Albeit of high technological import, epitaxial self-assembly of CdSe/ZnSe QDs is non-trivial and still not clearly understood. The origin and attributes of these QDs are significantly different from those of their III-V and group-IV counterparts. For III-V and group-IV heterosystems, QD-formation is assigned to the Stranski Krastanow (SK) transition, wherein elastic relaxation of misfit strain leads to the formation of coherent three-dimensional (3D) islands, from a supercritically strained two-dimensional (2D) epilayer. Unfortunately, this phenomenon is inconspicuous for the CdSe/ZnSe heterosystem. Well-defined 3D islands are not readily formed in conventional molecular beam epitaxial (MBE) growth of CdSe on ZnSe. Consequently, several alternative approaches have been adopted to induce/enhance formation of QDs. This thesis systematically investigates three such alternative approaches, along with conventional MBE, with emphasis on the formation-mechanism of QDs, and optimization of their morphological and optical attributes. It is shown here that no distinct 3D islands are formed in MBE growth of CdSe on ZnSe. The surface of the CdSe layer represents a rough 2D layer, characterized by a dense array of shallow (<1nm) abutting mounds. In capped samples, the CdSe deposit forms an inhomogeneous CdZnSe quantum well (QW)-like structure. This ternary QW consists of local Cd-rich inclusions, which confine excitons three-dimensionally, and act as QDs. The density of such QDs is very high (~ 1012 cm-2). The QDs defined by the composition inhomogeneities of the CdZnSe QW presumably originate from the shallow mounds of the uncapped CdSe surface. By a technique wherein a CdSe layer is grown at a low temperature (TG = 230 °C) and subsequently annealed at a significantly higher temperature (TA =310 °C), tiny but distinct 3D islands are formed. In this work, the mechanism underlying the formation of these islands is reported. While the CdSe deposit forms a quasi-two-dimensional (quasi-2D) layer at TG = 230 °C, subsequent annealing at TA = 310 °C results in a thermally activated “up-climb” of adatoms onto two-dimensional clusters (or precursors) and concomitant nucleation of 3D islands. The areal density of QDs, achieved by this technique, is at least a decade lower than that typical for conventional MBE growth. It is demonstrated that further reduction is possible by delaying the temperature ramp-up to TA. In the second technique, formation of distinct islands is demonstrated by deposition of amorphous selenium (a-Se) onto a 2D CdSe epilayer at room temperature and its subsequent desorption at a higher temperature (TD = 230 °C). Albeit the self-assembled islands are large, they are severely truncated during subsequent capping with ZnSe, presumably due to segregation of Cd and Zn-alloying of the islands. The segregation phenomenon is analyzed in this work and correlated to the optical properties of the QDs. Additionally, very distinct vertical correlation of QDs in QD-superlattices, wherein the first QD-layer is grown by this technique and the subsequent ones by migration enhanced epitaxy (MEE), is reported. The process steps of the third variant technique, developed in course of this work, are very similar to those of the previous one-the only alteration being the substitution of selenium with tellurium as the cap-forming-material. This leads not only to large alteration of the morphological and optical attributes of the QDs, but also to formation of unique self-assembled island-patterns. Oriented dashes, straight and buckled chains of islands, and aligned island-pairs are formed, depending on the thickness of the Te-cap layer. The islands are partially alloyed with Te and emit luminescence at very low energies (down to 1.7 eV at room temperature). The Te cap layer undergoes (poly)crystallization during temperature ramp-up (from room temperature to TD) for desorption. Here, it is shown that the self-assembled patterns of the island-ensembles are determined by the pattern of the grain boundaries of the polycrystalline Te layer. Based on an understanding of the mechanism of pattern formation, a simple and “clean” method for controlled positioning of individual QDs and QD-based extended nanostructures, is proposed in this work. The studies carried out in the framework of this thesis provide not only a deeper insight into the microscopic processes governing the heteroepitaxial self-assembly of CdSe/ZnSe(001) QDs, but also concrete approaches to achieve, optimize, and control several technologically-important features of QD-ensembles. Reduction and control of QD-areal-density, pronounced vertical correlation of distinctly-defined QDs in QD-superlattices, and self-assembly of QD-based extended structures, as demonstrated in this work, might turn out to be beneficial for envisioned applications in information-, and communication-technologies.
Die vorliegende Arbeit beschäftigt sich mit den strukturellen Aspekten einer adsorbat-induzierten Facettierung von vizinalen Ag(111)-Oberflächen. Bei dem Adsorbat handelte es sich um das organische Molekül Perylen-3,4,9,10-Tetracarbonsäure-Dianhydrid (PTCDA). Die Experimente wurden unter Ultrahochvakuum-Bedingungen durchgeführt, die Charakterisierung erfolgte hauptsächlich mit den Messmethoden Rastertunnelmikroskopie (STM) und niederenergetische Elektronenbeugung (LEED). Das planare Farbstoffmolekül PTCDA adsorbiert präferentiell an den Stufenkanten der verwendeten 8.5° Ag(111)-Vizinaloberflächen und induziert bei geeigneten Präparationsbedingungen eine Rekonstruktion in stark gestufte Facettenflächen und in stufenfreie (111)-Terrassen. Die beobachteten Facetten sind für das System PTCDA/Ag charakteristisch und stellen durch eine molekulare Überstruktur richtungsselektiv stabilisierte Ag-Kristallebenen dar. Durch die Variation der Stufenrichtung der Startoberfläche wurde eine Vielzahl von Facettentypen erhalten und nach Miller indiziert. In ihrer Gesamtheit erlauben sie einen Rückschluss auf das Aussehen der Gleichgewichtskristallform eines mit PTCDA bedeckten Ag-Kristalles und damit auf das richtungsabhängige Benetzungsverhalten von Ag. Aus der Sicht des Substrates bewirkt das Adsorbat eine massive Erhöhung der Steifheit der Stufen. Die durch eine molekulare Überstruktur stabilisierten Facettenflächen übernehmen die in der Kristallstruktur des Substrates angelegten Stufenrichtungen. Die gefundene Ausbildung von zwei typischen Facettensteigungen ist jedoch nicht durch die Ag-Kristallstruktur motivierbar. Die Facettierung wurde im Rahmen einer speziellen Adaption des Konzepts der Thermodynamik auf ebene gestufte Oberflächen als Orientierungsphasenseparation beschrieben. Dieses Konzept erlaubt eine korrekte Beschreibung der beobachteten lokalen Phänomene und zeigt zudem auf, dass das molekulare Gas, welches in den Messungen nicht erfasst wurde, eine wichtige Rolle bei der Rekonstruktion spielt. Es ergaben sich wichtige Indizien für die Existenz einer kritischen Inselgröße für PTCDA auf Ag(111). Es wurde eine vollständige strukturelle Analyse aller stabilen molekularen Überstrukturen auf vizinalen Ag(111)-Oberflächen durchgeführt. Es wurden insgesamt 16 solcher Überstrukturen gefunden, von denen bisher nur 3 Strukturen bekannt und veröffentlicht waren. Dichte und Kommensurabilität der Facettenüberstrukturen sind systematisch vom Stufentyp der Oberfläche abhängig. Die Frage nach dem Ursprung der beiden charakteristischen Facettensteigungen ist mit der Existenz von zwei Typen von Überstrukturgrenzen verknüpft. Die Grenze bestimmt die Lage der fischgrätartigen Überstruktur zu den Stufenkanten und die Länge und die Breite des Moleküls die beiden charakteristischen Stufenabstände. Letzteres geschieht vermöge einer lokalen Wechselwirkung der PTCDA-Moleküle mit den Stufen. Die Überstrukturgrenzen erweisen sich als wichtiges Element der Rekonstruktion. Es wurden außerdem die Abhängigkeiten der verschiedenen, aneinander angrenzenden Überstrukturen aufgezeigt. Auf den (111)-Terrassen fanden sich 3 metastabile Ausnahme-Strukturen, welche einen vertieften Einblick in die komplexe Bildungskinetik der bisher bekannten stabilen (111)-Struktur erlauben. Die Facetten bilden zusammen mit den benachbarten (111)-Terrassen regelmäßige, einem Reflexionsgitter ähnliche Muster mit einer Strukturweite von 5 bis 75nm. Die beobachteten Strukturweiten erreichen bei ausgedehntem Tempern typische Maximalwerte. STM-Messungen zeigen den Einfluss einer langreichweitigen Wechselwirkung zwischen den Facetten, vermittelt über elastische Eigenschaften des Substrates. Die Muster können als selbstorganisierte Zweiphasensysteme im thermodynamischen Gleichgewicht erklärt werden. Die Facetten wirken wie repulsiv wechselwirkende Defekte in einem elastischen Medium. Die Eignung dieser Muster als Templat wurde in Kooperation mit einer anderen Arbeitsgruppe am Beispiel der selektiven Deposition von Eisen belegt.