TY - THES A1 - Böhm, Christoph T1 - Thermal Stability of the Polyesters PCL and PLGA during Melt Electrowriting T1 - Thermische Stabilität der Polyester PCL und PLGA während des Melt Electrowriting Prozesses N2 - The focus of this thesis was to investigate how PCL and PLGA react to the heat exposure that comes with the MEW process over a defined timespan. To assess the thermal stability of PCL during MEW over 25 d, an automated collection of fibers has been used to determine the CTS on each day of heating for three different temperatures. PCL is exceptionally stable over 25 d at 75 °C, whereas for 85 °C and 95 °C a slight upward trend during the last 10 d could be observed, which is an indication for thermal degradation. Same trend could be observed for diameter of fibers produced at a fixed collector speed. For all temperatures, CTS during the first 5 d decreased due to inhomogeneities of the melt. Physical analysis of the fibers by XRD and mechanical testing showed no significant changes. To investigate the chemical details of the thermal durability, PCL was artificially aged over 25 d at 75 °C, 85 °C and 95 °C. Data from GPC analysis and rheology revealed that PCL is degrading steadily at all three temperatures. Combined with GC-MS analysis, two different mechanisms for degradation could be observed: random chain scission and unzipping. Additional GPC experiment using a mixture of PCL and a fluorescence labelled PCL showed that PCL was undergoing ester interchange reactions, which could explain its thermal stability. PLGA was established successfully as material for MEW. GPC results revealed that PLGA degraded heavily in the one-hour preheating period. To reduce the processing temperature, ATEC was blended with PLGA in three mixtures. This slowed down degradation and a processing window of 6 h could be established. Mechanical testing with fibers produced with PLGA and all three blends was performed. PLGA was very brittle, whereas the blends showed an elastic behavior. This could be explained by ester interchange reactions that formed a loosely crosslinked network with ATEC. N2 - Ziel dieser Arbeit war, die Veränderung von PCL und PLGA während des MEW-Verfahrens bei bestimmten Temperaturen über einen definierten Zeitraum zu untersuchen. Für die Bewertung der thermischen Stabilität von PCL während des MEW-Prozesses über 25 d wurden Fasern in einem vorgegebenen Druckmuster gesammelt, um täglich die CTS für drei verschiedene Temperaturen zu bestimmen. Allgemein war PCL bei 75 °C über 25 d thermisch stabil. Allerdings nahm die CTS bei allen Temperaturen während der ersten 5 d aufgrund von Inhomogenitäten der Schmelze ab. Bei 85 °C und 95 °C wurde in den letzten 10 d ein leichter Anstieg der CTS beobachtet, was auf thermische Degradation hinweist. Dieser Anstieg war ebenfalls im Durchmesser der Fasern zu beobachten, die mit konstanter Kollektorgeschwindigkeit hergestellt wurden. Die physikalische Untersuchung der Fasern mittels XRD und mechanischer Tests ergab keine signifikanten Veränderungen. Um die Chemie der thermischen Beständigkeit zu untersuchen, wurde PCL über 25 d bei 75 °C, 85 °C und 95 °C künstlich gealtert. GPC- und rheologische Analysen zeigten, dass PCL bei allen Temperaturen stetig abbaut. Mit der GC-MS-Analyse konnten zwei Abbaumechanismen beobachtet werden: zufällige Kettenspaltung und Unzipping. GPC-Messungen mit einer Mischung aus PCL und einem fluoreszenzmarkierten PCL zeigten, dass es zu Esteraustauschreaktionen kommt, welche die thermische Stabilität erklären. PLGA wurde erfolgreich als Material für MEW etabliert. Die GPC-Daten zeigten, dass PLGA während der einstündigen Aufheizphase stark abgebaut wurde. Um die Verarbeitungstemperatur zu senken, wurden drei Mischungen mit verschiedenen Verhältnissen von PLGA und ATEC hergestellt. Dadurch verlangsamte sich der Abbau, wodurch ein Verarbeitungsfenster von 6 h erreicht wurde. Mechanische Tests zeigten für PLGA ein sprödes, für die Mischungen ein elastisches Verhalten. Dies kann durch Esteraustauschreaktionen mit ATEC erklärt werden, durch die ein Polymernetzwerk entstehen könnte. KW - Degradation KW - Polylactid-co-Glycolid KW - Polycaprolacton KW - Additive Fertigung KW - polycaprolactone KW - poly(lactic-co-glycolic acid) KW - additive manufacturing KW - degradation KW - Rapid Prototyping KW - PCL KW - PLGA Y1 - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-306139 ER - TY - THES A1 - Bozkaya, Begüm T1 - Influence of Carbon Additives on the Electrochemical Performance of Modern Lead-Acid Batteries T1 - Einfluss von Kohlenstoffadditiven auf die elektrochemische Leistung moderner Blei-Säure-Batterien N2 - In the first part of this thesis, a validation of both short-term and long-term DCA tests on 2 V laboratory cells is focussed. The aim is to improve the laboratory cell level measurement technology for dynamic charge acceptance regarding the investigation of carbon additives. To address this issue, it is crucial to apply carbon additives generating a remarkable difference in charge acceptance. For this purpose, five different carbon additives providing a variation in the specific external surface were included as additives in the negative plates of 2 V lead-acid cells. Both short-term (charge acceptance test 2 from SBA and DCA from EN) and long-term (Run-in DCA from Ford) DCA tests were executed on the lead-acid cells. Further understanding of the mechanism was studied by applying electrochemical methods like cyclic voltammetry and electrochemical impedance spectroscopy. The second part of this thesis aims to understand the impact of carbon surface functional groups on the electrochemical activity of the negative electrodes as well as the DCA of 2 V lead-acid cells. In order to address this topic, commercially available activated carbon was modified by different chemical treatments to incorporate specific surface functional groups in the carbon structure. A series of activated carbons having a broad range of pH was prepared, which were used as additives in the negative electrodes. The corresponding lead-acid cells were subjected to cyclic voltammetry and DCA test according to EN. Further, the physical and chemical properties of the functionalized carbon additives were intensively analyzed to establish a structure-property relationship with a focus on DCA. N2 - Im ersten Teil dieser Arbeit geht es um die Validierung von Kurzzeit- und Langzeit-DCA-Tests an 2-V-Laborzellen. Ziel ist es, die Messtechnik für die dynamische Ladungsakzeptanz auf Laborzellenniveau im Hinblick auf die Untersuchung von Kohlenstoffadditiven zu verbessern. Dazu ist es entscheidend, Kohlenstoffadditive einzusetzen, die einen deutlichen Unterschied in der Ladungsakzeptanz bewirken. Zu diesem Zweck wurden fünf verschiedene Kohlenstoffadditive, die eine Variation der spezifischen äußeren Oberfläche bewirken, als Additive in die negativen Platten von 2-V-Blei-Säure-Zellen eingebracht. An den Blei-Säure-Zellen wurden sowohl Kurzzeit- (Ladeakzeptanztest 2 von SBA und DCA von EN) als auch Langzeit-DCA-Tests (Run-in DCA von Ford) durchgeführt. Zum weiteren Verständnis des Mechanismus wurden elektrochemische Methoden wie zyklische Voltammetrie und elektrochemische Impedanzspektroskopie eingesetzt. Der zweite Teil dieser Arbeit zielt darauf ab, den Einfluss der funktionellen Kohlenstoffoberflächengruppen auf die elektrochemische Aktivität der negativen Elektroden sowie auf die DCA von 2-V-Bleisäurezellen zu verstehen. Zu diesem Zweck wurde handelsübliche Aktivkohle durch verschiedene chemische Behandlungen modifiziert, um spezifische funktionelle Oberflächengruppen in die Kohlenstoffstruktur einzubringen. Es wurde eine Reihe von Aktivkohlen mit einem breiten pH-Bereich hergestellt, die als Zusätze in den negativen Elektroden verwendet wurden. Die entsprechenden Blei-Säure-Zellen wurden der zyklischen Voltammetrie und dem DCA-Test gemäß EN unterzogen. Außerdem wurden die physikalischen und chemischen Eigenschaften der funktionalisierten Kohlenstoffadditive intensiv analysiert, um eine Struktur-Eigenschafts-Beziehung mit Schwerpunkt auf DCA herzustellen. KW - Bleiakkumulator KW - Blei KW - Batterie KW - Kohlenstoff KW - Elektrochemie KW - Lead-acid batteries KW - Carbon additives KW - Dynamic charge acceptance KW - Carbon surface chemistry Y1 - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-319174 ER - TY - THES A1 - Hanio, Simon T1 - The impact of bile on intestinal permeability of drug substances T1 - Der Einfluss der Galle auf die intestinale Permeabilität von Arzneimittelwirkstoffen N2 - Most medicines are taken orally. To enter the systemic circulation, they dissolve in the intestinal fluid, cross the epithelial barrier, and pass through the liver. Intestinal absorption is driven by the unique features of the gastrointestinal tract, including the bile colloids formed in the lumen and the mucus layer covering the intestinal epithelium. Neglecting this multifaceted environment can lead to poor drug development decisions, especially for poorly water-soluble drugs that interact with bile and mucus. However, there is a lack of a rationale nexus of molecular interactions between oral medicines and gastrointestinal components with drug bioavailability. Against this background, this thesis aims to develop biopharmaceutical strategies to optimize the presentation of oral therapeutics to the intestinal epithelial barrier. In Chapter 1, the dynamics of bile colloids upon solubilization of the poorly-water soluble drug Perphenazine was studied. Perphenazine impacted molecular arrangement, structure, binding thermodynamics, and induced a morphological transition from vesicles to worm-like micelles. Despite these dynamics, the bile colloids ensured stable relative amounts of free drug substance. The chapter was published in Langmuir. Chapter 2 examined the impact of pharmaceutical polymeric excipients on bile-mediated drug solubilization. Perphenazine and Imatinib were introduced as model compounds interacting with bile, whereas Metoprolol did not. Some polymers altered the arrangement and geometry of bile colloids, thereby affecting the molecularly soluble amount of those drugs interacting with bile. These insights into the bile-drug-excipient interplay provide a blueprint to optimizing formulations leveraging bile solubilization. The chapter was published in Journal of Controlled Release. Chapter 3 deals with the impact of bile on porcine intestinal mucus. Mucus exposed to bile solution changed transiently, it stiffened, and the overall diffusion rate increased. The bile-induced changes eased the transport of the bile-interacting drug substance Fluphenazine, whereas Metoprolol was unaffected. This dichotomous pattern was linked to bioavailability in rats and generalized based on two previously published data sets. The outcomes point to a bile-mucus interaction relevant to drug delivery. The chapter is submitted. The Appendix provides a guide for biopharmaceutical characterization of drug substances by nuclear magnetic resonance spectroscopy aiming at establishing a predictive algorithm. In summary, this thesis deciphers bile-driven mechanisms shaping intestinal drug absorption. Based on these molecular insights, pharmaceuticals can be developed along a biopharmaceutical optimization, ultimately leading to better oral drugs of tomorrow. N2 - Die meisten Arzneimittel werden oral eingenommen. Um in den Blutkreislauf zu gelangen, liegen sie in der Darmflüssigkeit gelöst vor, überwinden die Epithelbarriere und passieren die Leber. Die intestinale Absorption wird durch die einzigartigen Eigenschaften des Magen-Darm-Trakts, einschließlich der im Lumen gebildeten Gallenkolloide und der Schleimschicht, die das Darmepithel bedeckt, bestimmt. Die Vernachlässigung dieser facettenreichen Umgebung kann zu schlechten Entscheidungen bei der Arzneimittelentwicklung führen, insbesondere bei schlecht wasserlöslich Wirkstoffen, die mit Galle und Schleim interagieren. Es fehlt jedoch eine rationale Verknüpfung der molekularen Wechselwirkungen zwischen oralen Arzneimitteln und gastrointestinalen Komponenten mit der Bioverfügbarkeit von Arzneimitteln. Vor diesem Hintergrund zielt diese Arbeit darauf ab, biopharmazeutische Strategien zur Optimierung der Präsentation von oralen Therapeutika an der intestinalen Epithelbarriere zu entwickeln. In Kapitel 1 wurde die Dynamik von Gallenkolloiden bei der Solubilisierung des schwer wasserlöslichen Wirkstoffes Perphenazin untersucht. Perphenazin beeinflusste die molekulare Anordnung, die Struktur sowie die Bindungsthermodynamik und führte zu einem morphologischen Übergang von Vesikeln hin zu wurmartigen Mizellen. Trotz dieser Dynamik sorgten die Gallenkolloide für stabile relative Mengen an freiem Arzneistoff. Dieses Kapitel wurde in Langmuir veröffentlicht. In Kapitel 2 wurde der Einfluss von pharmazeutischen polymeren Hilfsstoffen auf die Solubilisierung von Wirkstoffen durch Galle untersucht. Perphenazin und Imatinib wurden als Modellverbindungen eingeführt, die mit der Galle interagieren, während Metoprolol dies nicht tat. Einige Polymere veränderten die Anordnung und Geometrie der Gallenkolloide und beeinflussten somit die molekular lösliche Menge von solchen Wirkstoffen, die mit der Galle wechselwirken. Diese Einblicke in das Zusammenspiel von Galle und Arzneistoffen bieten einen Ansatz zur Optimierung von Formulierungen, die die Solubilisierung in der Galle nutzen. Dieses Kapitel wurde in Journal of Controlled Release veröffentlicht. Kapitel 3 befasst sich mit den Auswirkungen von Galle auf den Dünndarmschleim von Schweinen. Schleim, der Gallenlösung ausgesetzt war, veränderte sich vorübergehend, versteifte sich und die Gesamtdiffusionsrate nahm zu. Die durch die Galle hervorgerufenen Veränderungen erleichterten den Transport des mit der Galle interagierenden Wirkstoffs Fluphenazin, während Metoprolol unbeeinflusst blieb. Dieses dichotome Muster konnte mit der Bioverfügbarkeit bei Ratten verknüpft werden und durch zwei zuvor veröffentlichte Datensätze mit insgesamt 50 Verbindungen verallgemeinert werden. Die Ergebnisse deuten auf eine Wechselwirkung zwischen Galle und Schleim hin, die für die Verabreichung von Medikamenten relevant ist. Dieses Kapitel ist eingereicht. Der Anhang bietet einen Leitfaden für die biopharmazeutische Charakterisierung von Arzneimittelsubstanzen durch kernmagnetische Resonanzspektroskopie mit dem Ziel des Aufstellens von prädiktiven Algorithmen. Zusammenfassend entschlüsselt diese Arbeit die von der Galle gesteuerten Mechanismen, die die Aufnahme von Arzneimitteln im Darm beeinflussen. Auf der Grundlage dieser molekularen Erkenntnisse können Arzneimittel entlang einer biopharmazeutischen Optimierung entwickelt werden, was letztendlich zu besseren oralen Arzneimitteln führt. KW - Solubilisation KW - Galle KW - Bioverfügbarkeit KW - Pharmazeutischer Hilfsstoff KW - drug delivery KW - absorption KW - intestinal permeability KW - poor water-soluble drugs KW - intestinal mucus KW - pig KW - drug formulation KW - molecular biopharmaceutics KW - mucin KW - Schleim KW - Bile KW - Mucus Y1 - 2024 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-348906 ER - TY - THES A1 - Haider, Malik Salman T1 - Structure Property Relationship and Therapeutic Potential of Poly(2-oxazoline)s and Poly(2-oxazines)s based Amphiphiles T1 - Untersuchung der Struktur-Eigenschafts-Beziehung und des Therapeutischen Potenzials von Poly(2-oxazolinen) und Poly(2-oxazinen)-basierten Amphiphilen N2 - In the past decade, poly(2-oxazoline)s (POx) and very recently poly(2-oxazine)s (POzi) based amphiphiles have shown great potential for medical applications. Therefore, the major aim of this thesis was to further explore the pharmaceutical and biomedical applications of POx/POzi based ABA triblock and AB diblock copolymers, respectively with the special emphasis on structure property relationship (SPR). ABA triblock copolymers (with shorter side chain length in the hydrophobic block) have shown high solubilizing capacity for hydrophobic drugs. The issue of poor aqueous solubility was initially addressed by developing a (micellar) formulation library of 21 highly diverse, hydrophobic drugs with POx/POzi based ABA triblock copolymers. Theoretically, the extent of compatibility between polymers and drug was determined by calculating solubility parameters (SPs). The SPs were thoroughly investigated to check their applicability in present systems. The selected formulations were further characterized by various physico-chemical techniques. For the biomedical applications, a novel thermoresposive diblock copolymer was synthesized which has shown promising properties to be used as hydrogel bioink or can potentially be used as fugitive support material. The most important aspect i.e. SPR, was studied with respect to hydrophilic block in either tri- or di-block copolymers. In triblock copolymer, the hydrophilic block played an important role for ultra high drug loading, while in case of diblock, it has improved the printability of the hydrogels. Apart from the basic research, the therapeutic applications of two formulations i.e. mitotane (commercially available as tablet dosage form for adrenocortical carcinoma) and BT-44 (lead compound for nerve regeneration) were studied in more detail. N2 - In den letzten zehn Jahren haben auf Poly(2-oxazolinen) (POx) und in jüngster Zeit auf Poly(2-oxazinen) (POzi) basierende Amphiphile ein großes Potenzial für medizinische Anwendungen gezeigt. Daher war das Hauptziel dieser Arbeit die weitere Erforschung der pharmazeutischen und biomedizinischen Anwendungen von POx/POzi-basierten ABA-Triblock- und AB-Diblock-Copolymeren, jeweils mit besonderem Schwerpunkt auf Struktur-Eigenschafts-Beziehungen (SPR). ABA-Triblockcopolymere (mit kürzerer Seitenkettenlänge im hydrophoben Block) haben eine hohe Solubilisierungskapazität für hydrophobe Arzneimittel gezeigt. Das Problem der schlechten Wasserlöslichkeit wurde zunächst durch die Entwicklung einer (mizellaren) Formulierungsbibliothek von 21 sehr unterschiedlichen, hydrophoben Arzneimitteln mit ABA-Triblockcopolymeren auf POx/POzi-Basis angegangen. Theoretisch wurde das Ausmaß der Kompatibilität zwischen Polymeren und Arzneistoff durch Berechnung von Löslichkeitsparametern (SPs) bestimmt. Die SPs wurden gründlich untersucht, um ihre Anwendbarkeit in gegenwärtigen Systemen zu überprüfen. Die ausgewählten Formulierungen wurden weiter durch verschiedene physikalisch-chemische Techniken charakterisiert. Für biomedizinische Anwendungen wurde ein neuartiges thermoresponsives Diblockcopolymer synthetisiert, das vielversprechende Eigenschaften für die Verwendung als Hydrogel-Biotinte gezeigt hat oder möglicherweise als flüchtiges Trägermaterial verwendet werden kann. Der wichtigste Aspekt, d. h. SPR, wurde im Hinblick auf den hydrophilen Block in entweder Tri- oder Di-Block-Copolymeren untersucht. Beim Triblock-Copolymer spielte der hydrophile Block eine wichtige Rolle für die ultrahohe Wirkstoffbeladung, während er beim Diblock die Bedruckbarkeit der Hydrogele verbessert hat. Neben der Grundlagenforschung wurden die therapeutischen Anwendungen von zwei Formulierungen, nämlich Mitotan (kommerziell erhältlich als Tablettenform für das Nebennierenrindenkarzinom) und BT-44 (Leitsubstanz für die Nervenregeneration) genauer untersucht. KW - structure property relationship KW - Poly(2-oxazoline)s and Poly(2-oxazine)s KW - Importance of hydrophilic block in amphiphiles KW - micelles KW - drug delivery system KW - high drug loading KW - hydrogels KW - ring opening polymerization Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-289036 ER -