Refine
Has Fulltext
- yes (36)
Is part of the Bibliography
- yes (36)
Year of publication
Document Type
- Doctoral Thesis (34)
- Journal article (1)
- Preprint (1)
Keywords
- Spektroskopie (36) (remove)
Institute
- Institut für Physikalische und Theoretische Chemie (19)
- Physikalisches Institut (11)
- Institut für diagnostische und interventionelle Radiologie (Institut für Röntgendiagnostik) (3)
- Institut für Anorganische Chemie (1)
- Institut für Funktionsmaterialien und Biofabrikation (1)
- Institut für Geographie und Geologie (1)
EU-Project number / Contract (GA) number
- 614623 (2)
Um den jahrtausendealten Weg der Menschheit vom Papyrus über Buchdruck und siliziumbasierte Halbleiter in Richtung noch leistungsfähigerer Technologien zu gehen und weiterhin Heureka-Momente zu schaffen, bieten Kohlenstoffnanoröhren ein weites Forschungsfeld. Besonders die halbleitenden Charakteristika von SWNTs sowie die Manipulation dieser durch Dotierung bergen viele Möglichkeiten für zukünftige Anwendungen in moderner Elektrotechnologie. Der Weg zu einer industriellen Implementierung von SWNTs in neuartigen optoelektronischen Bauteilen ließe sich durch eine Ausweitung des Wissens bezüglich SWNTs und der dotierungsbasierten Anpassung ihrer Eigenschaften ebnen.
Mit dieser Erkenntniserweiterung als Zielsetzung wurden im Rahmen dieser Dissertation halbleitende, einwandige (6,5)-Kohlenstoffnanoröhren als chiralitätsreine, polymerstabilisierte Proben untersucht. Die ultrakurzzeitaufgelöste Spektroskopie der SWNTs erfolgte an organischen Suspensionen wie auch Dünnschichtfilmen, die je mittels eines gewissen Quantums an Gold(III)-chlorid dotiert worden waren. So konnten die ablaufenden Dynamiken auf einer ps-Zeitskala untersucht werden.
In Kapitel 4 konnte mittels transienter Absorptionsexperimente an redoxchemisch p-dotierter SWNT-Suspensionen zunächst gezeigt werden, dass sich die bei optischer Anregung gebildeten Trionen nicht analog zu Exzitonen diffusiv entlang der Nanoröhre bewegen, sondern lokalisiert vorliegen. Die längere trionischen Zerfallsdauer nach X$_1$- verglichen mit X$_1^+$-resonanter Anregung zeugt außerdem davon, dass das Trion aus dem Exziton gespeist wird. Der Einfluss der Dotierung auf die Zerfallsdynamiken von X$_1$ und X$_1^+$ wurde an SWNT-Dünnschichtfilmen untersucht. Das Photobleichsignal des Exzitons verschiebt hypsochrom und zerfällt schneller mit zunehmender Ladungsträgerdichte durch höherer Gold(III)-chloridkonzentrationen. Dies resultiert aus dem verringerten Abstand zwischen den Ladungsträgern, welche als nichtstrahlende Löschstellen fungieren. Für das X$_1^+$-PB ist ein ähnliches Verhalten zu beobachten. Dabei wird dieses Signal mit weiter steigender Dotierung von einer der H-Bande zuzuordnenden Photoabsorption überlagert. Diese lässt sich in einer starken Sättigung der Dotierung wie auch einer hohen Bandkantenverschiebung begründen.
In Kapitel 5 wurde die Größe der Exzitonen und Trionen in dotierten SWNT-Dünnschichtfilmen mittels des Phasenraumfüllmodells bestimmt. Dabei lag besonderes Augenmerk auf der Kompensation des PB/PA-Überlapps, dem schnellen Zerfall, einem Ausgleich von Differenzen zwischen Anrege- und Absorptionsspektrum sowie dem Anteil intrinsischer/dotierter Nanorohrsegmente, um korrigierte Größen $\xi_\mathrm{k}$ zu erhalten. Für die Trionengröße wurde zusätzlich der Überlapp der Absorptionsbanden einbezogen, um korrigierte Werte $\xi_{\mathrm{T,k}}$ zu bestimmen. $\xi_\mathrm{k}$ beträgt in der intrinsischen Form 6$\pm$2\,nm und bleibt bis zu einer Ladungsträgerdichte $n_{\mathrm{LT}}<0.10$\,nm$^{-1}$ etwa gleich, anschließend ist ein Absinken bis auf etwa 4\,nm bei $n_{\mathrm{LT}}\approx0.20$\,nm$^{-1}$ zu beobachten. Für diesen Trend ist die Überlagerung von Exziton- und H-Bande verantwortlich, da so der Faktor zur Bestimmung des Anteils intrinsischer Nanorohrsegmente an der SWNT verfälscht wird. Die Abweichung der intrinsischen Größe von den in der Literatur berichteten 13$\pm$3\,nm ist möglicherweise auf Unterschiede in der Probenpräparation zurückzuführen. Für die Trionengröße ergibt sich bei steigender Dotierung ein ähnliches Verhalten: Sie beträgt für $n_{\mathrm{LT}}<0.20$\,nm$^{-1}$ 1.83$\pm$0.47\,nm, was in der Größenordnung in guter Übereinstimmung mit der Literatur ist. Für höhere Dotierungen sinkt $\xi_{\mathrm{T,k}}$ bis auf 0.92$\pm$0.26nm ab. Dies erklärt sich dadurch, dass bei höherer $n_{\mathrm{LT}}$ die H-Bande das Spektrum dominiert, sodass der Einfluss der Absorptionsbandenüberlagerung nicht mehr vollständig durch den entsprechenden Korrekturfaktor kompensiert werden kann.
Kapitel 6 beschäftigte sich anstelle redoxchemischer Dotierung der nanoskaligen Halbleiter mit der (spektro-)elektrochemischen Untersuchung von Vorläufern molekularer Radikale. SWV-Messungen weisen dabei darauf hin, dass die Pyrene Pyr1-Pyr3 entsprechend der Anzahl ihrer Substituenten bei Reduktion Mono-, Bi- beziehungsweise Tetraradikale bilden. Die strukturelle Ähnlichkeit der Moleküle äußert sich in gleichen Reduktionspotentialen wie auch ähnlichen potentialabhängigen Absorptionsspektren. Während nur marginale Unterschiede in den PL-Spektren der neutralen und reduzierten Spezies festgestellt werden konnte, lieferte das zeitkorrelierte Einzelphotonenzählen aufschlussreichere Ergebnisse: So wird die Fluoreszenzlebensdauer stark von der Polarität der Umgegbung beeinflusst - bereits die Zugabe des Leitsalzes führt hier zu Änderungen. Die durchschnittliche Fluoreszenzlebensdauer $\tau_{\mathrm{av}}$ sinkt außerdem mit Reduktion und Radikalbildung; für höhere Emissionswellenlängen ist $\tau_{\mathrm{av}}$ außerdem höher. Insgesamt verdeutlichten die Experimente die gute Abschirmung zwischen Pyrenkern und Naphthalimidsubstituenten der Moleküle sowie die Sensibilität gegenüber dem Medium durch TICT, das Vorhandensein von Bi- und Tetraradikalen kann allerdings nicht vollständig belegt werden, wofür EPR-Messugen notwendig wären.
Diese Arbeit befasst sich mit zeitaufgelösten Prozessen in molekularen Systemen. Dabei wurde sowohl die Wellenpaketdynamik nach Photoanregung betrachtet als auch spektrale Eigenschaften mittels Absorptions- und zweidimensionaler Spektroskopie untersucht.
Zunächst widmet sich die Arbeit der Wellenpaket- und Populationsdynamik in zwei diabatischen, gekoppelten Zuständen. Nach impulsiver Anregung aus dem zu Beginn besetzten Zustand treten in der Populationsdynamik zwei deutlich verschiedene Oszillationen auf. Der langsamer variierende Populationstransfer besitzt die Periodendauer der Vibrationsbewegung und ist auf einen Wechsel der Zustände beim Durchlaufen des Wellenpakets durch die Kreuzungsregion der diabatischen Potentiale zurückzuführen. Die ultraschnelle Komponente mit einer Periodendauer von etwa 4 fs lässt sich als eine Art Rabi-Oszillation beschreiben, die durch die (zeitunabhängige) Kopplung hervorgerufen wird. Sie wurde mit Hilfe von analytischen Berechnungen ausführlich charakterisiert. Damit dieser Prozess auftreten kann müssen mehrere Bedingungen erfüllt werden: Das Wellenpaket muss über die Dauer der Oszillationen annähernd örtlich lokalisiert bleiben; dies ist an den Umkehrpunkten der Wellenpaketsbewegung der Fall. Die Amplitude der Oszillationen in den Populationen ist proportional zum Verhältnis der Kopplung zum Energieabstand der Zustände. Deshalb muss an den stationären Stellen die Kopplung groß im Vergleich zum Energieabstand sein. Die Amplitude der Oszillationen hängt außerdem von dem Populationsverhältnis und den Phasen der Komponenten des Wellenpakets in den beiden Zuständen ab. Die ultraschnellen Oszillationen bleiben auch in mehrdimensionalen Systemen mit unterschiedlichen Vibrationsfrequenzen je Freiheitsgrad erhalten.
Das gleiche Modell wurde benutzt, um Ladungstransferprozesse mittels linearer und 2D-Spektroskopie zu untersuchen. Eine Kopplung an die Umgebung wurde, aufbauend auf einer Quanten-Master-Gleichung in Markov-Näherung, wellenfunktionsbasiert mittels eines Quantum-Jump-Algorithmus mit expliziter Dephasierung beschrieben. Dabei findet mit vorher definierten Wahrscheinlichkeiten zu jedem Zeitschritt einer von drei stochastischen Prozessen statt. Neben kohärenter Propagation können Sprünge in einen anderen Eigenzustand des Systems und Dephasierungen auftreten. Zwei Dissipationsparameter spielen dabei eine Rolle. Dies ist zum einen die Stärke der System-Bad-Kopplung, welche die Gesamtrate der Energierelaxation beschreibt. Weiterhin beeinflusst die Dephasierungskonstante den Verlust kohärenter Phasen ohne Energieänderung. Fallenzustände wurden identifiziert, die durch sehr geringe Sprungraten in niedrigere Zustände charakterisiert sind. Die Langlebigkeit kann durch die Form der Eigenfunktionen erklärt werden, die eine deutlich andere Wahrscheinlichkeitsverteilung als die der Nicht-Fallenzustände besitzen. Dadurch werden die in die Sprungraten eingehenden Matrixelemente klein. Das Absorptionsspektrum zeigt Peaks an der Stelle der Fallenzustände, da nur die Eigenfunktionen der Fallenzustände große Franck-Condon-Faktoren mit der Anfangswellenfunktion besitzen. Verschiedene Kombinationen der Dissipationsparameter führen zu Änderungen der relativen Peakintensitäten und der Peakbreiten.
Die 2D-Spektren des Ladungstransfersystems werden störungstheoretisch über die Polarisation dritter Ordnung berechnet. Sie zeigen viele eng nebeneinander liegende Peaks in einer schachbrettmusterförmigen Anordnung, die sich auf Übergänge unter Mitwirkung der Fallenzustände zurückführen lassen. Höhere System-Bad-Kopplungen führen aufgrund der effizienten Energiedissipation zu einer Verschiebung zu kleineren Energien. Peaks, die mit schneller zerfallenden Fallenzuständen korrespondieren, bleichen schneller aus. Höhere Dephasierungskonstanten resultieren in verbreiterten Peaks. Um den Einfluss der Dissipation genauer zu charakterisieren, wurden gefilterte 2D-Spektren betrachtet. Dazu wurden Ausschnitte der Polarisation dritter Ordnung zu verschiedenen Zeiten fouriertransformiert. Längere Zeiten führen zu einer effektiveren Energierelaxation entlang der entsprechenden Zeitvariablen. Die Entvölkerung der höher liegenden Zustände lässt sich somit zeit- und energieaufgelöst betrachten. Weiterhin wurde gezeigt, dass sich der Zerfall eines einzelnen Peaks mit dem Populationsabfall des damit korrespondierenden Eigenzustandes in Einklang bringen lässt, obwohl die Zuordnung der Peaks im 2D-Spektrum zu Übergängen zwischen definierten Eigenzuständen nicht eindeutig ist.
Mit dem benutzten eindimensionalen Modell können auch Ladungstransferprozesse in organischen gemischtvalenten Verbindungen beschrieben werden. Es wurde die Frage untersucht, welche Prozesse nach einem optisch induzierten Energietransfer in solchen Systemen ablaufen. Experimentelle Daten (aufgenommen im Arbeitskreis von Prof. Lambert) deuten auf eine schnelle interne Konversion (IC) gefolgt von Thermalisierung hin. Um dies theoretisch zu überprüfen, wurden Absorptionsspektren bei verschiedenen Temperaturen berechnet und mit den gemessenen transienten Spektren verglichen. Es findet sich, abhängig von der Stärke der elektronischen Kopplung, eine sehr gute bis gute Übereinstimmung, was die Annahme eines schnellen ICs stützt.
Im letzten Teil der Arbeit wurden vibronische 2D-Spektren von molekularen Aggregaten betrachtet. Dazu wurde die zeitabhängige Schrödingergleichung für ein Monomer-, Dimer- und Trimersystem mit der Multi-Configuration Time-Dependent Hartree-Methode gelöst und die Polarisation nicht-störungstheoretisch berechnet. Der Hamiltonoperator des Trimers umfasst hierbei sieben gekoppelte elektronische Zustände und drei bzw. sechs Vibrationsfreiheitsgrade. Der betrachtete Photonenecho-Beitrag der Polarisation wurde mittels phasencodierter Laserpulse extrahiert. Die resultierenden Spektren sind geometrieabhängig, ein Winkel zwischen den Übergangsdipolmomenten der Monomere von 0° (180°) resultiert in einem H-Aggregat (J-Aggregat). Die Lage und Intensität der Peaks im rein elektronischen Trimer wurde analytisch erläutert. Die Spektren unter Einbeziehung der Vibration zeigen eine ausgeprägte vibronische Struktur. Es wurde gezeigt, wie die Spektren für höhere Aggregationsgrade durch die höhere Dichte an vibronischen Zuständen komplexer werden. Im J-Aggregat ist mit zunehmender Aggregation eine stärkere Rotverschiebung zu sehen. Das Spektrum des H-Aggregats zeigt eine im Vergleich zum J-Aggregat kompliziertere Struktur. Die Verwendung zweier Vibrationsfreiheitsgrade je Monomer führt zu Spektren mit überlappenden Peaks und einer zusätzlichen vibronischen Progression. Der Vergleich von Spektren verschiedener Mischungen von Monomer, Dimer und Trimer, entsprechend einem von Temperatur und Konzentration abhängigen Aggregationsgrad, zeigt den Einfluss dieser experimentellen Faktoren. Schließlich wurden mögliche Ansätze aufgezeigt, anhand der Spektren auf den Aggregationsgrad zu schließen.
Diese Arbeit befasst sich mit der störungstheoretischen Berechnung von zweidimensionalen Photonen-Echo-Spektren für das elektronische und vibronische Modell eines Homo- und Hetero-Dimers sowie für ein vibronisches Modell eines Monomers unter dem Einfluss einer System-Bad-Wechselwirkung. Bei der Analyse der Dimerspektren steht neben der Orientierungsmittelung der Polarisation dritter Ordnung der Unterschied zwischen elektronischen und vibronischen Spektren sowie der Vergleich der Spektren von Homo- und Hetero-Dimeren im Zentrum des Interesses. Bei der Analyse der Monomer-Spektren steht die Behandlung einer dissipativen Dynamik bzw. des vibrational-coolings innerhalb eines stochastischen Ansatzes im Vordergrund.
Der erste Teil dieser Arbeit konzentriert sich auf die störungstheoretische Berechnung der Polarisation dritter Ordnung in Dimeren. Dabei werden alle Aspekte und Ergebnisse für verschiedene Geometrien der Übergangsdipolmomente analysiert und diskutiert. Die Berechnungen berücksichtigen dabei auch die zufällige Anordnung der Moleküle in der Probe. Die Zusammenhänge zwischen den 2D-Spektren und den Eigenschaften der Monomereinheiten, die Abhängigkeit der Intensitäten mancher Peaks von der zeitlichen Abfolge der Pulse sowie der Einfluss der elektronischen Kopplung und verschiedener Übergangsdipolmomente ermöglichen ein grundlegendes Verständnis der elektronischen Photonen-Echo-Spektren. Im elektronischen Dimer wird der Hetero-Dimer-Charakter durch verschiedene Monomeranregungsenergien sowie unterschiedliche Übergangsdipolmomente der Monomereinheiten bestimmt. Der Einfluss dieser Größen auf die Photonen-Echo-Spektren kann durch die Kombination einer detaillierten analytischen Betrachtung und numerischen Rechnungen anschaulich nachvollzogen werden. In der vibronischen Betrachtungsweise zeigt sich, dass die Spektren deutlich an Komplexität gewinnen. Durch die Vibrationsfreiheitsgrade vervielfachen sich die möglichen Übergänge im System und damit die möglichen Peakpositionen im Spektrum. Jeder Peak spaltet in eine Vibrationssubstruktur auf, die je nach ihrer energetischen Position mit anderen überlagern kann. Der Vergleich zwischen Homo- und Hetero-Dimer-Spektren wird durch die Wahl verschiedener Vibrationsfrequenzen und unterschiedlicher Gleichgewichtsabstände entlang der Vibrationskoordinaten erweitert.
Die Berechnung des Orientierungsmittels erfolgt mit zwei verschiedenen Ansätzen. Zum einen wird das Mittel durch den numerischen sampling-Ansatz berechnet. Dabei werden Azimutal- und Polarwinkel in kleinen Winkelinkrementen abgetastet und für jede Kombination ein 2D-Spektrum berechnet. Die Einzelspektren werden anschließend gemittelt. Diese Methode erweist sich im Dimer als sehr effektiv. Zum anderen erlaubt die analytische Auswertung der Polarisation dritter Ordnung, das gemittelte Spektrum direkt in einer einzelnen Rechnung durch winkelgemittelte Gewichtungsfaktoren zu bestimmen. Bei der Berechnung der elektronischen 2D-Spektren ist diese Methode sehr leistungsfähig, da alle Ausdrücke analytisch bekannt sind. Für vibronische Systeme ist dieser Ansatz ebenfalls sehr leistungsstark, benötigt aber eine einmalige aufwendige Analyse vor der Berechnung. Trotz der deutlich erhöhten Anzahl an Zustandsvektoren, die propagiert werden müssen, ist diese Methode circa zweimal schneller als die direkte Mittelung mit der sampling-Methode.
Im zweiten Teil konzentriert sich die Arbeit auf die Beschreibung eines Monomers, das sich in einer dissipativen Umgebung befindet. Dabei wird auf die Lösung einer stochastischen Schrödingergleichung zurückgegriffen. Speziell wird die sogenannte quantum-state-diffusion-Methode benutzt. Dabei werden nicht nur die Erwartungswerte für die Energie und den Ort, sondern auch die Polarisation dritter Ordnung – eine phasensensitive Größe – bestimmt. In der theoretischen Fragestellung wird dabei, ausgehend von der von-Neumann Gleichung, die Zeitentwicklung der reduzierten Dichtematrix durch die Integration einer stochastischen zeitabhängigen Schrödingergleichung reproduziert. In Rechnungen koppelt die Stochastik über die Erwartungswerte von Ort und Impuls die verschiedenen störungstheoretischen Korrekturen der Wellenfunktion miteinander. Die Spektren, die aus den numerischen Simulationen erhalten werden, spiegeln das dissipative Verhalten des Systems detailliert wider. Eine Analyse der Erwartungswerte von Ort und Energie zeigt, dass sich die einzelnen elektronischen Zustände wie gedämpfte harmonische Oszillatoren verhalten und jeweils einen exponentiellen Zerfall abhängig von der Dissipationskonstante zeigen. Dieser Teil der Arbeit erweitert vorausgehende Untersuchungen, bei denen ein vereinfachter Ansatz zu Einsatz kam, der die korrelierte Stochastik nicht berücksichtigte.
Wachstum und Charakterisierung von Quantenpunkt-Mikrotürmchen mit adiabatischer Modenanpassung
(2013)
Verschiedene Konzepte zur Realisierung einer geeigneten Umgebung für Licht-
Materie-Wechselwirkung konkurrieren um Anerkennung und eine ständige Optimierung
der Systemparameter findet statt. Das Konzept von Mikrotürmchen scheint
prädestiniert, da es viele anwendungsfreundliche Eigenschaften in sich vereint. Allerdings
stellt die drastische Abnahme des Q Faktors für kleiner werdende Durchmesser
d einen wesentlichen Limitierungsfaktor dieser Strukturen dar. Für viele Anwendungen
resultiert daraus ein Kompromiss aus hohem Q Faktor und kleinem
Modenvolumen der Strukturen, wodurch das volle Potential des Resonatorsystems
nicht ausgeschöpft werden kann. Ziel dieser Arbeit war es, die drastische Abnahme
des Q Faktors von Mikrotürmchen mit Durchmessern um 1μm aufzuheben und
dadurch Resonatoren mit d < 1μm für ausgeprägte Licht-Materie-Wechselwirkung
herzustellen.
Dazu wurde erstmalig beabsichtigt eine Modenanpassung in Mikrotürmchen vorgenommen.
Mittels Molekularstrahlepitaxie konnte eine Übergangsregion, bestehend
aus drei Segmenten, in diese Strukturen implementiert und so ein adiabatischer
Modenübergang zwischen der aktiven Mittelschicht und den Spiegelbereichen
vorgenommen werden. Der positive Einfluss dadurch ergab sich in einer signifikanten
Verbesserung des gemessenen Q Faktors für Durchmesser unter 1μm.
Für d = 0.85μm konnte ein Q Faktor von 14 400 bestimmt werden. Dies stellt damit
den höchsten je gemessenen Wert für Mikrotürmchen im Submikrometerbereich
dar. Dadurch wird ein Bereich mit Modenvolumina < 3 kubischen Wellenlängen erschlossen und ausgeprägte Wechselwirkungseffekte im Mikrotürmchensystem sind zu erwarten. Starke
Quantenpunkt-Licht-Kopplung konnte in diesen Strukturen nachgewiesen werden.
Die höchste Vakuum-Rabiaufspaltung betrug 85μeV und die Visibilität wurde zu
0.41 bestimmt. Im Zuge der weiteren Optimierung der Systemparameter für die starke
Kopplung wurde ein ex-situ Ausheilschritt auf die verwendete Quantenpunktsorte
angewendet. In magnetooptischen Untersuchungen konnte damit eine Verdopplung
der mittleren Oszillatorstärke auf einen Wert von 12 abgeschätzt werden.
Weiter konnte in adiabatischen Mikrotürmchen über einen großen Durchmesserbereich
von 2.25 bis 0.95μm eindeutiger Laserbetrieb des Quantenpunktensembles
nachgewiesen werden. Dabei konnte eine kontinuierliche Reduzierung der Laserschwelle
von über zwei Größenordnungen für kleiner werdende Durchmesser beobachtet
werden. Für Durchmesser < 1.6μm betrug der Beta-Faktor der Mikrolaser in
etwa 0.5. Sie zeigten damit beinahe schwellenloses Verhalten.
Zuletzt wurde der elektrische Betrieb von adiabatischen Mikrotürmchen gezeigt. Dafür
wurde eine dotierte Struktur mit adiabatischem Design hergestellt. Im Vergleich
zur undotierten Struktur fielen die gemessenen Q Faktoren in etwa um 5 000 geringer
aus. Die spektralen Eigenschaften sowohl des Resonators als auch einzelner
Quantenpunktlinien zeigten vernachlässigbare Abhängigkeit der Anregungsart (optisch
oder elektrisch) und zeugen von einem erfolgreichen Konzept zum elektrischen
Betrieb der Bauteile. Zeitaufgelöste Messungen erlaubten die Beobachtung von interessanten
Dynamiken der Rekombination von Ladungsträgern in den Proben. Als
Ursache dafür wurde ein hohes intrinsisches Feld, welches auf Grund des Designs
der Schichtstruktur entsteht, identifiziert. Weiter zeigte sich, dass sich das interne
Feld durch Anregungsart und extern angelegte Spannungen manipulieren lässt.
This thesis describes the growth and characterization of both the all-oxide heterostructure
Fe3O4/ZnO and the spin-orbit coupling driven layered perovskite iridates.
As for Fe3O4/ZnO, the 100% spin-polarized Fe3O4 is a promising spin electrode candidate
for spintronic devices. However, the single crystalline ZnO substrates exhibit different polar surface termination which, together with substrate preparation method, can drastically affect the physical properties of Fe3O4/ZnO heterostructures. In this thesis two different methods of substrate preparation were investigated: a previously used in situ method involving sputtering and annealing treatments and a recent ex situ method containing only the annealing procedure. For the latter, the annealing treatment was performed in dry and humid O2 gas flow for the O- and Zn-terminated substrates, respectively, to produce atomically at surfaces as verified by atomic force microscopy(AFM). With these methods, four different ZnO substrates were fabricated and used further for Fe3O4 film growth. Fe3O4 films of 20 nm thickness were successfully grown by reactive molecular beam epitaxy. AFM measurements reveal a higher film surface roughness for the samples with in situ prepared substrates. Moreover, X-ray photoelectron spectroscopy (XPS) measurements indicate significant Zn substitution within the Fe3O4 film for these samples, whereas the samples with ex situ prepared substrates show stoichiometric Fe3O4 films. X-ray diffraction measurements confirm the observations from XPS, revealing additional peaks due to Zn substitution in Fe3O4 films grown on in situ prepared ZnO substrates. Conductivity, as well as magnetometry, measurements show the presence of Zn-doped ferrites in films grown on in situ prepared substrates. Such unintentionally intercalated Zn-doped ferrites dramatically change the electrical and magnetic properties of the films and, therefore, are not preferred in a high-quality heterostructure.
X-ray reflectivity (XRR) measurements show for the film grown on ex situ prepared Zn-terminated substrate a variation of film density close to the interface which is also confirmed by transmission electron microscopy (TEM). Using polarized neutron reflectometry, magnetic depth profiles of the films grown on ex situ prepared substrates clearly indicate Fe3O4 layers with reduced magnetization at the interfaces. This result is consistent with earlier observations made by resonant magnetic X-ray reflectometry (RMXR), but in contrast to the findings from XRR and TEM of this thesis. A detailed TEM study of all four samples shows that the sample with ex situ prepared O-terminated substrate has the sharpest interface, whereas those with ex situ prepared Zn-terminated as well as in situ prepared substrates indicate rougher interfaces. STEM-EELS composition profiles of the samples reveal the Zn substitution in the films with in situ prepared substrates and therefore confirm the presence of Zn-doped ferrites. Moreover, a change of the Fe oxidation state of the first Fe layer at the interface which was observed in previous studies done by RMXR, was not verified for the samples with in situ prepared substrates thus leaving the question of a possible presence of the magnetically dead layer open. Furthermore, density functional theory calculations were performed to determine the termination dependent layer sequences which are ...-Zn-O-(interface)-[Fe(octa)-O-Fe(tetra)-Fe(octa)-Fe(tetra)-O]-[...]-... and ...-O-Zn-(interface)-[O-Fe(octa)-O-Fe(tetra)-Fe(octa)-Fe(tetra)]-[...]-... for the samples with O- and Zn-terminated substrates, respectively. Spin density calculations show that in case of O-termination the topmost substrate layers imitate the spin polarization of film layers close to the interface. Here, the first O layer is affected much stronger than the first Zn layer. Due to the strong decrease of this effect toward deeper substrate layers, the substrate surface is supposed to be sensitive to the contiguous spin polarization of the film. Thus, the topmost O layer of the O-terminated substrate could play the most essential role for effective spin injection into ZnO.
The 5d transition metal oxides Ba2IrO4 (BIO) and Sr2IrO4 (SIO) are associated with the Ruddlesden-Popper iridate series with phase type "214" (RP{214), and due to the strong spin-orbit coupling belong to the class of Mott insulators. Moreover, they show many similarities of the isostructural high Tc-cuprate superconductors, e.g. crystal structure, magnetism and electronic band structure. Therefore, it is of great interest to activate a potential superconducting phase in (RP{214) iridates. However, only a small number of publications on PLD grown (RP{214) iridates in the literature exists. Furthermore, published data of soft X-ray angle resolved photoemission spectroscopy (SX-ARPES) experiments mainly originate from measurements which were performed on single crystals or MBE grown films of SIO and BIO. In this thesis La-doped SIO films (La0:2Sr1:8IrO4, further referred as LSIO) were used to pursue a potential superconducting phase.
A set of characterization methods was used to analyze the quality of the PLD grown BIO, SIO and LSIO films. AFM measurements demonstrate that thick PLD grown(RP{214) iridate films have rougher surfaces, indicating a transition from a 2D layer-bylayer growth (which is demonstrated by RHEED oscillations) to a 3D island-like growth mode. In addition, chemical depth profiling XPS measurements indicate an increase of the O and Ir relative concentrations in the topmost film layers. Constant energy k-space maps and energy distribution curves (EDCs) measured by SX-ARPES show for every grown film only weak energy band dispersions, which are in strong contrast to the results obtained on the MBE grown films and single crystals from the literature. In this thesis,
a subsequent TEM study reveals missing SrO layers within the grown films which occur mainly in the topmost layers, confirming the results and suggestions from XPS and SX-ARPES data: the PLD grown films have defects and, therefore, incoherently scatter photoelectrons. Nevertheless, the LSIO film shows small additional spectral weight between the highsymmetry M points close to the Fermi level which can be attributed to quasiparticle states which, in turn, indicates the formation of a Fermi-arc. However, neither conductivity measurements nor valence band analysis via XPS confirm an activation of a superconducting phase or presence of spectral weight of quasiparticle states at the Fermi level in this LSIO film.
It is possible that these discovered difficulties in growth are responsible for the low number of SX-ARPES publications on PLD grown (RP{214) iridate films. For further investigations of (RP{214) iridate films by SX-ARPES, their PLD growth recipes have to be improved to create high quality single crystalline films without imperfections.
Diese Dissertation beschäftigt sich mit der Exzitonendynamik molekularer Aggregate, die nach Mehrphotonen-Anregung auf ultrakurzer Zeitskala stattfindet. Hierbei liegt der Fokus auf der Charakterisierung der Exziton-Exziton-Annihilierung (EEA) mithilfe von zweidimensionaler optischer Spektroskopie fünfter Ordnung. Dazu werden zwei verschiedene Modellsysteme implementiert: Das elektronische Homodimer und das elektronische Homotrimer-Modell, wobei Letzteres eine Erweiterung des Dimer-Modells darstellt. Die Kopplung des quantenmechanischen Systems an die Umgebung wird mithilfe des Quantum-Jump-Ansatzes umgesetzt. Besonderes Interesse kommt der Analyse des Signals fünfter Ordnung in Abhängigkeit der Populationszeit T zu.
Anhand des Dimer-Modells als kleinstmögliches Aggregat lassen sich bereits gute Vorhersagen auch über das Verhalten größerer molekularer Aggregate treffen. Der Zerfall des oszillierenden Signals für lange Populationszeiten korreliert mit der EEA. Dies zeigt, dass die zweidimensionale optische Spektroskopie genutzt werden kann, um den Annihilierungsprozess zu charakterisieren. Innerhalb des Modells des Dimers wird weiterhin der Einfluss der Intraband-Relaxation untersucht. Zunehmende Intraband-Relaxation verhindert den Austausch zwischen den lokalen Zuständen, der essentiell für den Annihilierungsprozess ist, und die EEA wird blockiert.
Das elektronische Trimer-Modell erweitert das Dimer-Modell um eine Monomereinheit. Somit befinden sich die Exzitonen im Anschluss an die Anregung nicht mehr unvermeidlich nebeneinander. Es gibt somit eine Konfiguration, bei der sich die Exzitonen zunächst zueinander bewegen müssen, bevor die Startbedingung des Annihilierungsprozesses gegeben ist. Dieser zusätzliche Schritt wird auch Exzitonendiffusion genannt. Die Ergebnisse dieser Arbeit legen nahe, dass das erwartete Verhalten nur zu sehr kurzen Zeiten im Femtosekundenbereich auftritt und somit die Zeitskala der Exzitonendiffusion im Falle des Trimers nicht sichtbar wird. Es bedarf demnach eines größeren Modellsystems, bei dem sich der Effekt der zeitverzögert eintretenden EEA deutlich in der Zerfallsdynamik manifestieren kann.
Die Terahertz-Technologie erschließt permanent neue Forschungsbereiche und wird auch vermehrt im kommerziellen Bereich eingesetzt. Diese Entwicklung wird in eigenen Analysen dargestellt. Als Kernaspekte dieses Buchs werden technologische Verbesserungen für gepulste Terahertz-Systeme und der spektroskopische Einsatz für die Polymeranalytik vorgestellt. Einen besonderen Stellenwert nehmen dabei Untersuchungen an Polymermischungen im Schmelzezustand während der Prozessierung ein. Bemerkenswert ist hierbei das temperaturabhängige Verhalten von verschiedensten Polyamiden. Die Änderung der optischen und spektroskopischen Eigenschaften und die Einflussfaktoren werden tiefergehend betrachtet. Dabei werden verschiedene klassische und neuere Experimentalmethoden, Modellierungen und quantenchemische Simulationsmethoden eingesetzt, um insbesondere die intermolekularen Wechselwirkungen aufzuklären.
The present studies which have been performed in the work-group C-2 (Prof. W. Kiefer) within the program of the Sonderforschungsbereichs 347, deal with the FT-Raman and –IR spectroscopy on new organometallic complexes, synthesized in the work-groups B-2 (Prof. W. Malisch), B-3 (Prof. W. A. Schenk), D-1 (Prof. H. Werner) and D-4 (Prof. D. Stalke). The FT-Raman spectra recorded at 1064 nm led to very useful and interesting information. Furthermore, the DFT calculations which are known to offer promise of obtaining accurate vibrational wavenumbers, were successfully used for the assignment of the vibrational spectra. For the first time it has been possible to ascribe exactly the n(RhC) stretching mode in the vinylidene rhodium(I) complex trans-[RhF(=C=CH2)(PiPr3)2] by using isotopic substitution, in conjunction with theoretical calculations. This is also true for the complexes trans-[RhF(CO)(PiPr3)2], trans-[RhF(C2H4)(PiPr3)2], trans-[RhX(=C=CHPh)(PiPr3)2] (X = F, Cl, Br, I, Me, PhCºC) and trans-[RhX(CN-2,6-xylyl)(PiPr3)2] (X = F, Cl, Br, I, CºCPh). In addition, the comparison between the n(RhC) wavenumbers of the complexes trans-[RhF(=13C=13CH2)(PiPr3)2] and trans-[RhF(CO)(PiPr3)2], containing the isoelectronic ligands 13C=13CH2 and CO, which have the same reduced mass, indicated that the Rh-C bond is stronger in the carbonyl than in the vinylidene complex. Besides, the n(RhF) stretching mode, which has been observed at higher wavenumbers in the FT-Raman and -IR spectra of trans-[RhF(CO)(PiPr3)2], showed that the carbonyl ligand is a better p-acceptor and a less effective s-donor than the vinylidene one. Moreover, the comparison of the n(CºC) and n(Rh-C) modes from the FT-Raman spectrum of the complexes trans-[Rh(CºCPh)(L)(PiPr3)2] (L = C=CHPh, CO, CN-2,6-xylyl) point out that the p-acceptor ability of the ligand trans to CºCPh should rise in the order C=CH2 < CO < CN-2,6-xylyl £ C=CHPh. The investigated sensitivity of the n(RhC), n(CC), n(CO) and n(CN) vibrational modes to the electronic modifications occuring in the vinylidene, carbonyl, ethylene and isonitrile complexes, should allow in the future the examination of the p-acceptor or p-donor properties of further ligands. Likewise, we were able to characterize the influence of various X ligands on the RhC bond by using the n(RhC) stretching mode as a probe for the weakening of this. The calculated wavenumbers of the n(RhC) for the vinylidene complexes trans-[RhX(=C=CHR)(PiPr3)2], where R = H or Ph, suggested that the strength of the Rh=C bond increases along the sequence X = CºCPh < CH3 < I < Br < Cl < F. For the series of carbonyl compounds trans-[RhX(CO)(PiPr3)2], where X = F, Cl, Br and I, analogous results have been obtained and confirmed from the model compounds trans-[RhX(CO)(PMe3)2]. Since, the calculated vibrational modes for the ethylene complex trans-[RhF(C2H4)(PiPr3)2] were in good agreement with the experimental results and supported the description of this complex as a metallacyclopropane, we were interested in getting more information upon this class of compounds. In this context, we have recorded the FT-Raman and -IR spectra of the thioaldehyde complexes mer-[W(CO)3(dmpe)(h2-S=CH2)] and mer-[W(CO)3(dmpe)(h2-S=CD2)] which have been synthezised by B-3. The positions of the different WL vibrational modes anticipated by the DFT calculations, were consistent with the experimental results. Indeed, the analysis of the band shifts in the FT-Raman and –IR spectra of the isotopomer mer-[W(CO)3(dmpe)(h2-S=CD2)] confirmed our assignment. The different stereoisomers of complex mer-[W(CO)3(dmpe)(h2-S=CH2)] were investigated too, since RMN and IR-data have shown that complex mer-[W(CO)3(dmpe)(h2-S=CH2)] lead in solution to an equilibrium. Since the information on the vibrational spectra of the molybdenum and tungsten complexes Cp(CO)2M-PR2-X (M = Mo, W; R = Me, tBu, Ph; X = S, Se) is very scarce, we extended our research work to this class of compounds. We have tried to elucidate the bonding properties in these chalcogenoheterocycle complexes by taking advantage of the mass effect on the different metal atoms (W vs. Mo). Thus, the observed band shifts allowed to assign most of the ML fundamental modes of these complexes. This project and the following one were a cooperation within the work-group B-2. The Raman and IR spectra of the matrix isolated photoproducts expected by the UV irradiation of the iron silyl complex Cp(CO)2FeSiH2CH3 have been already reported by Claudia Fickert and Volker Nagel in their PhD-thesis. Since no exact assignment was feasible for these spectra, we were interested in the study of the reaction products created by irradiation of the carbonyl iron silyl complex Cp(CO)2FeCH2SiH3. Although the calculated characteristic vibrational modes of the metal ligand unit for the various photoproducts are significantly different in constitution, they are very similar in wavenumbers, which did not simplify their identification. However, the theoretical results have been found to be consistent with the earlier experimental results. Finally, the last part of this thesis has been devoted to the (2-Py)2E- anions which exhibit a high selectivity toward metal-coordination. All di(2-pyridyl) amides and -phosphides which were synthesized by D-4, coordinate the R2Al+ fragment via both ring nitrogen atoms. This already suggests that the charge density in the anions is coupled into the rings and accumulated at the ring nitrogen atoms, but the Lewis basicity of the central nitrogen atom in Et2Al(2-Py)2N is still high enough to coordinate a second equivalent AlEt3 to form the Lewis acid base adduct Et2Al(2-Py)2NAlEt3. Due to the higher electronegativity of the central nitrogen atom in Me2Al(2-Py)2N, Et2Al(2-Py)2N and Et2Al(2-Py)2NAlEt3, compared to the bridging two coordinated phosphorus atom in Me2Al(2-Py)2P and Et2Al(2-Py)2P, the di(2-pyridyl)amide is the hardest Lewis base. In the phosphides merely all charge density couples into the rings leaving the central phosphorus atom only attractive for soft metals. These results were confirmed by using DFT and MP2 calculations. Moreover, a similar behaviour has been observed and described for the benzothiazolyl complex [Me2Al{Py(Bth)P}], where complementary investigations are to be continued. The DFT calculations carried out on the model compounds analysed in these studies supply very accurate wavenumbers and molecular geometries, these being in excellent agreement with the experimental results obtained from the corresponding isolated complexes.
Spektroskopische Untersuchungen an elektrisch und optisch erzeugten Exziton-Polariton-Kondensaten
(2019)
Eine technologisch besonders vielversprechende Art von Mikrokavitäten besteht aus einem optisch aktiven Material zwischen zwei Spiegeln, wobei das Licht auf Größe seiner Wellenlänge eingesperrt wird. Mit diesem einfachen Konzept Licht auf Chipgröße einzufangen entstand die Möglichkeit neue Phänomene der Licht-Materie Wechselwirkung zu studieren. Der Oberflächenemitter (VCSEL), welcher sich das veränderte Strahlungsverhalten aufgrund der schwachen Kopplung und stimulierten Emission zu Nutze macht, ist bereits länger kommerziell sehr erfolgreich. Er umfasst ein erwartetes Marktvolumen von ca. 5.000 Millionen Euro bis 2024, welches sich auf verschiedenste Anwendungen im Bereich von Sensorik und Kommunikationstechnologie bezieht. Dauerhaft hohe Wachstumsraten von 15-20% pro Jahr lassen auf weiteres langfristiges Potential von Mikrokavitäten in der technologischen Gesellschaft der nächsten Generation hoffen.
Mit fortschreitender Entwicklung der Epitaxie-Verfahren gelang es Kavitäten solcher Qualität herzustellen, dass zum ersten Mal das Regime der starken Kopplung erreicht wurde. Starke Kopplung bedeutet in diesem Fall die Bildung eines neuen Quasiteilchens zwischen Photon und Exziton, dem Exziton-Polariton (Polariton). Dieses Quasiteilchen zeigt eine Reihe interessanter Eigenschaften, welche sowohl aus der Perspektive der Technologie, als auch aus der Sicht von Grundlagenforschung interessant sind. Bei systemabhängigen Teilchendichten erlaubt das Polariton ebenfalls die Erzeugung von kohärentem Licht über den Exziton-Polariton-Kondensatszustand (Kondensat), den Polariton-Laser. Die Eigenschaften des emittierten Lichtes ähneln denen eines VCSELs, allerdings bei einigen Größenordnungen geringerem Energieverbrauch, bzw. niedrigerer Laserschwelle, bei Wahl geeigneter Verstimmung von Exziton und Photon. Diese innovative Entwicklung kann daher unter anderem neue Möglichkeiten für besonders energiesparende Anwendungen in der Photonik eröffnen.
Die vorliegende Doktorarbeit soll zur Erweiterung des Forschungsstandes in diesem Gebiet zwischen Photonik und Festkörperphysik beitragen und untersucht zum einen den anwendungsorientierten Teil des Feldes mit Studien zur elektrischen Injektion, beleuchtet aber auch den interessanten Phasenübergang des Systems über seine Kohärenz- und Spineigenschaften. Es folgt eine knappe überblicksartige Darstellung der Ergebnisse, die in dieser Arbeit genauer ausgearbeitet werden.
Rauschanalyse und die optische Manipulation eines bistabilen elektrischen Polariton-Bauelements
Aufbauend auf der Realisierung eines elektrischen Polariton-Lasers wurde in dieser Arbeit ein optisches Potential in das elektrisch betriebene Kondensat mit einem externen Laser induziert. Dieses optische Potential ermöglicht die Manipulation der makroskopischen Besetzung der Grundzustandswellenfunktion, welches sich als verändertes Emissionsbild im Realraum darstellt. Der polaritonische Effekt wird über Verschiebung der Emissionslinie zu höheren Energien durch Wechselwirkung des Exzitonanteils nachgewiesen. Diese experimentellen Beobachtungen konnten mit Hilfe eines Gross-Pitaevskii-Differentialgleichungsansatzes erläutert und theoretisch nachgebildet werden.
Weiterhin zeigt der elektrische Polariton-Laser eine Bistabilität in seiner Emissionskennlinie an der polaritonischen Kondensationsschwelle. Die Hysterese hat ihren physikalischen Ursprung in der Lebenszeitabhängigkeit der Ladungsträger von der Dichte des Ladungsträgerreservoirs durch die progressive Abschirmung des inneren elektrischen Feldes. In dieser Arbeit wird zum tieferen Verständnis der Hysterese ein elektrisches Rauschen über den Anregungsstrom gelegt. Dieses elektrische Rauschen befindet sich auf der Mikrosekunden-Zeitskala und beeinflusst die Emissionscharakteristik, welche durch die Lebensdauer der Polaritonen im ps-Bereich bestimmt wird. Mit steigendem Rauschen wird ein Zusammenfall der Hysterese beobachtet, bis die Emissionscharakteristik monostabil erscheint. Diese experimentellen Befunde werden mit einem gekoppelten Ratengleichungssystem sowie mit Hilfe einer Gauss-verteilten Zufallsvariable in der Anregung modelliert und erklärt.
Die Hysterese ermöglicht außerdem den Nachweis eines optischen Schalteffekts über eine zusätzliche Ladungsträgerinjektion mit einem Laser weit über der Bandkante des Systems, um den positiven Rückkopplungseffekt zu erzeugen. Im Bereich der Hysterese wird das System auf den unteren Zustand elektrisch angeregt und dann mit Hilfe eines nicht-resonanten Laserpulses in den Kondensatszustand gehoben.
Polaritonfluss geleitet durch Kontrolle der lithographisch definierten Energielandschaft
Polaritonen können durch den photonischen Anteil weiterhin in Wellenleiterstrukturen eingesperrt werden, worin sie bei der Kondensation gerichtet entlang des Kanals mit nahe Lichtgeschwindigkeit fließen. Dies geschieht mit der Besonderheit über ihren Exzitonanteil stark wechselwirken zu können. Die Möglichkeit durch Lithographie solche eindimensionalen Kanäle zu definieren, wurde bereits in verschiedenen Prototypen für Polaritonen benutzt und untersucht. In dieser Arbeit werden zwei verschiedene, neue Ansätze zur Lenkung von gerichtetem Polaritonfluss vorgestellt: zum einen über die sogenannte Josephson-Kopplung zwischen zwei Wellenleitern, realisiert über halbgeätzte Spiegel und zum anderen über eine Mikroscheibe gekoppelt an zwei Wellenleiter. Der Begriff der Josephson-Kopplung ist hier angelehnt an den bekannten Effekt in Supraleitern, welcher phänomenologische Ähnlichkeiten aufweist. Die Verwendung in der Polaritonik ist historisch gewachsen. Die Josephson-Kopplung ermöglicht die Beobachung von Oszillationen des Polariton-Kondensats zwischen den Wellenleitern, in Abhängigkeit der verbleibenden Anzahl Spiegelpaare zwischen den Strukturen, wodurch eine definierte Selektion des Auskopplungsarms ermöglicht wird. Die Mikroscheibe funktioniert ähnlich einer Resonanztunneldiode. Sie ermöglicht eine Energieselektion der transmittierten Moden durch die Diskretisierung der Zustände in den niederdimensionalen Strukturen. Es ergibt sich die Bedingung, dass nur energetisch gleiche Niveaus zwischen Strukturübergängen koppeln können. Gleichzeitig erlaubt die Mikroscheibenanordnung eine Umkehrung der Flussrichtung.
Kohärenzeigenschaften und die Photonenstatistik von Polariton-Kondensaten unter photonischen Einschlusspotentialen
Die Kohärenzeigenschaften der Emission von Polariton-Kondensaten ist seit längerem ein aktives Forschungsfeld. Die noch ausstehenden Fragen betreffen die Beobachtung hoher Abweichungen von traditionellen, auf Inversion basierenden Lasersystemen (z.B. VCSELs). Diese haben selbst bei schwellenlosen Lasern einen Wert der Autokorrelationsfunktion zweiter Ordnung von Eins. Polariton-Kondensate jedoch zeigen erhöhte Werte in der Autokorrelationsfunktion, welches auf einen Mischzustand zwischen kohärentem und thermischem Licht hinweist.
In dieser Arbeit wurde ein systematischer Weg untersucht, die Kohärenzeigenschaften des Polariton-Kondensats denen eines traditionellen Lasers anzunähern. Dies geschieht über den lateralen photonischen Einschluss der Kondensate mittels lithographisch definierter Mikrotürmchen mit verschiedenen Durchmessern. In Kohärenzmessungen wird der Einfluss dieser Veränderung der Energielandschaft der Polariton-Kondensate auf die Autokorrelationseigenschaften zweiter Ordnung untersucht. Es wird ein direkter Zusammenhang zwischen großem Einschlusspotential und guten Korrelationseigenschaften nachgewiesen. Der Effekt wird theoretisch über den veränderten Einfluss der Phononen auf das Polariton-Relaxationsverhalten erklärt. Durch die stärkere Lokalisierung der Polaritonwellenfunktion in kleineren Mikrotürmchen wird die Streuwahrscheinlichkeit erhöht, was eine effizientere Relaxation in den Grundzustand ermöglicht. Dies verhindert zu starke Besetzungsfluktuationen der Grundmode in der Polariton-Lebenszeit, was bisher als Grund für die erhöhte Autokorrelation postuliert wurde.
Weiterhin wird eine direkte Messung der Photonenstatistik eines Polaritonkondensats entlang steigender Polaritondichte im Schwellbereich vorgestellt. Die Photonenstatistik eines thermischen Emitters zeigt einen exponentiellen Verlauf, während ein reiner Laser Poisson-verteilt emittiert. Der Zwischenbereich, der für einen Laser am Übergang zwischen thermischer und kohärenter Lichtquelle vorhergesagt wird, kann durch eine Überlagerung der beiden Zustände beschrieben werden. Über eine Anpassungsfunktion der gemessenen Verteilungsfunktionen kann der Phasenübergang des Kondensats mit Hilfe dem Anteil der kohärenten Partikel im System verfolgt werden. Dadurch, dass der gemessene Übergang dem Paradigma der thermisch-kohärenten Zustände folgt, wurde nachgewiesen, dass bei rötlicher Verstimmung die Interaktionen keinen signifikanten Anteil an der Ausbildung von Kohärenz im Polaritonsystem spielen.
Polarisationskontrolle von Polariton-Kondensaten
Die Polarisationseigenschaften des durch Polaritonenzerfall emittierten Lichts korrespondieren zum Spinzustand der Quasiteilchen. Unterhalb der Kondensationsschwelle ist diese Emission durch Spin-Relaxation der Ladungsträger unpolarisiert und oberhalb der Schwelle bildet sich unter bestimmten Voraussetzungen lineare Polarisation als Ordnungsparameter des Phasenübergangs aus. Der Prozess der stimulierten Streuung kann die (zirkulare) Polarisation des Lasers auch bei Anregung auf höheren Energien auf dem unteren Polaritonast erhalten. Dies resultiert aus sehr schneller Einnahme des Grundzustands, welche eine Spin-Relaxation verhindert. Bisher wurde, nach unserem Kenntnisstand, nur teilweise Erhaltung zirkularer Polarisation unter nicht-resonanter Anregung beobachtet. In dieser Arbeit wird vollständige zirkulare Polarisationserhaltung, energetisch 130 meV vom Kondensatszustand entfernt angeregt, nachgewiesen. Diese Polarisationserhaltung setzt an der Kondensationsschwelle ein, was auf den Erhalt durch stimulierte Streuung hinweist. Unter dieser Voraussetzung der Spinerhaltung erzeugt die linear polarisierte Anregung (als Überlagerung zirkularem Lichts beider Orientierungen) elliptisch polarisiertes Licht. Dies geschieht, weil eine linear polarisierte Anregung durch Fokussierung eines Objektivs leicht elliptisch wird. Der Grad der Elliptizität wird sowohl durch die Verstimmung zwischen Photon und Exziton Mode beeinflusst, als auch durch die Dichte im System. Dies kann erklärt werden über das spezielle Verhalten der Relaxationsprozesse auf dem unteren Polaritonast, welche von der transversal-elektrischen und transversal-magnetischen (TE-TM) energetischen Aufspaltung abhängen.
Weiterhin werden elliptische Mikrotürmchen untersucht, um den Einfluss dieses asymmetrischen photonischen Einschlusses auf die Kondensatseigenschaften herauszuarbeiten. Die Ellipse zwingt das Kondensat zu einer linearen Polarisation, welche sich entlang der langen Achse des Türmchens ausrichtet. In asymmetrischen Mikrotürmchen ist die Grundmode aufgespalten in zwei linear polarisierte Moden entlang der beiden orthogonal zueinander liegenden Hauptachsen, wobei die längere Achse das linear polarisierte Energieminimum des Systems bildet. Der Grad der linearen Polarisation nimmt mit geringerem Mikrotürmchendurchmesser und größerer Ellipzität zu. Dies geschieht durch erhöhten energetischen Abstand der beiden Moden. Bei Ellipsen mit einem langen Hauptachsendurchmesser von 2 Mikrometer und einem Achsenverhältnis von 3:2 kann ein nahezu vollständig linear polarisierter Zustand eines Polariton-Kondensats nachgewiesen werden.
Damit wurde erforscht, dass auch unter nicht-resonanter Anregung Exziton-Polariton-Kondensate experimentell und theoretisch jeglichen Spinzustand unter entsprechenden Anregungsbedingungen annehmen können.
The present thesis is devoted to the spectroscopic study of rare earth manganites RMnO3 (R = Gd, Dy, Tb, Eu(1 - x)Y(x)) in the submillimeter frequency range. A dynamic manifestation of a strong magnetoelectric coupling in these systems is the existence of electromagnons - spin waves excited by the electric component of the electromagnetic wave. The exact analytical solution of the Landau-Lifshitz equations obtained for cycloidal antiferromagnets builds the bridge between the inelastic neutron scattering and the optical experiments. A semi-quantitative agreement is achieved between the theory and the results by these two experimental techniques. Two suggested mechanisms of the magnetoelectric coupling, the inverse Dzyaloshinskii-Moriya (IDM) interaction and the symmetric Heisenberg exchange (HE) striction, are introduced in a perturbative manner. The qualitative conclusions regarding both static and dynamic electric properties are also in agreement with the experiment. GdMnO3 is the system in which the electromagnons were first detected at low frequencies. Far infrared measurements in GdMnO3 presented here have confirmed the existence of a second high frequency electromagnon at 75 reciprocal centimeter. The detection of an additional mode suggests the existence of at least short range ferroelectric order. Such order has not been observed in static experiments so far. The electromagnons in Eu(1 - x)Y(x)MnO3 helped to clarify the role of the rare earth magnetism. As the Y(3+) ions are diamagnetic and Eu(3+) ions possess Van Vleck paramagnetism only, it is the Mn subsystem that is primarily responsible for the magnetoelectric properties of rare earth manganites. The electromagnons in DyMnO3 and TbMnO3 do not change their excitation conditions upon the flop of the spin cycloid in external magnetic fields. This fact still lacks consistent theoretical explanation. Detailed measurements on TbMnO3 of different orientations have allowed to prove the existence of the IDM electromagnon. The study of DyMnO3 in external magnetic fields has shown that, depending on the Dy ordering, the electromagnons and static electric polarization can be either enhanced or suppressed. Thus, the magnetic order of rare earth moments still plays an important role. As a general result of the present work, the IDM interaction is capable to describe the static electric polarization and the weak electro-active excitation in the high-field phase of TbMnO3. The HE model is successful in explaining the high frequency electromagnon, including its excitation conditions and the spectral weight. However, both models are still unable to describe the energy and the spectral weight of the low frequency electromagnon. Further theoretical and experimental efforts are required in this direction.