TY - THES A1 - Knapp, Alexander Gerhard T1 - Resonant Spin Flip Raman-Spectroscopy of Electrons and Manganese-Ions in the n-doped Diluted Magnetic Semiconductor (Zn,Mn)Se:Cl T1 - Resonante Spin Flip Ramanspektroskopie von Elektronen und Manganionen im n-dotierten verdünnt magnetischen Halbleiter (Zn,Mn)Se:Cl N2 - Main focus of the present dissertation was to gain new insight about the interaction between magnetic ions and the conduction band of diluted magnetic semiconductors. This interaction in magnetic semiconductors with carrier concentrations near the metal-insulator transition (MIT) in an external magnetic field is barely researched. Hence, n-doped Zn1−xMnxSe:Cl samples were studied. Resonant Raman spectroscopy was employed at an external magnetic field between 1T and 7T and a temperature of 1.5K. The resulting magnetization of the material amplifies the splitting of states with opposite spins both in the valence and the conduction band. This is known as the "giant-Zeeman-effect". In this thesis, the resonance of the electron spin flip process, i.e. the enhancement of the signal depending on the excitation energy, was used as an indicator to determine the density of states of the charge carriers. The measured resonance profiles of each sample showed a structure, which consist of two partially overlapping Gaussian curves. The analysis of the Gaussian curves revealed that their respective maxima are separated independent of the magnetic field strenght by about 5 meV, which matches the binding energy of the donor bound exciton (D0, X). A widening of the full width at half maximum of the resonance profile was observed with increasing magnetic field. A detailed analysis of this behavior showed that the donor bound exciton spin flip resonance primarily accounts for the widening for all samples with doping concentrations below the metal insulator transition. A model was proposed for the interpretation of this observation. This is based on the fundamental assumptions of a spatially random distribution of the manganese ions on the group-II sublattice of the ZnSe crystal and the finite extension of the excitons. Thus, each exciton covers an individual quantity of manganese ions, which manifest as a local manganese concentration. This local manganese concentration is normally distributed for a set of excitons and hence, the evaluation of the distribution allows the determination of exciton radii Two trends were identified for the (D0, X) radii. The radius of the bound exciton decreases with increasing carrier concentration as well as with increasing manganese concentration. The determination of the (D0, X) radii by the use of resonant spin flip Raman spectroscopy and also the observation of the behavior of the (D0, X) radius depending on the carrier concentration, was achieved for the first time. For all samples with carrier concentrations below the metal-insulator transition, the obtained (X0) radii are up to a factor of 5.9 larger than the respective (D0, X) radii. This observation is explained by the unbound character of the (X0). For the first time, such an observation could be made by Raman spectroscopy.Beside the resonance studies, the shape of the Raman signal of the electron spin flip was analyzed. Thereby an obvious asymmetry of the signal, with a clear flank to lower Raman shifts, was observed. This asymmetry is most pronounced, when the spin flip process is excited near the (D0, X) resonance. To explain this observation, a theoretical model was introduced in this thesis. Based on the asymmetry of the resonantly excited spin flip signal, it was possible to estimate the (D0, X) radii, too. At external magnetic fields between 1.25T and 7T, the obtained radii lie between 2.38nm and 2.75nm. Additionally, the asymmetry of the electron spin flip signal was observed at different excitation energies. Here it is striking that the asymmetry vanishes with increasing excitation energy. At the highest excitation energy, where the electron spin flip was still detectable, the estimated radius of the exciton is 3.92nm. Beside the observations on the electron spin flip, the resonance behavior of the spin flip processes in the d-shell of the incorporated Mn ions was studied in this thesis. This was performed for the direct Mn spin flip process as well as for the sum process of the longitudinal optical phonon with the Mn spin flip. For the Stokes and anti-Stokes direct spin flip process and for the Stokes sum process, each the resonance curve is described by considering only one resonance mechanism. In contrast, resonance for the sum process in which an anti-Stokes Mn spin flip is involved, consists of two partially overlapping resonances due to different mechanisms. A detailed analysis of this resonance profile showed that for (Zn,Mn)Se at the chosen experimental parameters, an incoming and outgoing resonance can be achieved, separated by a few meV. Hereby, at a specific excitation energy range and a high excitation power, it was possible to achieve an inversion of the anti-Stokes to Stokes intensity, because only the anti-Stokes Mn spin flip process was enhanced resonantly. N2 - Ziel der Dissertation war das Erlangen neuer Erkenntnisse zur Wechselwirkung der magnetischen Ionen und des Leitungsbandes von verdünnten magnetischen Halbleitern. Diese Interaktion bei magnetischen Halbleitern mit Ladungsträgerkonzentration nahe des Metall-Isolator Übergangs (metal-insulator transition MIT) in externen Magnetfeldern ist bisher kaum erforscht. Daher wurden Untersuchung n-dotierte Zn1−xMnxSe:Cl untersucht. Als Analysetechnik wurde die resonante Spin Flip Raman-Spektroskopie bei einem externen Magnetfeld zwischen 1T und 7T und einer Temperatur von 1,5 K angewandt. Durch die entstehende Magnetisierung des Materials werden die Aufspaltungen der Zustände mit entgegengesetzten Spins sowohl im Valenz- als auch im Leitungsband verstärkt. Dies ist als "giant-Zeeman effect" bekannt. In dieser Arbeit wurde die Resonanz des Spin Flip Prozesses, d.h. die Signalerhöhung in Abhängigkeit der Anregungsenergie, als Indikator zur Bestimmung der Ladungsträgerzustandsdichte genutzt. Die gemessenen Resonanzprofile aller Proben zeigten dabei eine Struktur, welche aus sich zwei teilweise überlagernden Gaußkurven bestand. Mit steigendem Magnetfeld wurde eine deutliche Zunahme der Halbwertsbreite der Resonanzprofile beobachtet. Die detaillierte Analyse dieses Verhaltens zeigte, dass für alle Proben mit einer Dotierung unterhalb des Metall-Isolator-Übergangs, die Verbreiterung primär auf den Donor gebundenen Exzitonen Anteil der Resonanzkurve entfällt. Zur Deutung dieser Beobachtung wurde ein Modell entwickelt. Dieses beruht auf der grundlegenden Annahme einer räumlich statistisch Verteilung der Mangan-Ionen auf dem Gruppe-II Untergitter des ZnSe Kristalls, sowie der endlichen Ausdehnung der Exzitonen. Somit erfasst jedes einzelne Exziton eine individuelle Anzahl von Mangan-Ionen, was sich als lokale Mangankonzentration manifestiert. Diese lokale Mangankonzentration normalverteilt für ein Set von Exzitonen und deren Auswertung erlauben einen Rückschluss auf die Radien der Exzitonen. Zwei Trends für die (D0, X) Radien konnten identifiziert werden. Sowohl mit steigender Ladungsträgerkonzentration als auch mit steigendem Mangangehalt nimmt der Radius der gebundenen Exzitonen ab. Es gelangte erstmalig die Bestimmung der (D0, X) Radien mittels resonanter Spin Flip Raman-Spektroskopie und die Beobachtung des Verhaltens der (D0, X) Radien in Abhängigkeit der Ladungsträgerkonzentration. Die ermittelten (X0) Radien sind für die Proben mit Ladungsträgerkonzentrationen unterhalb des Metall-Isolator-Übergangs im Vergleich zu den (D0, X) Radien um einen Faktor von bis zu 5,9 größer. Diese Beobachtung lässt sich durch den ungebundenen Charakter der (X0) erklären. Aufgrund dessen erfasst ein (X0) während seiner Lebenszeit im Vergleich zu einem (D0, X) einen räumlich ausgedehnteren Bereich des Kristalls. Hierdurch konnte erstmalig mittels Raman-Spektroskopie solch eine Beobachtung gemacht werden. Neben den Resonanzuntersuchungen des elektronischen Spin Flips wurde dessen Preakform im Ramanspektrum analysiert. Dabei wurde eine deutliche Asymmetrie des Signals beobachtet, sichtbar als Flanke zu niedrigeren Raman- Verschiebungen. Zur Erklärung dieser Beobachtungen kann ebenfalls das eingeführte Modell angewandt werden. Anhand der Asymmetrie des resonant angeregten Spin Flip Signals konnten hiermit die Radien der (D0, X) bestimmt werden. Zusätzlich wurde die Asymmetrie bei unterschiedlichen Anregungsenergien sichtbar. Hierbei fiel auf, dass diese mit steigender Anregungsenergie abnimmt. Desweiteren wurde zusätzlich zu den Beobachtungen des elektronischen Spin Flips, das Resonanzverhalten des Spin Flips der einzelnen Mn-Ionen in dieser Arbeit untersucht. Dies wurde sowohl für den direkten Mn Spin Flip Prozess, als auch den Summenprozesses aus einem longitudinal optischen Phonon und einem Mn Spin Flip durchgeführt. Jeweils eine Resonanz wurde sowohl für die direkten Stokes und anti-Stokes Prozesse, als auch für den Stokes Summenprozess beobachtet. Im Gegensatz hierzu besteht das Resonanzprofil des Summenprozesses, bei dem ein Anti-Stokes Mn Spin Flip involviert ist, aus zwei sich überlappenden Resonanzanteile. Eine genaue Analyse dieses Resonanzprofils ergab, dass es bei (Zn,Mn)Se und den gewählten experimentellen Parametern möglich ist, sowohl eine eingehende als auch eine ausgehende Resonanz für diesen Summenprozess mit einer Energiedifferenz von wenigen meV zu erhalten. Die zusätzlich auftretende eingehende Resonanz konnte dabei dem optischen Übergang von dem mj = 1/2 Valenzband- zum mj = -1/2 Leitungsbandzustand zugeordnet werden. Die daraufhin folgende Anregung eines LO Phonons führt zu einer Reduzierung der Energie des gestreuten Photons. Dies erzeugt die beobachtete Überlagerung der Resonanzen, gemessen in der Energie der gestreuten Photonen. Hierdurch war es möglich, bei geeigneter Anregungsenergie und hoher Anregungsleistung eine Inversion der Anti-Stokes zu Stokes Intensität zu beobachten, da die eingehende Resonanz in diesem Fall nur für den Anti-Stokes Mn Spin Flip auftrat KW - Raman-Spektroskopie KW - Wide-gap-Halbleiter KW - n-Halbleiter KW - Spin flip KW - Zinkselenid KW - verdünnt magnetische Halbleiter KW - diluted magnetic Semiconductor Y1 - 2019 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-186099 ER - TY - THES A1 - Klein, Johannes Hubert T1 - Electron Transfer and Spin Chemistry in Iridium-Dipyrrin Dyads and Triads T1 - Elektronentransfer und Spinchemie in Iridium-Dipyrrin-Dyaden und -Triaden N2 - The successful synthesis of a family of donor-iridium complex-acceptor triads (T1–T6, pMV1 and mMV1) and their electrochemical and photophysical properties were presented in this work. Triarylamines (TAA) were used as donors and naphthalene diimide (NDI) as acceptor. A bis-cyclometalated phenylpyrazole iridium dipyrrin complex acts as a photosensitiser. In addition, a molecular structure of T1 was obtained by single crystal X-ray diffraction. Transient absorption spectroscopy experiments of these triads resembled that upon excitation a photoinduced electron transfer efficiently generates long-lived, charge-separated (CS) states. Thereby, the electron-transfer mechanism depends on the excitation energy. The presence of singlet and triplet CS states was clarified by magnetic-field dependent transient-absorption spectroscopy in the nanosecond time regime. It was demonstrated that the magnetic field effect of charge-recombination kinetics showed for the first time a transition from the coherent to the incoherent spin-flip regime. The lifetime of the CS states could be drastically prolonged by varying the spacer between the iridium complex and the NDI unit by using a biphenyl instead of a phenylene unit in T4. A mixed-valence (MV) state of two TAA donors linked to an iridium metal centre were generated upon photoexcitation of triad pMV1 and mMV1. The mixed-valence character in these triads was proven by the analysis of an intervalence charge-transfer (IV-CT) band in the (near-infrared) NIR spectral region by femtosecond pump-probe experiments. These findings were supported by TD-DFT calculations. The synthesis of dyads (D1–D4) was performed. Thereby the dipyrrin ligand was substituted with electron withdrawing groups. The electrochemical and photophysical characterisation revealed that in one case (D4) it was possible to generate a CS state upon photoexcitation. N2 - In dieser Arbeit wurden die erfolgreiche Synthese einer Donor-Iridiumkomplex-Akzeptor-Familie (Triaden T1–T6, pMV1 und mMV1) und deren elektrochemischen und photophyiskalischen Eigenschaften vorgestellt. Als Donor wurden Triarylamine (TAA) verwendet, als Akzeptoreinheit diente ein Naphthalin-Diimid (NDI). Ein bis-cyclometallierter Phenylpyrazol-Iridium-Dipyrrin-Komplex übernahm die Aufgabe des Photosensibilisators. Die synthetischen Arbeiten konnten mit einer molekularen Struktur von T1 mittels Röntgenbeugung eines Einkristalls ergänzt werden. Bei Photoanregung der Triaden mit transienter Absorptions-Spektroskopie wurde die sehr effiziente Bildung von langlebigen, ladungsgetrennten (CS) Zuständen beobachtet. Es wurde zudem herausgefunden, dass der Elektronentransfer (ET)-Mechanismus von der verwendeten Anregungswellenlänge abhängt. Der Nachweis von Singulett und Triplett CS-Zuständen wurde mittels magnetfeldabhängiger, transienter Absorptions-Spektroskopie erbracht. Eine Analyse des Magnetfeldeffekts der Ladungsrekombinations-Kinetik zeigte zum ersten Mal einen Übergang von einem kohärenten zu einem inkohärenten Spinumkehrprozess. Die Lebenszeit des CS-Zustandes ließ sich dramatisch verlängern indem die Phenylen- durch eine Biphenyl-Brückeneinheit zwischen dem Iridiumkomplex und dem NDI ersetzt wurde. Gemischvalente Zustände konnten mittels photinduziertem Elektronentransfer in den Triaden pMV1 und mMV1 erzeugt werden. Im Fall von pMV1 wurde eine intensive Intervalenz-Ladungstransfer (IV-CT) Bande im nahinfraroten Spektralbereich mittels Femtosekunden transienter Anregungs-Abfrage-Spektroskopie beobachtet werden. Die Analyse dieser IV-CT Bande wurde mit TD-DFT Rechnungen vervollständigt. Die Synthese von Dyaden (D1–D4) wurde erfolgreich durchgeführt, dabei wurde der Dipyrrin-Ligand mit elektronenziehenden Substituenten versehen. Die spektroskopische und elektrochemische Analyse erbrachte nach erfolgter Lichtanregung in einem Fall (D4) ebenfalls einen CS-Zustand. KW - Elektronentransfer KW - Spin flip KW - Triad KW - Ladungstransfer KW - Photosensibilisator KW - photoinduced electron transfer KW - charge-separated state KW - spin chemistry KW - donor-photosensibilisator-acceptor triad KW - iridium complex KW - photoinduzierter Elektronentransfer KW - Spinchemie KW - Donor-Photosensibilisator-Akzeptor Triade KW - Iridiumkomplexe Y1 - 2015 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-118726 ER - TY - THES A1 - Kehl, Christian T1 - Magnetic soft mode behaviour investigated via Multi-Spin Flip Raman Spectroscopy on near surface Cd1-xMnxTe/Cd1-yMgyTe Quantum wells T1 - Untersuchung des magnetischen Soft-Mode-Verhaltens an nahe an der Oberfläche liegenden Cd1-xMnxTe/Cd1-yMgyTe Quantentrögen mittels Multi-Spin Flip Raman Spektroskopie N2 - In the context of the ongoing discussion about a carrier-induced ferromagnetic phase transition in diluted-magnetic II-VI semiconductors (DMS), theoretical studies on coherent dynamics of localized spins coupled with a two-dimensional hole gas (2DHG) in DMS quantum wells (QWs) were done by K.V. KAVOKIN. His key for studying the exchange interaction of the localized spin ensemble (e.g. Mn2+) with the 2DHG is the Larmor frequency of the localized Mn-ion spins and thus their Mn-g-factor. It was shown that the 2DHG affects a time evolution of the (Mn-) spin system in an in-plane magnetic field resulting in the reduction of its Larmor frequency (Mn-g-factor) under the influence of an oscillating effective field of holes. This is called magnetic soft mode (behaviour). The experimental access for demonstrating this Mn-g-factor reduction with increasing hole concentration is the method of Multi-Spin-Flip (SF) Raman scattering combined with the variation of the carrier concentration by photo-excitation with an additional light source (two-colour experiment). The main motivation for this thesis was the experimental confirmation of the theoretically predicted magnetic soft mode and the analysis of its dependence on the hole-concentration and external B-field, as well as its disappearance with increasing sample temperature. For that purpose, CdMnTe/CdMgTe QWs (Mn: 0.6%, 1.0%) positioned close to the sample surface (13−19nm) were investigated in an in-plane applied external magnetic field (up to 4.5T in Voigt-geometry) via a two-colour experiment i.e. using two light sources. This allows the spin excitation of Mn-ions by simultaneously tuning the hole-concentration towards the ferromagnetic phase transition by photo-generated carriers. Thus, one tuneable laser is responsible for resonant below-barrier excitation as a probe for Multi-SF Raman scattering. The other laser excites photo-generated carriers from above barrier (2.41eV) for tuning the hole concentration in the QW. Positioning the QW close to the sample surface causes a surface-induced p-doping of the QW (intrinsic hole concentration in the QW) and enables the active tuning of the hole concentration by photo-generated carriers due to different tunnelling behaviour of electrons and holes from the QW to the surface. The Mn-g-factor was decreased by quasi-continuously increasing the above-barrier illumination (and thus the hole concentration), while the below-barrier excitation (Multi-PR probe) was kept at a constant low power. This results in a Mn-g-factor reduction starting from its atomic value g=2.01 to lowest evaluated Mn-g-factor in this thesis g=1.77. This is a magnetic softening of 12%. Apart from the general magnetic soft mode behaviour at low temperatures, one of the main experimental results in this thesis is the confirmation of the theoretical prediction that the magnetic soft mode behaviour in the external B-field does not only depend on the carrier concentration but also on the B-field strength itself. An additional aspect is the temperature dependence of the magnetic soft mode. The Mn-g-factor decrease is suppressed with increasing temperature almost reaching the atomic Mn-g-factor at 4.2K (g=1.99). This behaviour is due to the T-induced weakening of the transverse 2DHG spin susceptibility. The results of the investigations concerning the cap layer thickness impact on the QW carrier characteristics were investigated in the cap thickness range of 13nm to 19nm. The cap thickness configures on the one hand the intrinsic hole concentration of the QW ("2DHG offset") due to the surface-induced p-doping and sets the "starting point" for the Mn-g-factor reduction. On the other hand the cap thickness determines the probability of electron tunnelling to the surface and thus the efficiency of the hole tuning by light. The latter is the criterion for the range of Mn-g-factor reduction by light. This two dependences were pointed out by the photo-generated hole influence on the QW PL-spectra which results in tuning the exciton-trion ratio. In summary both mechanisms are of relevance for the hole tuning and thus for the magnetic soft-mode behaviour. The mechanism of tunnelling time prevails at small cap layer thicknesses while the surface-induced p-doping plays the major role for larger cap thicknesses (> 25nm). In conclusion, the presented method in this thesis is a sensitive tool to study the dynamics of the spin excitations and the paramagnetic susceptibility in the vicinity of the hole-induced ferromagnetic phase transition. N2 - Im Zusammenhang mit den aktuellen Diskussionen über einen ladungsträgerinduzierten ferromagnetischen Phasenübergang in verdünnt-magnetischen II-VI-Halbleitern wurden von K.V. KAVOKIN theoretische Untersuchungen zu kohärenter Dynamik von lokalisierten Spins durchgeführt, welche mit dem zweidimensionalen Lochgas im DMS Quantentrog (QT) koppeln. Die Larmorfrequenz der lokalisierten Mn-Ionen Spins und der damit verbundene Mn-g-Faktor sind dabei der experimentelle Zugang, um die Wechselwirkung des lokalisierten Spinensembles mit dem zweidimensionalen Lochgas zu untersuchen. Das 2DHG ruft eine zeitliche Entwicklung des (Mn-) Spinsystems in einem in der Quantentrogebene angelegten äußeren Magnetfeld hervor. Dies hat die Verringerung der Larmorfrequenz und damit des Mn-g-Faktors, beeinflusst durch ein oszillierendes effektives Austauschfeld der Löcher zur Folge. Dies wird magnetisches Softmode-Verhalten genannt. Multi-Spin-Flip(SF)-Raman-Spektroskopie in Verbindung mit einer zusätzlichen Lichtquelle (genannt Zwei-Farben-Experiment) ist das probate Mittel, um diese Reduzierung des Mn-g-Faktors durch die photo-generierte Erhöhung der Lochkonzentration des 2DHG zu demonstrieren. Die experimentelle Bestätigung des theoretisch vorhergesagten magnetischen Softmode-Verhaltens, sowie dessen Abhängigkeit von der Lochkonzentration und dem externen B-Feld, also auch dessen Verschwinden mit steigender Probentemperatur zu analysieren, war die Motivation dieser Arbeit. Aus diesem Grund wurden nahe (13-19nm) an der Probenoberflache liegende CdMnTe/CdMgTe Quantentroge (Mn: 0,6%; 1,0%) in einem parallel zur Quantentrogebene angelegten externen Magnetfeld (mit bis zu 4,5T) mittels Zwei-Farben-Experiment (d.h. mittels zweier Laser-Lichtquellen) untersucht. Dieses ermöglicht die Anregung der Mn-Spins bei gleichzeitiger Erhöhung der Lochkonzentration in Richtung des ferromagnetischen Phasenübergangs durch photo-generierte Ladungsträger. Dabei dient ein durchstimmbarer Laser zur resonanten Anregung im Quantentrog als Lichtquelle für die Multi-SF-Raman-Streuung. Der andere Laser hingegen erzeugt photogenerierte Ladungsträger oberhalb der Quantentrogbarriere (2,41eV), um die Lochkonzentration im Quantentrog einzustellen. Die Reduzierung des Mn-g-Faktors erfolgte durch quasikontinuierliche Erhöhung der Beleuchtung oberhalb der Barriere und folglich auch der Lochkonzentration, während die resonante Anregungsleistung im Quantentrog (d.h. die Multi-Spin-Flip-Sonde) niedrig und konstant gehalten wurde. Hiermit wurde die Verringerung des Mn-g-Faktors nachgewiesen, ausgehend von dessen atomaren Wert g=2,01 hin zu dem, in dieser Arbeit kleinsten ermittelten Wert von g =1,77. Dies entspricht einem magnetischen "softening" von 12%. Neben dem allgemeinen magnetischen Softmode-Verhalten bei niedriger Temperatur, war eines der wichtigsten experimentellen Ergebnisse dieser Arbeit die Bestätigung der theoretisch vorhergesagten Abhängigkeit des magnetischen Softmode-Verhaltens von der Magnetfeldstärke selbst und nicht nur von der Lochkonzentration im externen Magnetfeld. Die Mn-g-Faktor-Reduzierung wirkt sich bei kleinen B-Feldern stärker aus. Ein weiterer experimenteller Aspekt ist die Temperaturabhängigkeit des magnetischen Softmode-Verhaltens. Mit steigender Temperatur wird die Mn-g-Faktor-Reduzierung unterdrückt und der g-Faktor erreicht bei 4,2K mit g=1,99 fast seinen atomaren Wert. Grund dafür ist die temperaturinduzierte Abschwächung der transversalen 2DHG-Spin-Suszeptibilität. Die Auswirkung der Cap-Schichtdicke auf das Verhalten der Ladungsträgercharakteristik im Quantentrog wurde für Cap-Dicken im Bereich von 13nm bis 19nm untersucht. Die Cap-Dicke legt einerseits, durch die oberflächeninduzierte p-Dotierung, die intrinsische Lochkonzentration des Quantentrogs fest ("2DHG offset") und damit den "Startpunkt" für die Mn-g-Faktor-Reduzierung. Andererseits bestimmt die Cap-Dicke die Tunnelwahrscheinlichkeit der Elektronen zur Oberfläche und damit wiederum die Effizienz der Lochkonzentrationsbeeinflussung durch das eingestrahlte Licht. Letzteres ist das Kriterium dafür, wie groß der Einflussbereich ist, in dem eine Mn-g-Faktor-Reduzierung durch Licht stattfinden kann. Durch den Einfluss der photo-generierten Löcher auf das Quantentrog-PL-Spektrum und der damit verbundenen Beeinflussung des Exziton-Trion-Verhältnisses, konnten die beiden oben genannten Abhängigkeiten herausgearbeitet werden. Zusammenfassend sind beide Mechanismen für die Loch-Abstimmung im QT und damit für das magnetische soft-mode Verhalten von Bedeutung. Während der Mechanismus der Tunnelwahrscheinlichkeit bei schmalen Cap-Dicken überwiegt, spielt die oberflächeninduzierte p-Dotierung des QTs bei größeren Cap-Stärken (>25nm) die Hauptrolle. Fazit: Die, in dieser Arbeit präsentierte Methode ist ein sensibles Werkzeug, um die Dynamik der Spin-Anregungen und der paramagnetischen Suszeptibilität im Hinblick auf den Loch-induzierten ferromagnetischen Übergang zu untersuchen. KW - Raman-Spektroskopie KW - Quantenwell KW - Spin flip KW - Semimagnetischer Halbleiter KW - g-Faktor KW - Paramagnetic resonance KW - carrier-induced ferromagnetism KW - multi-spin flip Y1 - 2010 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-56088 ER - TY - THES A1 - Lentze, Michael T1 - Spin-flip Raman Untersuchungen an semimagnetischen II-VI Halbleiter-Quantentrögen und Volumenproben T1 - Spin-flip-Raman studies of semimagnetic II-VI heterostructures N2 - Im Zentrum dieser Arbeit standen ramanspektroskopische Untersuchungen der elektronischen spin-flip-Übergänge an semimagnetischen (Zn,Mn)Se Proben. Hierbei wurden sowohl Quantentrogstrukturen untersucht als auch volumenartige Proben. Ziel der Forschung war dabei, ein tieferes Verständnis der Wechselwirkungen der magnetischen Ionen mit den Leitungsbandelektronen der Materialien zu gewinnen. Im Hinblick auf mögliche zukünftige spin-basierte Bauelemente lag das Hauptaugenmerk auf dem Einfluss von n-Dotierung bis zu sehr hohen Konzentration. Hierfür standen verschiedene Probenreihen mit unterschiedlichen Dotierungskonzentrationen zur Verfügung. N2 - In the present doctoral thesis, spin flip Raman studies of semimagnetic (Zn,Mn)Se samples were in the focus of interest. Quantum wells as well as bulk-like materials were investigated. The main goal was a better understanding of the exchange interaction behaviour of heavily n-doped semimagnetic samples. The influence of doping on the exchange interaction is of special relevance with regard to spintronics applications. Several series of high quality MBE-grown (Zn,Mn)Se -samples samples were available. KW - Dotierter Halbleiter KW - Spin flip KW - Raman-Spektroskopie KW - Zinkselenid KW - Mangan KW - Zwei-Sechs-Halbleiter KW - Würzburg / Sonderforschungsbereich II-VI-Halbleiter KW - Dotierung KW - n-Halbleiter KW - Niederdimensionaler Halbleiter KW - semimagnetic semiconductor KW - II-VI heterostructures KW - spin-flip Raman spectroscopy KW - n-doping Y1 - 2009 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-34834 ER - TY - THES A1 - Keller, Dirk T1 - Optische Eigenschaften ZnSe-basierter zweidimensionaler Elektronengase und ihre Wechselwirkung mit magnetischen Ionen T1 - ZnSe-based QWs with a two-dimensional electron gas: Optical properties and interaction with magnetic ions N2 - In dieser Arbeit wurden nichtmagnetische und semimagnetische ZnSe-basierte Quantentröge untersucht. Im Mittelpunkt des Interesses standen hierbei vor allem die Modifikation der optischen Spektren mit einer zunehmenden Modulationsdotierung der Strukturen und der Einfluss von Spinflip-Streuungen der freien Band-Elektronen an den Mn-Ionen auf die Magnetisierung und somit die Zeeman-Aufspaltung der Strukturen. Als experimentelle Methoden wurden Photolumineszenz (PL), Photolumineszenzanregung (PLE) und Reflexionsmessungen verwendet, die in Magnetfeldern von bis zu B=48 T und bei Temperaturen im Bereich von 1.6 K bis 70 K durchgeführt wurden. Darüber hinaus wurde die Abhängigkeit der Spin-Gitter-Relaxationszeit der Mn-Ionen von der Mn-Konzentration und der Elektronengasdichte in den Quantentrögen durch zeitaufgelöste Lumineszenzmessungen untersucht. Der Einfluss eines Gradienten in der s/p-d-Austauschwechselwirkung auf die Diffusion der Ladungsträger bildet einen weiteren Schwerpunkt dieser Arbeit. Als experimentelle Methode wurde hierbei ortsaufgelöste Lumineszenz verwendet. N2 - In the present work, nonmagnetic and semimagnetic ZnSe based quantum wells were studied. The thesis was focussed on the modification of optical spectra with an increasing modulation-doping of the structures. Further emphasis was placed on the influence of the spinflip scattering of the free carriers and the Mn ions on the magnetization and thus the giant Zeeman splitting of the structures. As experimental methods, photoluminescence spectroscopy (PL), photoluminescence excitation spectroscopy (PLE) and reflection measurements were used and were performed in magnetic fields up to B=48 T and at temperatures within the range of 1.6 K to 70 K. In addition, the dependence of the spin-lattice relaxation time of the Mn ions on the Mn concentration and the electron density was examined by time-resolved luminescence spectroscopy. The influence of a gradient in the s/p-d-exchange interaction on the diffusion of carriers was studied by spatially resolved luminescence spectroscopy. KW - Zinkselenid KW - Dimension 2 KW - Elektronengas KW - Optische Eigenschaft KW - Manganselenide KW - Quantenwell KW - Elektronenstreuung KW - Spin flip KW - Manganion KW - Quantentrog KW - Magneto-optische Eigenschaften KW - 2DEG KW - Exziton KW - Spinflip-Streuung KW - quantum wells KW - magneto-optical properties KW - 2DEG KW - excitons KW - spinflip scattering Y1 - 2004 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-14774 ER -