In this work the influence of “active” bridge units on the electron transfer (ET) mechanism within organic donor-bridge-electrode arrays in self-assembled monolayers (SAMs) was studied by spectroscopic and electrochemical methods. In the first part of this work ferrocenealkanethiols 1 – 3 and the ferrocenearylthiols 4, 5 were investigated to get experience in the monolayer preparation for measuring ET rates. Cyclic voltammetry of the monolayers indicates that homogeneously mixed monolayers containing redox active molecules and dummy molecules were formed. For the known ferrocenealkanethiols 1 – 3 the ET rates could be confirmed compared to the ones measured by Creager et al. [206]. As expected the ET rate decreases by increasing chain length of the alkane spacer from 2 to 3. Changing the bonding between the redox centre and the alkane spacer with the same bridge lenght, e. g. by using a carboxy-group in case of 1, does not influence the ET behaviour very strong. The aromatic ferrocenethiols 4 and 5 show very high ET rates due to the strong conjugated system although the distance between the redox centre and the electrode is comparable to the C8-alkyl compound 2. The electronic coupling factors all indicate a nonadiabatic ET between the redox centre and the electrode. As expected the electronic coupling factors increase with decreasing spacer length or with an enlarged conjugated system. To sum up, experience in monolayer preparation could be obtained, the measured ET rates for well known ferrocenealkane-compounds 1 - 3 could be verified and the information could be transferred to the conjugated systems 4 and 5. In the second part the triarylamine- 29, 32 and the phenothiazinealkanethiol 35 have been examined relative to their ET behaviour in mixed monolayers. The cyclic voltammograms of the diluted monolayers indicate that homogeneously formed monolayers are present. The ET rates of triarylamine- 29, 32 and phenothiazinealkanethiols 35 are 10 to 100 times higher than compared to ferrocenealkanethiols with equal chain length[183, 206], whereas in a [Ru(bpy)2(pp)]+-containing monolayer the same value was observed [177]. Almost two parameters influence the ET rate constant: the electronic coupling matrix element and the reorganisation energy  [209]. The ET rate in donor substituted alkanethiols is mainly influenced by the reorganisation energy  [177] and even small changes have a dramatic effect on the observed processes, therefore an increasing ET rate from the ferrocene (high reorganisation energy) over the phenothiazine 35 and the [Ru(bpy)2(pp)]+ to the triarylamine chromophores 29 and 32 (low reorganisation energy) is observed. Furthermore the bonding between the redox centres and the alkane spacer plays an important role on the ET rate in case of the triarylamines 29 and 32 opposite to the assumption made by Creager et al. that the connection does not play any role. For the electron rich ether connected compound 29 the ET is not only dominated by the reorganisation energy but also by mesomeric effects where the positive charge of the electron rich derivative 29 is more located at the ether function so that the chain is formally shortend by one atom resulting in higher ET rates than compared to 32. In the third part of the thesis a series of “molecular wires” consisting of methoxy- or chloro-substituted triarylamines and phenothiazines with different bridge units and bridge length between the redox centre and the anchor thiol function have been prepared in order to investigate their ET-behaviour. Cyclic voltammetry and UV/vis-spectroscopy show that the oxidation potential and the energetic states could be controlled very well by introducing different redox centres and bridge units resulting in a decreasing oxidation potential of the redox centres and a bathochromic shift of the absorption bands in the UV/vis-spectra. Also the densitiy of the chromophores in mixed monolayers could be controlled very well for only three compounds (49, 52 and 87) with nitrile-substituted bridges reliable ET rates could be obtained. In these chromophores the ET rate decreases by increasing the density of the redox active molecules in the mixed monolayers indicating that the adsorption geometry changes with coverage with the chromophores tilting to a more upright orientation as the surface becomes more crowded. For all other compounds the measurements were limited by the fast ET rates. Conformational, as well as a very weak distance dependence of the ET resulting in very high ET rates [172] or unfavourable HOMO-LUMO energies of the donor, bridge and the electrode are reasons for this behaviour. The fact that compound 49 shows almost the same rate constant independent of the length (n = 2 or n = 3) may indicate that a hopping process is operating for which a much weaker length dependence is expected than in the case of a superexchange.
As a traditional industrial pigment, perylene bisimide (PBI) dyes have found wide-spread applications. In addition, PBI dyes have been considered as versatile and promising functional materials for organic-based electronic and optic devices, such as transistors and solar cells. For these novel demands, the control of self-organization of this type of dye and the investigation of the relationship between the supramolecular structure and the relevant optical and electronic properties is of great importance. The objective of this thesis focuses on gaining a better understanding of structural and functional properties of pi-stacks based on self-assembling PBIs. Studies include the synthesis and characterization of new functional PBI dyes, their aggregation in solution, in liquid crystalline state and on surfaces, and their fluorescence and charge transport properties. An overview of the formation, thermodynamics and structures of pi-stacks of functional pi- conjugated molecules in solution and in liquid crystalline phases is given in Chapter 2. Chapters 3 and 4 deal with the pi-pi aggregates of new, highly fluorescent PBIs without core-substituents. In Chapter 3, the self-assembly of a PBI with tridodecylphenyl substituents at imide N atoms both in solution and condensed phase has been studied in great detail. In condensed state, the dye exhibits a hexagonal columnar liquid crystalline (LC) phase as confirmed by DSC, OPM and X-ray diffraction analysis. The columnar stacking of this dye has been further confirmed by atomic force microscopy (AFM) where single columns could be well resolved The charge transport properties this dye have been investigated by pulse radiolysis-time resolved microwave conductivity (PR-TRMC) measurements. To shed more light on the nature of the pi-pi interaction of the unsubstituted PBIs, solvent depend aggregation properties have been investigated in Chapter 4. The studies are further extended from core-unsubstituted PBIs to core-substituted ones (Chapter 5 and 6). In Chapter 5, a series of highly soluble and fluorescent core-twisted PBIs that bear the same trialkylphenyl groups at the imide positions but different bay-substituents and were synthesized. These compounds are characterized by distortions of the perylene planes with dihedral angles in the range of 15-37° according to crystallographic data and molecular modeling studies. In contrast to the extended oligomeric aggregates formed for planar unsubstituted PBIs, this family of dyes formed discrete pi-pi-stacked dimers in apolar methylcyclohexane as concentration-dependent UV/Vis measurements and VPO analysis revealed. The Gibbs free energy of dimerization can be correlated with the twist angles of the dyes linearly. In condensed state, several of these PBIs form luminescent rectangular or hexagonal columnar liquid crystalline phases with low isotropization temperatures. The core-twisting effect on semiconducting properties has been examined in Chapter 6. In this chapter, a comparative study of the electrochemical and the charge transport properties of a series of non-substituted and chlorine-functionalized PBIs was performed. While Chapters 3-6 focus on one-component dye systems, Chapter 7 explored the possibility of a supramolecular engineering of co-aggregates formed by hydrogen-bonded 2:1 and 1:1 complex of oligo(p-phenylene vinylene)s (OPVs) and PBIs. Covalently linked donor-acceptor dye arrays have been prepared for comparison. Concentration and temperature-dependent UV/Vis spectroscopy revealed all hydrogen-bonded and covalent systems form well-ordered J-type aggregates in methylcyclohexane. With these hydrogen-bonded OPV-PBI complexes, fibers containing p-type and n-type molecules can be prepared on the nano-scale (1-20 nm). For the 2:1 OPV-PBI hydrogenbonded arrays hierarchically assembled chiral superstructures consisting of left-handed helical pi-pi co-aggregates (CD spectroscopy) of the two dyes that further assemble into right-handed nanometer-scale supercoils in the solid state (AFM study) have been observed. All of these well-defined OPV-PBI assemblies presented here exhibit photoinduced electron transfer on sub-ps timescale, while the electron recombination differs for different systems.Thus, it was suggested that such assemblies of p- and n-type semiconductors might serve as valuable nanoscopic functional units for organic electronics.
Die vorliegende Arbeit beschäftigt sich mit den strukturellen Aspekten einer adsorbat-induzierten Facettierung von vizinalen Ag(111)-Oberflächen. Bei dem Adsorbat handelte es sich um das organische Molekül Perylen-3,4,9,10-Tetracarbonsäure-Dianhydrid (PTCDA). Die Experimente wurden unter Ultrahochvakuum-Bedingungen durchgeführt, die Charakterisierung erfolgte hauptsächlich mit den Messmethoden Rastertunnelmikroskopie (STM) und niederenergetische Elektronenbeugung (LEED). Das planare Farbstoffmolekül PTCDA adsorbiert präferentiell an den Stufenkanten der verwendeten 8.5° Ag(111)-Vizinaloberflächen und induziert bei geeigneten Präparationsbedingungen eine Rekonstruktion in stark gestufte Facettenflächen und in stufenfreie (111)-Terrassen. Die beobachteten Facetten sind für das System PTCDA/Ag charakteristisch und stellen durch eine molekulare Überstruktur richtungsselektiv stabilisierte Ag-Kristallebenen dar. Durch die Variation der Stufenrichtung der Startoberfläche wurde eine Vielzahl von Facettentypen erhalten und nach Miller indiziert. In ihrer Gesamtheit erlauben sie einen Rückschluss auf das Aussehen der Gleichgewichtskristallform eines mit PTCDA bedeckten Ag-Kristalles und damit auf das richtungsabhängige Benetzungsverhalten von Ag. Aus der Sicht des Substrates bewirkt das Adsorbat eine massive Erhöhung der Steifheit der Stufen. Die durch eine molekulare Überstruktur stabilisierten Facettenflächen übernehmen die in der Kristallstruktur des Substrates angelegten Stufenrichtungen. Die gefundene Ausbildung von zwei typischen Facettensteigungen ist jedoch nicht durch die Ag-Kristallstruktur motivierbar. Die Facettierung wurde im Rahmen einer speziellen Adaption des Konzepts der Thermodynamik auf ebene gestufte Oberflächen als Orientierungsphasenseparation beschrieben. Dieses Konzept erlaubt eine korrekte Beschreibung der beobachteten lokalen Phänomene und zeigt zudem auf, dass das molekulare Gas, welches in den Messungen nicht erfasst wurde, eine wichtige Rolle bei der Rekonstruktion spielt. Es ergaben sich wichtige Indizien für die Existenz einer kritischen Inselgröße für PTCDA auf Ag(111). Es wurde eine vollständige strukturelle Analyse aller stabilen molekularen Überstrukturen auf vizinalen Ag(111)-Oberflächen durchgeführt. Es wurden insgesamt 16 solcher Überstrukturen gefunden, von denen bisher nur 3 Strukturen bekannt und veröffentlicht waren. Dichte und Kommensurabilität der Facettenüberstrukturen sind systematisch vom Stufentyp der Oberfläche abhängig. Die Frage nach dem Ursprung der beiden charakteristischen Facettensteigungen ist mit der Existenz von zwei Typen von Überstrukturgrenzen verknüpft. Die Grenze bestimmt die Lage der fischgrätartigen Überstruktur zu den Stufenkanten und die Länge und die Breite des Moleküls die beiden charakteristischen Stufenabstände. Letzteres geschieht vermöge einer lokalen Wechselwirkung der PTCDA-Moleküle mit den Stufen. Die Überstrukturgrenzen erweisen sich als wichtiges Element der Rekonstruktion. Es wurden außerdem die Abhängigkeiten der verschiedenen, aneinander angrenzenden Überstrukturen aufgezeigt. Auf den (111)-Terrassen fanden sich 3 metastabile Ausnahme-Strukturen, welche einen vertieften Einblick in die komplexe Bildungskinetik der bisher bekannten stabilen (111)-Struktur erlauben. Die Facetten bilden zusammen mit den benachbarten (111)-Terrassen regelmäßige, einem Reflexionsgitter ähnliche Muster mit einer Strukturweite von 5 bis 75nm. Die beobachteten Strukturweiten erreichen bei ausgedehntem Tempern typische Maximalwerte. STM-Messungen zeigen den Einfluss einer langreichweitigen Wechselwirkung zwischen den Facetten, vermittelt über elastische Eigenschaften des Substrates. Die Muster können als selbstorganisierte Zweiphasensysteme im thermodynamischen Gleichgewicht erklärt werden. Die Facetten wirken wie repulsiv wechselwirkende Defekte in einem elastischen Medium. Die Eignung dieser Muster als Templat wurde in Kooperation mit einer anderen Arbeitsgruppe am Beispiel der selektiven Deposition von Eisen belegt.
Diese Arbeit beschäftigt sich mit der Selbstorganisation von Zinkchlorin-Farbstoffen, welche sich strukturell von Chlorophyllen ableiten. Im Gegensatz zu allen anderen bakteriellen und pflanzlichen Lichtsammelpigmenten ist es den Bakteriochlorophyllen c, d und e der Lichtsammelsysteme grüner phototropher Bakterien möglich, allein durch nichtkovalente Wechselwirkungen zwischen den Farbstoff-Molekülen, ohne die Beteiligung von Proteinen, röhrenförmige Antennensysteme auszubilden, welche die am dichtest gepackten und effizientesten Lichtsammelsysteme in der Natur darstellen. Um einen Betrag zur Aufklärung dieser biologisch wichtigen Aggregate zu leisten, wurden im ersten Teil dieser Arbeit Zinkchlorine als Modellverbindungen für BChl c hergestellt. Mit den neu synthetisierten Zinkchlorinen ist es gelungen, Modellsysteme der natürlichen BChl-Selbstorganisate herzustellen, welche sich im Gegensatz zu den bisher in der Literatur beschriebenen Zinkchlorin-Aggregaten durch eine gute und dauerhafte Löslichkeit auszeichnen. Diese Eigenschaft erlaubte es sowohl spektroskopische als auch mikroskopische Untersuchungen zur Aufklärung der Aggregatstruktur durchzuführen. Durch Rasterkraftmikroskopie an den Zinkchlorin Aggregaten konnte erstmals ein mikroskopischer Beweis der stabförmigen Struktur von Aggregaten dieser Substanzklasse erhalten werden. Der zweite Teil dieser Arbeit beschäftigt sich mit Zinkchlorinen, denen aufgrund einer methylierten 31-Hydroxy-Gruppe die Fähigkeit zur Röhrenbildung fehlt, die aber durch Koordinationsbindungen und p-p-Wechselwirkungen weiterhin Stapel bilden können. Temperaturabhängige UV/Vis- und CD-spektroskopische Studien offenbarten die reversible Bildung von löslichen, chiralen Zinkchlorin-Stapelaggregaten. Rasterkraft- und rastertunnelmikroskopische Untersuchungen zeigen die Bildung von zwei Typen p-gestapelter Aggregate auf hoch geordnetem Graphit.
Albeit of high technological import, epitaxial self-assembly of CdSe/ZnSe QDs is non-trivial and still not clearly understood. The origin and attributes of these QDs are significantly different from those of their III-V and group-IV counterparts. For III-V and group-IV heterosystems, QD-formation is assigned to the Stranski Krastanow (SK) transition, wherein elastic relaxation of misfit strain leads to the formation of coherent three-dimensional (3D) islands, from a supercritically strained two-dimensional (2D) epilayer. Unfortunately, this phenomenon is inconspicuous for the CdSe/ZnSe heterosystem. Well-defined 3D islands are not readily formed in conventional molecular beam epitaxial (MBE) growth of CdSe on ZnSe. Consequently, several alternative approaches have been adopted to induce/enhance formation of QDs. This thesis systematically investigates three such alternative approaches, along with conventional MBE, with emphasis on the formation-mechanism of QDs, and optimization of their morphological and optical attributes. It is shown here that no distinct 3D islands are formed in MBE growth of CdSe on ZnSe. The surface of the CdSe layer represents a rough 2D layer, characterized by a dense array of shallow (<1nm) abutting mounds. In capped samples, the CdSe deposit forms an inhomogeneous CdZnSe quantum well (QW)-like structure. This ternary QW consists of local Cd-rich inclusions, which confine excitons three-dimensionally, and act as QDs. The density of such QDs is very high (~ 1012 cm-2). The QDs defined by the composition inhomogeneities of the CdZnSe QW presumably originate from the shallow mounds of the uncapped CdSe surface. By a technique wherein a CdSe layer is grown at a low temperature (TG = 230 °C) and subsequently annealed at a significantly higher temperature (TA =310 °C), tiny but distinct 3D islands are formed. In this work, the mechanism underlying the formation of these islands is reported. While the CdSe deposit forms a quasi-two-dimensional (quasi-2D) layer at TG = 230 °C, subsequent annealing at TA = 310 °C results in a thermally activated “up-climb” of adatoms onto two-dimensional clusters (or precursors) and concomitant nucleation of 3D islands. The areal density of QDs, achieved by this technique, is at least a decade lower than that typical for conventional MBE growth. It is demonstrated that further reduction is possible by delaying the temperature ramp-up to TA. In the second technique, formation of distinct islands is demonstrated by deposition of amorphous selenium (a-Se) onto a 2D CdSe epilayer at room temperature and its subsequent desorption at a higher temperature (TD = 230 °C). Albeit the self-assembled islands are large, they are severely truncated during subsequent capping with ZnSe, presumably due to segregation of Cd and Zn-alloying of the islands. The segregation phenomenon is analyzed in this work and correlated to the optical properties of the QDs. Additionally, very distinct vertical correlation of QDs in QD-superlattices, wherein the first QD-layer is grown by this technique and the subsequent ones by migration enhanced epitaxy (MEE), is reported. The process steps of the third variant technique, developed in course of this work, are very similar to those of the previous one-the only alteration being the substitution of selenium with tellurium as the cap-forming-material. This leads not only to large alteration of the morphological and optical attributes of the QDs, but also to formation of unique self-assembled island-patterns. Oriented dashes, straight and buckled chains of islands, and aligned island-pairs are formed, depending on the thickness of the Te-cap layer. The islands are partially alloyed with Te and emit luminescence at very low energies (down to 1.7 eV at room temperature). The Te cap layer undergoes (poly)crystallization during temperature ramp-up (from room temperature to TD) for desorption. Here, it is shown that the self-assembled patterns of the island-ensembles are determined by the pattern of the grain boundaries of the polycrystalline Te layer. Based on an understanding of the mechanism of pattern formation, a simple and “clean” method for controlled positioning of individual QDs and QD-based extended nanostructures, is proposed in this work. The studies carried out in the framework of this thesis provide not only a deeper insight into the microscopic processes governing the heteroepitaxial self-assembly of CdSe/ZnSe(001) QDs, but also concrete approaches to achieve, optimize, and control several technologically-important features of QD-ensembles. Reduction and control of QD-areal-density, pronounced vertical correlation of distinctly-defined QDs in QD-superlattices, and self-assembly of QD-based extended structures, as demonstrated in this work, might turn out to be beneficial for envisioned applications in information-, and communication-technologies.
Artificial light-harvesting (LH) systems have been obtained by self-assembly of naphthalene diimide-functionalized zinc chlorin dyads and triad in nonpolar, aprotic solvents. UV-vis, CD, and steady-state emission spectroscopy as well as atomic force microscopy showed that rod-like structures are formed by excitonic interactions of zinc chlorin units, while the appended naphthalene diimide dyes do not aggregate at the periphery of the cylinders. In all cases, photoexcitation of the enveloping naphthalene diimides at 540 and 620 nm, respectively, was followed by highly efficient energy-transfer processes to the inner zinc chlorin backbone, as revealed by time-resolved fluorescence spectroscopy on the picosecond time-scale. As a consequence, the LH efficiencies of zinc chlorin rod aggregates were increased by up to 63%. The effective utilization of solar energy recommends these biomimetic systems for an application in electronic materials on the nanoscale.
The role of elastic interactions, particularly for the self-organized formation of periodically faceted interfaces, was investigated in this thesis for archetype organic-metal interfaces. The cantilever bending technique was applied to study the change of surface stress upon formation of the interface between 3,4,9,10-perylene-tetracarboxylic-dianhydride (PTCDA) and Ag(111). This system is known to form a chemisorptive bonding. Indeed, the sign and the coverage-dependence of the surface stress change are in agreement to models and previous measurements of chemisorptive systems in literature. While the adsorption of molecules into the large domains is associated with a negative, i.e. compressive stress change, the formation of domain boundaries in the molecular layer induces a stress change of opposite sign, increasing the surface stress. The magnitude of the surface stress change of (-0.30 +- 0.10} N/m reflects a relatively weak binding of a PTCDA molecule to each individual single silver atom. It is emphasized, however, that if normalized to the surface stress change per molecule, this value corresponds to a stress change of (-2.2 +- 0.2) eV per molecule which is in the order of the suspected binding energy of this system. Therefore, these experiments reveal elastic interactions to be of significant order of magnitude for this system class. Thereby, they add a new point of view to the understanding of these interfaces. Besides, since the results are in agreement with the well-known properties of this interface, they establish the cantilever bending technique in the field of organic-metal interfaces. The mere existence of a bending of the sample implies an interesting detail for the PTCDA/Ag(111) interface in particular. It is the first experimental evidence for a structural change in the topmost substrate layers upon adsorption of PTCDA on Ag(111). Since such a modification has significant implications for the interpretation of other experimental results, a further investigation with more quantitative structural methods appears necessary. The main focus of this work, however, was on the investigation of the formation of the long-range ordered, self-organized faceted PTCDA/Ag(10 8 7) interface. Reciprocal space maps of this interface were recorded both by spot profile analysis low energy electron diffraction (SPA-LEED) and low energy electron microscopy (LEEM) in selected area LEED mode. Complementary to the reciprocal data, also microscopic real-space LEEM data were used to characterize the morphology of this interface. Six different facet faces ((111), (532), (743), (954), (13 9 5), and (542)) were observed for the preparation path of molecular adsorption on the substrate kept at 550 K. Facet-sensitive dark-field LEEM localized these facets to grow in homogeneous areas of microscopic extensions. If the pristine mesoscopic orientation locally deviates from the average orientation, e.g. in pristine step density, locally different facet types are formed, distorting the otherwise regular mesoscopic pattern. Hence, the original mesoscopic orientation of the substrate strongly determines the degree of order of the faceted surface and the facet species formed. The temperature-dependence of the interface formation was studied in a range between 418 K and 612 K in order to learn more about the kinetics of the process. Additional steeper facets of 27° inclination with respect to the (111) surface were observed in the low temperature regime. Furthermore, using facet-sensitive dark-field LEEM, spatial and size distributions of specific facets were studied for the different temperatures. The nucleation density of the facets did not depend on temperature and can therefore be concluded not to be limited by diffusion. Moreover, the facet dimensions were statistically analyzed. The total island size of the facets follows an exponential distribution, indicating a random growth mode in absence of any mutual facet interactions. While the length distribution of the facets also follows an exponential distribution, the width distribution is peaked, reflecting the high degree of lateral order. This anisotropy is temperature-dependent and occurs starting above 478 K substrate temperature during growth. The peaked distribution indicates the presence of a long-range interaction which leads to the structural order of the self-organized grating. The origin of this long-range interaction was investigated combining three complementary in-situ methods, all providing new insights into the formation of faceted organic-metal interfaces: the cantilever bending technique, high-resolution low energy electron diffraction (SPA-LEED), and microscopy (LEEM). The cantilever bending technique was applied for the first time to a faceting system at all. Below the faceting transition temperature the surface stress change associated with the formation of the PTCDA/Ag(10 8 7) interface resembles in shape and magnitude the one observed for the reference interface PTCDA/Ag(111). But above the transition temperature the absolute surface stress change of (-0.67 +- 0.10) N/m observed for the faceted PTCDA/Ag(10 8 7) interface is considerably larger than for the previous cases. Moreover, the stress change happens in distinguishable stages with a clearly resolvable fine structure of regimes of positive and negative stress changes. These different regimes of surface stress change can be correlated to different stages of the structural phase transition observed by the structural in-situ methods. Thereby, morphological objects (i.e. the facets) are assigned to a specific stress character. Thus, domains of different stress character can be identified on the surface. These stress domains are the prerequisite to apply continuum descriptions of the self-ordering process based on elastic interactions. Hence, the results are the first experimental verification that these continuum descriptions are indeed also applicable to the whole system class of faceting organic-metal interfaces. In conclusion, the results provide strong evidence for elastic interactions being the physical origin of long-range order for this system. In addition, the clear correlation of structural phase transition and surface stress change regimes suggests surface stress to play also an important role for the kinetics of the system. Indeed, the system seems to try to limit the overall stress change during the interface formation by forming facets of positive and negative stress character. Hence, the selection of specific facets could depend on the corresponding stress character. Furthermore, the system seems willing to re-facet at high coverages in order to prevent imperfect domain boundaries which are associated with an increase of surface stress. Finally, template-assisted growth of lateral, heterorganic nanostructures has been explored. Therefore, self-assembled monolayers as a second archetype class of molecules were grown on partially covered PTCDA/Ag(10 8 7) interfaces. Indeed, using standard surface science techniques, the basic principle of this growth scheme was confirmed to be successful.
The present thesis demonstrates the potential of dipolar aggregation of merocyanine dyes as novel directional and specific supramolecular binding motif for the creation of more elaborate supramolecular architectures beyond simple dimers. Furthermore, the self-assembly studies into bis(merocyanine) nanorods gave new insights into the kinetics of morphogenesis in supramolecular aggregates.
Perylene bisimide (PBI) dyes are a widely used class of industrial pigments, and currently have gained significant importance for organic-based electronic and optical devices. Structural modification at the PBI core results in changes of the optical and electronic properties, which enable tailored functions. Moreover, the aggregation behavior of PBIs is alterable and controllable to achieve new materials, among which organogels are of particular interest because of their potential for applications as supramolecular soft materials. In this work, new PBI-based organic gelators were designed, synthesized, and characterized, and the aggregation behaviors under different conditions were intensively studied by various spectroscopic and microscopic methods. In chapter 2, a brief overview is given on the structural and functional features of organogel systems. The definition, formation and reversibility of organogels are introduced. Some examples on dye based organogel are selected, among which PBI-based organogelators reported so far are especially emphasized. Some basic knowledges of supramolecular chirality are also overviewed such as characterization, amplification, and symmetry breaking of the chiral aggregates. According to our former experiences, PBIs tend to form aggregates because the planer aromatic cores interact with one another by pi-pi interaction. In chapter 3, a new PBI molecule is introduced which possesses amide groups between the conjugated core and periphery alkyl chains. It is found that well oriented aggregates are formed by hydrogen bonding and the pi-pi interaction of the cores. These interactions enable the aggregates to grow in one-dimension forming very long fibers, and these fibers further intercross to 3D network structures, e.g., organogels. In comparison to the very few PBI-based gelators reported before, one advantage of this gelator is that, it is more versatile and can gelate a wide range of organic solvents. Moreover, the well-organized fibers that are composed of extended π-stacks provide efficient pathways for n-type charge carriers. Interestingly, AFM studies reveal that the PBI molecules form well-defined helical fibers in toluene. Both left-handed (M) and right-handed (P) helicities can be observed without any preference for one handedness because the building block is intrinsically achiral. In chapter 4, we tried to influence the M/P enantiomeric ratio by applying external forces. For example, we utilized chiral solvents to generate chiral aggregates with a preferential handedness. AFM analysis of the helices showed that a enantiomeric ratio of about 60: 40 can be achieved by aggregation in chiral solvents R- or S-limonene. Moreover, the long aggregated fibres can align at macroscopic level in vortex flows upon rotary stirring In chapter 5, bulky tetra-phenoxy groups are introduced in the bay area of the PBI gelator. The conjugated core of the new molecule is now distorted because of the steric hindrance. UV/Vis studies reveal a J-type aggregation in apolar solvents like MCH due to intermolecular pi-pi-stacking and hydrogen-bonding interactions. Microscopic studies reveal formation of columnar aggregates in apolar solvent MCH, thus this molecule lacks the ability to form gels in this solvent, but form highly fluorescent lyotropic mesophases at higher concentration. On the other hand, in polar solvents like acetone and dioxane, participation of the solvent molecules in hydrogen bonding significantly reduced the aggregation propensity but enforced the gel formation. The outstanding fluorescence properties of the dye in both J-aggregated viscous lyotropic mesophases and bulk gel phases suggest very promising applications in photonics, photovoltaics, security printing, or as fluorescent sensors. In chapter 6, we did some studies on combining PBI molecules with inorganic gold nanorods. Gold nanorods were synthesized photochemically. By virtue of the thioacetate functionalized PBIs, the rods were connected end to end to form gold nanochains, which were characterized by absorption spectra and TEM measurement. Such chromophore-nanorod hybrids might be applied to guide electromagnetic radiation based on optical antenna technology.
This thesis included the synthesis of conformationally stable chiral perylene bisimide (PBI) dyes, the study of their optical properties in solution and their chiral self-sorting behaviour in nonpolar solvents in which dimerization via pi-pi-stacking takes place. Furthermore, the influence of PBI core chirality on the properties of these dyes in the condensed state has been also studied. We have demonstrated and quantified the prevalence of chiral self-recognition over self-discrimination in pi-stacking dimerization of PBIs. It has been shown that this self-recognition event is compromised by the increasing flexibility of the structures related to the size of the OEG bridging units. Moreover, the inherent chirality of these PBIs has been proven to strongly influence their condensed state properties, for which large differences between the pure enantiomers and the racemates were revealed, as well as between the different bridged macrocyclic PBIs.