Refine
Has Fulltext
- yes (39)
Is part of the Bibliography
- yes (39)
Year of publication
Document Type
- Doctoral Thesis (39)
Keywords
- Tissue Engineering (12)
- Fettgewebe (7)
- Knorpel (6)
- Hyaluronsäure (5)
- Gelenkknorpel (4)
- adipose tissue (4)
- Brustkrebs (3)
- Differenzierung (3)
- Extrazelluläre Matrix (3)
- Hyaliner Knorpel (3)
Institute
- Klinik und Poliklinik für Unfall-, Hand-, Plastische und Wiederherstellungschirurgie (Chirurgische Klinik II) (18)
- Graduate School of Life Sciences (14)
- Abteilung für Funktionswerkstoffe der Medizin und der Zahnheilkunde (8)
- Lehrstuhl für Orthopädie (5)
- Institut für Pharmazie und Lebensmittelchemie (2)
- Medizinische Fakultät (2)
- Fakultät für Chemie und Pharmazie (1)
- Klinik und Poliklinik für Hals-, Nasen- und Ohrenkrankheiten, plastische und ästhetische Operationen (1)
- Lehrstuhl für Tissue Engineering und Regenerative Medizin (1)
- Medizinische Klinik und Poliklinik II (1)
Sonstige beteiligte Institutionen
Das Tissue Engineering von Fettgewebe befasst sich mit der Herstellung von biologisch äquivalenten Gewebekonstrukten mit dem Ziel, diese in der Regenerativen Medizin zur Deckung von Weichteildefekten einzusetzen. Für die Ausreifung, Funktion und das Überleben von Adipozyten wurde die Bedeutung der Extrazellulärmatrix (EZM) zunehmend deutlich.18-20 Untersuchungen zur EZM und ihrer Einflussnahme auf die Adipogenese wurden bislang hauptsächlich an konventionellen zweidimensionalen Zellkulturen unter Verwendung von mesenchymalen Stammzellen aus dem Knochenmark (bone marrow-derived MSC), Präadipozyten der Mauszelllinie 3T3-L1 und intramuskulären Präadipozyten aus Rindern (bovine intramuscular preadipocytes, BIP) vorgenommen.23,56,69,76,115 Ziel dieser Arbeit war es Erkenntnisse über den Einfluss der EZM auf die adipogene Differenzierungsfähigkeit unter Verwendung von humanen mesenchymalen Stammzellen des Fettgewebes (human adipose-derived stem cells, hASC) zu gewinnen. Um in vitro eine natürlichere Mikroumgebung der Zellen zu generieren, wurde neben einer 2D Kultur vergleichend ein 3D Modell bestehend aus multizellulären Sphäroiden verwendet.84,85 Zudem war die Bestimmung eines stabilen Housekeeping-Gens notwendig, um valide Ergebnisse in qPCR-Analysen von Genexpressionsstudien zu gewährleisten.
Die Auswertung statistischer Parameter (Standardabweichung und Interquartilsbereich) sowie die Ergebnisse dreier zur Stabilitätsprüfung eingesetzten Softwares identifizierten EF1α als robustestes HKG.
Der Zusammenhang zwischen der EZM-Entwicklung und der Adipogenese wurde durch Hemmung der Kollagenentwicklung unter Verwendung von Ethyl-3,4-dihydroxybenzoat (EDHB) untersucht. Bei Betrachtung der Triglyceridsynthese mittels Histologie und quantitativer Analyse (Triglyceridassay) konnte in beiden Kultursystemen eine konzentrationsabhängige Hemmung der Adipogenese festgestellt werden. Im Unterschied zur 2D Kultur konnte der Triglyceridgehalt im 3D Modell annähernd auf das Niveau der nicht-induzierten Kontrolle gesenkt werden und damit ein tendenziell stärkerer negativer Effekt im 3D Modell demonstriert werden. In Untersuchungen zur Genexpression wurde die Expressionsrate der späten adipogenen Marker aP2 und C/EBPα maximal durch Zugabe von 0,05 mM EDHB gesenkt, wobei der Effekt in 3D erneut stärker ausgeprägt war.
Bei Betrachtung der Kollagenentwicklung zeigte sich immunhistochemisch zunächst eine Adipogenese-assoziierte Entwicklung der Kollagene I, IV und VI im 2D und 3D Modell. Durch die Zugabe von EDHB ließ sich die Kollagenbildung gleichermaßen in 2D und 3D konzentrationsabhängig inhibieren. Damit konnte ein Rückgang der Synthese von drei für die Adipozyten relevanten Kollagenen zusammen mit der Störung der adipogenen Differenzierung nachgewiesen werden. Auf mRNA-Ebene hingegen war eine unterschiedliche Expression von Kollagen I und IV nachweisbar. Für Kollagen I wurde eine Abnahme der Expression bei Differenzierung der Zellen beobachtet, während die Expressionsrate von Kollagen IV erst mit Beginn der Adipogenese gesteigert wurde. Die Genexpression der untersuchten Kollagene wurde durch EDHB nicht negativ beeinflusst.
Insgesamt weisen die Ergebnisse auf einen engen Zusammenhang der Kollagensynthese mit der Adipogenese hin. Inwieweit eine durch Zell-Matrix-Interaktionen ausgelöste Signaltransduktion und regulatorische Mechanismen in den Präadipozyten die Adipogenese beeinflussen, bleibt jedoch Gegenstand zukünftiger Forschung.
Elektrochemisch gestützte Abscheidung kupfer- und zinkdotierter Magnesiumphosphatschichten auf Titan
(2020)
Zur Entwicklung von Implantaten, welche eine komplikationsärmere Einheilung aufweisen, wurde eine dünne, homogene Beschichtung von Titanprobenkörpern mit Struvit mithilfe elektrochemischer Abscheidung generiert. Hierbei wurden dem Basiselektrolyt in den Versuchsreihen unterschiedliche Konzentrationen an Kupfer-(II)-nitrat-3-hydrat- und/oder Zinknitrat-6-hydratlösung hinzugefügt. Die experimentelle Freisetzung erfolgte in drei unterschiedlichen physiologischen Nährmedien: simulated body fluid (SBF), fetal calf serum (FCS) und Dulbecco’s Modified Eagle Medium (DMEM). Es konnte gezeigt werden, dass eine antibakteriell wirkende Menge an Kupfer- und Zinkionen freigesetzt wurde. Zusammenfassend stellt die elektrochemische Abscheidung von mit Kupfer- und Zink-dotierten Struvit auf Titanoberflächen einen vielversprechenden Ansatz in der Implantologie hinsichtlich der Einheilzeit im Knochen sowie der Risikominimierung des Verlustes dar.
As a major component of the articular cartilage extracellular matrix, hyaluronic acid is a widely used biomaterial in regenerative medicine and tissue engineering. According to its well-known interaction with multiple chondrocyte surface receptors which positively affects many cellular pathways, some approaches by combining mesenchymal stem cells and hyaluronic acid-based hydrogels are already driven in the field of cartilage regeneration and fat tissue. Nevertheless, a still remaining major problem is the development of the ideal matrix for this purpose. To generate a hydrogel for the use as a matrix, hyaluronic acid must be chemically modified, either derivatized or crosslinked and the resulting hydrogel is mostly shaped by the mold it is casted in whereas the stem cells are embedded during or after the gelation procedure which does not allow for the generation of zonal hierarchies, cell density or material gradients. This thesis focuses on the synthesis of different hyaluronic acid derivatives and poly(ethylene glycol) crosslinkers and the development of different hydrogel and bioink compositions that allow for adjustment of the printability, integration of growth factors, but also for the material and biological hydrogel, respectively bioink properties.
Gelenkknorpel besitzt aufgrund seiner avaskulären Natur und der fehlenden mitotischen Aktivität der Chondrozyten bei Schäden kaum Potential zur Selbstheilung. Traumatische Läsionen und degenerative Veränderungen münden im Krankheitsbild der Osteoarthrose, welches mit dem Untergang des Gelenkknorpels einhergeht. Ein neuerer Therapieansatz ist das Tissue Engineering von Gelenkknorpel, wobei jedoch die laterale Integration der Implantate mit dem nativen Knorpelgewebe problematisch bleibt. Ein Adhäsivum kann neben einer adäquaten Sofortadhäsion die Langzeitintegration fördern.
In dieser Arbeit wurden verschiedene Polyethylenglykol (PEG)-basierte Zweikomponentenkleber, ausgehend vom kommerziell erhältlichen Gewebekleber CoSeal™, auf ihre Eignung für Gelenkknorpel untersucht. Dabei wurde Hyaluronsäure (HA) als physiologischer Bestandteil von Gelenkknorpel in thiolierter Form (HA-SH) als Komponente verwendet und auf seine prointegrativen Eigenschaften untersucht.
Der den CoSeal™-Komponenten entsprechende 4-Succinimidyl-Glutarat/4-Thiol-PEG (4SG/4T-PEG)-Kleber hatte sich trotz seiner hohen Sofortadhäsionskraft auch nach der Substitution des 4T-PEG mit HA-SH als zu schnell in flüssiger Umgebung degradierend gezeigt, um eine suffiziente Langzeitintegration zu erreichen. Durch die Verwendung der langsamer degradierenden funktionellen 4-Succinimidyl-Carbonat-PEG (4C-PEG)-Komponente konnte die Langzeitadhäsionskraft in Kombination mit 4-Amin-PEG (4A-PEG) durch die stabilere Amid-Bindung zum einen und in Kombination mit HA-SH zum anderen signifikant gesteigert werden. Immunhistochemisch konnten bei beiden HA-haltigen Klebern Zeichen von Knorpelintegration nachgewiesen werden, während der 4C/4A-PEG-Kleber keine Integrationszeichen aufwies. Im 3-(4,5-Dimethylthiazol-2-yl)-2,5-diphenyltetrazolium Bromid (MTT)-Assay war bei keinem Adhäsivum eine zytotoxische Wirkung zu erkennen.
Insgesamt bieten die untersuchten PEG-basierten Adhäsiva im Vergleich zu den weitverbreiteten Fibrinklebern eine deutlich höhere Sofortadhäsion, welche vergleichbar mit glutaraldehydbasierten Klebern ist. Allerdings können die initialen adhäsiven Kräfte, trotz histologisch nachweisbaren Integrationszeichen bei Inkorporation von HA, nicht langfristig aufrechterhalten werden, so dass Fibrinkleber weiterhin die Spitzengruppe in Sachen Langzeitadhäsion bilden. Da PEG eine ausgezeichnete Biokompatibilität, einfache Anwendbarkeit und zahlreiche weitere chemische Anpassungsmöglichkeiten zur Feinabstimmung der Degradationseigenschaften bietet, ist in Zukunft ein erfolgreicher Einsatz auch im Bereich von Gelenkknorpel denkbar.
Für die experimentelle Untersuchung von Adhäsiva und Gelenkknorpel werden biomechanische Versuchsmodelle benötigt. Der Tensile-Test des Sandwich-Modells konnte im Rahmen dieser Arbeit erfolgreich etabliert und ein Protokoll festgelegt werden. In einem vergleichenden Versuch mit dem Push-Out-Test des Disc-Ring-Modells, welches als Referenzmodell dient, konnte in Bezug auf die Reproduzierbarkeit und Qualität der Messergebnisse die Gleichwertigkeit gezeigt werden. Insgesamt bietet er eine gute Alternative zum Push-Out-Test, um weiterführende Fragestellung, wie z.B. extrinsische Kraftwirkungen auf das Konstrukt, zu untersuchen.
Mineral biocements are brittle materials, which usually results in catastrophic failure during mechanical loading. Here, previous works demonstrated the feasibility of reducing brittleness by a dual-setting approach, in which a silica sol was simultaneously gelled during the setting of a brushite forming cement. The current thesis aimed at further improving this concept by both using a novel silicate based cement matrix for an enhanced bonding between cement and silica matrix as well as multifunctional silica precursors to increase the network density of the gel. Due to its well-known biocompatibility and osteogenic regeneration capacity, baghdadite was chosen as mineral component of such composites. This required in a first approach the conversion of baghdadite ceramics into self-setting cement formulations. This was investigated initially by using baghdadite as reactive filler in a brushite forming cement (Chapter 4). Here, the ß-TCP component in a equimolar mixture of ß-TCP and acidic monocalcium phosphate anhydrous was subsequently replaced by baghdadite at various concentrations (0, 5, 10, 20, 30, 50, and 100 wt%) to study the influence on physicochemical cement properties such as mechanical performance, radiopacity, phase composition and microstructure. X-ray diffraction profiles demonstrated the dissolution of baghdadite during the cement reaction without affecting the crystal structure of the precipitated brushite phase. In addition, EDX analysis showed that calcium is homogeneously distributed in the cement matrix, while zirconium and silicon form cluster-like aggregates ranging in size from a few micrometers to more than 50 µm. X-ray images and µ-CT analyses indicate improved X-ray visibility with increased incorporation of baghdadite in brushite cement, with an aluminum equivalent thickness nearly doubling at a baghdadite content of 50 wt%. At the same time, the compressive strength of brushite cement increased from 12.9 ± 3.1 MPa to 21.1 ± 4.1 MPa at a baghdadite content of 10 wt%. Cell culture medium conditioned with powdered brushite cement approached physiological pH values when increasing amounts of baghdadite were added to the cement (pH = 6.47 for pure brushite, pH = 7.02 for brushite with 20 wt% baghdadite substitution). Baghdadite substitution also affected the ion content in the culture medium and thus the proliferation activity of primary human osteoblasts in vitro. The results demonstrated for the first time the suitability of baghdadite as a reactive cement additive for improving the radiopacity, mechanical performance, and cytocompatibility of brushite cements.
A second approach (Chapter 5) aimed to produce single component baghdadite cements by an increase of baghdadite solubility to initiate a self-setting cement reaction. For this, the material was mechanically activated by longer grinding times of up to 24h leading to both a decrease in particle and crystallite size as well as a partial amorphization of baghdadite. Baghdadite cements were formed by adding water at a powder to liquid ratio of 2.0 g/ml. Maximum compressive strengths were determined to be ~2 MPa after 3 days of setting for a 24-hour ground material. Inductively coupled plasma mass spectrometry (ICP-MS) measurements showed an incongruent dissolution profile of the set cements, with preferential dissolution of calcium and only minor release of zirconium ions. Cement formation occurs under alkaline conditions, with the unground raw powder resulting in a pH of 11.9 during setting, while prolonged grinding increases the pH to about 12.3.
Finally, mechanically activated baghdadite cements were combined with inorganic silica networks (Chapter 6) to create dual-setting cements with a further improvement of mechanical performance. While a modification of the cement pastes with a TEOS derived sol was already thought to improve strength, it was hypothesized that using multi-arm silica precursors can further enhance their mechanical performance due to a higher network density. In addition, this should also reduce pore size of both gels and cement and hence will be able to adjust the release kinetics of incorporated drugs. For this, multi-armed silica precursors were synthesized by the reaction of various multivalent alcohols (ethylene glycol, glycerine, pentaerythrit) with an isocyanate modified silica precursor. After hydrolysis under acidic conditions, the sols were mixed with baghdadite cement powders in order to allow a simultaneous gel formation and cement setting. Since the silica monomers have a high degree of linkage sites, this resulted in a branched network that interpenetrated with the growing cement crystals. In addition to minor changes in the crystalline phase composition as determined by X-ray diffraction, the novel composites exhibited improved mechanical properties with up to 20 times higher compressive strength and further benefit from an about 50% lower overall porosity than the reference pure baghdadite cement. In addition, the initial burst release of the model drug vancomycin was completely inhibited by the added silica matrix. This observation was verified by testing for the antimicrobial activity with Staphylococcus aureus by measuring the inhibition zones of selected samples after 24 h and 48 h, whereas the antimicrobial effectiveness of a constant vancomycin release could be demonstrated.
The current thesis clearly demonstrated the high potential of baghdadite as a cement formulation for medical application. The initially poor mechanical properties of such cements can be overcome by special processing techniques or by combination with silica networks. The achieved mechanical performance is > 10 MPa and hence suitable for bone replacement under non-load bearing conditions. The high intrinsic radiopacity as well as the alkaline pH during setting may open the way ahead to further dental applications, e.g. as root canal sealers or filler in dental composites. Here, the high pH is thought to lead to antimicrobial properties of such materials similar to commonly applied calcium hydroxide or calcium silicates, however combined with an intrinsic radiopacity for X-ray imaging. This would simplify such formulations to single component materials which are less susceptible to demixing processes during transport, storage or processing.
The human body has very good self-healing capabilities for numerous different injuries to a variety of different tissues. This includes the main human mechanical framework, the skeleton. The skeleton is limited in its healing without additional aid by medicine mostly by the defect size. When the defect reaches a size above 2.5 cm the regeneration of the defect ends up faulty. Here is where implants, defect fillers and other support approaches developed in medicine can help the body to heal the big defect still successfully.
Usually sturdy implants (auto-/allo-/xenogenic) are implanted in the defect to bridge the distance, but for auto- and allogenic implants a suitable donor site must be found and for all sources the implant needs to be shaped into the defect specific site to ensure a perfect fit, the best support and good healing. This shaping is very time consuming and prone to error, already in the planning phase. The use of a material that is moldable and sets in the desired shape shortly after applying negates these disadvantages. Cementitious materials offer exactly this property by being in a pasty stage after the powder and liquid components have been mixed and the subsequently hardening to a solid implant. These properties also enable the extrusion, and therefore may also enable the injection, of the cement via a syringe in a minimal invasive approach.
To enable a good injection of the cement modifications are necessary. This work aimed to modify commonly used calcium phosphate-based cement systems based on α-TCP (apatitic) and β-TCP (brushitic). These have been modified with sodium phytate and phytic acid, respectively. Additionally, the α-TCP system has been modified with sodium pyrophosphate, in a second study, to create a storable aqueous paste that can be activated once needed with a highly concentrated sodium orthophosphate solution.
The powder phase of the α-TCP cement system consisted of nine parts α-TCP and one part CDHA. These were prepared to have different particle sizes and therefore enable a better powder flowability through the bimodal size distribution. α-TCP had a main particle size of 20 μm and CDHA of 2.6 μm. The modification with sodium phytate led to an adsorption of phytate ions on the surface of the α-TCP particles, where they started to form complexes with the Ca2+ ions in the solution. This adsorption had two effects. The first was to make the calcium ions unavailable, preventing supersaturation and ultimately the precipitation of CDHA what would lead to the cement hardening. The second was the increase of the absolute value of the surface charge, zeta potential, of the powder in the cement paste. Here a decrease from +3 mV to -40 mV could be measured. A strong value for the zeta potential leads to a higher repulsion of similarly charged particles and therefore prevents powder agglomeration and clogging on the nozzle during injection. These two modifications (bimodal particles size distribution and phytic acid) lead to a significant increase in the paste injectability. The unmodified paste was injectable for 30 % only, where all modified pastes were practically fully injectable ~90 % (the residual paste remained in the nozzle, while the syringe plunger already reached the end of the syringe).
A very similar observation could be made for the β-TCP system. This system was modified with phytic acid. The zeta potential was decreased even stronger from -10 ± 1.5 mV to -71.5 ± 12 mV. The adsorption of the phytate ions and subsequent formation of chelate complexes with the newly dissolved Ca2+ ions also showed a retarding effect in the cements setting reaction. Where the unmodified cement was not measurable in the rheometer, as the reaction was faster than the measurement setup (~1.5 min), the modified cements showed a transition through the gel point between 3-6 min. This means the pastes stayed between 2 and 4 times longer viscous than without the modification. Like with the first cement system also here the effects of the phytate addition showed its beneficial influence in the injectability measurement. The unmodified cement was not injectable at all, due to the same issue already encountered at the rheology measurements, but all modified pastes were fully injectable for at least 5 min (lowest phytate concentration) and at least 10 min (all other concentrations) after the mixing of powder and liquid.
The main goal of the last modification with sodium pyrophosphate was to create a paste that was stable in aqueous environment without setting until the activation takes place, but it should still show good injectability as this was the desired way of application after activation. Like before also the zeta potential changed after the addition of pyrophosphate. It could be lowered from -22 ± 2mV down to -61 to -68 ± 4mV (depending on the pyrophosphate concentration). The pastes were stored in airtight containers at room temperature and checked for their phase composition over 14 days. The unmodified paste showed a beginning phase conversion to hydroxyapatite between 7 and 14 days. All other pastes were still stable and unreacted. The pastes were activated with a high concentrated (30 wt%) sodium orthophosphate solution. After the activation the pastes were checked for their injectability and showed an increase from -57 ± 11% for the unmodified paste to -89 ± 3% (practically fully injectable as described earlier) for the best modified paste (PP005).
It can be concluded that the goal of enabling full injection of conventional calcium phosphate bone cement systems was reached. Additional work produced a storage stable paste that still ensures full injectability. Subsequent work already used the storable paste and modified it with hyaluronic acid to create an ink for 3D extrusion printing. The first two cement systems have also already been investigated in cell culture for their influence on osteoblasts and osteoclasts. The next steps would have to go more into the direction of translation. Figuring out what properties still need to be checked and where the modification needs adjustment to enable a clinical use of the presented systems.
Articular cartilage defects represent one of the most challenging clinical problem for orthopedic surgeons and cartilage damage after trauma can result in debilitating joint pain, functional impairment and in the long-term development of osteoarthritis. The lateral cartilage-cartilage integration is crucial for the long-term success and to prevent further tissue degeneration. Tissue adhesives and sealants are becoming increasingly more popular and can be a beneficial approach in fostering tissue integration, particularly in tissues like cartilage where alternative techniques, such as suturing, would instead introduce further damage. However, adhesive materials still require optimization regarding the maximization of adhesion strength on the one hand and long-term tissue integration on the other hand. In vitro models can be a valuable support in the investigation of potential candidates and their functional mechanisms. For the conducted experiments within this work, an in vitro disc/ring model obtained from porcine articular cartilage tissue was established. In addition to qualitative evaluation of regeneration, this model facilitates the implementation of biomechanical tests to quantify cartilage integration strength. Construct harvesting for histology and other evaluation methods could be standardized and is ethically less questionable compared to in vivo testing. The opportunity of cell culture technique application for the in vitro model allowed a better understanding of cartilage integration processes.
Tissue bonding requires chemical or physical interaction of the adhesive material and the substrate. Adhesive hydrogels can bind to the defect interface and simultaneously fill the gap of irregularly shaped defect voids. Fibrin gels are derived from the physiological blood-clot formation and are clinically applied for wound closure. Within this work, comparisons of different fibrin glue formulations with the commercial BioGlue® were assessed, which highlighted the need for good biocompatibility when applied on cartilage tissue in order to achieve satisfying long-term integration. Fibrin gel formulations can be adapted with regard to their long-term stability and when applied on cartilage disc/ring constructs improved integrative repair is observable. The kinetic of repairing processes was investigated in fibrin-treated cartilage composites as part of this work. After three days in vitro cultivation, deposited extracellular matrix (ECM) was obvious at the glued interface that increased further over time. Interfacial cell invasion from the surrounding native cartilage was detected from day ten of tissue culture. The ECM formation relies on molecular factors, e.g., as was shown representatively for ascorbic acid, and contributes to increasing integration strengths over time. The experiments performed with fibrin revealed that the treatment with a biocompatible adhesive that allows cartilage neosynthesis favors lateral cartilage integration in the long term. However, fibrin has limited immediate bonding strength, which is disadvantageous for use on articular cartilage that is subject to high mechanical stress. The continuing aim of this thesis was to further develop adhesive mechanisms and new adhesive hydrogels that retain the positive properties of fibrin but have an increased immediate bonding strength.
Two different photochemical approaches with the advantage of on-demand bonding were tested. Such treatment potentially eases the application for the professional user. First, an UV light induced crosslinking mechanism was transferred to fibrin glue to provide additional bonding strength. For this, the cartilage surface was functionalized with highly reactive light-sensitive diazirine groups, which allowed additional covalent bonds to the fibrin matrix and thus increased the adhesive strength. However, the disadvantages of this approach were the multi-step bonding reactions, the need for enzymatic pretreatment of the cartilage, expensive reagents, potential UV-light damage, and potential toxicity hazards. Due to the mentioned disadvantages, no further experiments, including long-term culture, were carried out. A second photosensitive approach focused on blue light induced crosslinking of fibrinogen (RuFib) via a photoinitiator molecule instead of using thrombin as a crosslinking mediator like in normal fibrin glue. The used ruthenium complex allowed inter- and intramolecular dityrosine binding of fibrinogen molecules. The advantage of this method is a one-step curing of fibrinogen via visible light that further achieved higher adhesive strengths than fibrin. In contrast to diazirine functionalization of cartilage, the ruthenium complex is of less toxicological concern. However, after in vitro cultivation of the disc/ring constructs, there was a decrease in integration strength. Compared to fibrin, a reduced cartilage synthesis was observed at the defect. It is also disadvantageous that a direct adjustment of the adhesive can only be made via protein concentration, since fibrinogen is a natural protein that has a fixed number of tyrosine binding sites without chemical modification.
An additional cartilage adhesive was developed that is based on a mussel-inspired adhesive mechanism in which reactivity to a variety of substrates is enabled via free DOPA amino acids. DOPA-based adhesion is known to function in moist environments, a major advantage for application on water-rich cartilage tissue surrounded by synovial liquid. Reactive DOPA groups were synthetically attached to a polymer, here POx, to allow easy chemical modifiability, e.g. insertion of hydrolyzable ester motifs for tunable degradation. The possibility of preparing an adhesive hybrid hydrogel of POx in combination with fibrinogen led to good cell compatibility as was similarly observed with fibrin, but with increased immediate adhesive strength. Degradation could be adjusted by the amount of ester linkages on the POx and a direct influence of degradation rates on the development of integration in the in vitro model could be shown.
Hydrogels are well suited to fill defect gaps and immediate integration can be achieved via adhesive properties. The results obtained show that for the success of long-term integration, a good ability of the adhesive to take up synthesized ECM components and cells to enable regeneration is required. The degradation kinetics of the adhesive must match the remodeling process to avoid intermediate loss of integration power and to allow long-term firm adhesion to the native tissue.
Hydrogels are not only important as adhesives for smaller lesions, but also for filling large defect volumes and populating them with cells to produce tissue engineered cartilage. Many different hydrogel types suitable for cartilage synthesis are reported in the literature. A long-term stable fibrin formulation was tested in this work not only as an adhesive but also as a bulk hydrogel construct. Agarose is also a material widely used in cartilage tissue engineering that has shown good cartilage neosynthesis and was included in integration assessment. In addition, a synthetic hyaluronic acid-based hydrogel (HA SH/P(AGE/G)) was used. The disc/ring construct was adapted for such experiments and the inner lumen of the cartilage ring was filled with the respective hydrogel. In contrast to agarose, fibrin and HA-SH/P(AGE/G) gels have a crosslink mechanism that led to immediate bonding upon contact with cartilage during curing. The enhanced cartilage neosynthesis in agarose compared to the other hydrogel types resulted in improved integration during in vitro culture. This shows that for the long-term success of a treatment, remodeling of the hydrogel into functional cartilage tissue is a very high priority. In order to successfully treat larger cartilage defects with hydrogels, new materials with these properties in combination with chemical modifiability and a direct adhesion mechanism are one of the most promising approaches.
Untersucht wurde der Einfluss mehrerer Chemotherapeutika auf den Chemokinrezeptor CXCR4 in
Myelomzelllinien auf Ebene des Promotors, der mRNA und der Rezeptorverteilung, wobei drei
Substanzen (Etoposid, Bortezomib und Dexamethason) als potenzielle Suppressoren des Promotors ausgemacht werden konnten. Abhängig vom Myelom-Zelltyp und der Dosierung können so evtl.
Rückschlüsse auf die beobachtete Suppression von CXCR4 bei erkrankten Patienten mit hoher CXCR4-Aktivität (hier: Malignes Myelom) durch die begleitende Chemotherapie gezogen werden, welche eine Diagnostik und Therapie bei diesen Patienten erschwert.
Hintergrund: Hintergrund für diese Arbeit waren Beobachtungen in klinischen Fallstudien von Lapa et al. am Universitätsklinikum Würzburg, die sich auf CXCR4 bezogen, welches u.a. bei Patienten mit
Multiplem Myelom überexprimiert wird und dadurch bereits als Target für Diagnostik und Therapie in der Klinik Anwendung findet. Dabei konnte bei PET-CT Untersuchungen in der Nuklearmedizin beobachtet werden, dass es durch die begleitende Chemotherapie der Patienten zu einer Suppression des markierten CXCR4-Signals kam, so dass es nicht mehr zur Verlaufsbeobachtung und
vor allem nicht mehr zur Radiotherapie und Therapiekontrolle verwendet werden konnte.
Um den Einfluss und mögliche Interaktionen der Chemotherapeutika auf CXCR4 zu untersuchen, war es Ziel dieser Arbeit, ein vergleichbares Szenario in-vitro nachzustellen und Einflüsse messbar zu
machen, um so mögliche Ansätze und Verbesserungsvorschläge für die klinische Anwendung zu
liefern.
Methoden/Ergebnisse: Hierfür wurden im ersten Teil INA-6 (Myelomzellen) und Mesenchymale
Stammzellen (MSC) kultiviert, in Ko-Kultur gebracht und nach einer bestimmten Zeit wieder getrennt, um anschließend den gegenseitigen Einfluss in Bezug auf CXCR4 zu messen. Zudem wurde der Einfluss von Dexamethason untersucht. Es zeigte sich eine enge Bindung zwischen INA-6 und MSC
sowie eine hohe CXCR4-Aktivität bei INA-6, jedoch konnte keine Induktion der CXCR4-Aktivität in MSC durch INA-6-Kontakt oder Dexamethason quantifiziert werden. Die Immunzytologie erwies sich aufgrund einer schweren Anfärbbarkeit von CXCR4 – auch mit verschiedensten Antikörpern und sogar Liganden-gekoppeltem Farbstoff– als kaum auswertbar, wobei eine Darstellung von CXCR4
generell aber gelang.
Der CXCR4-Promotor wurde mittels Software genauer analysiert, wobei einige relevante Bindestellen, u.a. für Glukokortikoide und NFkB gefunden wurden. Die Herstellung eines CXCR4-
pGl4.14-Promotor-Konstrukts war erfolgreich, ebenso dessen Einschleusung in Myelomzellen. Auch gelang die Herstellung stabiler transfizierter INA-6, sodass mit diesen anschließend konstantere Ergebnisse erzielt werden konnten.
Im größten Teil der Arbeit wurden geeignete Chemotherapeutika-Konzentrationen ermittelt und in Viabilitäts- und Apoptose-Versuchen überprüft. Die Stimulationsversuche mit diesen zeigten variable
Effekte abhängig vom Zelltyp (INA-6, MM1S), jedoch konnten Bortezomib, Etoposid und
Dexamethason konzentrationsabhängig als starke Suppressoren der CXCR4-Aktivität ausgemacht
werden, was sich v.a. auf Ebene der Promotoraktivität – gemessen mittels Luciferase - zeigte. Interpretation: In-vitro konnten somit drei potenzielle Suppressoren der CXCR4-Aktivität ausgemacht
werden: Etoposid, Bortezomib und Dexamethason. Zumindest beim INA-6-Zelltyp fiel dieser Effekt deutlich aus, wobei in der Klinik der entsprechende Zelltyp sowie die Dosierung der Medikamente berücksichtigt werden müssen. Hinzu kommen weitere Einflussfaktoren des menschlichen Körpers,
die nicht berücksichtig werden konnten. Die genauen Mechanismen der Suppression könnten sich aus den Bindestellen des Promotors erklären, die von uns analysiert wurden, aber auf die in weiteren Arbeiten noch näher eingegangen werden muss.
Chondrozyten stellen die zelluläre Komponente von hyalinem Knorpel dar, der die Gelenkflächen diarthrotischer Gelenke bedeckt. Über die perizelluläre Matrix (PZM) sind sie mit der extrazellulären Matrix des Knorpelgewebes, die im Wesentlichen aus Wasser, Kollagen-Typ-II (Koll-II) und Glykosaminoglykan (GAG) gebildet wird, verbunden. Die PZM gilt als wichtiges modulatorisches und protektives Element in der Signal- und Mechanotransduktion sowie für die Homöostase innerhalb des Knorpelgewebes. Degenerative und inflammatorische Prozesse führen zu irreparablen Schäden der Gewebearchitektur und -funktionalität. Die Regenerative Medizin strebt den Ersatz destruierter Gelenkflächen durch mittels Tissue Engineering hergestellten Neoknorpel an. 3D-Bioprinting gilt hier als attraktive Methode, nimmt jedoch über Scherkräfte während des Druckvorgangs auch schädigenden Einfluss auf das Überleben oder die Funktionalität der Zellen.
Zielsetzung dieser Arbeit war es, den möglichen protektiven Einfluss der PZM während des Druckvorgangs zu untersuchen. Aus porcinem Frischknorpel isolierte Chondrozyten wurden nach cast bzw. 3D-Bioprinting in Agarose-Biotinte hinsichtlich ihres Überlebens und ihrer Syntheseleistung von knorpelspezifischem Koll-II und GAG untersucht. Chondrozyten ohne PZM wurden mit Chondrozyten verglichen, die nach enzymatischer Isolation noch perizellulär Kollagen-Typ-VI als Marker der PZM aufwiesen. Chondrozyten mit PZM zeigten allgemein eine stärkere Produktion von Koll-II als Chondrozyten ohne PZM. Nach 3D-Bioprinting konnte für Chondrozyten ohne PZM eine signifikant geringere Produktion von GAG nachgewiesen werden als in der cast-Vergleichsgruppe, während dies für Chondrozyten mit PZM nicht gezeigt werden konnte.
Der gezeigte protektive Einfluss der PZM gegenüber Scherkräften während des Druckvorgangs eröffnet neue Methoden für das Cartilage Tissue Engineering. Weitere Untersuchungen sind notwendig, um dies zu bestätigen und die Translation in die klinische Forschung ermöglichen.