This thesis consists of two parts of original experimental work, its evaluation, and in- terpretation. Its final goal is to investigate dynamical charge transfer (CT) at a hetero- molecular interface with resonant photoelectron spectroscopy (RPES). In order to achieve this goal preliminary studies have been necessary. First two hetero-molecular inter- faces that exhibit adequate structural properties as well as an appropriate photoelec- tron spectroscopy (PES) spectrum of the valence regime have been identified. The de- sired CT analysis with RPES of these hetero-molecular systems is then conducted on the basis of the knowledge gained by previous RPES studies of homo-molecular sys- tems.
The characterization of hetero-molecular films on single crystal Ag surfaces in the first part of this thesis is performed with high resolution core level PES and valence PES. The reproduction of the core level PES data with reference spectra of homo-molecular films allows me to determine which molecule is in direct contact to the Ag surface and which one is situated in higher layers (not the first one). Due to the direct correspon- dence of core level and valence PES the assignment of features in the spectra of the latter technique can be achieved with the identification of the contributions extracted from the evaluation of the data of the former technique. It is found that the systems PTCDA on one monolayer (ML) of SnPc on Ag(111) and CuPc/1 ML PTCDA/Ag(111) are stable at 300 K which means that no significant layer exchange occurs for these systems. In contrast a vertical exchange of CuPc and PTCDA molecules is observed for PTCDA de- posited on top of 1 ML CuPc/Ag(111). Up to a coverage of approximately 0.5 ML of PTCDA molecules these diffuse into the first layer, replace CuPc molecules, and con- sequently force them into higher layers. Above a coverage of approximately 0.5 ML of PTCDA molecules these are also found in higher layers. The search for a promising system for the intended RPES study then leads to an investigation of hetero-molecular films with a combination of F4TCNQ and PTCDA molecules on Ag(110) within the same approach. Depositing F4TCNQ molecules onto a 1 ML PTCDA/Ag(110) film in the herringbone phase at 300 K results in an instable hetero-organic system which un- dergoes a layer exchange. Hereby PTCDA molecules in the first layer are replaced by F4TCNQ molecules similar to the behavior of the system PTCDA/1 ML CuPc/Ag(111). Switching the order of the preparation steps leads to a stable film of PTCDA/1.0 ML F4TCNQ/Ag(110) at 300 K. Among the stable hetero-molecular films only the system CuPc/1 ML PTCDA/Ag(111) exhibits the required wetting growth of the first two layers at 300 K and a valence PES spectrum with energetically separable molecular orbital signals in the same intensity range. Thus this system is identified to be appropriate for a detailed analysis with RPES.
The unexpected findings of vertical exchanges in the hetero-molecular films at 300 K motivate a study of the behavior at elevated temperatures for all systems investigated before. Therein it is revealed that annealing 1.5 ML SnPc/1 ML PTCDA/Ag(111) and
1.0 ML PTCDA/1 ML SnPc/Ag(111) to a temperature above the desorption temperature of molecules not in direct contact to the Ag(111) surface results in a 1 ML SnPc/Ag(111) film in both cases. Hence at elevated temperatures (approximately above 420 K) SnPc molecules replace PTCDA molecules in the first layer on Ag(111). At higher temper- atures (approximately above 470 K) PTCDA molecules and SnPc molecules situated above the first layer then desorb from the 1 ML SnPc/Ag(111) sample. Annealing all hetero-molecular films with CuPc and PTCDA molecules on Ag(111) to 570 K leads to a sample with CuPc and PTCDA molecules in the first and only layer. Depending on the initial CuPc coverage different ratios of both molecules are obtained. With a CuPc coverage of exactly 1 ML, or above, films with PTCDA coverages of approxi- mately 0.1–0.2 ML are produced. So at elevated temperatures CuPc molecules replace PTCDA molecules in the first layer of the system CuPc/1 ML PTCDA/Ag(111). Anal- ogously the layer exchange at 300 K for the system PTCDA/1 ML CuPc/Ag(111) is reversed at elevated temperatures. In the case of SnPc and CuPc coverages below 1 ML annealing vertical hetero-molecular systems with PTCDA on Ag(111) up to 570 K re- sults in a single layer of mixed hetero-molecular films with lateral long range order. In this way the system CuPc + PTCDA/Ag(111) is prepared and then characterized as a proper system for a detailed analysis with RPES. Additional annealing experiments of hetero-organic films consisting of F4TCNQ and PTCDA molecules on Ag(110) with an F4TCNQ coverage of 1.0 ML (and above) end in a submonolayer (sub-ML) film of F4TCNQ/Ag(110) that exhibits a contribution of amorphous carbon. Consequently, it can be concluded that at elevated temperatures part of the F4TCNQ molecules decom- pose.
In the second part of this thesis homo-molecular multilayer samples and (sub-)ML films on single crystalline metal surfaces are investigated with RPES in order to enable the final RPES study of vertical and lateral hetero-molecular interface systems. First a pho- ton energy (hν) dependent intensity variation of (groups of) molecular orbital signals of exemplary multilayer films (NTCDA and coronene) is studied and explained on the basis of the local character of the electronic transitions in near edge x-ray absorption fine structure (NEXAFS) spectroscopy in combination with the real space probability den- sity of the contributing molecular orbitals. This simple approach is found to be able to correctly describe relative intensity variations by orders of magnitude while it fails for hν dependent relative intensity changes in the same order of magnitude. After that the hν dependent line-shape evolution of an energetically separated molecular orbital signal of a CuPc multilayer is discussed in relation to small molecules in the gas phase and explained with an effect of electron vibration coupling. Through a comparison of the hν dependent line-shape evolution of the highest occupied molecular orbital (HOMO) of a CuPc with a SnPc multilayer the molecule specific character of this effect is identified. Then the same effect with either two (or more) electronic transitions or multiple coupling vibrational modes is observed for a coronene multilayer. Thereafter the influence of the adsorption on metal surfaces on this effect is studied and discussed with special emphasis on a possible contribution by features which are related to dynamical interface CT. For a sub-ML of SnPc/Au(111) no variation with respect to a SnPc multilayer film is detected while for a sub-ML of CuPc/Au(111) less intensity is distributed into the high binding energy (EB) part of the HOMO signal with respect to the corresponding multilayer film. In the RPES data of a sub-ML of coronene/Ag(111) a resonance specific variation of the hν dependent line-shape evolution of the HOMO signal is found by the revelation of a change of this effect with respect to the coronene multilayer data in only one of the two NEXAFS resonances. All these findings are consistently explained within one effect and a common set of parameters, namely all quantities that characterize the potential energy surfaces involved in the RPES process. Through that an alternative explanation that re- lies on dynamical CT can be excluded which influences the following CT analysis with RPES.
Three criteria for such an analysis of dynamical interface CT with RPES are identified. In the system coronene on Ag(111) a low EB feature is related to metal-molecule inter- face CT through the assignment of a particular final state and hence named CT state. In the EB region of the frontier molecular orbital signals of the molecule-metal inter- face systems with a signal from the lowest unoccupied molecular orbital (LUMO) in direct valence PES a broad line-shape is measured in RPES. This finding is related to interface CT by a possible explanation that emerges through the comparison to the line- shape of the CT state. The constant kinetic energy (EK ) features detected for several molecule-metal interfaces constitute the third criterion for a CT analysis with RPES. For the molecule-metal interface systems without a LUMO signal in direct valence PES the energy of these features can be calculated with the assignment of the responsible decay channel in combination with explicitly given simplifying assumptions. Through that the involvement of metal-molecule interface CT in the generation of these constant EK fea- tures is demonstrated. The RPES data of the lateral and the vertical hetero-molecular interface, identified in the first part, is then scanned for these three CT criteria. Thereby neither for the lateral hetero-molecular system CuPc + PTCDA/Ag(111) nor for the verti- cal hetero-molecular system CuPc/1 ML PTCDA/Ag(111) dynamical hetero-molecular interface CT can be confirmed. In the former system the molecule-metal interface in- teraction is found to dominate the physics of the system in RPES while in the latter system no hints for a significant hybridization at the CuPc-PTCDA interface can be revealed
Als Orbitaltomographie wird eine junge Methode innerhalb der Photoelektronenspektrokopie bezeichnet, welche es ermöglicht, Molekülorbitale mit hoher Ortsauflösung abzubilden. Hierfür werden die zu untersuchenden Moleküle durch elektromagnetische Strahlung angeregt und die mittels Photoeffekt emittierten Elektronen hinsichtlich ihres Impulses und ihrer kinetischen Energie charakterisiert. Moderne Photoemissionsexperimente erlauben die simultane Vermessung des gesamten Impulshalbraumes oberhalb der Probe. Die detektierte Intensitätsverteilung stellt dann unter bestimmten Bedingungen das Betragsquadrat eines hemisphärischen Schnittes durch den Fourierraum des spektroskopierten Orbitals dar, wobei der Radius der Hemisphäre von der Energie der anregenden Strahlung abhängt.
Bei den in dieser Arbeit untersuchten Systemen handelt es sich um adsorbierte Moleküle, die hochgeordnete Schichten auf kristallinen Edelmetalloberflächen bilden. Im Fall eindomänigen Wachstums liefern die parallel orientierten Moleküle identische Photoemissionssignale. Kommt es hingegen zur Ausbildung von Rotations- und Spiegeldomänen, stellt die gemessene Impulsverteilung eine Superposition der unterschiedlichen Einzelbeiträge dar. Somit lassen sich Rückschlüsse auf die Orientierungen der Moleküle auf den Substraten ziehen. Diese Charakterisierung molekularer Adsorptionsgeometrien wird anhand verschiedener Modellsysteme vorgestellt.
Variiert man die Energie der anregenden Strahlung und somit den Radius der hemisphärischen Schnitte durch den Impulsraum, ist es möglich den Fourierraum des untersuchten Molekülorbitals dreidimensional abzubilden. Kombiniert man die gemessenen Intensitäten mit Informationen über die Phase der Wellenfunktion im Impulsraum, die durch zusätzliche Experimente oder rechnerisch gewonnen werden können, lässt sich durch eine Fouriertransformation ein dreidimensionales Bild des Orbitals generieren, wie Schritt für Schritt gezeigt wird.
Im Zuge eines Photoemissionsprozesses kann das Molekül in einen angeregten vibronischen Zustand übergehen. Mittels Photoemissionsexperimenten mit hoher Energieauflösung lassen sich Unterschiede zwischen den Impulsverteilungen der schwingenden Moleküle und denen im vibronischen Grundzustand feststellen. Ein Vergleich der Messdaten mit Simulationen kann die Identifikation der angeregten Schwingungsmode ermöglichen, was eine neue Methode darstellt, Erkenntnisse über die Elektron-Phonon-Kopplung in molekularen Materialien zu gewinnen.
In dieser Arbeit wurden zwei Aspekte der Femtochemie mit den Methoden der Femtosekunden--Laserspektroskopie untersucht. Dabei wurden folgende Ziele verfolgt: Einerseits sollte die jüngst entwickelte Technik der adaptiven Pulsformung auf das Problem bindungsselektiver Photodissoziationsreaktionen angewandt werden, zum Anderen bestand die Aufgabe darin, die nichtadiabatische, photoinduzierte Dynamik am Beispiel der Photoisomerisierung von Stilben mit Hilfe der Photoelektronenspektroskopie zeitaufgelöst zu untersuchen. Die Methode der adaptiven Pulsformung wurde mit dem Ziel eingesetzt, eine bindungsselektive Photodissoziation zu verwirklichen. Dazu wurde diese Technik in Verbindung mit einem massenspektroskopischen Nachweis der Photofragmente verwendet. Die Experimente wurden an einigen Spezies der Methylhalogenide CH2XY (X,Y = Halogen) durchgeführt. Diese Verbindungen wurden als Modellsysteme gewählt, da sich gezeigt hat, dass auf Grund stark gekoppelter konkurrierender Dissoziationskanäle durch modenselektive Laseranregung keine Kontrolle erreicht werden kann. Mit dem hier durchgeführten Experiment an CH2ClBr wurde erfolgreich erstmals die Anwendung der adaptiven Femtosekunden-Pulsformung auf das Problem einer bindungsselektiven Photodissoziation demonstriert. Dabei konnte eine Steigerung der Dissoziation der stärkeren Kohlenstoff-Halogen Bindung um einen Faktor zwei erreicht werden. Weiterhin konnte experimentell gezeigt werden, dass das optimierte Produktverhältnis nicht durch eine einfache Variation der Laserpulsdauer oder Laserpulsenergie erzielt werden kann. Es wurde ein möglicher Mechanismus für die Kontrolle diskutiert, der im Gegensatz zu einem unmodulierten Laserpuls die Wellenpaketdynamik auf neutralen dissoziativen Potentialflächen zur Steuerung des Produktverhältnisses involviert. Wie sich aus einer genaueren Analyse des Fragmentspektrums ergab, wird durch den optimalen Laserpuls die Dissoziation in komplexer Weise moduliert. Dies zeigte sich z.B. auch durch eine Änderung des Isotopenverhältnisses in der Ausbeute des dissoziierten Br-Liganden vor und nach der Optimierung. Dieser Frage nach einer isotopenselektiven Photodissoziation wurde in einem weiteren Experiment an CH2Br2 nachgegangen. Dabei konnte jedoch nur eine geringe Variation von etwa fünf Prozent gegenüber dem natürlichen Isotopenverhältnis festgestellt werden. Als größtes experimentelles Problem stellte sich dabei die starke Intensitätsabhängigkeit der Produktausbeuten heraus, was die Suche nach der optimalen Pulsform stark einschränkte. Anhand des molekularen Photodetachments CH2I2-->CH2+I2 wurde gezeigt, dass durch die Analyse der optimalen Pulsformen Informationen über die Dynamik dieses Prozesses gewonnen werden können. Dazu wurde zunächst in einem Pump-Probe-Experiment die Dynamik der I2-Fragmentation nach einer Mehrphotonen-Anregung von CH2I2 mit 266nm Laserpulsen untersucht. Dieses Experiment ergab, dass das Molekül über einen angeregten Zwischenzustand auf einer sehr schnellen Zeitskala über Dissoziationskanälen zerfallen kann. Der dominante Kanal führt zu einer sequentiellen Abgabe einer der I-Liganden und resultiert in den Photoprodukten CH2I und I Im anderen Kanal, dem molekularen Photodetachment, werden die Photoprodukte I2 und CH2 gebildet. In einem Kontrollexperiment wurde dann versucht, das molekulare Photodetachment gegenüber dem dominanten sequentiellen Kanal mit geformten 800nm Laserpulsen zu optimieren. Es wurden Optimierungen mit dem Ziel der Maximierung der Ausbeute an den Photoprodukten I2 und CH2 gegenüber CH2I durchgeführt. Diese Experimente ergaben, dass für beide Fragmente des molekularen Photodetachments eine Steigerung des Produktverhältnisses um etwa einen Faktor drei möglich ist. Dabei zeigte sich, dass eine Maximierung auf ein Produktverhältnis (z.B. I2/CH2I) eine Steigerung des anderen um etwa den gleichen Faktor hervorruft. Dies ist ein deutlicher Hinweis, dass beide Photoprodukte über denselben Dissoziationskanal gebildet werden. Ein weiterer inweis wurde aus der Analyse der optimalen Pulsformen erhalten: In beiden Fällen weisen diese eine markante Doppelpulsstruktur mit einem zeitlichen Abstand von etwa 400fs auf. Dies erinnert stark an die Situation des Pump-Probe--Experiments, wo durch die Analyse des transienten Signals ebenfalls eine optimale Verzögerungszeit zwischen dem Pump- und Probe-Laserpuls von etwa 400fs ermittelt werden konnte, bei der die Produktverhältnisse gerade maximal sind. Im Vergleich zur Massenspektroskopie liefert die Photoelektronenspektroskopie in der kinetischen Energie der Photoelektronen eine zusätzliche Messgröße, die direkt Informationen über die Kerngeometrie des Systems liefern kann. Mit dieser Technik wurde die trans-cis-Photoisomerisierung von Stilben im ersten elektronisch angeregten Zustand S1(1Bu) zeitaufgelöst untersucht. Dabei ging es speziell um die Frage nach der Existenz eines weiteren 1Bu Zustandes, der in neueren theoretischen Untersuchungen diskutiert wurde. In einem Pump-Probe-Experiment wurde dazu das im Molekularstrahl präparierte trans-Stilben durch einen 266nm Laserpuls angeregt und die Dynamik durch einen weiteren 266nm Laserpuls abgefragt. Im Photoelektronenspektrum konnten zwei signifikante Beiträge mit unterschiedlicher Dynamik gefunden werden. Das transiente Signal des ersten Beitrags weist eine Zeitkonstante von etwa 20ps auf und konnte eindeutig der Isomerisierung des S1 Zustandes zugeordnet werden. Im Gegensatz dazu zeigte das Signal des zweiten Beitrags eine Zeitkonstante von 100fs. Dieses Signal könnte aus der Ionisation des S2 Zustandes resultieren, welcher bislang experimentell nicht beobachtet werden konnte.
The approach of using the combination of Ultraviolet (UPS) and Inverse Photoemission (IPS) to determine the transport levels in thin films of organic semiconductors is the scope of this work. For this matter all influences on the peak position and width in Photoelectron Spectroscopy are discussed with a special focus on organic semiconductors. Many of these influences are shown with experimental results of the investigation of diindenoperylene on Ag(111). These findings are applied to inorganic semiconductors silicon in order to establish the use of UPS and IPS on a well-understood system. Finally, the method is used to determine the transport level of several organic semiconductors (PTCDA, Alq3, CuPc, DIP, PBI-H4) and the corresponding exciton binding energies are calculated by comparison to optical absorption data.
The projects presented in this thesis cover the examination of the electronic and structural properties of organic thin films at noble metal-organic interfaces. Angle-resolved photoemission spectroscopy is used as the primary investigative tool due to the connection of the emitted photoelectrons to the electronic structure of the sample. The surveyed materials are of relevance for fundamental research and practical applications on their own, but also serve as archetypes for the photoemission techniques presented throughout the four main chapters of this thesis. The techniques are therefore outlined with their adaptation to other systems in mind and a special focus on the proper description of the final state.
The most basic description of the final state that is still adequate for the evaluation of photoemission data is a plane wave. Its simplicity enables a relatively intuitive interpretation of photoemission data, since the initial and final state are related to one another by a Fourier transform and a geometric factor in this approximation. Moreover, the initial states of some systems can be reconstructed in three dimensions by combining photoemission measurements at various excitation energies. This reconstruction can even be carried out solely based on experimental data by using suitable iterative algorithms.
Since the approximation of the final state in the photoemission process by a plane wave is not valid in all instances, knowledge on the limitations of its applicability is indispensable. This can be gained by a comparison to experimental data as well as calculations with a more detailed description of the photoemission final state. One possible appraoch is based on independently emitting atoms where the coherent superposition of partial, atomic final states produces the total final state. This approach can also be used for more intricate studies on organic thin films. To this end, experimental data can be related to theoretical calculations to gain extensive insights into the structural and electronic properties of molecules in organic thin films.
In this thesis, thin-film solar cells on the basis of Cu(In,Ga)(S,Se)2 (CIGSSe) were investigated.
Until today, most high efficient CIGSSe-based solar cells use a toxic and wetchemical deposited CdS buffer layer, which doesn’t allow a dry inline production. However, a promising and well-performing alternative buffer layer, namely indium sulfide, has been found which doesn’t comprise these disadvantages. In order to shed light on these well-performing devices, the surfaces and in particular the interfaces which play a major role for the charge carrier transport are investigated in the framework of this thesis. Both, the chemical and electronic properties of the solar cells’ interfaces were characterized.
In case of the physical vapor deposition of an InxSy-based buffer layer, the cleaning step of the CdS chemical-bath deposition is not present and thus changes of the absorber surface have to be taken into account. Therefore, adsorbate formation, oxidation, and segregation of absorber elements in dependence of the storing temperature and the humidity are investigated in the first part of this thesis.
The efficiencies of CIGSSe-based solar cells with an InxSy buffer layer depend on the nominal indium concentration x and display a maximum for x = 42 %. In this thesis, InxSy samples with a nominal indium concentration of 40.2% ≤ x ≤ 43.2% were investigated by surface-sensitive and surface-near bulk-sensitive techniques, namely with photoemission spectroscopy (PES) and x-ray emission spectroscopy (XES). The surfaces of the films were found to be sulfur-poor and indium-rich in comparison with stoichiometric In2S3. Moreover, a direct determination of the band alignment at the InxSy/CISSe interface in dependence of the nominal indium concentration x was conducted with the help of PES and inverse PES (IPES) and a flat band alignment was found for x = 42 %.
In order to study the impact of a heat treatment as it occurs during subsequent cell process steps, the indium sulfide-buffered absorbers were annealed for 30 minutes under UHV conditions at 200 °C after the initial data set was taken. Besides a reported enhanced solar cell performance, a significant copper diffusion from the absorber into the buffer layer takes place due to the thermal treatment. Accordingly, the impact of the copper diffusion on the hidden InxSy/CISSe interface was discussed and for x = 40.2% a significant cliff (downwards step in the conduction band) is observed. For increasing x, the alignment in the conduction band turns into a small upwards step (spike) for the region 41% ≤ x ≤ 43.2%. This explains the optimal solar cell performance for this indium contents.
In a further step, the sodium-doped indium sulfide buffer which leads to significantly higher efficient solar cells was investigated. It was demonstrated by PES/IPES that the enhanced performance can be ascribed to a significant larger surface band gap in comparison with undoped InxSy. The occurring spike in the Na:InxSy/CISSe band alignment gets reduced due to a Se diffusion induced by the thermal treatment. Furthermore, after the thermal treatment the sodium doped indium sulfide layer experiences a copper diffusion which is reduced by more than a factor of two compared to pure InxSy.
Next, the interface between the Na:InxSy buffer layer and the i-ZnO (i = intrinsic, non-deliberately doped), as a part of the transparent front contact was analyzed. The i-ZnO/Na:InxSy interface shows significant interdiffusion, leading to the formation of, e.g., ZnS and hence to a reduction of the nominal cliff in the conduction band alignment.
In the last part of this thesis, the well-established surface-sensitive reflective electron energy loss spectroscopy (REELS) was utilized to study the CIGSSe absorber, the InxSy buffer, and annealed InxSy buffer surfaces. By fitting the characteristic inelastic scattering cross sections λK(E) with Drude-Lindhard oscillators the dielectric function was identified. The determined dielectric functions are in good agreement with values from bulk-sensitive optical measurements on indium sulfide layers. In contrast, for the chalcopyrite-based absorber significant differences appear. In particular, a substantial larger surface band gap of the CIGSSe surface of E^Ex_Gap = (1.4±0.2) eV in comparison with bulk values is determined. This provides for the first time an independent verification of earlier PES/IPES results. Finally, the electrons’ inelastic mean free paths l for the three investigated surfaces are compared for different primary energies with theoretical values and the universal curve.
Elektronen-Korrelationen und Elektron-Phonon-Kopplung in einem nanostrukturierten Adsorbatsystem
(2004)
In meiner Arbeit werden die Auswirkungen von Vielteilcheneffekten in einem niedrigdimensionalen Adsorbatsystem untersucht. Ein solches System kann als einfaches Modellsystem zum Verständnis der Vielteilcheneffekte dienen. Mit Hilfe der Photoelektronenspektroskopie und Rastertunnelspektroskopie kann die Lebensdauer der Quasiteilchen direkt gemessen werden. An quasi-nulldimensionalen Quantenpunkten lässt sich außerdem der Einfluss der Dimensionalität und der Strukturgröße auf die Korrelationseffekte und Kopplungsstärken der Elektronen messen. Das Adsorbatsystem Stickstoff auf Kupfer (Cu(100)c(2x2)N) ist hierfür ideal geeignet. Bei der Adsorption von Stickstoff auf Cu(100) bilden sich auf Grund starker Verspannungen durch die inkommensurate c(2x2)-Bedeckung Stickstoff-Inseln mit einer typischen Größe von 5x5 nm². Auf diesen quasi-nulldimensionalen Quantenpunkten lässt sich lokal mit der Rastertunnelspektroskopie die elektronische Zustandsdichte messen. In den STS-Spektren und Bildern sind typische diskrete Eigenzustände eines Quantentrogs zu beobachten. Mit einem Modell gedämpfter, quasifreier Elektronen ist es gelungen, diese Eigenzustände zu simulieren und wichtige physikalische Größen, wie die effektive Masse, die Bindungsenergie und die mittlere Lebensdauer der Elektronen in den Inseln zu bestimmen. Mit Hilfe der Photoelektronenspektroskopie können zahlreiche adsorbatinduzierte Zustände identifiziert und die zweidimensionale Bandstruktur des Adsorbatsystems gemessen werden. Die Elektron-Phonon-Kopplung spielt in dem Stickstoff-Adsorbatsystem eine wichtige Rolle: Temperaturabhängige Messungen der zweidimensionalen Zustände lassen auf eine sehr starke Kopplung schließen mit Werten bis zu 1,4 für die Kopplungskonstante. Dabei ist die Kopplungsstärke wesentlich von der Lokalisierung der Adsorbatzustände abhängig. In der Nähe der Fermikante zeigt ein Adsorbatzustand eine außergewöhnliche Linienform. Die Spektralfunktion kann selbst bei recht hohen Temperaturen von 150 K mit dem Realteil der Selbstenergie der Elektron-Phonon-Kopplung beschrieben werden. Für die Phononenzustandsdichte wird dabei das Einstein-Modell verwendet auf Grund des dominierenden Anteils der adsorbatinduzierten optischen Phononen. Die Kopplungsstärke und der Beitrag der Elektron-Elektron und Elektron-Defekt-Streuung werden aus diesen Daten extrahiert. Auf Grund der sehr starken Elektron-Phonon-Kopplung könnte man spekulieren, ob sich in der Oberfläche Cooper-Paare bilden, deren Anziehung über ein optisches Adsorbatphonon vermittelt würde, und so eine exotische Oberflächen-Supraleitung verursachen.
In der vorliegenden Arbeit wurden Untersuchungen an Dünnschichtsolarzellen auf der Basis von Cu(In,Ga)(S,Se)2, der heute vielversprechendsten Dünnschichttechnologie, durchgeführt. Für eine weitere Optimierung der Zellen ist ein detailliertes Verständnis ihrer chemischen, elektronischen und strukturellen Eigenschaften notwendig. Insbesondere die in dieser Arbeit untersuchten Eigenschaften an den Grenzflächen der Zelle sind aufgrund ihrer zentralen Rolle für den Ladungsträgertransport von besonderem Interesse. Bei den vorliegenden Untersuchungen kamen verschiedene Spektroskopien zum Einsatz. Mit einer Kombination von Photoelektronenspektroskopie und Inverser Photoelektronenspektroskopie war es möglich, sowohl eine direkte Bestimmung der Valenz- und Leitungsbandanpassungen an den untersuchten Grenzflächen durchzuführen als auch Oberflächenbandlücken zu bestimmen. Die Messungen wurden durch die volumenempfindliche Röntgenemissionsspektroskopie ideal ergänzt, die - wie diese Arbeit zeigt - zusammen mit der Photoelektronenspektroskopie besonders nützlich bei der Analyse des Durchmischungsverhaltens an Grenzflächen oder auch des Einflusses chemischer Behandlungen auf die chemischen und elektronischen Eigenschaften von Oberflächen ist. Im ersten Teil der Arbeit wurden vier Grenzflächen in Proben auf der Basis des Cu(In,Ga)(S,Se)2-Absorbers von Shell Solar (München) untersucht. Es konnte dabei zunächst das Durchmischungsverhalten an der CdS/CuIn(S,Se)2-Grenzfläche in Abhängigkeit des S-Gehaltes an der Absorberoberfläche untersucht werden. Bei Messungen an der i-ZnO/CdS-Grenzfläche wurde ein flacher Leitungsbandverlauf gefunden, zudem konnte eine Durchmischung an dieser Grenzfläche ausgeschlossen werden. Eine besondere Herausforderung stellten die Messungen an der Grenzfläche des Absorbers zum Molybdänrückkontakt dar, da diese Grenzfläche nach ihrem Entstehen unweigerlich unter der etwa 1-2 um dicken Absorberschicht begraben liegt. Durch geeignetes Abspalten des Absorbers vom Rückkontakt gelang es, diese Grenzfläche freizulegen und zu spektroskopieren. Die Untersuchungen zur Vorbehandlung des Shell-Absorbers mit einer ammoniakalischen Cd-Lösung dienten dem Verständnis der positiven Einflüsse dieser Behandlung auf den Zellwirkungsgrad. Dabei wurde neben verschiedenen Reinigungswirkungen auf den Absorber als wichtigster Befund die Bildung einer sehr dünnen CdS-Schicht und, für hohe Cd-Konzentrationen, einer zusätzlichen Cd(OH)2-Schicht auf der Absorberoberfläche nachgewiesen. Die gewonnenen Erkenntnisse über die Cd-Behandlung haben eine besondere Bedeutung für die Untersuchung der Grenzfläche des Absorbers und einer mit ILGAR ("Ion Layer Gas Reaction") hergestellten Zn(O,OH)-Pufferschicht. An dieser Grenzfläche wurde die Bandanpassung mit und ohne vorherige Cd-Behandlung des Absorbers vermessen. Wird die Bandanpassung ohne Vorbehandlung noch durch Adsorbate auf dem Absorber dominiert, wobei man ein "Cliff" im Leitungsband findet, so ist der Leitungsbandverlauf für die Grenzfläche mit Cd-behandeltem Absorber flach, was im Einklang mit den sehr guten Wirkungsgraden steht, die mit solchen Zellen erreicht werden. Im zweiten Teil der Arbeit wurden Messungen an Dünnschichtsolarzellen mit selenfreiem Cu(In,Ga)S2 Absorber diskutiert. Ein Problem des Cu(In,Ga)S2-Systems besteht heute noch darin, daß die offene Klemmenspannung geringer ausfällt, als dies aufgrund der im Vergleich zu CuInSe2 größeren Bandlücke zu erwarten wäre. Modelle, die dies auf eine ungünstige Bandanpassung an der CdS/Cu(In,Ga)S2-Grenzfläche zurückführen, konnten in dieser Arbeit durch die Messung der Leitungsbandanpassung, die ein deutlich "Cliff"-artiges Verhalte aufweist, bestätigt werden. Untersuchungen des Einflusses unterschiedlicher Oberflächenzusammensetzungen auf die chemischen und elektronischen Eigenschaften der Cu(In,Ga)Se2-Absorberoberfläche ergaben, wie sich die Bandlücke des Absorbers mit wachsender Kupferverarmung vergrößert und gleichzeitig die Bandverbiegung zunimmt. Im letzten, rein grundlagenorientierten Teil dieser Arbeit wurden Röntgenabsorptions- und resonante Röntgenemissionsmessungen an CdS und ZnS im Vergleich zu von A. Fleszar berechneten theoretischen Spektren, die unter Berücksichtigung der Übergangsmatrixelemente aus einer LDA-Bandstruktur berechnet wurden, diskutiert. Es konnten dabei sowohl Anregungen in exzitonische Zustände als auch kohärente Emission mit Informationen über die Bandstruktur gefunden werden. Auch war es möglich, die Lebensdauern verschiedener Valenzlochzustände zu bestimmen. Es zeigt sich, daß so die Bestimmung einer unteren Grenze für die Bandlücke möglich ist, für eine genaue Bestimmung bei den untersuchten Verbindungen jedoch ein Vergleich mit theoretischen Berechnungen notwendig ist.
In oxidischen Heterostrukturen rufen Neuordnung von Ladung und Spin eine Vielzahl von unerwarteten physikalischen Eigenschaften hervor. Die Möglichkeit, Leitfähigkeit, Magnetismus oder auch Hochtemperatur-Supraleitung zu kontrollieren, machen diese künstlich hergestellten Materialien vor allem in Hinblick auf eine zukünftige Anwendung in der Mikroelektronik äußerst interessant. Dies erfordert jedoch ein grundsätzliches Verständnis für die zugrunde liegenden Mechanismen. Die vorliegende Doktorarbeit befasst sich mit photonengestützter Spektroskopie, die einen direkten Zugang zur elektronischen Struktur dieser Heterostruktursysteme ermöglicht. Ein weiteres Ziel ist es, geeignete spektroskopische Methoden zur Charakterisierung der vergrabenen Schichten zu etablieren.
Zwei prototypische oxidische Mehrschichtsysteme stehen im Zentrum der hier vorgestellten Untersuchungen. Das LaAlO3/SrTiO3-Heterostruktursystem weist ab einer kritischen LaAlO3-Filmdicke an der Grenzfläche ein zweidimensionales Elektronensystem mit hochmobilen Ladungsträgern auf. Als treibender Mechanismus wird die elektronische Rekonstruktion diskutiert. Im Rahmen dieser Arbeit wurde dieses zweidimensionale Elektronensystem mithilfe der Photoelektronenspektroskopie und der resonanten inelastischen Röntgenstreuung charakterisiert. Die daraus bestimmten Ladungsträgerdichten weisen im Vergleich mit Daten aus Transportmessungen auf eine Koexistenz von lokalisierten und mobilen Ladungsträgern an der Grenzfläche hin. Die Analyse von Rumpfniveau- und Valenzbandspektren zeigt, dass man zur Erklärung der experimentellen Resultate ein modifiziertes Bild der elektronischen Rekonstruktion benötigt, bei der Sauerstofffehlstellen an der LaAlO3-Oberfläche als Ladungsreservoir dienen könnten. Mithilfe der resonanten Photoelektronenspektroskopie war es möglich, die metallischen Zustände am chemischen Potential impulsaufgelöst zu spektroskopieren. So gelang es erstmals, die vergrabene Fermi-Fläche einer oxidischen Heterostruktur zu vermessen. Außerdem konnten Titan-artige Zustände identifiziert werden, die höchstwahrscheinlich durch Sauerstofffehlstellen im SrTiO3 lokalisiert sind. Diese werden als mögliche Quelle für den Ferromagnetismus interpretiert, der mit der supraleitenden Phase in der LaAlO3/SrTiO3-Heterostruktur koexistiert.
Bei dem anderen hier untersuchten Mehrschichtsystem handelt es sich um die LaNiO3-LaAlO3-Übergitterstruktur. Der Einbau des metallischen LaNiO3 in eine Heterostruktur ist aufgrund seiner Nähe zu einer korrelationsinduzierten isolierenden Phase hinsichtlich einer kontrollierten Ausbildung von neuartigen Phasen besonders interessant. In der Tat beobachtet man unterhalb einer LaNiO3-Schichtdicke von vier Einheitszellen einen kontinuierlichen Metall-Isolator-Übergang, der sich in den Valenzbandspektren durch einen Verlust an Quasiteilchenkohärenz äußert. Auch wenn die impulsaufgelösten
Daten am Fermi-Niveau durch Photoelektronenbeugung beeinflusst sind, so lässt sich dennoch eine Fermi-Fläche identifizieren. Ihre Topologie bietet die Möglichkeit eines Fermi-Flächen-Nestings mit der Ausbildung einer Spindichtewelle. Die Resultate unterstützen die Hinweise auf eine magnetische Ordnung im zweidimensionalen Grundzustand.
A plethora of novel material concepts are currently being investigated in the condensed matter research community. Some of them hold promise to shape our everyday world in a way that silicon-based semiconductor materials and the related development of semiconductor devices have done in the past. In this regard, the last decades have witnessed an explosion of studies concerned with so called ‘’quantum materials’’ with emerging novel functionalities. These could eventually lead to new generations of electronic and/or spintronic devices. One particular material class, the so called topological materials, play a central role. As far as their technological applicability is concerned, however, they are still facing outstanding challenges to date.
Predicted for the first time in 2005 and experimentally verified in 2007, two-dimensional topological insulators (2D TIs) (a.k.a. quantum spin Hall insulators) exhibit the outstanding property of hosting spin-polarized metallic states along the boundaries of the insulating 2D bulk material, which are protected from elastic single-particle backscattering and give rise to the quantum spin Hall effect (QSHE). Owing to these peculiar properties the QSHE holds promise for dissipationless charge and/or spin transport. However, also in today’s best 2D TIs the observation of the QSHE is still limited to cryogenic temperatures of maximum 100 K. Here, the discovery of bismuthene on SiC(0001) has marked a milestone towards a possible realization of the QSHE at or beyond room-temperature owing to the massively increased electronic bulk energy gap on the order of 1 eV. This thesis is devoted to and motivated by the goal of advancing its synthesis and to build a deeper understanding of its one-particle and two-particle electronic properties that goes beyond prior work.
Regarding the aspect of material synthesis, an improved growth procedure for bismuthene is elaborated that increases the domain size of the material considerably (by a factor of ≈ 3.2 - 6.5 compared to prior work). The improved film quality is an important step towards any future device application of bismuthene, but also facilitates all further basic studies of this material.
Moreover, the deposition of magnetic transition metals (Mn and Co) on bismuthene is investigated. Thereby, the formation of ordered magnetic Bi-Mn/Co alloys is realized, their structure is resolved with scanning tunneling microscopy (STM), and their pristine electronic properties are resolved with scanning tunneling spectroscopy (STS) and photoemission spectroscopy (PES). It is proposed that these ordered magnetic Bi-Mn/Co-alloys offer the potential to study the interplay between magnetism and topology in bismuthene in the future.
In this thesis, a wide variety of spectroscopic techniques are employed that aim to build an understanding of the single-particle, as well as two-particle level of description of bismuthene's electronic structure. The techniques involve STS and angle-resolved PES (ARPES) on the one hand, but also optical spectroscopy and time-resolved ARPES (trARPES), on the other hand. Moreover, these experiments are accompanied by advanced numerical modelling in form of GW and Bethe-Salpeter equation calculations provided by our theoretical colleagues. Notably, by merging many experimental and theoretical techniques, this work sets a benchmark for electronic structure investigations of 2D materials in general.
Based on the STS studies, electronic quasi-particle interferences in quasi-1D line defects in bismuthene that are reminiscent of Fabry-Pérot states are discovered. It is shown that they point to a hybridization of two pairs of helical boundary modes across the line defect, which is accompanied by a (partial) lifting of their topological protection against elastic single-particle backscattering.
Optical spectroscopy is used to reveal bismuthene's two-particle elecronic structure. Despite its monolayer thickness, a strong optical (two-particle) response due to enhanced electron-hole Coulomb interactions is observed. The presented combined experimental and theoretical approach (including GW and Bethe-Salpeter equation calculations) allows to conclude that two prominent optical transitions can be associated with excitonic transitions derived from the Rashba-split valence bands of bismuthene. On a broader scope this discovery might promote further experiments to elucidate links of excitonic and topological physics.
Finally, the excited conduction band states of bismuthene are mapped in energy and momentum space employing trARPES on bismuthene for the first time. The direct and indirect band gaps are succesfully extracted and the effect of excited charge carrier induced gap-renormalization is observed. In addition, an exceptionally fast excited charge carrier relaxation is identified which is explained by the presence of a quasi-metallic density of states from coupled topological boundary states of domain boundaries.
Im Rahmen dieser Arbeit wurden mit Hilfe von hochaufgelöster ARPES die Auswirkungen verschiedener intrinsischer und extrinsischer Einflüsse auf zweidimensionale elektronische Zustände untersucht: Eine Änderung der Morphologie aufgrund einer (2 × 1)-Rekonstruktion bewirkt beim OFZ von Au(110) im Vergleich zur nicht-rekonstruierten Oberfläche eine Verschiebung der Bindungsenergie von ca. 700meV. Dieses Verhalten wurde in LDA-slab-layer-Rechungen reproduziert und durch gezielte Modifikation der Oberflächenstruktur sowie kontrollierte Beeinflussung des OFZ durch die Adsorbate Ag, Na und Au verstanden. Eine Linienbreitenanalyse der sehr scharfen Minoritäts-QWS in dünnen Fe- Filmen auf W(110) ermöglichte eine Abschätzung der Elektron-Elektron- Wechselwirkung und eine Bestimmung der Elektron-Phonon-Kopplungskonstanten. Die starke Anisotropie der Dispersion der QWS ist des weiteren durch den Vergleich mit GGA-slab-layer-Rechnungen als intrinsische Eigenschaft dieser Zustände identifiziert worden. Mit Hilfe eines erweiterten PAM wurde zudem die k⊥-Dispersion des, den QWS zugrunde liegenden Volumenbandes, bestimmt. Die spinabhängigen Einflussfaktoren Spin-Orbit- und Austausch-Wechselwirkung sowie deren Kombination wurden am Beispiel des OFZ von dünnen Au-Filmen auf Ni(111), sowie an QWS in dünnen Ni-Filmen auf W(110) untersucht. Die in SPR-KKR-Photoemissionrechungen gefundene leichte Asymmetrie der spinaufgelösten Dispersion wurde in den spinintegrierten ARPESMessungen nicht beobachtet. Ab 9ML Au-Bedeckung konnte die Rashba- Aufspaltung des OFZ aufgelöst werden. Eine durch das W(110)-Substrat induzierte Rashba-Aufspaltung wurde bei sp-artigen QWS in dünnen Ni- Filmen beobachtet, welche jedoch mit weiteren Strukturen hybridisieren, was eine eindeutige Aussage über die tatsächliche Natur der Aufspaltung erschwert.
Photoelectron spectroscopy proves as a versatile tool for investigating various aspects of the electronic structure in strongly correlated electron systems. Influencing the manifestation of strong correlation in Ce-based surface alloys is the main task of this work. It is shown, that the manifestation of the Kondo ground state is influenced by a multitude of parameters such as the choice of the metal binding partner in binary Ce compounds, the surface alloy layer thickness and accompanying variations in the lattice structure as well as the interfaces to substrate or vacuum. Gaining access to these parameters allows to directly influence essential state variables, such as the f level occupancy nf or the Kondo temperature TK.
The center of this work are the intermetallic thin films of CePt5/Pt(111) and CeAgx/Ag(111). By utilizing different excitation energies, photoemission spectroscopy provides access to characteristic features of Kondo physics in the valence band, such as the Kondo resonance and its spin-orbit partner at the Fermi level, as well as the multiplet structure of the Ce 3d core levels. In this work both approaches are applied to CePt5/Pt(111) to determine nf and TK for a variety of surface alloy layer thicknesses. A temperature dependent study of the Ce 3d core levels allows to determine the systems TK for the different layer thicknesses. This leads to TK ≈200–270K in the thin layer thickness regime and TK >280K for larger layer thicknesses. These results are confirmed by fitting the Ce 3d multiplet based on the Gunnarsson-Schönhammer formalism for core level spectroscopy and additionally by valence band photoemission spectra of the respective Kondo resonances. The influence of varying layer thickness on the manifestation of strong correlation is subsequently studied for the surface alloy CeAgx/Ag(111). Furthermore, the heavy element Bi is added, to investigate the effects of strong spin-orbit coupling on the electronic structure of the surface alloy.
The present thesis is concerned with molecular beam epitaxy of magnetite (Fe3O4) thin films on semiconducting substrates and the characterization of their structural, chemical, electronic, and magnetic properties. Magnetite films could successfully be grown on ZnO substrates with high structural quality and atomically abrupt interfaces. The films are structurally almost completely relaxed exhibiting nearly the same in-plane and out-of-plane lattice constants as in the bulk material. Films are phase-pure and show only small deviations from the ideal stoichiometry at the surface and in some cases at the interface. Growth proceeds via wetting layer plus island mode and results in a domain structure of the films. Upon coalescence of growing islands twin-boundaries (rotational twinning) and anti-phase boundaries are formed. The overall magnetization is nearly bulk-like, but shows a slower approach to saturation, which can be ascribed to the reduced magnetization at anti-phase boundaries. However, the surface magnetization which was probed by x-ray magnetic circular dichroism was significantly decreased and is ascribed to a magnetically inactive layer at the surface. Such a reduced surface magnetization was also observed for films grown on InAs and GaAs. Magnetite could also be grown with nearly ideal iron-oxygen stoichiometry on InAs substrates. However, interfacial reactions of InAs with oxygen occur and result in arsenic oxides and indium enrichment. The grown films are of polycrystalline nature. For the fabrication of Fe3O4/GaAs films, a postoxidation of epitaxial Fe films on GaAs was applied. Growth proceeds by a transformation of the topmost Fe layers into magnetite. Depending on specific growth conditions, an Fe layer of different thickness remains at the interface. The structural properties are improved in comparison with films on InAs, and the resulting films are well oriented along [001] in growth direction. The magnetic properties are influenced by the presence of the Fe interface layer as well. The saturation magnetization is increased and the approach to saturation is faster than for films on the other substrates. We argue that this is connected to a decreased density of anti-phase boundaries because of the special growth method. Interface phases, viz. arsenic and gallium oxides, are quantified and different growth conditions are compared with respect to the interface composition.
The present thesis is concerned with the impact of alkali metal-doping on the electronic structure of semiconducting organic thin films. The organic molecular systems which have been studied are the polycyclic aromatic hydrocarbons picene, pentacene, and coronene. Motivated by reports about exceptional behavior like superconductivity and electronic correlations of their alkali metal-doped compounds, high quality films fabricated from the above named molecules have been studied. The electronic structure of the pristine materials and their doped compounds has been investigated using photoelectron spectroscopy. Core level and valence band studies of undoped films yield excellent photoemission spectra agreeing with or even outperforming previously reported data from the literature. Alkali metal-doping manifests itself in a uniform manner in the electronic structure for all probed samples: Opposed to reports from the literature about metallicity and even superconductivity in alkali metal-doped picene, pentacene, and coronene, all films exhibit insulating nature with an energy gap of the order of one electron-volt. Remarkably, this is independent of the doping concentration and the type of dopant, i.e., potassium, cesium, or sodium. Based on the interplay between narrow bandwidths in organic semiconductors and sufficiently high on-molecule Coulomb repulsion, the non-metallicity is attributed to the strong influence of electronic correlations leading to the formation of a Mott insulator. In the case of picene, this is consolidated by calculations using a combination of density functional theory and dynamical mean-field theory. Beyond the extensive considerations regarding electronic correlations, further intriguing aspects have been observed. The deposition of thin picene films leads to the formation of a non-equilibrium situation between substrate and film surface. Here, the establishment of a homogeneous chemical potential is hampered due to the only weak van der Waals-interactions between the molecular layers in the films. Consequently, spectral weight is measurable above the reference chemical potential in photoemission. Furthermore, it has been found that the acceptance of additional electrons in pentacene is limited. While picene and coronene are able to host up to three extra electrons, in pentacene the limit is already reached for one electron. Finally, further extrinsic effects, coming along with alkali metal-doping, have been scrutinized. The oxidation of potassium atoms induced by the reaction with molecular oxygen in the residual gas of the ultra-high vacuum system turned out to significantly influence the electronic structure of alkali metal-doped picene and coronene. Moreover, also the applied X-ray and UV irradiation caused a certain impact on the photoemission spectra. Surprisingly, both effects did not play a role in the studies of potassium-doped pentacene.
Eingebettet in ein Konzept zum Aufbau eines Hochleistungs-Feldeffekt-Transistors auf der Basis organischer Halbleiter (OFET), werden in der vorliegenden Dissertation fundamentale Aspekte des Aufbaus und der Funktion organischer Halbleiter-Bauelemente erforscht. Die Kenntnis, welche maximale Leistungsfähigkeit organische Halbleiter in OFETs prinzipiell erreichen können, ist von elementarem Interesse, sowohl um Transportmodelle zu verfeinern, als auch um Mechanismen und Optimierungsansätze zu finden, mit denen OFETs generell verbessert werden können. Es wird das Ziel verfolgt, sich der maximalen Leistungsfähigkeit eines gegebenen Materialsystems anzunähern. Aufwendige Präparationsstrategien werden für dieses Ziel bewusst in Kauf genommen, auch wenn deshalb vermutlich kein direkter Zugang zu Anwendungen eröffnet wird. An geeigneten Modellsystemen können einzelne wichtige Aspekte, wie die elektronische Struktur an Metallkontakten und im organischen Halbleitervolumen sowie das Wachstum von Schichten und Kristalliten organischer Halbleitermoleküle auf einkristallinen Isolatorsubstraten charakterisiert werden. Die Ergebnisse dieser grundlegenden Experimente fließen in den Aufbau des geplanten OFETs ein. Auf dem Weg zu einem funktionsfähigen Bauelement mit bestmöglichen Eigenschaften wurden wesentliche Fortschritte erzielt. Der erste Schwerpunkt dieser Arbeit ist die Untersuchung elektronischer Niveaus an Metallkontakt-Grenzflächen und im Volumen des Modellsystems PTCDA/Ag(111) mit Zwei-Photonen-Photoelektronenspektroskopie (2PPE). Die 2PPE-Spektren der PTCDA/Ag(111)-Grenzfläche sind dominiert durch einen unbesetzten, parallel zur Grenzfläche stark dispersiven Shockley-artigen Grenzflächenzustand (IS), der sich durch die Chemisorption der Moleküle auf der Ag(111)-Oberfläche bildet. Bei der Untersuchung von intramolekular angeregten elektronischen Zuständen von PTCDA mit 2PPE zeigen sich im Vergleich zum Untergrund der Spektren schwache Signale, die jedoch mit einer geeigneten Beschreibung des Untergrunds davon separiert werden können. Besonders interessant ist in diesem Zusammenhang das LUMO, das bei einer Anregung aus dem HOMO eine um 0,4 eV stärkere energetische Absenkung zeigt, als bei der Anregung aus dem HOMO-1. Dies kann durch die unterschiedlichen exzitonischen Zustände, die bei den Anregungen entstehen, erklärt werden. Neben den metallischen Kontakten ist die Grenzfläche zwischen organischem Halbleiter und Gate-Isolator entscheidend für die Leistungsfähigkeit eines OFETs. Am Beispiel des Wachstums von Diindenoperylen-Molekülen (DIP) auf einkristallinen Al2O3-Substraten wurde die morphologische und strukturelle Ausbildung von organischen Halbleiterschichten mit optischer Mikroskopie und Rasterkraftmikroskopie untersucht. Das Wachstum kann als stark anisotrop charakterisiert werden. Die – im Vergleich zu den Bindungsenergien mit dem Substrat – deutlich größeren Bindungsenergien innerhalb der DIP-(001)-Kristallebenen führen bei Substrattemperaturen von 440 K zu einem Wachstum von aufrecht stehenden Molekülen. Es zeigt sich, dass die während des Wachstums herrschende Substrattemperatur einen entscheidenden Einfluss auf die Morphologie der DIP-Schicht hat. So nimmt die Inselgröße von etwa 200 nm bei 350 K auf über 700 nm bei 450 K zu. Außerdem wird ein Ansteigen der Filmrauheit, besonders ab etwa 430 K, beobachtet, das auf den Übergang zu einem anderen Wachstumsmodus bei diesen Temperaturen hinweist. Bei etwas höheren Temperaturen von etwa 460 K wird das Wachstum von DIP-Kristalliten beobachtet. Dabei können – abhängig von den gewählten Präparationsparametern – drei unterschiedliche Kristallit-Typen unterschieden werden: „Mesa-Kristallite“ mit lateralen Abmessungen von mehreren Mikrometern, „Dendritische Kristallite“, die eine verzweigte Struktur aufweisen, die mithilfe der Wachstumskinetik erklärt werden kann und „Schichtkristallite“, deren Morphologie sich durch teilweise starke Krümmungen auszeichnet. Insgesamt zeigt sich, dass die Morphologie kristalliner Strukturen durch eine feine Balance der Präparationsparameter Substrattemperatur, Aufdampfrate, Substratmorphologie und Substratreinheit bestimmt wird, so dass kleine Änderungen dieser Parameter zu deutlich unterschiedlichen Kristallitformen führen. Schließlich wird das Konzept zum Aufbau eines Hochleistungs-OFET vorgestellt und in Details weiterentwickelt. Fortschritte werden in erster Linie bei der Präparation der Gate-Elektrode erzielt, die unter dem Al2O3-Substrat angebracht werden soll. Für die Ausdünnung des Substrats wird eine Bohrtechnik weiterentwickelt und mit einer nasschemischen Ätzmethode kombiniert, so dass Isolatorstärken von unter 10 µm erreicht werden können. Erste wenige OFETs wurden auf der Basis dieses Substrats präpariert, allerdings ohne dass die Bauteile Feldeffekte zeigten. Verbesserungsmöglichkeiten werden diskutiert.
Realization and Spectroscopy of the Quantum Spin Hall Insulator Bismuthene on Silicon Carbide
(2022)
Topological matter is one of the most vibrant research fields of contemporary solid state physics since the theoretical prediction of the quantum spin Hall effect in graphene in 2005. Quantum spin Hall insulators possess a vanishing bulk conductivity but symmetry-protected, helical edge states that give rise to dissipationless charge transport.
The experimental verification of this exotic state of matter in 2007 lead to a boost of research activity in this field, inspired by possible ground-breaking future applications.
However, the use of the quantum spin Hall materials available to date is limited to cryogenic temperatures owing to their comparably small bulk band gaps.
In this thesis, we follow a novel approach to realize a quantum spin Hall material with a large energy gap and epitaxially grow bismuthene, i.e., Bi atoms adopting a honeycomb lattice, in a \((\sqrt{3}\times\sqrt{3})\) reconstruction on the semiconductor SiC(0001). In this way, we profit both from the honeycomb symmetry as well as the large spin-orbit coupling of Bi, which, in combination, give rise to a topologically non-trivial band gap on the order of one electronvolt.
An in-depth theoretical analysis demonstrates that the covalent bond between the Si and Bi atoms is not only stabilizing the Bi film but is pivotal to attain the quantum spin Hall phase.
The preparation of high-quality, unreconstructed SiC(0001) substrates sets the basis for the formation of bismuthene and requires an extensive procedure in ultra-pure dry H\(_2\) gas. Scanning tunneling microscopy measurements unveil the (\(1\times1\)) surface periodicity and smooth terrace planes, which are suitable for the growth of single Bi layers by means of molecular beam epitaxy. The chemical configuration of the resulting Bi film and its oxidation upon exposure to ambient atmosphere are inspected with X-ray photoelectron spectroscopy.
Angle-resolved photoelectron spectroscopy reveals the excellent agreement of probed and calculated band structure. In particular, it evidences a characteristic Rashba-splitting of the valence bands at the K point. Scanning tunneling spectroscopy probes signatures of this splitting, as well, and allows to determine the full band gap with a magnitude of \(E_\text{gap}\approx0.8\,\text{eV}\).
Constant-current images and local-density-of-state maps confirm the presence of a planar honeycomb lattice, which forms several domains due to different, yet equivalent, nucleation sites of the (\(\sqrt{3}\times\sqrt{3}\))-Bi reconstruction.
Differential conductivity measurements demonstrate that bismuthene edge states evolve at atomic steps of the SiC substrate. The probed, metallic local density of states is in agreement with the density of states expected from the edge state's energy dispersion found in density functional theory calculations - besides a pronounced dip at the Fermi level.
By means of temperature- and energy-dependent tunneling spectroscopy it is shown that the spectral properties of this suppressed density of states are successfully captured in the framework of the Tomonaga-Luttinger liquid theory and most likely originate from enhanced electronic correlations in the edge channel.
The rich phase diagram of transition metal oxides essentially roots in the many body physics arising from strong Coulomb interactions within the underlying electron system.
Understanding such electronic correlation effects remains challenging for modern solid state physics, therefore experimental data is required for further progress in the field. For this reason, spectroscopic investigations of prototypical correlated materials are the scope of this thesis. The experimental methods focus on photoelectron spectroscopy, and the test materials are the correlated metal SrVO\(_3\) and the Mott insulator LaTiO\(_3\), both of which are fabricated as high quality thin films.
In SrVO\(_3\) thin films, a reduction of the film thickness induces a dimensional crossover from the metallic into the Mott insulating phase. In this thesis, an extrinsic chemical contribution from a surface over-oxidation is revealed that emerges additionally to the intrinsic change of the effective bandwidth usually identified to drive the transition. The two contributions are successfully disentangled by applying a capping layer that prevents the oxidation, allowing for a clean view on the dimensional crossover in fully stoichiometric samples. Indeed, these stoichiometric layers exhibit a higher critical thickness for the onset of the metallic phase than the bare and therefore over-oxidized thin films.
For LaTiO\(_3\) thin films, the tendency to over-oxidize is even stronger. An uncontrolled oxygen diffusion from the substrate into the film is found to corrupt the electronic properties of LaTiO\(_3\) layers grown on SrTiO\(_3\). The Mott insulating phase is only detected in stoichiometric films fabricated on more suitable DyScO\(_3\) substrates. In turn, it is demonstrated that a \(controlled\) incorporation of excess oxygen ions by increasing the oxygen growth pressure is an effective way of \(p\) doping the material which is used to drive the band filling induced Mott transition.
Gaining control of the oxygen stoichiometry in both materials allows for a systematic investigation of correlation effects in general and of the Mott transition in particular. The investigations are realized by various photoelectron spectroscopy techniques that provide a deep insight into the electronic structure. Resonant photoemission not only gives access to the titanium and vanadium related partial density of states of the valence band features, but also shows how the corresponding signal is enhanced by tuning the photon energy to the \(L\) absorption threshold. The enhanced intensity turns out to be very helpful for probing the Fermi surface topology and band dispersions by means of angular-resolved photoemission. The resulting momentum resolved electronic structure verifies central points of the theoretical description of the Mott transition, viz. the renormalization of the band width and a constant Luttinger volume in a correlated metal as the Mott phase is approached.
Spin- and angle-resolved photoelectron spectroscopy is the prime method to investigate
spin polarized electronic states at solid state surfaces. In how far the spin polarization
of an emitted photoelectron reflects the intrinsic spin character of an electronic state is
the main question in the work at hand. It turns out that the measured spin polarization
is strongly influenced by experimental conditions, namely by the polarization of the
incoming radiation and the excitation energy. The photoemission process thus plays a
non-negligible role in a spin-sensitive measurement. This work is dedicated to unravel
the relation between the result of a spin-resolved measurement and the spin character
in the ground state and, therefore, to gain a deep understanding of the spin-dependent
photoemission process.
Materials that exhibit significant spin-splittings in their electronic structure,
owing to a strong spin-orbit coupling, serve as model systems for the investigations in
this work. Therefore, systems with large Rashba-type spin-splittings as BiTeI(0001)
and the surface alloys BiAg2/Ag(111) and PbAg2/Ag(111) are investigated. Likewise,
the surface electronic structure of the topological insulators Bi2Te2Se(0001) and
Bi2Te3(0001) are analyzed.
Light polarization dependent photoemission experiments serve as a probe of the
orbital composition of electronic states. The knowledge of the orbital structure helps
to disentangle the spin-orbital texture inherent to the different surface states, when
in addition the spin-polarization is probed. It turns out that the topological surface
state of Bi2Te2Se(0001) as well as the Rashba-type surface state of BiTeI(0001) exhibit
chiral spin-textures associated with the p-like in-plane orbitals. In particular, opposite
chiralities are coupled to either tangentially or radially aligned p-like orbitals,
respectively. The results presented here are thus evidence that a coupling between
spin- and orbital part of the wave function occurs under the influence of spin-orbit
coupling, independent of the materials topology.
Systematic photon energy dependent measurements of the out-of-plane spin polarization
of the topological surface state of Bi2Te3(0001) reveal a strong dependence and
even a reversal of the sign of the photoelectron spin polarization with photon energy.
Similarly, the measured spin component perpendicular to the wave vector of the surface
state of BiAg2/Ag(111) shows strong modulations and sign reversals when the photon energy is changed. In BiAg2/Ag(111) the variations in the photoelectron spin
polarization are accompanied by significant changes and even a complete suppression
of the photoemission intensity from the surface state, indicating that the variations of
the spin polarization are strongly related to the photoemission cross section.
This relation is finally analyzed in detail by employing a simple model, which is
based on an evaluation of the transition matrix elements that describe the presented
experiments. The model shows that the underlying cause for the observed photoelectron
spin reversals can be found in the coupling of the spin structure to the spatial part
of the initial state wave function, revealing the crucial role of spin-orbit interaction
in the initial state wave function. The model is supported by ab initio photoemission
calculations, which show strong agreement with the experimental results.
Diese Arbeit befasst sich mit der Untersuchung und Manipulation von Halbleitern, bei
denen die Spin-Bahn-Kopplung (SBK) in Kombination mit einem Bruch der strukturellen Inversionssymmetrie zu einer impulsabhängigen Spinaufspaltung der Bandstruktur führt. Von besonderem Interesse ist hierbei der Zusammenhang zwischen der spinabhängigen elektronischen Struktur und der strukturellen Geometrie. Dieser wird durch eine Kombination komplementärer, oberflächensensitiver Messmethoden - insbesondere Rastertunnelmikroskopie
(STM) und Photoelektronenspektroskopie (PES) - an geeigneten
Modellsystemen untersucht. Der experimentelle Fokus liegt dabei auf den polaren Halbleitern BiTeX (X =I, Br, Cl). Zusätzliche Experimente werden an dünnen Schichten der topologischen Isolatoren (TI) Bi1,1-xSb0;9+xSe3 (x = 0. . . 1,1) und Bi2Te2Se durchgeführt. Die inversionsasymmetrische Kristallstruktur in BiTeX führt zur Existenz zweier nicht-äquivalenter Oberflächen mit unterschiedlicher Terminierung (Te oder X) und invertierter atomarer Stapelfolge. STM-Aufnahmen der Oberflächen gespaltener Einkristalle belegen für BiTeI(0001) eine Koexistenz beider Terminierungen auf einer Längenskala von etwa 100 nm, die sich auf Stapelfehler im Kristallvolumen zurückführen lassen. Diese Domänen sind groß genug, um eine vollständig entwickelte Banddispersion auszubilden und erzeugen daher eine Kombination der Bandstrukturen beider Terminierungen bei räumlich integrierenden Messmethoden. BiTeBr(0001) und BiTeCl(0001) hingegen zeichnen sich durch homogene Terminierungen auf einer makroskopischen Längenskala aus. Atomar
aufgelöste STM-Messungen zeigen für die drei Systeme unterschiedliche Defektdichten der einzelnen Lagen sowie verschiedene strukturelle Beeinflussungen durch die Halogene. PES-Messungen belegen einen starken Einfluss der Terminierung auf verschiedene Eigenschaften der Oberflächen, insbesondere auf die elektronische Bandstruktur, die Austrittsarbeit sowie auf die Wechselwirkung mit Adsorbaten. Die unterschiedliche Elektronegativität der Halogene resultiert in verschieden starken Ladungsübergängen innerhalb der kovalent-ionisch gebundenen BiTe+ X- Einheitszelle. Eine erweiterte Analyse der Oberflächeneigenschaften ist durch die Bedampfung mit Cs möglich, wobei eine Änderung der elektronischen Struktur durch die Wechselwirkung mit dem Alkalimetall studiert wird. Modifiziert man die Kristallstruktur sowie die chemische Zusammensetzung von BiTeI(0001) nahe der Oberfläche durch Heizen im Vakuum, bewirkt dies eine Veränderung der Bandstruktur in zwei Schritten. So führt zunächst der Verlust von Iod zum Verlust der Rashba-Aufspaltung, was vermutlich durch eine Aufhebung der Inversionsasymmetrie in der Einheitszelle verursacht wird. Anschließend bildet sich eine neue Kristallstruktur, die topologisch nichttriviale Oberflächenzustände hervorbringt. Der Umordnungsprozess betrifft allerdings nur die Kristalloberfläche - im Volumen bleibt die inversionsasymmetrische
Einheitszelle erhalten. Einem derartigen Hybridsystem werden bislang unbekannte elektronische Eigenschaften vorausgesagt. Eine systematische Untersuchung von Dünnschicht-TIs, die mittels Molekularstrahlepitaxie (MBE) erzeugt wurden, zeigt eine Veränderung der Morphologie und elektronischen Struktur in Abhängigkeit von Stöchiometrie und Substrat. Der Vergleich zwischen MBE und gewachsenen Einkristallen offenbart deutliche Unterschiede. Bei einem der Dünnschichtsysteme tritt sogar eine lokal inhomogene Zustandsdichte im Bindungsenergiebereich des topologischen Oberflächenzustands auf.
Transition metal oxides (TMO) represent a highly interesting material class as
they exhibit a variety of different emergent phenomena including multiferroicity and
superconductivity. These effects result from a significant interplay of charge, spin
and orbital degrees of freedom within the correlated d-electrons. Oxygen vacancies
(OV) at the surface of certain d0 TMO release free charge carriers and prompt the
formation of a two-dimensional electron gas (2DEG). Barium titanate (BaTiO3) is a
prototypical and promising d0 TMO. It displays ferroelectricity at room temperature
and features several structural phase transitions, from cubic over tetragonal (at
room temperature) and orthorhombic to rhombohedral. The spontaneous electric
polarization in BaTiO3 can be used to manipulate the physical properties of adjacent
materials, e.g. in thin films. Although the macroscopic properties of BaTiO3 are studied
in great detail, the microscopic electronic structure at the surface and interface of
BaTiO3 is not sufficiently understood yet due to the complex interplay of correlation
within the d states, oxygen vacancies at the surface, ferroelectricity in the bulk and
the structural phase transitions in BaTiO3.
This thesis investigates the electronic structure of different BaTiO3 systems by
means of angle-resolved photoelectron spectroscopy (ARPES). The valence band of
BaTiO3 single crystals is systematically characterized and compared to theoretical
band structure calculations. A finite p-d hybridization of titanium and oxygen states
was inferred at the high binding energy side of the valence band. In BaTiO3 thin films,
the occurrence of spectral weight near the Fermi level could be linked to a certain
amount of OV at the surface which effectively dopes the host system. By a systematic
study of the metallic surface states as a function of temperature and partial oxygen
pressure, a model was established which reflects the depletion and accumulation of
charge carriers at the surface of BaTiO3. An instability at T ~ 285K assumes a volatile
behavior of these surface states.
The ferroelectricity in BaTiO3 allows a control of the electronic structure at the interface
of BaTiO3-based heterostructures. Therefore, the interface electronic structure
of Bi/BaTiO3 was studied with respect to the strongly spin-orit coupled states in Bi by
also including a thickness dependent characterization. The ARPES results, indeed,
confirm the presence of Rashba spin-split electronic states in the bulk band gap of the ferroelectric substrate. By varying the film thickness in Bi/BaTiO3, it was able to modify
the energy position and the Fermi vector of the spin-split states. This observation
is associated with the appearance of an interface state which was observed for very
low film thickness. Both spectral findings suggest a significant coupling between the
Bi films and BaTiO3.