Refine
Has Fulltext
- yes (23)
Is part of the Bibliography
- yes (23) (remove)
Year of publication
Document Type
- Doctoral Thesis (23) (remove)
Language
- English (23) (remove)
Keywords
- Polymere (5)
- 3D-Druck (3)
- Biomaterial (3)
- Hydrogel (3)
- Lithium-Ionen-Akkumulator (3)
- Ringöffnungspolymerisation (3)
- Sol-Gel-Verfahren (3)
- biofabrication (3)
- Nanopartikel (2)
- Poly(2-oxazolin)e (2)
Institute
- Institut für Funktionsmaterialien und Biofabrikation (23) (remove)
Sonstige beteiligte Institutionen
The main focus of this work was to get a deeper understanding of the relationship between the structure of sol-gel films, their densification and their macroscopic cracking. First of all titania was chosen as model system. Therefore a synthesis route starting from the preparation of long-term stable amorphous redissoluble precursor powders based on acetylacetone as chelate ligand was utilized. The solubility and stability of the powders in various solvents can be determined by chemical synthesis and technological parameters. When dissolved in a solvent mixture of ethanol and 1,5-pentanediol, thin films can be easily prepared by dip-coating technique. Thereby the quality of the titania films enormously depends on the calcinations temperature and the solvent mixture is used. In order to investigate the influence of different solvents and solvent mixtures on the microstructure and densification of the precursors, the coating solutions were stripped off (sol powder) and analyzed as function of annealing temperature. It was pointed out that a high densification rate caused by the addition of 1,5-pentanediol, results in dense microstructure with trapped residual carbon. These impurities can retard the phase transformation of anatase to rutile. The analysis of so-called “film powders” scraped off multiple dip-coated substrates provides valuable information on the effect of air moisture and unidirectional densification during drying and aging on the structure of thin films. The high surface-to-volume ratio and access to air moisture determine the chemical composition of the as-prepared film, which controls shrinkage, crystallization and defect structure of the coatings. Further it was shown, that drying as a thin film results in the formation of closed pores and much denser microstructure than the respective sol powder. Without the addition of 1,5-pentanediol all –OEt moieties undergo hydrolysis reactions, which causes the formation of a rigid network. The presence of 1,5-pentanediol retards this hydrolysis reactions and provides some network plasticity. Generally the microstructure of thin films is comparatively close to the microstructure of the film powders. The addition of 1,5-pentandiol prevents hydrolysis and condensation reactions as like in the film powders. However even at 700 °C, thin films never transform to rutile, which was attributed to the tensile stresses in thin films. In thin films and in film powders as well a comparable amount of closed pores are formed during annealing. Further it was shown that most of the thin sol-gel films investigated form a dense crust on their tops during annealing. This explains why crack free films exhibit only closed pores. However, when cracks appear during thin film shrinkage in the coating, this crust is burst, which generates open porosity. The defect density in the coatings was determined by an automated analysis of surface images. The crack formation and quantity can be directly referred to tensile stresses in the coatings, which arise from hydrolysis and condensation during thin film drying and aging. Therefore when 1,5-pentanediol is added to the sol, thin film cracking was avoided, because hydrolysis and condensation reactions are retarded, which preserves a higher network flexibility. Furthermore the crack formation was significantly influenced by the atmospheric humidity that was used during the coating process, which was explained by different drying and condensation rates. Under certain chemical starting conditions water soluble precursor powders can be also obtained. In general the observations made with the water based coating solutions are mostly in agreement with the former results based on ethanol based coating solutions. For example the high surface-to-volume ratio of film powders compared to sol powders also significantly enhances film drying and densification. The addition of 1,5-pentanediol also clearly contributes to their densification behavior and phase evolution. As seen before in the case of ethanol based coatings, 1,5-pentanediol enhances the stability towards hydrolysis and condensation reactions and preserves some network plasticity. Therefore coatings prepared without the addition of 1,5-pentanediol already form cracks during film drying and aging because of tensile stresses. Thus, the addition of 1,5-pentanediol results in a reduction/prevention of crack formation. Nevertheless some differences were observed, i.e. the critical single coating film thickness of ethanol based coatings is nearly twice that of water based coatings. This was explained by the different surface tensions of the basis solvents, which during thin film drying causes significantly higher capillary forces and tensile stresses in water based coatings. When acetylacetone is replaced by triethanolamine as chelating ligand for titanium also re-dissolvable precursor powders can be synthesized. The film powders combine a high hydrolytic stability of the precursor with sufficient intermediate network flexibility. The different type of organics changes the drying and densification behavior: i.e. in contrast to film powders obtained from acetylacetone based precursor powders the structure of triethanolamine based film powders is unaffected by the thin film drying process. This high hydrolytic stability and plasticity of this precursor allows the preparation of defect free coatings up to single film thickness of 300 nm. However triethanolamine based thin films present at intermediary annealing temperatures a distinctively different microstructure compared to acetylacetone based films. The general validity of the conclusions was proved on the basis of zirconia coatings that were also prepared by the use of re-dissolvable precursor powders. In principle all conclusions concerning the interconnection of precursor chemistry, film formation, densification and structure were transferable to the respective zirconia coatings. Differences mainly arise only from differential material properties i.e. bulk density. Finally, it has been pointed out that the findings obtained on the densification behavior of thinsol-gel films are also a valuable tool for improved explanations of other important scientific questions concerning sol-gel films, i.e. scratch resistance of sol-gel coatings, fiber -bridging and – degradation of sol-gel coated fibers.
This work deals with the sintering of multi-material composites. It aims at the establishment of an alternative to the existing complex models for sintering. The development of the associated experimental procedure is also included in this work. The developed material model must be able to predict (i) the sintering kinetics and (ii) the viscous moduli of a material. An experimental approach with free sintering and hot-forging measurements is favoured in this work. The prediction of the sintering kinetics is addressed with the construction of a map of sintering kinetics data: the Master Sintering Diagram (MSD). The MSD is based on a generalized equation for solid-state diffusion, thus is suitable for any thermal activated diffusion. The MSD allows the prediction of sintering kinetics for a large range of temperatures and external loads. A novel approach to the determination of the viscous moduli is developed in this work: the cyclic unloading method. It is a hot-forging measurement (sintering under uniaxial compression) where the applied load is released for short periods. The measurements are carried out with continuous heating, so that the viscous moduli are determined over large ranges of temperatures and densities. The advantage of this method is the measurement of the viscous moduli in anisotropic microstructures. The material model is validated in two steps. Firstly, the predictions of sintering kinetics with the MSD are compared with experimental results: changes of thermal profile and changes of load are predicted with a maximum deviation of 10%. Secondly, the experimentally determined viscous moduli are used for the prediction of a bi-layer curvature using models for warpage from literature. The prediction is qualitatively good for a maximum deviation of 27%. The study of a sintering glass-ceramic tape on a rigid substrate is presented. It shows that this co-sintering problem can be qualitatively investigated with requirement of the material model. The formation of anisotropy intrinsic to the hot-forging experiments is also reported in this work. It appears to be a important point to address in the future for a better understanding of the cosintering.
In the framework of this thesis, new UV-patternable organic-inorganic hybrid polymers with higher refractive indices than reported in the literature for photonic applications were developed and studied with respect to their chemical structure, their optical properties, and their ability of being patterned by 1PP and 2PP. Particularly with 2PP, one could create 3D structures using the novel hybrid materials. The materials were prepared from hydrolysis and polycondensation reactions of · organo-alkoxysilanes and titanium alkoxide precursors, modified with and without CL and organo-alkoxysilanes precursors, and · organo-alkoxysilanes, titanium alkoxide and organophosphorus precursors. The major scope of this work was to increase the refractive index of ORMCER® materials based on only organo-alkoxysilanes. Thus, the parameters which influence the refractive index were investigated thoroughly. In particular, the synthesis parameters such as the introduction of titanium alkoxide and its concentration, the organo-alkoxysilanes, the catalyst concentration, the solvent used, but, also the processing parameters such as, the UV exposure dose, initiator concentration, and developer were investigated.
Starting off with solubility experiments of possible precursors, the present study reveals the whole development of a sol gel processing route for transparent p type semiconductive thin films with delafossite structure right to the fabrication of functional p-n junctions. The versatile sol formulation could successfully be modified for several oxide compositions, enabling the synthesis of CuAlO2, CuCrO2, CuMnO2, CuFeO2 and more. Although several differences in the sintering behaviour of powders and thin films could be observed, the powder experiments significantly contributed to the clearification of the intricate phase development during thermal annealing and also to optimization of the annealing sequence for thin film processing. Two different ternary systems turned out to be the most promising candidates for p-TCO application: Copper aluminum oxide for its high optical transmittance and copper chromium oxide for its low synthesis temperature, which allowed thin film deposition on low-cost borosilicate substrates. In order to combine the advantages of these two systems, the quaternary oxide composition CuAl1-xCrxO2 was investigated. With a higher optical transmittance than CuCrO2, a lower synthesis temperature than CuAlO2 and a lower resistivity than both parent systems, the optimum composition of the quaternary oxide is reached for x = 0.50. Compared to physical vapour deposition techniques, the undoped thin films presented here still need to make up some deficites in their optoelectronic performance. Although the best sol-gel samples are able to compete with RF sputtered samples or sampes deposited by PLD in transmittance, their resistivity is almost two orders of magnitude higher. The most probable reasons for this are the characteristic imperfections of sol-gel thin films like porosity and small crystallite size, which create barriers like grain boundaries and bottlenecks like barely connected particles. By additional effort such shortcomings can be repelled to a certain extend, but nevertheless the density of undoped sol-gel material always stays behind its pendants processed by physical vapour deposition.[246] Furthermore, such additional endeavour is likely to annihilate the advantage of sol-gel technique in processing costs. Extrinsic doping is a common method to decrease the resistivity of delafossite materials. Partially replacing the trivalent cations by divalent ones creates additional holes and thus generates additional charge carriers for p-type semiconductivity. This can improve the conductivity of delafossites by up to three orders of magnitude. Due to the compositorial flexibility of sol-gel processing, dopants could be introduced easily in this study by soluble precursors. However, improving the conductivity of CuAlO2 and CuAl0.5Cr0.5O2 via this method failed. Actually, this seems to be due to the fact that instead of being incorporated into the delafossite phase the dopant ions form intransparent phase impurities like spinels, which interfere with optical transmittance of the thin films. On the contrary, doping had a positive effect on the conductivity and the optical transmittance of copper chromium oxide, with magnesium being the most effective dopant. The resistivity could be decreased by more than three orders of magnitude, but in order to achieve this, much higher Mg concentrations than by other thin film deposition methods were necessary. This indicates a low doping efficiency in sol gel processed thin films, but also the ability of sol gel processing to incorporate more magnesium into the oxide than any other processing method. The extensive substitution of the chromium ions also increases the optical transmittance and allows sol gel processed thin films to draw level with thin films deposited by sputtering methods or PLD. Finally, the applicability of the delafossite thin films was proven by the asymmetric current voltage characteristics of heterojunctions between ITO and the delafossites. Shunting problems of the metallic contacts, on the other hand, reveal structural deficites of the delafossites, which should be the subject of further investigations.
Superparamagnetic nanocomposite microparticles, compromised of magnetite nanoparticles in a silica matrix, have been synthesised and surface-modified to act as adsorbers for substances (e.g. toxic heavy metals or valuable resources) dissolved in fluids like water. The particles can be used for a magnetic-extraction-assisted separation process of these target substances which thereby can be recovered from the fluid.
In the first part of his work, the causes for the sudden degradation of useable capacity of lithium-ion cells have been studied by means of complementary methods such as computed tomography, Post-Mortem studies and electrochemical analyses. The results obtained point unanimously to heterogeneous aging as a key-factor for the sudden degradation of cell capacity, which in turn is triggered by differences in local compression.
At high states of health, the capacity fade rate is moderate but some areas of the graphite electrode degrade faster than others. Still, the localized changes are hardly noticeable on cell level due to averaging effects. Lithium plating occurs first in unevenly compressed areas, creating patterns visible to the human eye. As lithium plating leads to rapid consumption of active lithium, a sudden drop in capacity is observed on cell level. Lithium plating appears to spread out from the initial areas over the whole graphite electrode, quickly consuming the remaining useful lithium and active graphite. It can be hypothesized that a self-amplifying circle of reciprocal acceleration of local lithium loss and material loss causes rapid local degradation.
Battery cell designers can improve cycle life by homogeneous pressure distribution in the cell and using negative active materials that are resilient to elevated discharge potentials such as improved carbons or lithium titanate. Also, a sufficiently oversized negative electrode and suitable electrolyte additives can help to avoid lithium plating. When packs are designed, care must be taken not to exert local pressure on parts of cells and to avoid both very high and low states of charge.
In the second part of this dissertation the resilience of cylindrical and pouchbag cells to shocks and different vibrations was investigated. Stresses inflicted by vibration and shock tests according to the widely recognized UN38.3 transport test were compared to a long-time test that exposed cells to a 186 days long ordeal of sine sweep vibrations with a profile based on real-world applications. All cells passed visual and electric inspection performed by TU München after the vibration tests. Only cylindrical cells subjected to long-term vibrations in axial direction showed an increase in impedance and a loss of capacity that could be recuperated in part.
The detailed analyses presented in this thesis gave more details on the damages inflicted by vibrations and shocks and revealed drastic damages in some cases. In cylindrical cells, only movement in axial direction caused damage. Long term vibrations were found to be especially detrimental.
No damage whatsoever could be detected for pouch cells, regardless of the test protocol and the direction of movement. The extreme resilience of pouchbag cells shows that the electrode stack of lithium-ion cells is resistant to vibrations, and that damages are caused by design imperfections that can be improved at low cost.
The findings of this work, and the general state of research show that it is most crucial to control the lithiation and thus potential of the graphite electrode.
In the last part of this work, a new, direct method for charge estimation based on changing transmission is presented. A correlation between transmission of short ultrasonic pulses and state of charge is found. This new technology allows direct measurement of the state of charge. The method is demonstrated for batteries with different positive active materials, showing its versatility. As the observed changes can be traced to the lithiation of graphite, it can be determined without a reference electrode. Already at this early stage of development, the found correlations allow estimation of state of charge. The present hysteresis in the signal height of the slow wave, which is unneglectable especially during discharging at higher currents, will be subject to further investigation.
The observed effects can be explained by effects on different length scales. Biot’s theory explains the second wave’s slowness based on the active material particles size in the range of 0.01 mm and electrolyte-filled pores. Lithiation of graphite changes the porosity of the electrode and thereby the velocity and wavelength of the impulse. When the wavelength approaches the length scale of the layers, 0.1 mm, scattering effects dampen the transmitted signal. Finally, the wavelength of the pulse should be shorter than the transducers diameter to obtain a homogeneous wave front.
To conclude, the new method allows the control of each individual cell in a pack independent from the electrical connections of the cells.
As the method shows great promise, further studies regarding factors such as long-term behavior, temperature and current rates should be conducted. In this thesis hysteresis was observed and a deeper understanding of the reasons behind it may allow further improvements of measurement precision.
In order to mimic the extracellular matrix for tissue engineering, recent research approaches often involve 3D printing or electrospinning of fibres to scaffolds as cell carrier material. Within this thesis, a micron fibre printing process, called melt electrospinning writing (MEW), combining both additive manufacturing and electrospinning, has been investigated and improved. Thus, a unique device was developed for accurate process control and manufacturing of high quality constructs. Thereby, different studies could be conducted in order to understand the electrohydrodynamic printing behaviour of different medically relevant thermoplastics as well as to characterise the influence of MEW on the resulting scaffold performance.
For reproducible scaffold printing, a commonly occurring processing instability was investigated and defined as pulsing, or in extreme cases as long beading. Here, processing analysis could be performed with the aim to overcome those instabilities and prevent the resulting manufacturing issues. Two different biocompatible polymers were utilised for this study: poly(ε-caprolactone) (PCL) as the only material available for MEW until then and poly(2-ethyl-2-oxazoline) for the first time. A hypothesis including the dependency of pulsing regarding involved mass flows regulated by the feeding pressure and the electrical field strength could be presented. Further, a guide via fibre diameter quantification was established to assess and accomplish high quality printing of scaffolds for subsequent research tasks.
By following a combined approach including small sized spinnerets, small flow rates and high field strengths, PCL fibres with submicron-sized fibre diameters (fØ = 817 ± 165 nm) were deposited to defined scaffolds. The resulting material characteristics could be investigated regarding molecular orientation and morphological aspects. Thereby, an alignment and isotropic crystallinity was observed that can be attributed to the distinct acceleration of the solidifying jet in the electrical field and by the collector uptake. Resulting submicron fibres formed accurate but mechanically sensitive structures requiring further preparation for a suitable use in cell biology. To overcome this handling issue, a coating procedure, by using hydrophilic and cross-linkable star-shaped molecules for preparing fibre adhesive but cell repellent collector surfaces, was used.
Printing PCL fibre patterns below the critical translation speed (CTS) revealed the opportunity to manufacture sinusoidal shaped fibres analogously to those observed using purely viscous fluids falling on a moving belt. No significant influence of the high voltage field during MEW processing could be observed on the buckling phenomenon. A study on the sinusoidal geometry revealed increasing peak-to-peak values and decreasing wavelengths as a function of decreasing collector speeds sc between CTS > sc ≥ 2/3 CTS independent of feeding pressures. Resulting scaffolds printed at 100 %, 90 %, 80 % and 70 % of CTS exhibited significantly different tensile properties, foremost regarding Young’s moduli (E = 42 ± 7 MPa to 173 ± 22 MPa at 1 – 3 % strain). As known from literature, a changed morphology and mechanical environment can impact cell performance substantially leading to a new opportunity of tailoring TE scaffolds.
Further, poly(L-lactide-co-ε-caprolactone-co-acryloyl carbonate) as well as poly(ε-caprolactone-co-acryloyl carbonate) (PCLAC) copolymers could be used for MEW printing. Those exhibit the opportunity for UV-initiated radical cross-linking in a post-processing step leading to significantly increased mechanical characteristics. Here, single fibres of the polymer composed of 90 mol.% CL and 10 mol.% AC showed a considerable maximum tensile strength of σmax = 53 ± 16 MPa. Furthermore, sinusoidal meanders made of PCLAC yielded a specific tensile stress-strain characteristic mimicking the qualitative behaviour of tendons or ligaments. Cell viability by L929 murine fibroblasts and live/dead staining with human mesenchymal stem cells revealed a promising biomaterial behaviour pointing out MEW printed PCLAC scaffolds as promising choice for medical repair of load-bearing soft tissue.
Indeed, one apparent drawback, the small throughput similar to other AM methods, may still prevent MEW’s industrial application yet. However, ongoing research focusses on enlargement of manufacturing speed with the clear perspective of relevant improvement. Thereby, the utilisation of large spinneret sizes may enable printing of high volume rates, while downsizing the resulting fibre diameter via electrical field and mechanical stretching by the collector uptake. Using this approach, limitations of FDM by small nozzle sizes could be overcome. Thinking visionary, such printing devices could be placed in hospitals for patient-specific printing-on-demand therapies one day. Taking the evolved high deposition precision combined with the unique small fibre diameter sizes into account, technical processing of high performance membranes, filters or functional surface finishes also stands to reason.
Several transition metal ions, like Fe2+, Co2+, Ni2+, and Zn2+ complex to the ditopic ligand 1,4-bis(2,2’:6’,2’’-terpyridin-4’-yl)benzene. Due to the high association constant, metal ion induced self-assembly of Fe2+, Co2+, and Ni2+ leads to extended, rigid-rod like metallo-supramolecular coordination polyelectrolytes (MEPEs) even in aqueous solution. Here, the kinetics of coordination and the kinetics of growth of MEPEs are presented. The species in solutions are analyzed by stopped-flow fluorescence spectroscopy, light scattering, viscometry and cryogenic transmission electron microscopy. At near-stoichiometric amounts of the reactants, high molar masses are obtained, which follow the order Ni-MEPE ~ Co-MEPE < Fe-MEPE. Furthermore, a way is presented to adjust the average molar mass, chain-length and viscosity of MEPEs using the monotopic chain stopper 4’-(phenyl)-2,2’:6’,2’’-terpyridine.
The present work aims towards the investigation of polymer degradation under biologically relevant conditions. In order to assess a potential degradation of polymers of interest for biomedical applications in vivo and associated effects on living tissue, representatives of poly(2-oxazoline)s and polypeptoids as well as poly(ethylene glycol) and poly(N-vinylpyrrolidone) for reference purposes are examined regarding their stability under oxidative and hydrolytic conditions as well as towards enzymatic degradation.
The polymers investigated in the framework of this thesis are generally considered to be non-biodegradable. Both poly(ethylene glycol) and poly(N-vinylpyrrolidone) are or were applied intensively in vivo provoking seriously harmful side effects like fatal blood poisoning from the oxidation of poly(ethylene glycol) chain ends or poly(N-vinylpyrrolidone) storage disease. Poly(2-alkyl-2-oxazoline)s and polypeptoids, both promising polymeric biomaterials for a wide variety of in vivo applications, are not clinically applied yet but undergo thorough investigations. However, comprising amide bonds within the backbone or the appending side chain, poly(2-alkyl-2-oxazoline)s and polypeptoids potentially offer a higher susceptibility towards (bio-)degradation. Representing the three most impactful initiators of degradation in vivo, the present study is focused on polymer deterioration by oxidative species, hydrolytic conditions and enzymes.
Oxidative species are generated in a variety of processes in vivo, both on purpose and as an unintentional by-product. Previous investigations revealed the susceptibility of poly(ethylene glycol), poly(N-vinylpyrrolidone), poly(2-alkyl-2-oxazoline)s and polypeptoids to deterioration by hydroxyl radicals deriving from hydrogen peroxide and copper ions. The obtained data confirm previous results of an apparent degradation rate increasing with increasing chain length due to self-inhibitory end group effects for all investigated polymer species. Although the exact concentrations of oxidative species in vivo are very controversial, with respect to their great variety and wide distribution the investigated polymers are likely prone to oxidative deterioration to some extent, with rates, mechanisms and degradation products strongly depending on the respective reactive species, polymer structure and chain length.
Like blood, most tissues of the human body benefit from a slightly alkaline pH value. Nevertheless, specific areas like the human stomach or tumor tissues possess acidic conditions potentially capable to cleave amide bonds comprised by poly(2-alkyl-2-oxazoline)s and polypeptoids. Unlike the hydrolysis of poly(2-alkyl-2-oxazoline)s resulting in side chain cleavage, the hydrolysis of polypeptoids induces backbone scission decreasing the polymer chain length tremendously and releasing, if performed exhaustively, the respective amino acids. Hydrolysis of polysarcosine is monitored by quantification of the released sarcosine via 1H-NMR spectroscopy and determination of the residual Mw via GPC. Its cyclic dimer sarcosine anhydride is formed as an intermediate product in this process via cyclization of unstable linear dimers of sarcosine.
Modification and degradation of bio(macro)molecules is an essential part of human metabolism. Polymers bearing amide bonds and showing a great similarity to natural occurring and widely distributed polypeptides, like poly(2-alkyl-2-oxazoline)s and polypeptoids, bear the potential of an enzymatic biodegradability by (more or less specific) peptidases. Just like the acidic hydrolysis described previously, peptidase activity would result in the cleavage of polymer amide bonds. The aim of the present thesis was to evaluate the stability of poly(2-alkyl-2-oxazoline)s and polypeptoids as well as poly(ethylene glycol) for the sake of reference under circumstances resembling in vivo conditions as closely as possible. Initial experiments focused on the degradation of dye-labeled upon incubation with homogenates of freshly harvested rat liver and kidney. However, although the obtained results are promising for the most part, they are considered rather unreliable and non-reproducible for various reasons. More conclusive data are attained from the incubation of non-labeled polymers in freshly laid chicken eggs. While no evidence for an enzymatic digestion of poly(ethylene glycol) in chicken egg white is found and deterioration of poly(2-methyl-2-oxazoline) upon incubation apparently derives from non-enzymatic hydrolysis, incubated polysarcosine samples reveal distinct elugram patterns depending on the respective C- and N-terminal end groups indicating both exopeptidase and endopeptidase activity. It has to be kept in mind though, that an enzymatic digestibility of polysarcosine does not necessarily imply the digestion of polypeptoids bearing longer side chains by peptidases as well, which should be investigated in further studies.
Aim of this thesis was the development of functionalizable hydrogel coatings for melt electrowritten PCL scaffolds and of bioprintable hydrogels for biofabrication.
Hydrogel coatings of melt electrowritten scaffolds enabled to control the surface hydrophilicity, thereby allowing cell-material interaction studies of biofunctionalized scaffolds in minimal protein adhesive environments. For this purpose, a hydrophilic star- shaped crosslinkable polymer was used and the coating conditions were optimized. Moreover, newly developed photosensitive scaffolds facilitated a time and pH independent biofunctionalization.
Bioprintable hydrogels for biofabrication were based on the allyl-functionalization of gelatin (GelAGE) and modified hyaluronic acid-products, to enable hydrogel crosslinking by means of the thiol-ene click chemistry. Optimization of GelAGE hydrogel properties was achieved through an in-depth analysis of the synthesis parameters, varying Ene:SH ratios, different crosslinking molecules and photoinitiators. Homogeneity of thiol-ene crosslinked networks was compared to free radical polymerized hydrogels and the applicability of GelAGE as bioink for extrusion-based bioprinting was investigated. Purely hyaluronic acid-based bioinks were hypothesized to maintain mechanical- and rheological properties, cell viabilities and the processability, upon further decreasing the overall hydrogel polymer and thiol content.
Hydrogel coatings: Highly structured PCL scaffolds were fabricated with MEW and subjected to coatings with six-armed star-shaped crosslinkable polymers (sP(EO-stat-PO)). Crosslinking results from the aqueous induced hydrolysis of reactive isocyanate groups (NCO) of sP(EO-stat-PO) and increased the surface hydrophilicity and provided a platform for biofunctionalizations in minimal protein adhesive environments. Not only the coating procedure was optimized with respect to sP(EO-stat-PO) concentrations and coating durations, instead scaffold pre-treatments were developed, which were fundamental to enhance the final hydrophilicity to completely avoid unspecific protein adsorption on sP(EO-stat-PO) coated scaffolds. The sP(EO-stat-PO) layer thickness of around 100 nm generally allows in vitro studies not only in dependence on the scaffold biofunctionalization but also on the scaffold architecture. The hydrogel coating extent was assessed via an indirect quantification of the NCO-hydrolysis products. Knowledge of NCO-hydrolysis kinetics enabled to achieve a balance of sufficiently coated scaffolds while maintaining the presence of NCO-groups that were exploited for subsequent biofunctionalizations. However, this time and pH dependent biofunctionalization was restricted to small biomolecules. In order to overcome this limitation and to couple high molecular weight biomolecules another reaction route was developed. This route was based on the photolysis of diazirine moieties and enabled a time and pH independent scaffold biofunctionalization with streptavidin and collagen type I. The fibril formation ability of collagen was used to obtain different collagen conformations on the scaffolds and a preliminary in vitro study demonstrated the applicability to investigate cell-material interactions.
The herein developed scaffolds could be applied to gain deeper insights into the fundamentals of cellular sensing. Especially the complexity by which cells sense e.g. collagen remain to be further elucidated. Therefore, different hierarchies of collagen-like conformations could be coupled to the scaffolds, e.g. gelatin or collagen-derived peptide sequences, and the activation of DDR receptors in dependence on the complexity of the coupled substances could be determined. Due to the strong streptavidin-biotin bond, streptavidin functionalized scaffolds could be applied as a versatile platform to allow immobilization of any biotinylated molecules.
Gelatin-based bioinks: First the GelAGE products were synthesized with respect to molecular weight distributions and amino acid composition integrity. A detailed study was conducted with varying molar ratios of reactants and synthesis durations and implied that gelatin degradation was most dominant for high alkaline synthesis conditions with long reaction times. Gelatin possesses multiple functionalizable groups and the predominant functionalization of amine groups was confirmed via different model substances and analyses. Polymer network homogeneity was proven for the GelAGE system compared to free radical polymerized hydrogels with GelMA. A detailed analysis of hydrogel compositions with varying functional group ratios and UV- or Vis-light photoinitiators was executed. The UV-initiator concentration is restricted due to cytotoxicity and potential cellular DNA damages upon UV-irradiation, whereas the more cytocompatible Vis- initiator system enabled mechanical stiffness tuning over a wide range by controlling the photoinitiator concentration at constant Ene:SH ratios and polymer weight percentages. Versatility of the GelAGE bioink for different AM techniques was proved by exploiting the thermo-gelling behavior of differently degraded GelAGE products for stereolithography and extrusion-based printing. Moreover, the viability of cell-laden GelAGE constructs was demonstrated for extrusion-based bioprinting. By applying different multifunctional thiol-macromolecular crosslinkers the mechanical and rheological properties improved concurrently to the processability. Importantly, lower thiol-crosslinker concentrations were required to yield superior mechanical strengths and physico-chemical properties of the hydrogels as compared to the small bis-thiol-crosslinker. Extrusion-based bioprinting with distinct encapsulated cells underlined the need for individual optimization of cell-laden hydrogel formulations.
Not only the viability of encapsulated cells in extrusion-based bioprinted constructs should be assessed, instead other parameters such as cell morphology or production of collagen or glycosaminoglycans should be considered as these represent some of the crucial prerequisites for cartilage Tissue Engineering applications. Moreover, these studies should be expanded to the stereolithographic approach and ultimately the versatility and cytocompatibility of formulations with macromolecular crosslinkers would be of interest. Macromolecular crosslinkers allowed reducing polymer weight percentages and amounts of thiol groups and are thus expected to contribute to increased cytocompatibility, especially in combination with the more cytocompatible Vis-initiator system, which remains to be elucidated.
Hyaluronic acid-based bioinks: Different molecular weight hyaluronic acid (HA) products were synthesized to bear ene- (HAPA) or thiol-functionalities (LHASH) to enable pure HA thiol-ene crosslinked hydrogels. Depending on the molecular weight of modified HA products, polymer weight percentages and Ene:SH ratios, a wide range of mechanical stiffness was covered. However, the manageability of high molecular weight HA (HHAPA) product solutions (HHAPA + LHASH) was restricted to 5.0 wt.-% as a consequence of the high viscosity. Based on the same HA thiol component (LHASH), hybrid hydrogels of HA with GelAGE were compared to pure HA hydrogels. Although the overall polymer weight percentage of HHAPA + LHASH hydrogels was significantly lowered compared to hybrid hydrogels (GelAGE + LHASH), similar mechanical and physico-chemical properties of pure HA hydrogels were determined with maintained Ene:SH ratios. Low viscous low molecular weight HA precursor solutions (LHAPA + LHASH) prevented the applicability for extrusion-based bioprinting, whereas the non-thermoresponsive HHAPA + LHASH system could be bioprinted with only one-fourth of the polymer content of hybrid formulations. The high viscous behavior of HHAPA + LHASH solutions, lower polymer weight percentages, decreased printing pressures and consequently declined shear stress during printing, were hypothesized to contribute to high cell viabilities in extrusion-based bioprinted constructs compared to the hybrid bioink.
The low molecular weight HA precursor formulation (LHAPA + LHASH) was not applicable for extrusion-based printing, but this system has potential for other AM techniques such as stereolithography. Similar to the GelAGE system a more detailed study on the functions of encapsulated cells would be useful to further develop this system. Moreover, the initiation with the Vis-initiator should be conducted.