TY - JOUR A1 - Böhm, Christoph A1 - Stahlhut, Philipp A1 - Weichhold, Jan A1 - Hrynevich, Andrei A1 - Teßmar, Jörg A1 - Dalton, Paul D. T1 - The Multiweek Thermal Stability of Medical-Grade Poly(ε-caprolactone) During Melt Electrowriting JF - Small N2 - Melt electrowriting (MEW) is a high-resolution additive manufacturing technology that places unique constraints on the processing of thermally degradable polymers. With a single nozzle, MEW operates at low throughput and in this study, medical-grade poly(ε-caprolactone) (PCL) is heated for 25 d at three different temperatures (75, 85, and 95 °C), collecting daily samples. There is an initial increase in the fiber diameter and decrease in the jet speed over the first 5 d, then the MEW process remains stable for the 75 and 85 °C groups. When the collector speed is fixed to a value at least 10% above the jet speed, the diameter remains constant for 25 d at 75 °C and only increases with time for 85 and 95 °C. Fiber fusion at increased layer height is observed for 85 and 95 °C, while the surface morphology of single fibers remain similar for all temperatures. The properties of the prints are assessed with no observable changes in the degree of crystallinity or the Young's modulus, while the yield strength decreases in later phases only for 95 °C. After the initial 5-d period, the MEW processing of PCL at 75 °C is extraordinarily stable with overall fiber diameters averaging 13.5 ± 1.0 µm over the entire 25-d period. KW - polycaprolactone KW - 3D printing KW - additive manufacturing KW - electrohydrodynamic KW - melt electrospinning writing Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-257741 VL - 18 IS - 3 ER - TY - THES A1 - Bakirci, Ezgi T1 - Development of \(In\) \(vitro\) Models for Tissue Engineering Applications Using a High-Resolution 3D Printing Technology T1 - Entwicklung von \(In\) \(vitro\)-Modellen für Tissue-Engineering-Anwendungen mithilfe einer hochauflösenden 3D-Drucktechnologie N2 - In vitro models mimic the tissue-specific anatomy and play essential roles in personalized medicine and disease treatments. As a sophisticated manufacturing technology, 3D printing overcomes the limitations of traditional technologies and provides an excellent potential for developing in vitro models to mimic native tissue. This thesis aims to investigate the potential of a high-resolution 3D printing technology, melt electrowriting (MEW), for fabricating in vitro models. MEW has a distinct capacity for depositing micron size fibers with a defined design. In this thesis, three approaches were used, including 1) extending the MEW polymer library for different biomedical applications, 2) developing in vitro models for evaluation of cell growth and migration toward the different matrices, and 3) studying the effect of scaffold designs and biochemical cues of microenvironments on cells. First, we introduce the MEW processability of (AB)n and (ABAC)n segmented copolymers, which have thermally reversible network formulation based on physical crosslinks. Bisurea segments are combined with hydrophobic poly(dimethylsiloxane) (PDMS) or hydrophilic poly(propylene oxide)-poly(ethylene oxide)-poly(propylene oxide) (PPO-PEG-PPO) segments to form the (AB)n segmented copolymers. (ABAC)n segmented copolymers contain all three segments: in addition to bisurea, both hydrophobic and hydrophilic segments are available in the same polymer chain, resulting in tunable mechanical and biological behaviors. MEW copolymers either support cells attachment or dissolve without cytotoxic side effects when in contact with the polymers at lower concentrations, indicating that this copolymer class has potential in biological applications. The unique biological and surface properties, transparency, adjustable hydrophilicity of these copolymers could be beneficial in several in vitro models. The second manuscript addresses the design and development of a melt electrowritten competitive 3D radial migration device. The approach differs from most of the previous literature, as MEW is not used here to produce cell invasive scaffolds but to fabricate an in vitro device. The device is utilized to systematically determine the matrix which promotes cell migration and growth of glioblastoma cells. The glioblastoma cell migration is tested on four different Matrigel concentrations using a melt electrowritten radial device. The glioblastoma U87 cell growth and migration increase at Matrigel concentrations 6 and 8 mg mL-1 In the development of this radial device, the accuracy, and precision of melt electrowritten circular shapes were investigated. The results show that the printing speed and design diameter are essential parameters for the accuracy of printed constructs. It is the first instance where MEW is used for the production of in vitro devices. The influence of biochemical cues and scaffold designs on astrocytes and glioblastoma is investigated in the last manuscript. A fiber comprising the box and triangle-shaped pores within MEW scaffolds are modified with biochemical cues, including RGD and IKVAV peptides using a reactive NCO-sP(EO-stat-PO) macromer. The results show that astrocytes and glioblastoma cells exhibit different phenotypes on scaffold designs and peptide-coated scaffolds. N2 - In-vitro-Modelle sind Werkzeuge, die die gewebespezifische Anatomie nachbilden und eine wesentliche Rolle in der personalisierten Medizin und bei der Behandlung von Krankheiten spielen. Als hochentwickelte, multifunktionale Fertigungstechnologie überwindet der 3D-Druck die Grenzen herkömmlicher Technologien und bietet ein hervorragendes Potenzial für die Herstellung von In-vitro-Modellen. Der 3D-Druck ist eine der vielversprechendsten Techniken, um biologische Materialien in einer komplexen Anordnung zusammenzusetzen, die das natürliche Gewebe nachahmt. In dieser Arbeit soll das Potenzial der hochauflösenden 3D-Drucktechnologie melt electrowriting (MEW), für die Herstellung von In-vitro-Modellen untersucht werden. Wir konzentrieren uns auf drei Ansätze: 1) die Erweiterung der MEW-Polymerbibliothek für verschiedene biomedizinische Anwendungen, 2) die Entwicklung von In-vitro-Modellen zur Bewertung des Zellwachstums und der Zellmigration in Richtung der verschiedenen Matrizes und 3) die Untersuchung der Auswirkungen von MEW-Gerüstdesigns und biochemischen Faktoren der Mikroumgebung auf Zellen. Zunächst haben wir die MEW-Verarbeitbarkeit von segmentierten (AB)n- und (ABAC)n-Copolymeren vorgestellt, die eine thermisch reversible Netzwerkformulierung auf der Grundlage physikalischer Vernetzungen aufweisen. Bisurea-Segmente werden mit hydrophoben hydrophobic poly(dimethyl siloxane) (PDMS) oder hydrophilen poly(propylene oxide)-poly(ethylene oxide)-poly(propylene oxide) (PPO-PEG-PPO) Segmenten kombiniert, um die (AB)n segmentierten Copolymere zu bilden. Segmentierte (ABAC)n-Copolymere enthalten alle drei Segmente: Zusätzlich zu den Bisurea-Segmenten sind sowohl hydrophobe als auch hydrophile Segmente in derselben Polymerkette vorhanden, was den segmentierten (ABAC)n-Copolymeren abstimmbare mechanische und biologische Eigenschaften verleiht. MEW-Copolymere unterstützten entweder die Anhaftung an Zellen oder lösten sich ohne zytotoxische Nebenwirkungen auf, wenn sie in niedrigeren Konzentrationen mit ihnen in Berührung kamen, was darauf hindeutet, dass diese Copolymerklasse über umfassende biologische Eigenschaften verfügt. Die einzigartigen biologischen Eigenschaften und Oberflächeneigenschaften, die Transparenz und die einstellbare Hydrophilie dieser Copolymere könnten in verschiedenen In-vitro-Modellen von Vorteil sein. Das zweite Manuskript befasst sich mit einem durch MEW hergestellten wettbewerbsfähigen 3D-Radialmigrationsdesign. Der Ansatz unterscheidet sich vom Großteil der MEW-Literatur, da MEW nicht zur Herstellung von invasiven Zellgerüsten verwendet wurde, sondern zur Herstellung eines In-vitro-Designs diente. Das Design wurde verwendet, um systematisch die Matrix zu bestimmen, die die Zellmigration und das Wachstum von Glioblastomzellen fördert. Die Migration der Glioblastomzellen wurde auf vier verschiedenen Matrigel-Konzentrationen unter Verwendung einer durch MEW hergestellten Radialvorrichtung getestet. Das Wachstum und die Migration der Glioblastomzellen U87 nahmen bei Matrigelkonzentrationen von 6 und 8 mg mL-1 zu. Wir untersuchten auch die Genauigkeit und Präzision der durch MEW erzeugten Kreisformen. Die Ergebnisse zeigten, dass die Druckgeschwindigkeit und der Designdurchmesser wesentliche Parameter für die Genauigkeit der gedruckten Konstrukte sind. Die Arbeit ist die erste Studie, die MEW für die Herstellung von In-vitro-Modellen verwendet. Im letzten Manuskript wurde der Einfluss von biochemische Funktionalisierung in Kombination mit Gerüstdesigns auf Astrozyten und Glioblastome untersucht. Die kastenförmigen und achteckigen MEW-Gerüste wurden mit biochemischen Wirkstoffen modifiziert, darunter RGD- und IKVAV-Peptide unter Verwendung von reaktivem NCO-sP(EO-stat-PO). Wir fanden heraus, dass Astrozyten und Glioblastomzellen unterschiedliche Phänotypen auf den verschiedenen Designs und mit Peptiden beschichteten Gerüsten aufweisen. KW - Melt electrowriting KW - 3D-Druck KW - 3D printing KW - In vitro model Y1 - 2024 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-251645 ER -