TY - JOUR A1 - Verma, Shwetabh A1 - Kehrer, Tobias A1 - Hesser, Jürgen A1 - Arba Mosquera, Samuel T1 - Analysis of Impact of Humidity and Temperature on Excimer Laser Ablation of Polyethylene Terephthalate, Polymethylmethacrylate, and Porcine Corneal Tissue JF - Lasers in Surgery and Medicine N2 - Background and Objectives To analyze the impact of humidity and temperature on excimer laser ablation of polyethylene terephthalate (PET), polymethylmethacrylate (PMMA) and porcine corneal tissue, and an ablation model to compensate for the temperature and humidity changes on ablation efficiency. Study Design/Materials and Methods The study was conducted using an AMARIS 1050RS (Schwind eye‐tech‐solutions) placed inside a climate chamber at ACTS. Ablations were performed on PET, PMMA, and porcine cornea. The impact of a wide range of temperature (~18°C to ~30°C) and relative humidity (~25% to ~80%) on laser ablation outcomes was tested using nine climate test settings. For porcine eyes, change in defocus was calculated from the difference of post‐ablation to pre‐ablation average keratometry readings. Laser scanning deflectometry was performed to measure refractive change achieved in PMMA. Multiple linear regression was performed using the least square method with predictive factors: temperature, relative humidity, time stamp. Influence of climate settings was modeled for pulse energy, pulse fluence, ablation efficiency on PMMA and porcine cornea tissue. Results Temperature changes did not affect laser pulse energy, pulse fluence (PET), and ablation efficiency (on PMMA or porcine corneal tissue) significantly. Changes in relative humidity were critical and significantly affected laser pulse energy, high fluence and low fluence. The opposite trend was observed between the ablation performance on PMMA and porcine cornea. Conclusions The proposed well‐fitting multi‐linear model can be utilized for compensation of temperature and humidity changes on ablation efficiency. Based on this model, a working window for optimum operation has been found (temperature 18°C to 28°C and relative humidity 25% to 65%) for a maximum deviation of ±2.5% in ablation efficiency in PMMA and porcine corneal tissue. KW - impact of humidity and temperature KW - excimer laser ablation KW - PMMA KW - cornea KW - PET KW - refractive surgery Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-213395 VL - 52 IS - 7 SP - 627 EP - 638 ER - TY - THES A1 - Weckwerth, Felix T1 - Antibiotikafreisetzung und Klebefestigkeit modifizierter PMMA Knochenzemente T1 - Antibiotic release and bonding strength of modified PMMA bone cements N2 - Im Rahmen dieser Arbeit wurden zwei modifizierte Knochenzemente auf ihre Klebefestigkeit und Antibiotikafreisetzung untersucht und mit dem herkömmlichen Biomet Bone Cement verglichen. Beiden Modifikationen wurde Hydroxyethylmethacrylat-Phosphat (HEMA-P) untergemischt. Die eine Modifikation war zusätzlich mit Natriumcarbonat und Calciumchlorid beladen. Der mit HEMA-P, Natriumcarbonat und Calciumchlorid modifizierte Knochenzement erreichte initial lediglich 85 Prozent der Zug- und 81 Prozent der Zugscherkräfte des Biomet Bone Cements. Nach einem künstlichem Alterungsprozess lagen die Zug- und Zugscherkräfte auch deutlich unter denen des Vergleichszementes. Allerdings konnte bei diesem Zement eine große Abgabemenge von Antibiotikum festgestellt werden. Diese lag nach Ablauf von 3 Wochen bei Gentamicin etwa zweifach und bei Vancomycin um den Faktor 25 über der Menge, die der Biomet Bone Cement freisetzte. Die Klebefestigkeit und Antibiotikaabgabewerte des mit HEMA-P modifizierten Zementes ähnelten den Werten des Biomet Bone Cementes N2 - The aim of the study was to examine two modified bone cements on its tensile strength and antibiotic release. Both cements were modified with Hydroxyethylmethacrylat phosphate (HEMA-P), the one modification was additionally loaded with Natriumcarbonat and calcium chloride. With HEMA-P, Natriumcarbonat and calcium chloride modified bone cement reached initially only 85 per cent of the tensile strength of the conventional Biomet Bone Cements. After an artificial aging process the tensile strength was also clearly under those of the comparison cement. However a large delivery quantity of antibiotic could be determined with this cement. This lay at expiration of 3 weeks with Gentamicin about doubly and with Vancomycin around the factor 25 over the quantity, which the Biomet Bone Cement set free. The tensile strength and antibiotic release of the cement modified with HEMA-P resembled the values of the Biomet Bone Cementes. KW - Knochenzement KW - PMMA KW - Antibiotikafreisetzung KW - antibiotic release KW - bone cement KW - tensile strength Y1 - 2009 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-38943 ER - TY - THES A1 - Driemel, Oliver T1 - Histopathologische Untersuchungen auf organische Veränderungen nach intraossärer Implantation von Poly(L-Lactid), Polymethyl-Methacrylat und kommerziell reinem Titan bei der Ratte N2 - Die Induktion von Autoimmunerkrankungen als systemische Wirkung wurde in den 1990iger Jahren nach vorangegangenem jahrzehntelangem Gebrauch den Silikonen ohne wissenschaftlichen Nachweis unterstellt. Dies zeigt, wie wichtig es ist, dass relativ neue (bioresorbierbare) Materialien auch systemisch gut charakterisiert werden. Zylinder (2,8 x 1,1 mm) und zerkleinerte Materialproben mit gleicher Masse (in Gelatinekapseln abgefüllt) aus a.) kommerziell reinem (cp) Titan, b.) Polymethyl-Methacrylat (PMMA) und c.) niedrig molekularem, amorphem Poly(L-Lactid) (Molekulargewicht Mvis: 120 000) wurden in das linke Femur von jeweils 25 spezifiziert pathogenfreien (SPF) Sprague Dawley-Ratten implantiert. Zwei weitere Gruppen von je 25 Tieren dienten als schein- operierte und unoperierte Kontrollgruppen. Geplant war eine Implantationszeit von bis zu 24 Monaten. Durch Übertragung von Keimen aus der Cara-Ratten-Zucht der Abteilung für Experimentelle Zahnmedizin der Zahn-, Mund- und Kieferklinik der Universität Würzburg entwickelte sich eine epidemische Pneumonie mit Mycoplasma pulmonis, superinfiziert mit Pasteurella pneumotropica. Deshalb musste aus tierschutzrechtlichen ethischen Gründen der Implantationsversuch nach neun Monaten terminiert werden. Alle Tiere wurden makroskopisch obduziert sowie Organpakete mit Lungen, Herz, Trachea und Bronchien, Thymus und Halslymphknoten, Mamma, Leber, Milz, Pankreas, Nieren und Gonaden entnommen und zur mikroskopischen Untersuchung in 5 %iger Formaldehyd-Lösung fixiert. Die histopathologische Auswertung konnte in keiner Gruppe Hinweise auf systemische Wirkungen der verwendeten Implantate identfizieren. Neue Biomaterialien sollten immer in geeigneten (eventuell langlebigeren) Versuchstiermodellen auch auf systemische Fernwirkungen hin untersucht werden. KW - PLLA KW - Poly(L-Lactid) KW - PMMA KW - Titan KW - PLLA KW - poly(l-lactide) KW - PMMA KW - Titanium Y1 - 2002 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-5147 ER -