540 Chemie und zugeordnete Wissenschaften
Refine
Has Fulltext
- yes (66)
Is part of the Bibliography
- yes (66)
Year of publication
Document Type
- Doctoral Thesis (46)
- Journal article (20)
Keywords
- Sol-Gel-Verfahren (9)
- Polymere (8)
- Biomaterial (5)
- Beschichtung (4)
- biofabrication (4)
- hydrogels (4)
- Dünne Schicht (3)
- Elektrochemie (3)
- Hydrogel (3)
- Lithium-Ionen-Akkumulator (3)
Institute
- Institut für Funktionsmaterialien und Biofabrikation (66) (remove)
Sonstige beteiligte Institutionen
- Fraunhofer-Institut für Silicatforschung ISC (3)
- Fraunhofer-Institut für Silicatforschung (2)
- Bayerisches Geoinstitut, Universität Bayreuth (1)
- Fraunhofer IOF (1)
- Fraunhofer Institut für Silicatforschung (Würzburg) (1)
- Fraunhofer Institut für Silicatforschung ISC (1)
- Fraunhofer-Institut für Silicatforschung ISC, Würzburg (1)
- Fraunhofer-Institute for Silicate Research ISC (1)
- Hochschule Aalen (1)
- Lehrstuhl für Anorganische Chemie I, Universität Bayreuth (1)
EU-Project number / Contract (GA) number
- 645993 (1)
Hydrogels are key components in bioink formulations to ensure printability and stability in biofabrication. In this study, a well-known Diels-Alder two-step post-polymerization modification approach is introduced into thermogelling diblock copolymers, comprising poly(2-methyl-2-oxazoline) and thermoresponsive poly(2-n-propyl-2-oxazine). The diblock copolymers are partially hydrolyzed and subsequently modified by acid/amine coupling with furan and maleimide moieties. While the thermogelling and shear-thinning properties allow excellent printability, trigger-less cell-friendly Diels-Alder click-chemistry yields long-term shape-fidelity. The introduced platform enables easy incorporation of cell-binding moieties (RGD-peptide) for cellular interaction. The hydrogel is functionalized with RGD-peptides using thiol-maleimide chemistry and cell proliferation as well as morphology of fibroblasts seeded on top of the hydrogels confirm the cell adhesion facilitated by the peptides. Finally, bioink formulations are tested for biocompatibility by incorporating fibroblasts homogenously inside the polymer solution pre-printing. After the printing and crosslinking process good cytocompatibility is confirmed. The established bioink system combines a two-step approach by physical precursor gelation followed by an additional chemical stabilization, offering a broad versatility for further biomechanical adaptation or bioresponsive peptide modification.
Die experimentelle Verbesserung der makroskopischen Eigenschaften (z. B. thermische oder mechanische Eigenschaften) von Keramiken ist aufgrund der zahlreichen erforderlichen Experimente zeitaufwändig und kostenintensiv. Simulationen hingegen können die Korrelation von Mikrostruktur und makroskopischen Eigenschaften nutzen, um die Eigenschaften von beliebigen Gefügekompositionen zu berechnen. In bisherigen Simulationen wurden meist stark vereinfachte Modelle herangezogen, welche die Mikrostruktur einer Keramik nur sehr grob widerspiegeln und deshalb keine zuverlässigen Ergebnisse liefern.
In der vorliegenden Arbeit wird die Mikrostruktur-Eigenschafts-Korrelation der drei wichtigsten Nicht-Oxid-Keramiken untersucht. Dies sind Aluminiumnitrid (AlN), Siliciumnitrid (Si3N4) und Siliciumcarbid (SiC). Diese drei Keramiktypen vertreten die häufigsten Mikrostrukturtypen, welche bei Nicht-Oxid-Keramiken auftreten können. Zu jedem Keramiktyp liegen zwei verschiedene Proben vor.
Alle drei untersuchten Keramiktypen sind zweiphasig. Die Hauptphase von AlN und Si3N4 besteht aus keramischen Körnern, die Nebenphase erstarrt während der Sinterung aus den zugesetzten Sinteradditiven. Die Restporosität von AlN und Si3N4 wird als vernachlässigbar angesehen und in den Simulationen nicht berücksichtigt. Bei den SiC-Proben handelt es sich um Keramiken mit bimodaler Korngröÿenverteilung. Durch Infiltration mit flüssigem Silicium wurden die Hohlräume zwischen den Körnern aufgefüllt, um porenfreie SiSiC-Proben zu erhalten.
Anhand von Simulationen werden zunächst reale Mikrostrukturen in Anlehnung an vorliegende Vergleichsproben nachgebildet. Diese Modelle werden durch Abgleich mit rasterelektronenmikroskopischen 2D-Aufnahmen der Proben verifiziert. An den Modellen werden mit der Methode der Finite-Element-Simulation makroskopische Eigenschaften (Wärmeleitfähigkeit, Elastizitätsmodul und Poisson-Zahl) der Keramiken simuliert und mit experimentellen Messungen an den vorliegenden Proben abgeglichen.
Der Vergleich der Mikrostruktur von den computergenerierten Gefügen und den vorliegenden Proben zeigt in der Mustererkennung durch das menschliche Auge und quantitativ in den Gefügeparametern eine gute Übereinstimmung. Für die makroskopischen Eigenschaften wird auf der Basis einer ausführlichen Literaturrecherche zu den Materialparametern der beteiligten Phasen eine gute Übereinstimmung zwischen den experimentell gemessenen und den simulierten Eigenschaften erreicht. Evtl. auftretende Abweichungen zwischen Experiment und Simulation können damit erklärt werden, dass die Proben Verunreinigungen enthalten, da aus der Literatur bekannt ist, dass Verunreinigungen eine Verschlechterung der Wärmeleitfähigkeit bewirken.
Nachdem die Gültigkeit der Modelle verifiziert ist, wird der Einfluss von charakteristischen
Mikrostrukturparametern und Phaseneigenschaften auf die Wärmeleitfähigkeit, den Elastizitätsmodul und die Poisson-Zahl der Keramiken untersucht. Hierzu werden die Mikrostrukturparameter von AlN und Si3N4 gezielt um die Parameter der vorliegenden Vergleichsproben variiert. Bei beiden Keramiktypen werden die Volumenanteile der beteiligten Phasen sowie die mittlere Sehnenlänge der keramischen Körner verändert. Bei den AlN-Keramiken wird zusätzlich der Dihedralwinkel variiert, welcher Auskunft über den Benetzungsgrad der Flüssigphase gibt; bei den Si3N4-Keramiken ist das Achsenverhältnis der langgezogenen Si3N4-Körner von Interesse und wird deshalb ebenfalls variiert. Es zeigt sich, dass die Aufteilung der Teilvolumina zwischen den zwei Phasen den größten Einfluss auf die Eigenschaften der Keramik hat, während die übrigen Mikrostrukturparameter nur eine untergeordnete Rolle spielen.
Um die Qualität der Simulationen zu überprüfen, wird die Simulationsreihe an AlN mit unterschiedlicher Aufteilung der Volumina zwischen den beiden Phasen in Relation zu etablierten Modellen aus der Literatur (Mischungsregel und Modell nach Ondracek) gesetzt. Alle Simulationsergebnisse für die Wärmeleitfähigkeit und den Elastizitätsmodul liegen innerhalb der jeweils oberen und unteren Grenze beider Modelle. Es konnte also eine Verbesserung gegenüber den etablierten Modellen erzielt werden.
An allen drei Keramiktypen wird der Einfluss der Materialeigenschaften der Haupt- und Nebenphase auf die makroskopischen Eigenschaften der Keramik untersucht. Hierfür werden die Wärmeleitfähigkeit, der Elastizitätsmodul und die Poisson-Zahl der Phasen getrennt voneinander über einen größeren Bereich variiert. Es stellt sich heraus, dass es vom Keramiktyp und dem Volumenanteil der Nebenphase abhängt, wie stark der Einfluss einer Komponenteneigenschaft auf die Eigenschaft der Keramik ist.
Mit den im Rahmen dieser Arbeit durchgeführten Simulationen wird der Einfluss von Mikrostrukturparametern und Phaseneigenschaften berechnet. Auf der Grundlage dieser Simulationen können die Architektur des Gefüges simuliert und die Eigenschaften von Keramiken für individuelle Anwendungen berechnet werden. Dies ist die Basis für die Produktion von maßgeschneiderten Keramiken. Zudem können mit den validierten Mikrostrukturmodellen die Eigenschaften von unbekannten Mischphasen ermittelt werden, was experimentell oft nicht möglich ist.
Im Rahmen dieser Arbeit wurde ein prinzipieller Zugang zur Mikroverkapselung anorganischer Latentwärmespeichermaterialien (LWS) erarbeitet. Dazu wurden zwei basische, kristallwasserreiche Salzhydrate mit Schmelztemperaturen im Umgebungstemperaturbereich als Kernmaterialien und anorganisch-organische Hybridpolymere mit kovalent verbundenen anorganischen und organischen Struktureinheiten (ORMOCER®e) als Verkapselungsmaterial verwendet. Der Prozess verläuft grenzflächenselektiv in der flüssigen Phase, initiiert durch die basischen LWS, in Form einer auch bei milden Temperaturen ablaufenden Michael-Typ-Addition zwischen Acrylat- (Acr) und Thiolmonomeren (SH). Optimierte Verkapselungsergebnisse wurden mit Hybridmonomeren erreicht, deren funktionelle Gruppen in einem unstöchiometrischen Verhältnis von Acr:SH ≈ 5:1 vorlagen und über das anorganische Rückgrat vorverknüpft waren. Bei Verwendung eines Mikrodosiersystems wurden gleichmäßige, geschlossene Mikrokapseln mit Durchmessern von etwa 40–50 µm bei Schichtdicken von < 5 µm erhalten. Aufgrund einer zu geringen inhärenten Barrierewirkung der verwendeten Hybridpolymere gegenüber Wasserdampf konnten jedoch erhebliche Kristallwasserverluste nicht verhindert werden, sodass die erhaltenen Mikrokapseln noch nicht zur Anwendung als LWS geeignet sind. Da die beobachtete Tolerierung und sogar Bevorzugung für das deutliche Missverhältnis zwischen den polymerisierenden Gruppen für eine Stufenpolymerisation sehr ungewöhnlich ist, wurden an Modellsystemen Untersuchungen zur Aufklärung des Reaktionsmechanismus vorgenommen. Dazu wurde zunächst ein Mercaptosiloxan (MS) hergestellt, dessen Ringgrößen- bzw. Funktionalitätsverteilung mittels 29Si-NMR- und GPC-Messungen sehr gut aufgeklärt werden konnte. Dieses wurde für Verkapselungsversuche mit Trimethylolpropantriacrylat (TMPTA) kombiniert und das Verhältnis funktioneller Gruppen Acr:SH systematisch variiert. An den erhaltenen Proben konnte via µ-Raman-Tiefenscan-Untersuchungen der Einfluss der Harzzusammensetzung auf die Kapselschichten aufgeklärt werden. Während bei Acr:SH = 1:1 maximale Schichtdicken erhalten wurden, ergaben sich bei Acrylatüberschuss von 4:1 bis 6:1 optimierte Schichten im Sinne der Vorgaben, die gleichmäßig dünn und vollständig waren. Bei Thiolüberschuss wurden dagegen keine vollständig ausgebildeten Schichten erhalten. Das für die LWS-Verkapselungen verwendete Modellsystem TMPTA/MS wurde zusätzlich in Volumenpolymerisationen in homogener organischer Phase untersucht, die mit der Base Triethylamin initiiert wurden. Dabei wurden die stöchiometriebezogenen Vergelungsgrenzen bestimmt. Die detektierte Grenze bei Acr:SH < 5:1 für Acrylatüberschuss lag signifikant unterhalb von Verhältnissen funktioneller Gruppen, für die in Verkapselungsversuchen noch geschlossene Schichten erhalten wurden. Entlang der flüssig-flüssig-Grenzfläche wird somit der Gelpunkt lokal innerhalb eines breiteren Bereichs des Verhältnisses funktioneller Gruppen in der Harzmischung erreicht, als bei einer Polymerisation im gesamten Volumen. Durch weitergehende Untersuchungen zum Vernetzungsverhalten in Abhängigkeit vom Verhältnis funktioneller Gruppen weiterer Acrylat- und Thiolmonomere mit anderen (durchschnittlichen) Funktionalitäten konnte das grundsätzliche Vorliegen eines Stufenmechanismus untermauert werden. Aus einer Kombination der Flory-Stockmayer-Theorie mit der Carothers’schen Gleichung konnten theoretische Vergelungsgrenzintervalle hergeleitet werden. Die experimentell bestimmten Vergelungsgrenzen standen in vollständiger Übereinstimmung mit den theoretisch errechneten Intervallen. Innerhalb des Modellsystems TMPTA/MS konnten zudem weitere Materialeigenschaften bestimmt und zusätzliche Erkenntnisse zum Vernetzungsverhalten gewonnen werden. Durch In-situ-Messungen mittels µ-Raman-Spektroskopie wurde die Entwicklung der Umsetzungsgrade N(C=C) und N(S–H) von Acrylat und Thiol im Verlauf der Reaktionszeit untersucht. Dabei wurden einige Einschränkungen der verwendeten Messmethode identifiziert und beschrieben. Mittels in-situ-mechanischer Spektroskopie nach Chambon und Winter konnte weiterhin das Vergelungsverhalten des Systems in Abhängigkeit von Monomerzusammensetzung, Initiatorkonzentration und Temperatur und Unterschiede innerhalb der kritischen Gele systematisch charakterisiert werden. Die stabilsten kritischen Gele und kürzesten Gelzeiten wurden für hohe Basenkonzentrationen und bei stöchiometrischem Monomerverhältnis, aber auch für Acrylatüberschuss bis Acr:SH = 3:1, erhalten. Damit konnte auch innerhalb der Volumenpolymerisationen eine Bevorzugung des untersuchten Monomersystems für Acrylatüberschuss nachgewiesen werden. Weiterhin wurde das Geschwindigkeitsgesetz der Reaktion aufgeklärt. Es ergab sich bis zum Gelpunkt, zu je erster Ordnung in den beiden Monomeren und der Initiatorbase. Außerdem wurde die Aktivierungsenthalpie der Polymerisation in homogener Phase mittels einer Arrhenius-Auftragung bestimmt.
Background: Culturing of cells is typically performed on standard tissue culture plates generating growth conditions, which in general do not reflect the native three-dimensional cellular environment. Recent investigations provide insights in parameters, which strongly affect the general cellular behavior triggering essential processes such as cell differentiation. The physical properties of the used material, such as stiffness, roughness, or topology, as well as the chemical composition of the cell-surface interface are shown to play a key role in the initiation of particular cellular responses. Methods: We extended our previous research, which identified thin films of metallo-supramolecular coordination polyelectrolytes (MEPEs) as substrate to trigger the differentiation of muscular precursor cells. Results: Here, we show that the same MEPEs similarly stimulate the osteogenic differentiation of pre-osteoblasts. Remarkably, MEPE modified surfaces also trigger the differentiation of primary bone derived mesenchymal stem cells (BMSCs) towards the osteogenic lineage. Conclusion: This result leads to the conclusion that these surfaces individually support the specification of cell differentiation toward lineages that correspond to the natural commitment of the particular cell types. We, therefore, propose that Fe-MEPEs may be used as scaffold for the treatment of defects at least in muscular or bone tissue.
Die vorliegende Arbeit beschreibt die Entwicklung von SiO2-basierten nano- und mikroskalig strukturierten Schichten, welche eine Temperaturstabilität > 500 °C sowie eine Strukturtreue > 90 % aufzeigen. Diese wurden unter Verwendung von hybridpolymeren, partikelmodifizierten Sol-Gel-Vorstufen via UV-basierter Nanoimprintlithographie (UV-NIL) hergestellt. Der Einfluss chemischer und verfahrenstechnischer Syntheseparameter auf die anorganische Netzwerkbildung der flüssigen Vorstufe (hybridpolymerer Binder), die Polymerisation und Verdichtung der hybridpolymeren Sol-Gel-Schichten während der thermischen Härtung sowie deren Strukturierung via UV-NIL wurden im Detail untersucht und die erhaltenen Zusammenhänge mit den resultierenden Materialeigenschaften korreliert. Dabei dienten die Kenntnisse hinsichtlich des Schrumpf- und Verdichtungsverhaltens von planaren Schichten als Basis für die daraus hergestellten, strukturierten Schichten.
Die Wandmaterialien innerhalb des Plasmagefäßes zukünftiger Fusionsreaktoren sind teilweise extremen thermischen und mechanischen Belastungen ausgesetzt. Der thermisch höchstbelastete Bereich der Wand des Torusgefäßes ist der Divertor. Hier werden die anfallende Fusionsasche (Helium) und erodierte Wandpartikel aus dem Plasma entfernt, wodurch aufgrund erhöhter Teilchen-Wand-Interaktion Wärmeflüsse von bis zu 15 MW/m² erreicht werden. Wolfram gilt momentan als ideales Wandmaterial mit direktem Plasmakontakt (Plasma-Facing-Material, PFM) für diese Beanspruchungen. Unterhalb des PFM muss die Wärme möglichst effizient in das Kühlmedium übertragen werden. Im zukünftigen Experimentalreaktor ITER wird dafür eine Kupferlegierung (CuCrZr) verwendet, welche eine hohe Wärmeleitfähigkeit besitzt und für Temperaturen von bis zu 350°C unter fusionsrelevanten Bedingungen einsetzbar ist. In dieser Konfiguration kann ITER mit einer Kühlmitteltemperatur von 150°C betrieben werden. Zur kommerziellen Energiegewinnung ist dies unzureichend, da die thermische Effizienz durch eine deutliche Anhebung der Kühlmitteltemperatur verbessert werden muss. Wird der konventionelle Ansatz einer Wasserkühlung zu Grunde gelegt, ist das Ziel die Kühlmitteltemperatur auf mindestens 300°C anzuheben. In der Folge ist CuCrZr als Wärmesenkenmaterial nicht mehr einsetzbar, da verstärkte Alterung und Festigkeitsverlust im Material auftritt. Zusätzlich vergrößern sich die thermisch induzierten Spannungen in der Komponente mit höheren Temperaturen, durch unterschiedlich große thermische Ausdehnungskoeffizienten der beteiligten Materialien. Für höhere Temperaturen stellt faserverstärktes Kupfer eine mögliche Alternative dar. Die Kombination der hohen Wärmeleitfähigkeit der Kupfermatrix mit der hohen Steifigkeit und Festigkeit von Siliziumcarbidfasern soll die nötigen thermischen und mechanischen Eigenschaften des Wärmesenkenmaterials auch für Temperaturen über 350°C gewährleisten. Im Rahmen dieser Arbeit wurden zwei unterschiedlich hergestellte SiC-Verstärkungsfasertypen hinsichtlich ihrer Eignung für die Herstellung eines Kupfer-Matrix-Komposits (CuMMC) untersucht. Die Zielstellung für das CuMMC beinhaltet eine Festigkeit von 300 MPa bei 300°C sowie eine möglichst hohe Wärmeleitfähigkeit von über 200 W m-1 K-1. Beide Parameter werden stark von der Faserfestigkeit und der Anbindung zwischen Faser und Matrix beeinflusst. Die Wärmeleitfähigkeit durch das CuMMC wird von der Kupfermatrix dominiert, wodurch geringere Faservolumenanteile von Vorteil sind. Höhere Faserfestigkeit erfordert geringere Faseranteile zum Erreichen mechanischer Vorgaben, womit die erzielbare Wärmeleitfähigkeit des CuMMCs steigt. Die Faserfestigkeit wird durch Einzel-Faser- Zugversuche validiert. Darüber hinaus ist die Anbindung zwischen Faser und Matrix essentiell, um die optimale Verstärkungswirkung durch die Fasern im CuMMC zu erzielen. Zur Faser-Matrix-Anbindung werden für jeden Fasertyp unterschiedliche Zwischenschichtsysteme verwendet, die anschließend durch Einzelfaser-Push-Out-Versuche validiert werden. Sind die Voraussetzungen von Faserfestigkeit und Anbindung für einen Fasertyp erfüllt, wird dieser für die Herstellung eines unidirektional verstärkten CuMMCs verwendet, welches bezüglich seiner mechanischen und thermischen Eigenschaften charakterisiert wird. Die mechanische Charakterisierung des CuMMCs erfolgt durch Zugversuche und dehnungsgeregelte, zyklische Versuche, wobei der Fokus neben der Festigkeit auf der Plastifizierung, Verfestigung und Schädigung innerhalb des CuMMCs liegt. Die thermische Charakterisierung erfolgt anhand der Wärmeleitfähigkeitsbestimmung sowohl parallel, als auch transversal zur Faserrichtung. Die mechanischen und thermischen Eigenschaften werden in Abhängigkeit von Faservolumenanteil und Temperatur untersucht. Um den Einfluss von längeren Betriebsphasen unter hoher thermischer Belastung analysieren zu können, wird das CuMMC bei 550°C für 400 h ausgelagert und anschließend wiederum mittels Vergleich seiner mechanischen und thermischen Eigenschaften auf mögliche Schädigungen untersucht. Zur Begutachtung von Schliff- und Bruchflächen zur Schadensanalyse stehen als bildgebende Untersuchungsmethoden neben Lichtmikroskopen ebenso Rasterelektronenmikroskope (REM) zur Verfügung.
Aim of this thesis was the development of functionalizable hydrogel coatings for melt electrowritten PCL scaffolds and of bioprintable hydrogels for biofabrication.
Hydrogel coatings of melt electrowritten scaffolds enabled to control the surface hydrophilicity, thereby allowing cell-material interaction studies of biofunctionalized scaffolds in minimal protein adhesive environments. For this purpose, a hydrophilic star- shaped crosslinkable polymer was used and the coating conditions were optimized. Moreover, newly developed photosensitive scaffolds facilitated a time and pH independent biofunctionalization.
Bioprintable hydrogels for biofabrication were based on the allyl-functionalization of gelatin (GelAGE) and modified hyaluronic acid-products, to enable hydrogel crosslinking by means of the thiol-ene click chemistry. Optimization of GelAGE hydrogel properties was achieved through an in-depth analysis of the synthesis parameters, varying Ene:SH ratios, different crosslinking molecules and photoinitiators. Homogeneity of thiol-ene crosslinked networks was compared to free radical polymerized hydrogels and the applicability of GelAGE as bioink for extrusion-based bioprinting was investigated. Purely hyaluronic acid-based bioinks were hypothesized to maintain mechanical- and rheological properties, cell viabilities and the processability, upon further decreasing the overall hydrogel polymer and thiol content.
Hydrogel coatings: Highly structured PCL scaffolds were fabricated with MEW and subjected to coatings with six-armed star-shaped crosslinkable polymers (sP(EO-stat-PO)). Crosslinking results from the aqueous induced hydrolysis of reactive isocyanate groups (NCO) of sP(EO-stat-PO) and increased the surface hydrophilicity and provided a platform for biofunctionalizations in minimal protein adhesive environments. Not only the coating procedure was optimized with respect to sP(EO-stat-PO) concentrations and coating durations, instead scaffold pre-treatments were developed, which were fundamental to enhance the final hydrophilicity to completely avoid unspecific protein adsorption on sP(EO-stat-PO) coated scaffolds. The sP(EO-stat-PO) layer thickness of around 100 nm generally allows in vitro studies not only in dependence on the scaffold biofunctionalization but also on the scaffold architecture. The hydrogel coating extent was assessed via an indirect quantification of the NCO-hydrolysis products. Knowledge of NCO-hydrolysis kinetics enabled to achieve a balance of sufficiently coated scaffolds while maintaining the presence of NCO-groups that were exploited for subsequent biofunctionalizations. However, this time and pH dependent biofunctionalization was restricted to small biomolecules. In order to overcome this limitation and to couple high molecular weight biomolecules another reaction route was developed. This route was based on the photolysis of diazirine moieties and enabled a time and pH independent scaffold biofunctionalization with streptavidin and collagen type I. The fibril formation ability of collagen was used to obtain different collagen conformations on the scaffolds and a preliminary in vitro study demonstrated the applicability to investigate cell-material interactions.
The herein developed scaffolds could be applied to gain deeper insights into the fundamentals of cellular sensing. Especially the complexity by which cells sense e.g. collagen remain to be further elucidated. Therefore, different hierarchies of collagen-like conformations could be coupled to the scaffolds, e.g. gelatin or collagen-derived peptide sequences, and the activation of DDR receptors in dependence on the complexity of the coupled substances could be determined. Due to the strong streptavidin-biotin bond, streptavidin functionalized scaffolds could be applied as a versatile platform to allow immobilization of any biotinylated molecules.
Gelatin-based bioinks: First the GelAGE products were synthesized with respect to molecular weight distributions and amino acid composition integrity. A detailed study was conducted with varying molar ratios of reactants and synthesis durations and implied that gelatin degradation was most dominant for high alkaline synthesis conditions with long reaction times. Gelatin possesses multiple functionalizable groups and the predominant functionalization of amine groups was confirmed via different model substances and analyses. Polymer network homogeneity was proven for the GelAGE system compared to free radical polymerized hydrogels with GelMA. A detailed analysis of hydrogel compositions with varying functional group ratios and UV- or Vis-light photoinitiators was executed. The UV-initiator concentration is restricted due to cytotoxicity and potential cellular DNA damages upon UV-irradiation, whereas the more cytocompatible Vis- initiator system enabled mechanical stiffness tuning over a wide range by controlling the photoinitiator concentration at constant Ene:SH ratios and polymer weight percentages. Versatility of the GelAGE bioink for different AM techniques was proved by exploiting the thermo-gelling behavior of differently degraded GelAGE products for stereolithography and extrusion-based printing. Moreover, the viability of cell-laden GelAGE constructs was demonstrated for extrusion-based bioprinting. By applying different multifunctional thiol-macromolecular crosslinkers the mechanical and rheological properties improved concurrently to the processability. Importantly, lower thiol-crosslinker concentrations were required to yield superior mechanical strengths and physico-chemical properties of the hydrogels as compared to the small bis-thiol-crosslinker. Extrusion-based bioprinting with distinct encapsulated cells underlined the need for individual optimization of cell-laden hydrogel formulations.
Not only the viability of encapsulated cells in extrusion-based bioprinted constructs should be assessed, instead other parameters such as cell morphology or production of collagen or glycosaminoglycans should be considered as these represent some of the crucial prerequisites for cartilage Tissue Engineering applications. Moreover, these studies should be expanded to the stereolithographic approach and ultimately the versatility and cytocompatibility of formulations with macromolecular crosslinkers would be of interest. Macromolecular crosslinkers allowed reducing polymer weight percentages and amounts of thiol groups and are thus expected to contribute to increased cytocompatibility, especially in combination with the more cytocompatible Vis-initiator system, which remains to be elucidated.
Hyaluronic acid-based bioinks: Different molecular weight hyaluronic acid (HA) products were synthesized to bear ene- (HAPA) or thiol-functionalities (LHASH) to enable pure HA thiol-ene crosslinked hydrogels. Depending on the molecular weight of modified HA products, polymer weight percentages and Ene:SH ratios, a wide range of mechanical stiffness was covered. However, the manageability of high molecular weight HA (HHAPA) product solutions (HHAPA + LHASH) was restricted to 5.0 wt.-% as a consequence of the high viscosity. Based on the same HA thiol component (LHASH), hybrid hydrogels of HA with GelAGE were compared to pure HA hydrogels. Although the overall polymer weight percentage of HHAPA + LHASH hydrogels was significantly lowered compared to hybrid hydrogels (GelAGE + LHASH), similar mechanical and physico-chemical properties of pure HA hydrogels were determined with maintained Ene:SH ratios. Low viscous low molecular weight HA precursor solutions (LHAPA + LHASH) prevented the applicability for extrusion-based bioprinting, whereas the non-thermoresponsive HHAPA + LHASH system could be bioprinted with only one-fourth of the polymer content of hybrid formulations. The high viscous behavior of HHAPA + LHASH solutions, lower polymer weight percentages, decreased printing pressures and consequently declined shear stress during printing, were hypothesized to contribute to high cell viabilities in extrusion-based bioprinted constructs compared to the hybrid bioink.
The low molecular weight HA precursor formulation (LHAPA + LHASH) was not applicable for extrusion-based printing, but this system has potential for other AM techniques such as stereolithography. Similar to the GelAGE system a more detailed study on the functions of encapsulated cells would be useful to further develop this system. Moreover, the initiation with the Vis-initiator should be conducted.
The detection of toxic gases, such as NH\(_{3}\) and CO, in the environment is of high interest in chemical, electronic, and automotive industry as even small amounts can display a health risk for workers. Sensors for the real‐time monitoring of these gases should be simple, robust, reversible, highly sensitive, inexpensive and show a fast response. The indicator supraparticles presented herein can fulfill all of these requirements. They consist of silica nanoparticles, which are assembled to supraparticles upon spray‐drying. Sensing molecules such as Reichardt's dye and a binuclear rhodium complex are loaded onto the microparticles to target NH\(_{3}\) and CO detection, respectively. The spray‐drying technique affords high flexibility in primary nanoparticle size selection and thus, easy adjustment of the porosity and specific surface area of the obtained micrometer‐sized supraparticles. This ultimately enables the fine‐tuning of the sensor sensitivity and response. For the application of the indicator supraparticles in a gas detection device, they can be immobilized on a coating. Due to their microscale size, they are large enough to poke out of thin coating layers, thus guaranteeing their gas accessibility, while being small enough to be applicable to flexible substrates.
Im Rahmen der vorliegenden Arbeit wurde ein neuer Beschichtungstyp für die Elektrodenmaterialien von Lithium-Ionen-Akkumulatoren entwickelt und charakterisiert. Dieser besteht aus einem speziellen anorganisch-organischen Hybridpolymer, das sich bezüglich seiner Zusammensetzung und Funktion gegenüber bestehenden Beschichtungsmaterialien abhebt. Das anorganisch-organische Netzwerk des Hybridpolymers konnte mittels Feststoff-NMR-Messungen vollständig aufgeklärt werden. Dabei zeigte sich ein stabiles anorganisches Gerüst aus hoch vernetzten Polysiloxan-Einheiten. Zusätzliche organische Modifizierungen liegen als lange bewegliche Ketten mit funktionellen Polyethylenoxid-Einheiten vor oder sind in Form von Polyethern und Diolen vernetzt. Mit dieser speziellen Netzwerkstruktur ist es möglich, Materialeigenschaften zu erzeugen, die über solche von rein anorganischen und rein organischen Beschichtungen hinausgehen. Zu den mit verschiedenen Methoden nachgewiesenen Eigenschaften zählen eine hohe ionische Leitfähigkeit von 10\(^{-4}\) S/cm, eine hohe Elastizität mit E = 63 kPa, eine hohe elektrochemische Stabilität bis 5,0 V vs. Li/Li\(^+\) und eine hohe thermische Stabilität.
Eine weitere Besonderheit des neuen Beschichtungsmaterials ist die mehrstufige Vernetzung der anfänglichen Prekursoren zu einem Hybridpolymer-Sol und dem abschließenden Hybridpolymer-Gel. Die im Beschichtungssol vorliegende Teilvernetzung der Vorstufen konnte detailliert mittels Flüssig-NMR-Messungen untersucht und beschrieben werden. Aus den Messungen ließ sich folgern, dass die organisch und anorganisch vernetzbaren Gruppen im Sol teilweise vernetzt vorliegen. Die sterisch erreichbaren Si-OR-Gruppen der so entstandenen Oligomere sind vorwiegend nicht hydrolysiert, wodurch deren anorganische Anbindung an die OH-Gruppen der Partikeloberflächen kinetisch bevorzugt ist. Damit lassen sich besonders homogene und vollständig bedeckende Beschichtungen der Elektrodenmaterialien erzeugen. Dies konnte mit verschiedenen physikalischen und chemischen Methoden nachgewiesen werden: simulationsgestützte Rückstreuanalysen mittels REM, hochaufgelöste TEM-Aufnahmen sowie Elementanalysen durch EDX und XPS.
Nach der Optimierung des nasschemischen Beschichtungsprozesses über Rotationsverdampfen ergaben sich für die verschiedenen Elektrodenmaterialien Li\(_4\)Ti\(_5\)O\(_{12}\), Li(Ni,Co,Mn)O\(_2\) und Li(Mn,Ni)\(_2\)O\(_4\) jeweils etwa 20 nm dicke Beschichtungen mit Hybridpolymer. Die Frage nach deren Lösungsmittelbeständigkeit konnte durch die Analyse von behandelten Proben mit TG, REM, XPS und ICP-OES aufgeklärt werden. Dabei zeigte sich sowohl für die Behandlung mit NMP, dem klassischen Lösungsmittel bei der Elektrodenfertigung mit PVDF-Binder, als auch für die Behandlung mit dessen umweltschonenderem Ersatzstoff Aceton eine gute Beständigkeit der Beschichtung. Die Beschichtung löste sich in den Lösungsmitteln an, blieb allerdings als geschlossene nanoskalige Beschichtung erhalten. Lediglich gegenüber dem Lösungsmittel H\(_2\)O, das in Kombination mit dem neuen Binder CMC eingesetzt wird, wurde eine mangelnde Schichtstabilität deutlich. Das dafür verantwortliche Quellverhalten der Beschichtung konnte mittels Dünnschicht-Modellsystem und daran durchgeführten REM-, IR- und EPA-Untersuchungen aufgeklärt werden. Die Optimierung des Hybridpolymer-Materials bezüglich einer besseren H\(_2\)O-Beständigkeit übersteigt den Rahmen dieser Arbeit und liefert die Grundlage für weitere künftige Forschungsarbeiten.
Aufgrund der vollständigen Bedeckung der neuen Beschichtung, ihrer besonderen Eigenschaften und ihrer Beständigkeit bei der klassischen Elektrodenfertigung ist es möglich, die Elektrodenmaterialien grundlegend hinsichtlich ihrer wichtigsten Eigenschaften zu verbessern. Hierfür wurden sowohl über die NMP- als auch über die Aceton-Route Elektroden gefertigt und zu Halbzellen und Vollzellen verarbeitet. Die REM-Analyse der Elektroden zeigte, dass die Partikelbeschichtungen keinen negativen Einfluss auf die Homogenität und Morphologie der Elektroden ausüben. Damit war es möglich, jeweils einen direkten Vergleich von beschichteten und unbeschichteten Materialien hinsichtlich ihrer elektrochemischen Performance anzustellen. Für die Kathodenmaterialien Li(Ni,Co,Mn)O\(_2\) und Li(Mn,Ni)\(_2\)O\(_4\) ergaben die Zyklenfestigkeits- und Impedanzmessungen klare Verbesserungen durch die Beschichtung. Verbunden mit einer Verbesserung der Energiedichte erhöhte sich bei beiden Materialien die Zyklenfestigkeit um mehr als 60 %. Bei Li(Mn,Ni)\(_2\)O\(_4\) zeigt sich die Verbesserung in einer erhöhten Zellspannung durch das vergleichsweise hohe Redoxpotential des Materials von etwa 4,7 V vs. Li/Li\(^+\), während sich bei Li(Ni,Co,Mn)O\(_2\) die Hochvoltfähigkeit des Materials verbessert, was mit einer vergrößerten Speicherkapazität verbunden ist. Dabei ist herauszustellen, dass für keines der Materialien ein negativer Einfluss der dünnen Beschichtung auf die Leistungsdichte festgestellt werden konnte.
Der erwartete Mechanismus für die verbesserte Elektrodenfunktion durch das Hybridpolymer ist die Bildung einer physikalischen Schutzschicht in Form einer Li\(^+\)-leitfähigen Membran. Diese umgibt das Elektrodenmaterial vollständig, ermöglicht die Ladungsträgerinterkalation und schützt die Elektrode gleichzeitig vor irreversiblen Reaktionen mit dem Elektrolyten. Damit verbunden ist eine verminderte Mn-Auslösung und eine verminderte Entwicklung von isolierenden Deckschichten aus Reaktionsprodukten wie LiF, Li\(_2\)O, Li\(_2\)CO\(_3\), was sich positiv auf die Alterung der Batteriezellen auswirkt. Die Funktion der Beschichtung wurde primär auf den Kathodenmaterialien demonstriert. Doch auch auf der Anodenseite wurde ihre Anwendungstauglichkeit aufgezeigt, was das große Potential der Beschichtung für eine breite Anwendung in Lithium-Ionen-Batterien verdeutlicht.
The present work aims towards the investigation of polymer degradation under biologically relevant conditions. In order to assess a potential degradation of polymers of interest for biomedical applications in vivo and associated effects on living tissue, representatives of poly(2-oxazoline)s and polypeptoids as well as poly(ethylene glycol) and poly(N-vinylpyrrolidone) for reference purposes are examined regarding their stability under oxidative and hydrolytic conditions as well as towards enzymatic degradation.
The polymers investigated in the framework of this thesis are generally considered to be non-biodegradable. Both poly(ethylene glycol) and poly(N-vinylpyrrolidone) are or were applied intensively in vivo provoking seriously harmful side effects like fatal blood poisoning from the oxidation of poly(ethylene glycol) chain ends or poly(N-vinylpyrrolidone) storage disease. Poly(2-alkyl-2-oxazoline)s and polypeptoids, both promising polymeric biomaterials for a wide variety of in vivo applications, are not clinically applied yet but undergo thorough investigations. However, comprising amide bonds within the backbone or the appending side chain, poly(2-alkyl-2-oxazoline)s and polypeptoids potentially offer a higher susceptibility towards (bio-)degradation. Representing the three most impactful initiators of degradation in vivo, the present study is focused on polymer deterioration by oxidative species, hydrolytic conditions and enzymes.
Oxidative species are generated in a variety of processes in vivo, both on purpose and as an unintentional by-product. Previous investigations revealed the susceptibility of poly(ethylene glycol), poly(N-vinylpyrrolidone), poly(2-alkyl-2-oxazoline)s and polypeptoids to deterioration by hydroxyl radicals deriving from hydrogen peroxide and copper ions. The obtained data confirm previous results of an apparent degradation rate increasing with increasing chain length due to self-inhibitory end group effects for all investigated polymer species. Although the exact concentrations of oxidative species in vivo are very controversial, with respect to their great variety and wide distribution the investigated polymers are likely prone to oxidative deterioration to some extent, with rates, mechanisms and degradation products strongly depending on the respective reactive species, polymer structure and chain length.
Like blood, most tissues of the human body benefit from a slightly alkaline pH value. Nevertheless, specific areas like the human stomach or tumor tissues possess acidic conditions potentially capable to cleave amide bonds comprised by poly(2-alkyl-2-oxazoline)s and polypeptoids. Unlike the hydrolysis of poly(2-alkyl-2-oxazoline)s resulting in side chain cleavage, the hydrolysis of polypeptoids induces backbone scission decreasing the polymer chain length tremendously and releasing, if performed exhaustively, the respective amino acids. Hydrolysis of polysarcosine is monitored by quantification of the released sarcosine via 1H-NMR spectroscopy and determination of the residual Mw via GPC. Its cyclic dimer sarcosine anhydride is formed as an intermediate product in this process via cyclization of unstable linear dimers of sarcosine.
Modification and degradation of bio(macro)molecules is an essential part of human metabolism. Polymers bearing amide bonds and showing a great similarity to natural occurring and widely distributed polypeptides, like poly(2-alkyl-2-oxazoline)s and polypeptoids, bear the potential of an enzymatic biodegradability by (more or less specific) peptidases. Just like the acidic hydrolysis described previously, peptidase activity would result in the cleavage of polymer amide bonds. The aim of the present thesis was to evaluate the stability of poly(2-alkyl-2-oxazoline)s and polypeptoids as well as poly(ethylene glycol) for the sake of reference under circumstances resembling in vivo conditions as closely as possible. Initial experiments focused on the degradation of dye-labeled upon incubation with homogenates of freshly harvested rat liver and kidney. However, although the obtained results are promising for the most part, they are considered rather unreliable and non-reproducible for various reasons. More conclusive data are attained from the incubation of non-labeled polymers in freshly laid chicken eggs. While no evidence for an enzymatic digestion of poly(ethylene glycol) in chicken egg white is found and deterioration of poly(2-methyl-2-oxazoline) upon incubation apparently derives from non-enzymatic hydrolysis, incubated polysarcosine samples reveal distinct elugram patterns depending on the respective C- and N-terminal end groups indicating both exopeptidase and endopeptidase activity. It has to be kept in mind though, that an enzymatic digestibility of polysarcosine does not necessarily imply the digestion of polypeptoids bearing longer side chains by peptidases as well, which should be investigated in further studies.