Refine
Has Fulltext
- yes (23)
Is part of the Bibliography
- yes (23)
Year of publication
Document Type
- Doctoral Thesis (23) (remove)
Language
- English (23) (remove)
Keywords
- Polymere (5)
- 3D-Druck (3)
- Biomaterial (3)
- Hydrogel (3)
- Lithium-Ionen-Akkumulator (3)
- Ringöffnungspolymerisation (3)
- Sol-Gel-Verfahren (3)
- biofabrication (3)
- Nanopartikel (2)
- Poly(2-oxazolin)e (2)
Institute
- Institut für Funktionsmaterialien und Biofabrikation (23) (remove)
Sonstige beteiligte Institutionen
This work deals with the sintering of multi-material composites. It aims at the establishment of an alternative to the existing complex models for sintering. The development of the associated experimental procedure is also included in this work. The developed material model must be able to predict (i) the sintering kinetics and (ii) the viscous moduli of a material. An experimental approach with free sintering and hot-forging measurements is favoured in this work. The prediction of the sintering kinetics is addressed with the construction of a map of sintering kinetics data: the Master Sintering Diagram (MSD). The MSD is based on a generalized equation for solid-state diffusion, thus is suitable for any thermal activated diffusion. The MSD allows the prediction of sintering kinetics for a large range of temperatures and external loads. A novel approach to the determination of the viscous moduli is developed in this work: the cyclic unloading method. It is a hot-forging measurement (sintering under uniaxial compression) where the applied load is released for short periods. The measurements are carried out with continuous heating, so that the viscous moduli are determined over large ranges of temperatures and densities. The advantage of this method is the measurement of the viscous moduli in anisotropic microstructures. The material model is validated in two steps. Firstly, the predictions of sintering kinetics with the MSD are compared with experimental results: changes of thermal profile and changes of load are predicted with a maximum deviation of 10%. Secondly, the experimentally determined viscous moduli are used for the prediction of a bi-layer curvature using models for warpage from literature. The prediction is qualitatively good for a maximum deviation of 27%. The study of a sintering glass-ceramic tape on a rigid substrate is presented. It shows that this co-sintering problem can be qualitatively investigated with requirement of the material model. The formation of anisotropy intrinsic to the hot-forging experiments is also reported in this work. It appears to be a important point to address in the future for a better understanding of the cosintering.
In order to mimic the extracellular matrix for tissue engineering, recent research approaches often involve 3D printing or electrospinning of fibres to scaffolds as cell carrier material. Within this thesis, a micron fibre printing process, called melt electrospinning writing (MEW), combining both additive manufacturing and electrospinning, has been investigated and improved. Thus, a unique device was developed for accurate process control and manufacturing of high quality constructs. Thereby, different studies could be conducted in order to understand the electrohydrodynamic printing behaviour of different medically relevant thermoplastics as well as to characterise the influence of MEW on the resulting scaffold performance.
For reproducible scaffold printing, a commonly occurring processing instability was investigated and defined as pulsing, or in extreme cases as long beading. Here, processing analysis could be performed with the aim to overcome those instabilities and prevent the resulting manufacturing issues. Two different biocompatible polymers were utilised for this study: poly(ε-caprolactone) (PCL) as the only material available for MEW until then and poly(2-ethyl-2-oxazoline) for the first time. A hypothesis including the dependency of pulsing regarding involved mass flows regulated by the feeding pressure and the electrical field strength could be presented. Further, a guide via fibre diameter quantification was established to assess and accomplish high quality printing of scaffolds for subsequent research tasks.
By following a combined approach including small sized spinnerets, small flow rates and high field strengths, PCL fibres with submicron-sized fibre diameters (fØ = 817 ± 165 nm) were deposited to defined scaffolds. The resulting material characteristics could be investigated regarding molecular orientation and morphological aspects. Thereby, an alignment and isotropic crystallinity was observed that can be attributed to the distinct acceleration of the solidifying jet in the electrical field and by the collector uptake. Resulting submicron fibres formed accurate but mechanically sensitive structures requiring further preparation for a suitable use in cell biology. To overcome this handling issue, a coating procedure, by using hydrophilic and cross-linkable star-shaped molecules for preparing fibre adhesive but cell repellent collector surfaces, was used.
Printing PCL fibre patterns below the critical translation speed (CTS) revealed the opportunity to manufacture sinusoidal shaped fibres analogously to those observed using purely viscous fluids falling on a moving belt. No significant influence of the high voltage field during MEW processing could be observed on the buckling phenomenon. A study on the sinusoidal geometry revealed increasing peak-to-peak values and decreasing wavelengths as a function of decreasing collector speeds sc between CTS > sc ≥ 2/3 CTS independent of feeding pressures. Resulting scaffolds printed at 100 %, 90 %, 80 % and 70 % of CTS exhibited significantly different tensile properties, foremost regarding Young’s moduli (E = 42 ± 7 MPa to 173 ± 22 MPa at 1 – 3 % strain). As known from literature, a changed morphology and mechanical environment can impact cell performance substantially leading to a new opportunity of tailoring TE scaffolds.
Further, poly(L-lactide-co-ε-caprolactone-co-acryloyl carbonate) as well as poly(ε-caprolactone-co-acryloyl carbonate) (PCLAC) copolymers could be used for MEW printing. Those exhibit the opportunity for UV-initiated radical cross-linking in a post-processing step leading to significantly increased mechanical characteristics. Here, single fibres of the polymer composed of 90 mol.% CL and 10 mol.% AC showed a considerable maximum tensile strength of σmax = 53 ± 16 MPa. Furthermore, sinusoidal meanders made of PCLAC yielded a specific tensile stress-strain characteristic mimicking the qualitative behaviour of tendons or ligaments. Cell viability by L929 murine fibroblasts and live/dead staining with human mesenchymal stem cells revealed a promising biomaterial behaviour pointing out MEW printed PCLAC scaffolds as promising choice for medical repair of load-bearing soft tissue.
Indeed, one apparent drawback, the small throughput similar to other AM methods, may still prevent MEW’s industrial application yet. However, ongoing research focusses on enlargement of manufacturing speed with the clear perspective of relevant improvement. Thereby, the utilisation of large spinneret sizes may enable printing of high volume rates, while downsizing the resulting fibre diameter via electrical field and mechanical stretching by the collector uptake. Using this approach, limitations of FDM by small nozzle sizes could be overcome. Thinking visionary, such printing devices could be placed in hospitals for patient-specific printing-on-demand therapies one day. Taking the evolved high deposition precision combined with the unique small fibre diameter sizes into account, technical processing of high performance membranes, filters or functional surface finishes also stands to reason.
Several transition metal ions, like Fe2+, Co2+, Ni2+, and Zn2+ complex to the ditopic ligand 1,4-bis(2,2’:6’,2’’-terpyridin-4’-yl)benzene. Due to the high association constant, metal ion induced self-assembly of Fe2+, Co2+, and Ni2+ leads to extended, rigid-rod like metallo-supramolecular coordination polyelectrolytes (MEPEs) even in aqueous solution. Here, the kinetics of coordination and the kinetics of growth of MEPEs are presented. The species in solutions are analyzed by stopped-flow fluorescence spectroscopy, light scattering, viscometry and cryogenic transmission electron microscopy. At near-stoichiometric amounts of the reactants, high molar masses are obtained, which follow the order Ni-MEPE ~ Co-MEPE < Fe-MEPE. Furthermore, a way is presented to adjust the average molar mass, chain-length and viscosity of MEPEs using the monotopic chain stopper 4’-(phenyl)-2,2’:6’,2’’-terpyridine.
The demand for LIB with enhanced energy densities leads to increased utilization of the space within the confinements of the battery housing or to the use of electrode material with increased intrinsic specific energy densities. Both requirements result in more stress on the battery electrodes and separator during cycling or aging. However, the effect of mechanical strain on the cell’s electrochemistry and thus the performance of batteries is rather unexplored compared to the impact of current or temperature, for example. The objective of this thesis was to give a better understanding of the electrochemical and mechanical interplay in current- and next-generation lithium based battery cells. Therefore, the thesis was structured into the investigations on SoA and next-generation LIBs. For SoA LIBs, the investigations of the interplay started at laboratory scale. Here, the expansion of various electrodes and also the impact of mechanical pressure and its distribution on the performance of the cells were
studied. The investigations at laboratory scale was followed by an examination of the electrochemical and mechanical interactions on large format commercial LIBs which are used in BEVs. Accordingly, the effect of bracing and its effect on the performance was studied in an aging and post-mortem study. To gain a deeper understanding of the mechanical changes in LIBs, an ultrasonic study was performed for pouch cells. Here, the mechanical changes were further investigated in dependence of SoC and SoH. The effects of the mechanical stress on the performance for next-generation batteries were studied at laboratory scale. In the beginning, the expansion of next-generation anode materials such as silicon and lithium was compared with today’s anode materials. Furthermore, the effect of mechanical pressure and electrolyte on the irreversible dilation and performance was investigated for lithium metal cells. Overall, it was shown that pressure has a significant effect on the performance of today’s and also future LIBs. The interplay of the electrochemical and mechanical effects inside a LIB has a considerable impact on the lifetime, capacity fading and impedance increase of the batteries.
While the field of electrochromic (EC) materials and devices (ECDs) continues to advance in terms of color palette and understanding the underlying mechanism, several scientific and technological challenges need to be addressed by optimizing the materials and understanding the electrochemical interplay of these materials in full cells. The main issue here is to further improve the EC profile for color neutrality and cycling stability in order to commercialize dimmable EC products. The transparent conductive substrates used in this work (FTO and ultra-thin ITO glass) have high visible light transmittance (τv > 85%) and low sheet resistance (< 25 Ω·sq-1). In addition, the Li+-containing gel electrolyte has sufficient ionic conductivity (2.8·10-4 S·cm-1 at 25 °C), so the investigated ECDs could achieve a fast response (required ionic conductivity is between 10−3 and 10−7 S·cm-1).
This work shows that the combination of cathodically-coloring Fe-MEPE with anodically-coloring non-stoichiometric nickel oxide (Ni1-xO) electrodes (prepared by the National Institute of Chemistry in Ljubljana, Slovenia) can be used in neutral-coloring type III ECDs. The Fe-MEPE/Ni1-xO ECD with the underbalanced CE (ECD1-1, 2: 1) and the balanced configuration (ECD1-2, 1: 1) are both nearly neutrally-colored (ECD1-1: a* = -6.7, b* = 8.8; ECD1-2: a* = -9.0, b* = 10.1) in the bright state with a τv of almost 70%. Due to the overbalancing of the CE (ECD1-3, 1:3), a deviation (a* = -2.8, b* = 19.9) from the neutral coloration occurred here. The balanced as well as the overbalanced ECD configurations show high electrochemical cycling stability (over 1,000 potentiostatic switching cycles). In general, the overbalanced configuration offers the advantage of a smaller operating voltage range (-1 V ↔ 2.5 V to -1 V ↔ 1.5 V), i.e., avoiding possible electrochemical degradation of the EC materials, electrolyte, or conductive layers. By using a Li RE in the full cell, insights into the optimal matching of electrochemical and optical properties between the two electrodes are obtained to achieve more stable ECDs. Thereby, the redox potentials of both EC electrodes (Fe-MEPE and Ni1-xO) can be measured during operation. The incomplete decolorization of ECD1-1 can be explained by the measured electrode potentials (below the required 4 V vs. Li/Li+), excluding side reactions and degradation at both electrodes. The results demonstrate the importance of using balanced and (slightly) overbalanced ECD configurations with complementary-coloring EC electrodes to achieve high cycling stability and fast switching at low operating voltages. Therefore, this three-electrode configuration provides an excellent method for in situ electrochemical characterization of the individual EC electrodes to better understand the redox processes during device operation and to further improve the optical contrast and cycle stability of ECDs.
The Fe-MEPE/Ni1-xO combination was tested on flexible ultrathin ITO glass (ECD1-4). Here, by applying a low voltage of -1 V ↔ 2.5 V, the MEPE/Ni1-xO ECDs can be reversibly switched from a colored (L* = 35.6, a* = 19.4, b* = -26.7) to a nearly colorless (L* = 78.5, a* = -14.0, b* = 21.3) state. This is accompanied by a change in τv from 6% to 53%. The ECDs exhibit fast response and good cycling stability (5% loss of optical contrast over 100 switching cycles).
To further improve color neutrality and cycling stability, ECDs combining Fe-MEPE and mixed metal oxides as ion storage layers were investigated. Titanium manganese oxide (TMO, Fraunhofer IST) and titanium vanadium oxide (TiVOx, EControl-Glas GmbH & Co. KG) electrodes are compared for use as optically-passive ion storage layers. TiVOx with a maximum charge density of approx. 27 mC·cm-2 and a coloration efficiency of η = 2 cm·C-1 at 584 nm shows a color change from yellow to light gray at 2 V vs. Ag/AgCl, while the slightly anodically-coloring Ti-rich TMO (10.5 mC·cm-², η584 nm = -4 cm·C-1) switches from light yellow to colorless at -2.5 V vs. Ag/AgCl. These materials show only a slight change in τv value from 85% to 75% and from 72% to 81%, respectively, thus reaching the requirements for highly transmissive optical-passive ion storage layers. The ECDs with Fe-MEPE in combination with TiVOx (ECD2-1) and TMO-1 (ECD2-2) are blue-purple in the dark state (0 V) and turn colorless by applying a voltage of 1.5 V, changing the τv value from 28% to 69% and from 21% to 57% in 3 s and 13 s, respectively. The ECDs show fast responses and high cyclability over more than 100 cycles.
In the last section, the simplification of cell architecture by using redox mediators shows that different redox mediators (KHCF(III), Fc-PF6, Fc-BF4, and TMTU) can be used in type II ECDs (4 instead of 5 layers) consisting of Fe-MEPE or Ni1-xO thin film electrodes. The combination of KHCF(III) with Fe-MEPE has a low cycling stability due to the electrochemical formation of Prussian blue (PB). This side reaction is undesirable as it decreases the optical contrast. It can be avoided by using Fc+- (ECD3-5/6) or TMTU-based (ECD3-7) redox mediators, which exhibit reversible redox behavior. A high τv value of 72% is obtained for the use of TMTU. Low concentrations (<0.1 M) of redox mediators decrease the cell voltage for complete switching without affecting the optical properties of the ECDs. The redox couple TMTU/TMFDS2+ (molar ratio of 1:0.1 in 1 M LiClO4/PC as electrolyte) works well in combination with
Ni1-xO electrodes (ECD3-10), with a change in τv value from 38% (colored at 2 V, L* = 67.1, a* = 3.9, b* = 17.2) to 70% at (decolored at -2 V, L* = 86.6, a* = -0.6, b* = 17.2). This result implies that incorporating redox mediators into the electrolyte is an effective means to simplify the cell assembly and color neutrality can be obtained with one optically active WE and a color-neutral redox mediator. Moreover, the combination of Ni1-xO and the colorless TMTU/TMFDS2+ redox mediator is a potential candidate to obtain neutrally colored ECDs.
It is shown that the lab-sized FTO- and ultra-thin ITO-glass-based ECDs are very attractive for energy-efficient EC applications, e.g., in architectural or automotive glazing, aircraft, ships, home appliances and displays. To monitor the EC performance and to prevent diverging electrode potentials during the switching process, the studied three-electrode configuration can help to extend the cycle stability as well as to improve the charge balancing of dimmable applications. The studied ECDs display a route towards neutral tint, e.g., EC active Ni1-xO, optically-inactive mixed metal oxides, and colorless redox mediators. Nevertheless, color neutrality should be further improved to meet the requirements for industrial applications. For future work, a scale-up process from lab-sized (few cm²) to prototype (few m²) ECDs will be necessary.
In the first part of his work, the causes for the sudden degradation of useable capacity of lithium-ion cells have been studied by means of complementary methods such as computed tomography, Post-Mortem studies and electrochemical analyses. The results obtained point unanimously to heterogeneous aging as a key-factor for the sudden degradation of cell capacity, which in turn is triggered by differences in local compression.
At high states of health, the capacity fade rate is moderate but some areas of the graphite electrode degrade faster than others. Still, the localized changes are hardly noticeable on cell level due to averaging effects. Lithium plating occurs first in unevenly compressed areas, creating patterns visible to the human eye. As lithium plating leads to rapid consumption of active lithium, a sudden drop in capacity is observed on cell level. Lithium plating appears to spread out from the initial areas over the whole graphite electrode, quickly consuming the remaining useful lithium and active graphite. It can be hypothesized that a self-amplifying circle of reciprocal acceleration of local lithium loss and material loss causes rapid local degradation.
Battery cell designers can improve cycle life by homogeneous pressure distribution in the cell and using negative active materials that are resilient to elevated discharge potentials such as improved carbons or lithium titanate. Also, a sufficiently oversized negative electrode and suitable electrolyte additives can help to avoid lithium plating. When packs are designed, care must be taken not to exert local pressure on parts of cells and to avoid both very high and low states of charge.
In the second part of this dissertation the resilience of cylindrical and pouchbag cells to shocks and different vibrations was investigated. Stresses inflicted by vibration and shock tests according to the widely recognized UN38.3 transport test were compared to a long-time test that exposed cells to a 186 days long ordeal of sine sweep vibrations with a profile based on real-world applications. All cells passed visual and electric inspection performed by TU München after the vibration tests. Only cylindrical cells subjected to long-term vibrations in axial direction showed an increase in impedance and a loss of capacity that could be recuperated in part.
The detailed analyses presented in this thesis gave more details on the damages inflicted by vibrations and shocks and revealed drastic damages in some cases. In cylindrical cells, only movement in axial direction caused damage. Long term vibrations were found to be especially detrimental.
No damage whatsoever could be detected for pouch cells, regardless of the test protocol and the direction of movement. The extreme resilience of pouchbag cells shows that the electrode stack of lithium-ion cells is resistant to vibrations, and that damages are caused by design imperfections that can be improved at low cost.
The findings of this work, and the general state of research show that it is most crucial to control the lithiation and thus potential of the graphite electrode.
In the last part of this work, a new, direct method for charge estimation based on changing transmission is presented. A correlation between transmission of short ultrasonic pulses and state of charge is found. This new technology allows direct measurement of the state of charge. The method is demonstrated for batteries with different positive active materials, showing its versatility. As the observed changes can be traced to the lithiation of graphite, it can be determined without a reference electrode. Already at this early stage of development, the found correlations allow estimation of state of charge. The present hysteresis in the signal height of the slow wave, which is unneglectable especially during discharging at higher currents, will be subject to further investigation.
The observed effects can be explained by effects on different length scales. Biot’s theory explains the second wave’s slowness based on the active material particles size in the range of 0.01 mm and electrolyte-filled pores. Lithiation of graphite changes the porosity of the electrode and thereby the velocity and wavelength of the impulse. When the wavelength approaches the length scale of the layers, 0.1 mm, scattering effects dampen the transmitted signal. Finally, the wavelength of the pulse should be shorter than the transducers diameter to obtain a homogeneous wave front.
To conclude, the new method allows the control of each individual cell in a pack independent from the electrical connections of the cells.
As the method shows great promise, further studies regarding factors such as long-term behavior, temperature and current rates should be conducted. In this thesis hysteresis was observed and a deeper understanding of the reasons behind it may allow further improvements of measurement precision.
Biofabrication technologies must address numerous parameters and conditions to reconstruct tissue complexity in vitro. A critical challenge is vascularization, especially for large constructs exceeding diffusion limits. This requires the creation of artificial vascular structures, a task demanding the convergence and integration of multiple engineering approaches. This doctoral dissertation aims to achieve two primary objectives: firstly, to implement and refine engineering methods for creating artificial microvascular structures using Melt Electrowriting (MEW)-assisted sacrificial templating, and secondly, to deepen the understanding of the critical factors influencing the printability of bioink formulations in 3D extrusion bioprinting.
In the first part of this dissertation, two innovative sacrificial templating techniques using MEW are explored. Utilizing a carbohydrate glass as a fugitive material, a pioneering advancement in the processing of sugars with MEW with a resolution under 100 microns was made. Furthermore, by introducing the “print-and-fuse” strategy as a groundbreaking method, biomimetic branching microchannels embedded in hydrogel matrices were fabricated, which can then be endothelialized to mirror in vivo vascular conditions.
The second part of the dissertation explores extrusion bioprinting. By introducing a simple binary bioink formulation, the correlation between physical properties and printability was showcased. In the next step, employing state-of-the-art machine-learning approaches revealed a deeper understanding of the correlations between bioink properties and printability in an extended library of hydrogel formulations.
This dissertation offers in-depth insights into two key biofabrication technologies. Future work could merge these into hybrid methods for the fabrication of vascularized constructs, combining MEW's precision with fine-tuned bioink properties in automated extrusion bioprinting.
Aim of this thesis was the development of functionalizable hydrogel coatings for melt electrowritten PCL scaffolds and of bioprintable hydrogels for biofabrication.
Hydrogel coatings of melt electrowritten scaffolds enabled to control the surface hydrophilicity, thereby allowing cell-material interaction studies of biofunctionalized scaffolds in minimal protein adhesive environments. For this purpose, a hydrophilic star- shaped crosslinkable polymer was used and the coating conditions were optimized. Moreover, newly developed photosensitive scaffolds facilitated a time and pH independent biofunctionalization.
Bioprintable hydrogels for biofabrication were based on the allyl-functionalization of gelatin (GelAGE) and modified hyaluronic acid-products, to enable hydrogel crosslinking by means of the thiol-ene click chemistry. Optimization of GelAGE hydrogel properties was achieved through an in-depth analysis of the synthesis parameters, varying Ene:SH ratios, different crosslinking molecules and photoinitiators. Homogeneity of thiol-ene crosslinked networks was compared to free radical polymerized hydrogels and the applicability of GelAGE as bioink for extrusion-based bioprinting was investigated. Purely hyaluronic acid-based bioinks were hypothesized to maintain mechanical- and rheological properties, cell viabilities and the processability, upon further decreasing the overall hydrogel polymer and thiol content.
Hydrogel coatings: Highly structured PCL scaffolds were fabricated with MEW and subjected to coatings with six-armed star-shaped crosslinkable polymers (sP(EO-stat-PO)). Crosslinking results from the aqueous induced hydrolysis of reactive isocyanate groups (NCO) of sP(EO-stat-PO) and increased the surface hydrophilicity and provided a platform for biofunctionalizations in minimal protein adhesive environments. Not only the coating procedure was optimized with respect to sP(EO-stat-PO) concentrations and coating durations, instead scaffold pre-treatments were developed, which were fundamental to enhance the final hydrophilicity to completely avoid unspecific protein adsorption on sP(EO-stat-PO) coated scaffolds. The sP(EO-stat-PO) layer thickness of around 100 nm generally allows in vitro studies not only in dependence on the scaffold biofunctionalization but also on the scaffold architecture. The hydrogel coating extent was assessed via an indirect quantification of the NCO-hydrolysis products. Knowledge of NCO-hydrolysis kinetics enabled to achieve a balance of sufficiently coated scaffolds while maintaining the presence of NCO-groups that were exploited for subsequent biofunctionalizations. However, this time and pH dependent biofunctionalization was restricted to small biomolecules. In order to overcome this limitation and to couple high molecular weight biomolecules another reaction route was developed. This route was based on the photolysis of diazirine moieties and enabled a time and pH independent scaffold biofunctionalization with streptavidin and collagen type I. The fibril formation ability of collagen was used to obtain different collagen conformations on the scaffolds and a preliminary in vitro study demonstrated the applicability to investigate cell-material interactions.
The herein developed scaffolds could be applied to gain deeper insights into the fundamentals of cellular sensing. Especially the complexity by which cells sense e.g. collagen remain to be further elucidated. Therefore, different hierarchies of collagen-like conformations could be coupled to the scaffolds, e.g. gelatin or collagen-derived peptide sequences, and the activation of DDR receptors in dependence on the complexity of the coupled substances could be determined. Due to the strong streptavidin-biotin bond, streptavidin functionalized scaffolds could be applied as a versatile platform to allow immobilization of any biotinylated molecules.
Gelatin-based bioinks: First the GelAGE products were synthesized with respect to molecular weight distributions and amino acid composition integrity. A detailed study was conducted with varying molar ratios of reactants and synthesis durations and implied that gelatin degradation was most dominant for high alkaline synthesis conditions with long reaction times. Gelatin possesses multiple functionalizable groups and the predominant functionalization of amine groups was confirmed via different model substances and analyses. Polymer network homogeneity was proven for the GelAGE system compared to free radical polymerized hydrogels with GelMA. A detailed analysis of hydrogel compositions with varying functional group ratios and UV- or Vis-light photoinitiators was executed. The UV-initiator concentration is restricted due to cytotoxicity and potential cellular DNA damages upon UV-irradiation, whereas the more cytocompatible Vis- initiator system enabled mechanical stiffness tuning over a wide range by controlling the photoinitiator concentration at constant Ene:SH ratios and polymer weight percentages. Versatility of the GelAGE bioink for different AM techniques was proved by exploiting the thermo-gelling behavior of differently degraded GelAGE products for stereolithography and extrusion-based printing. Moreover, the viability of cell-laden GelAGE constructs was demonstrated for extrusion-based bioprinting. By applying different multifunctional thiol-macromolecular crosslinkers the mechanical and rheological properties improved concurrently to the processability. Importantly, lower thiol-crosslinker concentrations were required to yield superior mechanical strengths and physico-chemical properties of the hydrogels as compared to the small bis-thiol-crosslinker. Extrusion-based bioprinting with distinct encapsulated cells underlined the need for individual optimization of cell-laden hydrogel formulations.
Not only the viability of encapsulated cells in extrusion-based bioprinted constructs should be assessed, instead other parameters such as cell morphology or production of collagen or glycosaminoglycans should be considered as these represent some of the crucial prerequisites for cartilage Tissue Engineering applications. Moreover, these studies should be expanded to the stereolithographic approach and ultimately the versatility and cytocompatibility of formulations with macromolecular crosslinkers would be of interest. Macromolecular crosslinkers allowed reducing polymer weight percentages and amounts of thiol groups and are thus expected to contribute to increased cytocompatibility, especially in combination with the more cytocompatible Vis-initiator system, which remains to be elucidated.
Hyaluronic acid-based bioinks: Different molecular weight hyaluronic acid (HA) products were synthesized to bear ene- (HAPA) or thiol-functionalities (LHASH) to enable pure HA thiol-ene crosslinked hydrogels. Depending on the molecular weight of modified HA products, polymer weight percentages and Ene:SH ratios, a wide range of mechanical stiffness was covered. However, the manageability of high molecular weight HA (HHAPA) product solutions (HHAPA + LHASH) was restricted to 5.0 wt.-% as a consequence of the high viscosity. Based on the same HA thiol component (LHASH), hybrid hydrogels of HA with GelAGE were compared to pure HA hydrogels. Although the overall polymer weight percentage of HHAPA + LHASH hydrogels was significantly lowered compared to hybrid hydrogels (GelAGE + LHASH), similar mechanical and physico-chemical properties of pure HA hydrogels were determined with maintained Ene:SH ratios. Low viscous low molecular weight HA precursor solutions (LHAPA + LHASH) prevented the applicability for extrusion-based bioprinting, whereas the non-thermoresponsive HHAPA + LHASH system could be bioprinted with only one-fourth of the polymer content of hybrid formulations. The high viscous behavior of HHAPA + LHASH solutions, lower polymer weight percentages, decreased printing pressures and consequently declined shear stress during printing, were hypothesized to contribute to high cell viabilities in extrusion-based bioprinted constructs compared to the hybrid bioink.
The low molecular weight HA precursor formulation (LHAPA + LHASH) was not applicable for extrusion-based printing, but this system has potential for other AM techniques such as stereolithography. Similar to the GelAGE system a more detailed study on the functions of encapsulated cells would be useful to further develop this system. Moreover, the initiation with the Vis-initiator should be conducted.
The present work aims towards the investigation of polymer degradation under biologically relevant conditions. In order to assess a potential degradation of polymers of interest for biomedical applications in vivo and associated effects on living tissue, representatives of poly(2-oxazoline)s and polypeptoids as well as poly(ethylene glycol) and poly(N-vinylpyrrolidone) for reference purposes are examined regarding their stability under oxidative and hydrolytic conditions as well as towards enzymatic degradation.
The polymers investigated in the framework of this thesis are generally considered to be non-biodegradable. Both poly(ethylene glycol) and poly(N-vinylpyrrolidone) are or were applied intensively in vivo provoking seriously harmful side effects like fatal blood poisoning from the oxidation of poly(ethylene glycol) chain ends or poly(N-vinylpyrrolidone) storage disease. Poly(2-alkyl-2-oxazoline)s and polypeptoids, both promising polymeric biomaterials for a wide variety of in vivo applications, are not clinically applied yet but undergo thorough investigations. However, comprising amide bonds within the backbone or the appending side chain, poly(2-alkyl-2-oxazoline)s and polypeptoids potentially offer a higher susceptibility towards (bio-)degradation. Representing the three most impactful initiators of degradation in vivo, the present study is focused on polymer deterioration by oxidative species, hydrolytic conditions and enzymes.
Oxidative species are generated in a variety of processes in vivo, both on purpose and as an unintentional by-product. Previous investigations revealed the susceptibility of poly(ethylene glycol), poly(N-vinylpyrrolidone), poly(2-alkyl-2-oxazoline)s and polypeptoids to deterioration by hydroxyl radicals deriving from hydrogen peroxide and copper ions. The obtained data confirm previous results of an apparent degradation rate increasing with increasing chain length due to self-inhibitory end group effects for all investigated polymer species. Although the exact concentrations of oxidative species in vivo are very controversial, with respect to their great variety and wide distribution the investigated polymers are likely prone to oxidative deterioration to some extent, with rates, mechanisms and degradation products strongly depending on the respective reactive species, polymer structure and chain length.
Like blood, most tissues of the human body benefit from a slightly alkaline pH value. Nevertheless, specific areas like the human stomach or tumor tissues possess acidic conditions potentially capable to cleave amide bonds comprised by poly(2-alkyl-2-oxazoline)s and polypeptoids. Unlike the hydrolysis of poly(2-alkyl-2-oxazoline)s resulting in side chain cleavage, the hydrolysis of polypeptoids induces backbone scission decreasing the polymer chain length tremendously and releasing, if performed exhaustively, the respective amino acids. Hydrolysis of polysarcosine is monitored by quantification of the released sarcosine via 1H-NMR spectroscopy and determination of the residual Mw via GPC. Its cyclic dimer sarcosine anhydride is formed as an intermediate product in this process via cyclization of unstable linear dimers of sarcosine.
Modification and degradation of bio(macro)molecules is an essential part of human metabolism. Polymers bearing amide bonds and showing a great similarity to natural occurring and widely distributed polypeptides, like poly(2-alkyl-2-oxazoline)s and polypeptoids, bear the potential of an enzymatic biodegradability by (more or less specific) peptidases. Just like the acidic hydrolysis described previously, peptidase activity would result in the cleavage of polymer amide bonds. The aim of the present thesis was to evaluate the stability of poly(2-alkyl-2-oxazoline)s and polypeptoids as well as poly(ethylene glycol) for the sake of reference under circumstances resembling in vivo conditions as closely as possible. Initial experiments focused on the degradation of dye-labeled upon incubation with homogenates of freshly harvested rat liver and kidney. However, although the obtained results are promising for the most part, they are considered rather unreliable and non-reproducible for various reasons. More conclusive data are attained from the incubation of non-labeled polymers in freshly laid chicken eggs. While no evidence for an enzymatic digestion of poly(ethylene glycol) in chicken egg white is found and deterioration of poly(2-methyl-2-oxazoline) upon incubation apparently derives from non-enzymatic hydrolysis, incubated polysarcosine samples reveal distinct elugram patterns depending on the respective C- and N-terminal end groups indicating both exopeptidase and endopeptidase activity. It has to be kept in mind though, that an enzymatic digestibility of polysarcosine does not necessarily imply the digestion of polypeptoids bearing longer side chains by peptidases as well, which should be investigated in further studies.
This thesis investigates different ligand designs for Ru(II) complexes and the activity of the complexes as photosensitizer (PS) in photocatalytic hydrogen evolution. The catalytic system typically contains a catalyst, a sacrificial electron donor (SED) and a PS, which needs to exhibit strong absorption and luminescence, as well as reversible redox behavior. Electron-withdrawing pyridine substituents on the terpyridine metal ion receptor result in an increase of excited-state lifetime and quantum yield (Φ = 74*10-5; τ = 3.8 ns) and lead to complex III-C1 exhibiting activity as PS. While the turn-over frequency (TOFmax) and turn-over number (TON) are relatively low (TOFmax = 57 mmolH2 molPS-1 min-1; TON(44 h) = 134 mmolH2 molPS-1), the catalytic system is long-lived, losing only 20% of its activity over the course of 12 days. Interestingly, the heteroleptic design in III-C1 proves to be beneficial for the performance as PS, despite III-C1 having comparable photophysical and electrochemical properties as the homoleptic complex IV-C2 (TOFmax = 35 mmolH2 molPS-1 min-1; TON(24 h) = 14 mmolH2 molPS-1). Reductive quenching of the excited PS by the SED is identified as rate-limiting step in both cases.
Hence, the ligands are designed to be more electron-accepting either via N-methylation of the peripheral pyridine substituents or introduction of a pyrimidine ring in the metal ion receptor, leading to increased excited-state lifetimes (τ = 9–40 ns) and luminescence quantum yields (Φ = 40–400*10-5). However, the more electron-accepting character of the ligands also results in anodically shifted reduction potentials, leading to a lack of driving force for the electron transfer from the reduced PS to the catalyst. Hence, this electron transfer step is found to be a limiting factor to the overall performance of the PS. While higher TOFmax in hydrogen evolution experiments are observed for pyrimidine-containing PS (TOFmax = 300–715 mmolH2 molPS-1 min-1), the longevity for these systems is reduced with half-life times of 2–6 h.
Expansion of the pyrimidine-containing ligands to dinuclear complexes yields a stronger absorptivity (ε = 100–135*103 L mol-1 cm-1), increased luminescence (τ = 90–125 ns, Φ = 210–350*10-5) and can also result in higher TOFmax given sufficient driving force for electron transfer to the catalyst (TOFmax = 1500 mmolH2 molPS-1 min-1). When comparing complexes with similar driving forces, stronger luminescence is reflected in a higher TOFmax. Besides thermodynamic considerations, kinetic effects and electron transfer efficiency are assumed to impact the observed activity in hydrogen evolution. In summary, this work shows that targeted ligand design can make the previously disregarded group of Ru(II) complexes with tridentate ligands attractive candidates for use as PS in photocatalytic hydrogen evolution.