TY - THES A1 - Bendias, Michel Kalle T1 - Quantum Spin Hall Effect - A new generation of microstructures T1 - Quantum Spin Hall Effekt - Eine neue Generation an Mikrostrukturen N2 - The presented thesis summarizes the results from four and a half years of intense lithography development on (Cd,Hg)Te/HgTe/(Cd,Hg)Te quantum well structures. The effort was motivated by the unique properties of this topological insulator. Previous work from Molenkamp at al.\ has proven that the transport through such a 2D TI is carried by electrons with opposite spin, counter-propagating in 1D channels along the sample edge. However, up to this thesis, the length of quantized spin Hall channels has never been reported to exceed 4 µm. Therefore, the main focus was put on a reproducible and easy-to-handle fabrication process that reveals the intrinsic material parameters. Every single lithography step in macro as well as microscopic sample fabrication has been re-evaluated. In the Development, the process changes have been presented along SEM pictures, microgaphs and, whenever possible, measurement responses. We have proven the conventional ion milling etch method to damage the remaining mesa and result in drastically lower electron mobilities in samples of microscopic size. The novel KI:I2:HBr wet etch method for macro and microstructure mesa fabrication has been shown to leave the crystalline structure intact and result in unprecedented mobilities, as high as in macroscopic characterization Hall bars. Difficulties, such as an irregular etch start and slower etching of the conductive QW have been overcome by concentration, design and etch flow adaptations. In consideration of the diffusive regime, a frame around the EBL write field electrically decouples the structure mesa from the outside wafer. As the smallest structure, the frame is etched first and guarantees a non-different etching of the conductive layer during the redox reaction. A tube-pump method assures reproducible etch results with mesa heights below 300 nm. The PMMA etch mask is easy to strip and leaves a clean mesa with no redeposition. From the very first attempts, to the final etch process, the reader has been provided with the characteristics and design requirements necessary to enable the fabrication of nearly any mesa shape within an EBL write field of 200 µm. Magneto resistance measurement of feed-back samples have been presented along the development chronology of wet etch method and subsequent lithography steps. With increasing feature quality, more and more physics has been revealed enabling detailed evaluation of smallest disturbances. The following lithography improvements have been implemented. They represent a tool-box for high quality macro and microstructure fabrication on (CdHg)Te/HgTe of almost any kind. The optical positive resist ECI 3027 can be used as wet and as dry etch mask for structure sizes larger than 1 µm. It serves to etch mesa structures larger than the EBL write field. The double layer PMMA is used for ohmic contact fabrication within the EBL write field. Its thickness allows to first dry etch the (Cd,Hg)Te cap layer and then evaporate the AuGe contact, in situ and self-aligned. Because of an undercut, up to 300 nm can be metalized without any sidewalls after the lift-off. An edge channel mismatch within the contact leads can be avoided, if the ohmic contacts are designed to reach close to the sample and beneath the later gate electrode. The MIBK cleaning step prior to the gate application removes PMMA residuals and thereby improves gate and potential homogeneity. The novel low HfO2-ALD process enables insulator growth into optical and EBL lift-off masks of any resolvable shape. Directly metalized after the insulator growth, the self-aligned method results in thin and homogeneous gate electrode reproducibly withholding gate voltages to +-10 V. The optical negative resist ARN 4340 exhibits an undercut when developed. Usable as dry etch mask and lift-off resist, it enables an in-situ application of ohmic contacts first etching close to the QW, then metalizing AuGe. Up to 500 nm thickness, the undercut guarantees an a clean lift-off with no sidewalls. The undertaken efforts have led to micro Hall bar measurements with Hall plateaus and SdH-oszillations in up to now unseen levels of detail. The gap resistance of several micro Hall bars with a clear QSH signal have been presented in Quantum Spin Hall. The first to exhibit longitudinal resistances close to the expected h/2e2 since years, they reveal unprecedented details in features and characteristics. It has been shown that their protection against backscattering through time reversal symmetry is not as rigid as previously claimed. Values below and above 12.9 kΩ been explained, introducing backscattering within the Landauer-Büttiker formalism of edge channel transport. Possible reasons have been discussed. Kondo, interaction and Rashba-backscattering arising from density inhomogeneities close to the edge are most plausible to explain features on and deviations from a quantized value. Interaction, tunneling and dephasing mechanisms as well as puddle size, density of states and Rashba Fields are gate voltage dependent. Therefore, features in the QSH signal are fingerprints of the characteristic potential landscape. Stable up to 11 K, two distinct but clear power laws have been found in the higher temperature dependence of the QSH in two samples. However, with ΔR = Tα, α = ¼ in one (QC0285) and α = 2 in the other (Q2745), none of the predicted dependencies could be confirmed. Whereas, the gap resistances of QC0285 remains QSH channel dominated up to 3.9 T and thereby confirmed the calculated lifting of the band inversion in magnetic field. The gate-dependent oscillating features in the QSH signal of Q2745 immediately increase in magnetic field. The distinct field dependencies allowed the assumption of two different dominant backscattering mechanisms. Resulting in undisturbed magneto transport and unprecedented QSH measurements The Novel Micro Hall Bar Process has proven to enable the fabrication of a new generation of microstructures. N2 - In der vorliegenden Dissertation wurden die Ergebnisse von viereinhalb Jahren lithographischer Prozessentwicklung an (Cd,Hg)Te/HgTe/(Cd,Hg)Te Quantum Well Strukturen präsentiert. Motiviert wurde der Aufwand mit den einzigartigen Eigenschaften des zweidimensionalen Topologischen Isolators. In früheren Arbeiten von Molenkamp et al. ist gezeigt worden, dass der Stromtransport im Quantum Spin Hall (QSH) Regime durch zwei Randkanäle mit Elektronen entgegengerichteter Spin- und Propagationsrichtung erfolgt. Trotz der Vorhersage geschützten Randkanaltransports durch Zeit-Umkehr Invarianz, gab es bis zu der hier vorgenommenen Prozessoptimierung keine ungestörten Quantum Spin Hall Messungen oberhalb einer Länge von 4 µm. Deswegen wurde das Hauptaugenmerk der Entwicklung auf einen möglichst einfachen, reproduzierbaren und ungestörten Herstellungsprozess für QSH Mikrostrukturen gelegt. Die Ergebnisse der vollständigen Überarbeitung jedes einzelnen Lithographie-Schrittes für marko- und mikroskopische Probenstrukturierung wurden in Development erläutert. Die Anpassungen wurden anhand von Elektronen-, Lichtmikroskop-Aufnahmen und wann immer möglich auch Messungen motiviert, überprüft und für besser befunden. Es wurde aufgezeigt, dass das bisher übliche Verfahren zum ätzen der Mesa mit beschleunigen Argon-Ionen das Material auch lateral beschädigt und mit drastisch reduzierten Elektronen-Beweglichkeiten in mikroskopischen Proben einhergeht. Ein neuartiger KI:I2:HBr nass-Ätzprozess hingegen, hat sich als nicht invasiv erwiesen. Ohne die Kristallstruktur zu zerstören lassen sich damit Mikrostrukturen herstellen, welche sich durch beispiellos hohe Beweglichkeiten und Signalgüte auszeichnen. Schwierigkeiten, wie der unregelmäßige Ätz-Start und das langsamere Ätzen der leitfähigen Schicht sind durch Konzentrations-, Design- und Flussanpassungen sukzessive gelöst worden. Unter Beachtung des diffusiven Ätz-Charakters, sorgt ein schmaler Rahmen um das Schreibfeld des Elektronen Mikroskops für eine elektrische Entkopplung der späteren Mesa innen, mit dem Elektronen-Reservoir außen. Damit wird sichergestellt, dass die Leitfähigkeit des Quantentroges in der Redoxreaktion des Ätzens eine untergeordnete Rolle spielt. Durch den regulierbaren Fluss einer Schlauchpumpe lassen sich so reproduzierbar saubere Mesas auch unterhalb 300 nm Höhe herstellen. Die PMMA Ätzmaske kann rückstandsfrei entfernen werden. Über die ersten Versuche, bis hin zum letztendlichen Prozess, wurde dem Leser dabei das notwendige Wissen und Verständnis zur Durchführung der Mikrostrukturierung an die Hand gegeben. Unter Beachtung der charakteristischen Eigenheiten des nasschemischen Prozesses, lassen sich so nahezu alle Mesa-Formen innerhalb eines 200x200 µm2 Schreibfeldes realisieren. Anhand von Hall-Messungen an Kontrollproben, wurde die sukzessive Erhöhung der Probenqualität durch den Ätzprozess und die vollständige Überarbeitung der darauf folgenden Lithographie-Prozesse bewiesen. Mit mehr und mehr Physik in den Messungen haben sich selbst kleine Auswirkungen des Lithographie-Prozesses auf die Probeneigenschaften testen lassen. Die folgenden Verbesserungen tragen maßgeblich zu diesem Ergebnis bei. Hier angewendet auf Mikro-Hall-Bars, lassen sich die Prozesse für die Herstellung fast jedweder Struktur auf (Cd,Hg)Te/HgTe anpassen. Der optische positiv Photo-Lack ECI 3027 kann sowohl als Nass- und auch Trockenätzmaske verwendet werden. Mit einer minimalen Auflösung größer 1 µ m wurde er hier eingesetzt, um Strukturen um das Elektronenmikroskop-Schreibfeld zu ätzen. Der PMMA Doppellagen Resist ist dick und weist nach dem Entwickeln ein unterhöhltes Lackprofil auf. Dies erlaubt ihn zuerst zum Heranätzen und dann zum Metallisieren der Ohmschen Kontakte zu nutzen. Bis zu 300 nm Metall können dabei ohne Überhöhungen in-situ und selbstjustierend aufgebracht werden. Es wurde gezeigt, dass Kontakte nahe der Hall-Bar bis unterhalb der späteren Gate-Elektrode, in höheren Magnetfeldern nicht zu Störungen der Messung führen. Der MIBK Reinigungs Schritt vor dem Aufbringen der Gate-Elektrode entfernt PMMA Rückstände vorheriger Prozesse. In Hall-Messungen wurde gezeigt, dass dies die Homogenität des Gate-Einflusses deutlich verbessert. Der neuartige Tieftemperatur HfO2 ALD Prozess ermöglicht Isolator Wachstum auf Photo-Resist und PMMA Lift-off Masken. Dies wiederum ermöglicht eine Gate-Metallisierung direkt im Anschluss. Dadurch lassen sich auch kleine Gate-Elektroden mit homogenem Potential-Einfluss herstellen, welche reproduzierbar Spannungen bis +-10 V aushalten. Der optische negativ Photo-Lack ARN 4340 ermöglicht das Heranätzen und Metallisieren von Ohmschen Kontakten in Strukturgrößen größer 1 µm. Das ebenfalls unterhöhlte Lackprofil erlaubt dabei die Aufbringung von bis zu 500 nm dicken Schichten und einen problemlosen Lift-off. Die unternommenen Anstrengungen haben dabei zu den bisher Besten und Detailsreichsten Messungen von Hall-Plateaus und Shubnikov-De Haas Oszillationen in (Cd,Hg)Te/ HgTe Mikrostrukturen geführt. Messungen mit einem klaren QSH Signal im Längswiderstand von mehreren Mikro-Hall-Bars wurden präsentiert. Nach jahrelangen Bemühungen weisen diese Proben erstmalig wieder einen Bandlücken-Widerstand nahe der erwarteten Quantisierung von zwei Randkanälen auf. Es wurde aufgezeigt, dass die vermeintliche geschützten Randzustände durchaus rück-streuen. Mit der Implementierung von Streuern im Landauer-Büttiker Formalismus für Randkanaltransport lassen sich Abweichungen unter- und oberhalb der erwarteten 12.9 kΩ begründen. Als mögliche Ursachen wurden Dichte-Inhomogenitäten ausgemacht, welche in Kondo-, Wechselwirkungs- und Rashba-Rückstreuprozessen resultieren. Im komplexen Zusammenspiel von Wechselwirkung, Tunnelprozessen und Spin-Dephasierung, der unbekannten Verteilung von Inhomogenitäten, ihrer Größe und Dichte sowie der Feldabhängig-keit aller Parameter, hat sich keiner der diskutierten Mechanismen als dominant bewiesen. In noch nie dagewesenen Details erwies sich die Gate- und Magnetfeldabhängigkeit des QSH Signals als ein Fingerabdruck der hintergründigen Potential-Landschaft. Die Signale von zwei unterschiedlichen Proben sind Temperatur- und Magnetfeldabhängig untersucht worden. Dabei haben mehrere Argumente zu der Schlussfolgerung geführt, dass unterschiedliche Rückstreumechanismen in den Proben dominieren: Mit einem flachen QSH Plateau in der einen (QC0285), und in Gate-Spannung oszillierender Merkmale auf dem QSH Signal der anderen Probe (Q2745), zeigen sich erste Unterschiede bereits in den Gate-Messungen. In Temperatur-abhängigen Messungen erweist sich deren QSH Signal zwar als stabil bis 11\,K, folgt dann aber ΔR = Tα mit α = 1/4 in QC0285 und α = 2 in Q2745. Im Magnetfeld bleibt die Bandlücke in QC0285 bis zum kritischen Feld der Invertierungsaufhebung Randkanal-Transport dominiert. Die Oszillierenden Merkmale auf dem QSH Signal in Q2745 dagegen, reagieren schon auf kleine Felder mit einer Erhöhung im Widerstand. Die unvergleichliche Qualität der hier präsentierten Hall-Messungen und QSH Signale und das bis ins letzte Detail optimierte Herstellungsverfahren, rechtfertigen es von einer neuen Generation an QSH Mikrostrukturen zu sprechen. KW - Topological insulators KW - Quecksilbertellurid KW - Quantum Spin Hall Effect KW - Lithography KW - Macroscopic transport KW - Quecksilbertellurid KW - Topologischer Isolator KW - Quanten-Hall-Effekt Y1 - 2018 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-168214 ER - TY - THES A1 - Leisegang, Markus T1 - Eine neue Methode zur Detektion ballistischen Transports im Rastertunnelmikroskop: Die Molekulare Nanosonde T1 - A new method for detecting ballistic transport in the scanning tunneling microscope: The molecular nanoprobe N2 - Verlustarmer Ladungsträgertransport ist für die Realisierung effizienter und kleiner elektronischer Bauteile von großem Interesse. Dies hilft entstehende Wärme zu minimieren und den Energieverbrauch gleichzeitig zu reduzieren. Einzelne Streuprozesse, die den Verlust bei Ladungsträgertransport bestimmen, laufen jedoch auf Längenskalen von Nano- bis Mikrometern ab. Um diese detailliert untersuchen zu können, bedarf es Messmethoden mit hoher zeitlicher oder örtlicher Auflösung. Für Letztere gibt es wenige etablierte Experimente, häufig basierend auf der Rastertunnelmikroskopie, welche jedoch verschiedenen Einschränkungen unterliegen. Um die Möglichkeiten der Detektion von Ladungsträgertransport auf Distanzen der mittleren freien Weglänge und damit im ballistischen Regime zu verbessern, wurde im Rahmen dieser Dissertation die Molekulare Nanosonde charakterisiert und etabliert. Diese Messmethode nutzt ein einzelnes Molekül als Detektor für Ladungsträger, welche mit der Sondenspitze des Rastertunnelmikroskops (RTM) wenige Nanometer entfernt vom Molekül in das untersuchte Substrat injiziert werden. Die hohe Auflösung des RTM in Kombination mit der geringen Ausdehnung des molekularen Detektors ermöglicht dabei atomare Kontrolle von Transportpfaden über wenige Nanometer. Der erste Teil dieser Arbeit widmet sich der Charakterisierung der Molekularen Nanosonde. Hierfür werden zunächst die elektronischen Eigenschaften dreier Phthalocyanine mittels Rastertunnelspektroskpie untersucht, welche im Folgenden zur Charakterisierung des Moleküls als Detektor Anwendung finden. Die anschließende Analyse der Potentiallandschaft der Tautomerisation von H2Pc und HPc zeigt, dass die NH- Streckschwinung einem effizienten Schaltprozess zu Grunde liegt. Darauf basierend wird der Einfluss der Umgebung anhand von einzelnen Adatomen sowie des Substrats selbst auf den molekularen Schalter analysiert. In beiden Fällen zeigt sich eine signifikante Änderung der Potentiallandschaft der Tautomerisation. Anschließend wird der Einfluss geometrischer Eigenschaften des Moleküls selbst untersucht, wobei sich eine Entkopplung vom Substrat auf Grund von dreidimensionalen tert-Butyl-Substituenten ergibt. Zusätzlich zeigt sich bei dem Vergleich von Naphthalocyanin zu Phthalocyanin der Einfluss lateraler Ausdehnung auf die Detektionsfläche, was einen nicht-punktförmigen Detektor bestätigt. Im letzten Abschnitt werden zwei Anwendungen der Molekularen Nanosonde präsentiert. Zunächst wird mit Phthalocyanin auf Ag(111) demonstriert, dass die Interferenz von ballistischen Ladungsträgern auf Distanzen von wenigen Nanometern mit dieser Technik detektierbar ist. Im zweiten Teil zeigt sich, dass der ballistische Transport auf einer Pd(110)-Oberfläche durch die anisotrope Reihenstruktur auf atomarer Skala moduliert wird. N2 - Low-loss charge carrier transport is of great interest for the realization of efficient and small electronic components. Improvements would minimize heat generation and reduce energy consumption at the same time. However, individual scattering processes that determine the loss in charge carrier transport occur on length scales from nanometers to micrometers. To study these in detail, measurement methods with high temporal or spatial resolution are required. For the latter, few established experiments exist, often based on scanning tunneling microscopy, which are however subject to various limitations. In order to improve the possibilities of detecting charge carrier transport at distances of the mean free path and thus in the ballistic regime, the molecular nanoprobe was characterized and established in this dissertation. This measurement technique uses a single molecule as a detector for charge carriers, which are injected into the substrate under investigation with the scanning tunneling microscope (STM) tip a few nanometers away from the molecule. The high resolution of the STM combined with the small size of the molecular detector allows atomic control of transport paths over a few nanometers. The first part of this work is devoted to the characterization of the molecular nanoprobe. For this purpose, the electronic properties of three phthalocyanines are first investigated by scanning tunneling spectroscopy, which will be applied in the following studies to characterize the molecular detector. The subsequent analysis of the potential landscape for tautomerization within H2Pc and HPc reveals that the N-H stretching mode underlies an efficient switching process. Based on these findings, the influence of the direct environment on the molecular switch is analyzed by means of individual adatoms as well as the substrate itself. In both cases, a significant change in the potential landscape of the tautomerization is shown. Subsequently, the influence of geometric properties of the molecule itself is investigated, revealing a decoupling from the substrate due to three-dimensional tert-butyl substituents. In addition, the comparison through naphthalocyanine to phthalocyanine reveals the influence of lateral expansion on the detection area, confirming a non-point molecular detector. In the last section, two applications of the molecular nanoprobe are presented. First, using phthalocyanine on Ag(111), it is demonstrated that the interference of ballistic charge carriers at distances of a few nanometers is detectable with this technique. In the second part, it is shown that the anisotropic Pd(110) surface structure leads to a strong modulation of the ballistic transport on the atomic scale. KW - Rastertunnelmikroskopie KW - Ladungstransport KW - Molekül KW - Nanosonde KW - Ballistischer Transport KW - Molekulare Sonde KW - Tautomerisation KW - Molekularer Schalter Y1 - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-250762 ER - TY - THES A1 - Gottscholl, Andreas Paul T1 - Optical Accessible Spin Defects in Hexagonal Boron Nitride: Identification, Control and Application of the Negatively Charged Boron Vacancy VB- T1 - Optisch zugängliche Spin-Defekte in hexagonalem Bornitrid: Identifizierung, Kontrolle und Anwendung der negativ geladenen Bor-Fehlstelle VB- N2 - In this work, a bridge was built between the so-far separate fields of spin defects and 2D systems: for the first time, an optically addressable spin defect (VB-) in a van der Waals material (hexagonal boron nitride) was identified and exploited. The results of this thesis are divided into three topics as follows: 1.) Identification of VB-: In the scope of this chapter, the defect ,the negatively charged boron vacancy VB-, is identified and characterized. An initialization and readout of the spin state can be demonstrated optically at room temperature and its spin Hamiltonian contributions can be quantified. 2.) Coherent Control of VB-: A coherent control is required for the defect to be utilized for quantum applications, which N2 - Im Rahmen dieser Arbeit konnte zum allerersten Mal ein optisch addressierbarer Spin Defekt in einem Van-der-Waals Material (hexagonales Bornitrid) nachgewiesen wer- den. Hervorzuheben ist hierbei der 2D Charakter des Materials hBN, welches als das Standardmaterial zur Verkapselung anderer 2D Materialien verwendet wird und somit unterschiedlichste Anwendungen des neu entdeckten Spindefektes denkbar macht. ... KW - Bornitrid KW - Boron Nitride Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-274326 ER - TY - THES A1 - Betzold, Simon T1 - Starke Licht-Materie-Wechselwirkung und Polaritonkondensation in hemisphärischen Mikrokavitäten mit eingebetteten organischen Halbleitern T1 - Strong light-matter interaction and polariton condensation in hemispherical microcavities with embedded organic semiconductors N2 - Kavitäts-Exziton-Polaritonen (Polaritonen) sind hybride Quasiteilchen, die sich aufgrund starker Kopplung von Halbleiter-Exzitonen mit Kavitätsphotonen ausbilden. Diese Quasiteilchen weisen eine Reihe interessanter Eigenschaften auf, was sie einerseits für die Grundlagenforschung, andererseits auch für die Entwicklung neuartiger Bauteile sehr vielversprechend macht. Bei Erreichen einer ausreichend großen Teilchendichte geht das System in den Exziton-Polariton-Kondensationszustand über, was zur Emission von laserartigem Licht führt. Organische Halbleiter als aktives Emittermaterial zeigen in diesem Kontext großes Potential, da deren Exzitonen neben großen Oszillatorstärken auch hohe Bindungsenergien aufweisen. Deshalb ist es möglich, unter Verwendung organischer Halbleiter selbst bei Umgebungsbedingungen äußerst stabile Polaritonen zu erzeugen. Eine wichtige Voraussetzung zur Umsetzung von integrierten opto-elektronischen Bauteilen basierend auf Polaritonen ist der kontrollierte räumliche Einschluss sowie die Realisierung von frei konfigurierbaren Potentiallandschaften. Diese Arbeit beschäftigt sich mit der Entwicklung und der Untersuchung geeigneter Plattformen zur Erzeugung von Exziton-Polaritonen und Polaritonkondensaten in hemisphärischen Mikrokavitäten, in die organische Halbleiter eingebettet sind. N2 - Cavity exciton-polaritons (polaritons) are hybrid quasiparticles which are formed due to the strong coupling of excitons with cavity photons. These quasiparticles exhibit a variety of interesting properties, rendering them very promising for both fundamental research and the development of novel opto-electronic devices. Once a suitably high particle density is reached, the system undergoes the transition into a state of exciton-polariton condensation, which leads to the emission of laser-like light. Organic semiconductors as active emitter material hold enormous potential in this context, as their excitons show both large oscillator strengths and high binding energies. Therefore it is possible to generate extremely stable polaritons using organic semiconductors even at ambient conditions. An important prerequisite for the implementation of integrated devices based on polaritons is the controlled spatial confinement and the realization of arbitrary potential landscapes. The present work deals with the development and investigation of suitable platforms for the generation of exciton-polaritons and polariton condensates in hemispheric microcavities with embedded organic semiconductors. KW - Exziton-Polariton KW - Organischer Halbleiter KW - Fourier-Spektroskopie KW - Laser KW - Optischer Resonator KW - FDTD Simulation KW - Hemisphärische Kavität Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-266654 ER - TY - THES A1 - Fischer, Mathias T1 - Transient Phenomena and Ionic Kinetics in Hybrid Metal Halide Perovskite Solar Cells T1 - Transiente Phänomene und ionische Kinetik in Hybrid-Metallhalogenid- Perowskit-Solarzellen N2 - The fact that photovoltaics is a key technology for climate-neutral energy production can be taken as a given. The question to what extent perovskite will be used for photovoltaic technologies has not yet been fully answered. From a photophysical point of view, however, it has the potential to make a useful contribution to the energy sector. However, it remains to be seen whether perovskite-based modules will be able to compete with established technologies in terms of durability and cost efficiency. The additional aspect of ionic migration poses an additional challenge. In the present work, primarily the interaction between ionic redistribution, capacitive properties and recombination dynamics was investigated. This was done using impedance spectroscopy, OCVD and IV characteristics as well as extensive numerical drift-diffusion simulations. The combination of experimental and numerical methods proved to be very fruitful. A suitable model for the description of solar cells with respect to mobile ions was introduced in chapter 4.4. The formal mathematical description of the model was transferred by a non-dimensionalization and suitable numerically solvable form. The implementation took place in the Julia language. By intelligent use of structural properties of the sparse systems of equations, automatic differentiation and the use of efficient integration methods, the simulation tool is not only remarkably fast in finding the solution, but also scales quasi-linearly with the grid resolution. The software package was released under an open source license. In conventional semiconductor diodes, capacitance measurements are often used to determine the space charge density. In the first experimental chapter 5, it is shown that although this is also possible for the ionic migration present in perovskites, it cannot be directly understood as doping related, since the space charge distribution strongly depends on the preconditions and can be manipulated by an externally applied voltage. The exact form of this behavior depends on the perovskite composition. This shows, among other things, that experimental results can only be interpreted within the framework of conventional semiconductors to a very limited extent. Nevertheless, the built-in 99 potential of the solar cell can be determined if the experiments are carried out properly. A statement concerning the type and charge of the mobile ions is not possible without further effort, while their number can be determined. The simulations were applied to experimental data in chapter 6. Thus, it could be shown that mobile ions make a significant contribution to the OCVD of perovskite solar cells. j-V characteristics and OCVD transients measured as a function of temperature and illumination intensities could be quantitatively modeled simultaneously using a single global set of parameters. By the simulations it was further possible to derive a simple experimental procedure to determine the concentration and the diffusivity of the mobile ions. The possibility of describing different experiments in a uniform temperaturedependent manner strongly supports the model of mobile ions in perovskites. In summary, this work has made an important contribution to the elucidation of ionic contributions to the (photo)electrical properties of perovskite solar cells. Established experimental techniques for conventional semiconductors have been reinterpreted with respect to ionic mass transport and new methods have been proposed to draw conclusions on the properties for ionic transport. As a result, the published simulation tools can be used for a number of further studies. N2 - Dass die Photovoltaik eine Schlüsseltechnologie für die klimaneutrale Energieerzeu- gung ist, kann als gegeben angesehen werden. Die Frage, inwieweit Perowskit für Photovoltaik-Technologien eingesetzt werden wird, ist noch nicht abschließend geklärt. Aus photophysikalischer Sicht hat es jedoch das Potenzial, einen sinnvollen Beitrag im Energiesektor zu leisten. Es bleibt jedoch abzuwarten, ob Module auf Perowskitbasis in Bezug auf Haltbarkeit und Kosteneffizienz mit den etablierten Technologien konkurrieren können. Der zusätzliche Aspekt der Ionenmigration stellt eine weitere Herausforderung im Bezug zu Degeneration und MPP-tracking dar. In der vorliegenden Arbeit wurde vor allem die Wechselwirkung zwischen Ionenumverteilung, kapazitiven Eigenschaften und Rekombinationsdynamik untersucht. Dazu wurden Impedanzspektroskopie, OCVD- und IV-Kennlinien sowie umfangreiche numerische Drift-Diffusions-Simulationen eingesetzt. Die Kombination von experimentellen und numerischen Methoden erwies sich als sehr fruchtbar. Ein geeignetes Modell zur Beschreibung von Solarzellen im Hinblick auf mobile Ionen wurde in Kapitel 4.4 vorgestellt. Die formale mathematische Beschreibung des Modells wurde durch eine Nichtdimensionalisierung und geeignete numerisch lösbare Form umgesetzt. Die Implementierung erfolgte in der Sprache Julia. Durch intelligente Ausnutzung struktureller Eigenschaften der dünn besetzten Gleichungssysteme, automatische Differenzierung und den Einsatz effizienter Integrationsmethoden ist das Simulationswerkzeug nicht nur bemerkenswert schnell in der Lösungsfindung, sondern skaliert auch quasi-linear mit der Gitterauflösung. Das Softwarepaket wurde unter einer Open- Source-Lizenz veröffentlicht. Bei herkömmlichen Halbleiterdioden werden häufig Kapazitätsmessungen zur Bestim- mung der Raumladungsdichte verwendet. Im ersten experimentellen Kapitel 5 wird gezeigt, dass dies zwar auch für die in Perowskiten vorhandene Ionenwanderung möglich ist, aber nicht direkt als dopingbedingt verstanden werden kann, da die Raum- ladungsverteilung stark von den Voraussetzungen abhängt und durch eine extern angelegte Spannung manipuliert werden kann. Die genaue Form dieses Verhaltens hängt von der Zusammensetzung des Perowskits ab. Dies zeigt u.a., dass experimentelle Ergebnisse nur sehr eingeschränkt im Rahmen konventioneller Halbleiter interpretiert werden können. Dennoch lässt sich das eingebaute Potenzial der Solarzelle bestimmen, wenn die Experimente richtig durchgeführt werden. Eine Aussage über die Art und Ladung der beweglichen Ionen ist ohne weiteren Aufwand nicht möglich, während ihre Anzahl bestimmt werden kann. Die Simulationen wurden in Kapitel 6 auf experimentelle Daten angewandt. So konnte gezeigt werden, dass mobile Ionen einen wesentlichen Beitrag zur OCVD von Perowskit-Solarzellen leisten. j-V -Charakteristika und OCVD-Transienten, die in Abhängigkeit von Temperatur und Beleuchtungsintensität gemessen wurden, konnten mit einem einzigen globalen Parametersatz gleichzeitig quantitativ modelliert werden. Durch die Simulationen war es ferner möglich, ein einfaches experimentelles Verfahren zur Bestim- mung der Konzentration und des Diffusionsvermögens der mobilen Ionen abzuleiten. Die Möglichkeit, verschiedene Experimente einheitlich und temperaturabhängig zu beschreiben, unterstützt das Modell der mobilen Ionen in Perowskiten sehr. Zusammenfassend kann gesagt werden, dass diese Arbeit einen wichtigen Beitrag zur Aufklärung der ionischen Beiträge zu den (photo)elektrischen Eigenschaften von Perowskit-Solarzellen geleistet hat. Etablierte experimentelle Techniken für konventionelle Halbleiter wurden im Hinblick auf den ionischen Massentransport neu interpretiert, und es wurden neue Methoden vorgeschlagen, um Rückschlüsse auf die für den ionischen Transport charakteristischen Eigenschaften zu ziehen. Das Ergebnis ist, dass die veröffentlichten Simulationswerkzeuge für eine Reihe weiterer Studien genutzt werden können. KW - Simulation KW - Perowskit KW - Dünnschichtsolarzelle KW - Fotovoltaik KW - Drift-Diffusion KW - Photoviltaics KW - Simulation KW - Perovskite KW - Solar-Cell Y1 - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-322204 ER - TY - THES A1 - Schwemmer, Tilman T1 - Relativistic corrections of Fermi surface instabilities T1 - Relativistische Korrekturen zu Fermiflächeninstabilitäten N2 - Relativistic effects crucially influence the fundamental properties of many quantum materials. In the accelerated reference frame of an electron, the electric field of the nuclei is transformed into a magnetic field that couples to the electron spin. The resulting interaction between an electron spin and its orbital angular momentum, known as spin-orbit coupling (SOC), is hence fundamental to the physics of many condensed matter phenomena. It is particularly important quantitatively in low-dimensional quantum systems, where its coexistence with inversion symmetry breaking can lead to a splitting of spin degeneracy and spin momentum locking. Using the paradigm of Landau Fermi liquid theory, the physics of SOC can be adequately incorporated in an effective single particle picture. In a weak coupling approach, electronic correlation effects beyond single particle propagator renormalization can trigger Fermi surface instabilities such as itinerant magnetism, electron nematic phases, superconductivity, or other symmetry broken states of matter. In this thesis, we use a weak coupling-based approach to study the effect of SOC on Fermi surface instabilities and, in particular, superconductivity. This encompasses a weak coupling renormalization group formulation of unconventional superconductivity as well as the random phase approximation. We propose a unified formulation for both of these two-particle Green’s function approaches based on the notion of a generalized susceptibility. In the half-Heusler semimetal and superconductor LuPtBi, both SOC and electronic correlation effects are prominent, and thus indispensable for any concise theoretical description. The metallic and weakly dispersive surface states of this material feature spin momentum locked Fermi surfaces, which we propose as a possible domain for the onset of unconventional surface superconductivity. Using our framework for the analysis of Fermi surface instability and combining it with ab-initio density functional theory calculations, we analyse the surface band structure of LuPtBi, and particularly its propensity towards Cooper pair formation. We study how the presence of strong SOC modifies the classification of two-electron wave functions as well as the screening of electron-electron interactions. Assuming an electronic mechanism, we identify a chiral superconducting condensate featuring Majorana edge modes to be energetically favoured over a wide range of model parameters. N2 - Relativistische Effekte bestimmen die Eigenschaften vieler Quantenmaterialien entscheidend. Im beschleunigten Bezugssystem eines Elektrons transformiert sich das elektrische Feld des Kerns in ein Magnetfeld, welches an den Spin des Elektrons koppelt. Die resultierende Wechselwirkung zwischen dem Spin eines Elektrons und seinem Bahndrehimpuls, bekannt als Spin-Bahn-Kopplung (engl. spin-orbit coupling SOC), ist für viele Phänomene der kondensierten Materie von grundlegender Bedeutung. In niedrigdimensionalen Quantensystemen, wo die Koexistenz von SOC und Inversionssymmetriebrechung zu einer Aufspaltung der Spinentartung und Kopplung des Spins an den Impulsfreiheitsgrad führen kann, besonders wichtig. Mit dem Paradigma von Landaus Fermi-Flüssigkeits-Theorie lässt sich die Physik des SOC in einem effektiven Ein-Teilchenbild gut modellieren. Ausgehend von einem schwach gekoppelten Bild können elektronische Korrelationseffekte, die über diese einfache Theorie hinausgehen, eine Instabilität der Fermi-Fläche auslösen, die zu Magnetismus, elektronisch-nematischen Phasen, Supraleitung oder anderen symmetriegebrochenen Materialzuständen führt. In dieser Dissertation verwenden wir einen auf schwacher Kopplung basierenden Ansatz, um die Wirkung von SOC auf Instabilitäten der Fermi-Fläche und insbesondere auf Supraleitung zu untersuchen. Wir betrachten eine störungstheoretische Renormierungsgruppenformulierung für unkonventionellen Supraleitung die Random-Phase-Approximation (RPA). Auf Grundlage der verallgemeinerten Suszeptibilität entwickeln wir eine einheitliche Formulierung für diese beiden Ansätze. Im Halb-Heusler-Halbmetall und Supraleiter LuPtBi sind sowohl SOC- als auch elektronische Korrelationseffekte für jede theoretische Beschreibung von großer Bedeutung. Der metallische und schwach dispersive Oberflächenzustand dieses Materials weist Fermi-Flächen mit gekoppeltem Spin und Impuls auf, die wir als mögliche Domäne für den Beginn unkonventioneller Oberflächensupraleitung vorschlagen. Wir kombinieren ab-initio Dichtefunktionaltheorieberechnungen für die Oberflächenbandstruktur von LuPtBi mit der Renormierungsgruppe und der RPA für eine Analyse der Fermi-Oberflächeninstabilitäten and der Kristalloberfläche. Wir untersuchen, wie die Existenz von starkem SOC die Klassifizierung von Zwei-Elektronen-Wellenfunktionen sowie die Abschirmung von Elektron-Elektronen-Wechselwirkungen modifiziert. Unter der Annahme eines elektronischen Mechanismus identifizieren wir ein chirales supraleitendes Kondensat mit Majorana-Randmoden, das über einen weiten Bereich von Modellparametern energetisch begünstigt ist. KW - Supraleitung KW - Random-phase-Approximation KW - Renormierungsgruppe KW - Fermionensystem KW - Spin-Bahn-Wechselwirkung KW - Correlated Fermions KW - Perturbative KW - Functional Renormalization Group KW - Quantum many-body systems KW - Spin-Orbit interaction KW - Unconventional/Topological superconductivity Y1 - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-319648 ER - TY - THES A1 - Scheffler, Lukas T1 - Molecular beam epitaxy of the half-Heusler antiferromagnet CuMnSb T1 - Molekularstrahlepitaxie des halb-Heusler Antiferromagneten CuMnSb N2 - This work presents a newly developed method for the epitaxial growth of the half-Heusler antiferromagnet CuMnSb. All necessary process steps, from buffer growth to the deposition of a protective layer, are presented in detail. Using structural, electrical, and magnetic characterization, the material parameters of the epitaxial CuMnSb layers are investigated. The successful growth of CuMnSb by molecular beam epitaxy is demonstrated on InAs (001), GaSb (001), and InP (001) substrates. While CuMnSb can be grown pseudomorphically on InAs and GaSb, the significant lattice mismatch for growth on InP leads to relaxation already at low film thicknesses. Due to the lower conductivity of GaSb compared to InAs, GaSb substrates are particularly suitable for the fabrication of CuMnSb layers for lateral electrical transport experiments. However, by growing a high-resistive ZnTe interlayer below the CuMnSb layer, lateral transport experiments on CuMnSb layers grown on InAs can also be realized. Protective layers of Ru and Al2O3 have proven to be suitable for protecting the CuMnSb layers from the environment. Structural characterization by high resolution X-ray diffraction (full width at half maximum of 7.7 ′′ of the rocking curve) and atomic force microscopy (root mean square surface roughness of 0.14 nm) reveals an outstanding crystal quality of the epitaxial CuMnSb layers. The half-Heusler crystal structure is confirmed by scanning transmission electron microscopy and the stoichiometric material composition by Rutherford backscattering spectrometry. In line with the high crystal quality, a new minimum value of the residual resistance of CuMnSb (𝜌0 = 35 μΩ ⋅ cm) could be measured utilizing basic electrical transport experiments. An elaborate study of epitaxial CuMnSb grown on GaSb reveals a dependence of the vertical lattice parameter on the Mn/Sb flux ratio. This characteristic enables the growth of tensile, unstrained, and compressive strained CuMnSb layers on a single substrate material. Additionally, it is shown that the Néel temperature has a maximum of 62 K at stoichiometric material composition and thus can be utilized as a selection tool for stoichiometric CuMnSb samples. Mn-related defects are believed to be the driving force for these observations. The magnetic characterization of the epitaxial CuMnSb films is performed by superconducting quantum interference device magnetometry. Magnetic behavior comparable to the bulk material is found, however, an additional complex magnetic phase appears in thin CuMnSb films and/or at low magnetic fields, which has not been previously reported for CuMnSb. This magnetic phase is believed to be localized at the CuMnSb surface and exhibits both superparamagnetic and spin-glass-like behavior. The exchange bias effect of CuMnSb is investigated in combination with different in- and out-of-plane ferromagnets. It is shown that the exchange bias effect can only be observed in combination with in-plane ferromagnets. Finally, the first attempts at the growth of fully epitaxial CuMnSb/NiMnSb heterostructures are presented. Both magnetic and structural studies by secondary-ion mass spectrometry indicate the interdiffusion of Cu and Ni atoms between the two half-Heusler layers, however, an exchange bias effect can be observed for the CuMnSb/NiMnSb heterostructures. Whether this exchange bias effect originates from exchange interaction between the CuMnSb and NiMnSb layers, or from ferromagnetic inclusions in the antiferromagnetic layer can not be conclusively identified. N2 - In dieser Arbeit wird eine neu entwickelte Methode für das epitaktische Wachstum des antiferromagnetischen halb-Heuslers CuMnSb vorgestellt. Alle notwendigen Prozessschritte, vom Pufferschichtwachstum bis hin zum Aufbringen einer Schutzschicht, werden detailliert dargestellt. Mittels struktureller, elektrischer und magnetischer Charakterisierung werden die Materialparameter der epitaktischen CuMnSb-Schichten untersucht. Das erfolgreiche Wachstum von CuMnSb durch Molekularstrahlepitaxie wird auf InAs (001), GaSb (001) und InP (001) Substraten demonstriert. Während CuMnSb auf InAs und GaSb pseudomorph gewachsen werden kann, führt die signifikante Gitterfehlanpassung beim Wachstum auf InP bereits bei geringen Schichtdicken zur Relaxation. Aufgrund der geringeren Leitfähigkeit von GaSb im Vergleich zu InAs sind GaSb-Substrate besonders geeignet für die Herstellung von CuMnSb-Schichten für laterale elektrische Transportexperimente. Durch Einbringen einer hochohmigen ZnTe-Zwischenschicht unterhalb der CuMnSb-Schicht können jedoch auch laterale Transportexperimente an CuMnSb-Schichten, die auf InAs gewachsen werden, durchgeführt werden. Schutzschichten aus Ru und Al2O3 haben sich als geeignet erwiesen, die CuMnSb-Schichten vor der Umgebung zu schützen. Die strukturelle Charakterisierung mittels hochauflösender Röntgendiffraktometrie (Halbwertsbreite der Rocking-Kurve von 7.7′′) und Rasterkraftmikroskopie (quadratisches Mittel der Oberflächenrauhigkeit von 0.14nm) zeigt eine hervorragende Kristallqualität der epitaktischen CuMnSb-Schichten. Die halb-Heusler Kristallstruktur wird durch Rastertransmissionselektronenmikroskopie und die stöchiometrische Materialzusammensetzung durch Rutherford- Rückstreuungsspektrometrie bestätigt. In Übereinstimmung mit der hohen Kristallqualität konnte ein neuer Minimalwert des Restwiderstands von CuMnSb (𝜌0 = 35μΩ⋅cm) mit Hilfe von einfachen elektrischen Transportexperimenten gemessen werden. Eine ausführliche Untersuchung von epitaktischem CuMnSb, das auf GaSb gewachsen wurde, zeigt eine Abhängigkeit der vertikalen Gitterkonstante vom Mn/Sb-Flussverhältnis. Diese Eigenschaft ermöglicht das Wachstum von zugverspannten, unverspannten und druckverspannten CuMnSb Schichten auf einem einzigen Substratmaterial. Darüber hinaus wird gezeigt, dass die Néel-Temperatur bei stöchiometrischer Materialzusammensetzung ein Maximum von 62 K aufweist und somit als Auswahlinstrument für stöchiometrische CuMnSb Proben dienen kann. Es wird angenommen, dass Mn-bezogene Defekte ursächlich für diese Beobachtungen sind. Die magnetische Charakterisierung der epitaktischen CuMnSb-Filme erfolgt mittels Magnetometrie. Das magnetische Verhalten ist mit dem des Volumenmaterials vergleichbar. Allerdings tritt in dünnen CuMnSb Filmen und/oder bei niedrigen Magnetfeldern eine zusätzliche komplexe magnetische Phase auf, die bisher noch nicht für CuMnSb beobachtet wurde. Es wird angenommen, dass diese magnetische Phase an der CuMnSb-Oberfläche lokalisiert ist und sowohl superparamagnetisches als auch Spin-Glas-artiges Verhalten zeigt. Der Exchange Bias Effekt von CuMnSb wird in Kombination mit verschiedenen Ferromagneten mit vertikaler und horizontaler remanenter Magnetisierung untersucht. Es wird gezeigt, dass der Exchange Bias Effekt nur in Kombination mit Ferromagneten mit horizontaler remanenter Magnetisierung beobachtet werden kann. Schließlich werden die ersten Versuche zum Wachstum von vollständig epitaktischen CuMnSb/NiMnSb-Heterostrukturen vorgestellt. Sowohl magnetische als auch strukturelle Untersuchungen mittels Sekundärionen-Massenspektrometrie weisen auf die Interdiffusion von Cu- und Ni-Atomen zwischen den beiden halb-Heusler Schichten hin. Der Exchange Bias Effekt kann an den CuMnSb/NiMnSb Heterostrukturen beobachtet werden. Ob dieser Exchange Bias Effekt auf Austauschwechselwirkungen zwischen den CuMnSb- und NiMnSb-Schichten oder auf ferromagnetische Einschlüsse in der antiferromagnetischen Schicht zurückzuführen ist, lässt sich nicht eindeutig feststellen. KW - Molekularstrahlepitaxie KW - Heuslersche Legierung KW - half-Heusler KW - Antiferromagnetikum KW - CuMnSb KW - Antiferromagnet KW - Heusler Y1 - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-322839 ER - TY - THES A1 - Kagerer, Philipp Thomas T1 - Two-Dimensional Ferromagnetism and Topology at the Surface of MnBi\(_2\)Te\(_4\) - Bi\(_2\)Te\(_3\) Heterostructures - MBE Growth, Magnetism and Electronic Properties T1 - Zweidimensionaler Ferromagnetismus und Topologie an der Oberfläche von MnBi\(_2\)Te\(_4\) - Bi\(_2\)Te\(_3\) Heterostrukturen - MBE Wachstum, Magnetismus und elektronische Eigenschaften N2 - In this thesis, a model system of a magnetic topological heterostructure is studied, namely a heterosystem consisting of a single ferromagnetic septuple-layer (SL) of \(MnBi_2Te_4\) on the surface of the three-dimensional topological insulator \(Bi_2Te_3\). Using MBE and developing a specialized experimental setup, the first part of this thesis deals with the growth of \(Bi_2Te_3\) and thin films of \(MnBi_2Te_4\) on \(BaF_2\)-substrates by the co-evaporation of its binary constituents. The structural analysis is conducted along several suitable probes such as X-ray diffraction (XRD, XRR), AFM and scanning tunnelling electron microscopy (STEM). It is furthermore found that the growth of a single septuple-layer of \(MnBi_2Te_4\) on the surface of \(Bi_2Te_3\) can be facilitated. By using X-ray absorption and circular magnetic dichroism (XAS, XMCD), the magnetic properties of \(MnBi_2Te_4\) are explored down to the monolayer limit. The layered nature of the vdW crystal and a strong uniaxial magnetocrystalline anisotropy establish stable out-of plane magnetic order at the surface of \(MnBi_2Te_4\), which is stable even down to the 2D limit. Pushing the material system to there, i.e. a single SL \(MnBi_2Te_4\) further allows to study the phase transition of this 2D ferromagnet and extract its critical behaviour with \(T_c \, = \, 14.89~k\) and \(\beta \, = \, 0.484\). Utilizing bulk crystals of the ferromagnetic \(Fe_3GeTe_2\) as substrate allows to influence, enhance and bias the magnetism in the single SL of \(MnBi_2Te_4\). By growing heterostructures of the type \(MnBi_2Te_4\) -- n layer \(Bi_2Te_3\) -- \(Fe_3GeTe_2\)for n between 0 and 2, it is shown, that a considerable magnetic coupling can be introduced between the \(MnBi_2Te_4\) top-layer and the substrate. Finally the interplay between topology and magnetism in the ferromagnetic extension is studied directly by angle-resolved photoemission spectroscopy. The heterostructure is found to host a linearly dispersing TSS at the centre of the Brillouin zone. Using low temperature and high-resolution ARPES a large magnetic gap opening of \(\sim\) 35 meV is found at the Dirac point of the TSS. By following its temperature evolution, it is apparent that the scaling behaviour coincides with the magnetic order parameter of the modified surface. N2 - In dieser Arbeit wird ein Modellsystem einer magnetischen topologischen Heterostruktur untersucht, genauer ein Heterosystem, das aus einer einzelnen ferromagnetischen Septupellage (SL) aus \(MnBi_2Te_4\) auf der Oberfläche des dreidimensionalen topologischen Isolators \(Bi_2Te_3\) besteht. Mittels MBE und eines eigens entwickelten Setups befasst sich der erste Teil mit dem Wachstum von \(Bi_2Te_3\) und \(MnBi_2Te_4\) auf \(BaF_2\)-Substraten durch die Ko-Verdampfung ihrer binären Bestandteile. Die Strukturanalyse wird mit Hilfe von Röntgenbeugung (XRD, XRR), AFM und Rastertunnel-Elektronenmikroskopie (STEM) durchgeführt. Darüber hinaus wird festgestellt, dass das Wachstum einer einzelnen SL von \(MnBi_2Te_4\) auf der Oberfläche von \(Bi_2Te_3\) möglich ist. Mit Hilfe von Röntgenabsorption und des zirkularen magnetischen Dichroismus (XAS, XMCD) werden die magnetischen Eigenschaften von \(MnBi_2Te_4\) bis zur Monolage untersucht. Die geschichtete Natur des vdW-Kristalls und eine starke uniaxiale magnetokristalline Anisotropie stabilisieren eine magnetische Ordnung an der Oberfläche von \(MnBi_2Te_4\), die sogar bis zum 2D-Limit stabil ist. Bei Betrachtung einer einzigen SL \(MnBi_2Te_4\), kann man den Phasenübergang dieses 2D-Ferromagneten weiter untersuchen und sein kritisches Verhalten mit \(T_c \, = \, 14,89~k\) und \(\beta \, = \, 0,484\) extrahieren. Die Verwendung von \(Fe_3GeTe_2\) als Substrat ermöglicht es, den Magnetismus in einzelnen SL von \(MnBi_2Te_4\) zu beeinflussen und zu verstärken. Durch Aufwachsen von Heterostrukturen des Typs \(MnBi_2Te_4\) -- n Schicht \(Bi_2Te_3\) -- \(Fe_3GeTe_2\) für n zwischen 0 und 2 wird gezeigt, dass eine beträchtliche magnetische Kopplung zwischen der \(MnBi_2Te_4\) Deckschicht und dem Substrat erreicht werden kann. Schließlich wird das Zusammenspiel zwischen Topologie und Magnetismus in dem System direkt durch winkelaufgelöstes ARPES untersucht. Die Heterostruktur weist einen linear dispergierendes TSS im Zentrum der Brillouin-Zone auf. In der Temperaturabhängigkeit wird eine große magnetische Lücke von \(\sim\) 35 meV am Dirac-Punkt des TSS gefunden, deren Skalierungsverhalten mit dem magnetischen Ordnungsparameter der modifizierten Oberfläche übereinstimmt. KW - Molekularstrahlepitaxie KW - ARPES KW - Magnetischer Röntgenzirkulardichroismus KW - Topologie KW - Magnetismus KW - Topological Insulator KW - Heterostructure Growth KW - Electronic Structure KW - Ferromagnetism Y1 - 2024 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-360121 ER -