Refine
Is part of the Bibliography
- yes (413)
Year of publication
Document Type
- Doctoral Thesis (413) (remove)
Keywords
- Molekularstrahlepitaxie (32)
- Topologischer Isolator (32)
- Quantenpunkt (30)
- Kernspintomografie (28)
- Photoelektronenspektroskopie (23)
- Organischer Halbleiter (20)
- NMR-Tomographie (19)
- NMR-Bildgebung (18)
- Quecksilbertellurid (18)
- Halbleiter (16)
Institute
- Physikalisches Institut (413) (remove)
Sonstige beteiligte Institutionen
- Universitätsklinikum Würzburg (3)
- ATLAS Collaboration (1)
- Bayerisches Zentrum für Angewandte Energieforschung e.V. (1)
- Biomedizinische NMR Forschungs GmbH am Max-Planck-Institut fuer biophysikalische Chemie (1)
- CERN (1)
- CERN (Geneva, Switzerland) (1)
- Department of Cellular Therapies, University of Navarra, Pamplona, Spain (1)
- Department of X-ray Microscopy, University of Würzburg, Würzburg, Germany (1)
- Deutsches Zentrum für Herzinsuffizienz (1)
- Didaktik der Physik (1)
ResearcherID
- D-1250-2010 (1)
- N-7500-2014 (1)
The present thesis is concerned with molecular beam epitaxy of magnetite (Fe3O4) thin films on semiconducting substrates and the characterization of their structural, chemical, electronic, and magnetic properties. Magnetite films could successfully be grown on ZnO substrates with high structural quality and atomically abrupt interfaces. The films are structurally almost completely relaxed exhibiting nearly the same in-plane and out-of-plane lattice constants as in the bulk material. Films are phase-pure and show only small deviations from the ideal stoichiometry at the surface and in some cases at the interface. Growth proceeds via wetting layer plus island mode and results in a domain structure of the films. Upon coalescence of growing islands twin-boundaries (rotational twinning) and anti-phase boundaries are formed. The overall magnetization is nearly bulk-like, but shows a slower approach to saturation, which can be ascribed to the reduced magnetization at anti-phase boundaries. However, the surface magnetization which was probed by x-ray magnetic circular dichroism was significantly decreased and is ascribed to a magnetically inactive layer at the surface. Such a reduced surface magnetization was also observed for films grown on InAs and GaAs. Magnetite could also be grown with nearly ideal iron-oxygen stoichiometry on InAs substrates. However, interfacial reactions of InAs with oxygen occur and result in arsenic oxides and indium enrichment. The grown films are of polycrystalline nature. For the fabrication of Fe3O4/GaAs films, a postoxidation of epitaxial Fe films on GaAs was applied. Growth proceeds by a transformation of the topmost Fe layers into magnetite. Depending on specific growth conditions, an Fe layer of different thickness remains at the interface. The structural properties are improved in comparison with films on InAs, and the resulting films are well oriented along [001] in growth direction. The magnetic properties are influenced by the presence of the Fe interface layer as well. The saturation magnetization is increased and the approach to saturation is faster than for films on the other substrates. We argue that this is connected to a decreased density of anti-phase boundaries because of the special growth method. Interface phases, viz. arsenic and gallium oxides, are quantified and different growth conditions are compared with respect to the interface composition.
Als Tiermodell ist die Maus aus der pharmazeutischen Grundlagenforschung nicht mehr wegzudenken. Aus diesem Grund nimmt besonders die Verfügbarkeit nicht invasiver Diagnoseverfahren für dieses Tiermodell einen sehr hohen Stellenwert ein. Ziel dieser Arbeit war die Entwicklung von in vivo MR-Untersuchungsmethoden zur Charakterisierung des kardiovaskulären Systems der Maus. Neben der morphologischen Bildgebung wurde ein besonderer Schwerpunkt auf die Quantifizierung funktioneller Parameter der arteriellen Gefäße wie auch des Herzens gelegt. Durch Implementieren einer PC-Cine-Sequenz mit dreidimensionaler Bewegungskodierung war es möglich, die Charakteristik der Bewegung des gesamten Myokards zu untersuchen. Die Aufnahme von Bewegungsvektoren für jeden Bildpunkt und die Bestimmung des Torsionswinkels innerhalb der Messschichten konnte die systolische Kontraktion als dreidimensionale Wringbewegung des Herzens bestätigen. Um die Qualität der morphologischen Gefäßbildgebung zu verbessern, sollte untersucht werden, inwieweit bestehende Verfahren zur Gefäßwanddarstellung optimiert werden können. Implementieren einer Multi-Schicht-Multi-Spin-Echo-Sequenz an einem 17,6 Tesla Spektrometer erlaubte durch das hohe B0-Feld einen deutlichen Signalgewinn. Erstmals wurde es möglich, die gesunde Gefäßwand darzustellen und so morphologische Veränderungen in einem möglichst frühen Zustand zu untersuchen. Neben der Untersuchung morphologischer Veränderungen sollte vor allem ein Schwerpunkt auf das Studium funktioneller Parameter der Gefäßwand gelegt werden. Dazu wurde in einem ersten Schritt mit einem PC-Cine-Verfahren die Umfangsdehnung in ihrem zeitlichen Verlauf ermittelt. Dabei zeigte sich, dass im Laufe einer arteriosklerotischen Plaqueprogression eine Änderung der Umfangsdehnung vor einer Änderung morphologischer Parameter beobachtet werden kann. Deshalb war es Ziel, im Verlauf dieser Arbeit weitere Verfahren zur Charakterisierung funktioneller Parameter des Gefäßsystems zu entwickeln. Um direkt Elastizitätsparameter ermitteln zu können, fehlt als Bezugsgröße der arterielle Pulsdruck (AP). Die Lösung der inkompressiblen Navier-Stokes-Gleichungen unter Anwendung der Lang-Wellen-Näherung und der Näherung für große Pulswellengeschwindigkeiten (PWV) erlaubte die Bestimmung der komplexen Impedanz und somit des arteriellen Pulsdrucks in der Frequenzdomäne. Dadurch war es möglich, den dynamischen Anteil des arteriellen Druckpulses direkt aus einer Messung der Pulswellengeschwindigkeit sowie aus dem Verlauf des Flusspulses zu bestimmen. Zur Ermittlung des AP muss die Pulswellengeschwindigkeit bestimmt werden. Für die MR-Bildgebung in murinen Gefäßen waren hierzu bisher keine Verfahren verfügbar. Da sich die Gefäßdehnung möglicherweise als Indikator für eine frühe Wandveränderung bei der Plaqueprogression zeigt, bestand ein großes Interesse in der Untersuchung von spezifischen gefäßmechanischen Eigenschaften wie beispielsweise der PWV. Im Rahmen dieser Arbeit konnten zwei MR-Methoden für die nicht invasive Bildgebung in der Maus entwickelt werden, die es ermöglichten, die lokale und die regionale Pulswellengeschwindigkeit zu bestimmen. Die Messung der lokalen Pulswellengeschwindigkeit beruht dabei auf der zeitaufgelösten Bestimmung der Gefäßwanddehnung sowie des Blutvolumenflusses. Zur Bestimmung der regionalen Pulswellengeschwindigkeit wurde eine Erweiterung der Zwei-Punkt-Transit-Zeit-Methode verwendet. Durch zeitaufgelöste bewegungskodierte Bildgebung entlang der Aorta konnte anhand von 30 Stützpunkten die Propagation des arteriellen Flusspulses vermessen werden. Die Messzeit gegenüber einer Zwei-Punkt-Methode ließ sich dadurch halbieren. Gleichzeitig bietet die Auswertung von 30 Messpunkten eine größere Sicherheit in der Bestimmung der PWV. Beide Methoden wurden an einem elastischen Gefäßphantom validiert. In vivo Tierstudien an apoE(−/−)-Mäusen und einer Kontrollgruppe zeigten für beide Methoden eine gute Übereinstimmung. Darüber hinaus konnte ein Ansteigen der Pulswellengeschwindigkeit in apoE(−/−)-Mäusen durch arteriosklerotische Veränderungen nachgewiesen werden. Zusammenfassend wurden in dieser Arbeit grundlegende Verfahren zur Untersuchung des kardiovaskulären Systems der Maus optimiert und entwickelt. Die Vielseitigkeit der MR-Bildgebung ermöglichte dabei die Erfassung von morphologischen und funktionellen Parametern. In Kombination können die beschriebenen Methoden als hilfreiche Werkzeuge für die pharmakologische Grundlagenforschung zur Charakterisierung von Herz-Kreislauf-Erkankungen in Mausmodellen eingesetzt werden.
Röntgenstrukturuntersuchungen an spintronischen Halbleiter- und Halbmetall-Dünnschichtsystemen
(2010)
In dieser Arbeit wurden die strukturellen Eigenschaften von spintronischen Halbleiter- und Halbmetall-Dünnschichtsystemen untersucht. Mit Röntgenreflektivitätsmessungen konnten die Schichtdicken und Grenzflächenrauigkeiten der Mehrschichtsysteme sehr genau bestimmt werden. Hierfür wurde die Software Fewlay verwendet, welche den Parratt-Formalismus zur Berechnung der Reflektivität nutzt. An reziproken Gitterkarten, die an möglichst hoch indizierten Bragg-Reflexen gemessen wurden, konnte das Relaxationsverhalten der Schichtsysteme untersucht werden.
Eingebettet in ein Konzept zum Aufbau eines Hochleistungs-Feldeffekt-Transistors auf der Basis organischer Halbleiter (OFET), werden in der vorliegenden Dissertation fundamentale Aspekte des Aufbaus und der Funktion organischer Halbleiter-Bauelemente erforscht. Die Kenntnis, welche maximale Leistungsfähigkeit organische Halbleiter in OFETs prinzipiell erreichen können, ist von elementarem Interesse, sowohl um Transportmodelle zu verfeinern, als auch um Mechanismen und Optimierungsansätze zu finden, mit denen OFETs generell verbessert werden können. Es wird das Ziel verfolgt, sich der maximalen Leistungsfähigkeit eines gegebenen Materialsystems anzunähern. Aufwendige Präparationsstrategien werden für dieses Ziel bewusst in Kauf genommen, auch wenn deshalb vermutlich kein direkter Zugang zu Anwendungen eröffnet wird. An geeigneten Modellsystemen können einzelne wichtige Aspekte, wie die elektronische Struktur an Metallkontakten und im organischen Halbleitervolumen sowie das Wachstum von Schichten und Kristalliten organischer Halbleitermoleküle auf einkristallinen Isolatorsubstraten charakterisiert werden. Die Ergebnisse dieser grundlegenden Experimente fließen in den Aufbau des geplanten OFETs ein. Auf dem Weg zu einem funktionsfähigen Bauelement mit bestmöglichen Eigenschaften wurden wesentliche Fortschritte erzielt. Der erste Schwerpunkt dieser Arbeit ist die Untersuchung elektronischer Niveaus an Metallkontakt-Grenzflächen und im Volumen des Modellsystems PTCDA/Ag(111) mit Zwei-Photonen-Photoelektronenspektroskopie (2PPE). Die 2PPE-Spektren der PTCDA/Ag(111)-Grenzfläche sind dominiert durch einen unbesetzten, parallel zur Grenzfläche stark dispersiven Shockley-artigen Grenzflächenzustand (IS), der sich durch die Chemisorption der Moleküle auf der Ag(111)-Oberfläche bildet. Bei der Untersuchung von intramolekular angeregten elektronischen Zuständen von PTCDA mit 2PPE zeigen sich im Vergleich zum Untergrund der Spektren schwache Signale, die jedoch mit einer geeigneten Beschreibung des Untergrunds davon separiert werden können. Besonders interessant ist in diesem Zusammenhang das LUMO, das bei einer Anregung aus dem HOMO eine um 0,4 eV stärkere energetische Absenkung zeigt, als bei der Anregung aus dem HOMO-1. Dies kann durch die unterschiedlichen exzitonischen Zustände, die bei den Anregungen entstehen, erklärt werden. Neben den metallischen Kontakten ist die Grenzfläche zwischen organischem Halbleiter und Gate-Isolator entscheidend für die Leistungsfähigkeit eines OFETs. Am Beispiel des Wachstums von Diindenoperylen-Molekülen (DIP) auf einkristallinen Al2O3-Substraten wurde die morphologische und strukturelle Ausbildung von organischen Halbleiterschichten mit optischer Mikroskopie und Rasterkraftmikroskopie untersucht. Das Wachstum kann als stark anisotrop charakterisiert werden. Die – im Vergleich zu den Bindungsenergien mit dem Substrat – deutlich größeren Bindungsenergien innerhalb der DIP-(001)-Kristallebenen führen bei Substrattemperaturen von 440 K zu einem Wachstum von aufrecht stehenden Molekülen. Es zeigt sich, dass die während des Wachstums herrschende Substrattemperatur einen entscheidenden Einfluss auf die Morphologie der DIP-Schicht hat. So nimmt die Inselgröße von etwa 200 nm bei 350 K auf über 700 nm bei 450 K zu. Außerdem wird ein Ansteigen der Filmrauheit, besonders ab etwa 430 K, beobachtet, das auf den Übergang zu einem anderen Wachstumsmodus bei diesen Temperaturen hinweist. Bei etwas höheren Temperaturen von etwa 460 K wird das Wachstum von DIP-Kristalliten beobachtet. Dabei können – abhängig von den gewählten Präparationsparametern – drei unterschiedliche Kristallit-Typen unterschieden werden: „Mesa-Kristallite“ mit lateralen Abmessungen von mehreren Mikrometern, „Dendritische Kristallite“, die eine verzweigte Struktur aufweisen, die mithilfe der Wachstumskinetik erklärt werden kann und „Schichtkristallite“, deren Morphologie sich durch teilweise starke Krümmungen auszeichnet. Insgesamt zeigt sich, dass die Morphologie kristalliner Strukturen durch eine feine Balance der Präparationsparameter Substrattemperatur, Aufdampfrate, Substratmorphologie und Substratreinheit bestimmt wird, so dass kleine Änderungen dieser Parameter zu deutlich unterschiedlichen Kristallitformen führen. Schließlich wird das Konzept zum Aufbau eines Hochleistungs-OFET vorgestellt und in Details weiterentwickelt. Fortschritte werden in erster Linie bei der Präparation der Gate-Elektrode erzielt, die unter dem Al2O3-Substrat angebracht werden soll. Für die Ausdünnung des Substrats wird eine Bohrtechnik weiterentwickelt und mit einer nasschemischen Ätzmethode kombiniert, so dass Isolatorstärken von unter 10 µm erreicht werden können. Erste wenige OFETs wurden auf der Basis dieses Substrats präpariert, allerdings ohne dass die Bauteile Feldeffekte zeigten. Verbesserungsmöglichkeiten werden diskutiert.
In der vorliegenden Arbeit wurden alternative Phased-Array Konfigurationen untersucht, die eine gleichmäßige rÄaumliche Verteilung der Spulensensitivitäten für eine 2D parallel beschleunigte NMR-Bildgebung zur Verfügung stellen sowie eine höhere lokale Dichte probenrauschdominierter Einzelspulen als konventionelle Arraygeometrien ermöglichen. Hierzu wurde zunächst eine neuartige 16-Kanal Doppel-Spiral Arraygeometrie einem Birdcage-ähnlichen Spulenarray mit zwei Ringen aus je acht Spulenelementen gegenübergestellt, welches gewöhnlich in der klinischen Routine für NMR-Untersuchungen am menschlichen Kopf eingesetzt wird. Unter Verwendung analytischer Biot-Savart Berechnungen in der Entwicklungsumgebung Matlab konnten die jeweiligen Kodiereigenschaften sowie das mit den unterschiedlichen Arraykonfigurationen erzielbare intrinsische Signal-Rausch-Verhältnis ermittelt und verglichen werden. Zudem wurde auf gleiche Weise der Einfluss geometrischer Variationen im Aufbau des Doppel-Spiral Volumenarrays auf die intrinsische Isolation zwischen dem inneren, um +pi verdrehten und dem Äußeren, um -pi verdrehten Einfach-Spiral Spulenarray untersucht und Phased-Array Designs mit 32 unabhÄangigen Empfangselementen evaluiert. Im Rahmen einer experimentellen Evaluierung des Doppel-Spiral Arraykonzepts wurden zuerst einzelne Spulenelemente der unterschiedlichen 16-Kanal Volumenarrays verglichen, bevor eine Doppel-Spiral Phased-Array Prototypenspule aufgebaut wurde. Mit dieser konnten sowohl die vorausgesetzte intrinsische Entkopplung der zwei Einzel-Spiral Spulenarrays als auch die in alle drei Raumrichtungen homogene Verteilung der einzelnen Spulensensitivitäten anhand von Experimenten im NMR-System nachgewiesen werden. So war trotz der relativ geringen Anzahl von sechs unabhängigen Einzelkanälen eine um den Faktor 4 beschleunigte NMR-Untersuchung des menschlichen Kopfes mittels einer 3D MP-RAGE-Bildgebungssequenz möglich. Diese hohe Beschleunigung konnte für jede beliebige Orientierung der Kodierrichtungen in gleichermaßen guter Bildqualität erzielt werden und erwies sich somit als unabhängig von der gewünschten Positionierung des dreidimensionalen Untersuchungsvolumens. Das auf diese Weise bestätigte Konzept einer Doppel-Spiral Arraygeometrie stellt allerdings nicht nur eine gleichmäßige Sensitivitätsvariation entlang aller Raumrichtungen zur Verfügung, sondern ermöglicht auch eine höhere Dichte probenrauschdominierter Einzelspulen. In einem zweiten Ansatz wurde das Konzept räumlich kompakter Quadratur-Arrayelemente untersucht, die aus einer geeigneten geometrischen Kombination zweier Einzelspulen entstehen. Die Evaluierung der Leistungsfähigkeit einer derartigen Arrayelementkonfiguration erfolgte in diesem Fall durch den Vergleich einer aus vier Quadratur-Arrayelementen aufgebauten 8-Kanal Phased-Array Spule mit einem konventionellen 4-Kanal Spulenarray, welches sich aus vier waagrechten, in Reihen angeordneten Einzelspulen zusammensetzt. Die Kodiereigenschaften der jeweiligen Phased-Array Spulen sowie das zur Verfügung stehende intrinsische SNR wurden erneut mit Hilfe von Biot-Savart Simulationen in Matlab ermittelt. Diese zeigten, dass durch eine solche neuartige Elementkonfiguration eine Steigerung des erzielbaren Signal-Rausch-Verhältnisses von nahezu 30% erreicht werden kann. Zudem konnte eine deutliche Verbesserung der Kodiereigenschaften in Folge einer, bei gleicher Ausdehnung der Arraystruktur, verdoppelten Anzahl an Einzelspulen beobachtet werden. Eine experimentelle Untersuchung erfolgte anhand einer einfachen aus vier Quadratur-Arrayelementen aufgebauten 8-Kanal Phased-Array Spule. Mit dieser wurden im Kernspintomographen NMR-Untersuchungen an Phantomen durchgeführt, die den SNR-Gewinn sowie die signifikante Verbesserung der Kodiereigenschaften durch die Verwendung von Quadratur-Elementen in guter Übereinstimmung mit den Simulationsergebnissen bestätigen konnten. Eine derartige Steigerung der Leistungsfähigkeit eines gewöhnlichen, flachen Spulenarrays durch das Hinzufügen senkrechter, intrinsisch entkoppelter Spulenelemente zeigt sich auch in den Resultaten coronal und sagittal orientierter NMR-Bildgebungsuntersuchungen der Wirbelsäule eines gesunden Probanden. Hierbei sind selbst bei Beschleunigungen von einem Faktor 4 keine Artefakte aufgrund einer schlecht konditionierten parallelen Bildrekonstruktion zu beobachten.
Im Rahmen der Arbeit wurden Halbleiterlaser aus photonischen Kristallen (PK) im Wellenlängenbereich von 1,3 und 1,5 µm untersucht. Insbesondere die Integration der Laser mit weiteren Bauelementen für die optische Telekommunikation stand im Vordergrund der Untersuchungen. Neben den versch. Anwendungen unterscheidet sich auch das Grundmaterial. Der kurzwellige Bereich um 1,3 µm wurde auf GaAs-basierten Material bearbeitet, die langwelligen Laser wurden auf InP-Basis bearbeitet. Photonische Kristalle bestehen aus einer periodisch angeordneten Brechungsindexvariation zwischen Luftlöchern in einer Halbleitermatrixstruktur. Die Ausbreitung elektromagnetischer Wellen wird durch das periodische Potential beeinflusst und es können z. B. Spiegel hergestellt werden. Die Reflektivität kann durch Variation der PK-Struktur angepasst werden. Weiterhin können Liniendefekte als effektive Wellenleiter benutzt werden. Es wurden mehrstufige Y-Kombinierer zur Zusammenführung der Emission mehrerer Laser auf der komplett aktiven Laserstruktur hergestellt. Die Definition der Bauteile erfolgte durch optische bzw. Elektronenstrahllithographie, die Strukturierung wurde mittels nass- und trockenchemischer Ätzverfahren sichergestellt. Weiterhin wurden Stegwellenleiter basierte Mikrolaser auf GaInNAs-Material hergestellt. Um abstimmbare Laser mit einem möglichst grossen Abstimmbereich herzustellen, wurden zwei Resonatoren mit unterschiedlicher Länge hergestellt. Zwischen beide Resonatoren wurde ein PK-Spiegel aus 2 bzw. 3 Lochreihen prozessiert. Dies ermöglicht das Abstimmen der Laser von 1307 bis 1340 nm. Im weiteren Verlauf wurden aktive und passive PK-Strukturen auf GaAs-Basis integriert. Hierzu wurden DWELL-Strukturen auf Basis von InGaAs/GaAs Quantenpunkten verwendet. Durch das Ankoppeln der Glasfaser an die Frontfacette des Lasers ist der laterale Abstand der Laserstrukturen durch die Dicke der Glasfaser auf 250 µm festgelegt. Durch die verlustarme Kopplung mehrerer Laser in einen Auskoppelwellenleiter kann die Flächenausnutzung deutlich gesteigert werden. Im Rahmen der Arbeit wurden vier Halbleiterlaser über PK Wellenleiter miteinander verbunden. Die gezeigten Laserstrukturen weisen eine Länge von unter 1,5 mm bei einer Gesamtbreite von 160 µm auf. Dies bedeutet, dass ein komplettes Modul schmaler als eine Glasfaser realisiert werden kann. Es konnte gezeigt werden, dass alle 4 Laser unabhängig von einander wellenlängenstabil ansteuerbar und abstimmbar sind. Die Seitenmodenunterdrückung im parallelen cw-Betrieb aller vier Laser liegt für den Laser mit der geringsten Seitenmodenunterdrückung immer noch bei mehr als 20 dB und der Leistungsunterschied zwischen den vier Lasern ist unter 2,5 dB. Weiterhin wurden PK-Strukturen bei einer Wellenlänge von 1,5 µm auf einem InP-Basis untersucht. Im Bereich der passiven Charakterisierung wurden W3-Wellenleiter spektral vermessen. Zu Beginn wurde das sog. Ministopband (MSB) des W3-Wellenleiters untersucht, um im Anschluss die Kopplung von zwei Wellenleitern mit Hilfe des Übersprechens im Bereich des MSB´s zu analysieren. Hierzu wurden zwei W3-Wellenleiter parallel zueinander strukturiert. Im Wellenlängenbereich des MSB erfolgt eine Übertragung vom Referenz- in den Monitorkanal. Durch die geometrischen Parameter der PK-Strukturen kann die spektrale Lage und Breite des Filters eingestellt werden. Die Filterung durch Übersprechen vom Referenz- in den Monitorkanal ist mit einer spektralen Breite von mehr als 10 nm noch relativ breitbandig. Daher wurden PK-Resonatoren hergestellt. Hierzu wurden Spiegel in die Wellenleiter prozessiert. Es wurden Filter mit einer spektralen Breite von weniger als 0,5 nm und Güten von über 9000 erreicht. Im Anschluss wurden die aktiven und passiven Bauteile auf einem Chip integriert. Die Laser erreichten eine max. Leistung von 28 mW. Die Integration zusätzlicher Funktionen hinter den Laser bedeutet eine Erhöhung der Komplexität und des Funktionsumfangs, ohne die Emissionsleistung des Lasers zu senken. Zusätzlich vereinfacht sich der Aufbau zur Charakterisierung und zum Betrieb der Laser. In den gezeigten Bauteilen wurde die durch den Laserrückspiegel transmittierte Lichtmode mittels eines Tapers in einen PK Wellenleiter geführt. Seitlich und am Ende des Wellenleiters wurde die erreichte Intensität mittels zweier getrennter Photodioden (PD) gemessen. Damit wird das Konzept der passiv untersuchten Wellenleiter zusammen mit den Lasern integriert. Bei konstanter Leistung und Wellenlänge müssen die beiden Photoströme konstant sein. Durch die sehr kompakte Bauform am Ende des Lasers mit einer zusätzlichen Länge von weniger als 100 µm ist das Bauelement sehr Verlustarm. Ändert sich die Wellenlänge ungewollt, so ändert sich das Verhältnis der Ströme in den PD. Für die Charakterisierung des Wellenlängenmonitors beträgt der Abstimmbereich 30 nm.
In the frame of this thesis vibronic and electronic states of organic molecules have been examined. A central question is the interaction within and between the molecules in thin films and at metal-organic interfaces. The main experimental tools were high resolution electron energy loss spectroscopy (HREELS) and high resolution near edge X-ray absortion fine structure (NEXFAS). The electronic and vibronic structure of thin NTCDA films was examined with low energy electrons as probe, i.e. HREELS. The spectra of the electronic excited molecular orbitals of submonolayer NTCDA on a Ag(111) shows a partially filled orbital. The interaction between this orbital and the total symetric molecular vibrations leads to the typical Fano peak profiles which are seen in the vibrational spectra. The sub-monolayer superstructure can be driven to a phase transition into an disordered phase upon cooling, which is also seen in the electronic and vibronic excitation spectra. Multilayers show flat lying or upright standing molecules as a function of the preparation conditions. The upright standing molecules show an island growth mode, where the islands are well ordered and exhibit a structure in diffraction experiments which can be attributed to the molecular crystal structure. In order to examine the order in more detail various thin films were examined using SPALEED as function of film thickness and preparation parameters. In case of a low temperature substrate no long range order leading to a diffraction pattern was found. In contrast growth on room temperature substrates leads to island growth of films in a structure of the molecular crystal, where two preferred orientations of the islands relative to the substrate were found. In case of thick films the reference to the substrate gets lost and the molecular crystals grow with a defined crystal direction with respect to the surface but with an arbitrary azimuthal orientation leading to circles in the diffraction pattern. NTCDA monolayers on a Ag(111) surface using HREELS as a tool were examined. The electronic excitation spectra reveal a partially filled molecular orbital which is strongly shifted compared to the multilayer. The existence of this state is responsible for the activation of normally forbidden Ag modes in the vibrational spectra. Due to the electron phonon coupling these modes exhibit a Fano like peak shape. Cooling a monolayer leads to a phase transition with strong changes in the spectroscopic features both in electronic and vibronic excitations. In case of the molecule ANQ the intramolecular interaction was examined. In the oxygen NEXAFS spectra a vibronic fine structure is found, which leads to the conclusion that asymmetric potentials are involved. It is an interesting question if the fundamental vibration is has C-H or C=O character. In order to address this question spectra of condensed and gas phase ANQ were compared to an ANQ derivate (ANQ- Br$_2$Cl$_2$), with the conclusion that the coupling is most likely to a C=O mode. High resolution C1s spectra of hydrogenated and fully deuterated naphthalene both in gas and condensed phase have been presented. Depending on the final state orbital distinct differences have been found between gas and condensed phase. A energetic shift of resonances (Res. B, C, D) is interpreted as effect of $\pi$-$\pi$ interaction in the condensed phase. This is especially notable for resonance B which is undoubtly assigned to an excitation into a $\pi^*$ orbital. The results lead to an interpretation, that for organic molecular crystals more than pure van-derWaals interaction has to be taken into account. In summary it is found that the intramolecular interaction in NEXAFS spectra is preferentially coupled to one or a few vibronic progressions. Due to the delocalized electronic system maybe even states which are not spatially near the core excited atom can be involved. It could be shown that a condensation of the molecules in thin films leads to changes within the spectra. The influence the intermolecular interaction can be clearly seen in this finding, where additional hints are found that more than mere van-der-Waals binding has to be taken into account.
Gegenstand der vorliegenden Arbeit ist die thermische Charakterisierung des Einflusses von ausfrierenden Füllgasen auf die Wärmeleitfähigkeit von Wärmedämmstoffen für kryogene Anwendungen am Beispiel von Kohlenstoffdioxid. Im Allgemeinen wird mit dem Wärmedämmmaterial der Wärmeverlust eines Gegenstandes herabgesetzt, der eine Temperaturdifferenz im Vergleich zur Umgebung aufweist. Um die Gesamtwärmeleitfähigkeit eines Dämmstoffes bei kryogenen Temperaturen, d.h. < 200 K, zu minimieren, wird das meist poröse Dämmmaterial in der Regel hinreichend evakuiert, um die Gaswärmeleitfähigkeit zu unterdrücken. Zur Evakuierung gibt es mehrere Möglichkeiten. Meist wird der Gasdruck durch Abpumpen der Füllgase abgesenkt. In dieser Arbeit wird jedoch das Evakuieren durch „Ausfrieren“ des Füllgases bei tiefen Temperaturen (Desublimations-Evakuierung) realisiert und untersucht. Die Problemstellung der vorliegenden Arbeit bestand zum einen in der experimentellen Untersuchung des Wärmetransportes unter Berücksichtigung desublimierter Gase in porösen Dämmmaterialien mit verschiedensten Bulk-Strukturen und zum anderen in deren theoretischen Beschreibung. Aus technischen Gründen wurde mit LN2 als Kryogen und mit CO2 als Füllgas gearbeitet. Die erreichbaren Temperaturen erlauben die Verwendung von CO2 als Füllgas, da hier der Restgasdruck ausreichend niedrig ist, um bei den untersuchten Proben die Gaswärmeleitfähigkeit zu unterdrücken. Im Rahmen dieser Arbeit wurde eine neue Messmethode zur Charakterisierung des Einflusses von desublimierten Füllgasen auf die Festkörperwärmeleitfähigkeit entwickelt, da die genaue Kenntnis der effektiven Wärmeleitfähigkeit für viele technische Anwendungen unerlässlich ist. Hierzu wurde einer bestehenden Platten-Apparatur zur Wärmeleitfähigkeitsbestimmung ein spezieller Probenbehälter implementiert, welcher die Untersuchung verschiedenster Probenmaterialien erlaubt. Dieser Probenbehälter ermöglicht die Injektion eines Gases in einen porösen Prüfkörper, welchem eine Temperatur von 77 K auf der kalten Seite und 293 K auf der warmen Seite aufgeprägt wurde. Dieses weiterentwickelte stationäre Messverfahren erlaubt neben der Bestimmung der Gesamtwärmeleitfähigkeit der gesamten Probe durch die Einbringung zusätzlicher Temperatursensoren in verschieden Positionen des porösen Materials auch die Bestimmung der effektiven Gesamtwärmeleitfähigkeit einzelner Schichten. Um ein breites Spektrum an porösen Materialien in dieser Arbeit abzudecken und die im Rahmen dieser Arbeit entwickelten Theorien zu validieren, wurden verschiedene Materialklassen untersucht. Neben einem Melaminharz-Schaum mit Zellgrößen um 100 µm und einem Polyimid-Vlies mit einem effektiven Faserdurchmesser um 7 µm wurden zwei Pulverproben untersucht, zum einen eine Schüttung aus Vollglaskugeln mit Partikeldurchmessern zwischen 1 und 10 µm und eine Schüttung aus getrübter Kieselsäure mit wesentlich kleineren Primär-Partikeln (<10 nm). Die erarbeiteten theoretischen Modelle zur Berechnung der Festkörperwärmeleitfähigkeit lassen erwarten, dass die Empfindlichkeit der Festkörperwärmeleitfähigkeit gegenüber abgeschiedenen Gasen je nach Materialklasse unterschiedlich groß ausfällt. Als Hauptmerkmal wurde das Vorhandensein von Punktkontakten zwischen den einzelnen Partikeln bzw. Elementen des porösen Materials identifiziert, sowie die spezifische Wechselwirkung (CO2-phil/phob). Die Punktkontakte sind mit ihren großen thermischen Widerständen maßgeblich für die Wärmeleitfähigkeit der Festkörperstruktur verantwortlich. Durch Ausfrieren der Füllgase an diesen Punktkontakten werden die thermischen Kontaktwiderstände stark herabgesetzt, so dass ein Anstieg der Festkörperwärmeleitfähigkeit erfolgt. Dieser fällt abhängig vom jeweiligen Material unterschiedlich hoch aus. Die bestehenden Festkörperwärmeleitfähigkeitsmodelle wurden um den Einfluß von desublimierten Füllgasen erweitert, um diese mit den Wärmeleitfähigkeitsmessungen zu vergleichen und eine Aussage über den Abscheidemechanismus treffen zu können. Das erweiterte Festkörperwärmeleitfähigkeitsmodell für die Vollglaskugel-Schüttung hat z.B. eine sehr starke Abhängigkeit von der geometrischen Verteilung des abgeschiedenen Gases gezeigt. Eine Konzentration der im Mittel abgeschiedenen Füllgase am Kontaktpunkt zwischen zwei Partikeln einer einfachen kubischen Anordnung erhöht die Wärmeleitfähigkeit um mehr als 800%, wohingegen die homogene Abscheidung auf der Oberfläche nur zu einer moderaten Erhöhung um ca. 30% führt. Die experimentellen Versuche konnten die theoretisch erwarteten großen Anstiege der Festkörperwärmeleitfähigkeit für die Schüttungen mit einer großen Punktkontaktdichte bestätigen. Diesen folgt die Polyimid-Faser-Probe mit einer geringen Punktkontaktdichte. Der Melaminharz-Schaum hingegen besitzt keine Punktkontakte und ist CO2-phob. Erwartungsgemäß zeigt dieser eine sehr geringe Abhängigkeit in der Festkörperwärmeleitfähigkeit von der injizierten Gasmenge. Absolute Zahlenwerte der mittleren Gesamtwärmeleitfähigkeiten der untersuchten porösen Materialien lagen für die Randtemperaturen 77 K und 293 K für die Vollglaskugel-Schüttung bei ca. 12∙10^-3 W/(mK), für die getrübte Kieselsäure bei ca. 1.7∙10^-3 W/(mK), für die Polyimid-Fasern bei ca. 0.8∙10^-3 W/(mK) und für den Melaminharz-Schaum bei ca. 4.5∙10^-3 W/(mK). Im Rahmen der injizierten CO2-Menge wurden die mittleren Gesamtwärmeleitfähigkeiten bei der Vollglaskugel-Schüttung und der getrübten Kieselsäure um ca. 15% im Vergleich zum evakuierten Zustand (ohne desublimiertes Füllgas) erhöht. Die Polyimid-Fasern und der Melaminharz-Schaum wiesen eine Erhöhung um ca. 7% bzw. 2% auf. Die relative Vergrößerung der Gesamtwärmeleitfähigkeit im kältesten Viertel der Probe fiel prozentual wesentlich stärker aus: ca. 300% für die getrübte Kieselsäure, ca. 75% für die Vollglaskugel-Schüttung, ca. 40% für die Polyimid-Fasern und ca. 5% für den Melaninharz-Schaum. Die Korrelation der erarbeiteten Festkörperwärmeleitfähigkeitsmodelle mit den gemessenen Wärmeleitfähigkeiten bedurfte jedoch weiterer Eingangsparameter, um eine eindeutige Schlussfolgerung über den Anlagerungsmechanismus (Punktkontaktanlagerung oder homogene Oberflächenanlagerung oder eine Kombination aus beiden) treffen zu können. Die Bestimmung der zwingend benötigten absoluten CO2-Verteilung innerhalb der Probe wurde dazu exemplarisch mittels Neutronen-Radiographie an der Vollglaskugelprobe in einem speziellen Probenbehälter am Helmholtz-Zentrum Berlin (HZB) durchgeführt. Die so ermittelte CO2-Verteilung innerhalb der Vollglaskugelprobe war in sehr gutem Einklang mit den durchgeführten Monte-Carlo-Simulationen zum Desublimationsverhalten. Das erarbeitete Simulations-Programm beschreibt den molekularen Stofftransport innerhalb eines porösen Dämmmaterials mit ebenfalls 77 K auf der kalten Seite und 300 K auf der warmen Seite. Der Programm-Algorithmus berücksichtigt dabei die spezifischen Adsorptionsenergien, sowie die temperaturabhängige Frequenz mit der ein adsorbiertes Gasmolekül an der Oberfläche schwingt, welche umgekehrt proportional zur Haftzeit an einem Ort ist. Die Simulation liefert als Ergebnis die durchschnittliche Haftdauer eines Teilchens an einem Ort, welche wiederum proportional zur Verteilung vieler Gasmoleküle, in diesem Fall der injizierten und anschließend desublimierten Gasmenge, ist. Die Ergebnisse zeigen sehr deutlich die Abhängigkeit der durchschnittlichen Haftzeit von der Temperatur und der Adsorptionsenergie. Weitere Informationen zur Wechselwirkung der CO2-Moleküle mit den untersuchten Proben lieferten die Adsorptionsmessungen an den Proben mit CO2 als Adsorptiv bzw. Adsorbens nach den Methoden von Brunauer, Emmett und Teller (BET) und der Methode nach Dubinin-Radushkevich (DR). Durch Kombination bzw. Korrelation der verschiedenen Untersuchungsmethoden und den theoretischen Modellen konnte bestimmt werden, dass das CO2 fast ausschließlich als homogene Schicht auf der Oberfläche der Vollglaskugeln desublimiert, welche eine entsprechend geringe Temperatur aufweisen. Weiterhin stellte sich heraus, dass eine starke Konzentration an der kalten Seite stattfindet, die zur warmen Seite exponentiell abnimmt. Die Auswertung der Korrelation zeigt Tendenzen einer leicht bevorzugten Abscheidung am Kontaktpunkt bei weiteren injizierten CO2-Mengen in die bereits mit CO2 beladene Probe. Die Betrachtung und Diskussion der Messergebnisse und Festkörperwärmeleitfähigkeitsmodelle der Polyimid-Fasern und der getrübten Kieselsäure lässt auf ein ähnliches Verhalten bei Desublimation der Füllgase innerhalb des porösen Probenkörpers schließen. Die Empfindlichkeit des Wärmeleitfähigkeitsanstiegs gegenüber weiteren Mengen an desublimiertem CO2 nahm tendenziell zu. Eine Ausnahme stellte jedoch der Melaminharz-Schaum dar, welcher eine abnehmende Empfindlichkeit des Wärmeleitfähigkeitsanstiegs gegenüber weiteren Mengen an desublimiertem CO2 aufwies. Dafür verantwortlich sind das abstoßende Verhalten von CO2 gegenüber Melaminharz und die Festkörperstruktur des Schaums.
Within the framework of this thesis the mechanisms of growth and reorganisation of surfaces within the first few layers were investigated that are the basis for the fabrication of high quality thin films and interfaces. Two model systems, PTCDA/Ag(111) and CdSe/ZnSe quantum dots (QD), were chosen to study such processes in detail and to demonstrate the power and improvements of the aberration corrected spectromicroscope SMART [1] simultaneously. The measurements benefit especially from the enhanced transmission of the microscope and also from its improved resolution. SMART, the first double–aberration corrected instrument of its kind [2], provided comprehensive methods (LEEM/PEEM, μ–LEED, μ–XPS) to study in–situ and in real time the surface reorganisation and to determine morphology, local structure and local chemical composition of the resulting thin film. Complementarily, a commercial AFM [3] was used ex–situ. XPEEM and μ–XPS measurements were made possible by attaching SMART to the high flux density beamline of the soft–X–ray source BESSY–II [4]. PTCDA/Ag(111) – Growth and structure of the first two layers Although PTCDA/Ag(111) is one of the most intensely studied model systems for the growth of organic semiconductor thin films, it still offers new insights into a complex growth behaviour. This study enlightens the temperature dependant influence of morphological features as small as monatomic Ag steps on the growth process of the first two layers. At low temperatures, single Ag steps act as diffusion barriers. But interdiffusion was observed already for the 2nd layer whereas domain boundaries in the 1st PTCDA–layer persist for crystallite growth in the 2nd layer. 1st layer islands are more compact and the more dendritic development of the 2nd layer indicates reduced interaction strength between 2nd and 1st layer. These findings were explained by a model consisting of structural and potential barriers. The second part of the PTCDA study reveals a variety of phases that appears only if at least two layers are deposited. Besides the six known rotational domains of the interface system PTCDA/Ag(111) [5], a further manifold of structures was discovered. It does not only show a surprising striped image contrast, but the 2nd layer also grows in an elongated way along these so–called ’ripples’. The latter show a rather large period and were found in a wide temperature range. Additionally the μ-LEED pattern of such a domain shows a new super–superstructure as well. This phase is explained by a structural model that introduces a rotated, more relaxed domain in the 2nd layer that does not exist in the first layer. Its structural parameters are similar to those of the bulk unitcells of PTCDA. The model is confirmed by the observation of two different rotational domains that grow on top of one single ’substrate’ domain in the 1st layer. The orientations of the ripple phases fit as well to the predictions of the model. The growth direction along the ripples corresponds to the short diagonal of the super–superstructure unitcell with diamond–like shape. CdSe/ZnSe – Inverse structuring by sublimation of an α-Te cap With the second model system the formation of CdSe quantum dots (QD) from strained epi-layers was investigated. In this case the structures do not form during deposition, but rather during sublimation of the so–called ‘ignition cap’. For these pilot experiments not only the process of QD formation itself was of interest, but also the portability of the preparation and the prevention of contaminations. It was found that the α-Se is well suited for capping and the last step of the QD preparation, the sublimation of the α-Te cap, needs a sufficiently high rate in rise of temperature. Subsequently the cap, the process of desorption and the final surface with the quantum structures were investigated in detail. The cap was deposited by the MBE-group in Würzburg as an amorphous Te layer but was found to contain a variety of structures. Holes, cracks, and micro–crystallites within an α-Te matrix were identified. Sublimation of the “ignition cap” was observed in real–time. Thus the discovered cap-structures could be correlated with the newly formed features as, e.g., QDs on the bare CdSe surface. Since CdSe/ZnSe QDs prefer to form in the neighbourhood of the Te μ–crystallites, Te was found to play a major role in their formation process. Different explanations as the impact of Te as a surfactant, an enhanced mobility of adatoms or as stressor nuclei are discussed. The spectromicroscopic characterisation of the CdSe surface with QDs revealed the crystallographic directions. An increased Cd signal of the film was found at positions of former holes. Several possibilities as segregation or surface termination are reviewed, that might explain this slight Cd variation. Therewith, an important step to a detailed understanding of the complex reorganisation process in coating systems could be achieved.
Die in dieser Arbeit untersuchten Solarzellen auf Basis des Verbindungshalbleiters Cu(In,Ga)(S,Se)2 sind zur Zeit das vielversprechendste Materialsystem im Bereich der Dünnschichtfotovoltaik. Um damit möglichst hohe Wirkungsgrade zu erreichen, ist eine CdS–Pufferschicht notwendig, welche aufgrund ihrer Toxizität und des schlecht integrierbaren, nasschemischen Abscheideprozesses durch alternative Pufferschichten ersetzt werden soll. Im Rahmen dieser Arbeit wurden solche Cd–freien Pufferschichten in Chalkopyrit–Dünnschichtsolarzellen untersucht. Dabei wurde insbesondere deren Grenzfläche zum Absorber charakterisiert, da diese eine wesentliche Rolle beim Ladungsträgertransport spielt. Die hier untersuchten (Zn,Mg)O–Schichten stellen ein vielversprechendes Materialsystem für solche Cd–freien Pufferschichten dar. Durch den Einbau von Magnesium können die elektronischen Eigenschaften der eigentlichen ZnO–Schicht an den Absorber angepasst werden, was zu deutlich höheren Wirkungsgraden führt. Als Hauptgrund geht man dabei von einer besseren Leitungsbandanpassung an der Grenzfläche aus, welche allerdings bisher nur grob anhand der Position des Valenzbandmaximums an der Oberfläche und der optischen Volumenbandlücke abgeschätzt werden konnte. In dieser Arbeit wurde diese Grenzfläche daher mittels Photoelektronenspektroskopie und Inverser Photoelektronenspektroskopie untersucht, wobei durch die Kombination beider Methoden die Valenz– und Leitungsbandpositionen direkt bestimmt werden konnten. Es wurde gezeigt, dass der Bandverlauf an der Grenzfläche tatsächlich durch die Änderung des Mg–Gehalts der (Zn,Mg)O–Schichten optimiert werden kann, was eine wichtige Voraussetzung für einen möglichst verlustarmen Ladungstransport ist. Im Fall von reinem ZnO wurde ein „cliff“ (Stufe nach unten) beobachtet, welches mit steigendem Mg–Gehalt abnimmt schließlich ganz verschwindet. Die weitere Erhöhung des Mg–Gehalts führt zur Bildung eines „spike“ (Stufe nach oben). Dass es sich bei einer solchen Stufe nicht um die abrupte Änderung des Bandverlaufs an einer „idealen“, scharf definierten Grenzfläche handelt, haben die vorliegenden Untersuchungen der chemischen Struktur gezeigt. Infolge der dabei beobachteten Durchmischungseffekte bildet sich eine sehr komplexe Grenzfläche mit endlicher Breite aus. So wurde bei der Deposition der (Zn,Mg)O–Schichten die Bildung von In–O–Verbindungen an der Grenzfläche beobachtet. Im Fall von Zn konnte die Diffusion in den Absorber nachgewiesen werden, wodurch es dort zur Bildung von ZnS kommt. Im weiteren Verlauf dieser Arbeit wurde die Grenzfläche zwischen der (Zn,Mg)O–Pufferschicht und CuInS2–Absorbern untersucht. Durch ihre höhere Bandlücke im Vergleich zu den oben untersuchten Cu(In,Ga)(S,Se)2–Absorbern erhofft man sich eine höhere Leerlaufspannung und dadurch bessere Wirkungsgrade. Bisher liegt dieser Leistungsanstieg allerdings unter den zu erwartenden Werten, wofür eine schlechte Anpassung des Leitungsbandverlaufs an die herkömmliche CdS–Pufferschicht verantwortlich gemacht wird. Gerade für dieses Materialsystem scheint sich daher (Zn,Mg)O als Pufferschicht anzubieten, um die Bandanpassung an der Grenzfläche zu optimieren. Bei den in dieser Arbeit durchgeführten Untersuchungen an dieser Grenzfläche konnten ebenfalls Durchmischungsprozesse beobachtet werden. Zusätzlich wurde gezeigt, dass auch bei diesem Materialsystem der Bandverlauf an der Grenzfläche durch die Variation des Mg–Gehalts angepasst werden kann. Insgesamt konnte so für beide Absorbertypen ein detailliertes Bild der (Zn,Mg)O/Puffer–Grenzfläche gezeichnet werden. Für hinreichend gute Wirkungsgrade von Zellen mit „trocken“ abgeschiedenen Pufferschichten ist in den meisten Fällen eine zusätzliche, nasschemische Vorbehandlung des Absorbers notwendig, deren Einfluss auf die Absorberoberfläche ebenfalls in dieser Arbeit untersucht wurde. Dabei hat sich gezeigt, dass durch eine solche Behandlung das auf der Oberfläche angereicherte Natrium vollständig entfernt wird, was eine deutliche Steigerung desWirkungsgrades zur Folge hat.Weitere Untersuchungen führten zu dem Ergebnis, dass eine solche Reinigung der Absorberoberfläche auch durch den Prozess der Sputterdeposition selbst hervorgerufen werden kann. So kommt es neben der Ablagerung des Schichtmaterials zu deutlichem Materialabtrag von der Absorberoberfläche, wodurch diese von Adsorbaten und von auf der Oberfläche sitzenden Oxidverbindungen gereinigt wird. Untersuchungen an Absorbern, welche in einem Cd2+–haltigen Bad vorbehandelt wurden, haben gezeigt, dass der dabei abgeschiedene CdS/Cd(OH)2–Film ebenfalls fast vollständig während der Sputterdeposition entfernt wird. Abschließend wurden auf In2S3–basierende Pufferschichten charakterisiert, welche aufgrund ihrer bisher erreichten hohen Wirkungsgrade eine weitere Alternative zu CdS–Puffern darstellen. Hier wurde an der Grenzfläche zum Absorber eine starke Diffusion der Cu–Atome in die Pufferschicht hinein beobachtet, wodurch es zur Bildung von CuInS2–Phasen kommt. Messungen an bei verschiedenen Temperaturen abgeschiedenen Schichten haben gezeigt, dass diese Diffusion durch hohe Temperaturen zusätzlich verstärkt wird. Gleichzeitig konnte auch die Diffusion von Ga–Atomen nachgewiesen werden, welche allerdings wesentlich schwächer ausfällt. Analog zu den vorangegangenen Ergebnissen konnte somit auch bei diesem Materialsystem die Ausbildung einer sehr komplexen Grenzflächenstruktur beobachtet werden.