Since the discovery of spin torque in 1996, independently by Berger and Slonczewski, and given its potential impact on information storage and communication technologies, (e.g. through the possibility of switching the magnetic configuration of a bit by current instead of a magnetic field, or the realization of high frequency spin torque oscillators (STO), this effect has been an important field of spintronics research. One aspect of this research focuses on ferromagnets with low damping. The lower the damping in a ferromagnet, the lower the critical current that is needed to induce switching of a spin valve or induce precession of its magnetization. In this thesis ferromagnetic resonance (FMR) studies of NiMnSb layers are presented along with experimental studies on various spin-torque (ST) devices using NiMnSb. NiMnSb, when crystallized in the half-Heusler structure, is a half-metal which is predicted to have 100% spin polarization, a consideration which further increases its potential as a candidate for memory devices based on the giant magnetoresistance (GMR) effect. The FMR measurements show an outstandingly low damping factor for NiMnSb, in low 10-3 range. This is about a factor of two lower than permalloy and well comparable to lowest damping for iron grown by molecular beam epitaxy (MBE). According to theory the 100% spin polarization properties of the bulk disappear at interfaces where the break in translational symmetry causes the gap in the minority spin band to collapse but can remain in other crystal symmetries such as (111). Consequently NiMnSb layers on (111)(In,Ga)As buffer are characterized in respect of anisotropies and damping. The FMR measurements on these samples indicates a higher damping that for the 001 samples, and a thickness dependent uniaxial in-plane anisotropy. Investigations of the material for device use is pursued by considering sub-micrometer sized elements of NiMnSb on 001 substrates, which were fabricated by electron-beam lithography and measured by ferromagnetic resonance. The damping remains in the low 10-3 range as determined directly by extracting the Gilbert damping from the line width. Additionally magnetostatic modes are observed in arrays of elements, which is further evidence of high material quality of the samples. By sputtering various metals on top of the NiMnSb, spin pumping from the ferromagnet into the non-magnetic layer is investigated. After these material investigations, pseudo-spin-valves using NiMnSb as one of the ferromagnet, in combination with Permalloy were fabricating using a self-aligned lithography process. These samples show a GMR ratio of 3.4% at room temperature and almost double at low temperature, comparing favourably to the best single stack GMR structures reported to date. Moreover, current induced switching measurements show promisingly low current densities are necessary to change the magnetic orientation of the free layer. These current densities compete with state-of-the-art GMR devices for metal based structures and almost with tunnel junction devices. The true potential of these devices however comes to light when they are operated as spin torque oscillators to emit high frequency, tunable, narrow spectrum electromagnetic waves. These Heusler based STOs show an outstanding q-factor of 4180, even when operating in the absence of an external field, a value which bests the highest value in the literature by more than an order of magnitude. While these devices currently still suffer from the same limited output power as all STO reported to date, their sub-micron lateral dimensions make the fabrication of an on-chip array of coupled oscillators, which is a promising path forward towards industrially relevant output power.
In this work the epitaxial growth and characterization of the half-metallic ferromagnet NiMnSb was presented. NiMnSb crystallizes in the C1b structure which is similar to the zinc blende structure from widely used III-V semiconductors. One special property of NiMnSb is the theoretical 100% spin-polarization at the Fermi edge. This makes it a perfect candidate for spintronic experiments and the material of choice for building novel spintronic devices. Another important topic in this work were the magnetic properties of NiMnSb, especially the low magnetic damping of the grown thin films. All grown layers were fabricated with the technique of MBE. The layer stacks for all different experiments and devices were grown on InP substrate in (001) or (111)B orientation. Before the NiMnSb layer a buffer layer of undoped (In,Ga)As was grown. Additional for some samples on InP(111)B, a Si doped (In,Ga)As layer was grown on top of the undoped (In,Ga)As layer. The dopant concentration of this n-doped layer was determined by ETCH-CV. All layers were investigated by structural and the NiMnSb layer additional by magnetic properties. For the structural investigation the in-situ technique RHEED and ex-situ tool HRXRD were used. RHEED observations showed a good quality of the grown buffer and half-metallic ferromagnet layers on both orientations. These results were strengthened by the HRXRD measurement. The vertical lattice constant could be determined. The received value of a(NiMnSb_vertical) = 5.925 Å for NiMnSb on InP(001) is in good agreement to the value a(NiMnSb_Lit) = 5.903 Å found in literature [Cas55]. For NiMnSb on InP(111)B a vertical lattice constant of a(NiMnSb_vertikal) = 6.017 Å could be determined. The horizontal lattice constant of the buffer and the half-metallic ferromagnet layer could be determined as the same of the substrate. For NiMnSb this conclusion is only valid up to a thickness of ≈40nm. To increase this maximum thickness, NiMnSb samples were grown on InP(001) substrates and capped with Ti/Au layers. Afterwards a reciprocal space map of the (533) reflex was drawn with GIXRD at the synchrotron beamline BW2 of HASYLAB [Kum07]. It has been shown that the critical thickness is more than doubled by depositing a Ti/Au capping directly after growth of NiMnSb without breaking the ultrahigh vacuum (UHV). The magnetic properties were determined with FMR experiments and SQUID measurements. The received magnetic damping parameter α from a 40nm thick NiMnSb layer on InP(001) could be determined to 3.19e−3 along [1-10]. The resulting line width of our NiMnSb layers on InP(001) is more than 4.88 times smaller than measured before [Hei04]. Another result is the direction dependence of the damping. It has been measured that the difference of the damping is changed by more than 42% when rotating the applied field by 45° from [1-10] to [100].With SQUID we measured a saturation magnetization of a 40nm thick NiMnSb layer as 4µB. NiMnSb layers on InP(111)B substrate where also measured with FMR with a surprising result. These layers not only showed a decreasing in the anisotropy field with increasing thickness but also an uniaxial anisotropy. This behaviour can be explained with defects on these samples. With an AFM triangle-like defects were measured. These defects originated from the buffer layer and influenced the magnetic properties. Another part of this work is dedicated to the behaviour of NiMnSb at temperatures around 80K. With our samples, no phase transition can be observed in the data of the Hall, anomalous Hall term and resistivity. The last part of this work discusses different spintronic devices build with our NiMnSb layers. In a first device the magnetization acts on the current. This Giant Magneto Resistance (GMR) device consisted of InP:S(001) - 180nm undoped (In,Ga)As - 40nm NiMnSb - 10nm Cu - 6nm NiFe - 10nm Ru in current perpendicular to plane (CPP) geometry. We received a Magneto-Resistance-Ratio of 3.4%. In a second device the current acts on the magnetization and makes use of the spin torque phenomena. This so called Spin Torque Oscillator (STO) emitted frequencies in the GHz range (13.94GHz - 14.1GHz). The last fabricated device is based on the magnetic vortex phenomena. For switching the core polarity the gyrotropic frequencies f + = 254MHz f − = 217MHz and a total static magnetic field of only mµ0H = 65mT were necessary. The reversal efficiency has been determined as better than 99% [Lou09].