Refine
Has Fulltext
- yes (14) (remove)
Is part of the Bibliography
- yes (14)
Year of publication
- 2016 (14) (remove)
Document Type
- Doctoral Thesis (14) (remove)
Keywords
- Topologischer Isolator (4)
- Quantenpunkt (3)
- Einzelphotonenemission (2)
- Heterostruktur (2)
- Molekularstrahlepitaxie (2)
- Nanodraht (2)
- Optischer Resonator (2)
- RHEED (2)
- AFM (1)
- ARPES (1)
Institute
- Physikalisches Institut (14) (remove)
Festkörperbasierte Einzelphotonenquellen als Grundbausteine der Quanteninformationstechnologie
(2016)
Die vorliegende Arbeit hatte das Ziel basierend auf Halbleiternanostrukturen eine effiziente und skalierbare Quelle einzelner und ununterscheidbarer Photonen zu entwickeln. Dies ist eine Basiskomponente von zukünftigen quantenphysikalischen Anwendungen wie der Quantenkommunikation oder dem Quantencomputer. Diese Konzepte nutzen gezielt quantenmechanische Systeme um einerseits Kommunikation absolut abhörsicher zu machen oder um neuartige Computer zu konstruieren, die bestimmte Aufgaben - wie die Produktzerlegung großer Zahlen - effizienter lösen als heutige Systeme. Ein mögliche Realisierung der Quantenkommunikation ist beispielsweise die Schlüsselverteilung zwischen zwei Parteien durch Verwendung des BB84-Protokolls. Dazu wird eine Lichtquelle benötigt, welche die physikalisch kleinstmögliche Lichtmenge - ein einzelnes Photon - aussendet. Der Kommunikationskanal wird dann über verschiedene Polarisationszustände dieser Photonen gegen ein Abhören nach außen hin abgesichert. Da die maximale Kommunikationsdistanz aufgrund von Verlusten im Quantenkanal beschränkt ist, muss das Signal für größere Distanzen mit Hilfe eines sog. Quantenrepeaters aufbereitet werden. Ein solcher kann ebenfalls unter Verwendung von Einzelphotonenquellen realisiert werden. Das Konzept des Quantenverstärkers stellt aber die zusätzliche Anforderung an die Einzelphotonenquelle, dass die ausgesendeten Lichtteilchen in der Summe ihrer Eigenschaften wie Energie und Polarisation immer gleich und somit ununterscheidbar sein müssen.
Auf Basis solcher ununterscheidbarer Photonen gibt es zudem mit dem linear optischen Quantenrechner auch mögliche theoretische Ansätze zur Realisierung eines Quantencomputers. Dabei kann über die Quanteninterferenz von ununterscheidbaren Photonen an optischen Bauteilen wie Strahlteilern ein Quanten-NOT-Gatter zur Berechnung spezieller Algorithmen realisiert werden.
Als vielversprechende Kandidaten für eine solche Lichtquelle einzelner Photonen haben sich in den letzten Jahren Halbleiter-Quantenpunkte herauskristallisiert. Dank des festkörperbasierten Ansatzes können diese Strukturen in komplexe photonische Umgebungen zur Erhöhung der Photonen-Extraktionseffizienz und -Emissionsrate eingebettet werden. Ziel dieser Arbeit war somit eine effiziente Quelle einzelner ununterscheidbarer Photonen zu realisieren. Im Hinblick auf die spätere Anwendbarkeit wurde der Fokus zudem auf die skalierbare bzw. deterministische Fabrikation der Quantenpunkt-Strukturen gelegt und zwei technologische Ansätze - die kryogene in-situ-Lithographie und das positionierte Wachstum von Quantenpunkten - untersucht.
Im ersten experimentellen Kapitel dieser Arbeit wird ein neuartiges Materialsystem vorgestellt, welches sich zur Generation einzelner Photonen eignet. Es können spektral scharfe Emissionslinien mit Linienbreiten bis knapp über 50 µeV aus Al$_{0,48}$In$_{0,52}$As Volumenmaterial beobachtet werden, wenn diese Schicht auf InP(111) Substraten abgeschieden wird. In Querschnitt-Rastertunnelmikroskopie-Messungen wurden ca. 16 nm große Cluster, welche eine um ungefähr 7 % höhere Indiumkonzentration im Vergleich zur nominellen Zusammensetzung des Volumenmaterials besitzen, gefunden. Über die Simulation dieser Strukturen konnten diese als Quelle der spektral scharfen Emissionslinien identifiziert werden. Zudem wurde mittels Auto- und Kreuzkorrelationsmessungen nachgewiesen, dass diese Nanocluster einzelne Photonen emittieren und verschieden geladene exzitonische und biexzitonische Ladungsträgerkomplexe binden können.
Anschließend wurde der Fokus auf InGaAs-Quantenpunkte gelegt und zunächst im Rahmen einer experimentellen und theoretischen Gemeinschaftsarbeit die Kohärenzeigenschaften eines gekoppelten Quantenpunkt-Mikrokavität-Systems untersucht. Über temperaturabhängige Zwei-Photonen Interferenz Messungen und dem Vergleich mit einem mikroskopischen Modell des Systems konnten gezielt die Bestandteile der Quantenpunkt-Dephasierung extrahiert werden. Auf diesen Ergebnissen aufbauend wurde die gepulste, strikt resonante Anregung von Quantenpunkten als experimentelle Schlüsseltechnik etabliert. Damit konnten bei tiefen Temperaturen nahezu vollständig ununterscheidbare Photonen durch eine Zwei-Photonen Interferenz Visibilität von über 98 % nachgewiesen werden.
Für ein skalierbares und deterministisches Quantenpunkt-Bauelement ist entweder die Kontrolle über die Position an welcher der Quantenpunkt gewachsen wird nötig, oder die Position an der eine Mikrokavität geätzt wird muss auf die Position eines selbstorganisiert gewachsenen Quantenpunktes abgestimmt werden. Im weiteren Verlauf werden Untersuchungen an beiden technologischen Ansätzen durchgeführt.
Zunächst wurde der Fokus auf positionierte Quantenpunkte gelegt. Mittels in das Substrat geätzter Nanolöcher wird der Ort der Quantenpunkt-Nukleation festgelegt. Durch die geätzten Grenzflächen in Quantenpunkt-Nähe entstehen jedoch auch Defektzustände, die negativen Einfluss auf die Kohärenz der Quantenpunkt-Emission nehmen. Deshalb wurde an diesem Typus von Quantenpunkten die strikt resonante Anregung etabliert und zum ersten Mal die kohärente Kopplung des Exzitons an ein resonantes Lichtfeld demonstriert. Zudem konnte die deterministische Kontrolle der Exzitonbesetzung über den Nachweis einer Rabi-Oszillation gezeigt werden.
Abschließend wird das Konzept der kryogenen in-situ-Lithographie vorgestellt. Diese erlaubt die laterale Ausrichtung der Mikrokavität an die Position eines selbstorganisiert gewachsenen Quantenpunktes. Damit konnte gezielt die Emission eines zuvor ausgewählten, spektral schmalen Quantenpunktes mit nahezu 75 % Gesamteffizienz eingesammelt werden. Die Ununterscheidbarkeit der Quantenpunkt-Photonen war dabei mit einer Zwei-Photonen Interferenz Visibilität von bis zu $\nu=(88\pm3)~\%$ sehr hoch. Damit wurde im Rahmen dieser Arbeit eine Einzelphotonenquelle realisiert, aus der sich sehr effizient kohärente Photonen auskoppeln lassen, was einen wichtigen Schritt hin zur deterministischen Fabrikation von Lichtquellen für quantenphysikalischen Anwendungen darstellt.
> In oxidischen Heterostrukturen kann es zur Ausbildung unerwarteter elektronischer und magnetischer Phasen kommen. Ein bekanntes Beispiel ist das Heterostruktursystem LaAlO\(_3\)/SrTiO\(_3\), an dessen Grenzfläche ein zweidimensionalen Elektronensystem (2DES) entsteht, sofern die LaAlO\(_3\)-Filmdicke einen kritischen Wert von mindestens vier Einheitszellen aufweist. Ähnliches Verhalten konnte an der Heterostruktur γ-Al\(_2\)O\(_3\)/SrTiO\(_3\) beobachtet werden. Die gemessenen Elektronenbeweglichkeiten und Flächenladungsträgerdichten übertreffen hierbei die in LaAlO\(_3\)/SrTiO\(_3\) um mehr als eine Größenordnung. Die vorliegende Arbeit beschäftigt sich mit der Herstellung sowie der Analyse dieser beiden Heterostruktursysteme. Die Hauptaspekte sind dabei die Untersuchung der physikalischen Eigenschaften an der Grenzfläche sowie das Verständnis der zugrundeliegenden Mechanismen.
>
> Im Hinblick auf das Wachstum wird demonstriert, dass die für LaAlO\(_3\)/SrTiO\(_3\) etablierte Wachstumsroutine der gepulsten Laserablation sowie die zur Überwachung des Schichtwachstums verwendete Methode der Beugung hochenergetischer Elektronen in Reflexion (RHEED) für das γ-Al\(_2\)O\(_3\)-Wachstum modifiziert werden müssen. So kann gezeigt werden, dass durch eine geeignete Variation der Wachstumsgeometrie die Resonanz von Oberflächenwellen, welche im Falle des γ-Al\(_2\)O\(_3\)-Wachstums die Beobachtung von RHEED-Oszillationen erschwert, vermieden werden kann und somit auch hier die Überwachung des heteroepitaktischen Schichtwachstum mittels Elektronenbeugung möglich wird.
>
> Für die Ausbildung des 2DES in LaAlO\(_3\)/SrTiO\(_3\) wird das Szenario der elektronischen Rekonstruktion als mögliche Ursache diskutiert, wonach das divergierende Potential innerhalb des polaren LaAlO\(_3\)-Films durch einen Ladungstransfer von der Probenoberfläche in die obersten Atomlagen des unpolaren SrTiO\(_3\)-Substrats kompensiert wird. Zudem sind die Eigenschaften der Heterostruktur von den Wachstumsparametern abhängig. So wird in der vorliegenden Arbeit eine deutliche Zunahme der Ladungsträgerkonzentration und der räumliche Ausdehnung der leitfähigen Schicht insbesondere für Proben, welche bei sehr niedrigen Sauerstoffhintergrunddrücken gewachsen wurden, gezeigt und auf die Erzeugung von Sauerstofffehlstellen innerhalb des Substrats zurückgeführt. Darüber hinaus wird erstmalig die Herstellung atomar scharfer Grenzflächen mit sehr geringer Defektdichte selbst bei sehr niedrigen Wachstumsdrücken belegt und erstmals auch direkt elektronenmikroskopisch nachgewiesen. Es werden allenfalls vernachlässigbare Effekte der Sauerstoffkonzentration auf charakteristische, strukturelle Merkmale der Probe beobachtet. Desweiteren zeigt diese Arbeit erstmalig eine von den Wachstumsbedingungen abhängige Gitterverzerrung des Films, was in Übereinstimmung mit Rechnungen auf Basis der Dichtefunktionaltheorie einen Hinweis auf ein komplexes Zusammenspiel von elektronischer Rekonstruktion, Sauerstofffehlstellen an der LaAlO\(_3\)-Oberfläche und einer Verzerrung der Kristallstruktur als Ursache für die Entstehung des 2DES in LaAlO\(_3\)/SrTiO\(_3\) liefert.
>
> Neben der mikroskopischen Analyse des 2DES in LaAlO\(_3\)/SrTiO\(_3\) wird die elektronische Struktur dieses Systems zudem mithilfe der resonanten inelastischen Röntgenstreuung charakterisiert. Die vorliegende Dissertation zeigt dabei, neben dem Nachweis lokalisierter Ladungsträger vor dem Einsetzen metallischen Verhaltens ab einer kritischen Schichtdicke von vier Einheitszellen, die Existenz eines Raman- und eines fluoreszenzartigen Signals in Abhängigkeit der verwendeten Photonenenergie, was wiederum auf einen unterschiedlichen elektronischen Charakter im Zwischenzustand zurückgeführt werden kann. Gestützt wird diese Interpretation durch vergleichbare Messungen an γ- Al\(_2\)O\(_3\)/SrTiO\(_3\). In diesem System finden sich zudem ebenfalls Anzeichen lokalisierter Ladungsträger unterhalb der kritischen Schichtdicke für metallisches Verhalten, was ein Hinweis auf einen mit LaAlO\(_3\)/SrTiO\(_3\) vergleichbaren Grundzustand sein könnte.
>
> Weitere Messungen mithilfe der resonanten Photoelektronenspektroskopie ermöglichen zudem eine direkte Beobachtung und Analyse der Ti 3d-Valenzelektronen. Messungen an LaAlO\(_3\)/SrTiO\(_3\) und γ-Al\(_2\)O\(_3\)/SrTiO\(_3\) liefern dabei Hinweise auf verschiedene elektronische Ti 3d-artige Zustände. Diese werden zum einen den mobilen Ladungsträgern des 2DES zugeschrieben, zum anderen als lokalisierte Elektronen in der Nähe von Sauerstofffehlstellen identifiziert. Eine Analyse des Resonanzverhaltens sowie der spektralen Form der beobachteten Signale zeigt quantitative Unterschiede, was auf einen unterschiedlichen treibenden Mechanismus in beiden Systemen hindeutet und im Hin- blick auf den Einfluss von Sauerstofffehlstellen auf das System diskutiert wird. Zudem zeigen impulsaufgelöste Messungen der Zustände am chemischen Potential eine unterschiedliche Intensitätsverteilung im k -Raum. Dies wird im Zusammenhang mit Matrixelementeffekten diskutiert und kann vermutlich auf Photoelektronendiffraktion bedingt durch die unterschiedliche Kristallstruktur des Filmmaterials, zurückgeführt werden.
The present work addressed the influence of spins on fundamental processes in organic
semiconductors. In most cases, the role of spins in the conversion of sun light
into electricity was of particular interest. However, also the reversed process, an electric
current creating luminescence, was investigated by means of spin sensitive measurements.
In this work, many material systems were probed with a variety of innovative
detection techniques based on electron paramagnetic resonance spectroscopy.
More precisely, the observable could be customized which resulted in the experimental
techniques photoluminescence detected magnetic resonance (PLDMR), electrically
detected magnetic resonance (EDMR), and electroluminescence detected magnetic
resonance (ELDMR). Besides the commonly used continuous wave EPR spectroscopy,
this selection of measurement methods yielded an access to almost all intermediate
steps occurring in organic semiconductors during the conversion of light into electricity
and vice versa. Special attention was paid to the fact that all results were applicable
to realistic working conditions of the investigated devices, i.e. room temperature application and realistic illumination conditions.
Molecular Beam Epitaxy and Characterization of Bi-Based V\(_2\)VI\(_3\) Topological Insulators
(2016)
The present thesis is addressed to the growth and characterization of Bi-based V2VI3 topological insulators (TIs). The TIs were grown by molecular beam epitaxy (MBE) on differently passivated Si(111) substrates, as well as InP(111) substrates. This allows the study of the influence of the substrate on the structural and electrical properties of the TIs.
The Bi2Se3 layers show a change of mosaicity-tilt and -twist for growth on the differently prepared Si(111) substrates, as well as a significant increase of crystalline quality for growth on the lateral nearly lattice matched InP(111). The rocking curve FWHMs observed for thick layers grown on InP are comparable to these of common zincblende layers, which are close to the resolution limit of standard high resolution X-ray diffraction (HRXRD) setups. The unexpected high structural crystalline quality achieved in this material system is remarkable due to the presence of weak van der Waals bonds between every block of five atomic layers, i.e. a quintuple layer (QL), in growth direction.
In addition to the mosaicity also twin domains, present in films of the V2VI3 material system, are studied. The twin defects are observed in Bi2Se3 layers grown on Si(111) and lattice matched InP(111) suggesting that the two dimensional surface lattice of the substrates can not determine the stacking order ABCABC... or ACBACB... in locally separated growth seeds. Therefore the growth on misoriented and rough InP(111) is analyzed.
The rough InP(111) with its facets within a hollow exceeding the height of a QL is able to provide its stacking information to the five atomic layers within a QL. By varying the roughness of the InP substrate surface, due to thermal annealing, the influence on the twinning within the layer is confirmed resulting in a complete suppression of twin domains on rough InP(111).
Focusing on the electrical properties of the Bi2Se3 films, the increased structural quality for films grown on lattice matched flat InP(111)B results in a marginal reduction of carrier density by about 10% compared to the layers grown on H-passivated Si(111), whereas the suppression of twin domains for growth on rough InP(111)B resulted in a reduction of carrier density by an order of magnitude. This implies, that the twin domains are a main crystal defect responsible for the high carrier density in the presented Bi2Se3 thin films.
Besides the binary Bi2Se3 also alloys with Sb and Te are fabricated to examine the influence of the compound specific point defects on the carrier density. Therefore growth series of the ternary materials Bi2Te(3-y)Se(y), Bi(2-x)Sb(x)Se3, and Bi(2-x)Sb(x)Te3, as well as the quaternary Bi(2-x)Sb(x)Te(3-y)Se(y) are studied.
To further reduce the carrier density of twin free Bi2Se3 layers grown on InP(111)B:Fe a series of Bi(2-x)Sb(x)Se3 alloys were grown under comparable growth conditions. This results in a reduction of the carrier density with a minimum in the composition range of about x=0.9-1.0.
The Bi(2-x)Sb(x)Te3 alloys exhibit a pn-transition, due to the dominating n-type and p-type point defects in its binary compounds, which is determined to reduce the bulk carrier density enabling the study the TI surface states. This pn-transition plays a significant role in realizing predicted applications and exotic effects, such as the quantum anomalous Hall effect.
The magnetic doping of topological insulators with transition metals is studied by incorporating Cr and V in the alloy Bi(2-x)Sb(x)Te3 by codeposition. The preferential incorporation of Cr on group-V sites is confirmed by EDX and XRD, whereas the incorporation of Cr reduces the crystalline quality of the layer. Magnetotransport measurements of the Cr-doped TIs display an anomalous Hall effect confirming the realization of a magnetic TI thin film. The quantum anomalous Hall effect is observed in V-doped Bi(2-x)Sb(x)Te3, where the V-doping results in higher Curie temperatures, as well as higher coercive fields compared to the Cr-doping of the TIs.
Moreover the present thesis contributes to the understanding of the role of the substrate concerning the crystalline quality of van der Waals bonded layers, such as the V2VI3 TIs, MoS2 and WoTe2. Furthermore, the fabrication of the thin film TIs Bi(2-x)Sb(x)Te(3-y)Se(y) in high crystalline quality serves as basis to explore the physics of topological insulators.
A novel growth method has been developed, allowing for the growth of strained HgTe shells on CdTe nanowires (NWs). The growth of CdTe-HgTe core-shell NWs required high attention in controlling basic parameters like substrate temperature and the intensity of supplied material fluxes. The difficulties in finding optimized growth conditions have been successfully overcome in this work.
We found the lateral redistribution of liquid growth seeds with a ZnTe growth start to be crucial to trigger vertical CdTe NW growth. Single crystalline zinc blende CdTe NWs grew, oriented along [111]B. The substrate temperature was the most critical parameter to achieve straight and long wires. In order to adjust it, the growth was monitored by reflection high-energy electron diffraction, which was used for fine tuning of the temperature over time in each growth run individually. For optimized growth conditions, a periodic diffraction pattern allowed for the detailed analysis of atomic arrangement on the surfaces and in the bulk. The ability to do so reflected the high crystal quality and ensemble uniformity of our CdTe NWs. The NW sides were formed by twelve stable, low-index crystalline facets. We observed two types stepped and polar sides, separated by in total six flat and non-polar facets.
The high crystalline quality of the cores allowed to grow epitaxial HgTe shells around. We reported on two different heterostructure geometries. In the first one, the CdTe NWs exhibit a closed HgTe shell, while for the second one, the CdTe NWs are overgrown mainly on one side. Scanning electron microscopy and scanning transmission electron microscopy confirmed, that many of the core-shell NWs are single crystalline zinc blende and have a high uniformity. The symmetry of the zinc blende unit cell was reduced by residual lattice strain. We used high-resolution X-ray diffraction to reveal the strain level caused by the small lattice mismatch in the heterostructures. Shear strain has been induced by the stepped hetero-interface, thereby stretching the lattice of the HgTe shell by 0.06 % along a direction oriented with an angle of 35 ° to the interface.
The different heterostructures obtained, were the base for further investigation of quasi-one-dimensional crystallites of HgTe. We therefore developed methods to reliably manipulate, align, localize and contact individual NWs, in order to characterize the charge transport in our samples. Bare CdTe cores were insulating, while the HgTe shells were conducting. At low temperature we found the mean free path of charge carriers to be smaller, but the phase coherence length to be larger than the sample size of several hundred nanometers. We observed universal conductance fluctuations and therefore drew the conclusion, that the trajectories of charge carriers are defined by elastic backscattering at randomly distributed scattering sites. When contacted with superconducting leads, we saw induced superconductivity, multiple Andreev reflections and the associated excess current. Thus, we achieved HgTe/superconductor interfaces with high interfacial transparency.
In addition, we reported on the appearance of peaks in differential resistance at Delta/e for HgTe-NW/superconductor and 2*Delta/e for superconductor/HgTe-NW/superconductor junctions, which is possibly related to unconventional pairing at the HgTe/superconductor interface. We noticed that the great advantage of our self-organized growth is the possibility to employ the metallic droplet, formerly seeding the NW growth, as a superconducting contact. The insulating wire cores with a metallic droplet at the tip have been overgrown with HgTe in a fully in-situ process. A very high interface quality was achieved in this case.
Ziel dieser Arbeit war die Reduktion des Modenvolumens in Mikrokavitäten. Ein klei-nes Modenvolumen ist für die Stärke der Licht-Materie-Wechselwirkung wesentlich, weil dadurch z.B. die Schwelle für kohärente Lichtemission gesenkt werden kann [1]. Der Purcell-Faktor, ein Maß für die Rate der spontanen Emission, wird durch ein mi-nimales Modenvolumen maximiert [2, 3]. Im Regime der starken Kopplung steigt mit Abnahme des Modenvolumens die Rabi-Aufspaltung und damit die maximale Tempe-ratur, bei der das entsprechende Bauteil funktioniert [4, 5]. Spektrale Eigenschaften treten deutlicher hervor und machen die Funktion der Struktur stabiler gegenüber stö-renden Einflüssen.
Der erste Ansatz, das Modenvolumen einer Mikrokavität zu reduzieren, zielte darauf, die Eindringtiefe der optischen Mode in die beiden Bragg-Spiegel einer Mikrokavität zu minimieren. Diese hängt im Wesentlichen vom Kontrast der Brechungsindizes der alternierenden Schichten eines Bragg-Spiegels ab. Ein maximaler Kontrast kann durch alternierende Schichten aus Halbleiter und Luft erreicht werden. Theoretisch kann auf diese Weise das Modenvolumen in vertikaler Richtung um mehr als einen Faktor 6 im Vergleich zu einer konventionellen Galliumarsenid/Aluminiumgalliumarsenid Mikro-kavität reduziert werden. Zur Herstellung dieser Strukturen wurden die aluminiumhal-tigen Schichten einer Galliumarsenid/Aluminiumgalliumarsenid Mikrokavität voll-ständig entfernt und so der Brechungsindexkontrast maximiert. Die Schichtdicken sind dabei entsprechend anzupassen, um weiterhin die Bragg-Bedingung zu erfüllen. Die Herstellung einer freitragenden Galliumarsenid/Luft-Mikrokavität konnte so erfolg-reich demonstriert werden. Die Photolumineszenz der Bauteile weist diskrete Reso-nanzen auf, deren Ursache in der begrenzten lateralen Größe der Strukturen liegt. In leistungsabhängigen Messungen kann durch ausgeprägtes Schwellenverhalten und auf-lösungsbegrenzte spektrale Linienbreiten Laseremission nachgewiesen werden. Wegen der Abhängigkeit der photonischen Resonanz vom genauen Brechungsindex in den freitragenden Schichten eignen sich die vorgestellten Strukturen auch zur Bestimmung von Brechungsindizes. Alternativ kann die photonische Resonanz durch Einbringen verschiedener Gase in die freitragenden Schichten abgestimmt werden. Beides konnte mit Erfolg nachgewiesen werden. Der Nachteil dieses Ansatzes liegt vor allem darin, dass ein elektrischer Betrieb der so gefertigten Strukturen nicht möglich ist. Hier bie-tet der zweite Ansatz eine bestmögliche Lösung.
Das alternative Konzept für den oberen Bragg-Spiegel einer konventionellen Galli-umarsenid/Aluminiumgalliumarsenid Mikrokavität ist das der Tamm-Plasmonen. Der photonische Einschluss wird hier durch einen unteren Bragg-Spiegel und einem dün-nen oberen Metallspiegel erreicht. An der Grenzfläche vom Halbleiter zum Metall bil-den sich die optischen Tamm-Plasmonen aus. Dabei kann der Metallspiegel gleichzei-tig auch als elektrischer Kontakt genutzt werden. Die Kopplung von Quantenfilm-Exzitonen an optische Tamm-Plasmonen wird in dieser Arbeit erfolgreich demons-triert. Im Regime der starken Kopplung wird mittels Stark-Effekt eine vollständige elektro-optische Verstimmung, d.h. vom Bereich positiver bis hin zur negativen Ver-stimmung, des Quantenfilm-Exzitons gegenüber der Tamm-Plasmonen Mode nachge-wiesen. Die Messungen bestätigen entsprechend des reduzierten Modenvolumens (Faktor 2) eine erhöhte Rabi-Aufspaltung. Dabei sind die spektrale Verschiebung und die Oszillatorstärke des Quantenfilm-Exzitons konsistent mit der Theorie und mit Li-teraturwerten. Der wesentliche Nachteil des Ansatzes liegt in der maximalen Güte, die durch den großen Extinktionskoeffizienten des Metallspiegels limitiert ist.
Neue Erkenntnisse über elektronische Eigenschaften von Festkörpern legen den Grundstein für innovative Anwendungen der Zukunft. Von zentraler Bedeutung sind insbesondere die Eigenschaften der Elektronenspins. Um diese besser zu verstehen, befasst sich die vorliegende Arbeit mit der experimentellen Analyse der elektronischen Struktur von topologischen Isolatoren (Sb$_2$Te$_3$ , Bi$_2$Se$_x$Te$_{3−x}$, Bi$_{1.5}$Sb$_{0.5}$Te$_{1.8}$Se$_{1.2} und Bi$_{1.4}$Sb$_{1.1}$Te$_{2.2}$S$_{0.3}$) und Kristallen mit starker Spin-Bahn-Wechselwirkung (BiTeI) mittels Photoelektronenspektroskopie. Zu Beginn werden die zum Verständnis dieser Arbeit benötigten Grundlagen erklärt sowie die unterschiedlichen zum Einsatz kommenden Techniken eingeführt. Der Hauptteil der Arbeit teilt sich in drei Forschungsschwerpunkte. Der erste Teil befasst sich mit den elektronischen Eigenschaften der Valenzbandstruktur von Sb2Te3 und den auftretenden Oberflächenzuständen. Durch gezielte Variation der Energie der anregenden Strahlung wird der Charakter der Wellenfunktion des topologischen Oberflächenzustands und dessen Wechselwirkung mit Valenzzuständen erforscht. Dabei spielt die Topologie der Volumenbandstruktur eine grundlegende Rolle. Der zusätzliche Vergleich zu Photoemissionsrechnungen ermöglicht detaillierte Einblicke in die Wechselwirkung zwischen Oberflächen- und Volumenzuständen und gibt Aufschluss darüber, wie diese vermittelt werden.
Im zweiten Abschnitt wird durch die Analyse des gemessenen Photoelektronenspins das Zusammenspiel der Spintextur des Grundzustands und Endzuständen in Bi2Te3 untersucht. Dabei treten, im Gegensatz zu Grundzustandsrechnungen, Radialkomponenten des Polarisationsvektors in nichtsymmetrischer Messgeometrie auf. Sowohl deren Energieabhängigkeit als auch deren Auftreten in Photoemissionsrechnungen (1-Schritt-Modell) deutet darauf hin, dass diese ihren Ursprung in Übergangsmatrixelementen des Photoemissionsprozesses haben. Dieses Ergebnis wird mit Spinpolarisationsmessungen am Oberflächenzustand des nicht-topologischen Schichtsystems BiTeI verglichen.
Im dritten Teil werden Auswirkungen unterschiedlicher Manipulationen der untersuchten Materialien auf deren elektronische Eigenschaften beschrieben. Die Adsorption von Bruchteilen einer monoatomaren Lage des Alkalimetalls Caesium auf die Oberfläche des topologischen Isolators Sb2Te3 wird systematisch untersucht. Dadurch kann dessen intrinsische p-Dotierung teilweise abgebaut werden, wobei die Valenzbandstruktur trotz der Reaktivität des Adsorbats intakt bleibt. Des Weiteren werden Auswirkungen von Änderungen der Kristallstöchiometrie durch Volumendotierung vergleichend diskutiert.
Ausblickend befasst sich das Kapitel mit dem Verhalten geringer Mengen ferromagnetischer
Materialen (Fe, Ni) auf den Oberflächen der topologischen Isolatoren. Für die verschiedenen Adsorbate werden Trends aufgezeigt, die von Temperatur und Zusammensetzung des Substratkristalls abhängen.
High-Resolution X-ray Imaging based on a Liquid-Metal-Jet-Source with and without X-ray Optics
(2016)
With increasing miniaturization in industry and medical technology, non-destructive testing techniques are an area of everincreasing importance. In this framework, X-ray microscopy offers an efficient tool for the analysis, understanding and quality assurance of microscopic species, in particular as it allows reconstructing three-dimensional data sets of the whole sample’s volumevia computed tomography (CT).
The following thesis describes the conceptualization, design, construction and characterization of a compact laboratory-based X-ray microscope in the hard X-ray regime around 9 keV, corresponding to a wavelength of 0.134 nm. Hereby, the main focus is on the optimization of resolution and contrast at relatively short exposure times. For this, a novel liquid-metal-jet anode source is the basis. Such only recently commercially available X-ray source reaches a higher brightness than other conventional laboratory sources, i.e. the number of emitted photons (X-ray quanta) per area and solid angle is exceptionally high. This is important in order to reach low exposure times. The reason for such high brightness is the usage of the rapidly renewing anode out of liquid metal which enables an effective dissipation of heat, normally limiting the creation of high intensities on a small area.
In order to cover a broad range of different samples, the microscope can be operated in two
modes. In the “micro-CT mode”, small pixels are realized with a crystal-scintillator and an
optical microscope via shadow projection geometry. Therefore, the resolution is limited by the emitted wavelength of the scintillator, as well as the blurring of the screen. However, samples in the millimeter range can be scanned routinely with low exposure times. Additionally, this mode is optimized with respect to in-line phase contrast, where edges of an object are enhanced and thus better visible.
In the second “nano-CT mode”, a higher resolution can be reached via X-ray lenses. However,
their production process is due to the physical properties of the hard X-ray range - namely high absorption and low diffraction - extremely difficult, leading typically to low performances. In combination with a low brightness, this leads to long exposure times and high requirements in terms of stability, which is one of the key problems of laboratory-based X-ray microscopy. With the here-developed setup and the high brightness of its source, structures down to 150 nm are resolved at moderate exposure times (several minutes per image) and nano-CTs can be obtained.
Viele Forschergruppen konzentrieren sich derzeit auf die Entwicklung von neuartigen Technologien, welche den Weg für die kommerzielle Nutzung einer Quantenkommunikation bereiten sollen. Erste Erfolge konnten dabei insbesondere auf dem Gebiet der Quantenschlüsselverteilung erzielt werden. In diesem Bereich nutzt man die Eigenschaft einzelner, ununterscheidbarer Photonen nicht kopiert werden zu können, um eine abhörsichere Übertragung sensibler Daten zu realisieren. Als Lichtquellen dafür eignen sich Halbleiter-Quantenpunkte. Diese Quantenpunkte lassen sich außerdem leicht in komplexe Halbleiter-Mikrostrukturen integrieren und sind somit besonders interessant für die Entwicklung solch fortschrittlicher Technologien, welche für eine abhörischere Kommunikation notwendig sind. Basierend auf diesem Hintergrund wurden in der vorliegenden Arbeit Halbleiter-Quantenpunkte spektroskopisch hinsichtlich ihres Potentials als Quanten-Lichtquelle für die Quantenkommunikation untersucht. Dabei wurden die Quantenpunkte aus InAs/GaAs und InP/GaInP unter anderem in einem speziellen Verfahren deterministisch positioniert und letztendlich in eine photonische Mikrostruktur integriert, welche aus einer Goldscheibe und einem dielektrischen Spiegel besteht. Als Grundcharakterisierungsmittel kam hauptsächlich die Mikrophotolumineszenzspektroskopie zur Bestimmung der Emissionseigenschaften zum Einsatz. Weiterführend wurden Photonen-Korrelationsmessungen zweiter Ordnung durchgeführt, um den Nachweis einer Quanten-Lichtquelle zu erbringen.
Einfluss eines RTA-Prozesses auf die Emissionseigenschaften von InAs/GaAs-Quantenpunkten
Zur Untersuchung des Einflusses eines Rapid-Thermal-Annealing-Prozesses auf die elektronischen Eigenschaften und die Oszillatorstärke selbstorganisierter InAs/GaAs-Quantenpunkte wurden Mikrophotolumineszenzmessungen an verschiedenen Proben im externen Magnetfeld von bis zu 5 T durchgeführt. Die Quantenpunkte wurden dabei in einem besonderen Verfahren gewachsen, bei dem die nominelle Quantenpunkthöhe durch eine bestimmte Bedeckungsschichtdicke vorgegeben wurde. Insgesamt wurden drei Proben mit Schichtdicken von 2 nm, 3 nm und 4 nm hergestellt, die jeweils nachträglich bei Temperaturen von 750° C bis 850° C für fünf Minuten ausgeheilt wurden. Anhand polarisationsaufgelöster Spektroskopie konnten aus den aufgenommenen Quantenpunktspektren die Zeemanaufspaltung und die diamagnetische Verschiebung extrahiert und damit der effektive Landé g-Faktor sowie der diamagnetische Koeffizient bestimmt werden. Die Auswertung der Zeemanaufspaltung zeigte, dass sowohl höhere Ausheiltemperaturen als auch dickere Bedeckungsschichten zu einer drastischen Abnahme der absoluten g-Faktoren sorgen. Dies lässt darauf schließen, dass eine dickere Bedeckungsschicht zu einer stärkeren Interdiffusion der Atome und einer steigenden Ausdehnung der Quantenpunkte für ex-situ Ausheilprozesse führt. Im Gegensatz dazu steigen die diamagnetischen Koeffizienten der Quantenpunkte mit zunehmender Ausheiltemperatur, was auf eine Ausdehnung der Exzitonwellenfunktion hindeutet. Außerdem wurden mittels zeitaufgelöster Mikrophotolumineszenzspektroskopie die Lebensdauern am Quantenpunktensemble bestimmt und eine Abnahme dieser mit steigender Temperatur festgestellt. Sowohl über die Untersuchungen des diamagnetischen Koeffizienten als auch über die Analyse der Lebensdauer konnte schließlich die Oszillatorstärke der Quantenpunkte ermittelt werden. Beide Messverfahren lieferten innerhalb der Fehlergrenzen ähnliche Ergebnisse. Die höchste Oszillatorstärke \(f_{\chi}=34,7\pm 5,2\) konnte für eine Schichtdicke von d = 3 nm und einer Ausheiltemperatur von 850° C über den diamagnetischen Koeffizienten berechnet werden. Im Falle der Bestimmung über die Lebensdauer ergab sich ein maximaler Wert von \(f_{\tau}=25,7\pm 5,7\). Dies entspricht einer deutlichen Steigerung der Oszillatorstärke im Vergleich zu den Referenzproben um einem Faktor größer als zwei. Des Weiteren konnte eine Ausdehnung der Schwerpunktswellenfunktion der Exzitonen um etwa 70% festgestellt werden. Insgesamt betrachtet, lässt sich durch ex-situ Rapid-Thermal-Annealing-Prozesse die Oszillatorstärke nachträglich deutlich erhöhen, wodurch InAs/GaAs-Quantenpunkte noch interessanter für Untersuchungen im Regime der starken Kopplung werden.
Temperatur- und Leistungsabhängigkeit der Emissionseigenschaften positionierter InAs/GaAs Quantenpunkte
Um einen Einblick in den Ablauf des Zerfallsprozesses eines Exzitons in positionierten Quantenpunkten zu bekommen, wurden temperatur- und leistungsabhängige Messungen durchgeführt. Diese Quantenpunkte wurden in einem speziellen Verfahren deterministisch an vorher definierten Stellen gewachsen. Anhand der Temperaturserien konnten dann Rückschlüsse auf die auftretenden Verlustkanäle in einem Quantenpunkt und dessen Emissionseigenschaften gezogen werden. Dabei wurden zwei dominante Prozesse als Ursache für den Intensitätsabfall bei höheren Temperaturen identifiziert. Die Anhebung der Elektronen im Grundzustand in die umgebende Barriere oder in delokalisierte Zustände in der Benetzungsschicht sorgt für die anfängliche Abnahme der Intensität bei niedrigeren Temperaturen. Der starke Abfall bei höheren Temperaturen ist dagegen dem Aufbruch der exzitonischen Bindung und der thermischen Aktivierung der Ladungsträger in das umgebende Substratmaterial geschuldet. Hierbei lassen sich exemplarisch für zwei verschiedene Quantenpunkte die Aktivierungsenergien \(E_{2A}=(102,2\pm 0,4)\) meV und \(E_{2B}=(163,2\pm 1,3)\) meV bestimmen, welche in etwa den Lokalisierungsenergien der Exzitonen in dem jeweiligen Quantenpunkt von 100 meV bzw. 144 meV entsprechen. Weiterhin deckte die Auswertung des Intensitätsprofils der Exzitonemission die Streuung der Exzitonen an akustischen und optischen Phononen als Hauptursache für die Zunahme der Linienbreite auf. Für hohe Temperaturen dominierte die Wechselwirkung mit longitudinalen optischen Phononen den Verlauf und es konnten für das InAs/GaAs Materialsystem typische Phononenenergien von \(E_{LOA}=(30,9\pm 4,8)\) meV und \(E_{LOB}=(32,2\pm 0,8)\) meV bestimmt werden. In abschließenden Messungen der Leistungsabhängigkeit der Linienbreite wurde festgestellt, dass spektrale Diffusion die inhärente Grenze für die Linienbreite bei niedrigen Temperaturen setzt.
Optische Spektroskopie an positionierten InP/GaInP-Quantenpunkten
Weiterhin wurden positionierte InP/GaInP-Quantenpunkte hinsichtlich der Nutzung als Quanten-Lichtquelle optisch spektroskopiert. Zunächst wurden die Emissionseigenschaften der Quantenpunkte in grundlegenden Experimenten analysiert. Leistungs- und polarisationsabhängige Messungen ließen dabei die Vermutung sowohl auf exzitonische als auch biexzitonische Zerfallsprozesse zu. Weiterhin brachten die Untersuchungen der Polarisation einen ungewöhnlich hohen Polarisationsgrad der Quantenpunktemission hervor. Aufgrund von lokalen Ordnungsphänomenen in der umgebenden GaInP-Matrix wurden im Mittel über 66 Quantenpunkte der Grad der Polarisation von Exziton und Biexziton zu \(p_{Mittel}=(93^{+7}_{-9})\)% bestimmt. Des Weiteren wiesen die Quantenpunkte eine sehr hohe Feinstrukturaufspaltung von \(\Delta_{FSS}^{Mittel}=(300\pm 130)\) µeV auf, welche sich nur durch eine stark anisotrope Quantenpunktform erklären lässt. Durch Auto- und Kreuzkorrelationsmessungen zweiter Ordnung wurden dann sowohl der nicht-klassische Einzelphotonencharakter von Exziton und Biexziton als auch erstmalig für diese Strukturen der kaskadierte Zerfall der Biexziton-Exziton-Kaskade demonstriert. Hierbei wurden \(g^{(2)}(0)\)-Werte von bis 0,08 erreicht. Diese Ergebnisse zeigen das Potential von positionierten InP/GaInP-Quantenpunkten als Grundbausteine für Quanten-Lichtquellen, insbesondere in Bezug auf den Einsatz in der Quantenkommunikation.
Realisierung einer Einzelphotonenquelle auf Basis einer Tamm-Plasmonen-Struktur
Nachdem die vorangegangen Untersuchungen die Eignung der positionierten InP/GaInP-Quantenpunkte als Emitter einzelner Photonen demonstrierten, befasst sich dieser Teil nun mit der Integration dieser Quantenpunkte in eine Tamm-Plasmonen-Struktur zur Realisierung einer effizienten Einzelphotonenquelle. Diese Strukturen bestehen aus einem dielektrischen Spiegel aus 30,5 AlGaAs/AlAs-Schichtpaaren und einer einigen Zehn Nanometer dicken Goldschicht, zwischen denen die Quantenpunkte eingebettet sind. Anhand von Messungen an einer planaren Tamm-Plasmonen-Struktur wurde das Bauteil charakterisiert und neben der Exziton- und Biexzitonemission der Zerfall eines Trions beobachtet, was durch Polarisations- und Korrelationsmessungen nachgewiesen wurde. Um eine Verstärkung der Einzelphotonenemission durch die Kopplung der Teilchen an eine lokalisierte Tamm-Plasmonen-Mode demonstrieren zu können, wurde ein Bereich der Probe mit mehreren Goldscheiben von Durchmessern von 3-6 µm abgerastert und die Lichtintensität aufgenommen. Unterhalb der untersuchten Goldscheiben konnte eine signifikante Erhöhung des Lumineszenzsignals festgestellt werden. Eine quantitative Analyse eines einzelnen Quantenpunktes mittels einer Temperaturserie lieferte dabei eine maximale Emissionsrate von \(\eta_{EPQ}^{Max}=(6,95\pm 0,76)\) MHz und damit eine Effizienz von \((6,95\pm 0,76)\)% solch einer Einzelphotonenquelle unter gepulster Anregung bei 82 MHz. Dies entspricht einer deutlichen Verbesserung der Effizienz im Vergleich zu Quantenpunkten im Volumenmaterial und sogar zu denen in einer planaren DBR-Resonatorstruktur. Positionierte InP/GaInP-Quantenpunkte in einer Tamm-Plasmonen-Struktur bilden somit eine vielversprechende Basis für die Realisierung hocheffizienter Einzelphotonenquellen.