Refine
Has Fulltext
- yes (22)
Is part of the Bibliography
- yes (22)
Year of publication
Document Type
- Doctoral Thesis (22) (remove)
Keywords
- 3D-Druck (22) (remove)
Institute
- Abteilung für Funktionswerkstoffe der Medizin und der Zahnheilkunde (7)
- Graduate School of Life Sciences (4)
- Institut für Funktionsmaterialien und Biofabrikation (3)
- Klinik und Polikliniken für Zahn-, Mund- und Kieferkrankheiten (3)
- Poliklinik für Zahnärztliche Prothetik (3)
- Graduate School of Science and Technology (2)
- Poliklinik für Zahnerhaltung und Parodontologie (2)
- Betriebswirtschaftliches Institut (1)
- Institut für Medizinische Lehre und Ausbildungsforschung (1)
- Klinik und Poliklinik für Mund-, Kiefer- und Plastische Gesichtschirurgie (1)
Ziel dieser Arbeit war die Herstellung individuell formbarer Strukturen mittels des 3D-Pulverdrucks auf Basis von bei Raumtemperatur hydraulisch abbindenden Knochenzementpulvern. Neben der Entwicklung neuartiger Zementformulierungen auf Basis von Magnesiumphosphaten war vor allem die gleichzeitige Ausstattung der Werkstoffe mit temperaturlabilen und bioaktiven Verbindungen ein wichtiger Entwicklungsschritt. Die Lokalisation der Wirkstoffe korreliert dabei mit entsprechenden Farbinformationen im Design der Konstrukte, die durch einen Mehrfarbendrucker physikalisch abgebildet werden. Das auf Calciumphosphat basierende System hat den Nachteil, dass die Abbindereaktion bei stark sauren pH-Werten abläuft, was negative Auswirkungen auf die gleichzeitige Ausstattung mit sensitiven Wirkstoffen hat. Zur Lösung dieser Problematik wurde ein neues Knochenzementpulver auf Magnesiumphosphatbasis entwickelt, welches unter neutralen pH-Bedingungen mit ammoniumhaltigem Binder zu dem Mineral Struvit abbindet. Das Zementpulver aus Trimagnesiumphosphat wurde bezüglich der pulvertechnologischen Eigenschaften, wie Partikelgröße, Partikelgrößenverteilung, Glättungseigenschaften und Schüttdichte sowie hinsichtlich des Abbindeverhaltens charakterisiert und für den Druckprozess optimiert. Die hohe Strukturgenauigkeit ermöglichte die Darstellung von makroporösen Strukturen mit einem minimalen Porendurchmesser von ca. 200 µm. Gute mechanische Kennwerte der gedruckten Strukturen, sowie eine hohe Umsetzungsrate zur gewünschten Phase Struvit wurden durch eine Nachhärtung in Ammoniumphosphatlösung erhalten. Die Druckfestigkeit betrug > 20 MPa und der Phasenanteil von Struvit konnte auf insgesamt 54 % gesteigert werden. Die Darstellung von wirkstoffmodifizierten Calciumphosphat- und Magnesiumphosphatstrukturen durch Verwendung eines Mehrfarbendruckers wurde beginnend vom Design der Strukturen bis hin zur experimentellen Bestimmung der Korrelation von Farbinformation und Binderapplikation etabliert. Zur Sicherstellung einer hohen Druckqualität und der Ortsständigkeit gedruckter Wirkstoffe erwies sich eine zusätzliche Modifikation des Tricalciumphosphatpulvers mit quellfähigen Polymeren (Hydroxypropylmethyl-cellulose (HPMC) bzw. Chitosan) als erfolgreich. Eine maximale Auflösung von ca. 400 µm konnte für eine HPMC/Chitosan/Calciumphosphat-Variante erreicht werden, während das hochreaktive Magnesiumphosphat/Magnesiumoxid-System eine Auflösung von 480 µm aufwies. Die Ortsständigkeit eingebrachter Lösungen war Voraussetzung für die Steuerung der Freisetzungskinetik. Das Freisetzungsverhalten in vitro wurde in Abhängigkeit von der Wirkstofflokalisation (homogen, Depot, Gradient) innerhalb der Matrix und unter Einbringung zusätzlicher polymerer Diffusionsbarrieren für den Wirkstoff Vancomycin untersucht. Dabei zeigte sich, dass die Modifikation der Matrices mit Polymeren zu einer verzögerten Freisetzung führte. Die lokale Wirkstoffmodifikation der Matrices in Form eines Depots oder Gradienten hatte Einfluss auf die Freisetzungskinetik, wobei eine lineare Freisetzung mit der Zeit (Kinetik 0. Ordnung) erreicht werden konnte. Die applizierten Wirkstoffe umfassten sowohl niedermolekulare Verbindungen, wie etwa das Antibiotikum Vancomycin oder das Polysaccharid Heparin, als auch proteinbasierte Faktoren wie den Knochenwachstumsfaktor rhBMP-2. Beurteilt wurde die pharmakologische Wirksamkeit der Verbindungen nach dem Druck, sowie nach der Freisetzung aus einer Calciumphosphatmatrix für den Wirkstoff Vancomycin. Es konnte belegt werden, dass die biologische Aktivität nach dem Druckprozess zu über 80 % erhalten blieb. Limitierend war der stark saure pH-Wert bei bruschitbasierten Systemen, der zu einer Inaktivierung des Proteins führte. Diesem Problem könnte durch die Nutzung des neutral abbindenden Magnesiumphosphatsystems entgegengewirkt werden. Abschließend erfolgten eine mikrostrukturelle Charakterisierung der Calciumphosphat- und Magnesiumphosphatmatrices mittels µ-CT-Analyse und Heliumpyknometrie, sowie eine quantitative Phasenanalyse nach Rietveld. Experimentell konnte nachgewiesen werden, dass mit Hilfe des 3D-Pulverdruck die Darstellung von Makroporen > 200 µm möglich ist. Die Analyse der Phasenzusammensetzung ergab, dass die Umsetzungsrate von Tricalciumphosphat und Trimagnesiumphosphat zu den gewünschten Phasen Bruschit und Struvit infolge des Nachhärtungsprozesses signifikant gesteigert werden konnte. Im Zuge dessen nahm die Porosität der gedruckten Matrices der Phase Struvit von 58 % auf 26 % und der Phase Bruschit von 47 % auf 38 % ab.
Ziel dieser Arbeit war die Etablierung einer Prozesskette zur Herstellung anatomischer PSI aus CaPC im 3D-Pulverdruck-Verfahren. Der Modellversuch sollte die klinische Anwendung des Verfahrens simulieren und gegenüber alternativen Verfahren einordnen. Weiterhin sollten wichtige Parameter der DCP erhoben werden, um deren Eignung als KEM für PSI darzulegen.
Vier Defekte eines Kadaverschädels dienten der Prüfung der Prozesskette in Hinsicht auf Präzision und Praktikabilität des Verfahrens. Grundlage der Prozesskette waren dreidimensionale CT-Datensätze der Defektsituationen, welche eine computergestützte Rekonstruktion erlaubten. Eine eigens programmierte CAD-Software berechnete die virtuellen Entwürfe der individuellen Defektdeckungen anhand kontralateraler Strukturen. Abschließend wurden die PSI im 3D-Pulverdruck-Verfahren hergestellt und am Kadaverschädel bewertet. Zur Bewertung der DCP als geeignete KEM wurden mechanische, strukturelle und thermische Eigenschaften mit gängigen experimentellen Verfahren bestimmt. Die ermittelten Druck- und Biegefestigkeiten zeigten gute Ergebnisse für nicht bis gering lasttragende Bereiche, wie sie am Gesichts- und Hirnschädel vorliegen. Ebenso konnte die stabile Integration der Implantate durch osteosynthetische Fixierung im Schraubenausreißversuch nachgewiesen werden. Vorangegangene Untersuchungen zum klinischen Verhalten der Materialien konnten gute osteokonduktive Eigenschaften herausstellen und machen diese zu einer potentiellen Alternative zum autologen Transplantat.
Die etablierte Prozesskette zeigte eine gute Praktikabilität und Wirtschaftlichkeit im Umgang mit DCPD / DCPA. Alle Modelldefekte konnten mit PSI rekonstruiert werden. Diese zeigten eine gute Passung in der Defektregion und eine gute äußere Kontur. Für eine tatsächliche klinische Anwendung 3D-pulvergedruckter CaPC-Implantate wird eine Validierung und schließlich Zertifizierung der gesamten Prozesskette einschließlich der Herstellung der Reaktanden erforderlich. Um das Verhalten der Implantate im menschlichen Organismus bewerten zu können, wäre zunächst der Einsatz als temporäres Implantat (z. B. als Platzhalter nach Unterkieferresektion vor definitiver autologer Rekonstruktion) als sinnvolle Erstanwendung denkbar.
Additive Fertigung – oftmals plakativ „3D-Druck“ genannt – bezeichnet eine Fertigungstechnologie, die die Herstellung physischer Gegenstände auf Basis digitaler, dreidimensionaler Modelle ermöglicht. Das grundlegende Funktionsprinzip und die Gemeinsamkeit aller additiven bzw. generativen Fertigungsverfahren ist die schichtweise Erzeugung des Objekts. Zu den wesentlichen Vorteilen der Technologie gehört die Designfreiheit, die die Integration komplexer Geometrien erlaubt.
Aufgrund der zunehmenden Verfügbarkeit kostengünstiger Geräte für den Heimgebrauch und der wachsenden Marktpräsenz von Druckdienstleistern steht die Technologie erstmals Endkunden in einer Art und Weise zur Verfügung wie es vormals, aufgrund hoher Kosten, lediglich großen Konzernen vorbehalten war. Infolgedessen ist die additive Fertigung vermehrt in den Fokus der breiten Öffentlichkeit geraten. Jedoch haben sich Wissenschaft und Forschung bisher vor allem mit Verfahrens- und Materialfragen befasst. Insbesondere Fragestellungen zu wirtschaftlichen und gesellschaftlichen Auswirkungen haben hingegen kaum Beachtung gefunden. Aus diesem Grund untersucht die vorliegende Dissertation die vielfältigen Implikationen und Auswirkungen der Technologie.
Zunächst werden Grundlagen der Fertigungstechnologie erläutert, die für das Verständnis der Arbeit eine zentrale Rolle spielen. Neben dem elementaren Funktionsprinzip der Technologie werden relevante Begrifflichkeiten aus dem Kontext der additiven Fertigung vorgestellt und zueinander in Beziehung gesetzt.
Im weiteren Verlauf werden dann Entwicklung und Akteure der Wertschöpfungskette der additiven Fertigung skizziert. Anschließend werden diverse Geschäftsmodelle im Kontext der additiven Fertigung systematisch visualisiert und erläutert. Ein weiterer wichtiger Aspekt sind die zu erwartenden wirtschaftlichen Potentiale, die sich aus einer Reihe technischer Charakteristika ableiten lassen. Festgehalten werden kann, dass der Gestaltungsspielraum von Fertigungssystemen hinsichtlich Komplexität, Effizienzsteigerung und Variantenvielfalt erweitert wird. Die gewonnenen Erkenntnisse werden außerdem genutzt, um zwei Vertreter der Branche exemplarisch mithilfe von Fallstudien zu analysieren.
Eines der untersuchten Fallbeispiele ist die populäre Online-Plattform und -Community Thingiverse, die das Veröffentlichen, Teilen und Remixen einer Vielzahl von druckbaren digitalen 3D-Modellen ermöglicht. Das Remixen, ursprünglich bekannt aus der Musikwelt, wird im Zuge des Aufkommens offener Online-Plattformen heute beim Entwurf beliebiger physischer Dinge eingesetzt. Trotz der unverkennbaren Bedeutung sowohl für die Quantität als auch für die Qualität der Innovationen auf diesen Plattformen, ist über den Prozess des Remixens und die Faktoren, die diese beeinflussen, wenig bekannt. Aus diesem Grund werden die Remix-Aktivitäten der Plattform explorativ analysiert. Auf Grundlage der Ergebnisse der Untersuchung werden fünf Thesen sowie praxisbezogene Empfehlungen bzw. Implikationen formuliert. Im Vordergrund der Analyse stehen die Rolle von Remixen in Design-Communities, verschiedene Muster im Prozess des Remixens, Funktionalitäten der Plattform, die das Remixen fördern und das Profil der remixenden Nutzerschaft.
Aufgrund enttäuschter Erwartungen an den 3D-Druck im Heimgebrauch wurde dieser demokratischen Form der Produktion kaum Beachtung geschenkt. Richtet man den Fokus jedoch nicht auf die Technik, sondern die Hobbyisten selbst, lassen sich neue Einblicke in die zugrunde liegenden Innovationsprozesse gewinnen. Die Ergebnisse einer qualitativen Studie mit über 75 Designern zeigen unter anderem, dass Designer das Konzept des Remixens bereits verinnerlicht haben und dieses über die Plattform hinaus in verschiedenen Kontexten einsetzen. Ein weiterer Beitrag, der die bisherige Theorie zu Innovationsprozessen erweitert, ist die Identifikation und Beschreibung von sechs unterschiedlichen Remix-Prozessen, die sich anhand der Merkmale Fähigkeiten, Auslöser und Motivation unterscheiden lassen.
The aim of the work was the development of thiol-ene cross-linked hydrogels based on functionalized poly(glycidol)s (PG) and hyaluronic acid (HA) for extrusion based 3D bioprinting. Additionally, the functionalization of the synthesized PG with peptides and the suitability of these polymers for physically cross-linked gels were investigated, in a proof of principle study in order to demonstrate the versatile use of PG polymers in hydrogel development.
First, the precursor polymers of the different hydrogel systems were synthesized. For thiol-ene cross-linked hydogels, linear allyl-functionalized PG (P(AGE-co-G)) and three different thiol-(SH-)functionalized polymers, ester-containing PG-SH (PG SHec), ester-free PG-SH (PG-SHef) and HA-SH were synthesized and analysed, The degree of functionalization of these polymers was adjustable.
For physically cross-linked hydrogels, peptide-functionalized PG (P(peptide-co-G)), was synthesized through polymer analogue thiol-ene modification of P(AGE-co-G).
Subsequently, thiol-ene cross-linked hydrogels were prepared with the synthesized thiol- and allyl-functionalized polymers. Depending on the origin of the used polymers, two different systems were obtained: on the one hand synthetic hydrogels consisting of PG-SHec/ef and P(AGE-co-G) and on the other hand hybrid gels, consisting of HA-SH and P(AGE-co-G). In synthetic gels, the degradability of the gels was determined by the applied PG-SH. The use of PG-SHec resulted in hydrolytically degradable hydrogels, whereas the cross-linking with PG-SHef resulted in non-degradable gels.
The physical properties of these different hydrogel systems were determined by swelling, mechanical and diffusion studies and subsequently compared among each other. In swelling studies the differences of degradable and non-degradable synthetic hydrogels as well as the differences of synthetic compared to hybrid hydrogels were demonstrated.
Next, the stiffness and the swelling ratios (SR) of the established hydrogel systems were examined in dependency of different parameters, such as incubation time, polymer concentration and UV irradiation. In general, these measurements revealed the same trends for synthetic and hybrid hydrogels: an increased polymer concentration as well as prolonged UV irradiation led to an increased network density. Moreover, it was demonstrated that the incorporation of additional non-bound HMW HA hampered the hydrogel cross-linking resulting in gels with decreased stiffness and increased SR. This effect was strongly dependent on the amount of additional HMW HA.
The diffusion of different molecular weight fluorescein isothiocyanate-dextran (FITC-dextran) through hybrid hydrogels (with/without HMW HA) gave information about the mesh size of these gels. The smallest FITC-dextran (4 kDa) completely diffused through both hydrogel systems within the first week, whereas only 55 % of 40 kDa and 5-10 % HMW FITC-dextrans (500 kDa and 2 MDa) could diffuse through the networks.
The applicability of synthetic and hybrid hydrogels for cartilage regeneration purpose was investigated through by biological examinations. It was proven that both gels support the survival of embedded human mesenchymal stromal cells (hMSCs) (21/28 d in vitro culture), however, the chondrogenic differentiation was significantly improved in hybrid hydrogels compared to synthetic gels. The addition of non-bound HMW HA resulted in a slightly less distinct chondrogenesis.
Lastly the printability of the established hydrogel systems was examined. Therefore, the viscoelastic properties of the hydrogel solutions were adjusted by incorporation of non-bound HMW HA. Both systems could be successfully printed with high resolution and high shape fidelity.
The introduction of the double printing approach with reinforcing PCL allowed printing of hydrogel solutions with lower viscosities. As a consequence, the amount of additional HMW HA necessary for printing could be reduced allowing successful printing of hybrid hydrogel solutions with embedded cells. It was demonstrated that the integrated cells survived the printing process with high viability measured after 21 d. Moreover, by this reinforcing technique, robust hydrogel-containing constructs were fabricated.
In addition to thiol-ene cross-linked hydrogels, hydrogel cross-linking via ionic interactions was investigated with a hybrid hydrogel based on HMW HA and peptide-functionalized PG. Rheological measurements revealed an increase in the viscosity of a 2 wt.% HMW HA solution by the addition of peptide-functionalized PG. The increase in viscosity could be attributed to the ionic interactions between the positively charge PG and the negatively charge HMW HA.
In conclusion, throughout this thesis thiol-ene chemistry and PG were introduced as promising cross-linking reaction and polymer precursor for the field of biofabrication. Furthermore, the differences of hybrid and synthetic hydrogels as well as chemically and physically cross-linked hydrogels were demonstrated.
Moreover, the double printing approach was demonstrated to be a promising tool for the fabrication of robust hydrogel-containing constructs. It opens the possibility of printing hydrogels that were not printable yet, due to too low viscosities.
Biofabrication is an advancing new research field that might, one day, lead to complex products like tissue replacements or tissue analogues for drug testing. Although great progress was made during the last years, there are still major hurdles like new types of materials and advanced processing techniques. The main focus of this thesis was to help overcoming this hurdles by challenging and improving existing fabrication processes like extrusion-based bioprinting but also by developing new techniques. Furthermore, this thesis assisted in designing and processing materials from novel building blocks like recombinant spider silk proteins or inks loaded with charged nanoparticles.
A novel 3D printing technique called Melt Electrospinning Writing (MEW) was used in Chapter 3 to create tubular constructs from thin polymer fibers (roughly 12 μm in diameter) by collecting the fibers onto rotating and translating cylinders. The main focus was put on the influence of the collector diameter and its rotation and translation on the morphology of the constructs generated by this approach. In a first step, the collector was not moving and the pattern generated by these settings was analyzed. It could be shown that the diameter of the stationary collectors had a big impact on the morphology of the constructs. The bigger the diameter of the mandrel (smallest collector diameters 0.5 mm, biggest 4.8 mm) got, the more the shape of the generated footprint converged into a circular one known from flat collectors. In a second set of experiments the mandrels were only rotated. Increasing the rotational velocity from 4.2 to 42.0 rpm transformed the morphology of the constructs from a figure-of-eight pattern to a sinusoidal and ultimately to a straight fiber morphology. It was possible to prove that the transformation of the pattern was comparable to what was known from increasing the speed using flat collectors and that at a critical speed, the so called critical translation speed, straight fibers would appear that were precisely stacking on top of each other. By combining rotation and translation of the mandrel, it was possible to print tubular constructs with defined winding angles. Using collections speeds close to the critical translation speed enabled higher control of fiber positioning and it was possible to generate precisely stacked constructs with winding angles between 5 and 60°.
In Chapter 4 a different approach was followed. It was based on extrusion-based bioprinting in combination with a hydrogel ink system. The ink was loaded with nanoparticles and the nanoparticle release was analyzed. In other words, two systems, a printable polyglycidol/hyaluronic acid ink and mesoporous silica nanoparticles (MSN), were combined to analyze charge driven release mechanism that could be fine-tuned using bioprinting. Thorough rheological evaluations proved that the charged nanoparticles, both negatively charged MSN-COOH and positively charged MSN-NH2, did not alter the shear thinning properties of the ink that revealed a negative base charge due to hyaluronic acid as one of its main components. Furthermore, it could be shown that the particles did also not have a negative effect on the recovery properties of the material after exposure to high shear. During printing, the observations made via rheological testing were supported by the fact that all materials could be printed at the same settings of the bioprinter. Using theses inks, it was possible to make constructs as big as 12x12x3 mm3 composed of 16 layers. The fiber diameters produced were about 627±31 μm and two-component constructs could be realized utilizing the two hydrogel print heads of the printer to fabricate one hybrid construct. The particle distribution within those constructs was homogeneous, both from a microscopic and a macroscopic point of view. Particle release from printed constructs was tracked over 6 weeks and revealed that the print geometry had an influence on the particle release. Printed in a geometry with direct contact between the strands containing different MSN, the positively charged particles quickly migrated into the strand previously containing only negatively charged MSN-COOH. The MSN-COOH seemed to be rather released into the surrounding liquid and also after 6 weeks no MSN-COOH signal could be detected in the strand previously only containing MSN-NH2. In case of a geometry without direct contact between the strands, the migration of the positively charged nanoparticles into the MSN-COOH containing strand was strongly delayed. This proved that the architecture of the printed construct can be used to fine-tune the particle release from nanoparticle containing printable hydrogel ink systems.
Chapter 5 discusses an approach using hydrogel inks based on recombinant spider silk proteins processed via extrusion-based bioprinting. The ink could be applied for printing at protein concentrations of 3 % w/v without the addition of thickeners or any post process crosslinking. Both, the recombinant protein eADF4(C16) and a modification introducing a RGD-sequence to the protein (eADF4(C16)-RGD), could be printed revealing a very good print fidelity. The RGD modification had positive effect on the adhesion of cells seeded onto printed constructs. Furthermore, human fibroblasts encapsulated in the ink at concentrations of 1.2 million cells per mL did not alter the print fidelity and did not interfere with the crosslinking mechanism of the ink. This enabled printing cell laden constructs with a cell survival rate of 70.1±7.6 %. Although the cell survival rate needs to be improved in further trials, the approach shown is one of the first leading towards the shift of the window of biofabrication because it is based on a new material that does not need potentially harmful post-process crosslinking and allows the direct encapsulation of cells staying viable throughout the print process.
Motivated by the great potential which is offered by the combination of additive manufacturing and tissue engineering, a novel polymeric bioink platform based on poly(2 oxazoline)s was developed which might help to further advance the young and upcoming field of biofabrication. In the present thesis, the synthesis as well as the characteristics of several diblock copolymers consisting of POx and POzi have been investigated with a special focus on their suitability as bioinks.
In general, the copolymerization of 2-oxazolines and 2-oxazines bearing different alkyl side chains was demonstrated to yield polymers in good agreement with the degree of polymerization aimed for and moderate to low dispersities.
For every diblock copolymer synthesized during the present study, a more or less pronounced dependency of the dynamic viscosity on temperature could be demonstrated. Diblock copolymers comprising a hydrophilic PMeOx block and a thermoresponsive PnPrOzi block showed temperature induced gelation above a degree of polymerization of 50 and a polymer concentration of 20 wt%. Such a behavior has never been described before for copolymers solely consisting of poly(cyclic imino ether)s.
Physically cross linked hydrogels based on POx b POzi copolymers exhibit reverse thermal gelation properties like described for solutions of PNiPAAm and Pluronic F127. However, by applying SANS, DLS, and SLS it could be demonstrated that the underlying gel formation mechanism is different for POx b POzi based hydrogels. It appears that polymersomes with low polydispersity are formed already at very low polymer concentrations of 6 mg/L. Increasing the polymer concentration resulted in the formation of a bicontinuous sponge like structure which might be formed due to the merger of several vesicles. For longer polymer chains a phase transition into a gyroid structure was postulated and corresponds well with the observed rheological data.
Stable hydrogels with an unusually high mechanical strength (G’ ~ 4 kPa) have been formed above TGel which could be adjusted over a range of 20 °C by changing the degree of polymerization if maintaining the symmetric polymer architecture. Variations of the chain ends revealed only a minor influence on TGel whereas the influence of the solvent should not be neglected as shown by a comparison of cell culture medium and MilliQ water.
Rotationally as well as oscillatory rheological measurements revealed a high suitability for printing as POx b POzi based hydrogels exhibit strong shear thinning behavior in combination with outstanding recovery properties after high shear stress.
Cell viability assays (WST-1) of PMeOx b PnPrOzi copolymers against NIH 3T3 fibroblasts and HaCat cells indicated that the polymers were well tolerated by the cells as no dose-dependent cytotoxicity could be observed after 24 h at non-gelling concentrations up to 100 g/L.
In summary, copolymers consisting of POx and POzi significantly increased the accessible range of properties of POx based materials. In particular thermogelation of aqueous solutions of diblock copolymers comprising PMeOx and PnPrOzi was never described before for any copolymer consisting solely of POx or POzi. In combination with other characteristics, e.g. very good cytocompatibility at high polymer concentrations and comparably high mechanical strength, the formed hydrogels could be successfully used for 3D bioprinting. Although the results appear promising and the developed hydrogel is a serious bioink candidate, competition is tough and it remains an open question which system or systems will be used in the future.
Der 3D-Druck ist ein elementarer Bestandteil der Biofabrikation. Beispielsweise wird mittels Biotinten und einem geeigneten 3D-Druckverfahren Schicht für Schicht eine Geometrie aufgebaut. Durch die Gestaltung von mikrofluidischen Druckköpfen wird eine Möglichkeit geschaffen multiple Materialansätze im Druckkopf zu vermischen und so in einem bestimmten Mischungsverhältnis zu drucken.
Mit dem DLP-SLA-Drucker Vida HD Crown and Bridge (EnvisionTEC) und dem Harz E-Shell 600 (EnvisionTEC) wurden zunächst die Auflösungsgrenzen des Druckers ermittelt sowie Komponenten für die Realisierung eines mikrofluidischen Druckkopfes prozessiert.
Bei den Komponenten handelt es sich zum einen um Geometrien, die beispielsweise als Mischeinheit im Kanal dienen können und des Weiteren um senkrechte Kanäle die Biotinten führen können, sowie um Kanäle, die als Zuläufe für den Hauptkanal des mikrofluidischen Druckkopfs dienen können.
Die Eigenschaften und die technische Realisierbarkeit der gedruckten Objekte wurden eruiert.
Dabei wurden die jeweiligen Geometrien und Kanalöffnungen vermessen, große Aspektverhältnisse der Geometrien untersucht und die Durchgängigkeit der Kanäle geprüft.
Zukünftig können die prozessierten Komponenten für einen mikrofluidischen Druckkopf variabel kombiniert werden und auf dieser Basis weiterführende Experimente stattfinden.
Ziel der Untersuchung:
Verglichen wurden die räumlichen Abweichungen der Bohrpfade nach virtueller Planung von Schablonen geführten Trepanationen mit Hilfe der Softwaresysteme SicatEndo (SE) und coDiagnostiX (CDX) und der benötigte Arbeitsaufwand.
Material und Methode:
Basierend auf µCT-Datensätzen von humanen obliterierten Frontzähnen wurden identische Kunststoffzähne und acht Zahnmodelle (4 Ober-, 4 Unterkiefer) hergestellt. Es wurde jeweils ein DVT und ein Oberflächenscan angefertigt. Diese Datensätze (DICOM; STL) wurden in die Softwaresysteme importiert und fusioniert. Anschließend wurden die Bohrpfade für je 16 Probenzähne pro Software geplant. Mit Hilfe der erstellten Schablonen wurden alle Trepanationen an den im Phantomkopf fixierten Modellen von einem Behandler durchgeführt. Nach Erschließung des apikalen Wurzelkanalanteils wurde ein DVT angefertigt und mit dem präoperativen DVT überlagert. Die räumliche drei-dimensionale (3D) Abweichung zwischen virtuell geplantem und tatsächlichem Bohrpfad wurde über die Vektorlänge bestimmt und der Arbeitsaufwand anhand der Planungszeit und der Anzahl der Mausklicks pro Kiefer erfasst.
Ergebnisse:
Für die Trepanationen mit SE zeigten sich signifikant geringe Abweichungen an der Bohrerspitze vestibulär-oral [CDX 0,54mm ± 0,32mm; SE 0,12mm ± 0,11mm; p < 0.05], 3D [CDX 0,74mm ± 0,26 mm; SE 0,35mm ± 0,17mm; p < 0.05] und hinsichtlich des Winkels [CDX 1,57° ± 0,76°; SE 0,68° ± 0,41°; p < 0.05] als mit CDX. Für CDX war der Planungsaufwand signifikant geringer als für SE hinsichtlich Planungszeit [CDX Ø 10min 50sec; SE Ø 20min 28sec] und hinsichtlich der Anzahl der Klicks pro Kiefer [CDX Ø 107; SE Ø 341].
Zusammenfassung:
Beide Planungssysteme ermöglichen ausreichend präzise Schablonen geführte Bohrungen zur Erschließung apikaler Wurzelkanalanteile.
The aim of this thesis was the preparation of a biomaterial ink for the fabrication of chemically crosslinked hydrogel scaffolds with low micron sized features using melt electrowriting (MEW). By developing a functional polymeric material based on 2-alkyl-2-oxazine (Ozi) and 2-alkyl-2-oxazoline (Ox) homo- and copolymers in combination with Diels-Alder (DA)-based dynamic covalent chemistry, it was possible to achieve this goal. This marks an important step for the additive manufacturing technique melt electrowriting (MEW), as soft and hydrophilic structures become available for the first time. The use of dynamic covalent chemistry is a very elegant and efficient method for consolidating covalent crosslinking with melt processing. It was shown that the high chemical versatility of the Ox and Ozi chemistry offers great potential to control the processing parameters. The established platform offers straight forward potential for modification with biological cues and fluorescent markers. This is essential for advanced biological applications. The physical properties of the material are readily controlled and the potential for 4D-printing was highlighted as well. The developed hydrogel architectures are excellent candidates for 3D cell culture applications. In particular, the low internal strength of some of the scaffolds in combination with the tendency of such constructs to collapse into thin strings could be interesting for the cultivation of muscle or nerve cells. In this context it was also possible to show that MEW printed hydrogel scaffolds can withstand the aspiration and ejection through a cannula. This allows the application as scaffolds for the minimally invasive delivery of implants or functional tissue equivalent structures to various locations in the human body.
Ziel dieser Arbeit war die Entwicklung und Charakterisierung vorgemischter Calciumphosphatzementpasten sowie die Übertragung des Konzepts dieser Pasten auf den 3D-Druck. Es wurden drei verschiedene Zementformulierungen untersucht, basierend auf Pulvermischungen aus α-TCP/DCPA/CaCO3 (Biozement D), TTCP/DCPA und β-TCP/MCPA, die auf verschiedene Materialeigenschaften geprüft und einem 3D-Druckversuch unterzogen wurden. Die Biozement D Paste wurde mit drei Pulver-Flüssigkeits-Verhältnissen (PLR) (80/20, 85/15, 87/13), die TTCP/DCPA Paste mit zwei PLR (83/17, 85/15), und die β-TCP/MCPA Paste ebenfalls mit zwei PLR (67/33, 70/30) getestet. Alle Pasten konnten mit dem 3D-Drucker erfolgreich verdruckt werden. Die Biozement D Paste mit dem PLR 85/15 stellte sich in ihrer Gruppe als die geeignetste Paste heraus. Bessere Ergebnisse bezüglich der Injizierbarkeit und Druckbarkeit erreichte die TTCP/DCPA Paste. Hier wurden mit beiden PLR formstabile Scaffolds erzielt. Feine Wabenmuster konnten mit dem PLR von 83/17 in Kombination mit einer hohen Druckgeschwindigkeit hergestellt werden. Mit dem höheren PLR (85/15) und einer niedrigeren Druckgeschwindigkeit stieg die Formstabilität weiter an, wodurch die hexagonale Struktur exakter gedruckt werden konnte. Ein gutes Druckergebnis konnte auch mit der β-TCP/MCPA Paste und dem PLR 70/30 erreicht werden.