The main focus of this work was to get a deeper understanding of the relationship between the structure of sol-gel films, their densification and their macroscopic cracking. First of all titania was chosen as model system. Therefore a synthesis route starting from the preparation of long-term stable amorphous redissoluble precursor powders based on acetylacetone as chelate ligand was utilized. The solubility and stability of the powders in various solvents can be determined by chemical synthesis and technological parameters. When dissolved in a solvent mixture of ethanol and 1,5-pentanediol, thin films can be easily prepared by dip-coating technique. Thereby the quality of the titania films enormously depends on the calcinations temperature and the solvent mixture is used. In order to investigate the influence of different solvents and solvent mixtures on the microstructure and densification of the precursors, the coating solutions were stripped off (sol powder) and analyzed as function of annealing temperature. It was pointed out that a high densification rate caused by the addition of 1,5-pentanediol, results in dense microstructure with trapped residual carbon. These impurities can retard the phase transformation of anatase to rutile. The analysis of so-called “film powders” scraped off multiple dip-coated substrates provides valuable information on the effect of air moisture and unidirectional densification during drying and aging on the structure of thin films. The high surface-to-volume ratio and access to air moisture determine the chemical composition of the as-prepared film, which controls shrinkage, crystallization and defect structure of the coatings. Further it was shown, that drying as a thin film results in the formation of closed pores and much denser microstructure than the respective sol powder. Without the addition of 1,5-pentanediol all –OEt moieties undergo hydrolysis reactions, which causes the formation of a rigid network. The presence of 1,5-pentanediol retards this hydrolysis reactions and provides some network plasticity. Generally the microstructure of thin films is comparatively close to the microstructure of the film powders. The addition of 1,5-pentandiol prevents hydrolysis and condensation reactions as like in the film powders. However even at 700 °C, thin films never transform to rutile, which was attributed to the tensile stresses in thin films. In thin films and in film powders as well a comparable amount of closed pores are formed during annealing. Further it was shown that most of the thin sol-gel films investigated form a dense crust on their tops during annealing. This explains why crack free films exhibit only closed pores. However, when cracks appear during thin film shrinkage in the coating, this crust is burst, which generates open porosity. The defect density in the coatings was determined by an automated analysis of surface images. The crack formation and quantity can be directly referred to tensile stresses in the coatings, which arise from hydrolysis and condensation during thin film drying and aging. Therefore when 1,5-pentanediol is added to the sol, thin film cracking was avoided, because hydrolysis and condensation reactions are retarded, which preserves a higher network flexibility. Furthermore the crack formation was significantly influenced by the atmospheric humidity that was used during the coating process, which was explained by different drying and condensation rates. Under certain chemical starting conditions water soluble precursor powders can be also obtained. In general the observations made with the water based coating solutions are mostly in agreement with the former results based on ethanol based coating solutions. For example the high surface-to-volume ratio of film powders compared to sol powders also significantly enhances film drying and densification. The addition of 1,5-pentanediol also clearly contributes to their densification behavior and phase evolution. As seen before in the case of ethanol based coatings, 1,5-pentanediol enhances the stability towards hydrolysis and condensation reactions and preserves some network plasticity. Therefore coatings prepared without the addition of 1,5-pentanediol already form cracks during film drying and aging because of tensile stresses. Thus, the addition of 1,5-pentanediol results in a reduction/prevention of crack formation. Nevertheless some differences were observed, i.e. the critical single coating film thickness of ethanol based coatings is nearly twice that of water based coatings. This was explained by the different surface tensions of the basis solvents, which during thin film drying causes significantly higher capillary forces and tensile stresses in water based coatings. When acetylacetone is replaced by triethanolamine as chelating ligand for titanium also re-dissolvable precursor powders can be synthesized. The film powders combine a high hydrolytic stability of the precursor with sufficient intermediate network flexibility. The different type of organics changes the drying and densification behavior: i.e. in contrast to film powders obtained from acetylacetone based precursor powders the structure of triethanolamine based film powders is unaffected by the thin film drying process. This high hydrolytic stability and plasticity of this precursor allows the preparation of defect free coatings up to single film thickness of 300 nm. However triethanolamine based thin films present at intermediary annealing temperatures a distinctively different microstructure compared to acetylacetone based films. The general validity of the conclusions was proved on the basis of zirconia coatings that were also prepared by the use of re-dissolvable precursor powders. In principle all conclusions concerning the interconnection of precursor chemistry, film formation, densification and structure were transferable to the respective zirconia coatings. Differences mainly arise only from differential material properties i.e. bulk density. Finally, it has been pointed out that the findings obtained on the densification behavior of thinsol-gel films are also a valuable tool for improved explanations of other important scientific questions concerning sol-gel films, i.e. scratch resistance of sol-gel coatings, fiber -bridging and – degradation of sol-gel coated fibers.
Im Rahmen der vorliegenden Arbeit wurde untersucht, wie sich organisch polymerisierbare Titan(IV)- und Zirkonium(IV)komplexe, die bei der Synthese anorganisch-organischer Hybrid-polymere verwendet werden, in Precursor-Solen für anorganische Beschichtungen verhalten. Dabei sollte ein Konzept zur Herstellung photochemisch strukturierter, anorganischer Dünnschichten erarbeitet werden. Als Beispiel für das anorganische Dünnschichtmaterial wurde Bleizirkonattitanat (PZT) und für die polymerisierbaren Liganden Methacrylsäure gewählt. Der Schwerpunkt der Arbeit lag dabei besonders auf den Untersuchungen der photochemischen Polymerisation mittels UV-lithographischer und Mehrphotonenpolymerisation sowie der in situ Untersuchung während der Pyrolyse des polymerisierten Materials und der Reaktion zur anorganischen Dünnschicht.
Der Prozess zur Herstellung photostrukturierter, anorganischer Dünnschichten kann in zwei Schritte eingeteilt werden. Nach der Synthese des Precursor-Sols erfolgten zunächst die licht-induzierte organische Polymerisation und die Entfernung der nicht polymerisierten Bereiche mit Hilfe eines Entwicklerbads. Im Anschluss daran wurden im zweiten Schritt die organischen Bestandteile durch eine thermische Behandlung entfernt und die Reaktion zum anorganischen Oxidmaterial induziert. Die homogensten Schichten wurden dabei mit einem n Butanol-basierten, methacrylat¬funktionalisierten PZT-Sol mit 25 Gew. % Feststoffgehalt auf Stahlsubstraten bei Pyrolyse¬bedingungen ab 500 bis 700 °C mit einer Heizrate von 5 K/min erreicht. An diesen Schichten konnte ferroelektrisches Verhalten nachgewiesen werden. Allerdings reichen die Eigenschaften noch nicht an in der Literatur beschrieben ferro- und piezoelektrische Dünnschichten heran, die ebenfalls aus PZT-Solen hergestellt wurden. Dies liegt zum einen an den zu geringen Schichtdicken und der damit verbundenen erhöhten Durchschlagsgefahr dieser Sol-Gel-basierten PZT-Schichten. Zum anderen reduzieren Grenzflächenreaktionen des chromhaltigen Substrats und der PZT-Solschicht zu Pb2(CrO4)O sehr drastisch die ferroelektrischen Eigenschaften, indem sich nicht-ferroelelektrische Oxidschichten mit niedrigen Permittivitäten bilden und die Beweglichkeit der Domänenwände durch Diffusion von Cr3+-Akzeptorionen in die PZT-Schicht verringert wird.
Zunächst wurde die PZT-Solsynthese untersucht. Dabei konnte gezeigt werden, dass die Nebenproduktbildung von verschiedenen Estern vermieden werden kann, wenn die leicht flüchtigen Bestandteile nach der Ligandenaustauschreaktion von Alkoxid gegen Methacrylsäure bei reduziertem Druck und damit verbundenen niedrigeren Reaktionstemperaturen, erfolgte. Die Bindung der Methacrylatliganden ist in jedem Fall bidentat. Bei den n Butanol-basierten PZT-Solen konnte trotz höherer Siedetemperatur und niedrigerem Dampfdruck ein größerer Anteil an Alkohol entfernt werden, als bei n-Propanol-basierten PZT-Solen. Dies wurde auf den etwas höheren +I Effekt des n Butanols und in der Folge der bevorzugten Ligandenaustauschreaktion von Methacryl¬säure gegen den n Butanol im Vergleich zu n Propanol zurückgeführt. Die Größe der PZT-Cluster war langzeitstabil, reproduzierbar herstellbar und betrug ca. 2,0 – 2,5 nm. Aus der Partikelgröße und dem spektros¬kopischen Nachweis von Metalloxobindungen konnte ein Strukturvorschlag basierend auf den zugrundeliegenden Titan- und Zirkoniumkomplexen erstellt werden. Dabei bilden MO6 Komplexe das Grundgerüst stäbchenförmiger, heterometallischer Cluster. Die polymerisierbaren Methacrylatliganden befinden sich auf der Oberfläche und sind gut zugänglich für die Polymerisationsreaktion. Die mittlere Anzahl an Methacrylatliganden pro PZT-Cluster wurde zu 5 - 25 je nach Gewichtung abgeschätzt.
Bei der UV-lithographischen Strukturierung ergaben sich zwei unerwartete Effekte. Zum einen trat nach der Schichtherstellung eine reversible Trübung des PZT-Sols auf, welches auf konzentrations¬bedingte Phasenseparation zurückgeführt werden konnte. Zum anderen setzte sich unter N2 Atmosphäre die lichtinduzierte radikalische Kettenreaktion in den methacrylat-funktionalisierten PZT-Solschichten auch in die unbelichteten Bereiche fort. Dieser Effekt wird sonst in dieser Deutlichkeit nur von kationischen Polymerisationsreaktionen beobachtet und auf lange Radikal¬lebensdauern zurückgeführt und wurde mittels Photo-Differentialkalorimetrie weitergehend untersucht. Allerdings konnte aufgrund der Probengeometrie der Einfluss der Atmosphäre mit der Photo-DSC-Methode nicht eindeutig geklärt werden. Die Qualität der pyrolysierten PZT-Schichten konnte durch Variation der Feststoffgehalte und der Pyrolysebedingungen optimiert werden. So wurden durch die Verdünnung der PZT-Sole auf 25 Gew. % Feststoffgehalt bei ansonsten analogen Pyrolyse¬bedingungen dichtere und homogenere Schichten erhalten, wohingegen PZT-Solschichten mit einem Feststoffgehalt von 31 Gew.-% eine xerogelartige Struktur durch agglomerierte Partikel zeigten. Die untersuchten Substrate wiesen einen deutlichen Einfluss auf die nach der Pyrolyse erhaltenen PZT-Schichten auf.
Unmetallisierte Silizium-Wafer eigneten sich zwar zur Untersuchung der UV-lithographischen Herstellung strukturierter Solschichten, bei der Pyrolyse bildeten sich jedoch unerwünschte Bleisilicat¬schmelzen, die der PZT-Bildung entgegen wirkten. Weiterhin wurden platinierten Silizium-Wafer mit Titanhaftvermittler¬schicht und SiO2-Sperrschicht verwendet. Diese Substrate zeigten eine durch die hohen Pyrolyse¬temperaturen induzierten Diffusion der Haftvermittlerschicht in die Platinmetallisierung und in der Folge eine Delamination aufgrund hoher Druckspannung in der PZT-Schicht, welche durch die Entfernung der organischen Bestandteile aus der Solschicht resultierte. In der Folge entstanden mechanisch instabile Proben. Die Delamination konnte durch Zwischensinterschritte bei 360 °C bzw. durch die Pyrolyse auf Heizplatten reduziert, jedoch nicht vollständig vermieden werden. Aus diesem Grund konnten keine ferroelektrischen Eigenschaften der PZT-Schichten auf diesen Substraten ermittelt werden. Lediglich auf Stahlsubstraten konnten elektrisch dichte Schichten hergestellt werden.
Die Polymerisationsreaktion eines ausgesuchten PZT-Sols, welches bei den Strukturierungs- und Pyrolyseuntersuchungen die besten Ergebnisse zeigte, wurde näher untersucht, um ein Verständnis zu den ablaufenden Reaktionen zu erhalten. Die Reaktion zeigt den für radikalische Kettenpolymerisationen typischen Trommsdorf- bzw. Gel-Effekt. Durch die Verdünnung der PZT-Cluster konnten trotz hoher Anzahl an C=C-Bindungen pro Monomer, d. h. stark quervernetzender Spezies, sehr hohe Umsetzungsgrade erreicht werden. Die initiator¬gehalts-abhängige Steigerung der Reaktionsenthalpie während der Belichtung konnte mit steigenden Umsetzungs¬graden korreliert werden. Dieses Verhalten wird in der Literatur für eine Vielzahl an methacrylatbasierten Monomeren beschrieben. Der empirische Zusammenhang zwischen der Reaktionsrate und der Initiatorkonzentration konnte für das methacrylat¬funktionalisierte PZT-Sol zu bestimmt werden. Die Gesamtaktivierungenergie konnte ebenfalls in Abhängigkeit vom Reaktionsumsatz ermittelt werden. Die Polymerisation eines konzentrierten PZT-Sols mit difunktionellen Monomeren zeigte höhere Umsetzungsgrade als die entsprechenden Reinsubstanzen und ein späteres Eintreten des Gelpunkts. Dies wird zurückgeführt auf die niedrigere Viskosität sowie die geringere Molekülgröße des Reaktivverdünners und die in der Folge bessere Infiltration des durch das PZT-Sol aufgespannten Netzwerks mit zusätzlichen kleinen und beweglichen Monomeren.
Da bei der thermischen Behandlung der polymerisierten PZT-Schichten die experimentellen Bedingungen, wie z. B. Heizrate oder Anfangstemperatur der Pyrolyse, einen signifikanten Einfluss besitzen, wurden energiedispersive in-situ-Röntgenbeugungsexperimente mit Hilfe von Synchrotron¬strahlung durch¬geführt. Hierbei konnte vor allem der Einfluss der organischen Polymerisation und der Anfangstemperatur der Pyrolyse auf die Phasenentwicklung des Precursor-Sols untersucht werden. Dabei zeigte sich besonders deutlich, dass die PZT-Bildungstemperatur durch die Belichtung der Probe und damit der Bildung des organischen Netzwerks steigt. Dies wird auf das starke organische Netzwerk und den erhöhten Energiebedarf zur Reorganisation zurückgeführt. Durch eine erhöhte Anfangstemperatur der Pyrolyse von 500 °C kann die in der Literatur beschriebene Verringerung der unerwünschten Pyrochlor-Phase beobachtet werden. Zudem ist die PZT-Bildungstemperatur hierbei niedriger als bei Pyrolysen ab Raumtemperatur. Dies wird mit einer durch den geringeren Anteil an Pyrochlor-Phase erhöhten Triebkraft zur PZT-Bildung erklärt. Die konsekutive Phasenumwandlung von Pyrochlor in die erwünschte PZT-Phase ist bei Pyrolysen ab Raumtemperatur später abgeschlossen als bei Pyrolysen ab 500 °C. Dies kann mit dem geringeren Anteil an Pyrochlor-Phase erklärt werden, da sich ab 500 °C bereits die PZT-Phase zu bilden beginnt. Der Vergleich der Halbwertsbreiten des intensitätsstarken Reflexes bei 31 ° zeigte, dass die Belichtung der Solschichten zu größeren Kristalliten führt, was auf eine niedrigere Nukleationsrate während der Kristallisation zurückzuführen ist.
Bei der Auswertung und Diskussion der Ergebnisse der im Rahmen dieser Arbeit untersuchten Thematik ergaben sich einige Ansatzpunkte für weitere Untersuchungen, die jedoch nicht im zeitlichen und thematischen Rahmen dieser Arbeit betrachtet werden konnten. So wäre es interessant weitere Substrate auf ihre Eignung bei der, für die Herstellung strukturierten PZT-Schichten notwendigen, hohen thermischen Belastung zu testen, da die hier untersuchten platinierten Silizium-Wafer bzw. die Stahlsubstrate deutliche Nachteile zeigten. Des Weiteren können neben den hier behandelten polymerisierbaren Carbonsäureliganden weitere mehrzähnige Liganden und dessen Einfluss auf die Precursormaterialien für die Herstellung strukturierter anorganischer Schichten untersucht werden. β-Diketone, Aminoalkohole und auch Phosphonate bilden ebenfalls stabile Metall-Ligand-Bindungen und könnten so die Integration polymerisierbarer Gruppen in die PZT-Cluster analog zu der im Rahmen dieser Arbeit verwendeten Carbonsäure ermöglichen.
Das hier erarbeitete Konzept könnte neben den untersuchten ferroelektrischen Schichtmaterialien ebenfalls auf andere dielektrische oder magnetische Materialklassen, wie z. B. Bariumtitanat oder Magnetit übertragen werden. Die Herstellung photostrukturierbarer anorganischer Schichten durch den Einbau polymerisierbarer Liganden eignet sich für zahlreiche Materialklassen, die über flüssige Sol-Gel-Vorstufen synthetisiert werden können.
Darüber hinaus können weitere Pyrolysebedingungen mit den hier vorgestellten Analysemethoden untersucht werden. So könnten z. B. verschiedene Atmosphären oder unterschiedliche Heizraten innerhalb eines Pyrolysezyklus variiert werden, um ihren Einfluss auf die Herstellung rissfreier und phasenreiner Schichten zu untersuchen. Dazu müsste der hier vorgestellte experimentelle Aufbau dahingehend erweitert werden, dass eine Gaszufuhr während der Pyrolyse möglich ist.
The study of magnetic phases in spintronic materials is crucial to both our fundamental understanding of magnetic interactions and for finding new effects for future applications.
In this thesis, we study the basic electrical and magnetic transport properties of both epitaxially-grown MnSi thin films, a helimagnetic metal only starting to be developed within our group, and parabolic-doped ultra-thin (Ga,Mn)As layers for future studies and applications.
Das Mischkristallsystem PbZrxTi1-xO3 (PZT) gehört durch seine ausgeprägten piezo- und ferroelektrischen Eigenschaften zu den meist verwendeten Funktionskeramiken. In Form von Dünnschichten auf flexiblen Metallsubstraten können sie für unterschiedlichste Anwendungen als Tastschalter, Vibrationsdämpfer, Mikroaktuator oder Ultraschallwandler eingesetzt werden. Ziel der vorliegenden Arbeit ist es, den Gefügeaufbau und den Phasenbestand von PZT-Schichten, die in einem mehrstufigen Sol-Gel-Prozeß auf Blechen der säure- und temperaturbeständigen Chrom-Nickel-Legierung Hastelloy abgeschieden worden sind, zu analysieren und mit ihren ferroelektrischen und die-lektrischen Eigenschaften zu korrelieren. Es wird nachgewiesen, daß das Gefüge gezielt mittels verschiedener Temperaturbehandlungen und unter-schiedlicher Neodymdotierung variiert werden kann. Durch Nd-Dotierung wird das Maximum der Keimbil-dungsrate zu niedrigeren Temperaturen hin verschoben und die Wachstumsgeschwindigkeit gegenüber undotierten Schichten verringert. Die Kristallisation in dotierten und undotierten Schichten ist heterogen und erfolgt bevorzugt an den Grenz- und Oberflächen sowie an den Porenrändern im Innern der Schichten. Die Zusammensetzung der PZT-Sol-Gel-Beschichtungen liegt im Bereich der morphotropen Phasengrenze (x=0,53) zwischen tetragonaler und rhomboedrischer Phase. Erstmals wurde die während der Temperatur-behandlung auftretende Gradientenbildung im Zr/Ti-Verhältnis systematisch mit dem Gefüge und dem Phasenbestand auf Nanometerskala in Verbindung gesetzt. Hierbei konnte aufgezeigt werden, dass langreichweitige Zr:Ti-Fluktuationen vorrangig während der Kri-stallisation der Pyrochlorphase entstehen. Bei der nachfolgenden Perowskitkristallisation wachsen die Kri-stalle über die entmischten Bereiche hinweg, so daß Schwankungen im Zr:Ti-Verhältnis innerhalb der Kristallite erhalten bleiben. Es wird dargelegt, daß die Fluktuationen im Zr:Ti-Verhältnis infolge der starken Spannungen innerhalb der Schicht nur geringe Auswirkungen auf den Verzerrungsgrad der Kristallite und die Zugehörigkeit zur rhomboedrischen oder tetragonalen Perowskitphase haben. Beim Übergang in den ferroelektrischen Zustand ist das Ausmaß der Gitterverzerrung unabhängig von der Kristallitgröße und in Nd-dotierten Schichten generell geringer als in undotierten Schichten. Es wird die Ausbildung einer Zwischenschicht zwischen Metallsubstrat und PZT-Schicht untersucht, die die resultierenden elektrischen Eigenschaften maßgeblich beeinflußt. Sie wird als Oxidschicht identifiziert, be-stehend aus kristallinem NiO und NiCr2O4, verschiedenen Chromoxiden und Pb2(CrO4)O, die als nicht-ferroelektrisches Dielektrikum die resultierende Dielektrizitätskonstante des Substrat-Schichtverbundes stark herabsetzt. Durch Aufbringen einer unterstöchiometrischen La0,75Sr0,2MnO3 (ULSM) - Elektrodierung vor der PZT-Beschichtung gelingt es, die Kontaktierung zu verbessern, die (001)-Orientierung in undotierten Schichten zu steigern und sehr schmale P-E-Hysteresekurven zu erhalten.
In the framework of this thesis, the structural and electronic properties of bismuth and lead deposited on Ag(111) have been investigated by means of low-temperature scanning tunneling microscopy (LT-STM) and spectroscopy (STS).
Prior to spectroscopic investigations the growth characteristics have been investigated by means of STM and low energy electron diffraction (LEED) measurements. Submonolayer coverages as well as thick films have been investigated for both systems.
Subsequently the quantum well characteristics of thick Pb films on Ag(111) have been analyzed and the quantum well character could be proved up to layer thicknesses of N ≈ 100 ML. The observed characteristics in STS spectra were explained by a simple cosine Taylor expansion and an in-plane energy dispersion could be detected by means of quasi-particle interferences.
The main part of this work investigates the giant Rashba-type spin-split surface alloys of
(√3 × √3)Pb/Ag(111)R30◦ and (√3 × √3)Bi/Ag(111)R30◦. With STS experiments the band positions and splitting strengths of the unoccupied (√3 × √3)Pb/Ag(111)R30◦ band
dispersions could be resolved, which were unclear so far. The investigation by means of quasi-particle interferences resulted in the observation of several scattering events, which could be assigned as intra- and inter-band transitions.
The analysis of scattering channels within a simple spin-conservation–approach turned out to be incomplete and led to contradictions between experiment and theory. In this framework more sophisticated DFT calculations could resolve the apparent deviations by a complete treatment of scattering in spin-orbit–coupled materials, which allows for
constructive interferences in spin-flip scattering processes as long as the total momentum J_
is conserved.
In a similar way the band dispersion of (√3 × √3)Bi/Ag(111)R30◦ was investigated. The
STS spectra confirmed a hybridization gap opening between both Rashba-split bands and several intra- and inter-band scattering events could be observed in the complete energy range. The analysis within a spin-conservation–approach again turned out to be insufficient for explaining the observed scattering events in spin-orbit–coupled materials, which was confi by DFT calculations. Within these calculations an inter-band scattering event that has been identified as spin-conserving in the simple model could be assigned as a spin-flip scattering channel. This illustrates evidently how an incomplete description can lead to completely different indications.
The present work shows that different spectroscopic STM modes are able to shed light on Rashba-split surface states. Whereas STS allowed to determine band onsets and splitting strengths, quasi-particle interferences could shed light on the band dispersions. A very important finding of this work is that spin-flip scattering events may result in constructive interferences, an eff which has so far been overlooked in related publications. Additionally it has been found that STM measurements can not distinguish between spin-conserving scattering events or spin-flip scattering events, which prevents to give a definite conclusion on the spin polarization for systems with mixed orbital symmetries just from the observed scattering events.
Im Rahmen dieser Arbeit wurde eine neuartige Methode entwickelt, mit der es möglich ist, Magnetisierungsverläufe ausgewählter Schichten und Grenzflächen in dünnen Schichtsystemen zu bestimmen. Diese Resonante Magnetische Röntgenreflektometrie (XRMR: X-ray Resonant Magnetic Reflectometry) kombiniert die Methode der konventionellen Röntgenreflektometrie mit resonanten magnetischen Effekten, die an Absorptionskanten magnetischer Atome auftreten. Analog zur herkömmlichen Reflektometrie, die Aussagen über Schichtdicken und vertikale Grenzflächenrauhigkeiten zulässt, liefert die XRMR das tiefenabhängige magneto-optische Profil der untersuchten magnetischen Schicht. Durch die Aufnahme zweier Reflexionsspektren bei invertierter Helizität des einfallenden Röntgenstrahls oder Umkehr der Magnetisierungsrichtung der Probe in der Nähe der Absorptionskante eines magnetischen Elements erhält man als Messsignal das Asymmetrieverhältnis, das die Information über das tiefenabhängige Magnetisierungsprofil der untersuchten Schicht enthält. Zur Anpassung an die gemessene Asymmetrie über ein optisches Näherungsverfahren ist die Modellierung der optischen Konstanten der magnetischen Schicht oder Grenzfläche notwendig, die hierzu in viele dünne Einzelschichten künstlich aufgeteilt wird. Wichtig hierbei ist die korrekte Bestimmung der dispersiven und absorptiven Ladungsanteilen des komplexen Brechungsindex durch vorherige Messung des Absorptionskoeffizienten und der Berechnung der Dispersion über die Kramers-Kronig-Relation. XRMR-Experimente wurden an Pt/Co-Schichtsystemen an den Synchrotronstrahlungsquellen HASYLAB/Hamburg und BESSYII/Berlin durchgeführt, um die Anwendbarkeit der Messmethodik im harten und weichen Röntgenbereich zu demonstrieren. Durch die intrinsische Elementselektivität resonanter Streuung und die Verstärkung magnetischer Effekte durch Interferenzerscheinungen ist es möglich, Informationen über sehr kleine induzierte magnetische Momente an der Grenzfläche zu einer ferromagnetischen Schicht zu erhalten. Dies konnte bei der Untersuchung einer einzelnen Pt/Co-Bilage gezeigt werden, bei der das Magnetisierungsprofil der Pt-Schicht an der Pt/Co-Grenzfläche bestimmt wurde. Im Weiteren konnte durch XRMR-Messungen an einer Serie von einzelnen Pt/Co-Grenzübergängen das Zusammenspiel von chemischer Grenzflächenrauhigkeit und induziertem Pt-Magnetisierungsprofil untersucht werden. Wichtig war es, die Einsetzbarkeit der Methode im weichen Röntgenbereich zu zeigen, in dem die L2,3 Kanten der 3d-Übergangsmetalle liegen, die für den Magnetismus eine herausragende Rolle spielen. Hierbei konnte durch Messung an der Co-L3 Kante das Magnetisierungsprofil einer einzelnen Co-Schicht in einer Pt/Co/Cu-Trilage extrahiert werden. Des Weiteren erlaubt die Methode die Aufnahme elementspezifischer Hysteresekurven vergrabener dünner Schichten in Schichtsystemen mit hoher Qualität. Das Verfahren ist daher prädestiniert zur quantitativen Untersuchung von modernen neuen magnetoelektronischen Komponenten wie GMR- und TMR-Sensoren, MRAM’s oder Halbleiterstrukturen der viel versprechenden „Spintronic“. Es können bei derartigen Systemen Grenzflächenphänomene vergrabener Schichten zerstörungsfrei untersucht werden und im Weiteren auch Themen, die eher der Grundlagenforschung zuzuordnen sind, wie induzierter Grenzflächenmagnetismus oder auch oszillatorische Austauschkopplung in Zukunft quantitativ und elementselektiv behandelt werden.
Investigation of Intermolecular Interaction in Organic Thin Films by means of NEXAFS Spectroscopy
(2009)
The present work reports on the electron–vibron coupling in large organic molecules and particularly on the intermolecular interaction in molecular condensates. The optical and electrical properties of these organic systems are in the focus of attention due to their crucial importance for the development of (hybrid) organic electronic devices. In particular, the charge transport mechanism and hence the interaction between condensed molecules is a matter of debate [1–4]. In order to shed light on this interaction, the spectroscopic signatures of isolated molecules in the gas phase and their condensed counterparts have been studied. The applied technique, near–edge x–ray absorption fine structure (NEXAFS) spectroscopy, is a local probe with high chemical selectivity, well suited for the investigation of the electronic structure of molecular valence levels [5]. In the experimental part, the experimental set–up developed in this work is described with special attention to the characteristic issues of gas phase measurements, energy calibration and the subsequent data evaluation. The high quality gas phase and solid state NEXAFS spectra are analysed with respect to energy positions, shape and intensity of the sharp pi*–resonances characteristic for these aromatic molecules. Where applicable, a detailed Franck–Condon (FC) analysis of the vibronic fine structure has been performed, yielding additional information on the changes that occur upon solid state formation. Together with former results on vibrational features in large organic molecules, this information has been used to investigate the correlation of vibrational energies in the ground and electronically excited state. We find a relatively good agreement with other empirical studies on vibronic structures in photoelectron spectroscopy (PES) spectra of small molecules [6]. The molecular compounds investigated are in general believed to interact via weak van–der–Waals forces only. The present results however reveal distinct differences between the spectra of the gas and solid phase that can not be explained within the context of a mere interaction by dispersive forces. In detail, differential red–shifts of 0.1 to 0.3eV of transitions assigned to the aromatic system have been observed in the C–K spectra of benzene–tetracarboxylic acid dianhydride (BTCDA), 1,4,5,8–naphthalene–tetracarboxylic acid dianhydride (NTCDA), and 3,4,9,10–perylene–tetracarboxylic acid dianhydride (PTCDA) upon solid state formation. From BTCDA to PTCDA the shift increases, indicating an improving intermolecular interaction with molecular size or a closer molecular packing. In contrast, all transitions assigned to the anhydride carbon atom (C1) do not show any shift. For the O–K spectra, small changes in relative intensity have been observed for BTCDA and NTCDA. In case of PTCDA, a blue–shift of up to 0.2eV is evident for the OB 1sLEMO+1 transition. Theoretical models for the intermolecular interaction have been proposed in this work, based on a change of molecular geometry and interaction of adjacent molecules in the ground and excited state, respectively. While an interaction of adjacent molecular orbitals may explain the experimental findings for one particular molecule, this model falls short for a comprehensive explanation of all three dianhydrides. For an interaction in the excited state, the excitonic coupling with the neighbours attached at an angle, quantum chemical calculations yield no significant change in peak positions for NTCDA. Unfortunately, results for the stacked neighbours as well as the larger compound PTCDA are still lacking. For tris (8–quinolinol) aluminum (Alq3), the observed peak–shifts are restricted to just one unoccupied orbital, the LEMO+2, which is mainly localised at the phenoxide side of the quinolinol ligands. Although the shifts differ for the individual edges, the main interaction can therefore be assigned to this orbital. In summary, NEXAFS spectroscopy, if performed with great care in terms of experimental details and data analysis especially for the gas phase data, provides very detailed and highly interesting data on the changes of the electronic structure of organic molecules upon condensation. The present data can be applied as a reference for further experimental and (highly desired) theoretical investigations, which are needed for a comprehensive understanding of the complex interaction mechanisms between organic molecules.
The results of this thesis contribute to the understanding of the electronic properties of organic thin-films and interfaces. It is demonstrated that photoemission spectroscopy is very useful for studying surfaces and interfaces. Additionally it is shown, that many-body effects can be relevant for organic thin films, in particular at interfaces with strong interaction. These effects can have general implications for the material properties. In the first part of this thesis a systematic series of polyacene molecules is investigated with NEXAFS spectroscopy. The comparison of the data with core level and IPES data indicates that core excitations and core excitons need to be understood as many-body excitations. This finding implies for example that a high exciton binding energy is not necessarily associated with strong localization of the excited electron at the hole. As these effects apply also for valence excitons they can be relevant for the separation of charges and for the electron-hole recombination at interfaces. In the next chapter some fundamental effects in organic multilayer films and at organic-metal interfaces are studied with core level and NEXAFS spectroscopy. In this context a series of selected molecules is investigated, namely BTCDA, BTCDI, PTCDA and PTCDI. It is shown that in case of strong interface interaction a density of adsorbate-substrate states is formed which can lead to significant charge transfer satellites in the PES and NEXAFS spectra, similar to what is known for transition metal compounds. Moreover, it is demonstrated that the data can be modeled qualitatively by a basic approach which fuses the single impurity Anderson model with the description of charge transfer satellites by Sawatzky et al. This approach, which is equivalent to that of Gunnarsson and Schönhammer, allows even a relatively simple semi-quantitative analysis of the experimental data. The comparison of different adsorbate layers indicates that these many-body effects are particularly strong in case of partial occupation of the LUMO derived DOS. In the third part an organic multilayer film (SnPc), an organic-metal interface with strong coupling (SnPc/Ag) and an organic-organic interface (SnPc/PTCDA/Ag) are studied exemplarily with resonant Auger spectroscopy. The comparison of the data gives evidence for the contribution of many-body effects to the autoionization spectra. Furthermore, it is found that the electron-vibration coupling and the substrate-adsorbate charge transfer occurs on the time scale of the core hole life time. Moreover, the interaction at the organic-organic interface is weak, comparable to the intermolecular interaction in the multilayer films, despite a considerable rigid level shift for the SnPc layer. Furthermore, weak but significant electron-electron correlation is found for the molecular frontier orbitals, which are important for the substrate-adsorbate charge transfer. Therefore, these strongly coupled adsorbate films are briefly discussed within the context of the Hubbard model in the last part of this thesis. From the data derived in this work it can be estimated that such monolayer films are in the regime of medium correlations. Consequently one can expect for these adsorbate films properties which are related to the extraordinary behavior of strongly correlated materials, for which Mott metal-insulator transitions, sophisticated magnetic properties and superconductivity can be observed. Additionally some results from the investigation of alkyl/Si self-assembled monolayers are briefly discussed in the appendix. It is demonstrated exemplarily for the alkyl chains that the electronic band structure of short, finitely repeating units can be well modeled by a comparatively simple quantum well approach. In principle this approach can also be applied to higher dimensional systems, which makes it very useful for the description of E(k) relations in the regime of repeating units of intermediate length. Furthermore, the photoelectron and NEXAFS spectra indicate strong interaction at the alkyl/Si interface. It was found that the interface states can be modified by moderate x-ray irradiation, which changes the properties for charge transport through the SAM.
The approach of using the combination of Ultraviolet (UPS) and Inverse Photoemission (IPS) to determine the transport levels in thin films of organic semiconductors is the scope of this work. For this matter all influences on the peak position and width in Photoelectron Spectroscopy are discussed with a special focus on organic semiconductors. Many of these influences are shown with experimental results of the investigation of diindenoperylene on Ag(111). These findings are applied to inorganic semiconductors silicon in order to establish the use of UPS and IPS on a well-understood system. Finally, the method is used to determine the transport level of several organic semiconductors (PTCDA, Alq3, CuPc, DIP, PBI-H4) and the corresponding exciton binding energies are calculated by comparison to optical absorption data.
In summary, we have prepared single-wall carbon nanotube (SWNT) thin films by the method of evaporation-induced self-assembly (EISA). Using the scalable two-plate or lens setups, sorts of different film types or patterns of SWNTs has been successfully fabricated directly from the evaporation of solvents and could be precisely controlled by the concentrations of SWNT in ambient conditions. The special geometry of meniscus as the capillary bridge has not only given rise to a much higher efficiency of fabrication than what previously reported but also allowed us to monitor the pinning and depinning process carefully and further investigate the mechanism underlying the formation of different film morphologies.
In contrast with the conventional "stick-slip" model, we have provided the new dynamical pinning and zipping model for the contact line (CL) behavior. By analyzing the motion of CL and varying deposited patterns, the traditionally so-called "stick" state should be treated as a dynamical pinning process due to the interfacial tension contrast between SWNT-covered and bare silicon surface. Besides, the plausible one-step "slip" motion could be dominated by the zipping-like kink propagation.
In addition, the experiments with heated substrates at higher temperatures between 30°C and 50 °C have shown that the striped pattern could be fabricated by both much lower SWNT and SDS concentrations than that in room temperature, which is consistent with our model of interfacial tension contrast. In this situation, the deposition rate was increased but the quality of SWNT alignment was undermined because the corresponding moving velocity of SWNT was also too fast for SWNTs to rotate when the evaporative rate was high.
The similar results were identified by the SWNT/polymer conjugates dispersed in chloroform under the similar setups and other identical conditions. The typical breathing motion of dynamical pinning and zipping-like propagation for depinning were confirmed by the new suspensions despite that some morphological parameters changed dramatically compared with that from the aqueous solution. For example, the spacing between stripes reached 100 µm ~ 200 µm because the large contact angle contrast between HDMS- and SWNT-covered surface accompanies with the high evaporation rate of chloroform in the pinning and depinning process. Likewise the average CL velocity for fabrication reached around 20 µm/s due to the much higher evaporation rate of chloroform than water.
Using alike suspensions, the modified EISA method called dose-controlled floating evaporative self-assembly (DFES) was employed to implement the self-assembly of SWNTs on the water/air interface and then deposit them on solid substrate by directed floating. Although the stripes were fabricated successfully by drops with certain doses and SWNT concentrations, there inevitably existed randomly oriented SWNTs from the water surface that built networks between the stripes containing well-aligned tubes. In order to slow down the evaporation rate and monitor the process detailedly, we used chlorobenzene as the solvent instead of chloroform and find the typical pinning/depinning movement of the CL. A preliminary analysis of the results in terms of chlorobenzene implied that the CL possibly followed the similar pinning/depinning process in consistence with our model with capillary bridge.
In the last part of the thesis, the primary research on the optical properties of these stripes of ultrahigh purity semiconducting nanotubes was conducted by fluorescence microscopy and photoluminescence excitation (PLE) spectroscopy. The energy transfer of the photogenerated excitons was confirmed between different tube species with controlled band gaps.
In short, the experiments performed in this thesis allowed to gain new insights about the fabrication of large-area SWNT thin films by the cost-effective solution-processed method and most importantly to uncover its intrinsic mechanism as well. Combined with the separation and selection technique like density gradient centrifugation or polyfluorene derivatives assisted method, highly monodisperse semiconducting nanotubes could be deposited into organized, controllable and functional arrays.
Beyond the ambient conditions, precise control for the evaporation under preset temperature and vapor pressure could possibly extend the technique to the industry level. Assisted by some other mature techniques such as roll-to-roll printing, the cost-effective method could be widely used in the manufacture of various thin film devices. More complex 2D or even 3D structures could be designed and accomplished by the method for the functional or stretchable requirements. Further research on the fundamental exciton transition and diffusion in different networks or structures of SWNTs will be the significant precondition for the real applications.
Looking ahead, from the individual carbon nanotube to its thin film, this promising material with outstanding properties had many challenges to overcome before the real-world applications. Thanks to the availability of pure and well-defined materials, the scalable solution-processed approaches for fabrication of thin films should be able to unlock the potential of carbon nanotubes and exploit them in (opto-)electronic devices in the foreseeing future.