3D-Pulverdruck von Calciumphosphat-Keramiken mit polymeren und anorganischen Bindersystemen

Polymer and inorganic 3D-rapid prototyping systems to build calciumphospate-ceramics

Please always quote using this URN: urn:nbn:de:bvb:20-opus-36373
  • Die vorliegende Arbeit hatte die Herstellung phasenreiner ß-Tricalciumphosphat (ß-TCP) - Implantate durch 3D-Pulverdruck zum Ziel. Variiert wurden hierbei die zum Druck verwendeten Pulver-Binder-Systeme. Als Verfestigungsmechanismen wurden hydraulisch abbindende Pulver-Binder-Systeme aus Tricalciumphosphat / Phosphorsäure bzw. Tetracalciumphosphat / Citronensäure untersucht, sowie der Zusatz quellfähiger Polymere zum Pulver, etwa Polyacrylsäure oder Hydroxypropylmethyl-Cellulose. Die gedruckten Strukturen wurden anschließend in Hinblick auf dieDie vorliegende Arbeit hatte die Herstellung phasenreiner ß-Tricalciumphosphat (ß-TCP) - Implantate durch 3D-Pulverdruck zum Ziel. Variiert wurden hierbei die zum Druck verwendeten Pulver-Binder-Systeme. Als Verfestigungsmechanismen wurden hydraulisch abbindende Pulver-Binder-Systeme aus Tricalciumphosphat / Phosphorsäure bzw. Tetracalciumphosphat / Citronensäure untersucht, sowie der Zusatz quellfähiger Polymere zum Pulver, etwa Polyacrylsäure oder Hydroxypropylmethyl-Cellulose. Die gedruckten Strukturen wurden anschließend in Hinblick auf die zu erreichende Auflösung, die mechanischen Eigenschaften und die Zusammensetzung des Endproduktes verglichen.show moreshow less
  • Custom made ß-tricalcium phosphate (ß-TCP) bone substitutes with a macroporous architecture were fabricated in this study using 3D powder printing with three different preparation strategies and analysed with regard to their mechanical and physical properties. Samples were either obtained by (A) using hydroxypropylmethylcellulose (5wt%) modified TCP (Ca/P=1.5) powder with water as a binder, (B) by using phosphoric acid (10%) as a binder with a calcium phosphate powder of a Ca/P ratio of 1.7 and different binder/volume ratios or (C) by printingCustom made ß-tricalcium phosphate (ß-TCP) bone substitutes with a macroporous architecture were fabricated in this study using 3D powder printing with three different preparation strategies and analysed with regard to their mechanical and physical properties. Samples were either obtained by (A) using hydroxypropylmethylcellulose (5wt%) modified TCP (Ca/P=1.5) powder with water as a binder, (B) by using phosphoric acid (10%) as a binder with a calcium phosphate powder of a Ca/P ratio of 1.7 and different binder/volume ratios or (C) by printing a tetracalcium phosphate (Ca/P=2.0) / dicalcium phosphate (Ca/P=1.0) / tricalcium phosphate powder mixture with citric acid (25wt%). The production process was followed by a heat treatment at 1100°C for all variations to produce phase pure ß-TCP (Ca/P=1.5). The results showed that ß-TCP samples fabricated according to method (B) showed the best printing resolution with a minimum macropore diameter of approximately 500µm and a compressive strength of up to 7.4 ± 0.7 MPa. Since the samples could be removed from the powder bed immediately after printing, this method would significantly decrease processing time for commercial fabrication.show moreshow less

Download full text files

Export metadata

Additional Services

Share in Twitter Search Google Scholar Statistics
Metadaten
Author: Michael Klarner
URN:urn:nbn:de:bvb:20-opus-36373
Document Type:Doctoral Thesis
Granting Institution:Universität Würzburg, Medizinische Fakultät
Faculties:Medizinische Fakultät / Klinik und Polikliniken für Zahn-, Mund- und Kieferkrankheiten
Date of final exam:2009/06/22
Language:German
Year of Completion:2009
Dewey Decimal Classification:6 Technik, Medizin, angewandte Wissenschaften / 61 Medizin und Gesundheit / 610 Medizin und Gesundheit
GND Keyword:Rapid Prototyping; Biomaterial
Tag:3D-Pulverdruck; Biokompatibel; Calciumphosphat; Knochenersatzwerkstoff; Tricalciumphosphat
3D - rapid prototyping; beta TCP; bone substitute; ß-tricalcium phosphate
Release Date:2009/06/22
Advisor:PD Dr. Uwe Gbureck