Refine
Has Fulltext
- yes (2)
Is part of the Bibliography
- yes (2)
Document Type
- Doctoral Thesis (2) (remove)
Keywords
- titania (2) (remove)
The main focus of this work was to get a deeper understanding of the relationship between the structure of sol-gel films, their densification and their macroscopic cracking. First of all titania was chosen as model system. Therefore a synthesis route starting from the preparation of long-term stable amorphous redissoluble precursor powders based on acetylacetone as chelate ligand was utilized. The solubility and stability of the powders in various solvents can be determined by chemical synthesis and technological parameters. When dissolved in a solvent mixture of ethanol and 1,5-pentanediol, thin films can be easily prepared by dip-coating technique. Thereby the quality of the titania films enormously depends on the calcinations temperature and the solvent mixture is used. In order to investigate the influence of different solvents and solvent mixtures on the microstructure and densification of the precursors, the coating solutions were stripped off (sol powder) and analyzed as function of annealing temperature. It was pointed out that a high densification rate caused by the addition of 1,5-pentanediol, results in dense microstructure with trapped residual carbon. These impurities can retard the phase transformation of anatase to rutile. The analysis of so-called “film powders” scraped off multiple dip-coated substrates provides valuable information on the effect of air moisture and unidirectional densification during drying and aging on the structure of thin films. The high surface-to-volume ratio and access to air moisture determine the chemical composition of the as-prepared film, which controls shrinkage, crystallization and defect structure of the coatings. Further it was shown, that drying as a thin film results in the formation of closed pores and much denser microstructure than the respective sol powder. Without the addition of 1,5-pentanediol all –OEt moieties undergo hydrolysis reactions, which causes the formation of a rigid network. The presence of 1,5-pentanediol retards this hydrolysis reactions and provides some network plasticity. Generally the microstructure of thin films is comparatively close to the microstructure of the film powders. The addition of 1,5-pentandiol prevents hydrolysis and condensation reactions as like in the film powders. However even at 700 °C, thin films never transform to rutile, which was attributed to the tensile stresses in thin films. In thin films and in film powders as well a comparable amount of closed pores are formed during annealing. Further it was shown that most of the thin sol-gel films investigated form a dense crust on their tops during annealing. This explains why crack free films exhibit only closed pores. However, when cracks appear during thin film shrinkage in the coating, this crust is burst, which generates open porosity. The defect density in the coatings was determined by an automated analysis of surface images. The crack formation and quantity can be directly referred to tensile stresses in the coatings, which arise from hydrolysis and condensation during thin film drying and aging. Therefore when 1,5-pentanediol is added to the sol, thin film cracking was avoided, because hydrolysis and condensation reactions are retarded, which preserves a higher network flexibility. Furthermore the crack formation was significantly influenced by the atmospheric humidity that was used during the coating process, which was explained by different drying and condensation rates. Under certain chemical starting conditions water soluble precursor powders can be also obtained. In general the observations made with the water based coating solutions are mostly in agreement with the former results based on ethanol based coating solutions. For example the high surface-to-volume ratio of film powders compared to sol powders also significantly enhances film drying and densification. The addition of 1,5-pentanediol also clearly contributes to their densification behavior and phase evolution. As seen before in the case of ethanol based coatings, 1,5-pentanediol enhances the stability towards hydrolysis and condensation reactions and preserves some network plasticity. Therefore coatings prepared without the addition of 1,5-pentanediol already form cracks during film drying and aging because of tensile stresses. Thus, the addition of 1,5-pentanediol results in a reduction/prevention of crack formation. Nevertheless some differences were observed, i.e. the critical single coating film thickness of ethanol based coatings is nearly twice that of water based coatings. This was explained by the different surface tensions of the basis solvents, which during thin film drying causes significantly higher capillary forces and tensile stresses in water based coatings. When acetylacetone is replaced by triethanolamine as chelating ligand for titanium also re-dissolvable precursor powders can be synthesized. The film powders combine a high hydrolytic stability of the precursor with sufficient intermediate network flexibility. The different type of organics changes the drying and densification behavior: i.e. in contrast to film powders obtained from acetylacetone based precursor powders the structure of triethanolamine based film powders is unaffected by the thin film drying process. This high hydrolytic stability and plasticity of this precursor allows the preparation of defect free coatings up to single film thickness of 300 nm. However triethanolamine based thin films present at intermediary annealing temperatures a distinctively different microstructure compared to acetylacetone based films. The general validity of the conclusions was proved on the basis of zirconia coatings that were also prepared by the use of re-dissolvable precursor powders. In principle all conclusions concerning the interconnection of precursor chemistry, film formation, densification and structure were transferable to the respective zirconia coatings. Differences mainly arise only from differential material properties i.e. bulk density. Finally, it has been pointed out that the findings obtained on the densification behavior of thinsol-gel films are also a valuable tool for improved explanations of other important scientific questions concerning sol-gel films, i.e. scratch resistance of sol-gel coatings, fiber -bridging and – degradation of sol-gel coated fibers.
Es wurde der Einfluss einer Substratfunktionalisierung auf die Flüssigphasenabscheidung von TiO2 auf dispersen Polymerlatexpartikeln in wässriger Lösung untersucht. Als Partikelsubstrate wurden zwei verschiedene Polystyrol-Latizes verwendet: Ein Latex mit einer geringen negativen Oberflächenladungsdichte (PS-Latex) und ein carboxylatfunktionalisierter Latex (PSC-Latex) mit einer hohen Dichte oberflächengebundener Ladungen. Durch die Adsorption von Polyelektrolyten aus wässriger Lösung konnte eine systematische Variation der Oberflächenfunktionalisierung erreicht werden. Dazu war bereits die Adsorption eines einzelnen kationischen Layers bzw. eines Polyelektrolytionenkomplexes durch die sequentielle Adsorption eines kationischen und eines anionischen Polyelektrolyten ausreichend, um eine effektive Kontrolle der TiO2-Abscheidung erzielen. Die Adsorption der kationischen Polymere PDADMAC und PAH sowie der anionischen Polymere PAA und PSS wurde mittels Zetapotentialmessungen untersucht. Bei der Adsorption von PDADMAC bzw. PAH auf dem schwach negativ geladenen PS-Latex konnte die in der Literatur beschriebene Überkompensation der Oberflächenladung, die einen Vorzeichenwechsel des Zetapotentials zur Folge hat, nicht beobachtet werden. Ebenso führte die zusätzliche Adsorption von PAA nicht zu einer signifikanten Änderung des Zetapotentials. Dagegen war die Adsorption von PSS durch ein deutlich negatives Zetapotential nachweisbar. Die erfolgreiche Adsorption von PDADMAC und PAH auf den unfunktionalisierten PS-Partikeln konnte mit Hilfe des Fluoreszenzmarkers 4-PSA direkt nachgewiesen werden. Die Adsorption der Polyelektrolyte auf dem Carboxylatlatex war durch deutliche Verschiebungen im pH-Profil des Zetapotentials nachweisbar. Mit der Adsorption entgegengesetzt geladener Polyelektrolyte konnte eine Umladung der Partikel erreicht werden, die allerdings nur in begrenzten pH-Bereichen zu beobachten war. Voraussetzung für die Abscheidung geschlossener TiO2-Schichten auf den jeweiligen Latexpartikeln war eine geeignete Oberflächenmodifikation. Die TiO2-Abscheidung auf dem PS-Latex war stark von der Art der Polyelektrolytlayer und dem pH-Wert der LPD-Lösung abhängig. Durch die Adsorption von PDADMAC bzw. PAH wurde eine deutliche Erhöhung der Keimdichte auf der Oberfläche erreicht. Die zusätzliche Adsorption von PAA war notwendig, um geschlossene Schichten zu erhalten. Auf PSC-Partikeln wurde mit allen untersuchten Polyelektrolytmodifikationen die Abscheidung dicht geschlossene Schichten erreicht, so dass eine Beteiligung der oberflächengebundenen Carboxylatgruppen an der Schichtbildung nahe liegt. Dabei war die Morphologie der LPD-Schichten weitgehend unabhängig vom Zetapotential der Latexpartikel und es konnte kein einfacher Zusammenhang zwischen der Oberflächenladung des Substrats und der TiO2-Abscheidung herausgearbeitet werden. Es wurden deutliche Unterschiede in den TiO2-Abscheidungsraten auf den verschiedenen Polyelektrolytlayern gefunden. Die Abscheidung von glatten, gleichmäßigen Schichten erfolgte dabei deutlich langsamer als die Bildung ungleichmäßiger Schichten. Glatte Schichten wiesen in zu Beginn der Abscheidung eine hohe Keimdichte auf. Schichten mit ungleichmäßiger Dicke entstanden durch schnelles, inselartiges Wachstum der Schicht ausgehend von einer niedrigen Keimdichte. Auf der Grundlage der Unterschiede in den Wachstumsgeschwindigkeiten der Schichten und dem Auftreten von homogenen Präzipitaten wurde ein Abscheidungsmechanismus durch Aggregation kolloidaler TiO2-Partikel aus homogener Nukleation in der Lösung diskutiert. Durch die Selbstorganisation einer Monolage von polyelektrolytfunktionalisierten Latexpartikeln an der Phasengrenze einer Octanolemulsion in Wasser konnten sphärische Template mit einer geordneten Oberflächenstruktur für die Mineralisation von Hohlkapseln erzeugt werden. Durch die TiO2-Abscheidung auf den Latexpartikeln und in den Zwickeln der Monolage wurden Kompositkapseln in einem Größenbereich von 50-150 µm mit einer hierarchisch strukturierten Oberfläche erhalten. Durch Auflösen des Polymertemplats in Toluol und Kalzinieren der Kompositkapseln wurden Hohlkugeln aus einem porösen anorganische Gerüst erzeugt. Die Mikrostruktur der auf den selbstorganisierten Templaten abgeschiedenen TiO2-Schicht in Abhängigkeit von der Kalzinierungstemperatur wurde durch Stickstoffsorptionsmessungen sowie Röntgendiffraktometrie charakterisiert und die photokatalytische Aktivität der getemperten Kapseln wurde anhand des UV-induzierten Abbaus von Dichloressigsäure untersucht.