The role of elastic interactions, particularly for the self-organized formation of periodically faceted interfaces, was investigated in this thesis for archetype organic-metal interfaces. The cantilever bending technique was applied to study the change of surface stress upon formation of the interface between 3,4,9,10-perylene-tetracarboxylic-dianhydride (PTCDA) and Ag(111). This system is known to form a chemisorptive bonding. Indeed, the sign and the coverage-dependence of the surface stress change are in agreement to models and previous measurements of chemisorptive systems in literature. While the adsorption of molecules into the large domains is associated with a negative, i.e. compressive stress change, the formation of domain boundaries in the molecular layer induces a stress change of opposite sign, increasing the surface stress. The magnitude of the surface stress change of (-0.30 +- 0.10} N/m reflects a relatively weak binding of a PTCDA molecule to each individual single silver atom. It is emphasized, however, that if normalized to the surface stress change per molecule, this value corresponds to a stress change of (-2.2 +- 0.2) eV per molecule which is in the order of the suspected binding energy of this system. Therefore, these experiments reveal elastic interactions to be of significant order of magnitude for this system class. Thereby, they add a new point of view to the understanding of these interfaces. Besides, since the results are in agreement with the well-known properties of this interface, they establish the cantilever bending technique in the field of organic-metal interfaces. The mere existence of a bending of the sample implies an interesting detail for the PTCDA/Ag(111) interface in particular. It is the first experimental evidence for a structural change in the topmost substrate layers upon adsorption of PTCDA on Ag(111). Since such a modification has significant implications for the interpretation of other experimental results, a further investigation with more quantitative structural methods appears necessary. The main focus of this work, however, was on the investigation of the formation of the long-range ordered, self-organized faceted PTCDA/Ag(10 8 7) interface. Reciprocal space maps of this interface were recorded both by spot profile analysis low energy electron diffraction (SPA-LEED) and low energy electron microscopy (LEEM) in selected area LEED mode. Complementary to the reciprocal data, also microscopic real-space LEEM data were used to characterize the morphology of this interface. Six different facet faces ((111), (532), (743), (954), (13 9 5), and (542)) were observed for the preparation path of molecular adsorption on the substrate kept at 550 K. Facet-sensitive dark-field LEEM localized these facets to grow in homogeneous areas of microscopic extensions. If the pristine mesoscopic orientation locally deviates from the average orientation, e.g. in pristine step density, locally different facet types are formed, distorting the otherwise regular mesoscopic pattern. Hence, the original mesoscopic orientation of the substrate strongly determines the degree of order of the faceted surface and the facet species formed. The temperature-dependence of the interface formation was studied in a range between 418 K and 612 K in order to learn more about the kinetics of the process. Additional steeper facets of 27° inclination with respect to the (111) surface were observed in the low temperature regime. Furthermore, using facet-sensitive dark-field LEEM, spatial and size distributions of specific facets were studied for the different temperatures. The nucleation density of the facets did not depend on temperature and can therefore be concluded not to be limited by diffusion. Moreover, the facet dimensions were statistically analyzed. The total island size of the facets follows an exponential distribution, indicating a random growth mode in absence of any mutual facet interactions. While the length distribution of the facets also follows an exponential distribution, the width distribution is peaked, reflecting the high degree of lateral order. This anisotropy is temperature-dependent and occurs starting above 478 K substrate temperature during growth. The peaked distribution indicates the presence of a long-range interaction which leads to the structural order of the self-organized grating. The origin of this long-range interaction was investigated combining three complementary in-situ methods, all providing new insights into the formation of faceted organic-metal interfaces: the cantilever bending technique, high-resolution low energy electron diffraction (SPA-LEED), and microscopy (LEEM). The cantilever bending technique was applied for the first time to a faceting system at all. Below the faceting transition temperature the surface stress change associated with the formation of the PTCDA/Ag(10 8 7) interface resembles in shape and magnitude the one observed for the reference interface PTCDA/Ag(111). But above the transition temperature the absolute surface stress change of (-0.67 +- 0.10) N/m observed for the faceted PTCDA/Ag(10 8 7) interface is considerably larger than for the previous cases. Moreover, the stress change happens in distinguishable stages with a clearly resolvable fine structure of regimes of positive and negative stress changes. These different regimes of surface stress change can be correlated to different stages of the structural phase transition observed by the structural in-situ methods. Thereby, morphological objects (i.e. the facets) are assigned to a specific stress character. Thus, domains of different stress character can be identified on the surface. These stress domains are the prerequisite to apply continuum descriptions of the self-ordering process based on elastic interactions. Hence, the results are the first experimental verification that these continuum descriptions are indeed also applicable to the whole system class of faceting organic-metal interfaces. In conclusion, the results provide strong evidence for elastic interactions being the physical origin of long-range order for this system. In addition, the clear correlation of structural phase transition and surface stress change regimes suggests surface stress to play also an important role for the kinetics of the system. Indeed, the system seems to try to limit the overall stress change during the interface formation by forming facets of positive and negative stress character. Hence, the selection of specific facets could depend on the corresponding stress character. Furthermore, the system seems willing to re-facet at high coverages in order to prevent imperfect domain boundaries which are associated with an increase of surface stress. Finally, template-assisted growth of lateral, heterorganic nanostructures has been explored. Therefore, self-assembled monolayers as a second archetype class of molecules were grown on partially covered PTCDA/Ag(10 8 7) interfaces. Indeed, using standard surface science techniques, the basic principle of this growth scheme was confirmed to be successful.
Albeit of high technological import, epitaxial self-assembly of CdSe/ZnSe QDs is non-trivial and still not clearly understood. The origin and attributes of these QDs are significantly different from those of their III-V and group-IV counterparts. For III-V and group-IV heterosystems, QD-formation is assigned to the Stranski Krastanow (SK) transition, wherein elastic relaxation of misfit strain leads to the formation of coherent three-dimensional (3D) islands, from a supercritically strained two-dimensional (2D) epilayer. Unfortunately, this phenomenon is inconspicuous for the CdSe/ZnSe heterosystem. Well-defined 3D islands are not readily formed in conventional molecular beam epitaxial (MBE) growth of CdSe on ZnSe. Consequently, several alternative approaches have been adopted to induce/enhance formation of QDs. This thesis systematically investigates three such alternative approaches, along with conventional MBE, with emphasis on the formation-mechanism of QDs, and optimization of their morphological and optical attributes. It is shown here that no distinct 3D islands are formed in MBE growth of CdSe on ZnSe. The surface of the CdSe layer represents a rough 2D layer, characterized by a dense array of shallow (<1nm) abutting mounds. In capped samples, the CdSe deposit forms an inhomogeneous CdZnSe quantum well (QW)-like structure. This ternary QW consists of local Cd-rich inclusions, which confine excitons three-dimensionally, and act as QDs. The density of such QDs is very high (~ 1012 cm-2). The QDs defined by the composition inhomogeneities of the CdZnSe QW presumably originate from the shallow mounds of the uncapped CdSe surface. By a technique wherein a CdSe layer is grown at a low temperature (TG = 230 °C) and subsequently annealed at a significantly higher temperature (TA =310 °C), tiny but distinct 3D islands are formed. In this work, the mechanism underlying the formation of these islands is reported. While the CdSe deposit forms a quasi-two-dimensional (quasi-2D) layer at TG = 230 °C, subsequent annealing at TA = 310 °C results in a thermally activated “up-climb” of adatoms onto two-dimensional clusters (or precursors) and concomitant nucleation of 3D islands. The areal density of QDs, achieved by this technique, is at least a decade lower than that typical for conventional MBE growth. It is demonstrated that further reduction is possible by delaying the temperature ramp-up to TA. In the second technique, formation of distinct islands is demonstrated by deposition of amorphous selenium (a-Se) onto a 2D CdSe epilayer at room temperature and its subsequent desorption at a higher temperature (TD = 230 °C). Albeit the self-assembled islands are large, they are severely truncated during subsequent capping with ZnSe, presumably due to segregation of Cd and Zn-alloying of the islands. The segregation phenomenon is analyzed in this work and correlated to the optical properties of the QDs. Additionally, very distinct vertical correlation of QDs in QD-superlattices, wherein the first QD-layer is grown by this technique and the subsequent ones by migration enhanced epitaxy (MEE), is reported. The process steps of the third variant technique, developed in course of this work, are very similar to those of the previous one-the only alteration being the substitution of selenium with tellurium as the cap-forming-material. This leads not only to large alteration of the morphological and optical attributes of the QDs, but also to formation of unique self-assembled island-patterns. Oriented dashes, straight and buckled chains of islands, and aligned island-pairs are formed, depending on the thickness of the Te-cap layer. The islands are partially alloyed with Te and emit luminescence at very low energies (down to 1.7 eV at room temperature). The Te cap layer undergoes (poly)crystallization during temperature ramp-up (from room temperature to TD) for desorption. Here, it is shown that the self-assembled patterns of the island-ensembles are determined by the pattern of the grain boundaries of the polycrystalline Te layer. Based on an understanding of the mechanism of pattern formation, a simple and “clean” method for controlled positioning of individual QDs and QD-based extended nanostructures, is proposed in this work. The studies carried out in the framework of this thesis provide not only a deeper insight into the microscopic processes governing the heteroepitaxial self-assembly of CdSe/ZnSe(001) QDs, but also concrete approaches to achieve, optimize, and control several technologically-important features of QD-ensembles. Reduction and control of QD-areal-density, pronounced vertical correlation of distinctly-defined QDs in QD-superlattices, and self-assembly of QD-based extended structures, as demonstrated in this work, might turn out to be beneficial for envisioned applications in information-, and communication-technologies.