Refine
Has Fulltext
- yes (21)
Is part of the Bibliography
- yes (21)
Year of publication
Document Type
- Doctoral Thesis (21)
Keywords
- Polymere (6)
- 3D-Druck (4)
- Ringöffnungspolymerisation (4)
- Biomaterial (3)
- Hydrogel (3)
- ring-opening polymerization (3)
- Biofabrication (2)
- Lichtstreuung (2)
- Poly(2-oxazolin)e (2)
- Poly(2-oxazoline)s (2)
Institute
- Institut für Funktionsmaterialien und Biofabrikation (8)
- Graduate School of Science and Technology (7)
- Abteilung für Funktionswerkstoffe der Medizin und der Zahnheilkunde (4)
- Graduate School of Life Sciences (3)
- Fakultät für Chemie und Pharmazie (2)
- Institut für Anorganische Chemie (2)
- Institut für Pharmazie und Lebensmittelchemie (1)
- Medizinische Klinik und Poliklinik II (1)
- Physikalisches Institut (1)
Sonstige beteiligte Institutionen
Motivated by the perceived great potential of chiral polymers, the presented work aimed at the investigation of synthesis, solubility and optical activity of chiral poly(2,4-disubstituted-2-oxazoline)s. A novel polymeric carrier based on ABA-type triblock copolymers poly(2-oxazoline)s with chiral and racemic hydrophobic blocks was developed for the formulation of chiral and achiral drugs (Fig. 5.1). Poly(2-methyl-2-oxazoline) (pMeOx) was used as hydrophilic A block, and poly(2-ethyl-4-ethyl-2-oxazoline) (pEtEtOx) and poly(2-propyl-4-methyl-2-oxazoline) (pPrMeOx) were used as hydrophobic B blocks. Curcumin (CUR), paclitaxel (PTX) and chiral/racemic ibuprofen (R/S/RS-IBU) were applied as model drugs. Nanoformulations were prepared consisting of these triblock copolymers and model drugs. ...
Die vorliegende Arbeit befasst sich mit der Synthese und Charakterisierung von nanostrukturierten Mikropartikelpulvern mit einstellbarem Zerfalls- und Dispergierungsverhalten und deren Anwendung als verstärkender Füllstoff sowie deren Eignung für Sensoranwendungen. Sie ist in drei Teilbereiche gegliedert: Der erste Teil beschreibt die Synthese der nanostrukturierten Mikropartikelpulvern durch Sprühtrocknung von kolloidalen oxidischen (silicatischen und eisenoxidischen) Nanopartikeln. Es wird ausgeführt, wie durch Variation der Art und Größe der Primärpartikel und deren mengenanteiligen Kombination Mikropartikel unterschiedlichster nanostruktureller Maserung und Ausprägung erhalten wurden. Das Spektrum dieser Partikel reichte von homogen verteilten Strukturen bis hin zu Kern-Satellit-Struktur, von kontrollierter Aggregierung bis hin zur vollständigen Dispergierbarkeit. Im zweiten Teil der Arbeit wurden die Partikel im Hinblick auf ihre Eignung und Verwendung als Füllstoffe für Elastomer-Matrices untersucht. Im Fokus stand die Verstärkungswirkung und die Korrelation mit dem Dispergierverhalten in PDMS. Im dritten Teil der Arbeit wurde das Syntheseprinzip der Herstellung nanostrukturierter Mikropartikel auf Hydroxid-basierte Systeme wie LDHs erweitert. Teil I: Von Silica-NP zu nanostrukturierten Mikropartikeln mit einstellbarem Zerfallsverhalten Um nanostrukturierte Mikropartikel mit einem integrierten Zerfallsverhalten zu erzeugen, wurden zunächst kolloidale Silica-NP mit einer Größe von 20 nm abgestuft mit unterschiedlichen Mengen (0, 1/10, 1/5, 1/3, 1/2, 2/3, 1) eines hydrophobierend wirkenden Silans (Triethoxyoctylsilan, OCTEO) modifiziert. Neben den beiden Extremen der vollständigen und unmodifizierten Varianten (1 und 0) wurden teilweise modifizierte Zwischenstufen erhalten, indem die Silanmenge auf 2/3, 1/2, 1/3, 1/5 und 1/10 im Vergleich zu den vollmodifizierten Silica-NP verringert wurde. Die modifizierten Nanopartikel zeigten beim Dispergieren in verschiedenen Flüssigkeiten (Wasser, Toluol) eindeutige und graduell klar differenzierbare Unterschiede in Abhängigkeit vom Bedeckungsgrad der Partikeloberfläche mit dem Silan. Wie erwartet nahm das hydrophobe Verhalten der Nanopartikel mit zunehmendem Bedeckungs- und damit Modifizierungsgrad zu und die Nanopartikel waren in unpolaren Flüssigkeiten wie Toluol gut dispergierbar, während sie in polaren Flüssigkeiten wie Wasser zur Agglomeration und Sedimentation neigten. In einem nächsten Schritt wurden die zu unterschiedlichen Graden mit OCTEO modifizierten kolloidalen Silica-NP mittels Sprühtrocknung in mikroskalige Pulver überführt. Die nanostrukturierten Mikropartikelpulver wurden mit verschiedenen Analysemethoden wie REM-Aufnahmen, BET-, FTIR- und TG-Messungen untersucht, und die Eigenschaften der gebildeten Partikel charakterisiert. Die nanostrukturierten Mikropartikel zeigten auf den REM-Aufnahmen abhängig vom Modifizierungsgrad der Nanopartikel ein sehr unterschiedliches Aussehen. Während die Mikropartikel aus vollständig modifizierten Nanopartikeln eine eher raue Oberfläche besaßen, hatten die aus unmodifizierten Nanopartiklen gebildeten eine sehr glatte, kompakt erscheinende Oberfläche, was als Hinweis auf eine Kondensation und eine damit verbundene Aggregation der Nanopartikel gewertet wurde. Da sich diese Hypothese anhand der Aufnahmen aber nicht beweisen ließ, wurden in einer nächsten weiterführenden Testreihe Nano-Indenter-Experimente unter dem REM mit den aus voll- und unmodifizierten Nanopartikeln aufgebauten Mikropartikeln durchgeführt. Die Ergebnisse bestätigten den ersten Eindruck der REM-Aufnahmen insofern, als das sich die sehr kompakt wirkenden unmodifizierten Partikel nicht mit einer Wolfram-Spitze eindrücken ließen und damit die Hypothese mechanisch stabiler Aggregate untermauerten. Ganz anders verhielten sich die vollmodifizierten Partikel, die mithilfe der Wolfram-Spitze so eingedrückt werden konnten, dass die Nanopartikel aus dem Mikropartikelverbund herausgelöst wurden und teilweise vereinzelt vorlagen. Hier handelte es sich mit hoher Wahrscheinlichkeit um Agglomerate, die unter der Einwirkung einer Scherkraft wieder vereinzelt werden konnten. Da es mit mikroskopischen Verfahren wie REM nicht möglich war, unmittelbare Aussagen bezüglich der Wechselwirkung der Nanopartikel im Mikropartikel zu treffen, wurden zunächst die Oberflächeneigenschaften mittels BET-, FTIR- und TG-Messungen untersucht. Im Hinblick auf die spätere Anwendung war es sehr wichtig, die Oberflächeneigenschaften der Mikropartikel möglichst umfassend zu charakterisieren, da diese entscheidend zur Dispergierbarkeit der Partikel in einem Matrixsystem beitragen. Mithilfe der FTIR- und TG-Messungen konnte die Anwesenheit und Menge von Silan auf der Partikeloberfläche bestimmt werden. Es zeigte sich ein klarer Trend für die zu verschiedenen Graden mit OCTEO modifizierten Silica-NP. Mit zunehmender Silanmenge nahm sowohl die Intensität der FTIR-Bande für die CH2- und CH3-Streckschwingung als auch der Masseverlust zu. Im Gegensatz zu diesen Messungen zeigte sich bei den BET-Messungen kein klarer Trend in Abhängigkeit vom Bedeckungsgrad der Silica-NP. Die höchsten Werte für die spezifische Oberfläche hatten Mikropartikel, die aus 1/5- und 1/3-modifizierten Silica-NP bestanden. Eine schlüssige Erklärung wird darin gesehen, dass durch die Alkylgruppen auf der Oberfläche ein Kondensieren der Silica-NP weitestgehend verhindert wurde und gleichzeitig noch genügend Mikroporen vorhanden blieben, die mit den Stickstoffmolekülen wechselwirken konnten. Neben den Standard-Analysemethoden wurden Dispergierbarkeitsuntersuchungen durchgeführt sowie die Hansen-Dispergierbarkeitsparameter (HDP) und die ET (30)-Werte mit dem Reichardt-Farbstoff bestimmt. Anhand der Dispergierbarkeitsuntersuchungen konnten erste qualitative Aussagen getroffen werden, ob es sich um hydrophile oder hydrophobe Partikel handelt. Diese ersten Ergebnisse und Trends konnten anschließend mit den HDP und dem RD quantitativ untermauert werden. Die Polarität der Mikropartikel, die aus zu unterschiedlichen Graden mit OCTEO modifizierten Silica-NP aufgebaut waren, nahm mit zunehmender Oberflächenbedeckung ab. Dieser Trend korrelierte mit den aus den FTIR- und TG-Messungen erhaltenen Werten. Da es mit den Silica-basierten Mikropartikeln nicht möglich war, unmittelbare Aussagen zum Agglomerations- bzw. Aggregationsgrad der Nanopartikel im Mikropartikel zu treffen, wurde das Prinzip der Agglomerations/Aggregationssteuerung über Oberflächenmodifikation auf magnetische Nanopartikel übertragen und so ein Modell geschaffen, das die Wechselwirkung auf nanopartikulärer Ebene sichtbar und messbar macht. Diese Informationen zum Agglomerationsgrad der Nanopartikel lieferten wertvolle Hinweise im Hinblick auf die Dispergierbarkeit der Partikel in einer Matrix: Handelte es sich bei den Partikeln um lose Agglomerate, könnten diese zum Beispiel in einem Elastomer wieder auf Primärpartikelgröße dispergiert werden, während Aggregate nur in undefinierte Sekundärstrukturen zerfallen. Gleichzeitig wurde mit dieser Systemübertragung die Frage beantwortet, ob es sich bei den teilmodifizierten Partikeln um eine Mischung aus voll- und unmodifizierten Partikeln handelte oder ob das Silan statistisch über die komplette Oberfläche verteilt war. Wie auch schon beim Silica-System wurden die Nanopartikel zunächst abgestuft mit OCTEO modifiziert (0, 1/10, 1/3, 1/2, 2/3, 1) und anschließend sprühgetrocknet. Aufgrund ihrer magnetischen Eigenschaften konnten die Eisenoxid-Partikel mittels ZFC- und FC-Messungen untersucht werden. Diese spezielle Analysemethode erlaubte es, Aussagen über den Grad der magnetischen Wechselwirkung der Partikel zu treffen und somit indirekt auch über den Grad der Agglomeration/ Aggregation der Nanopartikel im Mikropartikel. Es zeigten sich klare Unterschiede in den Werten für die Blocking-Temperatur (TB) zwischen den voll- und unmodifizierten Partikeln. TB ist die Temperatur, ab welcher die Magnetisierungsrichtung der Partikel aufgrund der thermischen Energie frei fluktuieren kann. Die vollmodifizierten Partikeln hatten einen sehr niedrigen Wert für TB, was auf eine schwache Dipol-Dipol- Wechselwirkung zwischen den einzelnen Eisenoxid-NP schließen ließ, während die unmodifizierten Eisenoxid-Partikel einen hohen TB-Wert hatten, woraus zu schließen war, dass es sich um Aggregate mit einem sehr geringen Partikel-Partikel-Abstand handelte und einer deshalb höheren Wechselwirkung. Die Werte der teilmodifizierten Partikel folgten dem Trend, dass mit zunehmender Silan-Bedeckung der TB-Wert abnahm. Um die Frage der Silan-Verteilung zu beantworten, wurde zusätzlich ein Mischsystem aus voll- und unmodifizierten Eisenoxid-NP versprüht. Sollte es sich bei den teilmodifizierten Partikeln (als Beispiel 1/2) nicht um eine statistische Verteilung der Octylgruppen auf der Oberfläche handeln, müssten die beiden Messungen Übereinstimmungen aufweisen. Dies war allerdings nicht der Fall, was mithilfe der ZFC- und FC-Messungen gezeigt werden konnte. Der TB-Wert des Mischsystems lag zwischen dem der voll- und zu 2/3-modifizierten Partikel, während der Tir-Wert dem der unmodifizierten Partikel entsprach. Die Breite der Aufspaltung zwischen TB undTir konnte als breite Partikelverteilung (Mischung aus Agglomeraten und Aggregaten) interpretiert werden. Im Hinblick auf die Anwendung als Füllstoff wurden die Mikropartikel in eine PDMS-Matrix eingearbeitet und erneut ZFC- und FC-Messungen durchgeführt, wobei die gleichen Trends wie bei den reinen nanostrukturierten Mikropartikeln erhalten wurden. Das bedeutete, dass sich die vollmodifizierten Eisenoxid-NP gut im Elastomer verteilt hatten und somit eine nur sehr geringe Dipol-Dipol-Wechselwirkung vorhanden war. Mit dem entwickelten System der nanostrukturierten Mikropartikel lässt sich der Agglomerations- bzw. Aggregationsgrad der Nanopartikel mehr oder weniger gezielt einstellen, und es können zusätzlich Voraussagen über die Redispergierbarkeit des Partikelpulvers in einer geeigneten Matrix gemacht werden. Basierend auf den gewonnen Erkenntnissen, die zum Verständnis der nanostrukturierten Mikropartikel beitrugen, wurden in einem nächsten Schritt gezielt komplexe Strukturen aufgebaut. Für eine gezielte Strukturierung von Nanopartikeln in Kern-Satellit-Partikel wurde zunächst große 100 nm Silica-NP mit einem PCE funktionalisiert und anschließend mit kleinen und großen unmodifizierten Silica-NP versprüht. Wurden die geeigneten Verhältnisse (70:20:10; 100 nm Mel : 100 nm blank : 20 nm blank) der Partikel zueinander gewählt, konnten Kern-Satellit-Strukturen auf der Mikropartikeloberfläche erzeugt werden. Beim Dispergieren der Mikropartikel in einer Flüssigkeit und in einem Elastomer (PDMS) konnten vereinzelte Kern-Satellit-Strukturen erhalten werden. Um zu bestätigen, dass es sich bei den dispergierten Kern-Satellit-Partikeln nicht um durch Trocknungseffekte entstandene Strukturen handelte, wurden in-situ-Flüssigkeitszellen- TEM-Aufnahmen gemacht. Die Aufnahmen konnten zeigen, dass sich die Kern-Satellit- Partikel in Abhängigkeit zueinander bewegen und nicht jeder Nanopartikel für sich, was auf eine Bindung der Partikel untereinander hindeutete. Neben den Silica-basierten Kern-Satellit-Partikeln konnten auch welche erzeugt werden, deren Satellit-Partikel aus Eisenoxid bestanden. Mit diesem System ist es möglich, multifunktionelle Partikel mit verschiedensten Eigenschaften und Strukturen herzustellen. Teil II: Anwendungspotential nanostrukturierter Mikropartikel Im zweiten Teil der Arbeit wurde zunächst die Anwendung der nanostrukturierten Mikropartikel als Füllstoff in IR und PDMS untersucht. Dafür wurde ein weiteres Silan, Si69TM, zur abgestuften Modifizierung der Silica-NP eingesetzt. Es handelt sich um ein multifunktionelles Silan, welches sowohl an die Partikeloberfläche als auch an das Elastomer binden kann. Bei den mechanischen Untersuchungen der IR-Silica-Komposite zeigte sich, dass das Silan einen entscheidenden Einfluss auf die Verstärkung bei kleinen Deformationen hatte. Während bei dem monofunktionellen Silan (OCTEO) eine direkte Korrelation zwischen Bedeckungsgrad und mechanischer Verstärkung (G‘) bei gleichbleibendem Füllstoffgehalt beobachtet werden konnte, hatte der Bedeckungsgrad beim multifunktionellen Silan (Si69TM) keinen Einfluss. Anders als bei kleinen Deformationen zeigte sich bei großen Deformationen ein gegenteiliges Bild. Die Verschleißrate der IR-Silica-Komposite nahm bei beiden Silantypen mit zunehmendem Modifizierungsgrad ab, wobei die mit Si69TM modifizierten Partikel-Komposite wesentlich beständiger gegen Verschleiß waren als die mit OCTEO modifizierten Partikel-Komposite, was auf die zusätzliche Matrixanbindung des Si69TM zurückzuführen war. Wurden die IR-Silica- Komposite mit den PDMS-Silica-Kompositen verglichen, konnten keine übereinstimmenden Trends gefunden werden. Im PDMS-System war die mechanische Verstärkung für Mikropartikel aus 2/3 mit OCTEO modifizierten Silica-NP maximal. Diese Unterschiede könnten sowohl auf die unterschiedliche Einarbeitung als auch auf die sehr unterschiedlichen Matrices zurückgeführt werden. Als weitere Anwendung wurden die nanostrukturierten Mikropartikel als Schersensoren für den 3D-Druck untersucht. Hierfür wurden die Silica-NP mit einem PCE modifiziert und anschließend sprühgetrocknet. Um die entstandenen Mikropartikel vollständig in einer Matrix zu dispergieren, waren hohe Scherkräfte und lange Scherzeiten erforderlich, was eine mögliche Anwendung als Schersensor nur schwer realisierbar macht. Teil III: Erweiterung des Ansatzes zur Herstellung nanostrukturierter Mikropartikel auf Hydroxid-basierte Systeme Im dritten Teil dieser Arbeit wurde das System zur Modifizierung von oxidischen Silicaund Eisenoxid-Partikeln auf ein hydroxidisches Systeme übertragen. Hierfür wurden mittels Fällungsprozess LDH-Partikel hergestellt, die anschließend mit OCTEO modifiziert und abschließend sprühgetrocknet wurden. In gleicher Weise wie bei den Mikropartikeln aus Silica-NP nahm der hydrophobe Charakter der LDH-Mikropartikel mit zunehmendem Modifizierungsgrad der Ausgangspartikel zu, was sich anhand von Untersuchungen zur Dispergierbarkeit in Flüssigkeiten unterschiedlicher Polarität zeigte. Zudem ließen sich die aus vollmodifizierten LDHs aufgebauten Mikropartikel in einer PDMS-Matrix wieder in vereinzelte Partikel dispergieren. Die Verstärkung der Komposite war für die teilmodifizierten Partikel (2/3) maximal, da es sich hier, wie auch bei den anderen Partikelsystemen (Silica und Eisenoxid), um eine Mischung aus vereinzelten LDHs und kleineren Aggregate handelte, was aufgrund der starken Füllstoff-Füllstoff-Wechselwirkung zu einer mechanischen Verstärkung bei kleinen Deformationen/Dehnungen führte. Die Eigenschaften der Polymer-Partikel-Komposite ließen sich über den Modifizierungsgrad der Primärpartikel einstellen. Dies konnte für alle drei Partikelsysteme (Silica, Eisenoxid und LDH) beobachtet werden. Ausblick In der vorliegenden Arbeit konnte die Synthese von verschiedenen nanostrukturierten Mikropartikeln und deren einstellbaren Zerfall gezeigt werden. Um den Zerfall der Mikropartikel noch gezielter einstellen zu können, sollte in weiterführenden Arbeiten vor allem die Modifizierung der Nanopartikel noch eingehender untersucht werden. Mithilfe der magnetischen Messungen konnte zwar zwischen einer Mischung aus un- und vollmodifizierten Partikel im Vergleich zu teilmodifizierten Partikel unterschieden werden, es konnten jedoch keine konkreten Aussagen zur Verteilung der Silanmoleküle auf der Partikeloberfläche getroffen werden. Hierfür sollten weitere Charakterisierungsmethoden hinzugezogen werden, die die Modifizierung auf molekularer Ebene analysieren. Zusätzlich sollte die Verteilung/Anordnung der teilmodifizierten Nanopartikel im Mikropartikel untersucht werden. Gerade für Nanopartikel mit einem geringen Modifizierungsgrad (1/10, 1/5 und 1/3) sind verschiedene Anordnungen möglich. Die Nanopartikel können sich während der Sprühtrocknung so anordnen, dass sich die Alkylketten entweder nach außen oder in die Mitte des Mikropartikels orientieren/ausrichten. Die Anordnung der Nanopartikel hat einen großen Einfluss auf die Polarität der entstehenden Mikropartikel- pulver. Darüber hinaus hat sie einen Einfluss auf die Aggregation der Nanopartikel untereinander und somit auf die Bildung von komplexen Unterstrukturen wie zum Beispiel Kern-Satellit-Partikel. Neben der Modifizierung der Nanopartikel sollte die Herstellung der komplexen Strukturen/Suprapartikel weiter optimiert werden. Mit einem detaillierten Verständnis der physikalischen Prozesse während der Sprühtrocknung könnte die Anzahl der Satelliten auf den Kernpartikel kontrollierter eingestellt werden. Grundsätzlich kann das hier entwickelte System der nanostrukturierten Mikropartikel mit einstellbarem Zerfallsverhalten an eine Vielzahl von Anwendungen angepasst werden. Da das System für zahlreiche Partikeltypen (Silica-, Eisenoxid-NP und LDH) geeignet ist, könnten verschiedene Partikel ko-versprüht und so Suprapartikel mit ganz neuen Funktionalitäten und Eigenschaften erzeugt werden. Diese können als verstärkende Füllstoffe in Elastomere oder zur Stabilisierung von Dispersionen eingesetzt werden. Mischpartikel aus Silica- und Eisenoxid-Partikel hätten zum Beispiel den Vorteil, dass sie eine Dispersion stabilisieren und gleichzeitig wieder magnetisch abgetrennt werden können. Diese Mischpartikel könnten auch als Füllstoffe in komplexe Kunststoffbauteile eingearbeitet werden, in denen sie zum einen als mechanisch verstärkender Füllstoff wirken und gleichzeitig durch induktive Erwärmung das Bauteil vernetzt. Beim induktiven Erwärmen handelt es sich um eine schonende Methode Bauteile gezielt zu vernetzen, indem die Wärme im Bauteil selbst, über magnetische Verluste der Magnetpartikel in einem magnetischen Wechselfeld, erzeugt wird und nicht über seine Oberfläche eingebracht werden muss. Eine weitere interessante Anwendung für Mischpartikel ist die als magnetooptisch aktiver Marker oder Tracer in der medizinischen Diagnostik. Aufgrund von Quenching-Effekten (Auslöschungseffekte) ist es schwierig magnetische Nanopartikel mit einer Farbigkeit oder Fluoreszenz auszustatten.[385] Mischt man jedoch die magnetischen Nanopartikel mit einem weiteren Partikelsystem wie zum Beispiel Silica-NP oder LDHs, können magnetooptische Eigenschaften erhalten werden
Structure-property relationships in poly(2-oxazoline)/poly(2-oxazine) based drug formulations
(2020)
According to estimates, more than 40% of all new chemical entities developed in pharmaceutical industry are practically insoluble in water. Naturally, the demand for excipients which increase the water solubility and thus, the bioavailability of such hydrophobic drugs is enormous. Poly(2-oxazoline)s (POx) are currently intensively discussed as highly versatile class of biomaterials. Although selected POx based micellar drug formulations exhibit extraordinarily high drug loadings > 50 wt.% enabling high anti-tumor efficacies in vivo, the formulation of other hydrophobic compounds has failed. This casts doubt on the general understanding in which a hydrophobic active pharmaceutical ingredient is dissolved rather unspecifically in the hydrophobic core of the micelles following the fundamental concept of “like dissolves like”. Therefore, a closer look at the interactions between all components within a formulation becomes increasingly important. To do so, a large vehicle platform was synthesized, loaded with various hydrophobic drugs of different structure, and the formulations subsequently characterized with conventional and less conventional techniques. The obtained in-depth insights helped to develop a more thorough understanding about the interaction of polymer and incorporated API finally revealing morphologies deviating from a classical core/shell structure. During these studies, the scarcely investigated polymer class of poly(2-oxazine)s (POzi) was found as promising drug-delivery vehicle for hydrophobic drugs. Apart from this fundamental research, the anti-tumor efficacy of the two APIs curcumin and atorvastatin has been studied in more detail. To increase the scope of POx and POzi based formulations designed for intravenous administration, a curcumin loaded hydrogel was developed as injectable drug-depot.
In the past decade, poly(2-oxazoline)s (POx) and very recently poly(2-oxazine)s (POzi) based amphiphiles have shown great potential for medical applications. Therefore, the major aim of this thesis was to further explore the pharmaceutical and biomedical applications of POx/POzi based ABA triblock and AB diblock copolymers, respectively with the special emphasis on structure property relationship (SPR). ABA triblock copolymers (with shorter side chain length in the hydrophobic block) have shown high solubilizing capacity for hydrophobic drugs. The issue of poor aqueous solubility was initially addressed by developing a (micellar) formulation library of 21 highly diverse, hydrophobic drugs with POx/POzi based ABA triblock copolymers. Theoretically, the extent of compatibility between polymers and drug was determined by calculating solubility parameters (SPs). The SPs were thoroughly investigated to check their applicability in present systems. The selected formulations were further characterized by various physico-chemical techniques. For the biomedical applications, a novel thermoresposive diblock copolymer was synthesized which has shown promising properties to be used as hydrogel bioink or can potentially be used as fugitive support material. The most important aspect i.e. SPR, was studied with respect to hydrophilic block in either tri- or di-block copolymers. In triblock copolymer, the hydrophilic block played an important role for ultra high drug loading, while in case of diblock, it has improved the printability of the hydrogels. Apart from the basic research, the therapeutic applications of two formulations i.e. mitotane (commercially available as tablet dosage form for adrenocortical carcinoma) and BT-44 (lead compound for nerve regeneration) were studied in more detail.
Sensitivity and selectivity remain the central technical requirement for analytical devices, detectors and sensors. Especially in the gas phase, concentrations of threat substances can be very low (e.g. explosives) or have severe effects on health even at low concentrations (e.g. benzene) while it contains many potential interferents. Preconcentration, facilitated by active or passive sampling of air by an adsorbent, followed by thermal desorption, results in these substances being released in a smaller volume, effectively increasing their concentration.
Traditionally, a wide range of adsorbents, such as active carbons or porous polymers, are used for preconcentration. However, many adsorbents either show chemical reactions due to active surfaces, serious water retention or high background emission due to thermal instability. Metal-organic frameworks (MOFs) are a hybrid substance class, composed inorganic and organic building blocks, being a special case of coordination polymers containing pores. They can be tailored for specific applications such as gas storage, separation, catalysis, sensors or drug delivery.
This thesis is focused on investigating MOFs for their use in thermal preconcentration for airborne detection systems. A pre-screening method for MOF-adsorbate interactions was developed and applied, namely inverse gas chromatography (iGC). Using this pulse chromatographic method, the interaction of MOFs and molecules from the class of explosives and volatile organic compounds was studied at different temperatures and compared to thermal desorption results.
In the first part, it is shown that archetype MOFs (HKUST-1, MIL-53 and Fe-BTC) outperformed the state-of-the-art polymeric adsorbent Tenax® TA in nitromethane preconcentration for a 1000 (later 1) ppm nitromethane source. For HKUST-1, a factor of more than 2000 per g of adsorbent was achieved, about 100 times higher than for Tenax. Thereby, a nitromethane concentration of 1 ppb could be increased to 2 ppm. High enrichment is addressed to the specific interaction of the nitro group as by iGC, which was determined by comparing nitromethane’s free enthalpy of adsorption with the respective saturated alkane. Also, HKUST-1 shows a similar mode of sorption (enthalpy-entropy compensation) for nitro and saturated alkanes.
In the second part, benzene of 1 ppm of concentration was enriched with a similar setup, using 2nd generation MOFs, primarily UiO-66 and UiO-67, under dry and humid (50 %rH) conditions using constant sampling times. Not any MOF within the study did surpass the polymeric Tenax in benzene preconcentration. This is most certainly due to low sampling times – while Tenax may be highly saturated after 600 s, MOFs are not. For regular UiO-66, four differently synthesized samples showed a strongly varying behavior for dry and humid enrichment which cannot be completely explained. iGC investigations with regular alkanes and BTEX compounds revealed that confinement factors and dispersive surface energy were different for all UiO-66 samples. Using physicochemical parameters from iGC, no unified hypothesis explaining all variances could be developed.
Altogether, it was shown that MOFs can replace or add to state-of-the-art adsorbents for the enrichment of specific analytes with preconcentration being a universal sensitivity-boosting concept for detectors and sensors. Especially with iGC as a powerful screening tool, most suitable MOFs for the respective target analyte can be evaluated. iGC can be used for determining “single point” retention volumes, which translate into partition coefficients for a specific MOF × analyte × temperature combination.
Die vorliegende Arbeit befasste sich mit der bisher relativ unbekannten Polymerklasse der Polypeptoide, die hinsichtlich ihrer Verwendung als Biomaterial näher untersucht werden sollte. Hierbei war die Untersuchung des Polymerisationssystems ein wesentlicher Schwerpunkt. Dies beinhaltete zum einen die Synthesen verschiedener Monomere sowie deren Polymerisationskinetiken und zum anderen Studien über die Stabilität des aktiven Kettenendes. Um mehr über die Polypeptoide zu erfahren, wurden die erhaltenen Homopolymere nach der Strukturanalyse hinsichtlich ihrer physikochemischen Eigen-schaften untersucht. Im Anschluss erfolgte die Synthese von (amphiphilen) Blockco-polypeptoiden, die sich in wässrigen Lösungen zu definierten Morphologien zusammen-lagern. Die resultierenden Morphologien, sowohl mizellare als auch vesikuläre Strukturen, wurden mit verschiedenen Methoden, wie z. B. der Pyren-Fluoreszenz-Spektroskpie und der dynamischen Lichtstreuung, untersucht. Erste Erkenntnisse über die Biokompatibilität der Polypeptoide sollte die Bestimmung der Zellviabilität in verschiedenen Polymerlösungen liefern.
Die verschiedenen Studien über die Polypeptoide zeigten, dass diese Polymerklasse über eine besonders lebende Polymerisation synthetisiert werden kann. Dabei resultieren Produkte, die sich durch eine Poisson-Verteilung und eine hohe Endgruppengenauigkeit auszeichnen. Zusätzlich bestehen Polypeptoide aus einem abbaubaren Rückgrat und, im Vergleich zu den Polypeptiden, besitzen sie eine erhöhte proteolytische Stabilität. Amphiphile Blockcopolypeptoide sind zudem in der Lage, sich in Lösung zu verschiedenen Morphologien anzuordnen. Durch die Variierung der Seitenkette und des f kann sowohl die Selbstorganisation als auch das Mikroumfeld der Aggregate abgestimmt werden. Darüber hinaus können die amphiphile Blockcopolymere, die sich zu Mizellen anordnen, hydrophobe Substanzen solubilisieren.
Polypeptoide liefern all die nötige chemische Vielseitigkeit und potentielle Biokompatibilität, um bestehende sowie neuartige Probleme in biomedizinischen Anwendungen zu bewältigen. Zukünftige in vivo und in vitro Test werden das Potential, aber auch die Grenzen dieser neuen Polymerklasse als Biomaterial zeigen.
The aim of this thesis was the preparation of a biomaterial ink for the fabrication of chemically crosslinked hydrogel scaffolds with low micron sized features using melt electrowriting (MEW). By developing a functional polymeric material based on 2-alkyl-2-oxazine (Ozi) and 2-alkyl-2-oxazoline (Ox) homo- and copolymers in combination with Diels-Alder (DA)-based dynamic covalent chemistry, it was possible to achieve this goal. This marks an important step for the additive manufacturing technique melt electrowriting (MEW), as soft and hydrophilic structures become available for the first time. The use of dynamic covalent chemistry is a very elegant and efficient method for consolidating covalent crosslinking with melt processing. It was shown that the high chemical versatility of the Ox and Ozi chemistry offers great potential to control the processing parameters. The established platform offers straight forward potential for modification with biological cues and fluorescent markers. This is essential for advanced biological applications. The physical properties of the material are readily controlled and the potential for 4D-printing was highlighted as well. The developed hydrogel architectures are excellent candidates for 3D cell culture applications. In particular, the low internal strength of some of the scaffolds in combination with the tendency of such constructs to collapse into thin strings could be interesting for the cultivation of muscle or nerve cells. In this context it was also possible to show that MEW printed hydrogel scaffolds can withstand the aspiration and ejection through a cannula. This allows the application as scaffolds for the minimally invasive delivery of implants or functional tissue equivalent structures to various locations in the human body.
In this work, the influence of aromatic structures on drug encapsulation, self-assembly and hydrogel formation was investigated. The physically crosslinked gelling systems were characterized and optimized for the use in biofabrication and applied in initial (bio)printing experiments.
Chapter I: The cytocompatible (first in vitro and in vivo studies) amphiphile PMeOx-b-PBzOx-b- PMeOx (A-PBzOx-A) was used for the solubilization of PTX, schizandrin A (SchA), curcumin (CUR), niraparib and HS-173.
Chapter II: Compared to the polymers A-PPheOx-A, A-PBzOx-A and A-PBzOzi-A, only the polymer A-PPheOzi-A showed a reversible temperature- and concentration-dependent inverse thermogelation, which is accompanied by a morphology change from long wormlike micelles in the gel to small spherical micelles in solution. The worm formation results from novel interactions between the hydrophilic and hydrophobic aromatic polymer blocks. Changes in the hydrophilic block significantly alter the gel system. Rheological properties can be optimized by concentration and temperature, which is why the hydrogel was used to significantly improve the printability and stability of Alg in a blend system.
Chapter III: By extending the side chain of the aromatic hydrophobic block, the inverse thermogelling polymer A-poly(2-phenethyl-2-oxazoline)-A (A-PPhenEtOx-A) is obtained. Rapid gelation upon cooling is achieved by inter-correlating spherical micelles. Based on ideal rheological properties, first cytocompatible bioprinting experiments were performed in combination with Alg. The polymers A- poly(2-benzhydryl-2-oxazoline)-A (A-PBhOx-A) and A-poly(2-benzhydryl-2-oxazine) (A-PBhOzi-A) are characterized by two aromatic benzyl units per hydrophobic repeating unit. Only the polymer A- PBhOzi-A exhibited inverse thermogelling behavior. Merging micelles could be observed by electron microscopy. The system was rheologically characterized and discussed with respect to an application in 3D printing.
Chapter IV: The thermogelling POx/POzi system, in particular the block copolymer PMeOx-b- PnPrOzi, was used in different applications in the field of biofabrication. The introduction of maleimide and furan units along the hydrophilic polymer part ensured additional stabilization by Diels-Alder crosslinking after the printing process.
Motivated by the great potential which is offered by the combination of additive manufacturing and tissue engineering, a novel polymeric bioink platform based on poly(2 oxazoline)s was developed which might help to further advance the young and upcoming field of biofabrication. In the present thesis, the synthesis as well as the characteristics of several diblock copolymers consisting of POx and POzi have been investigated with a special focus on their suitability as bioinks.
In general, the copolymerization of 2-oxazolines and 2-oxazines bearing different alkyl side chains was demonstrated to yield polymers in good agreement with the degree of polymerization aimed for and moderate to low dispersities.
For every diblock copolymer synthesized during the present study, a more or less pronounced dependency of the dynamic viscosity on temperature could be demonstrated. Diblock copolymers comprising a hydrophilic PMeOx block and a thermoresponsive PnPrOzi block showed temperature induced gelation above a degree of polymerization of 50 and a polymer concentration of 20 wt%. Such a behavior has never been described before for copolymers solely consisting of poly(cyclic imino ether)s.
Physically cross linked hydrogels based on POx b POzi copolymers exhibit reverse thermal gelation properties like described for solutions of PNiPAAm and Pluronic F127. However, by applying SANS, DLS, and SLS it could be demonstrated that the underlying gel formation mechanism is different for POx b POzi based hydrogels. It appears that polymersomes with low polydispersity are formed already at very low polymer concentrations of 6 mg/L. Increasing the polymer concentration resulted in the formation of a bicontinuous sponge like structure which might be formed due to the merger of several vesicles. For longer polymer chains a phase transition into a gyroid structure was postulated and corresponds well with the observed rheological data.
Stable hydrogels with an unusually high mechanical strength (G’ ~ 4 kPa) have been formed above TGel which could be adjusted over a range of 20 °C by changing the degree of polymerization if maintaining the symmetric polymer architecture. Variations of the chain ends revealed only a minor influence on TGel whereas the influence of the solvent should not be neglected as shown by a comparison of cell culture medium and MilliQ water.
Rotationally as well as oscillatory rheological measurements revealed a high suitability for printing as POx b POzi based hydrogels exhibit strong shear thinning behavior in combination with outstanding recovery properties after high shear stress.
Cell viability assays (WST-1) of PMeOx b PnPrOzi copolymers against NIH 3T3 fibroblasts and HaCat cells indicated that the polymers were well tolerated by the cells as no dose-dependent cytotoxicity could be observed after 24 h at non-gelling concentrations up to 100 g/L.
In summary, copolymers consisting of POx and POzi significantly increased the accessible range of properties of POx based materials. In particular thermogelation of aqueous solutions of diblock copolymers comprising PMeOx and PnPrOzi was never described before for any copolymer consisting solely of POx or POzi. In combination with other characteristics, e.g. very good cytocompatibility at high polymer concentrations and comparably high mechanical strength, the formed hydrogels could be successfully used for 3D bioprinting. Although the results appear promising and the developed hydrogel is a serious bioink candidate, competition is tough and it remains an open question which system or systems will be used in the future.
Motivated by the great potential offered by the combination of additive manufacturing technology and hydrogels, especially in the field of tissue engineering and regenerative medicine, a series of novel hybrid hydrogel inks were developed based on the recently described thermogelling poly(2-oxazoline)s-block-poly(2-oxazine)s diblock copolymers, which may help to expand the platform of available hydrogel inks for this transformative 3D printing technology (Fig. 5.1).
In the present thesis, the first reported thermogelling polymer solely consisting of POx and POzi, i.e., the diblock copolymer PMeOx-b-PnPrOzi comprising a hydrophilic block (PMeOx) and a thermoresponsive block (PnPrOzi), was selected and used as a proof-of-concept for the preparation of three novel hybrid hydrogels. Therefore, three batches of the diblock copolymers with a DP of 100 were synthesized for the study of three different hybrid hydrogels with a special focus on their suitability as (bio)inks for extrusion-based 3D printing. The PMeOx-b-PnPrOzi diblock copolymer solution shows a temperature induced reversible gelation behavior above a critical polymer concentration of 20 wt%, as described for the Pluronic F127 solution but with a unique gelation mechanism, working through the formation of a bicontinuous sponge-like structure from the physically crosslinked vesicles. Specially, its intrinsic shear thinning behavior and excellent recovery property with a certain yield point make it a promising ink candidate for extrusion-based printing technology.
Increasing the polymer concentration is the most traditional approach to improve the printability of an ink material, and serve as the major strategy available to improve the printability of PMeOx-b-PnPrOzi systems prior to this work. From the analysis of rheological properties related to printability, it came a conclusion that increasing the copolymer concentration does improve the hydrogel strength and thus the printability. However, such improvement is very limited and usually leads to other problems such as more viscous systems and stringent requirements on the printers, which are not ideal for the printing process and applications especially in the cell-embedded biofabrication field.
POx-b-POzi/clay Hybrid Hydrogel
An alternative method proposed to improve the printability of this thermoresponsive hydrogel ink is through nanoclay (Laponite XLG) addition, i.e., the first hybrid hydrogel system of PMeOx-b-PnPrOzi/clay (also named shortly as POx-b-POzi/clay) in this thesis. To optimize the viscoelastic properties of the ink material, Laponite XLG acted as a reinforcement additive and a physically crosslinker was blended with the copolymers. Compared with the pristine copolymer solution of PMeOx-b-PnPrOzi, the hybrid PMeOx-b-PnPrOzi/clay solution well retained the temperature induced gelation performance of the copolymers.
The obtained hybrid hydrogels exhibited a rapid in situ reversible thermogelation at a physiological relevant Tgel of around 15 ℃ and a rapid recovery of viscoelastic properties within a few seconds. More importantly, with the addition of only a small amount of 1.2 wt% clay, it exhibited obviously enhanced shear thinning character (n = 0.02), yield stress (240 Pa) and mechanical strength (storage modulus over 5 kPa). With this novel hybrid hydrogel, real three-dimensional constructs with multiple layers and various geometries are generation with greatly enhanced shape fidelity and resolution. In this context, the thermogelling properties of the hybrid hydrogels over a copolymer concentration range of 10-20 wt% and a clay concentration of 0-4 wt% were systematically investigated, and from which a printable window was obtained from the laboratory as a reference.
In fact, the printing performance of an ink is not only determined by the intrinsic physicochemical properties of the material, but is also influenced by the external printing environments as well as the printer parameter settings. All the printing experiments in this study were conducted under a relatively optimized conditions obtained from preliminary experiments. In future work, the relationship between material rheology properties, printer parameters and printing performance could be systematically explored. Such a fundamental study will help to develop models that allows the prediction and comparison of printing results from different researches based on the parameters available through rheology, which is very beneficial for further development of more advanced ink systems.
Although the printability has been significantly improved by the addition of nanoclay Laponite XLG, the hybrid hydrogels and their printed constructs still suffer from some major limitations. For example, these materials are still thermoresponsive, which will cause the printed constructs to collapse when the environment temperature changes below their Tgel. In addition, the formed hydrogel constructs are mechanical too weak for load-bearing applications, and the allowed incubation time is very limited during media exchange/addition as it will lead to dissolution of the hydrogels due to dilution effects. Therefore, it is essential to establish a second (chemical or physical) crosslinking mechanism that allows further solidification of the gels after printing. It should be kept in mind that the second crosslinking step will eliminate the thermoresponsive behavior of the gels and thus the possibility of cell recovery. In this case, besides through the traditional approach of copolymer modification to realize further crosslinking, like one of the well-known post-polymerization modification approach Diels-Alder reaction,[430] designing of interpenetrating networks (IPN) hydrogels serves as one of the major strategy for advanced (bio)ink preparation.[311] Therefore, the second hybrid hydrogel system of PMeOx-b-PnPrOzi/PDMAA/clay (also named shortly as POx-b-POzi/PDMAA/clay) was developed in this thesis, which is a 3D printable and highly stretchable ternary organic-inorganic IPN hydrogel.
POx-b-POzi/PDMAA/clay Hybrid Hydrogel
The nanocomposite IPN hydrogel combines a thermoresponsive hydrogel with clay described above and in situ polymerized poly(N, N-dimethylacrylamide). Before in situ polymerization, the thermoresponsive hydrogel precursors exhibited thermogelling behavior (Tgel ~ 25 ℃, G' ~ 6 kPa) and shear thinning properties, making the system well-suited for extrusion-based 3D printing. After chemical curing of the 3D-printed constructs by free radical polymerization, the resulting IPN hydrogels show excellent mechanical strength with a high stretchability to a tensile strain at break exceeding 550%. The hybrid hydrogel can sustain a high stretching deformation and recover quickly due to the energy dissipation from the non-covalent interactions. With this hybrid hydrogel, integrating with the advanced 3D-printing technique, various 3D constructs can be printed and cured successfully with high shape fidelity and geometric accuracy.
In this context, we also investigated the possibility of acrylic acid (AA) and 2-hydroxyethylmethacrylate (HEMA) as alternative hydrogel precursors. However, the addition of these two monomers affected the thermogelation of POx-b-POzi in an unfavorable manner, as these monomers competed more effectively with water molecules, preventing the hydration of nPrOzi block at lower temperatures and therefore, the liquefaction of the gels. Furthermore, the influence of the printing process and direction on the mechanical properties of the hydrogel was investigated and compared with the corresponding bulk materials obtained from a mold. No significant effects from the additive manufacturing process were observed due to a homogeneously adhesion and merging between sequentially deposited layers. In the future, further studies on the specific performance differences among hydrogels fabricated at different printing directions/speeds would be of great interest to the community, as this allows for a more accurately control and better predict of the printed structures.
This newly developed hybrid IPN hydrogel is expected to expand the material toolbox available for hydrogel-based 3D printing, and may be interesting for a wide range of applications including tissue engineering, drug delivery, soft robotics, and additive manufacturing in general. However, in this case, the low toxicity from the monomer DMAA and other small molecules residuals in the polymerized hydrogels made this hybrid hydrogel not ideal for bioprinting in the field of biofabrication. For this problem, cyto-/biocompatible monomers such as polyethylene glycol diacrylate (PEGDA) can be used as an alternative, while the overall properties of the hydrogels including mechanical properties should be re-evaluated accordingly. Moreover, the swelling behavior of the hydrogels should also be taken into account, as it may most likely affect the mechanical strength and geometry size of the printed scaffold, but is often be overlooked after printing. For example, regarding the specific hybrid hydrogel POx-b-POzi/PDMAA/clay in this work, an equilibrium swelling ratio of 1100% was determined. The printed hydrogel cuboid experienced a volume increasing over 6-fold after equilibrium swelling in water, and became mechanical fragile due to the formation of a swollen hydrogel network absorbing large amount of water.
POx-b-POzi/Alg/clay Hybrid Hydrogel
In the final part of this dissertation, to enable the cell-loaded bioprinting and long-term cell culture, the third hybrid hydrogel system POx-b-POzi/Alg/clay was introduced by replacing the monomer DMAA to the natural polysaccharides alginate. Initially, detailed rheological characterization and mechanical tests were performed to evaluate their printability and mechanically properties. Subsequently, some simple patterns were printed with the optimized hydrogel precursor solutions for the preliminary filament fusion and collapse test before proceeding to more complex printings. The fibers showed a sufficient stability which allows the creation of large structures with a height of a few centimeters and a suspended filament up to centimeter. Accordingly, various 3D constructs including suspended filaments were printed successfully with high stackability and shape fidelity. The structure after extrusion was physical crosslinked easily by soaking in CaCl2 solution and, thereafter exhibited a good mechanical flexibility and long-term stability. Interestingly, the mechanical strength and geometry size of the generated scaffolds were well maintained over a culture period of weeks in water, which is of great importance for clinical applications. In addition, the post-printing ionic crosslinking of alginate could also be realized by other di/trivalent cations such as Fe3+ and Tb3+.
Subsequently, the cell-laden printing with this hybrid hydrogel and post-printing crosslinking by Ca2+ ions highlighting its feasibility for 3D bioprinting. WST-1 assay of fibroblast suggested no-dose dependent cytocompatibility of the hydrogel precursor solution. The cell distribution was uniform throughout the printed construct, and proliferated with high cell viability during the 21 days culture. The presented hybrid approach, utilizing the beneficial properties of the POx-b-POzi base material, could be interesting for a wide range of bioprinting applications and potentially enabling also other biological bioinks such as collagen, hyaluronic acid, decellularized extracellular matrix or cellulose based bioinks. Although the results look promising and the developed hydrogel is an important bioink candidate, the long-term in vitro cell studies with different cell lines and clinical model establishment are still under investigation, which remains a long road but is of great importance before realizing real clinical application.
Last but not least, the improvement to the printability of thermogelling POx/POzi-based copolymers by the clay Laponite XLG was also demonstrated in another thermogelling copolymer PEtOx-b-PnPrOzi. This suggests that the addition of clay may be a general strategy to improve the printability of such polymers. Despite these advances in this work which significantly extended the (bio)material platform of additive manufacturing technology, the competition is still fierce and more work should be done in the further to reveal the potential and limitations of this kind of new and promising candidate (bio)ink materials. It is also highly expected for further creative works based on the thermogelling POx/POzi polymers, such as crosslinking in Ca2+ solution containing monomer acrylamide to prepare printable and mechanically tough hydrogels, research on POx-based support bath material, and print of clinically more relevant sophisticated structures such as 3D microvascular networks omnidirectionally.