After the discovery of three-dimensional topological insulators (TIs), such as tetradymite chalcogenides Bi$_2$Se$_3$, Bi$_2$Te$_3$ and Sb$_2$Te$_3$ – a new class of quantum materials characterized by their unique surface electronic properties – the solid state community got focused on topological states that are driven by strong electronic correlations and magnetism. An important material class is the magnetic TI (MTI) exhibiting the quantum anomalous Hall (QAH) effect, i.e. a dissipationless quantized edge-state transport in the absence of external magnetic field, originating from the interplay between ferromagnetism and a topologically non-trivial band structure. The unprecedented opportunities offered by these new exotic materials open a new avenue for the development of low-dissipation electronics, spintronics, and quantum computation. However, the major concern with QAH effect is its extremely low onset temperature, limiting its practical application. To resolve this problem, a comprehensive understanding of the microscopic origin of the underlying ferromagnetism is necessary.
V- and Cr-doped (Bi,Sb)$_2$Te$_3$ are the two prototypical systems that have been widely studied as realizations of the QAH state. Finding microscopic differences between the strongly correlated V and Cr impurities would help finding a relevant model of ferromagnetic coupling and eventually provide better control of the QAH effect in these systems. Therefore, this thesis first focuses on the V- and Cr-doped (Bi,Sb)$_2$Te$_3$ systems, to better understand these differences. Exploiting the unique capabilities of x-ray absorption spectroscopy and magnetic circular dichroism (XAS/XMCD), combined with advanced modeling based on multiplet ligand-field theory (MLFT), we provide a detailed microscopic insight into the local electronic and magnetic properties of these systems and determine microscopic parameters crucial for the comparison with theoretical models, which include the $d$-shell filling, spin and orbital magnetic moments. We find a strongly covalent ground state, dominated by the superposition of one and two Te-ligand-hole configurations, with a negligible contribution from a purely ionic 3+ configuration. Our findings indicate the importance of the Te $5p$ states for the ferromagnetism in (Bi, Sb)$_2$Te$_3$ and favor magnetic coupling mechanisms involving $pd$-exchange. Using state-of-the-art density functional theory (DFT) calculations in combination with XMCD and resonant photoelectron spectroscopy (resPES), we reveal the important role of the $3d$ impurity states in mediating magnetic exchange coupling. Our calculations illustrate that the kind and strength of the exchange coupling varies with the impurity $3d$-shell occupation. We find a weakening of ferromagnetic properties upon the increase of doping concentration, as well as with the substitution of Bi at the Sb site. Finally, we qualitatively describe the origin of the induced magnetic moments at the Te and Sb sites in the host lattice and discuss their role in mediating a robust ferromagnetism based on a $pd$-exchange interaction scenario. Our findings reveal important clues to designing higher $T_{\text{C}}$ MTIs.
Rare-earth ions typically exhibit larger magnetic moments than transition-metal ions and thus promise the opening of a wider exchange gap in the Dirac surface states of TIs, which is favorable for the realization of the high-temperature QAH effect. Therefore, we have further focused on Eu-doped Bi$_2$Te$_3$ and scrutinized whether the conditions for formation of a substantial gap in this system are present by combining spectroscopic and bulk characterization methods with theoretical calculations. For all studied Eu doping concentrations, our atomic multiplet analysis of the $M_{4,5}$ x-ray absorption and magnetic circular dichroism spectra reveals a Eu$^{2+}$ valence, unlike most other rare earth elements, and confirms a large magnetic moment. At temperatures below 10 K, bulk magnetometry indicates the onset of antiferromagnetic ordering. This is in good agreement with DFT results, which predict AFM interactions between the Eu impurities due to the direct overlap of the impurity wave functions. Our results support the notion of antiferromagnetism coexisting with topological surface states in rare-earth doped Bi$_2$Te$_3$ and corroborate the potential of such doping to result in an antiferromagnetic TI with exotic quantum properties.
The doping with impurities introduces disorder detrimental for the QAH effect, which may be avoided in stoichiometric, well-ordered magnetic compounds. In the last part of the thesis we have investigated the recently discovered intrinsic magnetic TI (IMTI) MnBi$_6$Te$_{10}$, where we have uncovered robust ferromagnetism with $T_{\text{C}} \approx 12$ K and connected its origin to the Mn/Bi intermixing. Our measurements reveal a magnetically intact surface with a large moment, and with FM properties similar to the bulk, which makes MnBi$_6$Te$_{10}$ a promising candidate for the QAH effect at elevated temperatures. Moreover, using an advanced ab initio MLFT approach we have determined the ground-state properties of Mn and revealed a predominant contribution of the $d^5$ configuration to the ground state, resulting in a $d$-shell electron occupation $n_d = 5.31$ and a large magnetic moment, in excellent agreement with our DFT calculations and the bulk magnetometry data. Our results together with first principle calculations based on the DFT-GGA$+U$, performed by our collaborators, suggest that carefully engineered intermixing plays a crucial role in achieving a robust long-range FM order and therefore could be the key for achieving enhanced QAH effect properties.
We expect our findings to aid better understanding of MTIs, which is essential to help increasing the temperature of the QAH effect, thus facilitating the realization of low-power electronics in the future.
Soft x-ray spectroscopic study of methanol and glycine peptides in different physical environments
(2017)
Ion-specific effects occur in a huge variety of aqueous solutions of electrolytes and larger molecules like peptides, altering properties such as viscosity, enzyme activity, protein stability, and salting-in and salting-out behavior of proteins. Typically, these type of effects are rationalized in terms of the Hofmeister series, which originally orders cations and anions according to their ability to enhance or suppress the solubility of proteins in water. This empirical order, however, is still not understood yet. Quite some effort was made to gain a molecular level understanding of this phenomenon, yet no consensus has been found about the underlying mechanisms and the determination and localization of the interaction sites.
Resonant inelastic soft x-ray scattering (RIXS) combines x-ray emission (XES) and absorption spectroscopies (XAS), probing the partial local density of states of both occupied and unoccupied electronic states and is thus a promising candidate to shed more light onto the issue. The studies presented in this work are directed towards an improved understanding of the interaction between salts and peptides. In order to address this topic, the impact of different physical environments on the electronic structure of small molecules (i.e., methanol and glycine derived peptides) is investigated systematically using soft x-ray spectroscopic methods, corroborated with density functional theory (DFT) calculations.
In a first step, molecules without any interactions to the surrounding are investigated, using gas-phase methanol as a model system. Thereby, the local and element specific character of RIXS is demonstrated and used to separately probe the local electronic structure of methanol’s hydroxyl and methyl group, respectively. The attribution of the observed emission features to distinct molecular orbitals is confirmed by DFT calculations, which also quantitatively explain the different relative intensities of the emission features. For resonant excitation of the O K pre-edge absorption resonance, strong isotope effects are found that are explained by dynamical processes at the hydroxyl group. This serves as an excellent example for possible consequences of a local change in the geometric structure or symmetry of a molecule on its electronic structure.
In the following, the sample system is expanded to the amino acid glycine and its smallest derived peptides diglycine and triglycine. As a first step, they are studied in their crystalline form in solid state. Again, a comprehensive picture of the electronic structure is developed by measuring RIXS maps at the oxygen and nitrogen K absorption edge, corroborated by DFT calculations. Similar to the case of methanol, dynamic processes at the protonated amino group of the molecules after exciting the nitrogen atom have a strong influence on the emission spectra. Furthermore, it is shown that RIXS can be used to selectively excite the peptide nitrogen to probe the electronic structure around it. A simple building block approach for XES spectra is applied to separate the contribution of the emission attributed to transitions into core holes at the peptide and the amino nitrogen, respectively.
In the aqueous solution, the surrounding water molecules slightly change the electronic structure, probably via interactions with the charged functional groups. The effects on the x-ray emission spectra, however, are rather small. Much bigger changes are observed when manipulating the protonation state of the functional groups by adjusting the pH value of the solution. A protonation of the carboxyl group at low pH values, as well as a deprotonation of the amino group at high pH values lead to striking changes in the shape of the RIXS maps. In a comprehensive study of glycine’s XES spectra at varying pH values, changes in the local electronic structure are not only observed in the immediate surrounding of the manipulated functional groups but also in more distant moieties of the molecule.
Finally, the study is extended to mixed aqueous solutions of diglycine and a variety of different salts as examples for systems where Hofmeister effects are observed. To investigate the influence of different cations and anions on the electronic structure of diglycine, two series of chlorine and potassium salts are used. Ion-specific effects are identified for both cases. Some of the changes in the x-ray emission spectra of diglycine in the mixed solutions qualitatively follow the Hofmeister series as a function of the used salt. The observed trends thereby indicate an increased interaction between the electron density around the peptide oxygen with the cations, whereas anions seem to interact with the amino group of the peptide.
This thesis focuses on the investigation of the electronic structure of amino acids and
salts in aqueous solution using X-ray spectroscopic methods. Both material groups are
of fundamental importance with regards to many physiological reactions, especially
for the Hofmeister effect which describes the solubility of proteins in salt solutions.
Hence, the investigation of the electronic structure of amino acids and the influence of
ions on the hydrogen bonding network of liquid water are important milestones to a
deeper understanding of the Hofmeister series.
Besides investigating the electronic structure of amino acids in aqueous solution,
the spectra were used to develop a building block model of the spectral fingerprints of
the functional groups and were compared to spectral signatures of suitable reference
molecules. In the framework of this thesis, it is shown that the building block approach
is a useful tool with allows the interpretation of spectral signatures of considerably
more complex molecules
In this work, the focus lies on the investigation of the occupied and unoccupied
electronic states of molecules in solid state, as well as in aqueous solution. Hereby,
different X-ray spectroscopic methods were applied. X-ray emission spectroscopy
(XES) was used to probe the occupied electronic structure of the solution, while the
unoccupied electronic structure was addressed by using X-ray absorption spectroscopy
(XAS). Finally, resonant inelastic X-ray scattering (RIXS) as a combination of XAS
and XES measurements provides the combined information about the unoccupied and
occupied molecular levels. The element specific character of the three measurement
methods is a feature which allows the investigation of the local electronic structure of
a single functional group. With RIXS, also non-equivalent atoms of the same element
can be addressed separately.
Within this thesis firstly, a library of the XE spectra of all 20 proteinogenic amino
acids in zwitterionic form is presented. From this sample-set XES fingerprints of
the protonated alpha-amino group NH3+ and the deprotonated carboxylic group COO- were evaluated and used to identify the XES fingerprints of the nitrogen and oxygen
containing functional groups of the side chains of the amino acids. The data is discussed
based on a building block approach. Furthermore, the XE spectra of the functional
groups of lysine and histidine, namely the NH2 group and the C3N2H4 ring structure,
are both compared to XE spectra of suitable reference molecules (imidazole, ammonia
and methylamine). It is found that the XE and RIXS spectra of the side chains of lysine
and histidine show large similarities to the XE spectra of the reference molecules. This
agreement in the XE and RIXS spectra allows a qualitative investigation of XE and
RIXS spectra of more complex amino acids using the XE and RIXS spectra of suitable
reference molecules.
The chemical structure of histidine and proline is quite different from the structures
of the other proteinogenic amino acids. Due to the unique chemical structure of
the side chain which in both cases consists of a heterocyclic ring structure, these two
amino acids were investigated in more detail. Zubavichus et al. [1] have shown that
amino acids are decomposing while exposed to X-ray radiation of the experiment. The
damage is irreversible and molecular fragments can adsorb on the membrane of the
experimental setup. This contamination can also create a spectral signature which
then overlaps with the signal of the solution and which complicates the interpretation
of the data. To record spectra which are free from contributions of adsorbed molecular
fragments on the membrane, the adsorption behavior was investigated.
In contrast to the solid phase in which the amino acids are present as salts in one
electronic conformation, the charge state of the amino acids can be manipulated in
aqueous solution by tuning the pH-value. By doing this, all possible charge states are
accessible (cation, anion, zwitterion). In this work it is shown that also the spectra
of the different charge states can be modeled by the spectra of suitable reference
molecules using the building block approach. The spectral changes occurring upon
protonation and deprotonation of the functional groups are explored and verified by
comparing them to theoretical calculations.
The comparison with measurements of pyrrolidine show that the electronic structure
which surrounds the nitrogen atom of proline is strongly influenced by the
ring structure of the side chain. Furthermore, the proline, pyrrolidine, and histidine
molecules are also degrading during the liquid sample measurements. This can be
observed by the detection of a new spectral component which increases with the
measurement time originating from the window membrane. In all cases, the speed of
the agglomeration of molecular fragments at the membrane was observed to be highly
sensitive to the pH value of the solution.
To understand the Hofmeister series, also the impact of the salt ions have to be
investigated. In this study the influence of potassium chloride (KCl) on the hydrogen
bond network of water was studied by using non-resonantly excited XES as well as
RIXS. A decreased dissociation of hydrogen molecules and changes in the molecular
vibrations could be detected. These changes were interpreted with a molecular
reorganization of the water molecules and a decreased number of hydrogen bonds.
Within the framework of this thesis the mechanisms of growth and reorganisation of surfaces within the first few layers were investigated that are the basis for the fabrication of high quality thin films and interfaces. Two model systems, PTCDA/Ag(111) and CdSe/ZnSe quantum dots (QD), were chosen to study such processes in detail and to demonstrate the power and improvements of the aberration corrected spectromicroscope SMART [1] simultaneously. The measurements benefit especially from the enhanced transmission of the microscope and also from its improved resolution. SMART, the first double–aberration corrected instrument of its kind [2], provided comprehensive methods (LEEM/PEEM, μ–LEED, μ–XPS) to study in–situ and in real time the surface reorganisation and to determine morphology, local structure and local chemical composition of the resulting thin film. Complementarily, a commercial AFM [3] was used ex–situ. XPEEM and μ–XPS measurements were made possible by attaching SMART to the high flux density beamline of the soft–X–ray source BESSY–II [4]. PTCDA/Ag(111) – Growth and structure of the first two layers Although PTCDA/Ag(111) is one of the most intensely studied model systems for the growth of organic semiconductor thin films, it still offers new insights into a complex growth behaviour. This study enlightens the temperature dependant influence of morphological features as small as monatomic Ag steps on the growth process of the first two layers. At low temperatures, single Ag steps act as diffusion barriers. But interdiffusion was observed already for the 2nd layer whereas domain boundaries in the 1st PTCDA–layer persist for crystallite growth in the 2nd layer. 1st layer islands are more compact and the more dendritic development of the 2nd layer indicates reduced interaction strength between 2nd and 1st layer. These findings were explained by a model consisting of structural and potential barriers. The second part of the PTCDA study reveals a variety of phases that appears only if at least two layers are deposited. Besides the six known rotational domains of the interface system PTCDA/Ag(111) [5], a further manifold of structures was discovered. It does not only show a surprising striped image contrast, but the 2nd layer also grows in an elongated way along these so–called ’ripples’. The latter show a rather large period and were found in a wide temperature range. Additionally the μ-LEED pattern of such a domain shows a new super–superstructure as well. This phase is explained by a structural model that introduces a rotated, more relaxed domain in the 2nd layer that does not exist in the first layer. Its structural parameters are similar to those of the bulk unitcells of PTCDA. The model is confirmed by the observation of two different rotational domains that grow on top of one single ’substrate’ domain in the 1st layer. The orientations of the ripple phases fit as well to the predictions of the model. The growth direction along the ripples corresponds to the short diagonal of the super–superstructure unitcell with diamond–like shape. CdSe/ZnSe – Inverse structuring by sublimation of an α-Te cap With the second model system the formation of CdSe quantum dots (QD) from strained epi-layers was investigated. In this case the structures do not form during deposition, but rather during sublimation of the so–called ‘ignition cap’. For these pilot experiments not only the process of QD formation itself was of interest, but also the portability of the preparation and the prevention of contaminations. It was found that the α-Se is well suited for capping and the last step of the QD preparation, the sublimation of the α-Te cap, needs a sufficiently high rate in rise of temperature. Subsequently the cap, the process of desorption and the final surface with the quantum structures were investigated in detail. The cap was deposited by the MBE-group in Würzburg as an amorphous Te layer but was found to contain a variety of structures. Holes, cracks, and micro–crystallites within an α-Te matrix were identified. Sublimation of the “ignition cap” was observed in real–time. Thus the discovered cap-structures could be correlated with the newly formed features as, e.g., QDs on the bare CdSe surface. Since CdSe/ZnSe QDs prefer to form in the neighbourhood of the Te μ–crystallites, Te was found to play a major role in their formation process. Different explanations as the impact of Te as a surfactant, an enhanced mobility of adatoms or as stressor nuclei are discussed. The spectromicroscopic characterisation of the CdSe surface with QDs revealed the crystallographic directions. An increased Cd signal of the film was found at positions of former holes. Several possibilities as segregation or surface termination are reviewed, that might explain this slight Cd variation. Therewith, an important step to a detailed understanding of the complex reorganisation process in coating systems could be achieved.
In this thesis, soft x-ray absorption spectroscopy (XAS) and resonant inelastic x-ray scattering (RIXS) studies of the electronic structure of selected organic molecules and liquids were carried out. The first part focuses on the used experimental techniques and the development of the instrumentation necessary for these studies, namely a soft x-ray spectrometer, and a temperature-controlled flow-through liquid cell. The former was optimized by a special analytical ray tracing method developed exclusively for this purpose. Due to its high transmission, the spectrometer facilitates a novel experimental approach of recording comprehensive 'RIXS maps', which are 2-dimensional plots of x-ray scattering intensities as a function of both, excitation and emission photon energy. The liquid cell extends these possibilities to the study of liquids, especially the interaction of molecules in liquids and their chemical reactions under well-controlled conditions. Organic molecules have attracted considerable attention in the last decade. The intense research activities related to these materials have two main motivations: on the one hand, organic molecules have a technological application as building blocks of organic semiconductors, while, on the other hand, organic molecules are the functional elements in biological systems. In order to cost-effectively produce optimized organic electronic devices, a fundamental knowledge of the electronic properties of the organic molecules interface is necessary. Therefore, many studies of the electronic structure of potential candidates for organic electronics exist. Two of these candidates, namely C60 and well-ordered multilayers PTCDA on a Ag(111) surface are investigated in this thesis. For the study of C60 molecules, a comprehensive 'RIXS map' was recorded and analyzed. The RIXS map taken in only 25 minutes allows a quantitative analysis of energy losses, yielding for example the HOMO-LUMO distance. It also identifies a core-excitonic state and facilitates a quantitative comparison of its binding energy with that of valence excitons in C60. Furthermore, decay channel-selective partial fluorescence yield XAS spectra can be extracted from the RIXS map, yielding information on the population of the core-excitonic state as a function of excitation energy. As a second model system of organic molecules relevant for organic electronics, PTCDA was chosen. The complex electronic structure of the occupied states of a highly ordered, flat-lying PTCDA multilayer on a Ag(111) surface was investigated by symmetry-resolved resonant x-ray emission spectroscopy. The rapidly occurring beam damage effects were characterized on the basis of irradiation-time dependent series of C and O x-ray emission spectra. Upon varying the excitation energy and emission geometry, atom- and symmetry-specific carbon K emission spectra with negligible beam damage effects were obtained that allow to distinguish between electronic states with sigma and pi symmetry. A density functional theory calculation of the PTCDA molecule reproduces the energy positions of the most prominent emission features remarkably well. In addition, the energy positions of the sigma and pi emissions agree well with the calculated energies of the respective orbitals. In order to shed light on the second aspect of organic molecules, namely their role in biological systems, first a detailed investigation of the electronic structure and proton dynamics of liquid water as the medium of most chemical and biochemical reactions was carried out. Therefore, a comprehensive oxygen K RIXS map of liquid water was recorded and analyzed in great detail. A temperature-dependent comparison with XAS and RIXS data of D2O, NaOH, and NaOD leads to the conclusion, that ultra-fast dissociation takes place in liquid water on the timescale of the oxygen 1s core hole lifetime, resulting in a characteristic spectral contribution in the RIXS spectra. The dissociation is promoted by intact hydrogen bonds with neighboring molecules. In consequence, the rate of dissociation directly depends on the initial hydrogen bond configuration. In the next step towards biologically relevant systems, the nitrogen K edges of the amino acids glycine and histidine were investigated in powderous form as well as in their native environment, namely in aqueous solution. X-ray absorption and emission spectra of the aqueous solutions were analyzed at pH-values of 6 and for glycine also at pH 12 and compared to the spectra of powders. A pH-value of 12 causes deprotonation of the amino group, leading to significant changes in the nitrogen spectra as compared to pH 6. The results from these four examples demonstrate that a wealth of novel information can be obtained by using the new experimental tools developed in this thesis, namely a highly sensitive x-ray spectrometer and a flow-through liquid cell.
This thesis was dedicated to the studies of the electronic and chemical properties of liquids and solutions using soft x-ray spectroscopies. The used photon-in-photon-out methods namely x-ray absorption spectroscopy (XAS), x-ray emission spectroscopy (XES), and resonant inelastic x-ray scattering (RIXS) appeared to be an excellent choice for these studies. In the framework of this thesis, the necessary experimental setup for using the above mentioned experimental techniques on liquids was developed. Hereby, a new flow-through liquid cell was introduced which simplifies the studies of liquids and solutions. The cell design is very flexible and thus can be modified for gases and liquid/solid interfaces. With this cell it is possible to study the samples under well-controlled conditions (temperature and flow rate). The novel flow-through liquid cell is part of the new SALSA synchrotron endstation including an electron analyzer and a novel high-resolution, high-transmission soft x-ray spectrometer. The latter makes it possible to measure two-dimensional RIXS maps in a very short time, which include the full excitation and emission information in one plot. Making use of the new instrumentation, a variety of different liquids and solutions were investigated. As first system, aqueous solutions of sodium hydroxide (NaOH) and sodium deuteroxide (NaOD) were investigated. In the XAS as well as in the XES spectra a pronounced concentration dependence was found. At non-resonant energies, the spectra are dominated by the solvent and thus look similar to water. Making use of the pre-pre-edge in the absorption spectra which can exclusively be attributed to OH- / OD- it was possible to extract the resonant emission spectra of the ions which show an indication for proton dynamics during the core-hole lifetime. For the solid state NaOH XES spectra it was possible to reveal a high energetic shoulder and a low energetic shoulder at the high energy emission feature. These shoulders can be assigned to self-dissociation processes where OH- forms O2- ions and H2O. The study of NaOH was also of interest for the studies of the amino acids, which were in the focus of the next part, since the pH-values of the respective solutions were controlled by NaOH. In the next part of this thesis, amino acid solutions were investigated. Amino acids are the building blocks of peptides and proteins and thus important for life science. The investigated representatives were glycine, the simplest amino acid, and lysine, an amino acid with two amine groups. Both amino acids react on pH-value changes at the amine group where the local environment at the nitrogen atom changes (NH2 ↔ NH3+). A strong change of the spectra induced by this protonation/deprotonation could be found. Furthermore, for low pH-values (protonated amine groups) the amine groups are influenced by strong proton dynamics. First DFT calculations confirm the dissociation model of the amino acids. Qualitatively the high energy peak in the N K XES spectra can be attributed to the deprotonated amine group and the low energy area for the protonated amine group. Besides amino acids, alcohols and acids are important in biological processes. Therefore, the smallest alcohol (methanol) and the smallest carboxylic acid (acetic acid) were under investigation. For the liquid methanol XES spectra a very good agreement with DFT calculations of gas phase methanol could be found. This observation suggests that the influence of the environment (hydrogen bonding) on the spectra is small. The achieved spectra are in good agreement with DFT calculations found in literature. It was possible to selectively excite the two non-equivalent oxygen atoms in acetic acid and to reveal the carboxyl specific C K XES. The carbon XAS spectra showed strong differences compared to gas phase measurements which might be a hint for the influence of the hydrogen bond network. The investigation of the electronic and chemical properties of liquids and solutions is a very young field of research and the results presented in this thesis show that it is a very interesting topic. The presented results can be seen as the fundamental frame work for all following studies. With the understanding of basic, i.e., simple, systems as shown in this work it will be possible to understand complex biological systems in their native environment, e.g., peptides and proteins, which are the building blocks of life.
Im Rahmen dieser Arbeit wurde eine neuartige Methode entwickelt, mit der es möglich ist, Magnetisierungsverläufe ausgewählter Schichten und Grenzflächen in dünnen Schichtsystemen zu bestimmen. Diese Resonante Magnetische Röntgenreflektometrie (XRMR: X-ray Resonant Magnetic Reflectometry) kombiniert die Methode der konventionellen Röntgenreflektometrie mit resonanten magnetischen Effekten, die an Absorptionskanten magnetischer Atome auftreten. Analog zur herkömmlichen Reflektometrie, die Aussagen über Schichtdicken und vertikale Grenzflächenrauhigkeiten zulässt, liefert die XRMR das tiefenabhängige magneto-optische Profil der untersuchten magnetischen Schicht. Durch die Aufnahme zweier Reflexionsspektren bei invertierter Helizität des einfallenden Röntgenstrahls oder Umkehr der Magnetisierungsrichtung der Probe in der Nähe der Absorptionskante eines magnetischen Elements erhält man als Messsignal das Asymmetrieverhältnis, das die Information über das tiefenabhängige Magnetisierungsprofil der untersuchten Schicht enthält. Zur Anpassung an die gemessene Asymmetrie über ein optisches Näherungsverfahren ist die Modellierung der optischen Konstanten der magnetischen Schicht oder Grenzfläche notwendig, die hierzu in viele dünne Einzelschichten künstlich aufgeteilt wird. Wichtig hierbei ist die korrekte Bestimmung der dispersiven und absorptiven Ladungsanteilen des komplexen Brechungsindex durch vorherige Messung des Absorptionskoeffizienten und der Berechnung der Dispersion über die Kramers-Kronig-Relation. XRMR-Experimente wurden an Pt/Co-Schichtsystemen an den Synchrotronstrahlungsquellen HASYLAB/Hamburg und BESSYII/Berlin durchgeführt, um die Anwendbarkeit der Messmethodik im harten und weichen Röntgenbereich zu demonstrieren. Durch die intrinsische Elementselektivität resonanter Streuung und die Verstärkung magnetischer Effekte durch Interferenzerscheinungen ist es möglich, Informationen über sehr kleine induzierte magnetische Momente an der Grenzfläche zu einer ferromagnetischen Schicht zu erhalten. Dies konnte bei der Untersuchung einer einzelnen Pt/Co-Bilage gezeigt werden, bei der das Magnetisierungsprofil der Pt-Schicht an der Pt/Co-Grenzfläche bestimmt wurde. Im Weiteren konnte durch XRMR-Messungen an einer Serie von einzelnen Pt/Co-Grenzübergängen das Zusammenspiel von chemischer Grenzflächenrauhigkeit und induziertem Pt-Magnetisierungsprofil untersucht werden. Wichtig war es, die Einsetzbarkeit der Methode im weichen Röntgenbereich zu zeigen, in dem die L2,3 Kanten der 3d-Übergangsmetalle liegen, die für den Magnetismus eine herausragende Rolle spielen. Hierbei konnte durch Messung an der Co-L3 Kante das Magnetisierungsprofil einer einzelnen Co-Schicht in einer Pt/Co/Cu-Trilage extrahiert werden. Des Weiteren erlaubt die Methode die Aufnahme elementspezifischer Hysteresekurven vergrabener dünner Schichten in Schichtsystemen mit hoher Qualität. Das Verfahren ist daher prädestiniert zur quantitativen Untersuchung von modernen neuen magnetoelektronischen Komponenten wie GMR- und TMR-Sensoren, MRAM’s oder Halbleiterstrukturen der viel versprechenden „Spintronic“. Es können bei derartigen Systemen Grenzflächenphänomene vergrabener Schichten zerstörungsfrei untersucht werden und im Weiteren auch Themen, die eher der Grundlagenforschung zuzuordnen sind, wie induzierter Grenzflächenmagnetismus oder auch oszillatorische Austauschkopplung in Zukunft quantitativ und elementselektiv behandelt werden.