TY - THES A1 - Samiepour, Marjan T1 - Fabrication and characterization of CPP-GMR and spin-transfer torque induced magnetic switching T1 - Herstellung und Charakterisierung von CPP-GMR und Spin-Transfer-Drehmoment induzierten magnetisches Schalten N2 - Even though the unique magnetic behavior for ferromagnets has been known for thousands of years, explaining this interesting phenomenon only occurred in the 20th century. It was in 1920, with the discovery of electron spin, that a clear explanation of how ferromagnets achieve their unique magnetic properties came to light. The electron carries an intrinsic electric charge and intrinsic angular momentum. Use of this property in a device was achieved in 1998 when Fert and Gru¨nberg independently found that the resistance of FM/NM/FM trilayer depended on the angle between the magnetization of the two layers. This phenomena which is called giant magnetoresistance (GMR) brought spin transfer into mainstream. This new discovery created a brand new research fi called “spintronics” or “spin based electronics” which exploits the intrinsic spin of electron. As expected spintronics delivered a new generation of magnetic devices which are currently used in magnetic disk drives and magnetic random access memories (MRAM). The potential advantages of spintronics devices are non-volatility, higher speed, increased data density and low power consumption. GMR devices are already used in industry as magnetic memories and read heads. The quality of GMR devices can be increased by developing new magnetic materials and also by going down to nanoscale. The desired characteristic properties of these new materials are higher spin polarization, higher curie temperature and better spin filtering. Half-metals are a good candidate for these devices since they are expected to have high polarization. Some examples of half-metals are Half-Heusler alloy, full Heusler alloy and Perovskite or double Perovskite oxides. The devices discussed in this thesis have NiMnSb half-Heusler alloy and permalloy as the ferromagnetic layers separated by Cu as the nonmagnetic layer. This dissertation includes mainly two parts, fabrication and characterization of nan- opillars. The layer stack used for the fabrication is Ru/Py/Cu/NiMnSb which is grown on an InP substrate with an (In,Ga)As buff by molecule beam epitaxy (MBE). A new method of fabrication using metal mask which has a higher yield of working samples over the previous method (using the resist mask) used in our group is discussed in detail. Also, the advantages of this new method and draw backs of the old method are explained thoroughly (in chapter 3). The second part (chapters 4 and 5) is focused on electrical measurements and charac- terization of the nanopillar, specially with regard to GMR and spin-transfer torque (STT) measurements. In chapter 4, the results of current perpendicular the plane giant mag- netoresistance (CPP-GMR) measurements at various temperatures and in-plane magnetic fi are presented. The dependence of CPP-GMR on bias current and shape anisotropy of the device are investigated. Results of these measurements show that the device has strong shape anisotropy. The following chapter deals with spin-transfer torque induced magnetic switching measurements done on the device. Critical current densities are on the order of 106 A/cm2, which is one order of magnitude smaller than the current industry standards. Our results show that the two possible magnetic configurations of the nanopillar (parallel and anti-parallel) have a strong dependence on the applied in-plane magnetic fi Fi- nally, four magnetic fi regimes based on the stability of the magnetic configuration (P stable, AP stable, both P and AP stable, both P and AP unstable) are identified. N2 - Obwohl das einzigartige ferromagnetische Verhalten seit Tausenden Jahren bekannt ist, traten Erklärungen zu diesem interessanten Phänomen erst im 20. Jahrhundert auf. Erst im Jahr 1920, mit der Entdeckung des Elekronenspin, gab es eine Vorstellung davon, wie die Ferromagnetika ihre einzigartigen magnetischen Eigenschaften erhalten. Die Elektronen sind sowohl Träger einer intrinsischen Ladung als auch eines intrinsichen Drehimpulses. Die Nutzung dieser Eigenschaften in Bauteilen wurde 1998 erreicht, als Fert und Grünberg unabhängig voneinander die Entdeckung machten, dass der Widerstand eines Dreischichtsystems bestehend aus FM/NM/FM abha¨ngig vom Winkel der Magnetisierung in den zwei ferromagnetischen Schichten ist. Dieses Phänomen, welches als Riesenmagnetwiderstand (GMR, Giant Magnetoresistance) bekannt ist, führte dazu, dass sich der Spintransport zu einem Mainstream entwickelte. Diese neuartige Entdeckung brachte ein ganz neues Forschungsgebiet hervor, das als sogenannte Spintronik oder auch spinbasierte Elektronik bekannt ist, welche den intrinsischen Spin der Elektronen nutzt. Wie erwartet lieferte die Spintronik eine neue Generation von magnetischen Bauelementen, welche in Festplatten und magnetoresistiven RAM-Speichern (MRAM, magnetic random access memory) zu fi sind. Die großen Vorteile der spintronischen Bauelemente sind die Nichtvolalität, die höheren Geschwindigkeiten, die verbesserte Datendichte und der geringerer Energieverbrauch. GMR-Bauteile werden bereits in der Industrie als magnetische Speicher und Leseköpfe verwendet. Die Qualität der GMR-Bauteile kann durch die Entwicklung von neuen magnetischen Materialien aber auch durch Verkleinerung, also Nutzung der Nanoskala verbessert wer- den. Zu den gewünschten charakteristischen Eigenschaften dieser neuen Materialien zählen eine höhere Spinpolarisation, höher erreichbare Curie-Temperaturen und eine verbesserte Spinfi tion. Halbmetalle, wie z.B., Heusler-Legierungen, Perovskite oder auch doppeloxide sind hierfür gute Kandidaten, weil von ihnen eine hohe Polarisierbarkeit erwartet wird. Die Bauteile, die in dieser Arbeit diskutiert werden, bestehen aus einer NiMnSb-Heusler-Legierung und Permalloy als ferromagnetische Schichten getrennt durch Cu als nichtmagnetische Schicht. Die Dissertation beinhaltet hauptsächlich zwei Aspekte nämlich die Herstellung und Charakterisierung von Nanosäulen. Die benutzte Schichtung zur Herstellung ist Ru/Py/Cu /NiMnSb, welche mittels MBE (molecular beam epitaxy) auf einem InP-Substrat mit einem (In,Ga)As-Puff gewachsen ist. Eine neue Herstellungsmethode, welche Metallmasken gegenüber der früher in unserer Arbeitsgruppe gängigen Methode (Verwendung von Resistmasken) nutzt, um eine erhöhte Probenfunktionalität zu erreichen, wird im Detail diskutiert. Ebenso werden die Vorteile dieser neuen Methode und das Detail der alten Methode vollständig in Kapitel 3 erläutert. Im Fokus des zweiten Teils (Kapitel 4 und 5) stehen elektrische Messungen und Charakterisierung der Nanos¨aulen im Hinblick auf den GMR und den Spintransfer-Moment-Messungen (SST). In Kapitel 4 werden die Ergebnisse der Strommessungen, die senkrecht zur GMR-Ebene (CPP-GMR) bei verschiedenen Temperaturen und eines in der Ebene angelegten Magnetfeldes durchgeführt wurden vorgestellt zudem wird die Abhängigkeit des CPP-GMR von Bias-Strömen und von der Formanisotropy der Bauteile untersucht. Ergebnisse dieser Messungen zeigen, dass die Bauteile eine groe Formanisotropy aufweisen. In den darauffolgenden Kapiteln werden Spintransfer-Moment Messungen, die durch magnetisches Schalten in den Bauteilen hervorgerufen wurden besprochen. Kritische Stromdichten liegen in der Größenordnung 106 A/cm2, welche eine Größenordnung kleiner ist als der aktuelle Industriestandard. Unsere Ergebnisse zeigen eine starke Abhängigkeit der zwei magnetischen Konfigurationsmöglichkeiten der Nanosäulen (parallel und anti- parallel) von dem in-plane Magnetfeld. Schließlich wurden vier magnetische Feldbereiche, basierend auf der Stabilität der magnetischen Konfiguration (P stabil, AP stabil, P und AP stabil, P und AP instabil) identifiziert. KW - Giantmagnetoresistance KW - spin-transfer torque KW - Heusler KW - CPP-GMR KW - Spin-Transfer-Drehmoment KW - Heusler KW - Riesenmagnetowiderstand KW - Spintronik Y1 - 2014 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-102226 ER - TY - THES A1 - Scheffler, Lukas T1 - Molecular beam epitaxy of the half-Heusler antiferromagnet CuMnSb T1 - Molekularstrahlepitaxie des halb-Heusler Antiferromagneten CuMnSb N2 - This work presents a newly developed method for the epitaxial growth of the half-Heusler antiferromagnet CuMnSb. All necessary process steps, from buffer growth to the deposition of a protective layer, are presented in detail. Using structural, electrical, and magnetic characterization, the material parameters of the epitaxial CuMnSb layers are investigated. The successful growth of CuMnSb by molecular beam epitaxy is demonstrated on InAs (001), GaSb (001), and InP (001) substrates. While CuMnSb can be grown pseudomorphically on InAs and GaSb, the significant lattice mismatch for growth on InP leads to relaxation already at low film thicknesses. Due to the lower conductivity of GaSb compared to InAs, GaSb substrates are particularly suitable for the fabrication of CuMnSb layers for lateral electrical transport experiments. However, by growing a high-resistive ZnTe interlayer below the CuMnSb layer, lateral transport experiments on CuMnSb layers grown on InAs can also be realized. Protective layers of Ru and Al2O3 have proven to be suitable for protecting the CuMnSb layers from the environment. Structural characterization by high resolution X-ray diffraction (full width at half maximum of 7.7 ′′ of the rocking curve) and atomic force microscopy (root mean square surface roughness of 0.14 nm) reveals an outstanding crystal quality of the epitaxial CuMnSb layers. The half-Heusler crystal structure is confirmed by scanning transmission electron microscopy and the stoichiometric material composition by Rutherford backscattering spectrometry. In line with the high crystal quality, a new minimum value of the residual resistance of CuMnSb (𝜌0 = 35 μΩ ⋅ cm) could be measured utilizing basic electrical transport experiments. An elaborate study of epitaxial CuMnSb grown on GaSb reveals a dependence of the vertical lattice parameter on the Mn/Sb flux ratio. This characteristic enables the growth of tensile, unstrained, and compressive strained CuMnSb layers on a single substrate material. Additionally, it is shown that the Néel temperature has a maximum of 62 K at stoichiometric material composition and thus can be utilized as a selection tool for stoichiometric CuMnSb samples. Mn-related defects are believed to be the driving force for these observations. The magnetic characterization of the epitaxial CuMnSb films is performed by superconducting quantum interference device magnetometry. Magnetic behavior comparable to the bulk material is found, however, an additional complex magnetic phase appears in thin CuMnSb films and/or at low magnetic fields, which has not been previously reported for CuMnSb. This magnetic phase is believed to be localized at the CuMnSb surface and exhibits both superparamagnetic and spin-glass-like behavior. The exchange bias effect of CuMnSb is investigated in combination with different in- and out-of-plane ferromagnets. It is shown that the exchange bias effect can only be observed in combination with in-plane ferromagnets. Finally, the first attempts at the growth of fully epitaxial CuMnSb/NiMnSb heterostructures are presented. Both magnetic and structural studies by secondary-ion mass spectrometry indicate the interdiffusion of Cu and Ni atoms between the two half-Heusler layers, however, an exchange bias effect can be observed for the CuMnSb/NiMnSb heterostructures. Whether this exchange bias effect originates from exchange interaction between the CuMnSb and NiMnSb layers, or from ferromagnetic inclusions in the antiferromagnetic layer can not be conclusively identified. N2 - In dieser Arbeit wird eine neu entwickelte Methode für das epitaktische Wachstum des antiferromagnetischen halb-Heuslers CuMnSb vorgestellt. Alle notwendigen Prozessschritte, vom Pufferschichtwachstum bis hin zum Aufbringen einer Schutzschicht, werden detailliert dargestellt. Mittels struktureller, elektrischer und magnetischer Charakterisierung werden die Materialparameter der epitaktischen CuMnSb-Schichten untersucht. Das erfolgreiche Wachstum von CuMnSb durch Molekularstrahlepitaxie wird auf InAs (001), GaSb (001) und InP (001) Substraten demonstriert. Während CuMnSb auf InAs und GaSb pseudomorph gewachsen werden kann, führt die signifikante Gitterfehlanpassung beim Wachstum auf InP bereits bei geringen Schichtdicken zur Relaxation. Aufgrund der geringeren Leitfähigkeit von GaSb im Vergleich zu InAs sind GaSb-Substrate besonders geeignet für die Herstellung von CuMnSb-Schichten für laterale elektrische Transportexperimente. Durch Einbringen einer hochohmigen ZnTe-Zwischenschicht unterhalb der CuMnSb-Schicht können jedoch auch laterale Transportexperimente an CuMnSb-Schichten, die auf InAs gewachsen werden, durchgeführt werden. Schutzschichten aus Ru und Al2O3 haben sich als geeignet erwiesen, die CuMnSb-Schichten vor der Umgebung zu schützen. Die strukturelle Charakterisierung mittels hochauflösender Röntgendiffraktometrie (Halbwertsbreite der Rocking-Kurve von 7.7′′) und Rasterkraftmikroskopie (quadratisches Mittel der Oberflächenrauhigkeit von 0.14nm) zeigt eine hervorragende Kristallqualität der epitaktischen CuMnSb-Schichten. Die halb-Heusler Kristallstruktur wird durch Rastertransmissionselektronenmikroskopie und die stöchiometrische Materialzusammensetzung durch Rutherford- Rückstreuungsspektrometrie bestätigt. In Übereinstimmung mit der hohen Kristallqualität konnte ein neuer Minimalwert des Restwiderstands von CuMnSb (𝜌0 = 35μΩ⋅cm) mit Hilfe von einfachen elektrischen Transportexperimenten gemessen werden. Eine ausführliche Untersuchung von epitaktischem CuMnSb, das auf GaSb gewachsen wurde, zeigt eine Abhängigkeit der vertikalen Gitterkonstante vom Mn/Sb-Flussverhältnis. Diese Eigenschaft ermöglicht das Wachstum von zugverspannten, unverspannten und druckverspannten CuMnSb Schichten auf einem einzigen Substratmaterial. Darüber hinaus wird gezeigt, dass die Néel-Temperatur bei stöchiometrischer Materialzusammensetzung ein Maximum von 62 K aufweist und somit als Auswahlinstrument für stöchiometrische CuMnSb Proben dienen kann. Es wird angenommen, dass Mn-bezogene Defekte ursächlich für diese Beobachtungen sind. Die magnetische Charakterisierung der epitaktischen CuMnSb-Filme erfolgt mittels Magnetometrie. Das magnetische Verhalten ist mit dem des Volumenmaterials vergleichbar. Allerdings tritt in dünnen CuMnSb Filmen und/oder bei niedrigen Magnetfeldern eine zusätzliche komplexe magnetische Phase auf, die bisher noch nicht für CuMnSb beobachtet wurde. Es wird angenommen, dass diese magnetische Phase an der CuMnSb-Oberfläche lokalisiert ist und sowohl superparamagnetisches als auch Spin-Glas-artiges Verhalten zeigt. Der Exchange Bias Effekt von CuMnSb wird in Kombination mit verschiedenen Ferromagneten mit vertikaler und horizontaler remanenter Magnetisierung untersucht. Es wird gezeigt, dass der Exchange Bias Effekt nur in Kombination mit Ferromagneten mit horizontaler remanenter Magnetisierung beobachtet werden kann. Schließlich werden die ersten Versuche zum Wachstum von vollständig epitaktischen CuMnSb/NiMnSb-Heterostrukturen vorgestellt. Sowohl magnetische als auch strukturelle Untersuchungen mittels Sekundärionen-Massenspektrometrie weisen auf die Interdiffusion von Cu- und Ni-Atomen zwischen den beiden halb-Heusler Schichten hin. Der Exchange Bias Effekt kann an den CuMnSb/NiMnSb Heterostrukturen beobachtet werden. Ob dieser Exchange Bias Effekt auf Austauschwechselwirkungen zwischen den CuMnSb- und NiMnSb-Schichten oder auf ferromagnetische Einschlüsse in der antiferromagnetischen Schicht zurückzuführen ist, lässt sich nicht eindeutig feststellen. KW - Molekularstrahlepitaxie KW - Heuslersche Legierung KW - half-Heusler KW - Antiferromagnetikum KW - CuMnSb KW - Antiferromagnet KW - Heusler Y1 - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-322839 ER -