This thesis reports a successful fabrication and characterisation of ferromagnetic/superconductor junction (F/S) on graphene. The thesis preposes a fabrication method to produce F/S junctions on graphene which make use of ALD grown Al2O3 as the tunnel barrier for the ferromagnetic contacts. Measurements done on F/G/S/G/F suggests that by injecting spin polarised current into the superconductor, a spin imbalance is created in the quasiparticle density of states of the superconductor which then diffuses through the graphene channel. The observed characteristic curves are similar to the ones which are already reported on metallic ferromagnet/superconductor junctions where the spin imbalance is created using Zeeman splitting. Further measurements also show that the curves loose their characteristic shapes when the temperature is increased above the critical temperature (Tc) or when the external magnetic field is higher then the critical field (Hc) of the superconducting contact. But to prove conclusively and doubtlessly the existence of spin imbalance in ferromagnet/superconductor junctions on graphene, more devices have to be made and characterised preferably in a dilution refrigerator.
Transition metal oxides (TMO) represent a highly interesting material class as
they exhibit a variety of different emergent phenomena including multiferroicity and
superconductivity. These effects result from a significant interplay of charge, spin
and orbital degrees of freedom within the correlated d-electrons. Oxygen vacancies
(OV) at the surface of certain d0 TMO release free charge carriers and prompt the
formation of a two-dimensional electron gas (2DEG). Barium titanate (BaTiO3) is a
prototypical and promising d0 TMO. It displays ferroelectricity at room temperature
and features several structural phase transitions, from cubic over tetragonal (at
room temperature) and orthorhombic to rhombohedral. The spontaneous electric
polarization in BaTiO3 can be used to manipulate the physical properties of adjacent
materials, e.g. in thin films. Although the macroscopic properties of BaTiO3 are studied
in great detail, the microscopic electronic structure at the surface and interface of
BaTiO3 is not sufficiently understood yet due to the complex interplay of correlation
within the d states, oxygen vacancies at the surface, ferroelectricity in the bulk and
the structural phase transitions in BaTiO3.
This thesis investigates the electronic structure of different BaTiO3 systems by
means of angle-resolved photoelectron spectroscopy (ARPES). The valence band of
BaTiO3 single crystals is systematically characterized and compared to theoretical
band structure calculations. A finite p-d hybridization of titanium and oxygen states
was inferred at the high binding energy side of the valence band. In BaTiO3 thin films,
the occurrence of spectral weight near the Fermi level could be linked to a certain
amount of OV at the surface which effectively dopes the host system. By a systematic
study of the metallic surface states as a function of temperature and partial oxygen
pressure, a model was established which reflects the depletion and accumulation of
charge carriers at the surface of BaTiO3. An instability at T ~ 285K assumes a volatile
behavior of these surface states.
The ferroelectricity in BaTiO3 allows a control of the electronic structure at the interface
of BaTiO3-based heterostructures. Therefore, the interface electronic structure
of Bi/BaTiO3 was studied with respect to the strongly spin-orit coupled states in Bi by
also including a thickness dependent characterization. The ARPES results, indeed,
confirm the presence of Rashba spin-split electronic states in the bulk band gap of the ferroelectric substrate. By varying the film thickness in Bi/BaTiO3, it was able to modify
the energy position and the Fermi vector of the spin-split states. This observation
is associated with the appearance of an interface state which was observed for very
low film thickness. Both spectral findings suggest a significant coupling between the
Bi films and BaTiO3.
The contribution of the present thesis consists of three parts. They are centered around investigating certain semiconductor heterointerfaces relevant to spin injection, exploring novel, diluted magnetic single barrier tunneling structures, and further developing diluted magnetic II-VI resonant tunneling diodes.
In the field of spintronics, spin manipulation and spin transport are the main principles that need to be implemented. The main focus of this thesis is to analyse semiconductor systems where high fidelity in these principles can be achieved. To this end, we use numerical methods for precise results, supplemented by simpler analytical models for interpretation.
The material system of 2D topological insulators, HgTe/CdTe quantum wells, is interesting not only because it provides a topologically distinct phase of matter, physically manifested in its protected transport properties, but also since within this system, ballistic transport of high quality can be realized, with Rashba spin-orbit coupling and electron densities that are tunable by electrical gating. Extending the Bernvevig-Hughes-Zhang model for 2D topological insulators, we derive an effective four-band model including Rashba spin-orbit terms due to an applied potential that breaks the spatial inversion symmetry of the quantum well. Spin transport in this system shows interesting physics because the effects of Rashba spin-orbit terms and the intrinsic Dirac-like spin-orbit terms compete. We show that the resulting spin Hall signal can be dominated by the effect of Rashba spin-orbit coupling. Based on spin splitting due to the latter, we propose a beam splitter setup for all-electrical generation and detection of spin currents. Its working principle is similar to optical birefringence. In this setup, we analyse spin current and spin polarization signals of different spin vector components and show that large in-plane spin polarization of the current can be obtained. Since spin is not a conserved quantity of the model,
we first analyse the transport of helicity, a conserved quantity even in presence of Rashba spin-orbit terms. The polarization defined in terms of helicity is related to in-plane polarization of the physical spin.
Further, we analyse thermoelectric transport in a setup showing the spin Hall effect. Due to spin-orbit coupling, an applied temperature gradient generates a transverse spin current, i.e. a spin Nernst effect, which is related to the spin Hall effect by a Mott-like relation. In the metallic energy regimes, the signals are qualitatively explained by simple analytic models. In the insulating regime, we observe a spin Nernst signal that originates from the finite-size induced overlap of edge states.
In the part on methods, we discuss two complementary methods for construction of effective semiconductor models, the envelope function theory and the method of invariants. Further, we present elements of transport theory, with some emphasis on spin-dependent signals. We show the connections of the adiabatic theorem of quantum mechanics to the semiclassical theory of electronic transport and to the characterization of topological phases. Further, as application of the adiabatic theorem to a control problem, we show that universal control of a single spin in a heavy-hole quantum dot is experimentally realizable without breaking time reversal invariance,
but using a quadrupole field which is adiabatically changed as control knob. For experimental realization, we propose a GaAs/GaAlAs quantum well system.
In pursuit of a novel generation of devices, exploration of spin properties of the particles is needed. Spintronics is a modern field in physics which exploits spin properties to be used in addition to the charge degree of freedom. Since the conductivity mismatch problem presents a fundamental obstacle for electrical spin injection from a ferromagnetic metal into a diffusive semiconductor [SFM+00], other means for injecting spin-polarized carriers must be used. With a tunnel contact, it is possible to achieve a highly spin-polarized room-temperature tunnel injection [JWS+05]. We used a novel approach and applied magnetic RTDs for spin manipulation. In this work, properties of all-II-VI magnetic resonant tunneling diodes (RTDs), as applied to spintronics, were reported. Growth conditions were optimized to increase the peak-to-valley ratio, and the design of the RTDs was optimized for observation of spin related transport effects. When an external magnetic field was applied, spin manipulation became possible. Selforganized CdSe quantum structures were grown and investigated using optical means. After embedding them into a (Zn,Be)Se tunneling barrier, the properties were assessed by the resonant tunneling.
Röntgenstrukturuntersuchungen an spintronischen Halbleiter- und Halbmetall-Dünnschichtsystemen
(2010)
In dieser Arbeit wurden die strukturellen Eigenschaften von spintronischen Halbleiter- und Halbmetall-Dünnschichtsystemen untersucht. Mit Röntgenreflektivitätsmessungen konnten die Schichtdicken und Grenzflächenrauigkeiten der Mehrschichtsysteme sehr genau bestimmt werden. Hierfür wurde die Software Fewlay verwendet, welche den Parratt-Formalismus zur Berechnung der Reflektivität nutzt. An reziproken Gitterkarten, die an möglichst hoch indizierten Bragg-Reflexen gemessen wurden, konnte das Relaxationsverhalten der Schichtsysteme untersucht werden.
Since the late 20th century, spintroncis has become a very active field of research [ŽFS04]. The prospect of spin based information technology, featuring strongly decreased energy consumption and possibly quantum-computation capabilities, has fueled this interest. Standard materials, like bulk gallium arsenide (GaAs), have experienced new attention in this context by exhibiting extraordinarily long lifetimes for nonequilibrium spin information, which is an important requirement for efficient spin based information storage and transfer. Another important factor is the lengthscale over which spin information can be transported in a given material and the role of external influences. Both aspects have been studied experimentally with innovative optical methods since the late 1990s by the groups of D. D. AWSHALOM and S. A. CROOKER et al. [KA99, CS05, CFL+05]. Although the pioneering experimental approaches presented by these authors led to a variety of insights into spin propagation, some questions were raised as well. Most prominently, the classical Einstein relation, which connects the mobility and diffusivity of a given particle species, seemed to be violated for electron spins in a bulk semiconductor. In essence, nonequilibrium spins appeared to move (diffuse) faster than the electrons that actually carry the spin. However, this contradiction was masked by the fact, that the material of interest was n-type GaAs with a doping concentration directly at the transition between metallic and insulating behavior (MIT). In this regime, the electron mobility is difficult to determine experimentally. Consequently, it was not a priori obvious that the spin diffusion rates determined by the newly introduced optical methods were in contradiction with established electrical transport data.
However, in an attempt to extend the available data of optical spin microscopy, another issue surfaced, concerning the mathematical drift-diffusion model that has been commonly used to evaluate lateral spin density measurements. Upon close investigation, this model appears to have a limited range of applicability, due to systematic discrepancies with the experimental data (chapter 4). These deviations are noticeable in original publications as well, and it is shown in the present work that they originate from the local heating of electrons in the process of optical spin pumping. Based on insights gained during the second half of the 20th century, it is recapitulated why conduction electrons are easily overheated at cryogenic temperatures. The main reason is the poor thermal coupling between electrons and the crystal lattice (chapter 3). Experiments in the present work showed that a significant thermal gradient exists in the conduction band under local optical excitation of electron–hole pairs. This information was used to develop a better mathematical model of spin diffusion, which allowed to derive the diffusivity of the undisturbed system, due to an effective consideration of electron overheating. In this way, spin diffusivities of n-GaAs were obtained as a function of temperature and doping density in the most interesting regime of the metal–insulator-transition.
The experiments presented in this work were performed on a series of n-type bulk GaAs samples, which comprised the transition between metallic conductivity and electrical insulation at low temperatures. Local electron temperature gradients were measured by a hyperspectral photoluminescence imaging technique with subsequent evaluation of the electron–acceptor (e,A$^0$) line shape. The local density of nonequilibrium conduction electron spins was deduced from scanning magneto-optic Kerr effect microscopy. Numerical evaluations were performed using the finite elements method in combination with a least-squares fitting procedure.
Chapter 1 provides an introduction to historical and recent research in the field of spintronics, as far as it is relevant for the understanding of the present work. Chapter 2 summarizes related physical concepts and experimental methods. Here, the main topics are semiconductor optics, relaxation of hot conduction electrons, and the dynamics of nonequilibrium electron spins in semiconductors.
Chapter 3 discusses optical heating effects due to local laser excitation of electron–hole pairs. Experimental evaluations of the acceptor-bound-exciton triplet lines led to the conclusion that the crystal lattice is usually not overheated even at high excitation densities. Here, the heat is efficiently dissipated to the bath, due to the good thermal conductivity of the lattice. Furthermore, the heating of the lattice is inherently limited by the weak heat transfer from the electron system, which on the other hand is also the reason why conduction electrons are easily overheated at temperatures below ≈ 30 K. Spatio-spectral imaging of the electron–acceptor-luminescence line shape allowed to trace the thermal gradient within the conduction band under focused laser excitation. A heat-diffusion model was formulated, which reproduces the experimental electron-temperature trend nicely for low-doped GaAs samples of n- and p-type. For high-doped n-type GaAs samples, it could be shown that the lateral electron-temperature profile is well approximated by a Gaussian. This facilitated easy integration of hot electron influence into the mathematical model of spin diffusion.
Chapter 4 deals with magneto-optical imaging of optically induced nonequilibrium conduction-electron spins in n-GaAs close to the MIT. First, the spectral dependence of the magneto-optic Kerr effect was examined in the vicinity of the fundamental band gap. Despite the marked differences among the investigated samples, the spectral shape of the Kerr rotation could be described in terms of a simple Lorentz-oscillator model in all cases. Based on this model, the linearity of the Kerr effect with respect to a nonequilibrium spin polarization is demonstrated, which is decisively important for further quantitative evaluations.
Furthermore, chapter 4 presents an experimental survey of spin relaxation in n-GaAs at the MIT. Here, the dependence of the spin relaxation time on bath temperature and doping density was deduced from Hanle-MOKE measurements. While all observed trends agree with established literature, the presented results extend the current portfolio by adding a coherent set of data.
Finally, diffusion of optically generated nonequilibrium conduction-electron spins was investigated by scanning MOKE microscopy. First, it is demonstrated that the standard diffusion model is inapplicable for data evaluation in certain situations. A systematic survey of the residual deviations between this model and the experimental data revealed that this situation unfortunately persisted in published works. Moreover, the temperature trend of the residual deviations suggests a close connection to the local overheating of conduction electrons. Consequently, a modified diffusion model was developed and evaluated, in order to compensate for the optical heating effect. From this model, much more reliable results were obtained, as compared to the standard diffusion model. Therefore, it was shown conclusively that the commonly reported anomalously large spin diffusivities were at least in parts caused by overheated conduction electrons.
In addition to these new insights some experimental and technological enhancements were realized in the course of this work. First, the optical resolution of scanning MOKE microscopy was improved by implementing a novel scanning mechanism, which allows the application of a larger aperture objective than in the usual scheme. Secondly, imaging photoluminescence spectroscopy was employed for spatially resolved electron-temperature measurements. Here, two different implementations were developed: One for lattice-temperature measurements by acceptor–bound exciton luminescence and a second for conduction-electron temperature measurements via the analysis of the electron–acceptor luminescence line shape.
It is shown in the present work that the originally stated anomalously high spin diffusivities were caused to a large extent by unwanted optical heating of the electron system. Although an efficient method was found to compensate for the influence of electron heating, it became also evident that the classical Einstein relation was nonetheless violated under the given experimental conditions. In this case however, it could be shown that this discrepancy did not originate from an experimental artifact, but was instead a manifestation of the fermionic nature of conduction electrons.
The present thesis “Hot spin carriers in cold semiconductors” investigates hot carrier effects in low-temperature photoinduced magneto-optical Kerr effect (MOKE) microscopy of electron spins in semiconductor heterostructures. Our studies reveal that the influence of hot photocarriers in magneto-optical pump-probe experiments is twofold.
First, it is commonly assumed that a measurement of the local Kerr rotation using an arbitrary probe wavelength maps the local electron spin polarization. This is the fundamental assumption that underlies the widely used two-color MOKE microscopy technique. Our continuous-wave (cw) spectroscopy experiments demonstrate that this assumption is not correct.
At low lattice temperatures the nonresonant spin excitation by the focused pump laser inevitably leads to a strong heating of the electron system. This heating, in turn, locally modifies the magneto-optical coefficient which links the experimentally observed Kerr rotation to the electron spin polarization. As a consequence, the spin-induced local Kerr rotation is augmented by spin-unrelated changes in the magneto-optical coefficient. A spatially resolved measurement of the Kerr rotation then does not correctly map the electron spin polarization profile.
We demonstrate different ways to overcome this limitation and to correctly measure the electron spin profile. For cw spectroscopy we show how the true local electron spin polarization can be obtained from a quantitative analysis of the full excitonic Kerr rotation spectrum. Alternatively, picosecond MOKE microscopy using a spectrally broad probe laser pulse mitigates hot-carrier effects on the magneto-optical spin detection and allows to directly observe the time-resolved expansion of optically excited electron spin packets in real-space.
Second, we show that hot photocarriers strongly modify the spin diffusion process. Owing to their high kinetic energy, hot carriers greatly enhance the electron spin diffusion coefficient with respect to the intrinsic value of the undisturbed system. Therefore, for steady-state excitation the spin diffusivity is strongly enhanced close to the pump spot center where hot electrons are present. Similarly, for short delays following pulsed excitation the high initial temperature of the electrons leads to a very fast initial expansion of the spin packet which gradually slows as the electrons cool down to the lattice temperature.
While few previous publications have recognized the possible influence of hot carriers on the electron spin transport properties, the present work is the first to directly observe and quantify such hot carrier contributions. We develop models which for steady-state and pulsed excitation quantitatively describe the experimentally observed electron spin diffusion. These models are capable of separating the intrinsic spin diffusivity from the hot electron contribution, and allow to obtain spin transport parameters of the undisturbed system.
We perform extensive cw and time-resolved spectroscopy studies of the lattice temperature dependence of the electron spin diffusion in bulk GaAs. Using our models we obtain a consistent set of parameters for the intrinsic temperature dependence of the electron spin diffusion coefficient and spin relaxation time and the hot carrier contributions which quantitatively describes all experimental observations. Our analysis unequivocally demonstrates that we have, as we believe for the first time, arrived at a coherent understanding of photoinduced low-temperature electron spin diffusion in bulk semiconductors.
Herstellung und Charakterisierung spintronischer und caloritronischer (Ga,Mn)As-Nanostrukturen
(2014)
Die elektronischen Bauteile, die aus unserer technischen Welt kaum wegzuddenken sind, werden immer kleiner. Aktuelle ICs bestehen zum Beispiel aus Milliarden von Transistoren, von denen jeder einzelne kleiner als 100nm (dem 100-stel des typischen Durchmessers eines Menschenhaars) ist. Dass die Entwicklung auch zukünftig weiter dem Trend des Mooreschen Gesetzes folgen wird, gilt hierbei als unbestritten.
Die interessanteste Fragestellung der Halbleiter- und Nanostrukturforschung in diesem Zusammenhang ist: Kann man die weitere Entwicklung der Informations- und Kommunikationstechnik dadurch erreichen, dass man die Miniaturisierung der Transistoren in Mikroprozessoren und Speicherbauelementen weiter vorantreibt oder ist man auf gänzlich neue Wege angewiesen?
Bei der weitergehenden Miniaturisierung ist die größte Hürde darin zu suchen, ob man in der
Lage sein wird die Verbrauchsleistung dieser Bauelemente weiter zu reduzieren, um die Überhitzung der Bauteile in den Griff zu bekommen und nicht zuletzt auch, um Energie zu sparen.
Die heutige Elektronik hat ihre Grundlagen in den 60er Jahren. Diese Art der Elektronik ist jedoch hinsichtlich der Effizienzsteigerungen und vor allem der Wärmeentwicklung an ihre Grenzen gestoßen. Hauptursache für diese problematische Wärmeentwicklung sind die elektrischen Verbindungen, die die Informationen zwischen der halbleiterbasierten Datenverarbeitung und den metallischen Speicherelementen hin und hertransportieren. Obwohl diese elektrischen Verbindungen zum aktuellen Zeitpunkt aus der Computerarchitektur nicht weg zu denken sind, ist es eines der Hauptziele diese Verbindungen nicht mehr verwenden zu müssen. Dies kann jedoch nur erreicht werden, wenn es gelingt, die Speicherelemente und Datenverarbeitung in einem einzigen Element (Halbleiter) zu vereinen.
Bisher wurde die Ladung eines Elektrons für die Verarbeitung von elektrischen Informationen
bzw. Zuständen benutzt. Was wäre jedoch, wenn man diese bisherige Basis völlig ändert? Der
Spin der Elektronen ist ein viel effektiverer Informationsträger als die Ladung der Elektronen
selbst, nicht zuletzt deshalb, weil die Veränderung des Spins eines Elektrons im Vergleich zu
dessen Bewegung einen weitaus geringeren Energiebetrag benötigt [1]. Die Technik, die zusätzlich zur Informationsverarbeitung durch makroskopische Elektronenströme den viel effektiveren Spin-Quantenzustand der Elektronen oder Löcher als Freiheitsgrad nutzt, ist die sogenannte Spintronik1. Die Spinfreiheitsgrade eröffnen, wegen der längeren Phasenkohärenzlänge, im Vergleich zu den orbitalen Freiheitsgraden, völlig neue Wege für zukünftige Entwicklungen wie z.B. den Quantencomputer. Damit wäre die Entwicklung niederenergetischer Bauelemente möglich, die fast keine Wärmeentwicklung aufweisen. Wegen dieser vielen Vorteile hat sich die Spintronik in Rekordzeit von einer interessanten wissenschaftlichen Beobachtung in Rekordzeit zu einer marktbewegenden Anwendung weiterentwickelt (Nobelpreis 2007). Seinen Anfang nahm diese Entwicklung 1988 mit der Entdeckung des GMR-Effekts. Nach nur 9 Jahren wurden 1997 erste Festplatten-Leseköpfe eingesetzt, die sich diesen Effekt zu Nutze machten. Leseköpfe, die den Riesenmagnetwiderstand nutzen, waren nunmehr um ein Vielfaches empfindlicher als es die konventionelle Technik zugelassen hätte. Die Speicherdichte und damit die Kapazitäten der Festplatten konnte somit erheblich gesteigert und Festplatten mit zuvor nie gekannter Speicherkapazität preiswert produziert werden. Seit dieser Zeit rückt der Elektronenspin immer weiter in den Brennpunkt von Forschung und Entwicklung.
Da sich der elektrische Widerstand von Halbleitern in einem weiten Bereich manipulieren lässt
(was für ferromagnetische Metalle nicht der Fall ist), werden logische Bauelemente aus halbleitenden Materialien hergestellt. Im Gegensatz dazu sind ferromagnetische Metalle sehr gute Kandidaten für die Speicherung von Informationen. Dies liegt vor allem daran, dass zufällige Magnetfelder viel schwächer sind, als zufällige elektrische Felder, was ferromagnetische Systeme wesentlich unanfälliger macht. Daher sind die magnetischen Speicher nicht flüchtig und zudem müssen deren Informationsgehalte nicht wie bei DRAM immer wieder aufgefrischt werden. Um die jeweiligen Vorteile der Materialklassen – die magnetisch energiesparende sowie dauerhafte Speicherfähigkeit der Metalle und die logischen Operationen der Halbleiter – miteinander kombinieren zu können und damit neuartige Bauelemente wie z.B. MRAMs (logische Operationen und dauerhafte Speicherung) zu bauen, sind ferromagnetischen Halbleiter unverzichtbar. Auf dieser Basis könnten Speicherelemente und Datenverarbeitung in einem einzigen Element (Halbleiter) dargestellt werden. Zugleich braucht man aber auch neue Wege, um diese Speicher zu magnetisieren und später auslesen zu können. Ein weiterer Vorteil liegt zudem darin, dass hierzu kein Einsatz beweglicher Teile notwendig ist. Die Magnetisierungskontrolle muss aber temperaturunabhängig sein!
Der am besten erforschte ferromagnetische Halbleiter ist (Ga,Mn)As, der deswegen die Modellrolle einnimmt und als Prototyp für alle ferromagnetischen Halbleiter dient. Die Kopplung seiner magnetischen und halbleitenden Eigenschaften durch Spin-Bahn-Wechselwirkung ist die Ursache vieler neuer Transportphänomene in diesem Materialsystem. Diese Phänomene sind vielfach die Grundlage für neuartige Anwendungen, Bauteildesigns und Wirkprinzipien.
Das Ziel dieser Arbeit ist es, die interessanten Anisotropien in (Ga,Mn)As, die von der sehr starken Spin-Bahn-Kopplung im Valenzband herrühren zu nutzen, sowie neue spinbezogene Effekte in verschiedenen magnetischen Bauelementen zu realisieren.
Die vorliegende Arbeit gliedert sich wie folgt: In Kapitel 1 wird auf die grundlegenden Eigenschaften des (Ga,Mn)As und einige neuartige Spineffekten, die dieses Material mit sich bringt, eingegangen. Das zur Erzeugung dieser Effekte notwendige fertigungstechnische Wissen, für die lithografische Erzeugung der spintronisch bzw. caloritronisch aktiven Nanostrukturen, wird im Kapitel 2 beschrieben.
Um mit dieser Welt der Spineffekte „kommunizieren“ und die Effekte kontrollieren zu können,
sind entsprechend angepasste und funktionsfähige Kontaktierungen notwendig. Mit der detaillierten Herstellung und Analyse dieser Kontakte beschäftigt sich das Kapitel 3. Es wurden
zwei Arten von Kontakten hergestellt und bei den Proben eingesetzt: in situ (innerhalb der
MBE-Wachstumskammer) und ex situ. Zusammenfassend lässt sich sagen, dass bei der ex situ-Probenpräparation, die Reproduzierbarkeit der Kontakte, besonders bei logisch magnetischen Elementen, nicht gewährleistet werden konnte. Bei funktionierender Kontaktierung war das magnetische Verhalten dann jedoch stets gleich. Bei den in situ-Kontakten war zwar einerseits das elektrische Verhalten reproduzierbar und sehr gut, aber das magnetische Verhalten war nicht zufriedenstellend, da die Relaxation nicht vollständig stattfand.
Im Rahmen dieser Arbeit konnten die ex situ-Kontakte optimiert werden. Dabei wurde auf die
Problematiken bereits existierender Proben eingegangen und es wurden verschiedene Lösungsan sätze dafür gefunden. So konnte z.B. gezeigt werden, dass die Haftungsprobleme hauptsächlich auf dem unsaubere Oberflächen zurückzuführen sind. Jede Schicht, die zwischen aufgedampfter Metallschicht und dem dotierten Halbleiter bestehen bleibt, unabhängig davon, ob es sich dabei um eine oxidierte Schicht, Lackreste oder eine, zum Teil verarmte Schicht handelt, beeinträchtigt die Funktionalität der Kontakte. Je kleiner die Dimension der Kontakte, desto stärker wirkt sich die unsaubere Oberfläche aus. So konnte gezeigt werden, dass ab einer Größe von ca. 500nm_500nm die Zuverlässigkeit der Kontakte elementar von der Reinheit der Oberflächen und deren Homogenität beeinflusst wird. Zur Abwendung dieser Komplikationen werden verschiedene Lösungsansätze vorgeschlagen. Wird die Oberfläche mit hochenergetischen Ionen versetzt, verarmt deren Dotierung, was zu einer massiven Änderung der Leitfähigkeit führt. Daher wurden entweder völlig andere Prozessparameter zur Reinigung eingesetzt, die den dotierten HL nicht verarmen oder einer der nasschemischen Schritte wurde so angepasst, dass die extrem verarmte Schicht der HL-Oberfläche entfernt wurde.
Die einfachsten spintronischen Bauelemente (Streifen) und magnetischen Logikelemente sowie
deren Ergebnisse werden im Kapitel 4 diskutiert.
Hier wurde eindeutig gezeigt, dass die Streifen bei niedrigen Stromdichten nicht völlig uniaxial
sind, während bei erhöhten Stromdichten die Uniaxialität immer dominanter wird. Dies war
jedoch zu erwarten, da bei erhöhten Stromdichten die Temperatur auch ansteigt und da, bei
erhöhter Temperatur, die biaxiale Anisotropie mit M4, die uniaxiale aber jedoch nur mit M2
abfällt – die dominante Anisotropie wechselt folglich von biaxial zu uniaxial [2]. Im Rahmen dieser Arbeit wurden die Grundlagen gelegt, um Speicherelemente und Datenverarbeitung in einem einzigen Halbleiter (Ga,Mn)As herzustellen. Auf Basis dieser Arbeit und den dabei gewonnenen litographischen Erkentnissen wurden, in nachfolgenden Arbeiten, solche Bauelemente realisiert [3].
Spin-Kaloritronik:
Wie schon Eingangs erwähnt, wird im Allgemeinen davon ausgegangen, dass die Miniaturisierung der zukünftigen Elektronik weitergeführt werden kann. Bei stetiger Verkleinerung der Strukturen kommt es in heutigen Anwendungen zu immer größeren Problemen bei der Wärmeabfuhr. Die Folgen der Temperaturdifferenzen innerhalb der Strukturen führen dabei zu sog. Hotspots oder sogar Materialschäden. Temperaturunterschiede müssen aber nicht nur negative Auswirkungen
haben. So wurde an einem ferromagnetischen System aus Nickel, Eisen und Platin der sogenannte Spin-Seebeck-Effekt gemessen, bei dem die Elektronen in den Regionen verschiedener Temperatur unterschiedliche Spinpolarisationen zeigen [4].
Eine Batterie, die diesen spinpolarisierten Strom nutzt, könnte einen entscheidenden Fortschritt
in der Spintronik bedeuten. Dieser Bereich der Forschung an thermoelektrischen Effekten, bei
denen ferromagnetische Materialien involviert sind, wird auch „spin-caloritronics“ genannt [5].
Die Kapitel 5 und 6 beschäftigen sich mit einer neuartigen Klasse spintronischer Bauteile. whärend das Kapitel 5 sich mit einer neuartigen Klasse spintronischer Bauteile, für die von uns
als Bezeichnung TAMT („tunnel anisotropic magneto thermopower“) eingeführt wurde, beschäftigt, wird in Kapitel 6 an einem veränderten Probenlayout der Nernst-Effekt nachgewiesen.
Die Geometrie wurde in beiden fällen so gewählt und hergestellt, dass durch die Anisotropien
des (Ga,Mn)As die beiden thermoelektrische Effekte (Seebeck- und Nernst-Effekt) auf einen
n+-p+-Übergang übertragen werden konnten. Durch einen Strom, in einem mit Silizium hoch
dotierten GaAs-Heizkanal, kann jeweils ein vertikaler Temperaturgradient erzeugt werden. Die
hierbei entstehenden Thermospannungen wurden durch eine vollständige elektrische Charaktri sierungsmessung mit Hilfe präziser Lock-in-Verstärker-Technik detektiert.
Das Kapitel 5 beschäftigt sich mit allen Bereichen, von der Idee bis hin zu Messungen und Analysen des Seebeck-Effektes an einem n-p-Übergang (TAMT). Außerdem ist ein sehr einfaches numerisches Modell dargestellt, dass den gefundenen Effekt theoretisch beschreibt.
Durch die bekannten thermoelektrischen Effekte ergibt sich ein Temperaturgradient der immer
zu einer Thermospannung und somit zu einem Thermostrom entlang des Gradienten führt. Für
zukünftige Entwicklungen ist es demnach wichtig, diese Effekte zu beachten und diese bei elektrischen Messungen an Nanostrukturen als mögliche, zusätzliche Ursache eines Messsignals in Betracht zu ziehen.
In den vorliegenden Proben ist der Seebeck-Effekt stark anisotrop, mit einem größeren Thermospannungswert für Magnetisierungen entlang der magnetisch harten Achsen des (Ga,Mn)As.
Es wurde ein einfaches Model entwickelt, welches das Tunneln von Elektronen zwischen zwei
unterschiedlich warmen Bereichen erklärt. Die Abhängigkeit des Effekts von der Temperatur des Heizkanals wurde anhand dieses Models sowohl qualitativ als auch größenordnungsmäßig korrekt beschrieben.
Die Nernst-Proben wurden von der Theorie bis zur Herstellung so entwickelt, dass in derselben
Anordnung eine im (Ga,Mn)As senkrecht zum Temperaturgradienten gerichtete Spannung
zusätzlich gemessen werden konnte. Diese wurde durch den Nernst-Effekt erklärt. Besonders interessant war, dass die Größe der Nernst-Spannung hierbei mit der Magnetisierung im (Ga,Mn)As verknüpft ist und somit ein aus der typischen Magnetisierungsumkehr hervorgehendes Verhalten zeigt.
Gegenüber den Magnetowiderstandseffekten entsteht beim Nernst-Effekt in sogenannten Fingerprints (vgl. Kapitel 1.3.3) ein dreistufiges Farbmuster anstelle eines zweistufigen hoch-tief-Systems. Die entstehende Temperatur im Heizkanal wird jeweils durch eine longitudinale Widerstandsmessung in einem senkrecht zum Kanal gerichteten äußeren Magnetfeld bestimmt. Die Magnetfeldabhängigkeit des Widerstands kommt hierbei durch den Effekt der schwachen Lokalisierung in dünnen Filmen zustande.
Zusammenfassend stellen die Magneto-Thermoelektrizitätseffekte eine wichtige weitere Transporteigenschaft in ferromagnetischen Halbleitern dar, die mit der Magnetisierung direkt zusammenhängen.
In dieser Arbeit wurden Thermospannungen an (Ga,Mn)As-Schichten mit vergleichsweise hoher
Mangankonzentration untersucht. Allerdings sind die Thermoelektrizitätseigenschaften zusammen mit Magneto-Widerstandsmessungen in Zukunft in der Lage, zusätzliche Informationen über die Bandstruktur sowie die Ladungsträgereigenschaften in Materialsystemen mit niedrigerem Mangangehalt, insbesondere in der Nähe des Metall-Isolator-Übergangs, zu liefern.
Inhalt des Anhangs ist eine ausführliche Anleitung zur Optimierung der Probenherstellung bzw.
der verschiedenen Bauelemente.
Fabrication and characterization of CPP-GMR and spin-transfer torque induced magnetic switching
(2014)
Even though the unique magnetic behavior for ferromagnets has been known for thousands of years, explaining this interesting phenomenon only occurred in the 20th century. It was in 1920, with the discovery of electron spin, that a clear explanation of how ferromagnets achieve their unique magnetic properties came to light. The electron carries an intrinsic electric charge and intrinsic angular momentum. Use of this property in a device was achieved in 1998 when Fert and Gru¨nberg independently found that the resistance of FM/NM/FM trilayer depended on the angle between the magnetization of the two layers. This phenomena which is called giant magnetoresistance (GMR) brought spin transfer into mainstream. This new discovery created a brand new research fi called “spintronics” or “spin based electronics” which exploits the intrinsic spin of electron.
As expected spintronics delivered a new generation of magnetic devices which are currently used in magnetic disk drives and magnetic random access memories (MRAM). The potential advantages of spintronics devices are non-volatility, higher speed, increased data density and low power consumption. GMR devices are already used in industry as magnetic memories and read heads.
The quality of GMR devices can be increased by developing new magnetic materials and also by going down to nanoscale. The desired characteristic properties of these new materials are higher spin polarization, higher curie temperature and better spin filtering. Half-metals are a good candidate for these devices since they are expected to have high polarization. Some examples of half-metals are Half-Heusler alloy, full Heusler alloy and Perovskite or double Perovskite oxides. The devices discussed in this thesis have NiMnSb half-Heusler alloy and permalloy as the ferromagnetic layers separated by Cu as the nonmagnetic layer.
This dissertation includes mainly two parts, fabrication and characterization of nan- opillars. The layer stack used for the fabrication is Ru/Py/Cu/NiMnSb which is grown on an InP substrate with an (In,Ga)As buff by molecule beam epitaxy (MBE). A new method of fabrication using metal mask which has a higher yield of working samples over the previous method (using the resist mask) used in our group is discussed in detail. Also, the advantages of this new method and draw backs of the old method are explained thoroughly (in chapter 3).
The second part (chapters 4 and 5) is focused on electrical measurements and charac- terization of the nanopillar, specially with regard to GMR and spin-transfer torque (STT)
measurements. In chapter 4, the results of current perpendicular the plane giant mag- netoresistance (CPP-GMR) measurements at various temperatures and in-plane magnetic fi are presented. The dependence of CPP-GMR on bias current and shape anisotropy of the device are investigated. Results of these measurements show that the device has strong shape anisotropy.
The following chapter deals with spin-transfer torque induced magnetic switching measurements done on the device. Critical current densities are on the order of 106 A/cm2, which is one order of magnitude smaller than the current industry standards. Our results show that the two possible magnetic configurations of the nanopillar (parallel and anti-parallel) have a strong dependence on the applied in-plane magnetic fi Fi- nally, four magnetic fi regimes based on the stability of the magnetic configuration (P stable, AP stable, both P and AP stable, both P and AP unstable) are identified.