TY - THES A1 - Schmid, Benjamin T1 - Surface preparation and Mn states of (Ga,Mn)As investigated by means of soft- and hard x-ray photoemission spectroscopy T1 - Oberflächenpräparation und Untersuchung der Mn Zustände in (Ga,Mn)As mit Hilfe von Photoemissionsspektroskopie im weichen und harten Röntgenbereich N2 - The present thesis deals with surface treatment, material improvement, and the electronic structure of the diluted magnetic semiconductor (Ga,Mn)As. The two key issues are the preparation of clean surfaces and the observation of potential valence hybridizations in (Ga,Mn)As by means of photoemission spectroscopy. Several cleaning methods are applied individually to (Ga,Mn)As and their e ects are compared in detail by various methods. Based on the results of each method, a sophisticated recipe has been elaborated, which provides clean, stoichiometric, and reconstructed surfaces, even if the sample was exposed to air prior to preparation. Moreover, the recipe works equally well for intentionally oxidized surfaces. The individual advantages of ex-situ wet- chemical etching and in situ ion-milling and tempering can be combined in an unique way. In regard to the post-growth annealing in order to optimize the electronic and magnetic properties of (Ga,Mn)As, the effect of surface segregation of interstitial Mn was quantifed. It turns out that the Mn concentration at the surface increases by a factor 4.3 after annealing at 190 C for 150 h. The removal of the segregated and oxidized species by wet-chemical etching allows a tentative estimate of the content of interstitial Mn. 19-23% of the overall Mn content in as-grown samples resides on interstitial positions. The complementary results of core level photoemission spectroscopy and resonant photoemission spectroscopy give hints to the fact that a sizeable valence hybridization of Mn is present in (Ga,Mn)As. This outlines that the simple Mn 3d5-con guration is too naive to refect the true electronic structure of substitutional Mn in (Ga,Mn)As. Great similarities in the core level spectra are found to MnAs. The bonding is thus dominantly of covalent, not ionic, character. Transport measurements, in particular for very low temperatures (<10 K), are in agreement with previous results. This shows that at low temperature, the conduction is mainly governed by variable-range hopping which is in line with the presence of an impurity band formed by substitutional Mn. In the light of the presented results, it is therefore concluded that a double-exchange interaction is the dominant mechanism leading to ferromagnetic coupling in (Ga,Mn)As. The valence hybridization and the presents of an impurity band, both of which are inherent properties of substitutional Mn, are indications for a double-exchange scenario, being at variance to a RKKY-based explanation. Contributions from a RKKY-like mechanism cannot definitely be excluded, however, they are not dominant. N2 - Die vorliegende Arbeit befasst sich mit der Oberflächenbehandlung, der Materialoptimierung und der elektronischen Struktur des verdünnten magnetischen Halbleiters (Ga,Mn)As. Die beiden Hauptaspekte sind dabei die Präparation sauberer Oberflächen und die Identifikation einer möglichen Valenzhybridisierung in (Ga,Mn)As mithilfe von Photoemissionspektroskopie. Mehrere Reinigungsmethoden wurden einzeln auf (Ga,Mn)As Oberflächen angewandt und deren Wirkung anhand mehrerer Untersuchungsmethoden verglichen. Basierend auf den Einzelergebnissen wurde eine spezielle Reinigungsprozedur ausgearbeitet, welche stöchiometrische, reine und wohldefinierte Oberflächen liefert, selbst wenn die Proben Umgebungsluft ausgesetzt wurde. Die beschriebene Vorgehensweise funktioniert des Weiteren auch bei absichtlich oxidierten Proben. Hierbei werden die individuellen Vorteile von ex situ nass-chemischen Ätzen, in situ Ionenstrahlätzen und Erhitzen auf besondere Art und Weise kombiniert. Im Hinblick auf das Ausheilen nach dem Wachstum konnte die Oberflächensegregation von interstitiellem Mangan quantifiziert werden, wobei sich zeigte, dass die Mangankonzentration an der Oberfläche um einen Faktor 4.3 nach 150 Stunden Ausheilen an Luft zunahm. Ein Vergleich zwischen ausgeheilten und anschließend geätzen Proben lässt eine vorsichtige Abschätzung des Anteils an interstitiellem Mangan in nicht ausheilten Proben zu. Hierbei zeigt sich, dass sich 19-23% das Gesamtgehalts an Mangan auf interstitiellen Gitterplätzen befindet. Komplementäre Untersuchungen mit Photoemissionsmethoden an Rumpfniveaus und mithilfe resonanter Photoemission geben Hinweis darauf, dass für Mangan in (Ga,Mn)As eine Valenzhybridisierung vorliegt. Dies führt zu dem Schluss, dass die simple Annahme eines zweifach positiv geladenen Mn-Atoms in 3d5-Kon guration zu pauschal ist, um die tatsächliche elektronische Struktur von substitutionellem Mn in (Ga,Mn)As widerzuspiegeln. Die Spektren zeigen eine große Ähnlichkeit zu Manganarsenid, was beweißt, dass die Bindung vorherrschend kovalenter und nicht ionischer Natur ist. Darüber hinaus sind ebenfalls durchgeführte Transportmessungen im Einklang mit bereits veröffentlichten Ergebnissen aus der Literatur. Dabei zeigt sich, dass der Ladungstransport, vor allem bei tiefen Temperaturen unterhalb von 10 K, durch variable range hopping statt findet. Dieses Verhalten steht im Einklang mit dem Vorhandensein eines Störstellenbandes, welches von substitutionellem Mn gebildet wird. Angesichts der hier gezeigten Daten kann gefolgert werden, dass ein Doppelaustausch der ausschlaggebende Mechanismus für das Auftreten ferromagnetischer Kopplung in (Ga,Mn)As ist. Sowohl die Valenzhybridisierung substitutionellem Mn als auch die Ausbildung eines Störstellenbandes durch selbiges, deuten auf einen Doppelaustausch in, was im Gegensatz zu einer RKKY-basierten Erklärung steht. Hierbei kann ein gewisse Bedeutung des RKKY-Modells nicht vollständig ausgeschlossen werden, jedoch ist diese definitiv nicht dominant. KW - Photoelektronenspektroskopie KW - Galliumarsenid KW - Manganarsenide KW - Magnetischer Halbleiter KW - Ferromagnetische Halbleiter KW - (Ga KW - Mn)As KW - Oberflächenpräparation KW - Photoemission spectroscopy KW - ferromagnetic semiconductors KW - (Ga KW - Mn)As KW - surface preparation Y1 - 2010 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-50057 ER - TY - THES A1 - Rüster, Christian T1 - Magnetotransport effects in lateral and vertical ferromagnetic semiconductor junctions T1 - Magnetotransport Effekte in lateralen und vertikalen ferromagnetischen Halbleiterdioden N2 - This work is an investigation of giant magnetoresistance (GMR), tunneling magnetoresistance (TMR) and tunneling anisotropic magnetoresistance (TAMR)effects in (Ga,Mn) based ferromagnetic semiconductor junctions. Detailed results are published in the following articles: [1] C. Rüster, T. Borzenko, C. Gould, G. Schmidt, L.W. Molenkamp, X. Liu, T.J.Wojtowicz, J.K. Furdyna, Z.G. Yu and M. Flatt´e, Very Large Magnetoresistance in Lateral Ferromagnetic (Ga,Mn)As Wires with Nanoconstrictions, Physical Review Letters 91, 216602 (2003). [2] C. Gould, C. Rüster, T. Jungwirth, E. Girgis, G.M. Schott, R. Giraud, K. Brunner, G. Schmidt and L.W. Molenkamp, Tunneling Anisotropic Magnetoresistance: A Spin-Valve-Like Tunnel Magnetoresistance Using a Single Magnetic Layer, Physical Review Letters 93, 117203 (2004). [3] C. Rüster, C. Gould, T. Jungwirth, J. Sinova, G.M. Schott, R. Giraud, K. Brunner, G. Schmidt and L.W. Molenkamp, Very Large Tunneling Anisotropic Magnetoresistance of a (Ga,Mn)As/GaAs/(Ga,Mn)As Stack, Physical Review Letters 94, 027203 (2005). [4] C. Rüster and C. Gould, T. Jungwirth, E. Girgis, G.M. Schott, R. Giraud, K. Brunner, G. Schmidt and L.W. Molenkamp, Tunneling anisotropic magnetoresistance: Creating a spin-valve-like signal using a single ferromagnetic semiconductor layer, Journal of Applied Physics 97, 10C506 (2005). N2 - Diese Arbeit enthält Untersuchungen von Magnetowiderstandseffekten in (Ga,Mn)As basierten ferromagnetischen Halbleiterdioden. Die Resultate wurden in den folgenden Artikeln veröffentlicht: [1] C. Rüster, T. Borzenko, C. Gould, G. Schmidt, L.W. Molenkamp, X. Liu, T.J.Wojtowicz, J.K. Furdyna, Z.G. Yu and M. Flatt´e, Very Large Magnetoresistance in Lateral Ferromagnetic (Ga,Mn)As Wires with Nanoconstrictions, Physical Review Letters 91, 216602 (2003). [2] C. Gould, C. Rüster, T. Jungwirth, E. Girgis, G.M. Schott, R. Giraud, K. Brunner, G. Schmidt and L.W. Molenkamp, Tunneling Anisotropic Magnetoresistance: A Spin-Valve-Like Tunnel Magnetoresistance Using a Single Magnetic Layer, Physical Review Letters 93, 117203 (2004). [3] C. Rüster, C. Gould, T. Jungwirth, J. Sinova, G.M. Schott, R. Giraud, K. Brunner, G. Schmidt and L.W. Molenkamp, Very Large Tunneling Anisotropic Magnetoresistance of a (Ga,Mn)As/GaAs/(Ga,Mn)As Stack, Physical Review Letters 94, 027203 (2005). [4] C. Rüster and C. Gould, T. Jungwirth, E. Girgis, G.M. Schott, R. Giraud, K. Brunner, G. Schmidt and L.W. Molenkamp, Tunneling anisotropic magnetoresistance: Creating a spin-valve-like signal using a single ferromagnetic semiconductor layer, Journal of Applied Physics 97, 10C506 (2005). KW - Galliumarsenid KW - Manganarsenide KW - Halbleiterdiode KW - Ferromagnetische Schicht KW - Magnetowiderstand KW - Spintronics KW - Ferromagnetische Halbleiter KW - Magnetotransport KW - Tunneldioden KW - Spintronics KW - ferromagnetic semiconductors KW - magnetotransport KW - tunneling diodes Y1 - 2005 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-15554 ER - TY - THES A1 - Ebel, Lars Frederik T1 - Molecular Beam Epitaxy and Characterization of Ferromagnetic Bulk and Thin (Ga,Mn)As Layers/Heterostructures T1 - Molekularstrahlepitaxie und Charakterisierung von dicken und dünnen ferromagnetischen (Ga,Mn)As Schichten/Heterostrukturen N2 - Die vorgelegte Arbeit untersucht den ferromagnetischen Halbleiter (Ga,Mn)As mit seinen komplexen Eigenschaften im Hinblick auf die Optimierung der Materialeigenschaften sehr dünner (4 nm) (Ga,Mn)As Schichten, welche mit der Technologie der Molekularstrahlepitaxie (MBE) hergestellt wurden. Zuerst werden die strukturellen, ferromagnetischen und elektrischen Eigenschaften von (Ga,Mn)As vorgestellt. Die Einflüsse von Punktdefekten, Grenzflächen- und Oberflächen-Effekten auf dicke und dünne (Ga,Mn)As Schichten werden mit Hilfe von vereinfachten, selbstkonsistenten Berechnungen der Bandkantenverläufe diskutiert. Der Experimental-Teil ist in drei Teile unterteilt: Der erste Teil untersucht den Einfluss der epitaktischen Wachstumsbedingungen auf die elektrischen und magnetischen Eigenschaften von dicken (70 nm) (Ga,Mn)As Schichten. Der zweite Teil führt ein alternatives, parabolisches Mn-Dotierprofil mit effektiver Schichtdicke von 4 nm ein im Vergleich zu einer gleich dünnen Schicht mit homogenem Mn-Dotierprofil. Es konnten einerseits verbesserte Eigenschaften dieser parabolischen Schicht erreicht werden, anderseits sind die magnetischen und elektrischen Eigenschaften vergleichbar zu dicken (Ga,Mn)As Schichten mit gleichem Mn-Gehalt von 4%. MBE Wachstumsbedingungen für (Ga,Mn)As Schichten mit parabolischem Mn-Dotierprofil und verringertem nominellem Mn-Gehalt von 2.5% wurden ebenfalls untersucht. Ein schmales Wachstumsfenster wurde hierbei ermittelt, in dem die Tieftemperatur-Eigenschaften verbessert sind. Der letzte Teil der Arbeit präsentiert eine Anwendung der magnetischen Anisotropiekontrolle einer dicken (Ga,Mn)As Schicht. N2 - The present thesis studies the (Ga,Mn)As material in terms of optimization of very thin (4 nm) (Ga,Mn)As layers, epitaxially fabricated by the molecular beam epitaxy (MBE) technology. First of all, the ferromagnetic semiconductor (Ga,Mn)As with its structural, magnetic and electrical properties is introduced. The influences of point defects, interface and surface effects on bulk and thin (Ga,Mn)As layers are discussed by simplified self-consistent band alignment calculations. The experimental part is divided in three blocks: The first part studies the influence of epitaxial growth parameter conditions on electrical and magnetic properties of bulk (70 nm) (Ga,Mn)As layers. The second part introduces an alternative, parabolical Mn doping-profile instead of a 4 nm layer with a homogeneous Mn doping-profile. Improved properties of the parabolic layer have been observed as well as comparable magnetic and electrical properties to bulk (Ga,Mn)As layers, both with a Mn content of 4%. MBE growth parameters for the (Ga,Mn)As layers with a parabolically graded Mn profile and lowered nominal Mn content of 2.5% have been investigated. A narrow growth window has been found in which low-temperature (LT) layer properties are improved. The last part of this thesis presents an application of magnetic anisotropy control of a bulk (Ga,Mn)As layer. KW - Molekularstrahlepitaxie KW - ferromagnetische Halbleiter KW - magnetische Anisotropie KW - GaMnAs KW - Molecular Beam Epitaxy KW - Ferromagnetic Semiconductors KW - Magnetic Anisotropy KW - GaMnAs KW - Galliumarsenid KW - Manganarsenide KW - Magnetischer Halbleiter Y1 - 2013 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-83942 ER - TY - THES A1 - Constantino, Jennifer Anne T1 - Characterization of Novel Magnetic Materials: Ultra-Thin (Ga,Mn)As and Epitaxial-Growth MnSi Thin Films T1 - Charakterisierung von neuen magnetischen Materialien: ultradünne (Ga,Mn)As und epitaktisch gewachsene MnSi Dünnschichten N2 - The study of magnetic phases in spintronic materials is crucial to both our fundamental understanding of magnetic interactions and for finding new effects for future applications. In this thesis, we study the basic electrical and magnetic transport properties of both epitaxially-grown MnSi thin films, a helimagnetic metal only starting to be developed within our group, and parabolic-doped ultra-thin (Ga,Mn)As layers for future studies and applications. N2 - Um einerseits ein fundamentales Verständnis magnetischer Wechselwirkungen zu erhalten und andererseits neue Effekte für zukünftige Anwendungen zu finden, ist es entscheidend, magnetische Phasen spintronischer Materialien zu untersuchen. In dieser Arbeit fokussieren wir uns auf grundlegende elektrische und magnetische Transporteigenschaften zweier Materialsysteme. Das sind zum Ersten ultradünne (Ga,Mn)As Filme mit parabolischen Dotierprofilen, und zum Zweiten epitaktisch gewachsene Dünnschichten aus MnSi, einem helimagnetischen Metal, dessen Entwicklung seit Kurzem in unserer Gruppe vorangetrieben wird. KW - Galliumarsenid KW - Manganarsenide KW - Dünne Schicht KW - Magnetischer Halbleiter KW - Helimagnetism KW - Manganese Silicide KW - Gallium Manganese Arsenide KW - Ferromagnetic Semiconductors KW - Magnetic Anisotropy KW - Mangansilicide KW - Magnetotransport KW - Mangan KW - Halbleiter KW - Herstellung Y1 - 2013 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-90578 ER -