TY - JOUR A1 - Hauptstein, Julia A1 - Forster, Leonard A1 - Nadernezhad, Ali A1 - Horder, Hannes A1 - Stahlhut, Philipp A1 - Groll, Jürgen A1 - Blunk, Torsten A1 - Teßmar, Jörg T1 - Bioink Platform Utilizing Dual-Stage Crosslinking of Hyaluronic Acid Tailored for Chondrogenic Differentiation of Mesenchymal Stromal Cells JF - Macromolecular Bioscience N2 - 3D bioprinting often involves application of highly concentrated polymeric bioinks to enable fabrication of stable cell-hydrogel constructs, although poor cell survival, compromised stem cell differentiation, and an inhomogeneous distribution of newly produced extracellular matrix (ECM) are frequently observed. Therefore, this study presents a bioink platform using a new versatile dual-stage crosslinking approach based on thiolated hyaluronic acid (HA-SH), which not only provides stand-alone 3D printability but also facilitates effective chondrogenic differentiation of mesenchymal stromal cells. A range of HA-SH with different molecular weights is synthesized and crosslinked with acrylated (PEG-diacryl) and allylated (PEG-diallyl) polyethylene glycol in a two-step reaction scheme. The initial Michael addition is used to achieve ink printability, followed by UV-mediated thiol–ene reaction to stabilize the printed bioink for long-term cell culture. Bioinks with high molecular weight HA-SH (>200 kDa) require comparably low polymer content to facilitate bioprinting. This leads to superior quality of cartilaginous constructs which possess a coherent ECM and a strongly increased stiffness of long-term cultured constructs. The dual-stage system may serve as an example to design platforms using two independent crosslinking reactions at one functional group, which allows adjusting printability as well as material and biological properties of bioinks. KW - hyaluronic acid KW - biofabrication KW - chondrogenic differentiation KW - dual-stage crosslinking KW - extracellular matrix Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-257556 VL - 22 IS - 2 ER - TY - JOUR A1 - Janzen, Dieter A1 - Bakirci, Ezgi A1 - Faber, Jessica A1 - Andrade Mier, Mateo A1 - Hauptstein, Julia A1 - Pal, Arindam A1 - Forster, Leonard A1 - Hazur, Jonas A1 - Boccaccini, Aldo R. A1 - Detsch, Rainer A1 - Teßmar, Jörg A1 - Budday, Silvia A1 - Blunk, Torsten A1 - Dalton, Paul D. A1 - Villmann, Carmen T1 - Reinforced Hyaluronic Acid-Based Matrices Promote 3D Neuronal Network Formation JF - Advanced Healthcare Materials N2 - 3D neuronal cultures attempt to better replicate the in vivo environment to study neurological/neurodegenerative diseases compared to 2D models. A challenge to establish 3D neuron culture models is the low elastic modulus (30–500 Pa) of the native brain. Here, an ultra-soft matrix based on thiolated hyaluronic acid (HA-SH) reinforced with a microfiber frame is formulated and used. Hyaluronic acid represents an essential component of the brain extracellular matrix (ECM). Box-shaped frames with a microfiber spacing of 200 µm composed of 10-layers of poly(ɛ-caprolactone) (PCL) microfibers (9.7 ± 0.2 µm) made via melt electrowriting (MEW) are used to reinforce the HA-SH matrix which has an elastic modulus of 95 Pa. The neuronal viability is low in pure HA-SH matrix, however, when astrocytes are pre-seeded below this reinforced construct, they significantly support neuronal survival, network formation quantified by neurite length, and neuronal firing shown by Ca\(^{2+}\) imaging. The astrocyte-seeded HA-SH matrix is able to match the neuronal viability to the level of Matrigel, a gold standard matrix for neuronal culture for over two decades. Thus, this 3D MEW frame reinforced HA-SH composite with neurons and astrocytes constitutes a reliable and reproducible system to further study brain diseases. KW - 3D model systems KW - melt electrowriting KW - cortical neurons KW - astrocytes KW - Ca\(^{2+}\)-Imaging KW - hyaluronic acid Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-318682 VL - 11 IS - 21 ER - TY - JOUR A1 - Hauptstein, Julia A1 - Forster, Leonard A1 - Nadernezhad, Ali A1 - Groll, Jürgen A1 - Teßmar, Jörg A1 - Blunk, Torsten T1 - Tethered TGF-β1 in a hyaluronic acid-based bioink for bioprinting cartilaginous tissues JF - International Journal of Molecular Sciences N2 - In 3D bioprinting for cartilage regeneration, bioinks that support chondrogenic development are of key importance. Growth factors covalently bound in non-printable hydrogels have been shown to effectively promote chondrogenesis. However, studies that investigate the functionality of tethered growth factors within 3D printable bioinks are still lacking. Therefore, in this study, we established a dual-stage crosslinked hyaluronic acid-based bioink that enabled covalent tethering of transforming growth factor-beta 1 (TGF-β1). Bone marrow-derived mesenchymal stromal cells (MSCs) were cultured over three weeks in vitro, and chondrogenic differentiation of MSCs within bioink constructs with tethered TGF-β1 was markedly enhanced, as compared to constructs with non-covalently incorporated TGF-β1. This was substantiated with regard to early TGF-β1 signaling, chondrogenic gene expression, qualitative and quantitative ECM deposition and distribution, and resulting construct stiffness. Furthermore, it was successfully demonstrated, in a comparative analysis of cast and printed bioinks, that covalently tethered TGF-β1 maintained its functionality after 3D printing. Taken together, the presented ink composition enabled the generation of high-quality cartilaginous tissues without the need for continuous exogenous growth factor supply and, thus, bears great potential for future investigation towards cartilage regeneration. Furthermore, growth factor tethering within bioinks, potentially leading to superior tissue development, may also be explored for other biofabrication applications. KW - biofabrication KW - bioink KW - chondrogenic differentiation KW - dual-stage crosslinking KW - hyaluronic acid KW - tethering KW - transforming growth factor-beta 1 Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-284239 SN - 1422-0067 VL - 23 IS - 2 ER - TY - JOUR A1 - Schmid, Rafael A1 - Schmidt, Sonja K. A1 - Hazur, Jonas A1 - Detsch, Rainer A1 - Maurer, Evelyn A1 - Boccaccini, Aldo R. A1 - Hauptstein, Julia A1 - Teßmar, Jörg A1 - Blunk, Torsten A1 - Schrüfer, Stefan A1 - Schubert, Dirk W. A1 - Horch, Raymund E. A1 - Bosserhoff, Anja K. A1 - Arkudas, Andreas A1 - Kengelbach-Weigand, Annika T1 - Comparison of hydrogels for the development of well-defined 3D cancer models of breast cancer and melanoma JF - Cancers N2 - Bioprinting offers the opportunity to fabricate precise 3D tumor models to study tumor pathophysiology and progression. However, the choice of the bioink used is important. In this study, cell behavior was studied in three mechanically and biologically different hydrogels (alginate, alginate dialdehyde crosslinked with gelatin (ADA–GEL), and thiol-modified hyaluronan (HA-SH crosslinked with PEGDA)) with cells from breast cancer (MDA-MB-231 and MCF-7) and melanoma (Mel Im and MV3), by analyzing survival, growth, and the amount of metabolically active, living cells via WST-8 labeling. Material characteristics were analyzed by dynamic mechanical analysis. Cell lines revealed significantly increased cell numbers in low-percentage alginate and HA-SH from day 1 to 14, while only Mel Im also revealed an increase in ADA–GEL. MCF-7 showed a preference for 1% alginate. Melanoma cells tended to proliferate better in ADA–GEL and HA-SH than mammary carcinoma cells. In 1% alginate, breast cancer cells showed equally good proliferation compared to melanoma cell lines. A smaller area was colonized in high-percentage alginate-based hydrogels. Moreover, 3% alginate was the stiffest material, and 2.5% ADA–GEL was the softest material. The other hydrogels were in the same range in between. Therefore, cellular responses were not only stiffness-dependent. With 1% alginate and HA-SH, we identified matrices that enable proliferation of all tested tumor cell lines while maintaining expected tumor heterogeneity. By adapting hydrogels, differences could be accentuated. This opens up the possibility of understanding and analyzing tumor heterogeneity by biofabrication. KW - breast cancer KW - melanoma KW - biofabrication KW - hydrogel KW - tumor heterogeneity Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-211195 SN - 2072-6694 VL - 12 IS - 8 ER - TY - THES A1 - Hauptstein, Julia T1 - Hyaluronic Acid-based Multifunctional Bioinks for 3D Bioprinting of Mesenchymal Stromal Cells for Cartilage Regeneration T1 - Hyaluronsäure-basierte multifunktionale Biotinten für den 3D Biodruck von mesenchymalen Stromazellen zur Knorpelregeneration N2 - Articular cartilage is a highly specialized tissue which provides a lubricated gliding surface in joints and thereby enables low-friction movement. If damaged once it has a very low intrinsic healing capacity and there is still no treatment in the clinic which can restore healthy cartilage tissue. 3D biofabrication presents a promising perspective in the field by combining healthy cells and bioactive ink materials. Thereby, the composition of the applied bioink is crucial for defect restoration, as it needs to have the physical properties for the fabrication process and also suitable chemical cues to provide a supportive environment for embedded cells. In the last years, ink compositions with high polymer contents and crosslink densities were frequently used to provide 3D printability and construct stability. But these dense polymeric networks were often associated with restricted bioactivity and impaired cell processes like differentiation and the distribution of newly produced extracellular matrix (ECM), which is especially important in the field of cartilage engineering. Therefore, the aim of this thesis was the development of hyaluronic acid (HA)-based bioinks with a reduced polymer content which are 3D printable and additionally facilitate chondrogenic differentiation of mesenchymal stromal cells (MSCs) and the homogeneous distribution of newly produced ECM. Starting from not-printable hydrogels with high polymer contents and restricted bioactivity, distinct stepwise improvements were achieved regarding stand-alone 3D printability as well as MSC differentiation and homogeneous ECM distribution. All newly developed inks in this thesis made a valuable contribution in the field of cartilage regeneration and represent promising approaches for potential clinical applications. The underlying mechanisms and established ink design criteria can further be applied to other biofabricated tissues, emphasizing their importance also in a more general research setting. N2 - Gelenkknorpel ermöglicht durch seine gleitfähige Oberfläche reibungsarme Bewegungen der Gelenke. Ist der Knorpel jedoch einmal geschädigt, kann er sich kaum selbst regenerieren und es gibt noch keine klinische Lösung, die das native Gewebe wiederherstellen kann. Ein vielversprechender Ansatz im Feld ist die 3D Biofabrikation, da sie gesunde Zellen mit bioaktiven Tintenmaterialen kombiniert. Hierbei ist die Zusammensetzung der Tinte besonders wichtig für die Funktionsweise des Konstruktes, da sie sowohl die physikalischen Voraussetzungen für den 3D Druck als auch die biologische Unterstützung für die Zellkultivierung mitbringen muss. Bisher wurden häufig Tintenzusammensetzungen mit hohen Polymergehalten und Vernetzungsdichten verwendet, um 3D-Druckbarkeit und Konstruktstabilität zu gewährleisten. Das verursachte jedoch häufig eine eingeschränkte Bioaktivität und die Beeinträchtigung von Zellprozessen wie Differenzierung und der Verteilung der neu gebildeten Extrazellulärmatrix (ECM), die insbesondere in der Knorpelregeneration von großer Bedeutung ist. Daher war das Ziel dieser Arbeit 3D-druckbare Tinten auf Hyaluronsäure (HA)-Basis mit reduziertem Polymergehalt zu entwickeln, die die chondrogene Differenzierung von mesenchymalen Stromazellen (MSCs) unterstützen und eine homogene Verteilung der neu produzierten ECM ermöglichen. Ausgehend von nicht-druckbaren Hydrogelen mit hohem Polymergehalt und eingeschränkter Bioaktivität wurde eine schrittweise Verbesserung hinsichtlich 3D-Druckbarkeit, MSC-Differenzierung und homogener ECM-Verteilung erreicht. Alle hier neu entwickelten Tinten leisten einen wertvollen Beitrag auf dem Gebiet der Knorpelregeneration mit Potenzial zur klinischen Anwendung. Die zugrunde liegenden Mechanismen und etablierten Designkriterien können weiterhin auch auf andere biofabrizierte Gewebe übertragen werden, was ihre Bedeutung auch für ein weiter gefasstes Forschungsfeld unterstreicht. KW - Hyaluronsäure KW - 3D-Druck KW - Mesenchymale Stromazelle KW - Gelenkknorpel KW - Extrazelluläre Matrix KW - Chondrogenic Differentiation KW - Biofabrication KW - Bioink KW - Cartilage Tissue Engineering KW - Bioprinting KW - Hyaluronic Acid KW - Mesenchymal Stromal Cell Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-260681 ER -