arbeit unterzieht diese theoretische Voraussage einem experimentellen Test. Mittels Rastertunnelmikroskopie (engl. scanning tunneling microscopy, STM) und Rastertunnelspektroskopie (engl. scanning tunneling spectroscopy, STS) wurde die lokale Zu-standsdichte entlang der Stufenkante charakterisiert. Die experimentellen Befunde zeigen eine nahezu perfekte Übereinstimmung mit dem theoretisch vorhergesagten Spinketten-Szenario. Gleichzeitig konnte eine bis dato in der Literatur überwiegend favorisierte Peierls-Instabilität ausgeschlossen werden. Um die Ausbildung von Spinketten auf goldinduzierten gestuften Siliziumoberflächen genau-er zu verstehen, wurde ein weiteres Probensystem der sogenannten Si(hhk)-Au-Familie -- Si(775)-Au -- detailliert untersucht. Basierend auf Dichte-Funktional-Theorie Rechnungen (durchgeführt von S.C. Erwin, Naval Research Laboratory, USA) und STM/STS-Experimen-ten wurde ein neues Strukturmodell für diese Oberfläche entwickelt. Außerdem konnte die Abwesenheit von Spinketten an den Si(775)-Au-Stufenkanten nachgewiesen werden. Als Ursache für die variierende Ladungsanhäufung an den Stufenkanten der Si(hhk)-Au-Systeme konnte ein Ladungsaustausch zwischen der Terrasse und der Stufenkante ausgemacht werden. Weiter wurde gezeigt, dass ein struktureller Defekt einen lokalisierten Spin an der Si(775)-Au-Stufenkante erzeugen kann. Dies untermauert das Bild des Ladungstransfers zwischen Terrasse und Stufenkante und legt außerdem nahe, Siliziumspinketten mit Hilfe von Oberflächenchemie zu modifizieren. Neben der Etablierung des Spinketten-Szenarios wurden verschiedene Wechselwirkungseffekte der Si(553)-Au-Spinkette mit ihrer Umgebung untersucht. In Zusammenarbeit mit der Gruppen um Prof. M. Horn-von Hoegen (Universität Duisburg-Essen) und S.C. Erwin konnte eine starke laterale Kopplung zwischen benachbarten Spinketten festgestellt werden, welche interessante Konsequenzen für die magnetische Ordnung der lokalisierten Spins mit sich bringt. Die entdeckte zentrierte Dreiecksanordnung der Spins führt zu magnetischer Frustration und suggeriert die Ausbildung einer zweidimensionalen Spin-Flüssigkeit. Des Weiteren konnte ein unerwartetes Wechselspiel zwischen benachbarten Gold- und Siliziumketten festgestellt werden. Es zeigte sich, dass die Goldketten auf die Siliziumketten einwirken, jedoch nicht umgekehrt. Diese lediglich in einer Richtung wirkende Beeinflussung erzeugt einen Symmetriebruch entlang der Siliziumstufenkante, der dazu führt, dass zwei Arten von Stufenkanten mit unterschiedlicher Direktionalität auftreten. Darüber hinaus konnte mit Hilfe hochaufgelöster STM-Aufnahmen die Existenz von Solitonen in beiden Kettenarten nachgewiesen werden. Dabei stellte sich heraus, dass die beiden Soliton-Typen miteinander wechselwirken und sich daher wider Erwarten nicht unabhängig sondern aneinander gekoppelt durch die Kettenstrukturen bewegen. Weiterhin suggerieren tunnelstromabhängige STM-Messungen, dass sich Solitonen in der Siliziumkette mit der Tunnelspitze des Rastertunnelmikroskops anregen lassen. Solitonen konnte außerdem eine wichtige Rolle im temperaturabhängigen Verhalten der Siliziumstufenkanten zugeschrieben werden. Es war bereits seit Längerem bekannt, dass die ausgeprägte x3 Überstruktur, die sich bei tiefen Temperaturen entlang der Stufenkante beobachten lässt, bei Raumtemperatur verschwindet. Um diese Temperaturabhängigkeit genauer zu untersuchen, wurde ein neu entdeckter, elektronischer Zustand, der sich den an der Stufenkanten lokalisierten Spins zuordnen lässt, mittels winkelaufgelöster Photoelektronenspektroskopie temperaturabhängig analysiert. Dabei stellte sich heraus, dass es sich bei dem Phasenübergang um einen speziellen Ordnungs-Unordnungs-Übergang handelt. Mit Hilfe komplementärer STM-Messungen konnte ein thermisch aktivierter Platzwechsel der lokalisierten Elektronenspins (d.h. die Erzeugung von Soliton-Antisoliton-Paaren) für das temperaturabhängige Verhalten der Siliziumstufenkante verantwortlich gemacht werden. Weiterhin konnte eine gezielte Manipulation des Si(553)-Au-Nanodrahtsystems durch sukzessive Dotierung mit Kaliumatomen realisiert werden. Dabei wurde ein Anstieg der Befüllung der goldinduzierten Oberflächenbänder, der letztendlich zu einem Metall-Isolator-Übergang führt, beobachtet. Außerdem deuten die experimentellen Befunde auf eine Modifizierung der Spinketten entlang der Stufenkante hin. [1] S. C. Erwin and F. Himpsel, Intrinsic magnetism at silicon surfaces, Nat. Commun. 1, 58 (2010). KW - Rastertunnelmikroskopie KW - Spinkette KW - ARPES KW - Tunnelspektroskopie KW - Quasi-1D Elektronensysteme KW - Atomketten Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-169347 ER - TY - THES A1 - Arnold, Johannes F. T. T1 - Funktionelle Bildgebung der Lunge und des Bronchialkarzinoms mittels Magnetresonanztomographie T1 - Functional Magnetic Resonance Imaging of the Lung and Non-Small-Cell Lung Cancer N2 - Ziel dieser Arbeit war es, die Magnetresonanztomographie (MRT) an der Lunge als Alternative zur traditionellen Lungenbildgebung voranzutreiben. So sollten MRT-Verfahren zur regionalen und quantitativen Lungenfunktionsprüfung für die klinische Routine entwickelt werden. Im Hinblick auf die Strahlentherapie von Patienten mit Bronchialkarzinom sollen funktionelle Lungenareale erkannt werden, um diese während der Bestrahlung optimal schonen zu können. An den zahlreichen Luft-Gewebe-Grenzflächen in der Lunge entstehen Magnetfeldinhomogenitäten. Daraus resultiert ein schneller Zerfall des MRT-Signals in der Lunge. Es wurde in dieser Arbeit ein Ansatz aufgezeigt, um die Ursache für den raschen Signalzerfall, nämlich die unterschiedlichen magnetischen Suszeptibilitäten von Lufträumen und Lungengewebe, zu beseitigen. Durch die intravaskuläre Injektion von paramagnetischen Kontrastmitteln kann die Suszeptibilität des Blutes an die Suszeptibilität der Lufträume angeglichen werden. Durch die Entwicklung einer MR-kompatiblen aktiven Atemkontrolle (MR-ABC) wurde in dieser Arbeit ein weiteres fundamentales Problem der Lungen-MRT adressiert: Die Bewegung während der Datenakquisition. Die MR-ABC detektiert Herzschlag und Atemposition und ist in der Lage die Atembewegung in jeder beliebigen Atemphase reproduzierbar für eine definierte Zeit auszusetzen. Dies wird durch einen Verschluss der Atemluftzufuhr realisiert. Traditionelle Verfahren können zwar ebenfalls die Atemphase detektieren, gestatten jedoch nicht deren Konservierung. Es wurde demonstriert, dass mit der MR-ABC hochauflösende Bilder der Lunge in hoher Bildqualität und durch die Verwendung langer Akquisitionsfenster in relativ kurzer Messzeit erreicht werden können. Eine regionale Lungenfunktionsprüfung ist für die Diagnose und Evaluierung vieler Krankheitsbilder vorteilhaft. In diesem Sinne wird seit einigen Jahren das Potential der Sauerstoff-verstärkten Lungen-MRT erforscht, die auf den paramagnetischen Eigenschaften des molekularen Sauerstoffs basiert. Im Blut gelöster Sauerstoff führt zu einer Verkürzung der T1-Relaxationszeit. Statt diese T1-Verkürzung quantitativ zu bestimmen wird aus praktischen Gründen meist ein T1-gewichteter Ansatz gewählt. In dieser Arbeit wurde jedoch gezeigt, dass nicht-quantitative Verfahren ein erhebliches Risiko zur Falschinterpretation beinhalten. Um Fehldiagnosen zu vermeiden, sollten deshalb prinzipiell quantitative Methoden zur Messung der durch die Sauerstoff-Verstärkung bedingten T1-Verkürzung in der Lunge verwendet werden. Herkömmliche Techniken zur quantitativen T1-Messung benötigen allerdings längere Messzeiten. Deshalb war zur Vermeidung von Bewegungsartefakten bisher die Datenaufnahme im Atemanhaltezustand notwendig. Wiederholtes Atemanhalten von mehreren Sekunden Dauer ist allerdings für einige Patienten sehr belastend. Aus diesem Grund wurden in dieser Arbeit zwei Methoden entwickelt, die eine quantitative Lungenfunktionsprüfung mittels MRT bei freier Atmung der Patienten ermöglichen. Eine gute Sauerstoffversorgung des Tumors wirkt sich positiv auf den Erfolg der Bestrahlung aus. Ein Ansatz zur Verbesserung der Strahlentherapie des Bronchialkarzinoms könnte daher in der Beatmung der Patienten mit hyperoxischen hypercapnischen Atemgasen während der Bestrahlung bestehen. In diesem Zusammenhang könnte die quantitative Messung der T1-Veränderung im Tumor nach Carbogenatmung ein Selektionskriterium darstellen, um diejenigen Patienten zu identifizieren, die von einer Carbogenbeatmung während der Bestrahlung profitieren können. Die Differenzierung zwischen vitalem Tumorgewebe, Nekrosen und atelektatischem Lungengewebe ist von großer Bedeutung bei der Bestrahlungsplanung des Bronchialkarzinoms. Einen neuen Ansatz bildet die in dieser Arbeit vorgestellte Magnetiserungstransfer-MRT. Um einen Magnetisierungstransfer zu erzeugen, wurde ein speziell auf die Bildgebung an der Lunge optimiertes Präparationsmodul entworfen. In Verbindung mit einer schnellen Bildakquisitionstechnik konnte die Magnetisierungstransfer-Lungenbildgebung in einem kurzen Atemstopp durchgeführt werden. Diese Technik wurde an mehreren Patienten mit Bronchialkarzinom evaluiert und die Ergebnisse mit denen der Fluor-Deoxyglykose-Positronen-Emissions-Tomographie (FDG-PET) verglichen. Es wurde festgestellt, dass mit diesem MRT-Verfahren ähnliche diagnostische Erkenntnisse erzielt werden können. Allerdings besitzt die MRT Vorteile im Hinblick auf räumliche Auflösung, Messzeit, Bildqualität, Kosten und Strahlenbelastung. Das erhebliche Potential für die Bestrahlungsplanung des Bronchialkarzinoms durch eine Magnetisierungstransfer-Bildgebung wurde damit nachgewiesen. N2 - The purpose of this work was to advance magnetic resonance imaging (MRI) to become an additional beneficial modality for lung imaging. MRI techniques for regional and quantitative assessment of pulmonary function, capable for clinical routine use, should be developed. Areas of sound and functional lung should be detected especially in patients with bronchial carcinoma undergoing radiotherapy, to be able to achieve an optimal protection for this kind of tissue during the irradiation process. Magnetic field inhomogeneities emerge from the numerous air-tissue-interfaces of the lung, causing an accelerated MRI signal decay. Therefore, this work postulates a new approach to eliminate the source of this signal decay acceleration, namely the differences in magnetic susceptibility between air sacks and lung tissue. By intravascular injection of paramagnetic contrast agent, the susceptibility of blood can be matched with the susceptibility of the air spaces. Removing the susceptibility differences could prolong the effective transverse relaxation time T2* by many factors. The development of an MR-compatible active breathing control device (MR-ABC) addressed another fundamental obstacle of lung MRI: motion occurring during the data sampling process. MR-ABC allows for the detection of heart and respiratory phases and is able to reproducibly freeze the breathing motion in any desired respiratory phase for a predefined amount of time. This is performed by a shutter that closes the breathing gas delivery. It was demonstrated that using MR-ABC high-resolution high-quality images of the lung can be acquired in a comparably short amount of time due to prolonged acquisition intervals. Regional assessment of pulmonary function is beneficial for diagnosis and evaluation of many lung diseases. In this respect, in the last few years the potential of oxygen-enhanced lung MRI based upon the paramagnetic properties of the molecular oxygen, started to be explored. Dissolved oxygen in the blood leads to a decrease in T1 relaxation time. Due to practical reasons this drop in T1 relaxation time is commonly assessed by T1-weighted imaging approaches instead of quantitative T1 measurements. However, in this work it was demonstrated that non-quantitative approaches comprehend severe risks of misinterpretation. Therefore, to avoid misdiagnosis, quantitative measurements of the oxygen-based T1 decrement in the lung should always be used. On the other hand, common quantitative T1 measurement techniques require longer measurement times, and therefore require imaging during breath-holding to avoid motion artifacts. Repeated breath-holding of several seconds may be very demanding for some patients, especially for those with lung cancer. For this reason, in this work two methods were developed to allow for a quantitative assessment of regional lung function by MRI during free-breathing. These techniques were applied to investigate regional oxygen transfer in lung cancer patients. Local defects of lung function could be demonstrated in these patients. A good oxygen supply of the tumor tissue is positively correlated to the success of radiation therapy. Reoxygenation of former hypoxic areas can improve the sensitivity of the tumor to irradiation. Thus, one approach to improve radiotherapy of bronchogenic carcinoma could be to use hyperoxic, hypercapnic breathing gases such as carbogen during the irradiation. In this respect, the quantitative measurement of the T1 alteration in the tumor due to the switching of breathing gas to carbogen could provide a selection criterion for patients who can benefit from an ARCON approach. In a preliminary study, the T1 alteration in the tumor after switching of breathing gas to carbogen was assessed in a variety of lung cancer patients. Differentiation of vital tumor, necrotic tissue and atelectasis is of paramount importance in radiation therapy planning of bronchial carcinoma. Unfortunately, discrimination of these tissues by using computer tomography or positron emission tomography is usually problematic in the clinical routine. This work proposes a new approach based on magnetization transfer MRI. The extent of magnetization transfer is mainly dependent on the macromolecular environment of the protons, which is different in tumor tissue and atelectatic tissue. To produce magnetization transfer, a magnetization preparation module was developed and particularly optimized for application to lung imaging. In conjunction with a fast readout imaging sequence, magnetization transfer lung imaging could be performed in a single short breath-hold period. This technique was evaluated in several patients with bronchial carcinoma. The results of magnetization transfer imaging were compared to the results of a fluorodeoxyglucose positron emission tomography (FDG-PET) investigation. It was found that using the MRI technique, similar diagnostic information as with the FDG-PET could be obtained. KW - Magnetische Resonanz KW - Lunge KW - Nicht-kleinzelliges Bronchialkarzinom KW - MRI KW - Lung KW - NSCLC Y1 - 2008 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-26388 ER - TY - THES A1 - Armer, Melina Brigitte Melanie T1 - High-Quality Lead-Free Double Perovskite Single Crystals and their Optical Properties T1 - Optische Eigenschaften von bleifreien Doppelperowskit Einkristallen N2 - The presented thesis deals with the investigation of the characteristic physical properties of lead-free double perovskites. For this purpose lead-free double perovskite single crystals were grown from solution. In order to assess the influence of growth temperature on tail states in the material, the crystals were studied using Photoluminescence Excitation (PLE) and Transmission measurements. Additionally, lead-free double perovskite solar cells and thin films were investigated to address the correlation of precursor stoichiometry and solar cell efficiency. In a last step a new earth abundant lead-free double perovskite was introduced and its physical properties were studied by photoluminescene and absorptance. Like this it was possible to assess the suitability of this material for solar cell applications in the future. N2 - Um die charakteristischen physikalischen Eigenschaften von bleifreien Doppelperowskiten näher zu untersuchen, wurden im Rahmen dieser Arbeit Einkristalle aus einer Lösung gezogen. Um den Einfluss der Wachstumstemperatur auf sogenannte „tail states“ in den Kristallen zu untersuchen, wurde hierbei auf optische Methoden wie „photoluminescence excitation“ (PLE) und Transmission zurückgegriffen. Des Weiteren wurden Solarzellen mit bleifreiem Doppelperowskit als Absorberschicht näher untersucht. Hierbei wurden unter anderem Dünnfilme genutzt, um den Einfluss der Filmstöchiometrie auf die Solarzelleffizienzen zu untersuchen. Zuletzt wurde ein weiteres Doppelperowskitmaterial mittels Photolumineszenz und Absorptionmessungen untersucht um Rückschlüsse auf seine Eignung als Absorberschicht in Solarzellen zu ziehen. KW - Perowskit KW - Fotovoltaik KW - Kristallzüchtung KW - Perovskite KW - Lead-free double perovskite KW - crystal growth KW - Photoluminescence KW - Solar cell Y1 - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-327503 ER - TY - THES A1 - Anneser, Katrin T1 - Elektrochemische Doppelschichtkondensatoren zur Stabilisierung fluktuierender photovoltaischer Leistung T1 - Electric double layer capacitors for stabilizing intermittent photovoltaic power N2 - Der Ausbau der regenerativen Energiequellen führt vermehrt zu unvorhersehbaren Schwankungen der erzeugten Leistung, da Windkraft und Photovoltaik von natürlichen Bedingungen abhängen. Gerade Kurzzeitfluktuationen im Sekunden- bis Minutenbereich, die bei Solarzellen durch die Verschattung von vorüberziehenden Wolken zustande kommen, wird bislang wenig Beachtung geschenkt. Kurzzeitspeicher müssen eine hohe Zyklenstabilität aufweisen, um zur Glättung dieser Leistungsfluktuationen in Frage zu kommen. Im Rahmen der vorliegenden Dissertation wurden elektrochemische Doppelschichtkondensatoren für die Kopplung mit Siliziumsolarzellen und organischen Solarmodulen mit Hilfe von Simulationen und Messungen untersucht. Zusätzlich wurden grundlegende Fragestellungen zur Prozessierung und Alterung von Doppelschichtkondensatoren im Hinblick auf ein in der Literatur bereits diskutiertes System betrachtet, das beide Komponenten in einem Bauteil integriert - den sogenannten photocapacitor. Um die Druckbarkeit des gesamten elektrochemischen Doppelschichtkondensators zu ermöglichen, wurde der konventionell verwendete Flüssigelektrolyt durch einen Polymer-Gel-Elektrolyten auf Basis von Polyvinylalkohol und einer Säure ersetzt. Durch eine Verbesserung der Prozessierung konnte ein größerer Anteil der spezifischen Fläche der porösen Kohlenstoffelektroden vom Elektrolyten benetzt und somit zur Speicherung genutzt werden. Die Untersuchungen zeigen, dass mit Polymer-Gel-Elektrolyten ähnliche Kapazitäten erreicht werden wie mit Flüssigelektrolyten. Im Hinblick auf die Anwendung im gekoppelten System muss der elektrochemische Doppelschichtkondensator den gleichen Umweltbedingungen hinsichtlich Temperatur und Luftfeuchte standhalten wie die Solarzelle. Hierzu wurden umfangreiche Alterungstests durchgeführt und festgestellt, dass die Kapazität zwar bei Austrocknung des wasserhaltigen Polymer-Gel-Elektrolyten sinkt, bei einer Wiederbefeuchtung aber auch eine Regeneration des Speichers erfolgt. Zur passenden Auslegung des elektrochemischen Doppelschichtkondensators wurde eine detaillierte Analyse der Leistungsfluktuationen durchgeführt, die mit einem eigens entwickelten MPP-Messgerät an organischen Solarmodulen gemessen wurden. Anhand der Daten wurde analysiert, welche Energiemengen für welche Zeit im Kurzzeitspeicher zwischengespeichert werden müssen, um eine effiziente Glättung der ins Netz einzuspeisenden Leistung zu erreichen. Aus der Statistik der Fluktuationen wurde eine Kapazität berechnet, die als Richtwert in die Simulationen einging und dann mit anderen Kapazitäten verglichen wurde. Neben einem idealen MPP-Tracking für verschiedene Arten von Solarzellen und Beleuchtungsprofilen konnte die Simulation auch die Kopplung aus Solarzelle und elektrochemischem Doppelschichtkondensator mit zwei verschiedenen Betriebsstrategien nachbilden. Zum einen wurde ein fester Lastwiderstand genutzt, zum anderen eine Zielspannung für den Kurzzeitspeicher und somit auch die Solarzelle vorgegeben und der Lastwiderstand variabel so angepasst, dass die Zielspannung gehalten wird. Beide Betriebsmethoden haben einen Energieverlust gegenüber der MPP-getrackten Solarzelle zu verzeichnen, führen aber zu einer Glättung der Leistung des gekoppelten Systems. Die Simulation konnte für Siliziumsolarzellen mit einem Demonstratorversuch im Labor und für organische Solarzellen unter realen Bedingungen validiert werden. Insgesamt ergibt sich eine vielversprechende Glättung der Leistungsfluktuationen von Solarzellen durch den Einsatz von elektrochemischen Doppelschichtkondensatoren. N2 - The increased usage of regenerative energy sources leads to more unpredictable fluctuations in power output, as wind power and photovoltaics depend on natural conditions. Especially short-term fluctuations in the range of seconds to minutes, which occur in solar cells due to the shading by passing clouds, have received little attention so far. Corresponding short-term storage units that can be used to smooth these power fluctuations must have a high cycle stability. In the scope of this thesis the suitability of electrochemical double layer capacitors for coupling with silicon solar cells and organic solar modules was investigated with simulations and measurements. Processing methods and aging of electrochemical double layer capacitors in respect to an integrated system consisting of both components - already discussed in the literature as the so-called photocapacitor - were considered. As the liquid electrolyte was replaced by a polymer gel electrolyte based on polyvinyl alcohol and an acid in order to enable printability of the entire electrochemical double-layer capacitor. An increase of the capacitance to the level of the capacitance for electrodes with liquid electrolytes was achieved by improved processing in which a larger proportion of the specific area of the porous carbon electrodes could be wetted by the electrolyte and thus used for storage. In the application as coupled system the electrochemical double-layer capacitor must withstand the same environmental conditions with regard to temperature and humidity as the solar cell. Extensive aging tests were carried out and it was found that, although the capacitance decreases when the water-containing polymer gel electrolyte dries out, remoistening also regenerates the storage capacitance. A detailed analysis of the power fluctuations, which were measured under real conditions with small organic solar modules using a specially developed MPP measuring device, was carried out to determine the appropriate characteristics of the electrochemical double layer capacitor. Using a mathematically smoothed mean curve, it was determined which amounts of energy have to be stored in the short-term storage device for which time in order to achieve the smoothed curve. From the statistics of the fluctuations a capacitance could be calculated which was used as a guide value in the simulations and could then be compared to the impact of other capacities. In addition to ideal MPP tracking for different types of solar cells and lighting profiles, the simulation was also able to model the coupling of solar cell and electrochemical double layer capacitor with two different operating strategies. On the one hand a fixed load resistance was used, on the other hand a target voltage for the short-term storage device and thus also for the solar cell was specified. The load resistance was variably adapted so that the target voltage was reached. Both operating methods show an energy loss compared to the MPP tracked solar cell without storage component, but lead to smoothing of the power output of the coupled system. The simulation could be validated for silicon solar cells with a demonstrator test in the laboratory and for organic solar cells on the external test setup under real conditions. Overall, the use of electrochemical double layer capacitors results in a promising smoothing of the power fluctuations of solar cells. KW - Energie KW - Photovoltaik KW - Energiespeicher Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-199339 ER - TY - THES A1 - Andelovic, Kristina T1 - Characterization of arterial hemodynamics using mouse models of atherosclerosis and tissue-engineered artery models T1 - Charakterisierung arterieller Hämodynamiken in atherosklerotischen Mausmodellen und tissue-engineerten Arterienmodellen N2 - Within this thesis, three main approaches for the assessment and investigation of altered hemodynamics like wall shear stress, oscillatory shear index and the arterial pulse wave velocity in atherosclerosis development and progression were conducted: 1. The establishment of a fast method for the simultaneous assessment of 3D WSS and PWV in the complete murine aortic arch via high-resolution 4D-flow MRI 2. The utilization of serial in vivo measurements in atherosclerotic mouse models using high-resolution 4D-flow MRI, which were divided into studies describing altered hemodynamics in late and early atherosclerosis 3. The development of tissue-engineered artery models for the controllable application and variation of hemodynamic and biologic parameters, divided in native artery models and biofabricated artery models, aiming for the investigation of the relationship between atherogenesis and hemodynamics Chapter 2 describes the establishment of a method for the simultaneous measurement of 3D WSS and PWV in the murine aortic arch at, using ultra high-field MRI at 17.6T [16], based on the previously published method for fast, self-navigated wall shear stress measurements in the murine aortic arch using radial 4D-phase contrast MRI at 17.6 T [4]. This work is based on the collective work of Dr. Patrick Winter, who developed the method and the author of this thesis, Kristina Andelovic, who performed the experiments and statistical analyses. As the method described in this chapter is basis for the following in vivo studies and undividable into the sub-parts of the contributors without losing important information, this chapter was not split into the single parts to provide fundamental information about the measurement and analysis methods and therefore better understandability for the following studies. The main challenge in this chapter was to overcome the issue of the need for a high spatial resolution to determine the velocity gradients at the vascular wall for the WSS quantification and a high temporal resolution for the assessment of the PWV without prolonging the acquisition time due to the need for two separate measurements. Moreover, for a full coverage of the hemodynamics in the murine aortic arch, a 3D measurement is needed, which was achieved by utilization of retrospective navigation and radial trajectories, enabling a highly flexible reconstruction framework to either reconstruct images at lower spatial resolution and higher frame rates for the acquisition of the PWV or higher spatial resolution and lower frame rates for the acquisition of the 3D WSS in a reasonable measurement time of only 35 minutes. This enabled the in vivo assessment of all relevant hemodynamic parameters related to atherosclerosis development and progression in one experimental session. This method was validated in healthy wild type and atherosclerotic Apoe-/- mice, indicating no differences in robustness between pathological and healthy mice. The heterogeneous distribution of plaque development and arterial stiffening in atherosclerosis [10, 12], however, points out the importance of local PWV measurements. Therefore, future studies should focus on the 3D acquisition of the local PWV in the murine aortic arch based on the presented method, in order to enable spatially resolved correlations of local arterial stiffness with other hemodynamic parameters and plaque composition. In Chapter 3, the previously established methods were used for the investigation of changing aortic hemodynamics during ageing and atherosclerosis in healthy wild type and atherosclerotic Apoe-/- mice using the previously established methods [4, 16] based on high-resolution 4D-flow MRI. In this work, serial measurements of healthy and atherosclerotic mice were conducted to track all changes in hemodynamics in the complete aortic arch over time. Moreover, spatially resolved 2D projection maps of WSS and OSI of the complete aortic arch were generated. This important feature allowed for the pixel-wise statistical analysis of inter- and intragroup hemodynamic changes over time and most importantly – at a glance. The study revealed converse differences of local hemodynamic profiles in healthy WT and atherosclerotic Apoe−/− mice, with decreasing longWSS and increasing OSI, while showing constant PWV in healthy mice and increasing longWSS and decreasing OSI, while showing increased PWV in diseased mice. Moreover, spatially resolved correlations between WSS, PWV, plaque and vessel wall characteristics were enabled, giving detailed insights into coherences between hemodynamics and plaque composition. Here, the circWSS was identified as a potential marker of plaque size and composition in advanced atherosclerosis. Moreover, correlations with PWV values identified the maximum radStrain could serve as a potential marker for vascular elasticity. This study demonstrated the feasibility and utility of high-resolution 4D flow MRI to spatially resolve, visualize and analyze statistical differences in all relevant hemodynamic parameters over time and between healthy and diseased mice, which could significantly improve our understanding of plaque progression towards vulnerability. In future studies the relation of vascular elasticity and radial strain should be further investigated and validated with local PWV measurements and CFD. Moreover, the 2D histological datasets were not reflecting the 3D properties and regional characteristics of the atherosclerotic plaques. Therefore, future studies will include 3D plaque volume and composition analysis like morphological measurements with MRI or light-sheet microscopy to further improve the analysis of the relationship between hemodynamics and atherosclerosis. Chapter 4 aimed at the description and investigation of hemodynamics in early stages of atherosclerosis. Moreover, this study included measurements of hemodynamics at baseline levels in healthy WT and atherosclerotic mouse models. Due to the lack of hemodynamic-related studies in Ldlr-/- mice, which are the most used mouse models in atherosclerosis research together with the Apoe-/- mouse model, this model was included in this study to describe changing hemodynamics in the aortic arch at baseline levels and during early atherosclerosis development and progression for the first time. In this study, distinct differences in aortic geometries of these mouse models at baseline levels were described for the first time, which result in significantly different flow- and WSS profiles in the Ldlr-/- mouse model. Further basal characterization of different parameters revealed only characteristic differences in lipid profiles, proving that the geometry is highly influencing the local WSS in these models. Most interestingly, calculation of the atherogenic index of plasma revealed a significantly higher risk in Ldlr-/- mice with ongoing atherosclerosis development, but significantly greater plaque areas in the aortic arch of Apoe-/- mice. Due to the given basal WSS and OSI profile in these two mouse models – two parameters highly influencing plaque development and progression – there is evidence that the regional plaque development differs between these mouse models during very early atherogenesis. Therefore, future studies should focus on the spatiotemporal evaluation of plaque development and composition in the three defined aortic regions using morphological measurements with MRI or 3D histological analyses like LSFM. Moreover, this study offers an excellent basis for future studies incorporating CFD simulations, analyzing the different measured parameter combinations (e.g., aortic geometry of the Ldlr-/- mouse with the lipid profile of the Apoe-/- mouse), simulating the resulting plaque development and composition. This could help to understand the complex interplay between altered hemodynamics, serum lipids and atherosclerosis and significantly improve our basic understanding of key factors initiating atherosclerosis development. Chapter 5 describes the establishment of a tissue-engineered artery model, which is based on native, decellularized porcine carotid artery scaffolds, cultured in a MRI-suitable bioreactor-system [23] for the investigation of hemodynamic-related atherosclerosis development in a controllable manner, using the previously established methods for WSS and PWV assessment [4, 16]. This in vitro artery model aimed for the reduction of animal experiments, while simultaneously offering a simplified, but completely controllable physical and biological environment. For this, a very fast and gentle decellularization protocol was established in a first step, which resulted in porcine carotid artery scaffolds showing complete acellularity while maintaining the extracellular matrix composition, overall ultrastructure and mechanical strength of native arteries. Moreover, a good cellular adhesion and proliferation was achieved, which was evaluated with isolated human blood outgrowth endothelial cells. Most importantly, an MRI-suitable artery chamber was designed for the simultaneous cultivation and assessment of high-resolution 4D hemodynamics in the described artery models. Using high-resolution 4D-flow MRI, the bioreactor system was proven to be suitable to quantify the volume flow, the two components of the WSS and the radStrain as well as the PWV in artery models, with obtained values being comparable to values found in literature for in vivo measurements. Moreover, the identification of first atherosclerotic processes like intimal thickening is achievable by three-dimensional assessment of the vessel wall morphology in the in vitro models. However, one limitation is the lack of a medial smooth muscle cell layer due to the dense ECM. Here, the utilization of the laser-cutting technology for the generation of holes and / or pits on a microscale, eventually enabling seeding of the media with SMCs showed promising results in a first try and should be further investigated in future studies. Therefore, the proposed artery model possesses all relevant components for the extension to an atherosclerosis model which may pave the way towards a significant improvement of our understanding of the key mechanisms in atherogenesis. Chapter 6 describes the development of an easy-to-prepare, low cost and fully customizable artery model based on biomaterials. Here, thermoresponsive sacrificial scaffolds, processed with the technique of MEW were used for the creation of variable, biomimetic shapes to mimic the geometric properties of the aortic arch, consisting of both, bifurcations and curvatures. After embedding the sacrificial scaffold into a gelatin-hydrogel containing SMCs, it was crosslinked with bacterial transglutaminase before dissolution and flushing of the sacrificial scaffold. The hereby generated channel was subsequently seeded with ECs, resulting in an easy-to-prepare, fast and low-cost artery model. In contrast to the native artery model, this model is therefore more variable in size and shape and offers the possibility to include smooth muscle cells from the beginning. Moreover, a custom-built and highly adaptable perfusion chamber was designed specifically for the scaffold structure, which enabled a one-step creation and simultaneously offering the possibility for dynamic cultivation of the artery models, making it an excellent basis for the development of in vitro disease test systems for e.g., flow-related atherosclerosis research. Due to time constraints, the extension to an atherosclerosis model could not be achieved within the scope of this thesis. Therefore, future studies will focus on the development and validation of an in vitro atherosclerosis model based on the proposed bi- and three-layered artery models. In conclusion, this thesis paved the way for a fast acquisition and detailed analyses of changing hemodynamics during atherosclerosis development and progression, including spatially resolved analyses of all relevant hemodynamic parameters over time and in between different groups. Moreover, to reduce animal experiments, while gaining control over various parameters influencing atherosclerosis development, promising artery models were established, which have the potential to serve as a new platform for basic atherosclerosis research. N2 - Im Rahmen dieser Arbeit wurden drei Hauptansätze zur Bewertung und Untersuchung der veränderten Hämodynamik wie Wandschubspannung, des oszillatorischen Scherindex und der arteriellen Pulswellengeschwindigkeit bei der Entwicklung und Progression der Atherosklerose durchgeführt: 1. Die Etablierung einer schnellen Methode zur gleichzeitigen Bestimmung der 3D-Wandschubspannung und der Pulswellengeschwindigkeit im gesamten Aortenbogen der Maus mittels hochauflösender 4D-Fluss-MRT 2. Die Verwendung von seriellen in vivo Messungen in atherosklerotischen Mausmodellen mittels hochauflösender 4D-Fluss-MRT, die in Studien zur Beschreibung der veränderten Hämodynamik bei später und früher Atherosklerose aufgeteilt wurden 3. Die Entwicklung von tissue-engineerten Arterienmodellen für die kontrollierte Anwendung und Variation von hämodynamischen und biologischen Parametern, unterteilt in native Arterienmodelle und biofabrizierte Arterienmodelle, mit dem Ziel, die Beziehung zwischen Atherogenese und veränderter Hämodynamik zu untersuchen Kapitel 2 beschreibt die Etablierung einer Methode zur gleichzeitigen Messung von 3D-Wandschubspannung und Pulswellengeschwindigkeit im Aortenbogen der Maus unter Verwendung der Ultrahochfeld-MRT bei 17,6T [16], die auf der zuvor veröffentlichten Methode zur schnellen, selbstnavigierten Messung der Wandschubspannung im Aortenbogen der Maus unter Verwendung der radialen 4D-Phasenkontrast-MRT bei 17,6T [4] basiert. Dieses Projekt basiert auf der gemeinsamen Arbeit von Dr. Patrick Winter, der diese Methode entwickelt hat, und der Autorin dieser Thesis, Kristina Andelovic, die die Experimente und statistischen Analysen durchgeführt hat. Da die in diesem Kapitel beschriebene Methode die Grundlage für die folgenden in vivo Studien darstellt und sich nicht in die einzelnen Beiträge der Autoren aufteilen lässt, ohne dass wichtige Informationen verloren gehen, wurde dieses Kapitel nicht in die einzelnen Teile aufgeteilt, um grundlegende Informationen über die Mess- und Analysemethoden zu liefern und somit eine bessere Verständlichkeit für die folgenden Studien zu gewährleisten. Die größte Herausforderung in diesem Kapitel bestand darin, die Anforderung an eine hohe räumliche Auflösung zur Bestimmung der Geschwindigkeitsgradienten an der Gefäßwand für die WSS-Quantifizierung und an eine hohe zeitliche Auflösung für die Bestimmung der Pulswellengeschwindigkeit zu erfüllen, ohne die Messzeit aufgrund der Notwendigkeit von zwei separaten Messungen zu verlängern. Darüber hinaus ist für eine vollständige Erfassung der Hämodynamik im murinen Aortenbogen eine vollständige 3D-Messung des Aortenbogens erforderlich, die durch die Nutzung der retrospektiven Navigation und radialen Trajektorien erreicht wurde. Dies wurde durch ein hoch flexibles Rekonstruktionssystem ermöglicht, das entweder Bilder mit geringerer räumlicher Auflösung und höheren Bildraten für die Erfassung der Pulswellengeschwindigkeit oder mit höherer räumlicher Auflösung und niedrigeren Bildraten für die Erfassung der 3D-WSS in einer angemessenen Messzeit von nur 35 Minuten rekonstruieren konnte. Die in vivo-Bestimmung aller relevanter hämodynamischen Parameter, die mit der Entwicklung und dem Fortschreiten der Atherosklerose zusammenhängen, wurde somit in einer einzigen experimentellen Sitzung ermöglicht. Die Methode wurde an gesunden Wildtyp- und atherosklerotischen Apoe-/- Mäusen validiert, wobei keine Unterschiede in der Robustheit der Messungen zwischen pathologischen und gesunden Mäusen festgestellt werden konnten. Die heterogene Verteilung der Plaqueentwicklung und Arterienversteifung in der Atherosklerose [10, 12] weist jedoch auf die Wichtigkeit lokaler PWV-Messungen hin. Zukünftige Studien sollten sich daher auf die 3D-Erfassung der lokalen PWV im murinen Aortenbogen auf Grundlage der vorgestellten Methode konzentrieren, um räumlich aufgelöste Korrelationen der lokalen arteriellen Steifigkeit mit anderen hämodynamischen Parametern und der Plaquezusammensetzung zu ermöglichen. In Kapitel 3 wurden die zuvor etablierten Methoden zur Untersuchung der sich verändernden Hämodynamik in der Aorta während des Alterns und der Atherosklerose bei gesunden Wildtyp- und atherosklerotischen Apoe-/- Mäusen verwendet [4, 16], die auf hochauflösender 4D-Fluss MRT basieren. In dieser Arbeit wurden serielle Messungen an gesunden und atherosklerotischen Mäusen durchgeführt, um alle Veränderungen der Hämodynamik im gesamten Aortenbogen über die Zeit zu verfolgen. Zudem wurden in dieser Arbeit räumlich aufgelöste 2D-Projektionskarten der WSS und des OSI des gesamten Aortenbogens generiert. Diese Methode ermöglichte die pixelweise statistische Analyse der Unterschiede und hämodynamischen Veränderungen zwischen und innerhalb von Gruppen im Zeitverlauf und die Visualisierung auf einen Blick. Die Studie ergab sich gegensätzlich entwickelnde lokale hämodynamische Profile bei gesunden WT- und atherosklerotischen Apoe-/- Mäusen, wobei die longWSS über die Zeit abnahm und der OSI zunahm, während die PWV bei gesunden Mäusen konstant blieb. Im Gegensatz nahm die longWSS zu und der OSI bei kranken Mäusen ab, während die PWV über die Zeit zunahm. Darüber hinaus wurden räumlich aufgelöste Korrelationen zwischen WSS, PWV, Plaque und Gefäßwandeigenschaften ermöglicht, die detaillierte Einblicke in die Zusammenhänge zwischen Hämodynamik und Plaquezusammensetzung in der Atherosklerose bieten. Dabei wurde die zirkumferentielle WSS als potenzieller Marker für die Plaquegröße und -zusammensetzung bei fortgeschrittener Atherosklerose identifiziert. Darüber hinaus ergaben Korrelationen mit der PWV, dass der maximale radiale Druck als potenzieller Marker für die vaskuläre Elastizität dienen könnte. Zusammengefasst demonstriert diese Studie die Nützlichkeit der hochauflösenden 4D-Fluss MRT zur räumlichen Auflösung, Visualisierung und Analyse statistischer Unterschiede in allen relevanten hämodynamischen Parametern im Zeitverlauf und zwischen gesunden und erkrankten Mäusen, was unser Verständnis der Plaqueprogression in Richtung Vulnerabilität erheblich verbessern könnte. In zukünftigen Studien sollte jedoch der Zusammenhang zwischen Gefäßelastizität und radialem Druck weiter untersucht und mit lokalen PWV-Messungen und CFD validiert werden. Darüber hinaus spiegelten die histologischen 2D-Datensätze nicht die 3D-Eigenschaften und regionalen Charakteristika der atherosklerotischen Plaques wider. Daher sollten künftige Studien eine Analyse des 3D-Plaquevolumens und der 3D-Plaquenzusammensetzung sowie morphologische Messungen mittels MRT oder der Lichtblattmikroskopie mit einbeziehen, um das fundamentale Verständnis der Beziehung zwischen veränderter Hämodynamik und der Atherosklerose weiter zu verbessern. In Kapitel 4 ging es um die Beschreibung und Untersuchung der Hämodynamik in frühen Stadien der Atherosklerose. Darüber hinaus umfasste diese Studie zum ersten Mal Messungen der basalen Hämodynamik in gesunden WT- und atherosklerotischen Mausmodellen. Aufgrund des Mangels an Studien, die die Hämodynamik in Ldlr-/- Mäusen beschreiben, die zusammen mit dem Apoe-/- Mausmodell die am häufigsten verwendeten Mausmodelle in der Atheroskleroseforschung sind, wurde dieses Modell in diese Studie integriert, um erstmals die sich verändernde Hämodynamik im Aortenbogen zu Beginn und während der Entwicklung und Progression der frühen Atherosklerose zu beschreiben. In dieser Studie wurden erstmals deutliche Unterschiede in den basalen Aortengeometrien dieser Mausmodelle identifiziert, die zu signifikant unterschiedlichen Fluss- und WSS-Profilen im Ldlr-/- Mausmodell führen. Eine weitere basale Charakterisierung verschiedener Parameter ergab nur modell-charakteristische Unterschiede in den Lipidprofilen, was beweist, dass die Geometrie die lokale WSS in diesen Modellen stark beeinflusst. Interessanterweise ergab die Berechnung des atherogenen Plasma-Indexes ein signifikant höheres Risiko bei Ldlr-/- Mäusen mit fortschreitender Atheroskleroseentwicklung, aber signifikant größere Plaqueflächen im Aortenbogen der Apoe-/- Mäuse. Aufgrund des gegebenen basalen WSS- und OSI-Profils in diesen beiden Mausmodellen - zwei Parameter, die die Plaque-Entwicklung und -Progression stark beeinflussen - gibt es Hinweise darauf, dass sich die regionale Plaque-Entwicklung zwischen diesen Mausmodellen während der Atherogenese stark unterscheidet. Daher sollten sich künftige Studien auf die räumlich-zeitliche Bewertung der Plaqueentwicklung und -Zusammensetzung in den drei definierten Aortenregionen konzentrieren, wobei morphologische Messungen mittels MRT oder histologische 3D-Analysen wie LSFM zum Einsatz kommen. Darüber hinaus bietet diese Studie eine hervorragende Grundlage für künftige Studien mit CFD-Simulationen, in denen die verschiedenen gemessenen Parameterkombinationen (z. B. die Aortengeometrie der Ldlr-/-Maus mit dem Lipidprofil der Apoe-/- Maus) analysiert und die daraus resultierende Plaqueentwicklung und -Zusammensetzung simuliert werden. Dies könnte zum Verständnis des komplexen Zusammenspiels zwischen veränderter Hämodynamik, Serumlipiden und Atherosklerose beitragen und unser grundlegendes Verständnis der Schlüsselfaktoren für die Entstehung von Atherosklerose deutlich verbessern. In Kapitel 5 wird die Etablierung eines tissue-engineerten Arterienmodells beschrieben, das auf nativen, von Schweinehalsschlagadern hergestellten, dezellularisierten Gerüststrukturen basiert. Diese wurden zudem in einem MRT-geeigneten Bioreaktorsystem [23] kultiviert, um die hämodynamisch bedingte Atheroskleroseentwicklung auf kontrollierbare Weise zu untersuchen, wobei hierfür die zuvor etablierten Methoden zur WSS- und PWV-Bewertung [4, 16] verwendet wurden. Dieses in vitro Arterienmodell zielte auf die Reduzierung von Tierversuchen ab und bot gleichzeitig eine vereinfachte, aber vollständig kontrollierbare physikalische und biologische Umgebung. Zu diesem Zweck wurde in einem ersten Schritt ein sehr schnelles und schonendes Dezellularisierungsverfahren etabliert, das zu Gerüststrukturen basierend auf Schweinehalsschlagadern führte, die eine vollständige Azellularität aufwiesen, wobei gleichzeitig die Zusammensetzung der extrazellulären Matrix, die allgemeine Ultrastruktur und die mechanischen Eigenschaften der nativen Arterien erhalten blieben. Darüber hinaus wurde eine gute Zelladhäsion und -proliferation erreicht, die mit isolierten menschlichen Endothelzellen aus humanem Vollblut untersucht wurde. Darüber hinaus wurde zum ersten Mal eine MRT-geeignete Arterienkammer für die gleichzeitige Kultivierung der generierten Modelle und der Untersuchung der hochauflösenden 4D-Hämodynamik in diesen Arterienmodellen entwickelt. Unter Verwendung der hochauflösenden 4D-Fluss-MRT erwies sich das Bioreaktorsystem als sehr geeignet, den Volumenstrom, die beiden Komponenten der WSS inklusive dem radialen Druck und die PWV in den Arterienmodellen zu quantifizieren, wobei die erhaltenen Werte sehr gut mit den in der Literatur gefundenen Werten für in vivo-Messungen vergleichbar sind. Darüber hinaus lassen sich durch die dreidimensionale Untersuchung der Gefäßwandmorphologie in den in vitro-Modellen erste atherosklerotische Prozesse wie die Verdickung der Intima erkennen. Eine Einschränkung ist jedoch das Fehlen einer medialen glatten Muskelzellschicht aufgrund der dichten ECM des Gewebegerüsts. Die Verwendung der Laserschneidetechnik zur Erzeugung von Löchern und / oder Gruben im Mikrometerbereich, die eine Besiedlung des Mediums mit SMCs ermöglichen, zeigte in einem ersten Versuch vielversprechende Ergebnisse und sollte in zukünftigen Studien daher dringend weiter untersucht werden. Das präsentierte Arterienmodell verfügt somit über alle relevanten Komponenten für die Erweiterung zu einem Atherosklerosemodell und ebnet den Weg für ein deutlich besseres Verständnis der Schlüsselmechanismen in der Atherogenese. Kapitel 6 beschreibt die Entwicklung eines einfach herzustellenden, kostengünstigen und vollständig an gegebene Bedürfnisse anpassbaren Arterienmodells auf Grundlage von Biomaterialien. Hier wurden thermoresponsive Opfergerüststrukturen, die mit der MEW-Technik hergestellt wurden, zur Herstellung variabler, biomimetischer Formen verwendet, um die geometrischen Eigenschaften des Aortenbogens, bestehend aus Verzweigungen und Krümmungen, zu imitieren. Nach der Einbettung der Opfergerüststruktur in ein Gelatin-Hydrogel, das zudem SMCs enthält, wurde es mit bakterieller Transglutaminase vernetzt, bevor es aufgelöst und gespült wurde. Der so entstandene Hydrogelkanal wurde anschließend mit Endothelzellen besiedelt, wodurch ein einfach zu erstellendes, schnelles und kostengünstiges Arterienmodell entstand. Im Gegensatz zum nativen Arterienmodell ist dieses Modell daher deutlich variabler in Größe und Form und bietet die wichtige Möglichkeit, von Anfang an glatte Muskelzellen mit einzubringen. Darüber hinaus wurde speziell für die gegebene Gerüststruktur eine maßgeschneiderte und hochgradig anpassungsfähige Perfusionskammer entwickelt, die eine sehr schnelle und einstufige Herstellung des Arterienmodells ermöglicht und gleichzeitig die Möglichkeit zur dynamischen Kultivierung der Modelle bietet, was eine hervorragende Grundlage für die Entwicklung von in vitro Krankheits-Testsystemen für z.B. die Atheroskleroseforschung im Zusammenhang mit der Hämodynamik darstellt. Aus Zeitgründen konnte die Ausweitung auf ein Atherosklerosemodell jedoch im Rahmen dieser Arbeit nicht realisiert werden. Daher werden sich zukünftige Studien auf die Entwicklung und Validierung eines in vitro-Atherosklerosemodells konzentrieren, das auf den hier entwickelten zwei- und dreischichtigen Arterienmodellen basiert. Zusammenfassend lässt sich sagen, dass diese Arbeit den Weg für eine schnelle Erfassung und detaillierte Analyse der sich verändernden Hämodynamik während der Entwicklung und der Progression der Atherosklerose geebnet hat, einschließlich räumlich aufgelöster Analysen aller relevanten hämodynamischen Parameter im Zeitverlauf innerhalb einer Gruppe und zwischen verschiedenen Gruppen. Darüber hinaus wurden vielversprechende Arterienmodelle etabliert, die das Potenzial haben, als neue Plattform für die Atherosklerose-Grundlagenforschung zu dienen, um Tierversuche zu minimieren und gleichzeitig die Kontrolle über verschiedene Parameter zu erlangen, die die Atheroskleroseentwicklung beeinflussen. KW - Hämodynamik KW - Arteriosklerose KW - Tissue Engineering KW - Atherosclerosis KW - MRI KW - Hemodynamics KW - Tissue Engineering KW - Biofabrication KW - Artery Models Y1 - 2024 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-303601 ER - TY - THES A1 - Ames, Christopher T1 - Molecular Beam Epitaxy of 2D and 3D HgTe, a Topological Insulator T1 - Molekularstrahlepitaxie von 2D und 3D HgTe, ein topologischer Isolator N2 - In the present thesis the MBE growth and sample characterization of HgTe structures is investigated and discussed. Due to the first experimental discovery of the quantum Spin Hall effect (QSHE) in HgTe quantum wells, this material system attains a huge interest in the spintronics society. Because of the long history of growing Hg-based heterostructures here at the Experimentelle Physik III in Würzburg, there are very good requirements to analyze this material system more precisely and in new directions. Since in former days only doped HgTe quantum wells were grown, this thesis deals with the MBE growth in the (001) direction of undoped HgTe quantum wells, surface located quantum wells and three dimensional bulk layers. All Hg-based layers were grown on CdTe substrates which generate strain in the layer stack and provide therefore new physical effects. In the same time, the (001) CdTe growth was investigated on n-doped (001) GaAs:Si because the Japanese supplier of CdTe substrates had a supply bottleneck due to the Tohoku earthquake and its aftermath in 2011. After a short introduction of the material system, the experimental techniques were demonstrated and explained explicitly. After that, the experimental part of this thesis is displayed. So, the investigation of the (001) CdTe growth on (001) GaAs:Si is discussed in chapter 4. Firstly, the surface preparation of GaAs:Si by oxide desorption is explored and analyzed. Here, rapid thermal desorption of the GaAs oxide with following cool down in Zn atmosphere provides the best results for the CdTe due to small holes at the surface, while e.g. an atomic flat GaAs buffer deteriorates the CdTe growth quality. The following ZnTe layer supplies the (001) growth direction of the CdTe and exhibits best end results of the CdTe for 30 seconds growth time at a flux ratio of Zn/Te ~ 1/1.2. Without this ZnTe layer, CdTe will grow in the (111) direction. However, the main investigation is here the optimization of the MBE growth of CdTe. The substrate temperature, Cd/Te flux ratio and the growth time has to be adjusted systematically. Therefore, a complex growth process is developed and established. This optimized CdTe growth process results in a RMS roughness of around 2.5 nm and a FWHM value of the HRXRD w-scan of 150 arcsec. Compared to the literature, there is no lower FWHM value traceable for this growth direction. Furthermore, etch pit density measurements show that the surface crystallinity is matchable with the commercial CdTe substrates (around 1x10^4 cm^(-2)). However, this whole process is not completely perfect and offers still room for improvements. The growth of undoped HgTe quantum wells was also a new direction in research in contrast to the previous n-doped grown HgTe quantum wells. Here in chapter 5, the goal of very low carrier densities was achieved and therefore it is now possible to do transport experiments in the n - and p - region by tuning the gate voltage. To achieve this high sample quality, very precise growth of symmetric HgTe QWs and their HRXRD characterization is examined. Here, the quantum well thickness can now determined accurate to under 0.3 nm. Furthermore, the transport analysis of different quantum well thicknesses shows that the carrier density and mobility increase with rising HgTe layer thickness. However, it is found out that the band gap of the HgTe QW closes indirectly at a thickness of 11.6 nm. This is caused by the tensile strained growth on CdTe substrates. Moreover, surface quantum wells are studied. These quantum wells exhibit no or a very thin HgCdTe cap. Though, oxidization and contamination of the surface reduces here the carrier mobility immensely and a HgCdTe layer of around 5 nm provides the pleasing results for transport experiments with superconductors connected to the topological insulator [119]. A completely new achievement is the realization of MBE growth of HgTe quantum wells on CdTe/GaAs:Si substrates. This is attended by the optimization of the CdTe growth on GaAs:Si. It exposes that HgTe quantum wells grown in-situ on optimized CdTe/GaAs:Si show very nice transport data with clear Hall plateaus, SdH oscillations, low carrier densities and carrier mobilities up to 500 000 cm^2/Vs. Furthermore, a new oxide etching process is developed and analyzed which should serve as an alternative to the standard HCl process which generates volcano defects at some time. However, during the testing time the result does not differ in Nomarski, HRXRD, AFM and transport measurements. Here, long-time tests or etching and mounting in nitrogen atmosphere may provide new elaborate results. The main focus of this thesis is on the MBE growth and standard characterization of HgTe bulk layers and is discussed in chapter 6. Due to the tensile strained growth on lattice mismatched CdTe, HgTe bulk opens up a band gap of around 22 meV at the G-point and exhibits therefore its topological surface states. The analysis of surface condition, roughness, crystalline quality, carrier density and mobility via Nomarski, AFM, XPS, HRXRD and transport measurements is therefore included in this work. Layer thickness dependence of carrier density and mobility is identified for bulk layer grown directly on CdTe substrates. So, there is no clear correlation visible between HgTe layer thickness and carrier density or mobility. So, the carrier density is almost constant around 1x10^11 cm^(-2) at 0 V gate voltage. The carrier mobility of these bulk samples however scatters between 5 000 and 60 000 cm^2/Vs almost randomly. Further experiments should be made for a clearer understanding and therefore the avoidance of unusable bad samples.But, other topological insulator materials show much higher carrier densities and lower mobility values. For example, Bi2Se3 exhibits just density values around 1019 cm^(-2) and mobility values clearly below 5000 cm2/Vs. The carrier density however depends much on lithography and surface treatment after growth. Furthermore, the relaxation behavior and critical thickness of HgTe grown on CdTe is determined and is in very good agreement with theoretical prediction (d_c = 155 nm). The embedding of the HgTe bulk layer between HgCdTe layers created a further huge improvement. Similar to the quantum well structures the carrier mobility increases immensely while the carrier density levels at around 1x10^11 cm^(-2) at 0 V gate voltage as well. Additionally, the relaxation behavior and critical thickness of these barrier layers has to be determined. HgCdTe grown on commercial CdTe shows a behavior as predicted except the critical thickness which is slightly higher than expected (d_c = 850 nm). Otherwise, the relaxation of HgCdTe grown on CdTe/GaAs:Si occurs in two parts. The layer is fully strained up to 250 nm. Between 250 nm and 725 nm the HgCdTe film starts to relax randomly up to 10 %. The relaxation behavior for thicknesses larger than 725 nm occurs than linearly to the inverse layer thickness. A explanation is given due to rough interface conditions and crystalline defects of the CdTe/GaAs:Si compared to the commercial CdTe substrate. HRXRD and AFM data support this statement. Another point is that the HgCdTe barriers protect the active HgTe layer and because of the high carrier mobilities the Hall measurements provide new transport data which have to be interpreted more in detail in the future. In addition, HgTe bulk samples show very interesting transport data by gating the sample from the top and the back. It is now possible to manipulate the carrier densities of the top and bottom surface states almost separately. The back gate consisting of the n-doped GaAs substrate and the thick insulating CdTe buffer can tune the carrier density for Delta(n) ~ 3x10^11 cm^(-2). This is sufficient to tune the Fermi energy from the p-type into the n-type region [138]. In this thesis it is shown that strained HgTe bulk layers exhibit superior transport data by embedding between HgCdTe barrier layers. The n-doped GaAs can here serve as a back gate. Furthermore, MBE growth of high crystalline, undoped HgTe quantum wells shows also new and extended transport output. Finally, it is notable that due to the investigated CdTe growth on GaAs the Hg-based heterostructure MBE growth is partially independent from commercial suppliers. N2 - In der vorliegenden Dissertation wurde das MBE-Wachstum von HgTe Strukturen erforscht und die anschließende Probencharakterisierung durchgeführt und diskutiert. Durch die erste experimentelle Entdeckung des Quanten-Spin-Hall-Effekts (QSHE) in HgTe Quantentrögen hat dieses Materialsystem großes Interesse im Gebiet der Spintronics erfahren. Aufgrund der langen Wachstumshistorie von quecksilberbasierenden Heterostrukturen am Lehrstuhl Experimentelle Physik III der Universität Würzburg sind die Voraussetzungen ausgesprochen gut, um dieses Materialsystem sehr ausführlich und auch in neue Richtungen hin zu untersuchen. Da vor dieser Doktorarbeit fast ausschließlich dotierte HgTe Quantentröge auf verschiedenen Substratorientierungen gewachsen wurden, beschäftigte sich diese Dissertation nun mit dem MBE-Wachstum von undotierten HgTe Quantentrögen, oberflächennahen Quantentrögen und dreidimensionalen Volumenkristallen. Alle quecksilberbasierenden Schichten wurden hierzu auf CdTe Substraten gewachsen, welche tensile Verspannung in den Schichten erzeugten und lieferten daher neue physikalische Effekte. In der selben Zeit wurde weiterhin das Wachstum von (001) CdTe auf n-dotiertem (001) GaAs:Si erforscht, da der japanische Zulieferer der CdTe Substrate eine Lieferengpass hatte aufgrund des Tohoku Erdbebens und seinen verheerenden Folgen im Jahr 2011. Die Erforschung des MBE-Wachstums von (001) CdTe auf (001) GaAs:Si wird im Kapitel 4 behandelt. Zuerst wurde hier die Oberflächenvorbereitung des GaAs:Si Substrates durch thermische Desorption untersucht und ausgewertet. Es stellte sich heraus, dass schnelle, thermische Desorption des GaAs - Oxides mit anschließendem Abkühlen in Zn Atmosphäre die besten Ergebnisse für das spätere CdTe durch kleine Löcher an der Oberfläche liefert, während zum Beispiel ein glatter GaAs Puffer das CdTe Wachstum verschlechtert. Der folgende ZnTe Film verschafft die gewünschte (001) Wachstumsrichtung für CdTe und weist bei 30 Sekunden Wachstumszeit bei einem Flussverhältnis von Zn/Te ~ 1/1.2 die besten Endergebnisse für CdTe auf. Jedoch war die Haupterneuerung hier die Optimierung des CdTe Wachstums. Dafür wurde ein komplexer Wachstumsprozess entwickelt und etabliert. Dieser optimierte CdTe Wachstumsprozess lieferte Ergebnisse von einer RMS Rauigkeit von ungefähr 2.5 nm und FWHMWerte der HRXRD w-Scans von 150 arcsec. Die Defektätzdichte-Messung zeigte weiterhin, dass die Oberflächenkristallinität vergleichbar mit kommerziell erwerbbaren CdTe Substraten ist (um 1x10^4 cm^(-2)). Des Weiteren ist kein niedrigerer Wert für die Halbwertsbreite des w-Scans in der Literatur für diese Wachstumsrichtung aufgeführt. Dies spiricht ebenfalls für die hohe Qualität der Schichten. Jedoch ist dieser Wachstumsprozess noch nicht endgültig ausgereift und bietet weiterhin noch Platz für Verbesserungen. Das Wachstum von undotierten HgTe Quantentrögen war ebenso eine neue Forschungsrichtung im Gegensatz zu den dotierten HgTe Quantentrögen, die in der Vergangenheit gewachsen wurden. Das Ziel hierbei, die Ladungsträgerdichte zu verringern, wurde erreicht und daher ist es nun möglich, Transportexperimente sowohl im n- als auch im p-Regime durchzuführen, indem eine Gatespannung angelegt wird. Des Weiteren experimentierten andere Arbeitsgruppen mit diesen Quantentrögen, bei denen die Fermi Energie in der Bandlücke liegt [143]. Außerdem wurde das sehr präzise MBE Wachstum anhand von symmetrischen HgTe Quantentrögen und ihren HRXRD Charakterisierungen behandelt. Daher kann nun die Quantentrogdicke präzise auf 0,3 nm angegeben werden. Die Transportergebnisse von verschieden dicken Quantentrögen zeigten, dass die Ladungsträgerdichte und Beweglichkeit mit steigender HgTe Schichtdicke zunimmt. Jedoch wurde auch herausgefunden, dass sich die Bandlücke von HgTe Quantentrögen indirekt bei einer Dicke von 11.6 nm schließt. Dies wird durch das verspannte Wachstum auf CdTe Substraten verursacht. Überdies wurden oberflächennahe Quantentröge untersucht. Diese Quantentröge besitzen keine oder nur eine sehr dünne HgCdTe Deckschicht. Allerdings verringerte Oxidation und Oberflächenverschmutzung hier die Ladungsträgerbeweglichkeit dramatisch und eine HgCdTe Schicht von ungefähr 5 nm lieferte ansprechende Transportergebnisse für Supraleiter, die den topologischen Isolator kontaktieren. Eine komplett neue Errungenschaft war die Realisierung, via MBE, HgTe Quantentröge auf CdTe/GaAs:Si Substrate zu wachsen. Dies ging einher mit der Optimierung des CdTe Wachstums auf GaAs:Si. Es zeigte sich, dass HgTe Quantentröge, die in-situ auf optimierten CdTe/GaAs:Si gewachsen wurden, sehr schöne Transportergebnisse mit deutlichen Hall Quantisierungen, SdH Oszillationen, niedrigen Ladungsträgerdichten und Beweglichkeiten bis zu 500 000 cm^2/Vs erreichen. Des Weiteren wurde ein neues Oxidätzverfahren entwickelt und untersucht, welches als Alternative zum Standard-HCl-Prozess dienen sollte, da dieses manchmal vulkan-artige Defekte hervorruft. Jedoch ergab sich kein Unterschied in den Nomarski, HRXRD, AFM und Transportexperimenten. Hier könnten vielleicht Langzeittests oder Ätzen und Befestigen in Stickstoffatmosphäre neue, gewinnbringende Ergbnisse aufzeigen. Der Hauptfokus dieser Doktorarbeit lag auf dem MBE Wachstum und der Standardcharakterisierung von HgTe Volumenkristallen und wurde in Kapitel 6 diskutiert. Durch das tensil verpannte Wachstum auf CdTe entsteht für HgTe als Volumenkristall eine Bandlücke von ungefähr 22 meV am G Punkt und zeigt somit seine topologischen Oberflächenzustände. Die Analyse der Oberfächenbeschaffenheit, der Rauigkeit, der kristallinen Qualität, der Ladungsdrägerdichte und Beweglichkeit mit Hilfe von Nomarski, AFM, XPS, HRXRD und Transportmessungen ist in dieser Arbeit anzutreffen. Außerdem wurde die Schichtdickenabhängigkeit von Ladungsträgerdichte und Beweglichkeit von HgTe Volumenkristallen, die direkt auf CdTe Substraten gewachsen wurden, ermittelt worden. So erhöhte sich durchschnittlich die Dichte und Beweglichkeit mit zunehmender HgTe Schichtdicke, aber die Beweglichkeit ging selten über μ ~ 40 000 cm^2/Vs hinaus. Die Ladungsträgerdichte n hing jedoch sehr von der Litographie und der Behandlung der Oberfläche nach dem Wachstum ab. Des Weiteren wurde das Relaxationsverhalten und die kritische Dicke bestimmt, welches sehr gut mit den theoretischen Vorhersagen übereinstimmt (dc = 155 nm). Das Einbetten des HgTe Volumenkristalls in HgCdTe Schichten brachte eine weitere große Verbesserung mit sich. Ähnlich wie bei den Quantentrögen erhörte sich die Beweglichkeit μ immens, während sich die Ladungsträgerdichte bei ungefähr 1x10^11 cm^(-2) einpendelte. Zusätzlich wurde auch hier das Relaxationsverhalten und die kritische Schichtdicke dieser Barrierenschichten ermittelt. HgCdTe, gewachsen auf kommerziellen CdTe Substraten, zeigte ein Verhalten ähnlich zu dem Erwarteten mit der Ausnahme, dass die kritische Schichtdicke leicht höher ist als die Vorhergesagte (dc = 850 nm). Auf der anderen Seite findet die Relaxation von HgCdTe auf CdTe/GaAs:Si zweigeteilt ab. Bis 250 nm ist die Schicht noch voll verspannt. Zwischen 250 nm und 725 nm beginnt die HgCdTe Schicht willkürlich bis zu 10 % zu relaxieren. Das Relaxationsverhalten für Dicken über 725 nm findet dann wieder linear zur invers aufgetragenen Schichtdicke statt. Eine Erklärung wurde durch das raue Interface der Schichten und der Defekte im Kristall von CdTe/GaAs:Si gegeben, im Vergleich zu den kommerziellen CdTe Substraten. HRXRD und AFM Ergebnisse belegten diese Aussage. Die HgCdTe Barrieren schützen die aktive HgTe Schicht und daher liegen nach Hall Messungen aufgrund der hohen Ladungsträgerbeweglichkeiten neue Transportergbnisse vor, welche in der Zukunft ausführlicher interpretiert werden müssen. Darüber hinaus zeigten HgTe Volumenkristalle neue, interessante Transportergebnisse durch das gleichzeitige Benutzen eines Top- und Backgates. Es ist nun möglich, die Ladungsträger der oberen und unteren Oberflächenzustände nahezu getrennt zu verändern und zu ermitteln. Das Backgate, bestehend aus dem n-dotierten GaAs:Si Substrate und dem dicken isolierenden CdTe Puffer, kann die Ladungsträgerdichte um ungefähr Delta(n) ~ 3x10^11 cm^(-2) varieren. Das ist ausreichend, um die Fermi Energie vom p- in den n-Bereich einzustellen [138]. In dieser Dissertation wurde also gezeigt, dass verspannte HgTe Volumenkristalle durch das Einbetten in HgCdTe Barrieren neue Transportergebnisse liefern. Das n-dotierte GaAs konnte hierbei als Backgate genutzt werden. Des Weiteren zeigte das MBE Wachstum von hochkristallinen , undotiereten HgTe Quantentrögen ebenso neue und erweiterte Transportergebnisse. Zuletzt ist es bemerkenswert, dass durch das erforschte CdTe Wachstum auf GaAs das MBE Wachstum von quecksilberbasierenden Heterostrukturen auf CdTe Substraten teilweise unabhänigig ist von kommerziellen Zulieferbetrieben. KW - Quecksilbertellurid KW - Topologischer Isolator KW - MBE KW - HgTe KW - topological insulator KW - Molekularstrahlepitaxie Y1 - 2015 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-151136 ER - TY - THES A1 - Albert, Ferdinand T1 - Vertikale und laterale Emissionseigenschaften von Halbleiter-Quantenpunkt-Mikroresonatoren im Regime der schwachen und starken Licht-Materie-Wechselwirkung T1 - Vertical and lateral emission properties of semiconductor quantum-dot-microresonators in the regime of weak and strong light matter interaction N2 - Die vorliegende Arbeit beschäftigt sich mit der Licht-Materie-Wechselwirkung in Quantenpunkt-Mikroresonatoren und deren vertikalen und lateralen Emissionseigenschaften. Quantenpunkte sind nanoskopische Strukturen, in denen die Beweglichkeit der Ladungsträger unterhalb der de-Broglie-Wellenlänge eingeschränkt ist, wodurch die elektronische Zustandsdichte diskrete Werte annimmt. Sie werden daher auch als künstliche Atome bezeichnet. Um die Emissionseigenschaften der Quantenpunkte zu modifizieren, werden sie im Rahmen dieser Arbeit als aktive Schicht in Mikrosäulenresonatoren eingebracht. Diese bestehen aus einer GaAs lambda-Kavität, die zwischen zwei Braggspiegeln aus alternierenden GaAs und AlAs Schichten eingefasst ist. Diese Resonatoren bieten sowohl eine vertikale Emission über Fabry-Perot Moden, als auch eine laterale Emission über Fl� ustergaleriemoden. Die Licht-Materie-Wechselwirkung zwischen den Resonatormoden und lokalisierten Ladungsträgern in den Quantenpunkten, genannt Exzitonen, kann in zwei Regime unterteilt werden. Im Regime der starken Kopplung wird der spontane Emissionsprozess in einem Quantenpunkt reversibel und das emittierte Photon kann wieder durch den Quantenpunkt absorbiert werden. Die theoretische Beschreibung der Kopplung eines Exzitons an die Resonatormode erfolgt über das Jaynes-Cummings Modell und kann im Tavis-Cummings Modell auf mehrere Emitter erweitert werden. Ist die Dämpfung des Systems zu gross, so befindet man sich im Regime der schwachen Kopplung, in dem die Emissionsrate des Quantenpunkts durch den Purcell-Effekt erhöht werden kann. In diesem Regime können Mikrolaser mit hohen Einkopplungsraten der spontanen Emission in die Resonatormode und niedrigen Schwellpumpströmen realisiert werden. Zur Charakterisierung der Proben werden vor allem die Methoden der Mikro-Elektrolumineszenz und der Photonenkorrelationsmessungen eingesetzt. N2 - The present work deals with the light-matter interaction in quantum dot microcavities and their vertical and lateral emission properties. Quantum dots are nanoscopic structures, in which charge carriers are confi� ned in all three dimensions below the de-Broglie wavelength. As a consequence, the density of electronic states becomes singular and quantum dots are therefore referred to as arti� cal atoms. To modify the emission properties of quantum dots, they are introduced in micropillar cavities. These consist of a GaAs � -cavity, which is sandwiched between two Bragg mirrors of alternating layers of GaAs and AlAs. The micropillar resonators provide both a vertical emission via Fabry-P� erot modes, as well as a lateral emission via whispering gallery modes. The light-matter interaction between the microcavity modes and the localized charge carriers, called exzitons, can be devided into two regimes. In the strong coupling regime, the spontaneous emission process becomes reversible and an emitted photon can be reabsorbed by the quantum dot. The theoretical description of the coupling of a two-level emitter with a photonic mode is given by the Jaynes-Cummings model. For multiple two-level emitters, it can be extended to the Tavis-Cummings model. In the weak coupling regime the spontaneous emission rate of a quantum dot can be increased by the Purcell e� ect. Here, microlasers with high spontaneous emission coupling factors and low lasing thresholds can be realized. In order to investigate the samples, especially the methods of microelectroluminescence and photon correlation measurements are applied. KW - Drei-Fünf-Halbleiter KW - Quantenpunkt KW - Halbleiterlaser KW - Quantenoptik KW - Mikrolaser KW - Mikrosäulenresonator KW - Quantenpunkt KW - Flüstergaleriemode KW - Galliumarsenidlaser KW - Optischer Resonator KW - Mikrooptik KW - Mikroresonator Y1 - 2012 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-93016 ER - TY - THES A1 - Al-Baidhani, Mohammed T1 - Spectroscopy as a tool to investigate the high energy optical properties of nanostructured magnetically doped topological insulator T1 - Spektroskopie als Methode zur Untersuchung der optischen Eigenschaften nanostrukturierter, magnetisch dotierter Topologischer Isolatoren bei hohen Energien N2 - In this dissertation the electronic and high-energy optical properties of thin nanoscale films of the magnetic topological insulator (MTI) (V,Cr)y(BixSb1-x)2-yTe3 are studied by means of X-ray photoelectron spectroscopy (XPS) and electron energy-loss spectroscopy (EELS). Magnetic topological insulators are presently of broad interest as the combination of ferromagnetism and spin-orbit coupling in these materials leads to a new topological phase, the quantum anomalous Hall state (QAHS), with dissipation less conduction channels. Determining and controlling the physical properties of these complex materials is therefore desirable for a fundamental understanding of the QAHS and for their possible application in spintronics. EELS can directly probe the electron energy-loss function of a material from which one can obtain the complex dynamic dielectric function by means of the Kramers-Kronig transformation and the Drude-Lindhard model of plasmon oscillations. The XPS core-level spectra in (V,Cr)y(BixSb1-x)2-yTe3 are analyzed in detail with regards to inelastic background contributions. It is shown that the spectra can be accurately described based on the electron energy-loss function obtained from an independent EELS measurement. This allows for a comprehensive and quantitative analysis of the XPS data, which will facilitate future core-level spectroscopy studies in this class of topological materials. From the EELS data, furthermore, the bulk and surface optical properties were estimated, and compared to ab initio calculations based on density functional theory (DFT) performed in the GW approximation for Sb2Te3. The experimental results show a good agreement with the calculated complex dielectric function and the calculated energy-loss function. The positions of the main plasmon modes reported here are expected to be generally similar in other materials in this class of nanoscale TI films. Hence, the present work introduces EELS as a powerful method to access the high-energy optical properties of TI thin films. Based on the presented results it will be interesting to explore more systematically the effects of stoichiometry, magnetic doping, film thickness and surface morphology on the electron-loss function, potentially leading to a better understanding of the complex interplay of structural, electronic, magnetic and optical properties in MTI nanostructures. N2 - Die vorliegende Dissertation beschäftigt sich mit den elektronischen und hochen- ergetischen optischen Eigenschaften von auf der Nanoskala dünnen Filmen des magnetischen topologischen Isolators (MTI) (V,Cr)y(BixSb1−x)2−yTe3 mithilfe von Röntgenphotoelektronenspektroskopie (engl.: X-ray photoelectron spectroscopy, XPS), sowie Elektronenenergieverlustspektroskopie (engl.: electron energy-loss spectroscopy, EELS). Magnetische topologische Isolatoren sind gegenwärtig von großem Interesse, da die Kombination von Ferromagnetismus und Spin-Bahn- Kopplung in diesen Materialien zu einer neuen topologischen Phase führt, der Quanten-Anomalen-Hall-Phase (engl.: quantum anomalous Hall state, QAHS), die sich durch verlustfreie Leitungskanäle auszeichnet. Bestimmung und Kontrolle der physikalischen Eigenschaften dieser komplexen Materialien ist somit erstrebenswert für ein fundamentales Verständnis des QAHS sowie für Anwendungen in der Spin- tronik. EELS erlaubt die direkte Untersuchung der Elektronenenergieverlustfunk- tion eines Materials, aus der man, mithilfe der Kramers-Kronig-Transformation und des Drude-Lindhard-Modells von Plasmonenoszillationen, die komplexe dynamis- che dielektrische Funktion des Materials erhält. In den XPS-Spektren der Rumpfniveaus in (V,Cr)y(BixSb1−x)2−yTe3 wird detail- liert insbesondere der Beitrag des inelastischen Untergrunds analysiert. Es kann gezeigt werden, dass, basierend auf der in einem unabhängigen EELS-Experiment gewonnenen Elektronenenergieverlustfunktion, die Rumpfniveauspektren präzise beschrieben werden können. Dies erlaubt eine umfangreiche und quantitative Anal- yse der Daten, was zukünftige Rumpfniveaustudien dieser Klasse topologischer Materialien erleichtern wird. Die mit EELS gewonnenen Daten ermöglichen weiter- hin eine Abschätzung der optischen Eigenschaften von Volumen und Oberfläche der Materialien, die in der vorliegenden Arbeit mit ab initio Berechnungen aus der Literatur für Sb2Te3 verglichen werden, welche auf Basis der Dichtefunktionaltheo- rie (DFT) in GW-näherung durchgeführt wurden. Die experimentellen Ergebnisse zeigen gute Übereinstimmungen mit der berechneten komplexen dielektrischen Funktion, sowie mit der Energieverlustfunktion. Es wird erwartet, dass die hier beschriebenen Positionen der Hauptplasmonenmoden im Allgemeinen ähnlich zu denen anderer Materialien dieser Klasse auf der Nanoskala dünner topologischer Isolatoren sind. Somit stellt die vorliegende Arbeit das EELS Experiment als eine mächtige Methode vor, die einen Zugang zu den hochenergetischen optischen Eigen- schaften dünner TIs schafft. Basierend auf den hier vorgestellten Ergebnissen bleibt es interessant sein die Auswirkungen von Stöchiometrie, magnetischer Dotierung, Filmdicke, sowie Oberflächenmorphologie auf die Energieverlustfunktion system- atischer zu untersuchen, um damit ein besseres Verständnis für das komplexe Zusammenspiel aus strukturellen, elektronischen und optischen Eigenschaften in MTI-Nanostrukturen zu erlangen. KW - spectroscopy KW - XPS KW - REELS KW - topological insulator KW - QAHE KW - Topologischer Isolator KW - Optische Eigenschaft KW - Elektronenspektroskopie Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-157221 ER - TY - THES A1 - Adler, Florian Rudolf T1 - Electronic Correlations in Two-dimensional Triangular Adatom Lattices T1 - Elektronische Korrelationen in zweidimensionalen Adatom-Dreiecksgittern N2 - Two-dimensional triangular lattices of group IV adatoms on semiconductor substrates provide a rich playground for the investigation of Mott-Hubbard physics. The possibility to combine various types of adatoms and substrates makes members of this material class versatile model systems to study the influence of correlation strength, band filling and spin-orbit coupling on the electronic structure - both experimentally and with dedicated many-body calculation techniques. The latter predict exotic ground states such as chiral superconductivity or spin liquid behavior for these frustrated lattices, however, experimental confirmation is still lacking. In this work, three different systems, namely the \(\alpha\)-phases of Sn/SiC(0001), Pb/Si(111), and potassium-doped Sn/Si(111) are investigated with scanning tunneling microscopy and photoemission spectroscopy in this regard. The results are potentially relevant for spintronic applications or quantum computing. For the novel group IV triangular lattice Sn/SiC(0001), a combined experimental and theoretical study reveals that the system features surprisingly strong electronic correlations because they are boosted by the substrate through its partly ionic character and weak screening capabilities. Interestingly, the spectral function, measured for the first time via angle-resolved photoemission, does not show any additional superstructure beyond the intrinsic \(\sqrt{3} \times \sqrt{3} R30^{\circ}\) reconstruction, thereby raising curiosity regarding the ground-state spin pattern. For Pb/Si(111), preceding studies have noted a phase transition of the surface reconstruction from \(\sqrt{3} \times \sqrt{3} R30^{\circ}\) to \(3 \times 3\) at 86 K. In this thesis, investigations of the low-temperature phase with high-resolution scanning tunneling microscopy and spectroscopy unveil the formation of a charge-ordered ground state. It is disentangled from a concomitant structural rearrangement which is found to be 2-up/1-down, in contrast to previous predictions. Applying an extended variational cluster approach, a phase diagram of local and nonlocal Coulomb interactions is mapped out. Based on a comparison of theoretical spectral functions with scattering vectors found via quasiparticle interference, Pb/Si(111) is placed in said phase diagram and electronic correlations are found to be the driving force of the charge-ordered state. In order to realize a doped Mott insulator in a frustrated geometry, potassium was evaporated onto the well-known correlated Sn/Si(111) system. Instead of the expected insulator-to-metal transition, scanning tunneling spectroscopy data indicates that the electronic structure of Sn/Si(111) is only affected locally around potassium atoms while a metallization is suppressed. The potassium atoms were found to be adsorbed on empty \(T_4\) sites of the substrate which eventually leads to the formation of two types of K-Sn alloys with a relative potassium content of 1/3 and 1/2, respectively. Complementary measurements of the spectral function via angle-resolved photoemission reveal that the lower Hubbard band of Sn/Si(111) gradually changes its shape upon potassium deposition. Once the tin and potassium portion on the surface are equal, this evolution is complete and the system can be described as a band insulator without the need to include Coulomb interactions. N2 - Zweidimensionale Dreiecksgitter aus Adatomen der vierten Hauptgruppe auf Halbleitersubstraten bieten eine reichhaltige Spielwiese für die Untersuchung von Mott-Hubbard-Physik. Die Möglichkeit, verschiedene Adatomsorten und Substrate zu kombinieren, macht die Mitglieder dieser Materialklasse zu vielseitigen Modellsystemen, um den Einfluss von Korrelationsstärke, Bandfüllung und Spin-Bahn-Kopplung auf die elektronische Struktur zu untersuchen - sowohl im Experiment als auch mit Vielkörper-Rechnungen. Letztere prognostizieren exotische Grundzustände, wie z.B. chirale Supraleitung oder eine Spin-Flüssigkeit, wobei eine experimentelle Bestätigung jeweils noch aussteht. In dieser Dissertation werden drei derartige Systeme, nämlich die \(\alpha\)-Phasen von Sn/SiC(0001), Pb/Si(111) und kaliumdotiertem Sn/Si(111) mittels Rastertunnelmikroskopie und Photoemissionsspektroskopie diesbezüglich untersucht. Die Resultate sind potentiell relevant für Anwendungen im Bereich der Spintronik oder Quantencomputer. Für das erst kürzlich realisierte Gruppe-IV-Dreiecksgitter Sn/SiC(0001) zeigt diese Studie, bei der experimentelle und theoretische Methoden kombiniert werden, dass das System unerwartet starke Korrelationen aufweist, weil sie durch den teilweise ionischen Charakter und das geringe Abschirmungsvermögen des Substrats verstärkt werden. Die Spektralfunktion, die erstmals mit winkelaufgelöster Photoemission gemessen wird, zeigt keine überstruktur außer der intrinsischen \(\sqrt{3} \times \sqrt{3} R30^{\circ}\) Rekonstruktion des Gitters, was die Frage nach der Anordnung der Spins im Grundzustand aufwirft. Bei Pb/Si(111) haben bereits frühere Veröffentlichungen einen Phasenübergang bei der Oberflächenrekonstruktion von \(\sqrt{3}\times\sqrt{3}R30^{\circ}\) auf \(3 \times 3\) bei 86 K festgestellt. In dieser Arbeit zeigen Untersuchungen der Niedrigtemperaturphase mit hochaufgelöster Rastertunnelmikroskopie und -spektroskopie die Entstehung eines ladungsgeordneten Zustands. Dieser wird von der begleitend auftretenden strukturellen Neuordnung getrennt, welche entgegen bisheriger Voraussagen eine 2-hoch/1-tief-Anordnung aufweist. Mit Hilfe einer neu entwickelten Cluster-Rechenmethode wird ein Phasendiagramm erstellt, in dem die lokale und nichtlokale Coulomb-Wechselwirkung gegeneinander aufgetragen sind. Durch einen Vergleich zwischen theoretischen Spektralfunktionen mit Streuvektoren, die mittels Quasiteilchen-Interferenz bestimmt werden, kann Pb/Si(111) in besagtem Phasendiagramm platziert werden. Dadurch stellt sich heraus, dass elektronische Korrelationen die treibende Kraft für den ladungsgeordneten Zustand in Pb/Si(111) sind. Um einen dotierten Mott-Isolator in einem frustrierten System zu verwirklichen, wird Kalium auf das bekannte, korrelierte System Sn/Si(111) aufgebracht. Statt des erwarteten Isolator-Metall übergangs zeigen Messungen mit Rastertunnelspektroskopie, dass die elektronische Struktur von Sn/Si(111) nur lokal in der unmittelbaren Umgebung der Kaliumatome beeinflusst wird, ohne dass das System metallisch wird. Die Kaliumatome werden auf freien \(T_4\)-Plätzen des Substrats adsorbiert, was letztendlich zur Ausbildung von zwei unterschiedlichen Kalium-Zinn-Legierungen mit einem Kaliumanteil von 1/3 bzw. 1/2 führt. Komplementäre Messungen der Spektralfunktion mit winkelaufgelöster Photoemission zeigen, dass das untere Hubbardband von Sn/Si(111) durch die Kalium-Deposition allmählich seine Form verändert. Sobald Zinn und Kalium zu gleichen Teilen auf der Oberfläche vorliegen, ist diese Transformation beendet und das System kann als einfacher Bandisolator ohne die Notwendigkeit, elektronische Korrelationen zu berücksichtigen, beschrieben werden. KW - Rastertunnelmikroskopie KW - ARPES KW - Elektronenkorrelation KW - Oberflächenphysik Y1 - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-241758 ER -