TY - THES A1 - Hecht [geb. Wagener], Reinhard Johannes T1 - Processing and Characterization of Bulk Heterojunction Solar Cells Based on New Organic n-Type Semiconductors T1 - Prozessierung und Charakterisierung von Bulk-Heterojucktion Solarzellen auf Basis von neuen organischen n-Halbleitern N2 - This thesis established the fabrication of organic solar cells of DA dye donors and fullerene acceptors under ambient conditions in our laboratory, however, with reduced power conversion efficiencies compared to inert conditions. It was shown that moisture had the strongest impact on the stability and reproducibility of the solar cells. Therefore, utilization of robust materials, inverted device architectures and fast fabrication/characterization are recommended if processing takes place in air. Furthermore, the dyad concept was successfully explored in merocyanine dye-fullerene dyads and power conversion efficiencies of up to 1.14 % and 1.59 % were measured under ambient and inert conditions, respectively. It was determined that the major drawback in comparison to comparable BHJ devices was the inability of the dyad molecules to undergo phase separation. Finally, two series of small molecules were designed in order to obtain electron transport materials, using the acceptor-core-acceptor motive. By variation of the acceptor units especially the LUMO levels could be lowered effectively. Investigation of the compounds in organic thin film transistors helped to identify promising molecules with electron transport properties. Electron transport mobilities of up to 7.3 × 10−2 cm2 V−1 s−1 (ADA2b) and 1.39 × 10−2 cm2 V−1 s−1 (AπA1b) were measured in air for the ADA and AπA dyes, respectively. Investigation of selected molecules in organic solar cells proved that these molecules work as active layer components, even though power conversion efficiencies cannot compete with fullerene based devices yet. Thus, this thesis shows new possibilities that might help to develop and design small molecules as substitutes for fullerene acceptors. N2 - In dieser Arbeit wurde gezeigt, dass die Herstellung und Charakterisierung von organischen Solarzellen auf Basis von kleinen DA-Farbstoffen in Kombination mit Fullerenakzeptoren unter Umgebungsbedingungen möglich ist. Außerdem konnte herausgefunden werden, dass die Luftfeuchtigkeit den größten Einfluss auf die Stabilität und die Reproduzierbarkeit der organischen Solarzellen hat. Aus diesem Grund sind der Austausch labiler Komponenten, die Verwendung von invertierten Bauteilarchitekturen sowie eine zügige Herstellung und Charakterisierung bei Prozessierung an Luft zu empfehlen. In weiteren Experimenten konnte das Dyadenkonzept erfolgreich angewendet werden, sodass sich Effizienzen von 1.14 und 1.59 % unter ambienten bzw. inerten Bedingungen messen ließen. Das Unvermögen der Dyaden, separate Phasen aus Donor- und Akzeptorverbindung zu bilden, konnte als größte Schwäche der Verbindungen ausgemacht werden. Schlussendlich wurden zwei Serien von Molekülen mit der Absicht Elektronentransportmaterialien zu generieren basierend auf einem Akzeptor-Kern-Akzeptor-Strukturmotiv entworfen. Die Variation der Akzeptoren ermöglichte in der Tat eine systematische Absenkung der Grenzorbitale und insbesondere der LUMO-Niveaus. Weiterhin wurden die Verbindungen in organischen Dünnfilmtransistoren untersucht, um mehr über ihre Ladungstransporteigenschaften zu erfahren. Dabei konnten Moleküle ausgemacht werden, die zum Elektronentransport an Luft in der Lage sind. Für die besten ADA- und AπA-Farbstoffe konnten so jeweils Elektronenmobilitäten von 7.3 × 10−2 cm2 V–1 s–1 (ADA2b) und 1.39 × 10−2 cm2 V–1 s–1 (AπA1b) gemessen werden. Weitere Untersuchungen von ausgewählten Verbindungen in organischen Solarzellen, konnten beweisen, dass diese neu kreierten Moleküle im Prinzip als Aktivmaterialien funktionieren können, wenn auch die erzielten Effizienzen noch nicht mit denen von Fulleren-basierten Solarzellen konkurrieren konnten. Damit zeigt diese Arbeit neue Möglichkeiten auf, die bei der Entwicklung und dem Design von kleinen Molekülen als Alternativen zu Fullereneakzeptoren hilfreich sein können. KW - organic solar cells KW - A-D-A dyes KW - dyads KW - merocyanines KW - n-type semiconductors KW - Heterosolarzelle KW - Halbleiter KW - Merocyanine Y1 - 2019 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-161385 ER - TY - JOUR A1 - Stolte, Matthias A1 - Hecht, Reinhard A1 - Xie, Zengqi A1 - Liu, Linlin A1 - Kaufmann, Christina A1 - Kudzus, Astrid A1 - Schmidt, David A1 - Würthner, Frank T1 - Crystal Engineering of 1D Exciton Systems Composed of Single‐ and Double‐Stranded Perylene Bisimide J‐Aggregates JF - Advanced Optical Materials N2 - Single crystals of three at bay area tetraphenoxy‐substituted perylene bisimide dyes are grown by vacuum sublimation. X‐ray analysis reveals the self‐assembly of these highly twisted perylene bisimides (PBIs) in the solid state via imide–imide hydrogen bonding into hydrogen‐bonded PBI chains. The crystallographic insights disclose that the conformation and sterical congestion imparted by the phenoxy substituents can be controlled by ortho‐substituents. Accordingly, whilst sterically less demanding methyl and isopropyl substituents afford double‐stranded PBI chains of complementary P and M atropo‐enantiomers, single hydrogen‐bonded chains of homochiral PBIs are observed for the sterically more demanding ortho‐phenyl substituents. Investigation of the absorption and fluorescence properties of microcrystals and thin films of these PBIs allow for an unambiguous interpretation of these exciton systems. Thus, the J‐aggregates of the double‐stranded crystals exhibit a much larger (negative) exciton coupling than the single‐stranded one, which in contrast has the higher solid‐state fluorescence quantum yield. KW - fluorescence KW - J‐aggregates KW - perylene bisimides KW - reabsorption KW - single crystal structure Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-218221 VL - 8 IS - 18 ER - TY - JOUR A1 - Wildervanck, Martijn J. A1 - Hecht, Reinhard A1 - Nowak-Król, Agnieszka T1 - Synthesis and strong solvatochromism of push-pull thienylthiazole boron complexes JF - Molecules N2 - The solvatochromic behavior of two donor-π bridge-acceptor (D-π-A) compounds based on the 2-(3-boryl-2-thienyl)thiazole π-linker and indandione acceptor moiety are investigated. DFT/TD-DFT calculations were performed in combination with steady-state absorption and emission measurements, along with electrochemical studies, to elucidate the effect of two different strongly electron-donating hydrazonyl units on the solvatochromic and fluorescence behavior of these compounds. The Lippert–Mataga equation was used to estimate the change in dipole moments (Δµ) between ground and excited states based on the measured spectroscopic properties in solvents of varying polarity with the data being supported by theoretical studies. The two asymmetrical D-π-A molecules feature strong solvatochromic shifts in fluorescence of up to ~4300 cm\(^{−1}\) and a concomitant change of the emission color from yellow to red. These changes were accompanied by an increase in Stokes shift to reach values as large as ~5700–5800 cm\(^{−1}\). Quantum yields of ca. 0.75 could be observed for the N,N-dimethylhydrazonyl derivative in nonpolar solvents, which gradually decreased along with increasing solvent polarity, as opposed to the consistently reduced values obtained for the N,N-diphenylhydrazonyl derivative of up to ca. 0.20 in nonpolar solvents. These two push–pull molecules are contrasted with a structurally similar acceptor-π bridge-acceptor (A-π-A) compound. KW - solvatochromism KW - donor–acceptor KW - fluorescence KW - hydrazone KW - Lippert–Mataga plot KW - push–pull thienylthiazole KW - tetracoordinated boron Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-286186 SN - 1420-3049 VL - 27 IS - 17 ER -