TY - THES A1 - Delporte, Marc T1 - A phenomenological approach to the prediction of material behaviours during co-sintering N2 - This work deals with the sintering of multi-material composites. It aims at the establishment of an alternative to the existing complex models for sintering. The development of the associated experimental procedure is also included in this work. The developed material model must be able to predict (i) the sintering kinetics and (ii) the viscous moduli of a material. An experimental approach with free sintering and hot-forging measurements is favoured in this work. The prediction of the sintering kinetics is addressed with the construction of a map of sintering kinetics data: the Master Sintering Diagram (MSD). The MSD is based on a generalized equation for solid-state diffusion, thus is suitable for any thermal activated diffusion. The MSD allows the prediction of sintering kinetics for a large range of temperatures and external loads. A novel approach to the determination of the viscous moduli is developed in this work: the cyclic unloading method. It is a hot-forging measurement (sintering under uniaxial compression) where the applied load is released for short periods. The measurements are carried out with continuous heating, so that the viscous moduli are determined over large ranges of temperatures and densities. The advantage of this method is the measurement of the viscous moduli in anisotropic microstructures. The material model is validated in two steps. Firstly, the predictions of sintering kinetics with the MSD are compared with experimental results: changes of thermal profile and changes of load are predicted with a maximum deviation of 10%. Secondly, the experimentally determined viscous moduli are used for the prediction of a bi-layer curvature using models for warpage from literature. The prediction is qualitatively good for a maximum deviation of 27%. The study of a sintering glass-ceramic tape on a rigid substrate is presented. It shows that this co-sintering problem can be qualitatively investigated with requirement of the material model. The formation of anisotropy intrinsic to the hot-forging experiments is also reported in this work. It appears to be a important point to address in the future for a better understanding of the cosintering. N2 - Die vorliegende Arbeit behandelt das Thema Kosintern. Ziel ist, die bisher verwendeten komplexen Sintermodelle durch ein einfacheres Verfahren zu ersetzen. Zusätzlich wird ein Messverfahren entwickelt, um die zur Beschreibung des Kosinterns erforderlichen Messdaten zu erhalten. Der experimentelle Ansatz beinhaltet Sinterungen ohne Last sowie mit einachsiger Belastung. Das Verfahren ermöglicht die Vorhersage (i) der Sinterkinetik und (ii) der viskosen Moduli. Um den Sinterpfad von Grünkörpern vorhersagen zu können, wird ein Kennfeld verwendet: das Master Sintering Diagram (MSD). Das MSD wird durch eine allgemeine Gleichung für das Festphasensintern definiert und lässt sich damit für alle thermisch aktivierten Diffusionsmechanismen anwenden. Die Vorhersage gilt für breite Bereiche von Temperaturen und äußeren Lasten. Eine neuartige Messmethode für die Erfassung der viskosen Moduli wird in der Arbeit entwickelt: das cyclic unloading dilatometry. Sie besteht in Hot-forging Versuchen mit konstanter Last, bei denen die sinterenden Proben regelmäßig für kurz Zeit entlastet werden. Die Versuche werden mit konstanter Aufheizrampe durchgeführt, so dass die viskose Moduli für breite Bereiche von Temperaturen und Dichten erfasst werden. Ein Vorteil dieser Messmethode ist es, die viskosen Eigenschaften von anisotropen Materialien messen zu können. Das Vorhersageverfahren wird in zwei Schritten geprüft. Erstens werden Vorhersagen vom MSD mit experimentellen Daten verglichen: die maximale Abweichung bei Änderung der Temperaturrampe und der ¨außeren Last liegt bei 10%. Zweitens werden die viskose Moduli aus dem MSD zur Vorhersage der Krümmung eines Zweischicht-Systems verwendet. Dazu wird ein in der Literatur beschriebenes Modell verwendet. Die qualitative Vorhersage ist gut: die maximale Abweichung zur experimentellen Krümmung liegt bei 27%. Zusätzlich wird eine Studie über ein Zweischicht-System aus Glas und Keramik vorgestellt, bei dem die Keramik nicht sintert. Es wird gezeigt, dass dieser Fall ohne Hilfe des Sintermodells qualitativ verstanden werden kann. Die Entwicklung der Anisotropie in der Mikrostruktur der keramischen Grünkörper durch die anisotrope Last beim Sintern wird diskutiert. Das volle Verständnis der anisotropen Mikrostrukturentwicklung beim Sintern unter anisotropen Randbedingungen erfordert weitere Arbeiten. KW - Sintern KW - sintering KW - modelling KW - composites Y1 - 2009 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-44235 ER - TY - JOUR A1 - Borova, Solomiia A1 - Schlutt, Christine A1 - Nickel, Joachim A1 - Luxenhofer, Robert T1 - A Transient Initiator for Polypeptoids Postpolymerization α‐Functionalization via Activation of a Thioester Group JF - Macromolecular Chemistry and Physics N2 - Here, a postpolymerization modification method for an α-terminal functionalized poly-(N-methyl-glycine), also known as polysarcosine, is introduced. 4-(Methylthio)phenyl piperidine-4-carboxylate as an initiator for the ring-opening polymerization of N-methyl-glycine-N-carboxyanhydride followed by oxidation of the thioester group to yield an α-terminal reactive 4-(methylsulfonyl)phenyl piperidine-4-carboxylate polymer is utilized. This represents an activated carboxylic acid terminus, allowing straightforward modification with nucleophiles under mild reaction conditions and provides the possibility to introduce a wide variety of nucleophiles as exemplified using small molecules, fluorescent dyes, and model proteins. The new initiator yielded polymers with well-defined molar mass, low dispersity, and high end-group fidelity, as observed by gel permeation chromatography, nuclear magnetic resonance spectroscopy, and matrix-assisted laser desorption/ionization time-of-flight mass spectroscopy. The introduced method can be of great interest for bioconjugation, but requires optimization, especially for protein conjugation. KW - ring-opening polymerization KW - bioconjugation KW - functional initiators KW - polypeptoids KW - postpolymerization modification Y1 - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-257587 VL - 223 IS - 3 ER - TY - JOUR A1 - Hahn, Lukas A1 - Luxenhofer, Robert A1 - Helten, Holger A1 - Forster, Stefan A1 - Fritze, Lars A1 - Polzin, Lando A1 - Keßler, Larissa T1 - ABA Type Amphiphiles with Poly(2-benzhydryl-2-oxazine) Moieties: Synthesis, Characterization and Inverse Thermogelation JF - Macromolecular Chemistry and Physics N2 - Thermoresponsive polymers are frequently involved in the development of materials for various applications. Here, polymers containing poly(2- benzhydryl-2-oxazine) (pBhOzi) repeating units are described for the first time. The homopolymer pBhOzi and an ABA type amphiphile comprising two flanking hydrophilic A blocks of poly(2-methyl-2-oxazoline) (pMeOx) and the hydrophobic aromatic pBhOzi central B block (pMeOx-b-pBhOzi-b-pMeOx) are synthesized and the latter is shown to exhibit inverse thermogelling properties at concentrations of 20 wt.% in water. This behavior stands in contrast to a homologue ABA amphiphile consisting of a central poly(2-benzhydryl-2-oxazoline) block (pMeOx-b-pBhOx-b-pMeOx). No inverse thermogelling is observed with this polymer even at 25 wt.%. For 25 wt.% pMeOx-b-pBhOzi-b-pMeOx, a surprisingly high storage modulus of ≈22 kPa and high values for the yield and flow points of 480 Pa and 1.3 kPa are obtained. Exceeding the yield point, pronounced shear thinning is observed. Interestingly, only little difference between self-assemblies of pMeOx-b-pBhOzi-b-pMeOx and pMeOx-b-pBhOx-b-pMeOx is observed by dynamic light scattering while transmission electron microscopy images suggest that the micelles of pMeOx-b-pBhOzi-b-pMeOx interact through their hydrophilic coronas, which is probably decisive for the gel formation. Overall, this study introduces new building blocks for poly(2-oxazoline) and poly(2-oxazine)-based self-assemblies, but additional studies will be needed to unravel the exact mechanism. KW - inverse thermogels KW - physical hydrogels KW - poly(2-oxazine) KW - poly(2- oxazoline) KW - self-assembly Y1 - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-265124 VL - 222 IS - 17 ER - TY - JOUR A1 - Schneider, Michael A1 - Tschöpe, André A1 - Hanselmann, Doris A1 - Ballweg, Thomas A1 - Gellermann, Carsten A1 - Franzreb, Matthias A1 - Mandel, Karl T1 - Adsorber Particles with Magnetically‐Supported Improved Electrochemical Conversion Behavior for Waste Water Treatment Processes JF - Particle & Particle Systems Characterization N2 - Micron‐sized supraparticles, consisting of a plurality of discrete nano‐ and microscale functional units, are assembled and fused by means of a droplet extrusion process. By combining nano magnetite, activated carbon, and conductive carbon with a polymeric binder matrix, particles are obtained which unite good magnetic properties, electrical conductivity, and adsorber activity through the high accessible surface area of the incorporated activated carbon of about 570 m\(^{2}\) g\(^{-1}\), thereby enabling a new approach toward sustainable water treatment processes. Due to the interplay of the components, it is possible to adsorb target substances, dissolved in the water which is demonstrated by the adsorption of the model dye methylene blue. A very fast adsorption kinetic and an adsorption capacity of about 400 mg g\(^{-1}\) is determined. By using the developed composite particles, it is also possible to electrochemically alter substances flowing through a magnetically‐stabilized fluidized‐bed reactor by electrochemically charging/discharging, significantly supported by the magnetic field enabling alternatingly optimum mobility/adsorption phases with contact/charging intervals. The electrochemical conversion can be increased up to 151% depending on the applied flow‐rate and electrical voltage. By applying an external magnetic field, a further increase of electrochemical conversion of up to 70% can be observed. KW - composite supraparticles KW - dye adsorption KW - electrochemical conversion KW - magnetic particles KW - water purification Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-214738 VL - 37 IS - 2 ER - TY - THES A1 - Mayer, Christian T1 - Alternative Keimbildner für transparente, farblose LAS-Glaskeramiken T1 - Nucleating agents for transparent, colorless LAS-glass ceramics N2 - In LAS-Glaskeramiken, die besondere Verbreitung bei Anwendungen als Kochfläche, Brandschutzglas und Bauteil für präzise Optik gefunden haben, werden vorrangig die Keimbildner TiO2 und ZrO2 eingesetzt. Transparente Glaskeramiken weisen jedoch eine mehr oder weniger starke Gelbfärbung auf, die vorrangig aus dem Einsatz von TiO2 zusammen mit unvermeidbaren Fe2O3-Verunreinigungen resultiert. Die Minimierung dieser Gelbfärbung gewinnt zunehmend an Bedeutung. Ziel der vorliegenden Arbeit ist die Prüfung, inwiefern die Verringerung der Eigenfarbe einer transparenten LAS-Glaskeramik durch Ersatz des färbenden Keimbildners TiO2 durch einen weniger färbenden Keimbildner möglich ist, ohne dass das gute Keimbildungsvermögen beeinträchtigt wird. Verschiedene alternative Keimbildner zu TiO2 wurden stets in Kombination mit ZrO2 hinsichtlich Keimbildungsvermögen und Färbung/Transmission untersucht sowie andere Kerneigenschaften im Vergleich zu der Standardkeimbildnerkombination TiO2/ZrO2 diskutiert. Signifikante Vorteile bzgl. Eigenfarbe und Transmission gegenüber dem TiO2/ZrO2-gekeimten Referenzmaterial konnten nur bei der Keimbildnerkombination SnO2/ZrO2 gefunden werden. Die Transmission ist mit 89% statt 87% beim Referenzmaterial höher, die Eigenfarbe ist mit dem Farbort a*/b* = -0,1/+2,3 deutlich näher am Unbuntpunkt als die Referenz a*/b* = -0,6/+5,1, der Yellowness Index reduziert sich von 9,5 auf 4,6. N2 - LAS-glass ceramics, which are widely-used as cooktop panels, fire protection glasses and precise optical devices, are commonly doped with TiO2 and ZrO2 as nucleating agents. Transparent glass ceramics show a more or less intense yellow coloring, which is mainly caused by the use of TiO2 together with unavoidable Fe2O3 contamination. The reduction of yellowness becomes more important. Object of the dissertation is the investigation, whether the yellowness could be reduced by substitution of the coloring TiO2 by a less coloring nucleating agent. Thereby, the nucleating power should be maintained. Several alternative nucleating agents have been tested regarding the nucleating power, coloring/transmission as well as other key properties. The second nucleating agent ZrO2 remained basically unchanged. The results have been compared with the commonly used nucleating agents TiO2 and ZrO2. Significant advantages concerning coloring and transmission have exclusively been found with the combination of SnO2 and ZrO2. The transmission of 89% is higher than reference of 87% and the coloring is definitely lower (a*/b* = -0.1/+2.3 instead of a*/b* = -0.6/+5.1), the yellowness index could be reduced from 9.5 down to 4.6. KW - Glaskeramik KW - Keimbildung KW - Glaskeramik KW - Keimbildner KW - glass ceramic KW - nucleating agents Y1 - 2006 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-19206 ER - TY - THES A1 - Mallak, Matthias T1 - Beschichtung planarer Substrate durch Flüssigphasenabscheidung von Titandioxid T1 - Liquid Phase Deposition of titanium dioxide for coating of planar substrates N2 - Es wurden planare Substrate mittels Flüssigphasenabscheidung mit Titandioxid beschichtet. Durch Absorption von Polyelektrolyten konnte die chemische Beschaffenheit der Substratoberfläche so verändert werden, daß die verwendbaren Substratmaterialien zur Beschichtung mit dem LPD-Verfahren um Glas, Polycarbonat, PET und Polyethylen erweitert wurden. Bedeutung kommt besonders der LPD-Beschichtung auf Borosilicatglas zu, da damit erstmalig ein Vergleich zwischen TiO2-Schichten aus der Flüssigphasenabscheidung und Schichten, die mittels Sol-Gel-Verfahren gewonnen wurden, möglich wurde. Der systematische Vergleich zwischen den Schichten der beiden Beschichtungsverfahren, ergab, daß Sol-Gel-Beschichtungen eine thermische Nachbehandlung mit Temperaturen größer 400°C benötigen, um ihre optimalen optischen und mechanischen Eigenschaften zu erreichen. Dabei tritt zwar eine starke Schrumpfung durch die Pyrolyse organischer Reste und Kristallisation auf. Jedoch führt diese Schrumpfung zu keiner Rißbildung oder Delaminierung. Im Gegenteil, die Ausbildung eines anorganischen Netzwerkes führt zum Aushärten der Schicht. Die bei höheren Temperaturen auftretende Kristallisation ermöglicht einen höheren Brechungsindex der Schicht bei gleichbleibend sehr guter Transparenz. Die bereits teilkristallin abgeschiedenen TiO2-Filme aus dem LPD-Verfahren schrumpfen zwar weit weniger stark als die Sol-Gel-Schichten, durch eine schlechte Haftung auf der Glasoberfläche verbreitern sich jedoch bereits vorhandene schmale Risse. Die Pyrolyse des Polyelektrolytlayers führt zum Verlust der haftvermittelnden Schicht und damit zu einem drastischen Rückgang der Schichthaftung und daraus bedingend der Bleistifthärte. Die Rißbildung verursacht einen starken Anstieg der Schichttrübung. Weiterhin verursacht die Rißverbreitung bei steigender Temperatur einen geringeren Brechzahlanstieg, als dies das LPD-Material ermöglichen würde. Durch diese Ergebnisse wird offensichtlich, daß für Substrate, die hohe Temperaturen ermöglichen, Sol-Gel-Beschichtungen dem LPD-Verfahren vorzuziehen ist. Für thermisch nicht belastbare Substrate stellt die Flüssigphasenabscheidung jedoch ein sehr gutes Beschichtungsverfahren dar. Um bestmögliche Ergebnisse mit dem LPD-Verfahren zu erzielen, kommt der Modifizierung der Substratoberfläche eine entscheiden Bedeutung zu. Zur bereits bekannten Oberflächenmodifizierung durch Ätzen mit Natriumperoxodisulfat (Hydroxylierung) wurde hierbei die zusätzliche bzw. alleinige Funktionalisierung durch Adsorption eines Polyelektrolytbilayers untersucht. Durch die Verwendung eines Polyelektrolytbilayers konnte die Dichte an Kristallisationsstellen im Vergleich zum unbehandelten bzw. hydroxylierten Substrat erhöht werden. Dies führte im Einklang mit dem bekannten Schichtwachstummodell zu gleichmäßigeren Beschichtungen. Der Einsatz des Polyelektrolytbilayers konnte in allen Fällen dazu genutzt werden, die Trübung der Schicht zu verringern. Dabei wurden Trübungswerte größer 50 % meist auf Werte von ca. 20 % und kleiner verbessert. Hohe Keimdichten bewirken dabei eine geringe Trübung. Jedoch konnte auch bei geringeren Keimdichten durch den Polyelektrolytbilayer geringe Trübungswerte erreicht werden. Bei der mechanischen Charakterisierung der TiO2-Schichten konnte festgestellt werden, daß bei den polymeren Substraten durch Hydroxylierung oder den Polyelektrolytbilayer die Schichthaftung verbessert werden. Eine Abhängigkeit der mechanischen Schichteigenschaften von der Substrathärt konnte mit Ausnahme des sehr weichen Polyethylens nicht gefunden werden. Jedoch ist für eine hohe Bleistifthärte eine gute Haftung nötig. Abriebuntersuchungen mit einem Filzstempel (Crockmetertest) zeigten ein analoges Verhalten zum Bleistifthärtetest. Um eventuell auftretende Nachteile der weichen Polymere ausgleichen zu können, wurden parallel Polystyrolsubstrate, beschichtet mit einer ORMOCER®-Hartschicht, untersucht. Dabei wurden sehr gute Ergebnisse in Hinblick auf Keimstellendichte, optische und mechanische Eigenschaften erzielt. N2 - Planar substrates were coated with titanium dioxide by liquid phase deposition. The chemical properties of substrate surface were changed through adsorption of polyelectrolytes, so that coating of glass, polycarbonate, PET and polyethylene with the LPD process could be done. Especially the LPD-Coating on borofloatglass is of importance. For the first time, a comparison between coatings from liquid phase deposition and coatings from sol-gel process became possible. The systematic comparison between the films of the two coating processes showed that sol-gel coatings need a thermal treatment at temperature above 400 °C to unfold their optimal optical and mechanical properties. Thereby a high shrinkage caused by pyrolysis of organic residues and crystrallisation occurs. But that shrinkage does not lead to formation of cracks or delamination. In Contrast, the formation of a inorganic backbone leads to a hardening of the film. At higher temperature emerging crystallisation enables a higher refractive index with constant very good transparency. The partially crystalline films from the LPD-process shrink much less than the sol-gel films. But caused by a bad adhesion on the glass surface small cracks get broadened. Pyrolysis of polyelectrolytes leads to a loss of the bonding agent and associated with that to dramatic decrease in adhesion and pencil hardness. The formation of cracks causes an high increase in the haze of the film. The broadening of cracks at rising temperature avoids a higher increase in refractive index as could be possible from the LPD-material properties. These results reveal that for substrates tolerating high temperatures sol-gel-coating is preferable to the LPD-process. For thermal non-stable substrates the liquid phase deposition is a very suitable coating technique. To achieve best possible results with the LPD-Process, the modification of the substrate surface is of importance. Beside the already known surface modification through etching with sodium peroxodisulfate (hydroxylation) the additional or exclusive surfacemodification through of adsorption a polyelectrolytebilayer was investigated. By the application of a polyelectrolytebilayer the density of nucleation sites could be increased in comparison with the untreated or hydroxylated substrate. This leads in consistence with the known film formation model to more homogeneous coatings. In general the application of the polyelectrolytebilayer reduced the haze of the film. In most cases the haze was decreased from 50 % and higher to 20% and lower. High densities of nucleation sites effect a low haze. But using the polyelectrolytebilayer low haze could also achieved despite a low nuclei density. Based on the mechanical characterisation of the TiO2-films could be demonstrated that on polymeric substrates the adhesion increases if hydroxylation or polyelctrolytebilayers are used. A dependence of mechanical film properties on the hardness of the substrate could not be detected with the exception of the very soft polyethylene. For a high pencil hardness a high adhesion is the crucial factor . Abrasion test with a felt die (Crockmeter)showed an analogue behaviour as the pencil hardness test. To compensate potential disadvantages from the soft polymers, polystyrene substrates with a ORMOCER®-hardcover-film were examined. Films on these substrates showed very good results refering to the density of nucleation sites, optical and mechanical properties. KW - Anorganische Beschichtung KW - Beschichtung KW - Titandioxid KW - Polystyrol KW - Kunststoff KW - Biomimetik KW - Polyelektrolyt KW - Oberflächenfunktionalisierung KW - Layer-by-Layer-Verfahren KW - surface modification KW - layer-by-layer-process Y1 - 2006 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-25008 ER - TY - THES A1 - Kocic, Nikola T1 - Bestimmung des Keimbildungsexponenten für die Kristallisation von Polymeren durch nicht-isotherme DSC-Analysen T1 - Determination of the nucleation parameter for the crystallization of polymers by non-isothermal DSC-analysis N2 - Thermoplastische Kunststoffe (sog. Thermoplaste) lassen sich in einem be-stimmten Temperaturbereich beliebig oft schmelzen und in einer gewünschten Form erstarren. Grundvoraussetzung für eine bestimmte Anwendung eines thermoplastischen Bauteils sind die Gebrauchseigenschaften des Materials, die im Wesentlichen vom Ablauf der Erstarrung abhängen. Die Moleküle einiger Thermoplaste können bei der Erstarrung geordnete kristalline Bereiche bilden. Dies sind die sog. teilkristallinen Kunststoffe, deren Erstarrungsprozess Kristallisation genannt wird. Die dabei entstehenden Kristallstrukturen werden zusammen mit deren Charakteristiken allgemein als Morphologie der teilkristallinen Kunststoffe bezeichnet. Die Morphologie hat einen signifikanten Einfluss auf die mechanischen, thermischen und optischen Eigenschaften des Materials. Dementsprechend stellen Kenntnisse über die Kristallisation eine wertvolle Hilfe bei der Vorhersage der Gebrauchseigenschaften eines teilkristallinen Kunststoffs dar. Um die Kristallisation zu starten, muss zunächst eine Energiebarriere überwunden werden, die an erster Stelle vom molekularen Aufbau des Kunststoffs abhängt. Somit weisen beispielsweise Kunststoffe mit linearen, regelmäßigen Molekülen und kleinen Seitengruppen eine niedrigere Energiebarriere und aus diesem Grund eine starke Neigung zur Kristallisation auf. Einige Zusatzstoffe wie z. B. unterschiedliche Additive, Farbstoffe oder Füllstoffe können die Energiebarriere und infolgedessen die Kristallisation eines teilkristallinen Kunststoffs wesentlich beeinflussen. Das Ziel dieser Dissertation war es, ein bestehendes Kristallisationsmodell zu erweitern und es an gefüllte oder additivmodifizierte teilkristalline Kunststoffe anzupassen. Das erweiterte Modell soll die Ermittlung eines Kristallisationspa-rameters, des sog. Keimbildungsexponenten, eines gefüllten oder additivmodifizierten teilkristallinen Kunststoffs bei der nicht-isothermen Kristallisation ermöglichen. Der Keimbildungsexponent ist mit der erwähnten Energiebarriere eng verbunden und bestimmt somit den Ablauf des Kristallisationsprozesses bzw. die daraus folgende Morphologie. Ein wesentlicher Schwerpunkt der Arbeit lag darin, die vorgeschlagene Modellerweiterung bei verschiedenen Abkühlgeschwindigkeiten zu überprüfen. Im Anschluss sollten die Beziehungen zwischen den berechneten Keimbildungsexponenten und experimentell ermittelten me-chanischen Eigenschaften (E-Modul, Streckspannung und Schlagzähigkeit) überprüft werden. Für die Untersuchungen wurden drei verschiedene Polymersysteme verwendet: PP / Talkum, HDPE / Talkum sowie PA6 / Bentonit. Hierbei weist der Füllstoff eine stark positive, schwach positive bzw. inhibierende Wirkung auf die Kristallisation der entsprechenden Polymermatrix auf. Hinsichtlich reiner Polymere wurde eine gute Übereinstimmung zwischen den ermittelten und Literaturwerten des Keimbildungsexponenten festgestellt. Die Zugabe von positiv wirkendem Talkum in PP bzw. HDPE führt zu einer Abnah-me des Keimbildungsexponenten, was zu dickeren Kristallen des jeweiligen Kunststoffs führte. Im Gegensatz dazu bewirkte die Bentonitzugabe einen zu-nehmenden Keimbildungsexponenten, was anschließend dünnere PA6-Kristalle zur Folge hat. Die durchgeführten Untersuchungen zeigen außerdem, dass die Füllstoffpartikelgröße einen ausgeprägten Einfluss auf den ermittelten Keimbildungsexponenten hat. Weiterhin wurde festgestellt, dass der ermittelte Keimbildungsexponent durch die (DSC)-Abkühlgeschwindigkeit beeinflusst wird. Es wurde ferner gezeigt, dass sich dieser Einfluss ab einer bestimmten Abkühlgeschwindigkeit (20 K/min im Falle des PP und HDPE bzw. 15 K/min im Falle des PA6) nicht mehr ändert, was zu einem konstanten Keimbildungsexponenten führt. Um den Einfluss der Abkühlgeschwindigkeit auf die modellierte Größe zu berücksichtigen, sind weitere Untersuchungen nötig. Die Ergebnisse der Arbeit zeigen weiterhin, dass der berechnete Keimbildungsexponent mit den experimentell ermittelten Werten für E-Modul, Streckspannung und Charpy-Schlagzähigkeit bei talkumgefülltem PP gut korreliert. Solche Korrelationen wurden jedoch bei den HDPE- und PA6-Proben nicht gefunden. Der Grund hierfür könnte eine ausgeprägte Orientierung der HDPE-Makromoleküle bzw. ein starker mikromechanischer Effekt des exfolierten Bentonits sein. Diese Effekte konnten im Rahmen der Arbeiten bestätigt werden. Die in dieser Arbeit erzielten Ergebnisse zeigen, dass die vorgeschlagene Mo-dellerweiterung auch bei gefüllten oder additivmodifizierten Kunststoffen zufriedenstellende Resultate liefert. Die entsprechende Berechnung erfordert dabei lediglich eine DSC-Messung, was im Vergleich zum Stand der Technik in einen niedrigeren Messaufwand resultiert. Die vorliegende Arbeit liefert daher einen signifikanten Beitrag zur Erstellung des Zusammenhangs zwischen der Kristallisation, der Morphologie und dem mechanischen Verhalten von teilkristallinen Polymeren. N2 - Thermosoftening polymers, also called thermoplastics, can be repeatedly melt-ed and solidified into a desired shape in a certain temperature range. The basic requirements for a particular application of a thermoplastic component are its functional characteristics, which significantly depend on the solidification pro-cess. The molecules of some thermoplastics can form ordered crystalline regions during the solidification process. These are so-called semi-crystalline polymers, whose solidification process is called crystallization. The resulting crystal struc-ture elements, together with their properties, are commonly referred to as the morphology of semi-crystalline polymers. The morphology has a significant in-fluence on the mechanical, thermal and optical properties of the material. Ac-cordingly, knowledge about the crystallization is a valuable aid in predicting the final properties of a semi-crystalline polymer. In order for the crystallization to start, it is necessary for an activation energy barrier to be overcome. The activation energy barrier depends on the molecular structure of the polymer. Polymers with linear, regular molecules and small side groups possess a low activation energy barrier and therefore crystallize most easily. Some ingredients, such as various additives, pigments or fillers, can significantly affect the energy barrier and consequently the crystallization of a semi-crystalline polymer. The aim of this thesis was to extend an existing crystallization model and adapt it to filled or additive-modified semi-crystalline polymers. The extended model should allow the determination of a crystallization parameter, the so-called nu-cleation parameter of filled or additive-modified semi-crystalline polymers during non-isothermal crystallization. The nucleation parameter is closely connected with the activation energy barrier and thus determines the crystallization process and consequentially the resulting morphology. An important task in this work was to verify the proposed model extension for different cooling rates. In addition, the correlations of the calculated nucleation parameter with experimentally determined mechanical properties (Young’s modulus, yield stress and impact strength) are established and discussed. In this research, three different polymer systems were used: PP / talc, HDPE / talc and PA6 / bentonite. In these three materials, the filler has a strong positive, a weak (positive) and a negative influence on the crystallization of a given polymer, respectively. A good agreement between the values of the nucleation parameter determined in this work and those found in literature was obtained as regards pure poly-mers. The addition of positive-acting talc in PP and HDPE leads to a decreased nucleation parameter, resulting in an increase of the crystal thickness of PP and HDPE. By contrast, the addition of bentonite increases the nucleation parameter of PA6 and therefore leads to a decrease in the crystal thickness of PA6. It was also shown that the filler particle size has a significant influence on the nucleation parameter. Furthermore, it was shown that the DSC cooling rate up to a certain value (20 K/min as regards PP und HDPE i.e. 15 K/min regarding PA6) has an influence on the determined nucleation parameter. Afterwards, the nucleation parameter reaches a plateau and shows no further changes with the cooling rate. To be able to add the influence of the cooling rate into the model, further studies are needed. Furthermore, it was shown that the obtained nucleation parameters correlates well with the Young modulus, yield stress and impact strength as regards PP filled with talc. In contrast to PP, such correlations were not found for HDPE and PA6 samples. The possible reason for the absence of correlations could be the orientation of the HDPE molecules, i.e. the strong reinforcing effects of the intercalated bentonite in PA6. These effects were confirmed in the scope of the work. The results obtained in this work show that the proposed model extension is applicable as regards filled semi-crystalline polymers. In comparison to the state of the art, the proposed model extension requires only a single DSC-measurement resulting in a lower measuring expenditure. Therefore, the pre-sent work provides a significant contribution to establishing the mathematical relationship between the crystallization, morphology and the mechanical behavior of semi-crystalline polymers. KW - Kristallisation KW - Polymer KW - Morphologie KW - Polymere KW - Keimbildung KW - Kalorimetrie Y1 - 2014 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-113950 ER - TY - THES A1 - Belka, Janina T1 - Biomaterialien auf der Basis von Terpyridin-koordinierten Metallionen T1 - Biomaterials based on terpyridine-coordinated metal ions N2 - In der vorliegenden Arbeit wird der Einfluss von Metallkomplexverbindungen auf der Basis von monotopen und ditopen Terpyridin-Liganden auf Zellen behandelt. Es können mehrere Möglichkeiten aufgezeigt werden, wie MEPE als kontrollierte Freisetzungssysteme für Zel-lanwendungen eingesetzt werden können. Es werden 2D-Beschichtungen, 3D-Knochenzemente und Terpyridin funktionalisierte Alginate hergestellt. Es ist möglich, definier-te, homogene Fe-MEPE Schichten auf Borosilikatglas mithilfe der Layer by Layer Technik und mittels Tauschbeschichtung abzuscheiden. Um die Oberfläche und somit die Freisetzung von Metallionen zu erhöhen, werden zusätzlich poröse SiO2-Schichten hergestellt, welche mit Fe-MEPE infiltriert werden. Um die Anwendbarkeit von Metallkomplexverbindungen auf der Basis von monotopen und ditopen Terpyridin-Liganden als Knochenersatzmaterial zu testen werden Hydroxylapatit Knochenzemente synthetisiert. Ziel ist eine retardierende Freisetzung der Metallionen ohne Burst Effekt und ohne den Verlust der Druckstabilitäten der HA Zemen-te. Die Funktionalisierung von Alginat mit 1-Amino-5-(2,2ʹ:6ʹ,2ʹʹ-terpyrid-4ʹ-yl-oxy)pentan resultiert in Hydrogelen, welche ein anderes Gelierverhalten als das unfunktionalisierte Alginat zeigen. Zudem ist es möglich mit Fe(II)- /Ca(II)-Salzmischungen Hydrogele auszubilden. Die funktionalisierten Alginate sind zudem bioaktiv. Zum grundlegenden Verständnis der MEPE Zell Wechselwirkung werden zunächst Zytotoxo-zitätsuntersuchungen mittels WST-1 Test von L929 und C2C12-Zellen mit wässrigen M(II)MEPE Lösungen (Metallionen M= Fe(II), Co(II), Ni(II), Zn(II)) in einem Konzentrationsbe-reich von 1,56x10-11 bis 1,6x10-5 mol L-1 durchgeführt. Fe-MEPE zeigt im betrachteten Kon-zentrationsbereich keine zytotoxischen Eigenschaften auf die eingesetzte Fibroblastenzelllinie. Bei Konzentrationen über 1x10-6 mol L-1 Fe-MEPE sinkt die Mitochondrienaktivität der C2C12-Zellen auf 40%. Dagegen wirken Co- und Zn-MEPE ab einer Konzentration von 1x10-7 mol L-1 stark zytotoxisch auf L929 und C2C12-Zellen. Um selektiv die Differenzierung von C2C12, MG63, humanen mesenchymalen Stammzellen (hMSCs) und humanen Endothelzellen anzuregen, werden die Zellen auf den hergestellten 2D Beschichtungen ausgesät. Es kann gezeigt werden, dass Fe-MEPE die Proliferation zu-gunsten der Stoffwechselaktivität von C2C12, MG63-Zellen und hMSCs hemmt. Bei weiterer Betrachtung der spezifischen myogenen Differenzierungsmarker der C2C12-Zellen bzw. der spezifischen Gene der osteogenen Differenzierung (Osteocalcin und ALP) mithilfe qRT-PCR können erhebliche Stimulierungen auf der mRNA Basis detektiert werden. Auch auf enzymatischer Ebene zeigen Fe-MEPE modifizierte Oberflächen einen stimulierenden Effekt auf die Aktivität der alkalischen Phosphatase der MG63 Zelllinie und humaner mesenchyma-ler Stammzellen. Somit kann eine Stimulierung der myogenen Differenzierung von C2C12-Zellen, sowie oste-ogenen Differenzierung von MG63-Zellen und hMSCs mittels Fe-MEPE beschichteten Ober-flächen innerhalb von drei Tagen nachgewiesen werden. Die Ergebnisse zeigen, dass Fe-MEPE funktionalisierte Oberflächen als innovative Scaffolds für die Behandlung von Kno-chendefekten eingesetzt werden können. N2 - In this thesis the influence of metal complexes based on monotopic and ditopic terpyridine ligands on cells is discussed. There are several ways MEPE can be used as a controlled re-lease system for cell applications. 2D planar and porous coatings, 3D bone cements and ter-pyridine functionalised alginates are produced. It is possible to deposit defined, homogeneous Fe-MEPE layers on borosilicate glass using the layer by layer technique and by dip coating. In order to increase the surface and thus the release of metal ions, porous SiO2 layers are addi-tionally produced, which are infiltrated with Fe-MEPE. To test the applicability of monosubsti-tuted and ditopic terpyridine ligand metal complexes as bone substitutes, hydroxyapatite bone cements are synthesized. The intent is to release the metal ions without a burst effect and without losing the pressure stability of the HA cements. The functionalization of alginate with 1-amino-5-(2,2'-6',2'-terpyrid-4'-yl-oxy) pentane results in hydrogels which exhibit a different gelling behavior than the unfunctionalised alginate. It is possible to form hydrogels with aqueous Fe (II) / Ca (II) salt mixtures. The functionalized algi-nates are bioactive. To gain a basic understanding of the MEPE cell interaction, cytotoxicity studies are first per-formed by WST-1 assay of L929 and C2C12 cells with aqueous M (II) MEPE solutions (metal ions M = Fe (II), Co (II), Ni (II), Zn (II)) in a concentration range of 1.56 × 10 -11 to 1.6 × 10 -5 mole L-1. In the concentration range Fe-MEPE shows no cytotoxic properties on the fibroblast cell line. At concentrations above 1x10-6 mol L-1 Fe-MEPE the mitochondrial activity of C2C12 cells decreases to 40%. In contrast, Co and Zn MEPEs have a strong cytotoxic effect on L929 and C2C12 cells at a concentration of 1x10-7 mol L-1. C2C12, MG63, human mes-enchymal stem cells (hMSCs) and human endothelial cells are seeded on the prepared Fe-MEPE 2D coatings to selectively stimulate the differentiation. It can be shown that Fe-MEPE inhibits the proliferation in favor of the metabolic activity of C2C12, MG63 cells and hMSCs. Further consideration of the specific myogenic differentiation markers of the C2C12 cells or the specific genes of osteogenic differentiation (osteocalcin and ALP) by means of qRT-PCR, significant mRNA-based stimuli can be detected. Likewise on the enzymatic level, the Fe-MEPE modified surfaces have a stimulating effect on the alkaline phosphatase activity of the MG63 cell line and human mesenchymal stem cells. During 3 days Fe-MEPE stimulates my-ogenic differentiation of C2C12 cells as well as osteogenic differentiation of MG63 cells and hMSCs. Thus, the results indicate that Fe-MEPE functionalized surfaces may serve as inno-vative scaffold for the treatment of bone defects. KW - Biologisches Material KW - Terpyridin <2,2':6',2''-> KW - Terpyridinderivate <2,2':6',2''-> KW - Knochen KW - Biomaterial KW - Terpyridin Y1 - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-210659 ER - TY - JOUR A1 - Straßer, Marion A1 - Schrauth, Joachim H. X. A1 - Dembski, Sofia A1 - Haddad, Daniel A1 - Ahrens, Bernd A1 - Schweizer, Stefan A1 - Christ, Bastian A1 - Cubukova, Alevtina A1 - Metzger, Marco A1 - Walles, Heike A1 - Jakob, Peter M. A1 - Sextl, Gerhard T1 - Calcium fluoride based multifunctional nanoparticles for multimodal imaging JF - Beilstein Journal of Nanotechnology N2 - New multifunctional nanoparticles (NPs) that can be used as contrast agents (CA) in different imaging techniques, such as photoluminescence (PL) microscopy and magnetic resonance imaging (MRI), open new possibilities for medical imaging, e.g., in the fields of diagnostics or tissue characterization in regenerative medicine. The focus of this study is on the synthesis and characterization of CaF\(_{2}\):(Tb\(^{3+}\),Gd\(^{3+}\)) NPs. Fabricated in a wet-chemical procedure, the spherical NPs with a diameter of 5–10 nm show a crystalline structure. Simultaneous doping of the NPs with different lanthanide ions, leading to paramagnetism and fluorescence, makes them suitable for MR and PL imaging. Owing to the Gd\(^{3+}\) ions on the surface, the NPs reduce the MR T\(_{1}\) relaxation time constant as a function of their concentration. Thus, the NPs can be used as a MRI CA with a mean relaxivity of about r = 0.471 mL·mg\(^{−1}\)·s\(^{−1}\). Repeated MRI examinations of four different batches prove the reproducibility of the NP synthesis and determine the long-term stability of the CAs. No cytotoxicity of NP concentrations between 0.5 and 1 mg·mL\(^{−1}\) was observed after exposure to human dermal fibroblasts over 24 h. Overall this study shows, that the CaF\(_{2}\):(Tb\(^{3+}\),Gd\(^{3+}\)) NPs are suitable for medical imaging. KW - calcium fluoride nanoparticles KW - magnetic resonance imaging (MRI) KW - multifunctional nanoparticles KW - multimodal imaging KW - photoluminescence Y1 - 2017 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-170657 VL - 8 ER - TY - JOUR A1 - Emmert, M. A1 - Witzel, P. A1 - Heinrich, D. T1 - Challenges in tissue engineering - towards cell control inside artificial scaffolds JF - Soft Matter N2 - Control of living cells is vital for the survival of organisms. Each cell inside an organism is exposed to diverse external mechano-chemical cues, all coordinated in a spatio-temporal pattern triggering individual cell functions. This complex interplay between external chemical cues and mechanical 3D environments is translated into intracellular signaling loops. Here, we describe how external mechano-chemical cues control cell functions, especially cell migration, and influence intracellular information transport. In particular, this work focuses on the quantitative analysis of (1) intracellular vesicle transport to understand intracellular state changes in response to external cues, (2) cellular sensing of external chemotactic cues, and (3) the cells' ability to migrate in 3D structured environments, artificially fabricated to mimic the 3D environment of tissue in the human body. KW - chemotaxis KW - intracellular transport KW - cytoskeleton dynamics KW - adhesion KW - diffusion Y1 - 2016 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:bvb:20-opus-191341 VL - 12 IS - 19 ER -