68.00.00 Surfaces and interfaces; thin films and nanosystems (structure and nonelectronic properties) (for surface and interface chemistry, see 82.65.+r, for surface magnetism, see 75.70.Rf)
Refine
Has Fulltext
- yes (2)
Is part of the Bibliography
- yes (2)
Document Type
- Doctoral Thesis (2)
Keywords
- Anisotropic Magnetoresistance (1)
- Anorganische Beschichtung (1)
- Beschichtung (1)
- Biomimetik (1)
- Epitaxy (1)
- Kunststoff (1)
- Layer-by-Layer-Verfahren (1)
- Magnetische Eigenschaft (1)
- Magnetismus (1)
- Magnetometry (1)
- Magnetoresistance (1)
- Magnetowiderstand (1)
- Mangansilicide (1)
- MnSi (1)
- Molekularstrahlepitaxie (1)
- Oberflächenfunktionalisierung (1)
- Polyelektrolyt (1)
- Polystyrol (1)
- Röntgendiffraktometrie (1)
- Titandioxid (1)
- Twin Domains (1)
- Twin Suppression (1)
- XRD (1)
- Zwillingsbildung (1)
- layer-by-layer-process (1)
- surface modification (1)
Institute
This thesis describes the growth and characterization of epitaxial MnSi thin films on Si substrates. The interest in this material system stems from the rich magnetic phase diagram resulting from the noncentrosymmetric B20 crystal structure. Here neighboring spins prefer a tilted relative arrangement in contrast to ferro- and antiferromagnets, which leads to a helical ground state where crystal and spin helix chirality are linked [IEM+85]. This link makes the characterization and control of the crystal chirality the main goal of this thesis.
After a brief description of the material properties and applied methods, the thesis itself is divided into four main parts. In the first part the advancement of the MBE growth process of MnSi on Si\((111)\) substrate as well as the fundamental structural characterization are described. Here the improvement of the substrate interface by an adjusted substrate preparation process is demonstrated, which is the basis for well ordered flat MnSi layers. On this foundation the influence of Mn/Si flux ratio and substrate temperature on the MnSi layer growth is investigated via XRD and clear boundaries to identify the optimal growth conditions are determined. The nonstoichiometric phases outside of this optimal growth window are identified as HMS and Mn\(_5\)Si\(_3\).
Additionally, a regime at high substrate temperatures and low Mn flux is discovered, where MnSi islands are growing incorporated in a Si layer, which could be interesting for further investigations as a size confinement can change the magnetic phase diagram [DBS+18]. XRD measurements demonstrate the homogeneity of the grown MnSi layers over most of the 3 inch wafer diameter and a small \(\omega\)-FWHM of about 0.02° demonstrates the high quality of the layers. XRD and TEM measurements also show that relaxation of the layers happens via misfit dislocations at the interface to the substrate.
The second part of the thesis is concerned with the crystal chirality. Here azimuthal \(\phi\)-scans of asymmetric XRD reflections reveal twin domains with a \(\pm\)30° rotation to the substrate. These twin domains seem to consist of left and right-handed MnSi, which are connected by a mirror operation at the \((\bar{1}10)\) plane. For some of the asymmetric XRD reflections this results in different intensities for the different twin domains, which reveals that one of the domains is rotated +30° and the other is rotated -30°. From XRD and TEM measurements an equal volume fraction of both domains is deduced. Different mechanisms to suppress these twin domains are investigated and successfully achieved with the growth on chiral Si surfaces, namely Si\((321)\) and Si\((531)\). Azimuthal \(\phi\)-scans of asymmetric XRD reflections demonstrate a suppression of up to 92%. The successful twin suppression is an important step in the use of MnSi for the proposed spintronics applications with skyrmions as information carriers, as discussed in the introduction.
Because of this achievement, the third part of the thesis on the magnetic properties of the MnSi thin films is not only concerned with the principal behavior, but also with the difference between twinned and twin suppressed layers. Magnetometry measurements are used to demonstrate, that the MnSi layers behave principally as expected from the literature. The analysis of saturation and residual magnetization hints to the twin suppression on Si\((321)\) and Si\((531)\) substrates and further investigations with more samples can complete this picture. For comparable layers on Si\((111)\), Si\((321)\) and Si\((531)\) the Curie-Weiss temperature is identical within 1 K and the critical field within 0.1 T.
Temperature dependent magnetoresistivity measurements also demonstrate the expected \(T^2\) behavior not only on Si\((111)\) but also on Si\((321)\) substrates. This demonstrates the successful growth of MnSi on Si\((321)\) and Si\((531)\) substrates. The latter measurements also reveal a residual resistivity of less then half for MnSi on Si\((321)\) in comparison to Si\((111)\). This can be explained with the reduced number of domain boundaries demonstrating the successful suppression of one of the twin domains. The homogeneity of the residual resistivity as well as the charge carrier density over a wide area of the Si\((111)\) wafer is also demonstrated with these measurements as well as Hall effect measurements.
The fourth part shows the AMR and PHE of MnSi depending on the angle between in plane current and magnetic field direction with respect to the crystal direction. This was proposed as a tool to identify skyrmions [YKT+15]. The influence of the higher C\(_{3\mathrm{v}}\) symmetry of the twinned system instead of the C\(_3\) symmetry of a B20 single crystal is demonstrated. The difference could serve as a useful additional tool to prove the twin suppression on the chiral substrates. But this is only possible for rotations with specific symmetry surfaces and not for the studied unsymmetrical Si\((321)\) surface. Measurements for MnSi layers on Si\((111)\) above the critical magnetic field demonstrate the attenuation of AMR and PHE parameters for increasing resistivity, as expected from literature [WC67]. Even if a direct comparison to the parameters on Si\((321)\) is not possible, the higher values of the parameters on Si\((321)\) can be explained considering the reduced charge carrier scattering from domain boundaries. Below the critical magnetic field, which would be the region where a skyrmion lattice could be expected, magnetic hysteresis complicates the analysis. Only one phase transition at the critical magnetic field can be clearly observed, which leaves the existence of a skyrmion lattice in thin epitaxial MnSi layers open.
The best method to solve this question seems to be a more direct approach in the form of Lorentz-TEM, which was also successfully used to visualize the skyrmion lattice for thin plates of bulk MnSi [TYY+12]. For the detection of in plane skyrmions, lamellas would have to be prepared for a side view, which seems in principle possible.
The demonstrated successful twin suppression for MnSi on Si\((321)\) and Si\((531)\) substrates may also be applied to other material systems.
Suppressing the twinning in FeGe on Si\((111)\) would lead to a single chirality skyrmion lattice near room temperature [HC12]. This could bring the application of skyrmions as information carriers in spintronics within reach.
Glossary:
MBE Molecular Beam Epitaxy
XRD X-Ray Diffraction
HMS Higher Manganese Silicide
FWHM Full Width Half Maximum
TEM Tunneling Electron Microscopy
AMR Anisotropic MagnetoResistance
PHE Planar Hall Effect
Bibliography:
[IEM+85] M. Ishida, Y. Endoh, S. Mitsuda, Y. Ishikawa, and M. Tanaka. Crystal Chirality and Helicity of the Helical Spin Density Wave in MnSi. II. Polarized Neutron Diffraction. Journal of the Physical Society of Japan, 54(8):2975, 1985.
[DBS+18] B. Das, B. Balasubramanian, R. Skomski, P. Mukherjee, S. R. Valloppilly, G. C. Hadjipanayis, and D. J. Sellmyer. Effect of size confinement on skyrmionic properties of MnSi nanomagnets. Nanoscale, 10(20):9504, 2018.
[YKT+15] T. Yokouchi, N. Kanazawa, A. Tsukazaki, Y. Kozuka, A. Kikkawa, Y. Taguchi, M. Kawasaki, M. Ichikawa, F. Kagawa, and Y. Tokura. Formation of In-plane Skyrmions in Epitaxial MnSi Thin Films as Revealed by Planar Hall Effect. Journal of the Physical Society of Japan, 84(10):104708, 2015.
[WC67] R. H. Walden and R. F. Cotellessa. Magnetoresistance of Nickel-Copper Single-Crystal Thin Films. Journal of Applied Physics, 38(3):1335, 1967.
[TYY+12] A. Tonomura, X. Yu, K. Yanagisawa, T. Matsuda, Y. Onose, N. Kanazawa, H. S. Park, and Y. Tokura. Real-Space Observation of Skyrmion Lattice in Helimagnet MnSi Thin Samples. Nano Letters, 12(3):1673, 2012.
[HC12] S. X. Huang and C. L. Chien. Extended Skyrmion Phase in Epitaxial FeGe(111) Thin Films. Physical Review Letters, 108(26):267201, 2012.
Es wurden planare Substrate mittels Flüssigphasenabscheidung mit Titandioxid beschichtet. Durch Absorption von Polyelektrolyten konnte die chemische Beschaffenheit der Substratoberfläche so verändert werden, daß die verwendbaren Substratmaterialien zur Beschichtung mit dem LPD-Verfahren um Glas, Polycarbonat, PET und Polyethylen erweitert wurden. Bedeutung kommt besonders der LPD-Beschichtung auf Borosilicatglas zu, da damit erstmalig ein Vergleich zwischen TiO2-Schichten aus der Flüssigphasenabscheidung und Schichten, die mittels Sol-Gel-Verfahren gewonnen wurden, möglich wurde. Der systematische Vergleich zwischen den Schichten der beiden Beschichtungsverfahren, ergab, daß Sol-Gel-Beschichtungen eine thermische Nachbehandlung mit Temperaturen größer 400°C benötigen, um ihre optimalen optischen und mechanischen Eigenschaften zu erreichen. Dabei tritt zwar eine starke Schrumpfung durch die Pyrolyse organischer Reste und Kristallisation auf. Jedoch führt diese Schrumpfung zu keiner Rißbildung oder Delaminierung. Im Gegenteil, die Ausbildung eines anorganischen Netzwerkes führt zum Aushärten der Schicht. Die bei höheren Temperaturen auftretende Kristallisation ermöglicht einen höheren Brechungsindex der Schicht bei gleichbleibend sehr guter Transparenz. Die bereits teilkristallin abgeschiedenen TiO2-Filme aus dem LPD-Verfahren schrumpfen zwar weit weniger stark als die Sol-Gel-Schichten, durch eine schlechte Haftung auf der Glasoberfläche verbreitern sich jedoch bereits vorhandene schmale Risse. Die Pyrolyse des Polyelektrolytlayers führt zum Verlust der haftvermittelnden Schicht und damit zu einem drastischen Rückgang der Schichthaftung und daraus bedingend der Bleistifthärte. Die Rißbildung verursacht einen starken Anstieg der Schichttrübung. Weiterhin verursacht die Rißverbreitung bei steigender Temperatur einen geringeren Brechzahlanstieg, als dies das LPD-Material ermöglichen würde. Durch diese Ergebnisse wird offensichtlich, daß für Substrate, die hohe Temperaturen ermöglichen, Sol-Gel-Beschichtungen dem LPD-Verfahren vorzuziehen ist. Für thermisch nicht belastbare Substrate stellt die Flüssigphasenabscheidung jedoch ein sehr gutes Beschichtungsverfahren dar. Um bestmögliche Ergebnisse mit dem LPD-Verfahren zu erzielen, kommt der Modifizierung der Substratoberfläche eine entscheiden Bedeutung zu. Zur bereits bekannten Oberflächenmodifizierung durch Ätzen mit Natriumperoxodisulfat (Hydroxylierung) wurde hierbei die zusätzliche bzw. alleinige Funktionalisierung durch Adsorption eines Polyelektrolytbilayers untersucht. Durch die Verwendung eines Polyelektrolytbilayers konnte die Dichte an Kristallisationsstellen im Vergleich zum unbehandelten bzw. hydroxylierten Substrat erhöht werden. Dies führte im Einklang mit dem bekannten Schichtwachstummodell zu gleichmäßigeren Beschichtungen. Der Einsatz des Polyelektrolytbilayers konnte in allen Fällen dazu genutzt werden, die Trübung der Schicht zu verringern. Dabei wurden Trübungswerte größer 50 % meist auf Werte von ca. 20 % und kleiner verbessert. Hohe Keimdichten bewirken dabei eine geringe Trübung. Jedoch konnte auch bei geringeren Keimdichten durch den Polyelektrolytbilayer geringe Trübungswerte erreicht werden. Bei der mechanischen Charakterisierung der TiO2-Schichten konnte festgestellt werden, daß bei den polymeren Substraten durch Hydroxylierung oder den Polyelektrolytbilayer die Schichthaftung verbessert werden. Eine Abhängigkeit der mechanischen Schichteigenschaften von der Substrathärt konnte mit Ausnahme des sehr weichen Polyethylens nicht gefunden werden. Jedoch ist für eine hohe Bleistifthärte eine gute Haftung nötig. Abriebuntersuchungen mit einem Filzstempel (Crockmetertest) zeigten ein analoges Verhalten zum Bleistifthärtetest. Um eventuell auftretende Nachteile der weichen Polymere ausgleichen zu können, wurden parallel Polystyrolsubstrate, beschichtet mit einer ORMOCER®-Hartschicht, untersucht. Dabei wurden sehr gute Ergebnisse in Hinblick auf Keimstellendichte, optische und mechanische Eigenschaften erzielt.