Refine
Has Fulltext
- yes (61)
Is part of the Bibliography
- yes (61)
Year of publication
Document Type
- Doctoral Thesis (61)
Keywords
- Biomaterial (7)
- Hydrogel (7)
- Tissue Engineering (6)
- Calciumphosphate (5)
- Knochenzement (5)
- 3D-Druck (4)
- Nanopartikel (4)
- Ringöffnungspolymerisation (4)
- Calciumphosphat (3)
- Elektrospinnen (3)
Institute
- Abteilung für Funktionswerkstoffe der Medizin und der Zahnheilkunde (37)
- Graduate School of Life Sciences (13)
- Fakultät für Chemie und Pharmazie (11)
- Institut für Funktionsmaterialien und Biofabrikation (8)
- Lehrstuhl für Tissue Engineering und Regenerative Medizin (6)
- Institut für Organische Chemie (2)
- Institut für Pharmazie und Lebensmittelchemie (2)
- Klinik und Poliklinik für Hals-, Nasen- und Ohrenkrankheiten, plastische und ästhetische Operationen (2)
- Klinik und Poliklinik für Mund-, Kiefer- und Plastische Gesichtschirurgie (2)
- Klinik und Polikliniken für Zahn-, Mund- und Kieferkrankheiten (2)
Sonstige beteiligte Institutionen
In Tissue Engineering, scaffolds composed of natural polymers often show a distinct lack in stability. The natural polymer gelatin is highly fragile under physiological conditions, nevertheless displaying a broad variety of favorable properties. The aim of this study was to fabricate electrospun gelatin nanofibers, in situ functionalized and stabilized during the spinning process with highly reactive star polymer NCO-sP(EO-stat-PO) (“sPEG”). A spinning protocol for homogenous, non-beaded, 500 to 1000 nm thick nanofibers from different ratios of gelatin and sPEG was successfully established. Fibers were subsequently characterized and tested with SEM imaging, tensile tests, water incubation, FTIR, EDX, and cell culture. It was shown that adding sPEG during the spinning process leads to an increase in visible fiber crosslinking, mechanical stability, and stability in water. The nanofibers were further shown to be biocompatible in cell culture with RAW 264.7 macrophages.
The aim of this thesis was the application of the functional prepolymer NCO-sP(EO-stat-PO) for the development of new biomaterials. First, the influence of the star-shaped polymers on the mechanical properties of biocements and bone adhesives was investigated. 3-armed star-shaped macromers were used as an additive for a mineral bone cement, and the influence on the mechanical properties was studied. Additionally, a previously developed bone adhesive was examined regarding cytocompatibility. The second topic was the examination of novel functionalization steps which were performed on the surface of electrospun fibers modified with NCO-sP(EO-stat-PO). This established method of functionalizing electrospun meshes was advanced regarding the modification with proteins which was then demonstrated in a biological application. Two different kinds of antibodies were immobilized on the fiber surface in a consecutive manner and the influence of these proteins on the cell behavior was investigated. The final topic involved the quantification of surface-bound peptide sequences. By functionalization of the peptides with the UV-reactive molecule 2-mercaptopyridine it was possible to quantify this compound via UV measurements by cleavage of disulfide bridges and indirectly draw conclusions about the number of immobilized peptides.
In the field of mineral biocements and bone adhesives, NCO-sP(EO-stat-PO) was able to influence the setting behavior and mechanical performance of mineral bone cements based on calcium phosphate chemistry. The addition of NCO-sP(EO-stat-PO) resulted in a pseudo-ductile fracture behavior due to the formation of a hydrogel network in the cement, which was then mineralized by nanosized hydroxyapatite crystals following cement setting. Accordingly, a commercially available aluminum silicate cement from civil engineering could be modified.
In addition, it could be shown that the use of NCO-sP(EO-stat-PO) is beneficial for adjusting specific material properties of bone adhesives. Here, the crosslinking behavior of the prepolymer in an aqueous medium was exploited to form an interpenetrating network (IPN) together with a photochemically curing poly(ethylene glycol) dimethacrylate (PEGDMA) matrix. This could be used for the development of a bone adhesive with an improved adhesion to bone in a wet environment. The developed bone adhesive was further investigated in terms of possible influences of the initiator systems. In addition, the material system was tested for cytocompatibility by using different cell lines.
Moreover, the preparation of electrospun fiber meshes via solution electrospinning consisting of poly(lactide-co-glycolide) (PLGA) as a backbone polymer and NCO-sP(EO-stat-PO) as functional additive is an established method for the application of the meshes as a replacement of the native extracellular matrix (ECM). In general, these fibers reveal diameters in the nanometer range, are protein and cell repellent due to the hydrophilic properties of the prepolymer and show a specific biofunctionalization by immobilization of peptide sequences. Here, the isocyanate groups presented on the fiber surface after electrospinning were used to carry out various functionalization steps, while retaining the properties of protein and cell repellency. The modification of the electrospun fibers involved the immobilization of analogs or antagonists of tumor necrosis factor (TNF) and the indirect detection of these by interaction with a light-producing enzyme. Here, a multimodal modification of the fiber surface with RGD to mediate cell adhesion and two different antibodies could be achieved. After culturing the cell line HT1080, the pro- or anti-inflammatory response of cells could be detected by IL-8 specific ELISA measurements.
Furthermore, the quantification of molecules on the surface of electrospun fibers was investigated. It was tested whether the detection by means of super-resolution microscopy would be possible. Therefore, experiments were performed with short amino acid sequences such as RGD for quantification by fluorescence microscopy. Based on earlier results, in which a UV-spectrometrically active molecule was used to detect the quantification of RGD, it was shown that short peptides can also be quantified in a small scale on flat functional substrates (2D) such as NCO-sP(EO-stat-PO) hydrogel coatings, and modified electrospun fibers produced from PLGA and NCO-sP(EO-stat-PO) (3D). In addition, a collagen sequence was used to prove that a successful quantification can be carried out as well for longer peptide chains.
These studies have revealed that NCO-sP(EO-stat-PO) can serve as a functional additive for many applications and should be considered for further studies on the development of novel biomaterials. The rapid crosslinking reaction, the resulting hydrogel formation and the biocompatibility are to be mentioned as positive properties, which makes the prepolymer interesting for future applications.
The aim of the work was the development of thiol-ene cross-linked hydrogels based on functionalized poly(glycidol)s (PG) and hyaluronic acid (HA) for extrusion based 3D bioprinting. Additionally, the functionalization of the synthesized PG with peptides and the suitability of these polymers for physically cross-linked gels were investigated, in a proof of principle study in order to demonstrate the versatile use of PG polymers in hydrogel development.
First, the precursor polymers of the different hydrogel systems were synthesized. For thiol-ene cross-linked hydogels, linear allyl-functionalized PG (P(AGE-co-G)) and three different thiol-(SH-)functionalized polymers, ester-containing PG-SH (PG SHec), ester-free PG-SH (PG-SHef) and HA-SH were synthesized and analysed, The degree of functionalization of these polymers was adjustable.
For physically cross-linked hydrogels, peptide-functionalized PG (P(peptide-co-G)), was synthesized through polymer analogue thiol-ene modification of P(AGE-co-G).
Subsequently, thiol-ene cross-linked hydrogels were prepared with the synthesized thiol- and allyl-functionalized polymers. Depending on the origin of the used polymers, two different systems were obtained: on the one hand synthetic hydrogels consisting of PG-SHec/ef and P(AGE-co-G) and on the other hand hybrid gels, consisting of HA-SH and P(AGE-co-G). In synthetic gels, the degradability of the gels was determined by the applied PG-SH. The use of PG-SHec resulted in hydrolytically degradable hydrogels, whereas the cross-linking with PG-SHef resulted in non-degradable gels.
The physical properties of these different hydrogel systems were determined by swelling, mechanical and diffusion studies and subsequently compared among each other. In swelling studies the differences of degradable and non-degradable synthetic hydrogels as well as the differences of synthetic compared to hybrid hydrogels were demonstrated.
Next, the stiffness and the swelling ratios (SR) of the established hydrogel systems were examined in dependency of different parameters, such as incubation time, polymer concentration and UV irradiation. In general, these measurements revealed the same trends for synthetic and hybrid hydrogels: an increased polymer concentration as well as prolonged UV irradiation led to an increased network density. Moreover, it was demonstrated that the incorporation of additional non-bound HMW HA hampered the hydrogel cross-linking resulting in gels with decreased stiffness and increased SR. This effect was strongly dependent on the amount of additional HMW HA.
The diffusion of different molecular weight fluorescein isothiocyanate-dextran (FITC-dextran) through hybrid hydrogels (with/without HMW HA) gave information about the mesh size of these gels. The smallest FITC-dextran (4 kDa) completely diffused through both hydrogel systems within the first week, whereas only 55 % of 40 kDa and 5-10 % HMW FITC-dextrans (500 kDa and 2 MDa) could diffuse through the networks.
The applicability of synthetic and hybrid hydrogels for cartilage regeneration purpose was investigated through by biological examinations. It was proven that both gels support the survival of embedded human mesenchymal stromal cells (hMSCs) (21/28 d in vitro culture), however, the chondrogenic differentiation was significantly improved in hybrid hydrogels compared to synthetic gels. The addition of non-bound HMW HA resulted in a slightly less distinct chondrogenesis.
Lastly the printability of the established hydrogel systems was examined. Therefore, the viscoelastic properties of the hydrogel solutions were adjusted by incorporation of non-bound HMW HA. Both systems could be successfully printed with high resolution and high shape fidelity.
The introduction of the double printing approach with reinforcing PCL allowed printing of hydrogel solutions with lower viscosities. As a consequence, the amount of additional HMW HA necessary for printing could be reduced allowing successful printing of hybrid hydrogel solutions with embedded cells. It was demonstrated that the integrated cells survived the printing process with high viability measured after 21 d. Moreover, by this reinforcing technique, robust hydrogel-containing constructs were fabricated.
In addition to thiol-ene cross-linked hydrogels, hydrogel cross-linking via ionic interactions was investigated with a hybrid hydrogel based on HMW HA and peptide-functionalized PG. Rheological measurements revealed an increase in the viscosity of a 2 wt.% HMW HA solution by the addition of peptide-functionalized PG. The increase in viscosity could be attributed to the ionic interactions between the positively charge PG and the negatively charge HMW HA.
In conclusion, throughout this thesis thiol-ene chemistry and PG were introduced as promising cross-linking reaction and polymer precursor for the field of biofabrication. Furthermore, the differences of hybrid and synthetic hydrogels as well as chemically and physically cross-linked hydrogels were demonstrated.
Moreover, the double printing approach was demonstrated to be a promising tool for the fabrication of robust hydrogel-containing constructs. It opens the possibility of printing hydrogels that were not printable yet, due to too low viscosities.
Biofabrication is an advancing new research field that might, one day, lead to complex products like tissue replacements or tissue analogues for drug testing. Although great progress was made during the last years, there are still major hurdles like new types of materials and advanced processing techniques. The main focus of this thesis was to help overcoming this hurdles by challenging and improving existing fabrication processes like extrusion-based bioprinting but also by developing new techniques. Furthermore, this thesis assisted in designing and processing materials from novel building blocks like recombinant spider silk proteins or inks loaded with charged nanoparticles.
A novel 3D printing technique called Melt Electrospinning Writing (MEW) was used in Chapter 3 to create tubular constructs from thin polymer fibers (roughly 12 μm in diameter) by collecting the fibers onto rotating and translating cylinders. The main focus was put on the influence of the collector diameter and its rotation and translation on the morphology of the constructs generated by this approach. In a first step, the collector was not moving and the pattern generated by these settings was analyzed. It could be shown that the diameter of the stationary collectors had a big impact on the morphology of the constructs. The bigger the diameter of the mandrel (smallest collector diameters 0.5 mm, biggest 4.8 mm) got, the more the shape of the generated footprint converged into a circular one known from flat collectors. In a second set of experiments the mandrels were only rotated. Increasing the rotational velocity from 4.2 to 42.0 rpm transformed the morphology of the constructs from a figure-of-eight pattern to a sinusoidal and ultimately to a straight fiber morphology. It was possible to prove that the transformation of the pattern was comparable to what was known from increasing the speed using flat collectors and that at a critical speed, the so called critical translation speed, straight fibers would appear that were precisely stacking on top of each other. By combining rotation and translation of the mandrel, it was possible to print tubular constructs with defined winding angles. Using collections speeds close to the critical translation speed enabled higher control of fiber positioning and it was possible to generate precisely stacked constructs with winding angles between 5 and 60°.
In Chapter 4 a different approach was followed. It was based on extrusion-based bioprinting in combination with a hydrogel ink system. The ink was loaded with nanoparticles and the nanoparticle release was analyzed. In other words, two systems, a printable polyglycidol/hyaluronic acid ink and mesoporous silica nanoparticles (MSN), were combined to analyze charge driven release mechanism that could be fine-tuned using bioprinting. Thorough rheological evaluations proved that the charged nanoparticles, both negatively charged MSN-COOH and positively charged MSN-NH2, did not alter the shear thinning properties of the ink that revealed a negative base charge due to hyaluronic acid as one of its main components. Furthermore, it could be shown that the particles did also not have a negative effect on the recovery properties of the material after exposure to high shear. During printing, the observations made via rheological testing were supported by the fact that all materials could be printed at the same settings of the bioprinter. Using theses inks, it was possible to make constructs as big as 12x12x3 mm3 composed of 16 layers. The fiber diameters produced were about 627±31 μm and two-component constructs could be realized utilizing the two hydrogel print heads of the printer to fabricate one hybrid construct. The particle distribution within those constructs was homogeneous, both from a microscopic and a macroscopic point of view. Particle release from printed constructs was tracked over 6 weeks and revealed that the print geometry had an influence on the particle release. Printed in a geometry with direct contact between the strands containing different MSN, the positively charged particles quickly migrated into the strand previously containing only negatively charged MSN-COOH. The MSN-COOH seemed to be rather released into the surrounding liquid and also after 6 weeks no MSN-COOH signal could be detected in the strand previously only containing MSN-NH2. In case of a geometry without direct contact between the strands, the migration of the positively charged nanoparticles into the MSN-COOH containing strand was strongly delayed. This proved that the architecture of the printed construct can be used to fine-tune the particle release from nanoparticle containing printable hydrogel ink systems.
Chapter 5 discusses an approach using hydrogel inks based on recombinant spider silk proteins processed via extrusion-based bioprinting. The ink could be applied for printing at protein concentrations of 3 % w/v without the addition of thickeners or any post process crosslinking. Both, the recombinant protein eADF4(C16) and a modification introducing a RGD-sequence to the protein (eADF4(C16)-RGD), could be printed revealing a very good print fidelity. The RGD modification had positive effect on the adhesion of cells seeded onto printed constructs. Furthermore, human fibroblasts encapsulated in the ink at concentrations of 1.2 million cells per mL did not alter the print fidelity and did not interfere with the crosslinking mechanism of the ink. This enabled printing cell laden constructs with a cell survival rate of 70.1±7.6 %. Although the cell survival rate needs to be improved in further trials, the approach shown is one of the first leading towards the shift of the window of biofabrication because it is based on a new material that does not need potentially harmful post-process crosslinking and allows the direct encapsulation of cells staying viable throughout the print process.
The aim of this thesis was the development of a multifunctional coating system for AuNPs based on thioether polymers, providing both excellent colloidal stability and a variable possibility to introduce functionalities for biological applications.
First, two thioether-polymer systems were synthesised as a systematic investigation into colloidal stabilisation efficacy. Besides commonly used monovalent poly(ethylene glycol) (PEG-SR), its structural analogue linear poly(glycidol) (PG-SR) bearing multiple statistically distributed thioether moieties along the backbone was synthesised. Additionally, respective thiol analogues (PEG-SH and PG-SH) were produced and applied as reference.
Successive modification of varyingly large AuNPs with aforementioned thiol- and thioether-polymers was performed via ligand exchange reaction on citrate stabilised AuNPs. An increased stabilisation efficacy of both thioether-polymers against biological and physiological conditions, as well as against freeze-drying compared to thiol analogues was determined.
Based on the excellent colloidal stabilisation efficacy and multi-functionalisability of thioether-PG, a plethora of functional groups, such as charged groups, hydrophilic/hydrophobic chains, as well as bio-active moieties namely diazirine and biotin was introduced to the AuNP surface. Moreover, the generic and covalent binding of diazirine-modified PG-SR with biomolecules including peptides and proteins was thoroughly demonstrated.
Lastly, diverse applicability and bioactivity of aforementioned modified particles in various studies was displayed, once more verifying the introduction of functionalities. On the one hand the electrostatic interaction of charged AuNPs with hydrogels based on hyaluronic acid was applied to tune the release kinetics of particles from three-dimensional scaffolds. On the other hand the strong complexation of siRNA onto two positively charged AuNPs was proven. The amount of siRNA payload was tuneable by varying the surface charge, ionic strength of the surrounding medium and the N/P ratio. Moreover, the biological activity and selectivity of the biotin-streptavidin conjugation was verified with respectively functionalised particles in controlled agglomeration test and in laser-triggered cell elimination experiments. In the latter, streptavidin-functionalised AuNPs resulted in excellent depletion of biotinylated cells whereas unfunctionalised control particles failed, excluding unspecific binding of these particles to the cell surface.
The key hypothesis of this work represented the question, if mimicking the zonal composition and structural porosity of musculoskeletal tissues influences invading cells positively and leads to advantageous results for tissue engineering. Conventional approaches in tissue engineering are limited in producing monolithic “scaffolds” that provide locally variating biological key signals and pore architectures, imitating the alignment of collagenous fibres in bone and cartilage tissues, respectively. In order to fill this gap in available tissue engineering strategies, a new fabrication technique was evolved for the production of scaffolds to validate the hypothesis.
Therefore, a new solidification based platform procedure was developed. This process comprises the directional solidification of multiple flowable precursors that are “cryostructured” to prepare a controlled anisotropic pore structure. Porous scaffolds are attained through ice crystal removal by lyophilisation. Optionally, electrostatic spinning of polymers may be applied to provide an external mesh on top or around the scaffolds. A consolidation step generates monolithic matrices from multi zonal structures. To serve as matrix for tissue engineering approaches or direct implantation as medical device, the scaffold is sterilized.
An Adjustable Cryostructuring Device (ACD) was successively developed; individual parts were conceptualized by computer aided design (CAD) and assembled. During optimisation, a significant performance improvement of the ACDs accessible external temperature gradient was achieved, from (1.3 ± 0.1) K/mm to (9.0 ± 0.1) K/mm. Additionally, four different configurations of the device were made available that enabled the directional solidification of collagenous precursors in a highly controlled manner with various sample sizes and shapes.
By using alginate as a model substance the process was systematically evaluated. Cryostructuring diagraphs were analysed yielding solidification parameters, which were associated to pore sizes and alignments that were determined by image processing. Thereby, a precise control over pore size and alignment through electrical regulation of the ACD could be demonstrated.
To obtain tissue mimetic scaffolds for the musculoskeletal system, collagens and calcium phosphates had to be prepared to serve as raw materials. Extraction and purification protocols were established to generate collagen I and collagen II, while the calcium phosphates brushite and hydroxyapatite were produced by precipitation reactions.
Besides the successive augmentation of the ACD also an optimization of the processing steps was crucial. Firstly, the concentrations and the individual behaviour of respective precursor components had to be screened. Together with the insights gained by videographic examination of solidifying collagen solutions, essential knowledge was gained that facilitated the production of more complex scaffolds. Phenomena of ice crystal growth during cryostructuring were discussed. By evolutionary steps, a cryostructuring of multi-layered precursors with consecutive anisotropic pores could be achieved and successfully transferred from alginate to collagenous precursors. Finally, very smooth interfaces that were hardly detectable by scanning electron microscopy (SEM) could be attained. For the used collagenous systems, a dependency relation between adjustable processing parameters and different resulting solidification morphologies was created.
Dehydrothermal-, diisocyanate-, and carbodiimide- based cross linking methods were evaluated, whereby the “zero length” cross linking by carbodiimide was found to be most suitable. Afterwards, a formulation for the cross linking solution was elaborated, which generated favourable outcomes by application inside a reduced pressure apparatus. As a consequence, a pore collapse during wet chemical cross linking could be avoided.
Complex monolithic scaffolds featuring continuous pores were fabricated that mimicked structure and respective composition of different areas of native tissues by the presence of biochemical key stimulants. At first, three types of bone scaffolds were produced from collagen I and hydroxyapatite with appropriate sizes to fit critical sized defects in rat femurs. They either featured an isotropic or anisotropic porosity and partly also contained glycosaminoglycans (GAGs). Furthermore, meniscus scaffolds were prepared by processing two precursors with biomimetic contents of collagen I, collagen II and GAGs. Here, the pore structures were created under boundary conditions, which allowed an ice crystal growth that was nearly orthogonal to the external temperature gradient. Thereby, the preferential alignment of collagen fibres in the natural meniscus tissue could be mimicked. Those scaffolds owned appropriate sizes for cell culture in well plates or even an authentic meniscus shape and size. Finally, osteochondral scaffolds, sized to either fit well plates or perfusion reactors for cell culture, were fabricated to mimic the composition of subchondral bone and different cartilage zones. Collagen I and the resorbable calcium phosphate brushite were used for the subchondral zone, whereas the cartilage zones were composed out of collagen I, collagen II and tissue mimetic contents of GAGs. The pore structure corresponded to the one that is dominating the volume of natural osteochondral tissue.
Energy dispersive X-ray spectroscopy (EDX) and SEM were used to analyse the composition and pore structure of the individual scaffold zones, respectively. The cross section pore diameters were determined to (65 ± 25) µm, (88 ± 35) µm and(93 ± 42) µm for the anisotropic, the isotropic and GAG containing isotropic bone scaffolds. Furthermore, the meniscus scaffolds showed pore diameters of (93 ± 21) µm in the inner meniscus zone and (248 ± 63) µm inside the outer meniscus zone. Pore sizes of (82 ± 25) µm, (83 ± 29) µm and (85 ± 39) µm were present inside the subchondral, the lower chondral and the upper chondral zone of osteochondral scaffolds. Depending on the fabrication parameters, the respective scaffold zones were also found to feature a specific micro- and nanostructure at their inner surfaces.
Degradation studies were carried out under physiological conditions and resulted in a mean mass loss of (0.52 ± 0.13) %, (1.56 ± 0.10) % and (0.80 ± 0.10) % per day for bone, meniscus and osteochondral scaffolds, respectively. Rheological measurements were used to determine the viscosity changes upon cooling of different precursors. Micro computer tomography (µ-CT) investigations were applied to characterize the 3D microstructure of osteochondral scaffolds. To obtain an osteochondral scaffold with four zones of tissue mimetic microstructure alignment, a poly (D, L-lactide-co-glycolide) mesh was deposited on the upper chondral zone by electrostatic spinning. In case of the bone scaffolds, the retention / release capacity of bone morphogenetic protein 2 (BMP-2) was evaluated by an enzyme linked immunosorbent assay (ELISA). Due to the high presence of attractive BMP binding sites, only less than 0.1 % of the initially loaded cytokine was released. The suitability of combining the cryostructuring process with 3D powder printed calcium phosphate substrates was evaluated with osteochondral scaffolds, but did not appear to yield more preferable results than the non-combined approach.
A new custom build confined compression setup was elaborated together with a suitable evaluation procedure for the mechanical characterisation under physiological conditions. For bone and cartilage scaffolds, apparent elastic moduli of (37.6 ± 6.9) kPa and (3.14 ± 0.85) kPa were measured. A similar behaviour of the scaffolds to natural cartilage and bone tissue was demonstrated in terms of elastic energy storage. Under physiological frequencies, less than 1.0 % and 0.8 % of the exerted energy was lost for bone and cartilage scaffolds, respectively. With average relaxation times of (0.613 ± 0.040) sec and (0.815 ± 0.077) sec, measured for the cartilage and bone scaffolds, they respond four orders of magnitude faster than the native tissues. Additionally, all kinds of produced scaffolds were able to withstand cyclic compression at un-physiological frequencies as high as 20 Hz without a loss in structural integrity.
With the presented new method, scaffolds could be fabricated whose extent in mimicking of native tissues exceeded the one of scaffolds producible by state of the art methods. This allowed a testing of the key hypothesis: The biological evaluation of an anisotropic pore structure in vivo revealed a higher functionality of immigrated cells and led finally to advantageous healing outcomes. Moreover, the mimicking of local compositions in combination with a consecutive anisotropic porosity that approaches native tissue structures could be demonstrated to induce zone specific matrix remodelling in stem cells in vitro. Additionally, clues for a zone specific chondrogenic stem cell differentiation were attained without the supplementation of growth factors.
Thereby, the hypothesis that an increased approximation of the hierarchically compositional and structurally anisotropic properties of musculoskeletal tissues would lead to an improved cellular response and a better healing quality, could be confirmed. With a special focus on cell free in situ tissue engineering approaches, the insights gained within this thesis may be directly transferred to clinical regenerative therapies.
Chemoselective poly(oxazolines) (POx) and poly[(oligo ethylene glycol) acrylates] were synthesized. An initiator was produced for the preparation of poly(oxazoline)s capable of participating in click chemistry reactions which allows the functionalization of the polymer at the α terminus which was confirmed by 1H NMR spectroscopy. The initiator was used for the polymerization of hydrophilic 2 methyl 2 oxazoline (MeOx), whereby chemoselective, alkyne functionalized polymers could be prepared for Cu-catalyzed azide–alkyne cycloaddition. The desired molecular weight could be achieved through the living, ring opening cationic polymerization and was confirmed by 1H NMR, SEC and MALDI ToF measurements. Polymers were terminated with piperidine if no further functionalization was needed, or with an ester derivate for enabling amine attachment in a subsequent step. In addition, polymers were functionalized by termination with NaN3 in order to provide the counterpart to the azide–alkyne reaction. IR spectroscopy was suitable for the azide detection. The coupling of polymers showed the reactivity and could be confirmed by SEC, 1H NMR and IR spectroscopy.
The composition of cysteine functionalized POx was completed by thiol–ene chemistry. Since the commercially available iso 2 propyl 2 oxazoline is not available for the cationic polymerization, 2 butenyl and 2 decenyl 2 oxazoline (ButenOx and DecenOx) were first prepared. The synthesis of both copolymers, based on MeOx could be confirmed by 1H NMR as well as with SEC, whereby narrow distributions with dispersities of 1.06 could be achieved. The cysteine functionalization of the copolymers was enabled by the creation of a thiazolidine component which could be synthesized by acetal and formyl protection of cysteine and subsequent functionalization with a thiol. The component enabled the reaction with a polymer by thiol–ene reaction which was started by the addition of dimethoxyphenyl-acetophenone and was catalyzed by irradiation with UV light. Both copolymers, with a shorter (polymers with BuenOx) and longer (polymers with DecenOx) hydrophobic sidechain could be functionalized. 1H NMR spectroscopic analysis showed a quantitative reaction with the thiazolidine derivate. After deprotection by acidic workup the desired, cysteine functionalized polymer could be isolated. Quantification of cysteine functions was ensured by a modified TNBSA assay, whereby the thiols were first oxidized in order to confirm an independent measurement of amine functions. Both, the TNBSA assay as well as the NMR measurement showed the desired number of cysteine residues.
The cytotoxicity of functionalized polymers with different compositions was tested by a luminescent cell viability assay (LCVA). Both, the amount of cysteine functions (5–10%) in the copolymers as well as the length of the hydrophobic side chain were varied. All polymers did not show cytotoxicity up to concentrations of 10 mg∙mL-1. The cell activity and cell numbers only decreased below 50% and 20% respectively, when copolymers with 5% cysteine and longer sidechains were measured, which was attributed to a contamination of the sample itself. The cooperation partner performed Native Chemical Ligation (NCL) with model peptides and purified the products by HPLC. A sterically non demanding peptide was synthesized, consisting of an aromatic amino acid and four glycine units. The aromatic unit was used for the quantification of the polymer–peptide conjugate in the 1H NMR spectroscopy. A polymer having five cysteine side chains has been fully implemented by NCL to a conjugate of one polymer with five peptides. A sterically more demanding peptide was additionally used and MALDI ToF measurements confirmed the successful conjugation.
Furthermore the cysteine functionalized polymer was used for nanogel synthesis. The thiol of the cysteine function was oxidized in an inverse mini-emulsion by H2O2, resulting in nanogels (~500 nm) which could be confirmed by SEM, AFM, DLS and NTA measurements.
Besides POx, oligo (ethylene glycol)acrylates (OEGA) were polymerized; by copolymerization with the reactive pentafluorophenyl acrylate (PFPA) reactive and amphiphilic polymers were obtained. The synthesis of PFPA could be confirmed spectroscopically by 1H , 19F NMR, and by FT IR. Copolymers were synthesized by RAFT polymerization with narrow dispersities. Functionalization with an amine functionalized thiazolidine led to a hydrophilic cysteine functionalized polymer after acidic deprotection. Apart from this polymer, a thioester functionalization was successfully performed by reaction of the active polymer with a cyclic amine functionalized thioester which does not release a toxic by product (such as the resulting thiol) during NCL and thus features a very high potential to replace former thioester.
The aim of the thesis was to develop water soluble poly(2-oxazoline) (POx) copolymers with new side group functionalities, which can be used for the formation of hydrogels in biomedical applications and for the development of peptide-polymer conjugates.
First, random copolymers of the monomer MeOx or EtOx with ButEnOx and EtOx with DecEnOx were synthesized and characterized. The vinyl functionality brought into the copolymer by the monomers ButEnOx and DecEnOx would later serve for post-polymerization functionalization. The synthesized copolymers were further functionalized with thiols via post-polymerization functionalization using a newly developed synthesis protocol or with a protected catechol molecule for hydrogel formation. For the formation of peptide-polymer conjugates, a cyclic thioester, namely thiolactone acrylamide and an azlactone precursor, whose synthesis was newly developed, were attached to the side chain of P(EtOx-co-ButEnOx) copolymers.
The application of the functionalized thiol copolymers as hydrogels using thiol-ene chemistry for cross-linking was demonstrated. The swelling behavior and mechanical properties were characterized. The hydrophilicity of the network as well as the cross-linking density strongly influenced the swelling behavior and the mechanical strength of the hydrogels. All hydrogels showed good cell viability results.
The hydrogel networks based on MeOx and EtOx were loaded with two dyes, fluorescein and methylene blue. It was observed that the uptake of the more hydrophilic dye fluorescein depended more on the ability of the hydrogel to swell. In contrast, the uptake of the more hydrophobic dye methylene blue was less dependent on the swelling degree, but much more on the hydrophilicity of the network.
For the potential application as cartilage glue, (biohybrid) hydrogels were synthesized based on the catechol-functionalized copolymers, with and without additional fibrinogen, using sodium periodate as the oxidizing agent. The system allowed for degradation due to the incorporated ester linkages at the cross-linking points. The swelling behavior as well as the mechanical properties were characterized. As expected, hydrogels with higher degrees of cross-linking showed less swelling and higher elastic modulus. The addition of fibrinogen however increased the elasticity of the network, which can be favorable for the intended application as a cartilage glue. Biological evaluation clearly demonstrated the advantage of degradable ester links in the hydrogel network, where chondrocytes were able to bridge the artificial gap in contrast to hydrogels without any ester motifs.
Lastly, different ways to form peptide-polymer conjugates were presented. Peptides were attached with the thiol of the terminal cysteine group to the vinyl side chain of P(EtOx-co-ButEnOx) copolymers by radical thiol-ene chemistry. Another approach was to use a cyclic thioester, thiolactone, or an azlactone functionality to bind a model peptide via native chemical ligation. The two latter named strategies to bind peptides to POx side chains are especially interesting as one and in the case of thiolactone two free thiols are still present at the binding site after the reaction, which can, for example, be used for further thiol-ene cross-linking to form POx hydrogels.
In summary, side functional poly(oxazoline) copolymers show great potential for numerous biomedical applications. The various side chain functionalities can be introduced by an appropriate monomer or by post-polymerization functionalization, as demonstrated. By their multi-functionality, hydrogel characteristics, such as cross-linking degree and mechanical strength, can be fine-tuned and adjusted depending on the application in the human body. In addition, the presented chemoselective and orthogonal reaction strategies can be used in the future to synthesize polymer conjugates, which can, for example, be used in drug delivery or in tissue regeneration.
The outcome of the innate immune response to biomaterials mainly determines whether the material will be incorporated in the body to fulfill its desired function or, when it gets encapsulated, will be rejected in the worst case. Macrophages are key players in this process, and their polarization state with either pro- (M1), anti-inflammatory (M2), or intermediate characteristics is crucial for deciding on the biomaterial’s fate. While a transient initial pro-inflammatory state is helpful, a prolonged inflammation deteriorates the proper healing and subsequent regeneration. Therefore, biomaterial-based polarization may aid in driving macrophages in the desired direction. However, the in vivo process is highly complex, and a mono-culture of macrophages in vitro displays only one part of the cellular system, but, to this date, there is a lack of established co-cultures to assess the immune response to biomaterials. Thus, this thesis aimed to establish a functional co-culture system of human macrophages and human mesenchymal stromal cells (hMSCs) to improve the assessment of the immune response to biomaterials in vitro. Together with macrophages, hMSCs are involved in tissue regeneration and inflammatory reactions and can modulate the immune response. In particular, endogenously derived hMSCs considerably contribute to the successful engrafting of biomaterials. This thesis focused on poly(ε-caprolactone) (PCL) fiber-based scaffolds produced by the technique of melt electrowriting (MEW) as biomaterial constructs. Via this fabrication technique, uniform, precisely ordered scaffolds varying in geometry and pore size have been created in-house.
To determine the impact of scaffold geometries and pore sizes on macrophages, mono-cultures incubated on scaffolds were conducted. As a pre-requisite to achieve a functional co-culture system on scaffolds, setups for direct and indirect systems in 2D have initially been established. These setups were analyzed for the capability of cell-cell communication. In parallel, a co-culture medium suitable for both cell types was defined, prior to the establishment of a step-by-step procedure for the co-cultivation of human macrophages and hMSCs on fiber-based scaffolds.
Regarding the scaffold morphologies tested within this thesis to improve M2-like polarization, box-shaped scaffolds outperformed triangular-, round- or disordered-shaped ones. Upon further investigation of scaffolds with box-shaped pores and precise inter-fiber spacing from 100 µm down to only 40 µm, decreasing pore sizes facilitated primary human macrophage elongation accompanied by their differentiation towards the M2 type, which was most pronounced for the smallest pore size of 40 µm. To the best of my knowledge, this was the first time that the elongation of human macrophages in a 3D environment has been correlated to their M2-like polarization. Thus, these results may set the stage for the design, the assessment, and the selection of new biomaterials, which can positively affect the tissue regeneration.
The cell communication of both cell types, detected via mitochondria exchange in direct and indirect co-cultures systems, took place in both directions, i.e., from hMSCs to macrophages and vice versa. Thereby, in direct co-culture, tunneling nanotubes enabled the transfer from one cell type to the respective other, while in indirect co-culture, a non-directional transfer through extracellular vesicles (EVs) released into the medium seemed likely. Moreover, the phagocytic activity of macrophages after 2D co-cultivation and hence immunomodulation by hMSCs increased with the highest phagocytic rate after 48 h being most pronounced in direct co-cultivation.
As the commonly used serum supplements for macrophages and hMSCs, i.e., human serum (hS) and fetal calf serum (FCS), respectively, failed to support the respective other cell type during prolonged cultivation, these sera were replaced by human platelet lysate (hPL), which has been proven to be the optimal supplement for the co-cultivation of human macrophages with hMSCs within this thesis. Thereby, the phenotype of both cell types, the distribution of both cell populations, the phagocytic activity of macrophages, and the gene expression profiles were maintained and comparable to the respective standard mono-culture conditions. This was even true when hPL was applied without the anticoagulant heparin in all cultures with macrophages, and therefore, heparin was omitted for further experiments comprising hPL and macrophages.
Accordingly, a step-by-step operating procedure for the co-cultivation on fiber-based scaffolds has been established comprising the setup for 3D cultivation as well as the description of methods for the analysis of phenotypical and molecular changes upon contact with the biomaterial. The evaluation of the macrophage response depending on the cultivation with or without hMSCs and either on scaffolds or on plastic surfaces has been successfully achieved and confirmed the functionality of the suggested procedures.
In conclusion, the functional co-culture system of human macrophages and hMSCs established here can now be employed to assess biomaterials in terms of the immune response in a more in vivo-related way. Moreover, specifically designed scaffolds used within the present thesis showed auspicious design criteria positively influencing the macrophage polarization towards the anti-inflammatory, pro-healing type and might be adaptable to other biomaterials in future approaches.
Hence, follow-up experiments should focus on the evaluation of the co-culture outcome on promising scaffolds, and the suggested operating procedures should be adjusted to further kinds of biomaterials, such as cements or hydrogels.
The implantation of any foreign material into the body automatically starts an immune reaction that serves as the first, mandatory step to regenerate tissue. The course of this initial immune reaction decides on the fate of the implant: either the biomaterial will be integrated into the host tissue to subsequently fulfill its intended function (e.g., tissue regeneration), or it will be repelled by fibrous encapsulation that determines the implant failure. Especially neutrophils and macrophages play major roles during this inflammatory response and hence mainly decide on the biomaterial's fate. For clinically relevant tissue engineering approaches, biomaterials may be designed in shape and morphology as well as in their surface functionality to improve the healing outcome, but also to trigger stem cell responses during the subsequent tissue regeneration phase.
The main focus of this thesis was to unravel the influence of scaffold characteristics, including scaffold morphology and surface functionality, on primary human innate immune cells (neutrophils and macrophages) and human mesenchymal stromal cells (hMSCs) to assess their in vitro immune response and tissue regeneration capacity, respectively. The fiber-based constructs were produced either via melt electrowriting (MEW), when the precise control over scaffold morphology was required, or via solution electrospinning (ES), when the scaffold design could be neglected. All the fiber-based scaffolds used throughout this thesis were composed of the polymer poly(ε caprolactone) (PCL).
A novel strategy to model and alleviate the first direct cell contact of the immune system with a peptide-bioactived fibrous material was presented in chapter 3 by treating the material with human neutrophil elastase (HNE) to imitate the neutrophil attack. The main focus of this study was put on the effect of HNE towards an RGDS-based peptide that was immobilized on the surface of a fibrous material to improve subsequent L929 cell adhesion. The elastase efficiently degraded the peptide-functionality, as evidenced by a decreased L929 cell adhesion, since the peptide integrated a specific HNE-cleavage site (AAPV-motif). A sacrificial hydrogel coating based on primary oxidized hyaluronic acid (proxHA), which dissolved within a few days after the neutrophil attack, provided an optimal protection of the peptide-bioactivated fibrous mesh, i.e, the hydrogel alleviated the neutrophil attack and largely ensured the biomaterial's integrity. Thus, according to these results, a means to protect the biomaterial is required to overcome the neutrophil attack.
Chapter 4 was based on the advancement of melt electrowriting (MEW) to improve the printing resolution of MEW scaffolds in terms of minimal inter-fiber distances and a concomitant high stacking precision. Initially, to gain a better MEW understanding, the influence of several parameters, including spinneret diameter, applied pressure, and collector velocity on mechanical properties, crystallinity, fiber diameter and fiber surface morphology was analyzed. Afterward, innovative MEW designs (e.g., box-, triangle-, round , and wall-shaped scaffolds) have been established by pushing the printing parameters to their physical limits. Further, the inter-fiber distance within a standardized box-structured scaffold was successfully reduced to 40 µm, while simultaneously a high stacking precision was maintained. In collaboration with a co-worker of my department (Tina Tylek, who performed all cell-based experiments in this study), these novel MEW scaffolds have been proven to facilitate human monocyte-derived macrophage polarization towards the regenerative M2 type in an elongation-driven manner with a more pronounced effect with decreasing pore sizes.
Finally, a pro-adipogenic platform for hMSCs was developed in chapter 5 using MEW scaffolds with immobilized, complex ECM proteins (e.g., human decellularized adipose tissue (DAT), laminin (LN), and fibronectin (FN)) to test for the adipogenic differentiation potential in vitro. Within this thesis, a special short-term adipogenic induction regime enabled to more thoroughly assess the intrinsic pro-adipogenic capacity of the composite biomaterials and prevented any possible masking by the commonly used long-term application of adipogenic differentiation reagents. The scaffolds with incorporated DAT consistently showed the highest adipogenic outcome and hence provided an adipo-inductive microenvironment for hMSCs, which holds great promise for applications in soft tissue regeneration.
Future studies should combine all three addressed projects in a more in vivo-related manner, comprising a co-cultivation setup of neutrophils, macrophages, and MSCs. The MEW-scaffold, particularly due to its ability to combine surface functionality and adjustable morphology, has been proven to be a successful approach for wound healing and paves the way for subsequent tissue regeneration.
Synthetic bone replacement materials have their application in non-load bearing defects with the function of (re-)construction or substitution of bone. This tissue itself represents a biological composite material based on mineralized collagen fibrils and combines the mechanical strength of the mineral with the ductility of the organic matrix. By mimicking these outstanding properties with polymer-cement-composites, an imitation of bone is feasible. A promising approach for such replacement materials are dual setting systems, which are generated by dissolution-precipitation reaction with cement setting in parallel to polymerization and gelation of the organic phase forming a coherent hydrogel network. Hereby, the high brittleness of the pure inorganic network was shifted to a more ductile and elastic behavior.
The aim of this thesis was focused on the development of different dual setting systems to modify pure calcium phosphate cements’ (CPCs’) mechanical performance by incorporation of a hydrogel matrix.
A dual setting system based on hydroxyapatite (HA) and cross-linked 2-hydroxyethyl methacrylate (HEMA) via radical polymerization was advanced by homogenous incorporation of a degradable cross-linker composed of poly(ethylene glycol) (PEG) as well as poly(lactic acid) (PLA) with reactive terminal methacrylate functionalities (PEG-PLLA-DMA). By integration of this high molecular weight structure in the HEMA-hydrogel network, a significant increase in energy absorption (toughness) under 4-point bending testing was observed. An addition of only 10 wt% hydrogel precursor (referred to the liquid phase) resulted in a duplication of stress over a period of 8 days. Additionally, the calculated elasticity was positively affected and up to six times higher compared to pure HA. With a constantly applied force during compressive strength testing, a deformation and thus strain levels of about 10 % were reached immediately after preparation.
For higher degradability, the system was modified in a second approach regarding organic as well as inorganic phase. The latter component was changed by brushite forming cement that is resorbable in vivo due to solubility processes. This CPC was combined with a hydrogel based on PEG-PLLA-DMA and other dimethacrylated PEGs with different molecular weights and concentrations. Hereby, new reaction conditions were created including a shift to acidic conditions. On this ground, the challenge was to find a new radical initiator system. Suitable candidates were ascorbic acid and hydrogen peroxide. that started the polymerization and successful gelation in this environment. These highly flexible dual set composites showed a very high ductility with an overall low strength compared to HA-based models. After removal of the applied force during compressive strength testing, a complete shape recovery was observed for the samples containing the highest polymeric amount (50 wt%) of PEG-PLLA-DMA.
Regarding phase distribution in the constructs, a homogenously incorporated hydrogel network was demonstrated in a decalcifying study with ethylenediaminetetraacetic acid. Intact, coherent hydrogels remained after dissolution of the inorganic phase via calcium ion complexation.
In a third approach, the synthetic hydrogel matrix of the previously described system was replaced by the natural biopolymer gelatin. Simultaneously to brushite formation, physical as well as chemical cross-linking by the compound genipin was performed in the dual setting materials. Thanks to the incorporation of gelatin, elasticity increased significantly, in which concentrations up to 10.0 w/v% resulted in a certain cohesion of samples after compressive strength testing. They did not dissociate in little pieces but remained intact cuboid specimens though having cracks or fissures. Furthermore, the drug release of two active pharmaceutical ingredients (vancomycin and rifampicin) was investigated over a time frame of 5 weeks. The release exponent was determined according to Korsmeyer-Peppas with n = 0.5 which corresponds to the drug liberation model of Higuchi. A sustained release was observed for the antibiotic vancomycin encapsulated in composites with a gelatin concentration of 10.0 w/v% and a powder-to-liquid ratio of 2.5 g/mL.
With respect to these developments of different dual setting systems, three novel approaches were successfully established by polymerization of monomers and cross-linking of precursors forming an incorporated, homogenous hydrogel matrix in a calcium phosphate network. All studies showed an essential transfer of mechanical performance in direction of flexibility and bendability.
Adipose tissue defects and related pathologies still represent major challenges in reconstructive surgery. Based on to the paradigm ‘replace with alike’, adipose tissue is considered the ideal substitute material for damaged soft tissue [1-3]. Yet the transfer of autologous fat, particularly larger volumes, is confined by deficient and unpredictable long term results, as well as considerable operative morbidity at the donor and recipient site [4-6], calling for innovative treatment options to improve patient care.
With the aim to achieve complete regeneration of soft tissue defects, adipose tissue engineering holds great promise to provide functional, biologically active adipose tissue equivalents. Here, especially long-term maintenance of volume and shape, as well as sufficient vascularization of engineered adipose tissue represent critical and unresolved challenges [7-9]. For adipose tissue engineering approaches to be successful, it is thus essential to generate constructs that retain their initial volume in vivo, as well as to ensure their rapid vascularization to support cell survival and differentiation for full tissue regeneration [9,10]. Therefore, it was the ultimate goal of this thesis to develop volume-stable 3D adipose tissue constructs and to identify applicable strategies for sufficient vascularization of engineered constructs. The feasibility of the investigated approaches was verified by translation from in vitro to in vivo as a critical step for the advancement of potential regenerative therapies.
For the development of volume-stable constructs, the combination of two biomaterials with complementary properties was successfully implemented. In contrast to previous approaches in the field using mainly non-degradable solid structures for mechanical protection of developing adipose tissue [11-13], the combination of a cell-instructive hydrogel component with a biodegradable porous support structure of adequate texture was shown advantageous for the generation of volume-stable adipose tissue. Specifically, stable fibrin hydrogels previously developed in our group [14] served as cell carrier and supported the adipogenic development of adipose-derived stem cells (ASCs) as reflected by lipid accumulation and leptin secretion. Stable fibrin gels were thereby shown to be equally supportive of adipogenesis compared to commercial TissuCol hydrogels in vitro. Using ASCs as a safe source of autologous cells [15,16] added substantial practicability to the approach. To enhance the mechanical strength of the engineered constructs, porous biodegradable poly(ε caprolactone)-based polyurethane (PU) scaffolds were introduced as support structures and shown to exhibit adequately sized pores to host adipocytes as well as interconnectivity to allow coherent tissue formation and vascularization. Low wettability and impaired cell attachment indicated that PU scaffolds alone were insufficient in retaining cells within the pores, yet cytocompatibility and differentiation of ASCs were adequately demonstrated, rendering the PU scaffolds suitable as support structures for the generation of stable fibrin/PU composite constructs (Chapter 3).
Volume-stable adipose tissue constructs were generated by seeding the pre-established stable fibrin/PU composites with ASCs. Investigation of size and weight in vitro revealed that composite constructs featured enhanced stability relative to stable fibrin gels alone. Comparing stable fibrin gels and TissuCol as hydrogel components, it was found that TissuCol gels were less resilient to degradation and contraction. Composite constructs were fully characterized, showing good cell viability of ASCs and strong adipogenic development as indicated by functional analysis via histological Oil Red O staining of lipid vacuoles, qRT-PCR analysis of prominent adipogenic markers (PPARγ, C/EBPα, GLUT4, aP2) and quantification of leptin secretion. In a pilot study in vivo, investigating the suitability of the constructs for transplantation, stable fibrin/PU composites provided with a vascular pedicle gave rise to areas of well-vascularized adipose tissue, contrasted by insufficient capillary formation and adipogenesis in constructs implanted without pedicle. The biomaterial combination of stable fibrin gels and porous biodegradable PU scaffolds was thereby shown highly suitable for the generation of volume-stable adipose tissue constructs in vivo, and in addition, the effectiveness of immediate vascularization upon implantation to support adipose tissue formation was demonstrated (Chapter 4).
Further pursuing the objective to investigate adequate vascularization strategies for engineered adipose tissue, hypoxic preconditioning was conducted as a possible approach for in vitro prevascularization. In 2D culture experiments, analysis on the cellular level illustrated that the adipogenic potential of ASCs was reduced under hypoxic conditions when applied in the differentiation phase, irrespective of the oxygen tension encountered by the cells during expansion. Hypoxic treatment of ASCs in 3D constructs prepared from stable fibrin gels similarly resulted in reduced adipogenesis, whereas endothelial CD31 expression as well as enhanced leptin and vascular endothelial growth factor (VEGF) secretion indicated that hypoxic treatment indeed resulted in a pro-angiogenic response of ASCs. Especially the observed profound regulation of leptin production by hypoxia and the dual role of leptin as adipokine and angiogenic modulator were considered an interesting connection advocating further study. Having confirmed the hypothesis that hypoxia may generate a pro-angiogenic milieu inside ASC-seeded constructs, faster vessel ingrowth and improved vascularization as well as an enhanced tolerance of hypoxia-treated ASCs towards ischemic conditions upon implanatation may be expected, but remain to be verified in rodent models in vivo (Chapter 5).
Having previously been utilized for bone and cartilage engineering [17-19], as well as for revascularization and wound healing applications [20-22], stromal-vascular fraction (SVF) cells were investigated as a novel cell source for adipose tissue engineering. Providing cells with adipogenic differentiation as well as vascularization potential, the SVF was applied with the specific aim to promote adipogenesis and vascularization in engineered constructs in vivo. With only basic in vitro investigations by Lin et al. addressing the SVF for adipose repair to date [23], the present work thoroughly investigated SVF cells for adipose tissue construct generation in vitro, and in particular, pioneered the application of these cells for adipose tissue engineering in vivo.
Initial in vitro experiments compared SVF- and ASC-seeded stable fibrin constructs in different medium compositions employing preadipocyte (PGM-2) and endothelial cell culture medium (EGM-2). It was found that a 1:1 mixture of PGM-2 and EGM-2, as previously established for co-culture models of adipogenesis [24], efficiently maintained cells with adipogenic and endothelial potential in SVF-seeded constructs in short and long-term culture setups. Observations on the cellular level were supported by analysis of mRNA expression of characteristic adipogenic and endothelial markers. In preparation of the evaluation of SVF-seeded constructs under in vivo conditions, a whole mount staining (WMS) method, facilitating the 3D visualization of adipocytes and blood vessels, was successfully established and optimized using native adipose tissue as template (Chapter 6).
In a subcutaneous nude mouse model, SVF cells were, for the first time in vivo, elucidated for their potential to support the functional assembly of vascularized adipose tissue. Investigating the effect of adipogenic precultivation of SVF-seeded stable fibrin constructs in vitro prior to implantation on the in vivo outcome, hormonal induction was shown beneficial in terms of adipocyte development, whereas a strong vascularization potential was observed when no adipogenic inducers were added. Via histological analysis, it was proven that the developed structures were of human origin and derived from the implanted cells. Applying SVF cells without precultivation in vitro but comparing two different fibrin carriers, namely stable fibrin and TissuCol gels, revealed that TissuCol profoundly supported adipose formation by SVF cells in vivo. This was contrasted by only minor SVF cell development and a strong reduction of cell numbers in stable fibrin gels implanted without precultivation. Histomorphometric analysis of adipocytes and capillary structures was conducted to verify the qualitative results, concluding that particularly SVF cells in TissuCol were highly suited for adipose regeneration in vivo. Employing the established WMS technique, the close interaction of mature adipocytes and blood vessels in TissuCol constructs was impressively shown and via species-specific human vimentin staining, the expected strong involvement of implanted SVF cells in the formation of coherent adipose tissue was confirmed (Chapter 7).
With the development of biodegradable volume-stable adipose tissue constructs, the application of ASCs and SVF cells as two promising cell sources for functional adipose regeneration, as well as the thorough evaluation of strategies for construct vascularization in vitro and in vivo, this thesis provides valuable solutions to current challenges in adipose tissue engineering. The presented findings further open up new perspectives for innovative treatments to cure soft tissue defects and serve as a basis for directed approaches towards the generation of clinically applicable soft tissue substitutes.
Zur Erhöhung der mechanischen Stabilität mineralischer Knochenzemente aus Calciumorthophosphaten (CPC) wurde in einem TTCP/DCPA-System das Zementedukt TTCP mit verschiedenen biokompatiblen Oxiden (SiO2, TiO2, ZrO2) während des Herstellungsprozesses dotiert. Dies führte zur Bildung von Calciummetallaten und einer Herabsetzung der Löslichkeit der TTCP-Komponente des Zements. Gegenüber einem oxidfreien Zement konnte die Druckfestigkeit von 65 MPa auf 80 MPa (SiO2) bzw. 100 MPa (TiO2) gesteigert werden.
In einem zweiten Ansatz zur Verbesserung der Injizierbarkeit wurden die Wechselwirkungen der Partikeloberflächen mit der flüssigen Zementphase betrachtet. Durch biokompatible Additive sollte eine repulsive elektrostatische Wechselwirkung eingestellt werden, um Partikelagglomerate effektiv zu dispergieren und eine verflüssigende Wirkung zu erreichen. Die Injizierbarkeit eines TTCP/DCPA-Zements durch eine Kanüle mit 800 µm Durchmesser konnte durch die Verwendung von 500 mM tri-Natriumzitrat-Lösung aufgrund einer deutlichen Herabsetzung der Viskosität der Zementpaste signifikant gesteigert werden (>95%, P/L 3,3/1, Kraftaufwand 20 N).
Abschließend wurde der Einfluss der Partikelgrößenverteilung auf die Festigkeit und Injizierbarkeit einer auf monomodaler Partikelgrößenverteilung basierten Zementmatrix untersucht. Hierzu wurden einem mechanisch aktivierten a-TCP-System unreaktive, feinkörnige Füllstoffpopulationen (TiO2, CaHPO4, CaCO3) zugesetzt und systematisch deren Effekt in Verbindung mit einer Partikelaufladung durch tri-Natriumzitrat auf die rheologischen und mechanischen Eigenschaften untersucht.
Erst die Kombination einer bimodalen Partikelgrößenverteilung mit tri-Natriumzitrat-Lösung führte zu einer starken Erniedrigung der Viskosität, damit zur nahezu vollständigen Injizierbarkeit der Zemente und einer teilweise signifikanten Steigerung der mechanischen Festigkeiten (z.B. 72 MPa reiner a-TCP-Zement auf 142 MPa mit Zusatz von CaHPO4).
Aim of this thesis was to combine the versatility of sulfur-chemistry, regarding redox-sensitivity as well as chemo- and site-specific conjugation, with multifunctionality of poly(glycidol)s as an alternative to poly(ethylene glycol).
First the homo- and copolymerizations of EEGE and AGE were performed with respect to molar-mass distribution and reaction kinetics. A detailed study was given, varying the polymerization parameters such as DP, counter ion, solvent and monomer influence. It can be concluded that in general the rates for all polymerizations are higher using K+, in contrast to Cs+, as counter ion for the active alkoxide species. Unfortunately, K+ as counter ion commonly leads to a reduced control over polymer dispersity. In this thesis it was shown that the broad molar-mass distributions might be reduced by adding the monomer in a step-wise manner. In experiments with a syringe pump, for continuously adding the monomer, a significant reduction of the dispersities could be found using K+ as counter ion.
In analogy to the oxyanionic polymerization of epoxides, the polymerization of episulfides via a thioanionic mechanism with various DPs was successful with thiols/DBU as initiator. In most experiments bimodality could be observed due to the dimerization, caused by oxidation processes by introduced oxygen during synthesis. Reducing this was successful by modifying the degassing procedure, e.g. repeated degassing cycles after each step, i.e. initiation, monomer addition and quenching. Unfortunately, it was not always possible to completely avoid the dimerization due to oxidation. Thiophenol, butanethiol, mercaptoethanol and dithiothreitol were used as thiol initiators, all being capable to initiate the polymerization. With the prediction and the narrow molar-mass distributions, the living character of the polymerization is therefore indicated.
Homo- and copolymers of poly(glycidol) were used to functionalize these polymers with side-chains bearing amines, thiols, carboxylic acids and cysteines. The cysteine side-chains were obtained using a newly synthesized thiol-functional thiazolidine. For this, cysteine was protected using a condensation reaction with acetone yielding a dimethyl-substituted thiazolidine. Protection of the ring-amine was obtained via a mixed-anhydride route using formic acid and acetic anhydride. The carboxylic acid of 2,2-dimethylthiazolidine-4-carboxylic acid was activated with CDI and cysteamine attached. The obtained crystalline mercaptothiazolidine was subjected to thiol-ene click chemistry with allyl-functional poly(glycidol). A systematic comparison of thermal- versus photo-initiation showed a much higher yield and reaction rate for the UV-light mediated thiol-ene synthesis with DMPA as photo-initiator. Hydrolysis of the protected thiazolidine-functionalities was obtained upon heating the samples for 5 d at 70 °C in 0.1 M HCl. Dialysis against acetic acid lead to cysteine-functional poly(glycidol)s, storable as the acetate salt even under non-inert atmosphere. An oxidative TNBSA assay was developed to quantify the cysteine-content without the influence of the thiol-functionality. A cooperation partner coupled C-terminal thioester peptides with the cysteine-functional poly(glycidol)s and showed the good accessibility and reactivity of the cysteines along the backbone. SDS-PAGE, HPLC and MALDI-ToF measurements confirmed the successful coupling.
Tumorzellen, Stromazellen, Extrazellulärmatrix (EZM) und lösliche Faktoren in der Tumormikroumgebung beeinflussen und verstärken sich gegenseitig in der Ausbildung eines malignen Phänotyps. Sowohl die fibrotische EZM als auch eine kleine Subpopulation von pluripotenten Tumorstammzellen sind bekanntermaßen für die Steigerung der Tumoraggressivität verantwortlich. Inwiefern diese beiden unabhängigen Faktoren im Kontext von Brustkrebs miteinander in Beziehung stehen, ist jedoch bis heute unklar.
Um untersuchen zu können, welchen Beitrag Tumorzellen, Stromazellen, EZM und lösliche Faktoren einzeln und im Zusammenspiel zur Malignität eines Tumors leisten, ist die Entwicklung geeigneter in-vitro-Modelle unabdingbar. Daher war es das Ziel dieser Arbeit, ein 3D-Mikrotumormodell zu generieren, in dem eine Analyse dieser genannten Faktoren stattfinden könnte. An diesem Modell wurden darüber hinaus erste Untersuchungen von im Tumorkontext bekannten EZM-Proteinen durchgeführt. Um die dreidimensionale Anordnung von Tumorzellen und ihrer Gewebeumgebung adäquat wiedergeben zu können, beinhalteten die 3D-Tumorsphäroide sowohl Brustkrebszellen (MDA-MB-231) als auch Stromazellen (hASCs).
Die EZM als wichtiger Bestandteil der (Tumor-) Mikroumgebung sollte übersichtshalber durch Hämatoxylin-Eosin-Färbung und detaillierter durch immunhistochemische Analyse nach zwei verschiedenen Kulturzeitpunkten charakterisiert werden, um EZM-Veränderungen im zeitlichen Verlauf darzustellen. Im Fokus der Analyse standen die beiden wichtigsten profibrotischen EZM-Proteine Fibronektin und Kollagen I, die maßgeblich an der Pathogenese von Brustkrebs beteiligt sind. Zudem wurde das Vorkommen des Myofibroblastenmarkers α-SMA untersucht.
An den Sphäroiden einer Kontrollgruppe, die lediglich hASCs beinhaltete, sollte vergleichend eine Analyse der genannten EZM-Proteine sowie α-SMA durchgeführt werden. Um schließlich den Einfluss der von Tumorzellen sezernierten löslichen Faktoren in der Tumormikroumgebung herauszustellen, wurden Sphäroide aus hASCs in tumorkonditioniertem Medium gezüchtet und darin ebenfalls Matrixproteine und α-SMA untersucht.
Abschließend erfolgte eine Korrelation der EZM-Analyse mit dem Vorhandensein von Tumorstammzellen in den 3D-Tumorsphäroiden. Dafür wurden die Tumorstammzellen mithilfe eines GFP-basierten Reporters für den Stammzellmarker NANOG (NANOG-GFP-Reporterzelllinie) in mikroskopischen Aufnahmen der 3D-Tumorsphäroide nachgewiesen und im Kontext mit der EZM lokalisiert.
In this thesis, non-modified POx, namely PnPrOx and PcycloPrOx, with an LCST in the physiological range between 20 and 37°C have been utilized as materials for three different biofabrication approaches. Their thermoresponsive behavior and processability were exploited to establish an easy-to-apply coating for cell sheet engineering, a novel method to create biomimetic scaffolds based on aligned fibrils via Melt Electrowriting (MEW) and the application of melt electrowritten sacrificial scaffolds for microchannel creation for hydrogels.
Chapter 3 describes the establishment of a thermoresponsive coating for tissue culture plates. Here, PnPrOx was simply dissolved in water and dried in well plates and petri dishes in an oven. PnPrOx adsorbed to the surface, and the addition of warm media generated a cell culture compatible coating. It was shown that different cell types were able to attach and proliferate. After confluency, temperature reduction led to the detachment of cell sheets. Compared to standard procedures for surface coating, the thermoresponsive polymer is not bound covalently to the surface and therefore does not require specialized equipment and chemical knowledge. However, it should be noted that the detachment of the cell layer requires the dissolution of the PnPrOx-coating, leading to possible polymer contamination. Although it is only a small amount of polymer dissolved in the media, the detached cell sheets need to be washed by media exchange for further processing if required. ...
Aufgrund der sich umkehrenden Alterspyramide in Deutschland leiden bereits jetzt immer mehr Menschen an Gelenkknorpelschäden. Doch nicht nur das Alter, sondern auch Unfälle und Sportverletzungen und Übergewicht können zu irreversiblen Knorpeldefekten führen. Obwohl es diverse Behandlungsmöglichkeiten gibt, können die bisherige Methoden nicht als dauerhafte Heilung betrachtet werden. Im Rahmen des internationalen Forschungsprojektes BIO-CHIP sollte eine vielsprechende Behandlungsmethode mit neuartigen Arzneimitteln untersucht werden.
Als Ausgangsmaterial des Arzneimittels, ein hergestelltes Knorpelimplantat, dienen patienteneigene Knorpelzellen aus der Nase. Diese werden isoliert, vermehrt und letztlich auf einer Matrix zu einem Knorpelimplantat kultiviert. Wesentliche Voraussetzung für die Implantatfreigabe stellt neben toxikologischen und biologischen Unbedenklichkeitstests die Beurteilung der Viabilität dar. Diese wurde bisher anhand von Histologieschnitten von der Pathologie durchgeführt.
Ziel der vorliegenden Arbeit war die Entwicklung und Validierung eines standardisierten und objektiven Viabilitätstests für die Chondrozyten innerhalb der Knorpelmatrix. Hierfür wurde die LDH als Marker für irreversibel geschädigte Zellen verwendet. Die LDH Konzentration konnte mit dem CyQuant LDH-Assay durch die Messung der Absorption gemessen werden. Es konnte nachgewiesen werden, dass LDH die erforderliche Stabilität und Nachweisbarkeit im Medium besitzt. Mithilfe der Lyse, analog zum Herstellungsprozess, gezüchteter Mini-Knorpelimplantate, konnten die maximal erreichbaren LDH Konzentrationen ermittelt werden. Mithilfe dieser Konzentrationen wurde eine Eichkurve generiert. Diese dient als Beurteilung der Viabilität zukünftig gemessener Absorptionen des Überstandmediums.
Das entwickelte Verfahren erfordert keine invasiven Eingriffe am Implantat und zeichnet sich durch eine einfache Durchführung aus, da nur der Überstand gemessen werden muss. Die durchgeführte Validierung der Methode bescheinigte eine hohe Robustheit, Linearität, Genauigkeit und Präzision.
In einigen Punkten konnte diese Arbeit die Ergebnisse früherer Studien bestätigen.
Einstellungs- und Nadelmodi (wenn auch mit unterschiedlicher Ausprägung)
haben einen Einfluss auf die verbesserte Sichtbarkeit der Regionalanästhesienadeln
im Ultraschall. Damit diese sonographisch besser erkannt werden, sollten sie
in einem flacheren Winkel (30-45°) eingestochen werden. Größere Nadellumina
haben einen Vorteil in der Sichtbarkeit im Ultraschall. Auch konnte gezeigt werden,
dass der Nadelschliff einen Einfluss darauf hat, wie gut die Anästhesiekanülenspitze
sonographisch gesehen wird. Allein die (in der Arbeit untersuchten) Nadelbeschichtungs-
Arten brachten keinen wesentlichen Effekt für die verbesserte
Erkennbarkeit.
Es war jedoch auffallend, dass die subjektiven und objektiven Resultate in einem
relativ hohen Maße nicht übereinstimmten. Gründe dafür sehe ich v.a. im gewählten
Verfahren der objektiven Untersuchung (mit der Bildbearbeitungssoftware
muss die region of interest zielgenauer erfasst werden, um störende Umgebungseinflüsse
auszuschließen).
Echogene Nadeloberflächen (auch wenn diese nicht Gegenstand der vorliegenden
Untersuchung waren), weisen eine verbesserte Ultraschall-Reflexion auf. Sie
werden dazu beitragen, dass die sichere Anwendung der USRA weiter zunimmt.
Verbesserte Sonographiegeräte, zusätzliche Hilfsmittel (GPS-Unterstützung) und
neueste Nadelentwicklungen versprechen einen wichtigen Fortschritt auf dem
Gebiet der ultraschallunterstützten Regionalanästhesie (USRA). Diese Weiterentwicklungen
werden der USRA den Stellenwert als Gold-Standard in der
Regionalanästhesie sichern.
The basement membrane separates the epithelium from the stroma of any given barrier tissue and is essential in regulating cellular behavior, as mechanical barrier and as structural support. It further plays an important role for new tissue formation, homeostasis, and pathological processes, such as diabetes or cancer. Breakdown of the basement membrane is believed to be essential for tumor invasion and metastasization. Since the basement membrane is crucial for many body functions, the development of artificial basement membranes is indispensable for the ultimate formation of engineered functional tissue, however, challenging due to their complex structure.
Electrospinning enables the production of fibers in the nano- or microscale range with morphological similarities to the randomly orientated collagen and elastic fibers in the basement membrane. However, electrospun fibers often lack the functional similarity to guide cells and maintain tissue-specific functions. Hence, their possible applications as matrix structure for tissue engineering are limited.
Herein, the potential of polyester meshes, modified with six armed star-shaped pre-polymers and cell-adhesion-mediating peptides, was evaluated to act as functional isotropic and bipolar artificial basement membranes. Thereby, the meshes were shown to be biocompatible and stable including under dynamic conditions, and the degradation profile to correlate with the rate of new tissue formation. The different peptide sequences did not influence the morphology and integrity of the fibers. The modified membranes exhibited protein-repellent properties over 12 months, indicating the long-term stability of the cross-linked star-polymer surfaces.
Cell culture experiments with primary fibroblasts and a human keratinocyte cell line (HaCaT) revealed that cell adhesion and growth strongly depends on the peptide sequences and their combinations employed. HaCaT cells grew to confluence on membranes modified with a combination of laminin/collagen type IV derived binding sequences and with a combination of fibronectin/laminin/collagen type IV derived peptide sequences. Fibroblasts strongly adhered to the fibronectin derived binding sequence and to membranes containing a combination of fibronectin/laminin/collagen type IV derived peptide sequences. The adhesion and growth of fibroblasts and HaCaT cells were significantly reduced on membranes modified with laminin, as well as collagen IV derived peptide sequences. HaCaT cells and fibroblasts barely adhered onto meshes without peptide sequences.
Co-culture experiments at the air-liquid interface with fibroblasts and HaCaT cells confirmed the possibility of creating biocompatible, biofunctional and biomimetic isotropic and bipolar basement membranes, based on the functionalized fibers. HaCaT cells grew in several layers, differentiating towards the surface and expressing cytokeratin 10 in the suprabasal and cytokeratin 14 in the basal layers. Migration of fibroblasts into the electrospun membrane was shown by vimentin staining. Moreover, specific staining against laminin type V, collagen type I, III, IV and fibronectin illustrated that cells started to remodel the electrospun membrane and produced new extracellular matrix proteins following the adhesion to the synthetic surface structures.
The culturing of primary human skin keratinocytes proved to be difficult on electrospun fibers. Cells attached to the membrane, but failed to form a multilayered, well-stratified, and keratinized epidermal layer. Changing the fiber composition and fixation methods did not promote tissue development. Further investigations of the membrane demonstrated the tremendous influence of the pore size of the membrane on epithelial formation. Furthermore, primary keratinocytes reacted more sensitive to pH changes in the medium than HaCaT cells did.
Since primary keratinocytes did not adequately develop on the functionalized meshes, polycarbonate membranes were used instead of electrospun meshes to establish oral mucosa models. The tissue-engineered models represented important features of native human oral mucosa. They consisted of a multilayered epithelium with stratum basale, stratum spinosum, stratum granulosum, and stratum corneum. The models formed a physical barrier and the expression of characteristic cell markers was comparable with that in native human oral mucosa. The results from the ET-50 assay and the irritation study reflected the reproducibility of the tissue equivalents.
Altogether, electrospinning enables the production of fibers with structural similarity to the basement membrane. Incorporating extracellular matrix components to mimic the functional composition offers a safe and promising way to modify the fibers so that they can be used for different tissue engineering applications. The resultant biomimetic membranes that can be functionalized with binding sequences derived from widely varying proteins can be used as a toolbox to study the influence of isotropic and bipolar basement membranes on tissue formation and matrix remodeling systematically, with regards to the biochemical composition and the influence and importance of mono- and co-culture. The oral mucosa models may be useful for toxicity and permeation studies, to monitor the irritation potential of oral health care products and biomaterials or as a disease model.
Intraperitoneal adhesions are fibrous bands that connect tissues in the peritoneal cavity that are usually separated. These adhesions form as a consequence of trauma, inflammation or surgical interventions and often result in severe consequences such as chronic pain, small bowel obstructions or female infertility.
The aim of this thesis was to develop a synthetic barrier device for adhesion prevention made of modified poly(lactide) [PLA]. Solid PLA films (SurgiWrap®) are already successfully in clinical use due to the good biocompatibility and the biodegradability of the material resulting in non-toxic degradation products since lactic acid is naturally part of the metabolic circles of the human body. Considering the brittleness and stiffness of the films, the long degradation time of several months as well as the need for suturing, there is potential for optimization. Through a copolymerization with the hydrophilic poly(ethylene glycol) [PEG], a reduction of the degradation time was intendend. Moreover, the copolymerization should also lead to an improvement of the mechanical properties of the films since PEG acts as plasticizer for PLA. Linear PLA-PEG-PLA triblock copolymers as well as star-shaped PEG-PLA copolymers were synthesized via standard ring opening polymerization to tailor the barrier properties. Besides solid films, solution electrospun meshes from PLA and the synthesized PEG-PLA copolymers were investigated for a potential application as well. Since suturing of a barrier additionally induces adhesion formation, alginate coated membranes were prepared in order to achieve self-adhesiveness. With the intention to reduce infections and consequently inflammation, electrospun meshes and solvent cast films were loaded with the antibacterial drug triclosan and drug release as well as antibacterial efficacy was investigated.
Mechanical tests confirmed that through the variation of the PEG content and branching the mechanical properties can be tailored and are in good accordance with the glass transition temperatures [Tg] of the polymers. Consequently, potentially adequate mechanical properties for surgical handling as well as for the performance within the patient’s body were successfully achieved. Degradation studies revealed that the degradation time was significantly shorter for PEG-PLA membranes than for PLA films and with an appropriate PEG content could be adjusted to the intended time frame. Cell adhesion and viability tests confirmed the non-toxicity of the clinically used PLA films as well as of PEG-PLA films and meshes. With a bioadhesion test the benefit of an alginate coated side towards the pure PLA film concerning self-adhesiveness was successfully demonstrated. Moreover, optical evaluations and a T-peel test of different alginate coated PLA films showed that the cohesion between the chemically different layers was distinctly enhanced by the use of an appropriate PEG-PLA mesh as intermediate cohesion promoting layer. In in vitro release studies with triclosan loaded films a higher release was determined for PEG-PLA than for PLA films. In agar diffusion tests a higher and longer inhibition of staphylococcus aureus growth was observed confirming the release results. Moreover, drug loaded meshes (especially drug loaded after electrospinning) showed enhanced and elongated bacterial inhibition in comparison to films.