This thesis includes measurements that were recorded by cooperation partners. The EPR spec‐ trosa mentioned in section 5.2 were recorded by Michael Auth from the Dyakonov Group (Ex‐ perimental Physics VI, Julius‐Maximilians‐Universität, Würzburg). The TREFISH experiments and transient absorption in section 5.4 spectra were performed by Jašinskas et al. from the V. Gulbi‐ nas group (Center for Physical Sciences and Technology, Vilnius, Lithuania). This dissertation investigated the interactions of semiconducting single‐walled carbon nanotubes (SWNTs) of (6,5) chirality with their environment. Shear‐mixing provided high‐quality SWNT sus‐ pensions, which was complemented by various film preparation techniques. These techniques were in turn used to prepare heterostructures with MoS2 and hBN, which were examined with a newly constructed photoluminescence microscope specifically for this purpose. Finally, the change of spectral properties of SWNTs upon doping was investigated in more detail, as well as the behaviour of charge carriers in the tubes themselves. To optimise the SWNT sample preparation techniques that supplied the other experiments, the sample quality of shear‐mixed preparations was compared with that of sonicated samples. It was found that the quantum efficiency of sheared suspensions exceeds that of sonicated suspensions as soon as the sonication time exceeds 30 min. The higher PLQY is due to the lower defect concentration in shear‐mixed samples. Via transient absorption, a mean lifetime of 17.3 ps and a mean distance between defects of 192.1 nm could be determined. Furthermore, it was found that the increased efficiency of horn sonication is probably not only due to higher shear forces acting on the SWNT bundles but also that the shortening of PFO‐BPy strands plays a significant role. Sonication of very long polymer strands significantly increased their effectiveness in shear mixing. While previous approaches could only achieve very low concentrations of SWNTs in suspensions, pre‐sonicated polymer yielded results which were comparable with much shorter PFO‐BPy batches. Reference experiments also showed that different aggregation processes are relevant during production and further processing. Initial reprocessing of carbon nanotube raw material requires 7 h sonication time and over 24 h shear mixing before no increase in carbon nano concentration is detectable. However, only a few minutes of sonication or shear mixing are required when reprocessing the residue produced during the separation of the slurry. This discrepancy indicates that different aggregates are present, with markedly different aggregation properties. To study low‐dimensional heterostructures, a PL microscope was set up with the ability to ob‐ serve single SWNTs as well as monolayers of other low‐dimensional systems. Furthermore, sam‐ ples were prepared which bring single SWNTs into contact with 2D materials such as h‐BN andMoS2 layers and the changes in the photoluminescence spectrum were documented. For h‐BN, it was observed whether previous methods for depositing SWNTs could be transferred for photo‐ luminescence spectroscopy. SWNTs were successfully deposited on monolayers via a modified drip coating, with the limitation that SWNTs aggregate more at the edges of the monolayers. Upon contact of SWNTs with MoS2, significant changes in the emission properties of the mono‐ layers were observed. The fluorescence, which was mainly dominated by excitons, was shifted towards trion emission. Reference experiments excluded PFO‐BPy and toluene as potential causes. Based on the change in the emission behaviour of MoS2, the most plausible explanation is a photoinduced charge transfer leading to delocalised charge carriers on MoS2. In contrast, on SWNTs, the introduction of additional charges would constitute a quenching centre, which would quench their PL emission, making them undetectable in the PL image. In the last chapter, the electronic properties of doped SWNTs and the behaviour of charge carri‐ ers inside the tubes should be investigated. First, the change in the conductivity of SWNT films with increasing doping levels was docu‐ mented. The resistance of the films drops drastically at minimum doping. After the initial in‐ troduction of charges, the resistance drops with increasing dopant concentration according to a double logarithmic curve. The initial drop could be due to a reduction of contact resistances within the SWNT network film, but this could not be further investigated within the scope of this PhD thesis. In cooperation with Andreas Sperlich and Michael Auth, the spin concentration of SWNTs at different doping levels was determined. The obtained concentrations were compared with the carrier concentrations determined from PL and absorption spectra. At low spin densities, good agreement with previous models was found. Furthermore, the presence of isolated spins strongly suggests a localised charge carrier distribution at temperatures around 10 K. When the charge density is increased, the spin density deviates significantly from the charge carrier con‐ centration. This discrepancy is attributed to the increasing delocalisation of charge carriers at high charge densities and the interactions of neighbouring spins. These results strongly indicate the existence of localised charge carriers in SWNTs at low temperatures. Next, the effect of doping on the Raman spectra of SWNT suspensions was investigated. In gen‐ eral, doping is expected to reduce the intensity of the Raman bands, i.e. a consequence of the reduced resonance gain due to bleaching of the S2 transition. However, similar to the resistivity measurements, the oscillator strength of the G+ band drops sharply in the first doping steps. It was also found that the G+ band decreases more than would be expected due to loss of reso‐ nance condition. Furthermore, the G‐ is bleached faster than the G+ band. All these anomalies suggest that resonance enhancement is not the only relevant effect. Another much faster deac‐ tivation path for the excitons may be introduced by doping. This would leave less time for the scattering process to occur and reduce the oscillator strength of the Raman bands. In cooperation with Vidmantas et al., the photoinduced charge carrier behaviour of SWNT/PCBM films was investigated. The required films were prepared by drop coating. The SWNT suspen‐ sions required for this were obtained from sheared SWNT preparations. Using transient absorp‐ tion and TREFISH, a number of charge transfer effects were identified and their dynamics in‐ vestigated: the recombination of neutral excitons (< 50 ps), the electron transfer from carbon nanotubes to PCBM molecules (< 1 ps), the decay of charge‐transfer excitons (∼200 ps), the recombination of charge carriers between charge‐transfer excitons (1 ns to 4 ns) and finally the propagation through the SWNT network (∼20 ns)
Um den jahrtausendealten Weg der Menschheit vom Papyrus über Buchdruck und siliziumbasierte Halbleiter in Richtung noch leistungsfähigerer Technologien zu gehen und weiterhin Heureka-Momente zu schaffen, bieten Kohlenstoffnanoröhren ein weites Forschungsfeld. Besonders die halbleitenden Charakteristika von SWNTs sowie die Manipulation dieser durch Dotierung bergen viele Möglichkeiten für zukünftige Anwendungen in moderner Elektrotechnologie. Der Weg zu einer industriellen Implementierung von SWNTs in neuartigen optoelektronischen Bauteilen ließe sich durch eine Ausweitung des Wissens bezüglich SWNTs und der dotierungsbasierten Anpassung ihrer Eigenschaften ebnen.
Mit dieser Erkenntniserweiterung als Zielsetzung wurden im Rahmen dieser Dissertation halbleitende, einwandige (6,5)-Kohlenstoffnanoröhren als chiralitätsreine, polymerstabilisierte Proben untersucht. Die ultrakurzzeitaufgelöste Spektroskopie der SWNTs erfolgte an organischen Suspensionen wie auch Dünnschichtfilmen, die je mittels eines gewissen Quantums an Gold(III)-chlorid dotiert worden waren. So konnten die ablaufenden Dynamiken auf einer ps-Zeitskala untersucht werden.
In Kapitel 4 konnte mittels transienter Absorptionsexperimente an redoxchemisch p-dotierter SWNT-Suspensionen zunächst gezeigt werden, dass sich die bei optischer Anregung gebildeten Trionen nicht analog zu Exzitonen diffusiv entlang der Nanoröhre bewegen, sondern lokalisiert vorliegen. Die längere trionischen Zerfallsdauer nach X$_1$- verglichen mit X$_1^+$-resonanter Anregung zeugt außerdem davon, dass das Trion aus dem Exziton gespeist wird. Der Einfluss der Dotierung auf die Zerfallsdynamiken von X$_1$ und X$_1^+$ wurde an SWNT-Dünnschichtfilmen untersucht. Das Photobleichsignal des Exzitons verschiebt hypsochrom und zerfällt schneller mit zunehmender Ladungsträgerdichte durch höherer Gold(III)-chloridkonzentrationen. Dies resultiert aus dem verringerten Abstand zwischen den Ladungsträgern, welche als nichtstrahlende Löschstellen fungieren. Für das X$_1^+$-PB ist ein ähnliches Verhalten zu beobachten. Dabei wird dieses Signal mit weiter steigender Dotierung von einer der H-Bande zuzuordnenden Photoabsorption überlagert. Diese lässt sich in einer starken Sättigung der Dotierung wie auch einer hohen Bandkantenverschiebung begründen.
In Kapitel 5 wurde die Größe der Exzitonen und Trionen in dotierten SWNT-Dünnschichtfilmen mittels des Phasenraumfüllmodells bestimmt. Dabei lag besonderes Augenmerk auf der Kompensation des PB/PA-Überlapps, dem schnellen Zerfall, einem Ausgleich von Differenzen zwischen Anrege- und Absorptionsspektrum sowie dem Anteil intrinsischer/dotierter Nanorohrsegmente, um korrigierte Größen $\xi_\mathrm{k}$ zu erhalten. Für die Trionengröße wurde zusätzlich der Überlapp der Absorptionsbanden einbezogen, um korrigierte Werte $\xi_{\mathrm{T,k}}$ zu bestimmen. $\xi_\mathrm{k}$ beträgt in der intrinsischen Form 6$\pm$2\,nm und bleibt bis zu einer Ladungsträgerdichte $n_{\mathrm{LT}}<0.10$\,nm$^{-1}$ etwa gleich, anschließend ist ein Absinken bis auf etwa 4\,nm bei $n_{\mathrm{LT}}\approx0.20$\,nm$^{-1}$ zu beobachten. Für diesen Trend ist die Überlagerung von Exziton- und H-Bande verantwortlich, da so der Faktor zur Bestimmung des Anteils intrinsischer Nanorohrsegmente an der SWNT verfälscht wird. Die Abweichung der intrinsischen Größe von den in der Literatur berichteten 13$\pm$3\,nm ist möglicherweise auf Unterschiede in der Probenpräparation zurückzuführen. Für die Trionengröße ergibt sich bei steigender Dotierung ein ähnliches Verhalten: Sie beträgt für $n_{\mathrm{LT}}<0.20$\,nm$^{-1}$ 1.83$\pm$0.47\,nm, was in der Größenordnung in guter Übereinstimmung mit der Literatur ist. Für höhere Dotierungen sinkt $\xi_{\mathrm{T,k}}$ bis auf 0.92$\pm$0.26nm ab. Dies erklärt sich dadurch, dass bei höherer $n_{\mathrm{LT}}$ die H-Bande das Spektrum dominiert, sodass der Einfluss der Absorptionsbandenüberlagerung nicht mehr vollständig durch den entsprechenden Korrekturfaktor kompensiert werden kann.
Kapitel 6 beschäftigte sich anstelle redoxchemischer Dotierung der nanoskaligen Halbleiter mit der (spektro-)elektrochemischen Untersuchung von Vorläufern molekularer Radikale. SWV-Messungen weisen dabei darauf hin, dass die Pyrene Pyr1-Pyr3 entsprechend der Anzahl ihrer Substituenten bei Reduktion Mono-, Bi- beziehungsweise Tetraradikale bilden. Die strukturelle Ähnlichkeit der Moleküle äußert sich in gleichen Reduktionspotentialen wie auch ähnlichen potentialabhängigen Absorptionsspektren. Während nur marginale Unterschiede in den PL-Spektren der neutralen und reduzierten Spezies festgestellt werden konnte, lieferte das zeitkorrelierte Einzelphotonenzählen aufschlussreichere Ergebnisse: So wird die Fluoreszenzlebensdauer stark von der Polarität der Umgegbung beeinflusst - bereits die Zugabe des Leitsalzes führt hier zu Änderungen. Die durchschnittliche Fluoreszenzlebensdauer $\tau_{\mathrm{av}}$ sinkt außerdem mit Reduktion und Radikalbildung; für höhere Emissionswellenlängen ist $\tau_{\mathrm{av}}$ außerdem höher. Insgesamt verdeutlichten die Experimente die gute Abschirmung zwischen Pyrenkern und Naphthalimidsubstituenten der Moleküle sowie die Sensibilität gegenüber dem Medium durch TICT, das Vorhandensein von Bi- und Tetraradikalen kann allerdings nicht vollständig belegt werden, wofür EPR-Messugen notwendig wären.
Nanoröhren, die auf dem Element Kohlenstoff basieren, besitzen ein großes Potential für ihre
Anwendung als neuartige und nachhaltige Materialien im Bereich der Optoelektronik und weiteren
zukunftsweisenden Technologiefeldern. Um jedoch hierfür genutzt werden zu können, ist
ein tiefgreifendes Kenntnis über ihre außergewöhnlichen photophysikalischen Eigenschaften notwendig.
Kohlenstoffnanoröhren sind als eindimensionale Halbleiter sehr vielseitige Materialien.
Jedoch ist der Zusammenhang zwischen ihrer Eignung als Halbleiter und der dafür notwendigen
Dotierung nur sehr unzureichend verstanden.
Die Ziele der vorliegenden Dissertation waren deshalb, ein grundlegendes Verständnis der photophysikalischen
Energietransferprozesse in Nanoröhren zu erlangen und den Einfluss von gezielten
Dotierungen auf diese Prozesse im Hinblick auf ihre Eigenschaften als eindimensionale Halbleiter
detailliert zu untersuchen. Die Grundlage für die Experimente bildeten verschiedene Filme
aus einwandigen (6,5)-Kohlenstoffnanoröhren, die durch ein Polyfluoren-Copolymer in einer
organischen Lösungsmittelumgebung isoliert wurden. Mit Hilfe der Ultrakurzzeitspektroskopie
wurden die auf einer schnellen (ps-ns) Zeitskala ablaufenden photophysikalischen Prozesse an
diesen Filmen unter verschiedenen Bedingungen untersucht und analysiert.
In Kapitel 4 wurde der generelle Energietransfer der Kohlenstoffnanoröhren in Polymermatrizen
im Detail studiert. Hierbei wurden durch Simulationen theoretische dreidimensionale
Verteilungen von Kohlenstoffnanoröhren erzeugt und die nach einem Energietransfer vorliegenden
Polarisationsanisotropien berechnet. Verschiedene Berechnungsansätze ergaben, dass die
Nanorohrdichte ϱSWCNT für ein Massenüberschuss X der Matrix nahezu unabhängig von dem
Röhrenvolumen war und durch ϱSWCNT = X−1 · 40 000 μm−1 angenähert werden konnte. Die
Simulationen lieferten von der Röhrendichte abhängige Gaußverteilungen der zwischen den
Nanoröhren vorliegenden Abständen. Aus den Verteilungen konnte weiterhin der Anteil an Röhren
bestimmt werden, die für einen Energietransfer zur Verfügung stehen. Weitere Simulationen
von Nanorohrverteilungen lieferten die Polarisationsanisotropie in Abhängigkeit von der Anzahl
an durchgeführten Energietransferschritten. Die Ergebnisse aus den Simulationen wurden zur
Interpretation der Ultrakurzzeitmessungen angewandt. Hierbei wurden durch die Variation der
Polymermatrix die zwischen den Nanoröhren vorliegenden Abstände verändert und damit die
Art und Intensität des Energietransfers kontrolliert. In Messungen der transienten Anisotropie
zeigte sich, dass ein Exziton nach seiner Erzeugung zwei depolarisierende Energietransferschritte
durchführte. Die Zerfallsdynamiken des Exzitons gaben auch klare Hinweise auf weitere nicht
depolarisierende Energietransferprozesse, die durch parallel zueinander stehende Übergangsdipolmomente
ermöglicht wurden. Eine Erklärung für dieses Verhalten lieferte die faserige
Struktur der Filme, die sich in Aufnahmen durch das Elektronenmikroskop zeigte.
Das Kapitel 5 beschäftigte sich mit dem Aufbau eines transienten Nahinfrarotspektrometers
und den nötigen experimentellen Umbauten zur Messung der transienten Absorption für energiearme
Signale im Spektralbereich unterhalb von 1.4 eV. Hierzu wurde die Weißlichterzeugung
für die Verwendung von Calciumfluorid umgebaut. Das erzeugte Weißlicht wurde in das aufgebaute
Prismenspektrometer eingekoppelt, um es weitestgehend linear auf einer Energieskala zu dispergieren. Auf diese Weise wurden energiearme Spektralkomponenten nicht auf unverhältnismäßig
viele Pixel verteilt und konnten mit ausreichender Intensität detektiert werden. Die
Lichtdetektion erfolgte mittels zweier Detektorzeilen aus Indiumgalliumarsenid, die das transiente
Signal durch eine direkte Referenzierung stabilisierten. Weiterhin wurde in diesem Kapitel die
Justage und die programmierte Ansteuerung des Systems detailliert beschrieben. Hierbei wurde
auf die Justage der Einkopplung per Freistrahl, die Kalibrierung mittels Bandpassspektren
sowie auf die Aufnahme von Weißlichtspektren und transienten Karten detailliert eingegangen.
An Nanorohrdispersionen durchgeführten Testmessungen zeigten, dass das transiente Nahinfrarotspektrometer
mit direkter Signalreferenzierung einwandfrei funktionierte und daher den
beobachtbaren Spektralbereich auf den Bereich von Energien bis unterhalb von 1 eV erweiterte.
Damit ermöglichte der Aufbau einen Zugang zu der Beobachtung größerer Nanorohrchiralitäten
sowie zu der Untersuchung von energiearmen, spektralen Signaturen von Nanorohrdefekten.
In Kapitel 6 wurde das transiente Nahinfrarotspektrometer genutzt, um das zeitabhängige
Verhalten von redoxchemisch p-dotierten Nanoröhren zu charakterisieren und quantitativ zu
beschreiben. Hierzu wurden die spektralen Eigenschaften von SWCNT-Dünnfilmen als Funktion
eines steigenden Dotierungsgrades durch die Messungen der transienten und linearen Absorption
studiert. In der linearen Absorption im Bereich von 0.9 - 2.5 eV vereinfachte sich das Spektrum
mit ansteigender Dotierung stark und verlor vor allem im Bereich des ersten Subbandes
deutlich an Oszillatorstärke. Bei starker Dotierung verschwanden die Signalbeiträge von X1
und der Phononenseitenbande. Weiterhin bleichte auch die bei mittleren Dotierungsgraden
auftauchende Trionenabsorption aus und ging in die breite Absorptionsbande der H-Bande über.
Das Erscheinen und Verschwinden der trionischen sowie exzitonischen Absorption war ebenfalls
in der transienten Absorption durch zeitgleich auftretende/verschwindende Photobleichsignale
zu erkennen. Sowohl der Zerfall des exzitonischen PB-Signals wie auch des Trions beschleunigte
sich mit einer steigenden Dotierung. Die Zerfallszeit des Exzitons im undotierten Film betrug
6.87 ps und verkürzte sich auf 0.732 ps bei höheren Dotierungsgraden. Die Zerfallszeit des Photobleichens
des Trions reduzierte sich von 2.02 ps auf 0.440 ps. Auffallend war hierbei, dass das
Trion im Vergleich zu dem Exziton exponentiell zerfiel und damit auf eine Lokalisierung dieses
Zustandes hinweist. Bei höheren Dotierungsmittelkonzentrationen tauchte in der transienten
Absorption ein neuer Signalbeitrag auf. Die Existenz dieses Signals konnte auf die H-Bande
zurückgeführt werden und könnte auf einer Verschiebung des linearen Absorptionsspektrums
aufgrund einer Renormalisierung der Bandlücke oder der Sättigung von Ladungsträgern beruhen.
Das Signal zeigte eine klare Abhängigkeit vom Dotierungsgrad des Nanorohrfilmes. So wies es
eine hypsochrome Verschiebung auf, wurde spektral breiter und seine Zerfallsdauer reduzierte
sich von 1.62 ps auf 0.520 ps mit steigendem Dotierungsgrad.
Nanoelectronics is an essential technology for down-scaling beyond the limit of silicon-based electronics. Single-Wall Carbon Nanotubes (SWNT) are semiconducting components that exhibit a large variety of properties that make them usable for sensing, telecommunication, or computational tasks. Due to their high surface to volume ratio, carbon nanotubes are strongly affected by molecular adsorptions, and almost all properties depend on surface adsorption. SWNT with smaller diameters (0.7-0.9nm) show a stronger sensitivity to surface effects. An optimized synthesis route was developed to produce these nanotubes directly. They were produced with a clean surface, high quality, and large lengths of 2 μ m. The results complement previous studies on larger diameters (0.9-1.4nm). They allow performing statistically significant assumptions for a perfect nanotube, which is selected from a subset of nanotubes with good emission intensity, and high mechanical durability. The adsorption of molecules on the surface of carbon nanotubes influences the motion and binding strength of chargeseparated states in this system. To gain insight into the adsorption processes on the surface with a minimum of concurrent overlapping effects, a microscopic setup, and a measurement technique were developed. The system was estimated to exhibit excellent properties like long exciton diffusion lengths (>350nm), and big exciton sizes (8.5(5)nm), which was substantiated by a simulation. We studied the adsorption processes at the surface of Single-Wall Carbon Nanotubes for molecules in the gas phase, solvent molecules, and surfactant molecules. The experiments were all carried out on suspended individualized carbon nanotubes on a silicon wafer substrate. The experiments in the gas-phase showed that the excitonic emission energy and intensity experiences a rapid blue shift during observation. This shift was associated with the spontaneous desorption of large clusters of gaseous molecules caused by laser heat up. The measurement of this desorption was essential for creating a reference to an initially clean surface and allows us to perform a comparison with previous measurements on this topic. Furthermore, the adsorption of hydrogen on the nanotube surface at high temperatures was investigated. It was found that a new emission mode arises slightly red-shifted to the excitonic emission in these systems. The new signal is almost equally strong as the main excitonic peak and was associated with the brightening of dark excitons at sp3-defects through a K-phonon assisted pathway. The finding is useful for the direct synthesis of spintronic devices as these systems are known to act as single-photon emitters. The suspended nanotubes were further studied to estimate the effect of solvent adsorption on the excitonic states during nanotube dispersion for each nanotube individually. A significant quantum yield loss is observable for hexane and acetonitrile, while the emission intensity was found to be the strongest in toluene. The reference to a clean surface allowed us to estimate the exact influence of the dielectric environment of adsorbing solvents on the excitonic emission energy. Solvent adsorption was found to lead to an energy shift that is almost twice as high as suggested in previous studies. The amount of this energy shift, however, was comparably similar for all solvents, which suggests that the influence of the distinct dielectric constant in the outer environment less significantly influences the energy shift than previously thought. An interesting phenomenon was found when using acetonitrile as a solvent, which leads to greatly enhanced emission properties. The emission is more than twice as high as in the same air-suspended nanotubes, which suggests a process that depends on the laser intensity. In this study, it was reasonably explained how an energy down-conversion is possible through the coupling of the excitonic states with solvent vibrations. The strength of this coupling, however, also suggests adsorptions to the inside of the tubular nanotube structure leading to a coupled vibration of linear acetonitrile molecules that are adsorbed to the inner surface. The findings are important for the field of nanofluidics and provide an excellent system for efficient energy down-conversion in the transmission window of biological tissue. Having separated the pure effect of solvent adsorption allowed us to study the undisturbed molecular adsorption of polymers in these systems. The addition of polyfluorene polymer leads to a slow but stepwise intensity increase. The intensity increase is overlapping with a concurrent process that leads to an intensity decrease. Unfortunately, observing the stepwise process has a low spacial resolution of only 100-250nm, which is in the range of the exciton diffusion length in these systems and hinders detailed analysis. The two competing and overlapping processes processes are considered to originate from slow π-stacking and fast side-chain binding. Insights into this process are essential for selecting suitably formed polymers. However, the findings also emphasize the importance of solvent selection during nanotube dispersion since solvent effects were proven to be far more critical on the quantum yield in these systems. These measurements can shed light on the ongoing debate on polymers adsorption during nanotube individualization and allow us to direct the discussion more towards the selection of suitable solvents. This work provides fundamental insights into the adsorption of various molecules on the surface of individually observed suspended Single-Wall Carbon Nanotubes. It allows observing the adsorption of individual molecules below the optical limit in the solid, liquid, and gas phases. Nanotubes are able to act as sensing material for detecting changes in their direct surrounding. These fundamental findings are also crucial for increasing the quantum yield of solvent-dispersed nanotubes. They can provide better light-harvesting systems for microscopy in biological tissue and set the base for a more efficient telecommunication infrastructure with nano-scale spintronics devices and lasing components. The newly discovered solvent alignment in the nanotube surrounding can potentially also be used for supercapacitors that are needed for caching the calculation results in computational devices that use polymer wrapped nanotubes as transistors. Although fundamental, these studies develop a strategy to enlighten this room that is barely only visible at the bottom of the nano-scale.
Ziel dieser Dissertation war es zu einem besseren Verständnis hinsichtlich folgender Themen beizutragen und Möglichkeiten aufzuzeigen, mit welchen die Voraussetzungen für Anwendungen von einzelnen, funktionalisierten Kohlenstoffnanoröhren, wie u.a. Einzelphotonenquellen, erfüllt werden können.
Eine wesentliche Voraussetzung für die Funktionalisierung von einzelnen Kohlenstoffnanoröhren ist zunächst eine Probenpräparation, welche SWNT-Suspensionen mit einem hohen Anteil an vereinzelten SWNTs hoher PL-Intensität bereitstellen kann. Um solche SWNT-Suspensionen herstellen zu können, wurden drei verschiedene Rohmaterialien und Dispergiermittel auf deren Entbündelungseffizienz- und relativer Photolumineszenzquantenausbeute untersucht. Anhand von photolumineszenzspektroskopischen Untersuchungen und Messungen der Extinktion stellte sich heraus, dass in Kombination des unaufbereiteten CVD-Kohlenstoffnanorohrrußes mit dem Copolymer PFO:BPy als Dispergiermittel und einem speziell in dieser Dissertation entwickelten Herstellungsverfahren für die Mikroskopieproben, stabile (6,5)-SWNT-Suspensionen mit einem großen Anteil an einzelnen SWNTs hoher PL-Intensität, hergestellt werden können.
Letztere Suspension diente als Ausgangsmaterial für die, in dieser Dissertation neuartige, entwickelte Methodik zur Differenzierung zwischen einzelnen SWNTs und Aggregaten mittels PL- und Ramanmessungen an einem PL-Mikroskopie-Aufbau, welche eine weitere Voraussetzung für Einzelpartikelstudien darstellt. Hierbei wurden im Rahmen einer statistischen Messreihe PL- und Ramanspektren von 150 SWNT-Objekten aufgenommen und hieraus resultierend die Parameter FWHM, Energie des S1-Emissions-Zustands und relative Photolumineszenzquantenausbeute ermittelt. Schließlich konnten die zwischen einer einzelnen SWNT und einem Aggregat charakteristischen Differenzen anhand der Korrelationen zwischen den drei Parametern dargestellt werden. Zudem erfolgte eine statistische Analyse zur Bestimmung der statistischen Signifikanz dieser Korrelationen. Hierbei wurde anhand der nicht-parametrischen Spearman-Korrelationskoeffizienten und der p-Werte gezeigt, dass in Kombination dieser drei Messparameter mit einer hohen Wahrscheinlichkeit zwischen einer einzelnen SWNT und einem Aggregat differenziert werden kann. Demnach konnte eine neuartige, im Vergleich zur Literatur, praktikable Methodik zur Differenzierung zwischen einzelnen SWNTs und Aggregaten, etabliert werden, welche die Voraussetzung für Einzelrohrstudien ist.
Der Fokus dieser Dissertation ist die Entschlüsselung der Reaktionsmechanismen der Arylierung und reduktiven Alkylierung von (6,5)-SWNTs im Ensemble und auf Einzelrohrbasis. Durch diese kovalenten Funktionalisierungsverfahren entstehen neue fluoreszierende Defekt-Zustände, deren zeitabhängiges Intensitätsverhalten in der vorliegenden Arbeit näher untersucht wurde. Hinsichtlich der Arylierung von SWNTs mit Diazoniumsalzen postulieren Studien einen zweistufigen Reaktionsmechanismus, welcher durch eine kombinatorische, spektroskopische Gesamtbetrachtung im Rahmen dieser Dissertation bestätigt werden konnte. Auch konnte erstmalig in der Literatur gezeigt werden, dass die Reaktion in hohem Maße reproduzierbar ist.
Reproduzierbarkeitsstudien wurden auch im Falle der reduktiven Alkylierung unternommen, wobei erstmalig festgestellt wurde, dass diese Reaktion lediglich im hohen Maße reproduzierbar ist, sofern die Reduktionslösung mindestens 17 Stunden vor Reaktionsstart angesetzt wird. Basierend auf diesem Resultat, wurden reproduzierbare Messreihen zur Untersuchung der Reaktionsbedingungen und des Reaktionsmechanismus unternommen, da diesbezüglich unzureichend Kenntnis in der Literatur vorhanden ist.
Zur Klärung des Reaktionsmechanismus, von welchem lediglich Annahmen existieren, wurde zum einen der Einfluss der Laseranregung auf die Reaktion untersucht. Da lediglich für den Falle des Ansetzens der Reduktionslösung unmittelbar vor Messbeginn, wobei die reaktiven SO2- -Radikale erzeugt werden, ein Einfluss der Laseranregung festgestellt werden konnte, nicht jedoch im weiteren Reaktionsverlauf, ist von keiner radikalischen Reaktion im Funktionalisierungsschritt auszugehen. Dies konnte durch den Einsatz von Konstitutionsisomeren des Iodbutans bestätigt werden, wobei das Iodbutanisomer, welches im Fall einer radikalischen Reaktion die höchste Reaktivität zeigen sollte, zu keiner Funktionalisierung der SWNTs führte. Im Gegensatz hierzu, konnte durch das 1-Iodbutan, mit dem primären C-Atom, eine hohe PL-Intensität der defekt-induzierten Zustände E11- und T- verzeichnet werden, was die weitere Annahme einer SN2-Reaktion stützt.
Im Rahmen dieser Dissertation konnte zudem erstmalig entdeckt werden, dass unter deren alkalischen, reduktiven Bedingungen, eine Funktionalisierung mit Acetonitril erfolgen kann, was durch die Durchstimmung der PL-Intensität des Defektzustands bei Variation des Volumenanteils von Acetonitril bestätigt werden konnte. Hierbei gilt es jedoch weiter zu analysieren, auf welche Art die Koordination bzw. Funktionalisierung von Acetonitril an den SWNTs erfolgt, was u.a. durch Ramanmessungen untersucht werden könnte.
Auch konnten neuartige Kenntnisse bezüglich der Reaktionskinetik basierend auf den Studien dieser Dissertation erhalten werden, wobei festgestellt wurde, dass das Reaktionsprofil mit dem einer komplexen Folgereaktion angenähert werden kann.
Zudem konnten neuartige Kenntnisse aus der Thermodynamik, wie die Ermittlung der Aktivierungsenergie der Adsorption von DOC-Molekülen auf der SWNT-Oberfläche, durch die Zugabe des Tensids DOC zum Reaktionsansatz und dem hieraus resultierenden Reaktionsabbruch, erhalten werden.
Schließlich fand eine Übertragung der Ergebnisse aus den Ensemblestudien der reduktiven Alkylierung auf Einzelpartikeluntersuchungen statt, wobei letztere erstmalig im Rahmen dieser Arbeit durchgeführt wurden. Aus der statistischen Analyse, welche von Martina Wederhake durchgeführt wurde, resultierte durch Erhöhung des Stoffmengenverhältnisses von 1-Iodbutan zu Kohlenstoff eine inhomogene Steigerung des Funktionalisierungsgrades. Ausblickend gilt es nun zu prüfen, ob die zeitlichen Reaktionsverläufe der photolumineszierenden Zustände, welche aus den Ensemble-Studien erhalten wurden, auf Einzelrohrbasis reproduziert werden können.
Es lässt sich demnach festhalten, dass mithilfe der Studien dieser Dissertation ein Probenherstellungsverfahren, welches stabile SWNT-Suspensionen mit einem großen Anteil an einzelnen Kohlenstoffnanoröhren, hoher PL-Intensität ermöglicht, etabliert werden konnte. Zudem wurde eine neuartige, praktikable und statistisch signifikante Methodik zur Differenzierung zwischen einzelnen Kohlenstoffnanoröhren und Aggregaten entwickelt. Schließlich konnten neue, essentielle Informationen bezüglich des Reaktionsmechanismus und den Reaktionsbedingungen der Arylierung und reduktiven Alkylierung von halbleitenden (6,5)-SWNTs erhalten werden. Wie in der Einleitung bereits erwähnt, sind sowohl der Erhalt einer stabilen SWNT-Suspension mit einem großen Anteil an einzelnen Nanoröhren hoher PL-Intensität, die Möglichkeit der Identifizierung einzelner SWNTs, als auch ein ausgiebiges Verständnis der Reaktionsmechanismen der Funktionalisierungsreaktionen, essentielle Voraussetzungen für die Verwirklichung von Einzelphotonenquellen auf Basis einzelner, funktionalisierter Kohlenstoffnanoröhren. Diese können aufgrund derer geeigneter Emissionseigenschaften als vielversprechende Kandidaten für das Ausgangsmaterial von Einzelphotonenquellen in der Quanteninformationstechnologie angesehen werden.
Doping plays a decisive role for the functionality of semiconductor-based (opto-)electronic
devices. Hence, the technological utilization of semiconductors necessitates control and a
fundamental understanding of the doping process. However, for low-dimensional systems like
carbon nanotubes, neither concentration nor distribution of charge carriers is currently well known.
The research presented in this thesis investigated the doping of semiconducting carbon nanotubes by spectroscopic methods. Samples of highly purified, intrinsic (6,5) single-wall carbon nanotubes were fabricated using polymer stabilization.
Chapter 4 showed that both electro- and redox chemical $p$-doping lead to identical bleaching,
blueshift, broadening and asymmetry of the S$_1$ exciton absorption band. The similar spectral changes induced by both doping schemes suggest that optical spectra can not be used to infer what process was used for doping. Perhaps more importantly, it also indicates that the distribution of charges and the character of the charge transfer states does not depend on the method by which doping was achieved.
The detailed analysis of the doping-induced spectral changes in chapter 5 suggests that surplus charges are distributed inhomogeneously. The hypothesis of carrier localization is consistent with the high sensitivity of the S$_1$ exciton photoluminescence to additional charge carriers and with the stretched-exponential decay of the exciton population following ultrafast excitation.
Both aspects are in good agreement with diffusion-limited contact quenching of excitons
at localized charges. Moreover, localized charges act – similar to structural defects – as
perturbations to the bandstructure as evidenced by a doping-induced increase of the D-band
antiresonance in the mid-infrared spectrum.
Quantum mechanical model calculations also suggest that counterions play a crucial role in
carrier localization. Counterion adsorption at the nanotube surface is thus believed to induce charge traps of more than 100 meV depth with a carrier localization length on the order of 3 - 4 nm. The doping-induced bleach of interband absorption is accompanied by an absorption increase in the IR region below 600 meV. The observed shift of the IR peak position indicates a continuous transition from localized to rather delocalized charge carriers. This transition is caused by the increase of the overlap of charge carrier wavefunctions at higher charge densities and was modeled by classical Monte-Carlo simulations of intraband absorption.
Chapter 6 discussed the spectroscopy of heavily (degenerately) doped nanotubes, which are
characterized by a Drude-response of free-carrier intraband absorption in the optical conductivity spectrum. In the NIR spectral region, the S$_1$ exciton and X$+^_1$ trion absorption is replaced by a nearly 1 eV broad and constant absorption signal, the so-called H-band. The linear and transient absorption spectra of heavily doped nanotubes suggest that the H-band can be attributed to free-carrier interband transitions.
Chapter 7 dealt with the quantification of charge carrier densities by linear absorption spectroscopy.
A particularly good measure of the carrier density is the S$_1$ exciton bleach. For a
bleach below about 50 %, the carrier density is proportional to the bleach. At higher doping
levels, deviations from the linear behavior were observed. For doping levels exceeding a
fully bleached S$_1$ band, the determination of the normalized oscillator strength f$\text{1st}$ over the
whole first subband region (trion, exciton, free e-h pairs) is recommended for quantification of carrier densities. Based on the nanotube density of states, the carrier density $n$ can be estimated using $n = 0.74\,\text{nm}^{−1} \cdot (1 − f_\text{1st})$.
In the last part of this thesis (chapter 8), the time-resolved spectroelectrochemistry was
extended to systems beyond photostable carbon nanotube films. The integration of a flowelectrolysis cell into the transient absorption spectrometer allows the investigation of in-situ electrochemically generated but photounstable molecules due to a continuous exchange of sample volume. First time-resolved experiments were successfully performed using the dye
methylene blue and its electrochemically reduced form leucomethylene blue.
Einwandige Kohlenstoffnanoröhren weisen aufgrund ihrer besonderen Struktur viele für ein rein kohlenstoffhaltiges Makromolekül ungewöhnliche Eigenschaften auf. Dies macht sie sowohl für die Erforschung grundlegender Phänomene in eindimensionalen Nanostrukturen als auch für potenzielle Anwendungen äußerst interessant. Da alle Atome einer SWNT Oberflächenatome sind, führt dies zu einer besonders ausgeprägten Empfindlichkeit ihrer elektronischen Eigenschaften auf Wechselwirkungen mit der Umgebung. Lokale zeitabhängige Änderungen in diesen Wechselwirkungen führen daher zu Phänomenen wie dem Photolumineszenz-Blinken und spektraler Diffusion. Die Erforschung und Kontrolle der Parameter, die für die Beeinflussung der elektronischen Eigenschaften von SWNTs durch Umgebungseinflüsse entscheidend sind, wird neben der spezifischen Synthese eine maßgebliche Rolle dabei spielen, ob und in welcher Form SWNTs in optoelektronischen Bauteilen zukünftig Anwendung finden. Die vorliegende Arbeit liefert einen Beitrag zum Verständnis dieser Wechselwirkungen, indem die Dynamik von Energietransferprozessen innerhalb von SWNTs und zwischen SWNTs untersucht wurde.
Im Rahmen dieser Arbeit wurden homogene und inhomogene Beiträge zur Linienverbreiterung von in einer Matrix eingebetteten SWNTs bestimmt. Dabei wurde erstmals beobachtet, dass die spektrale Diffusion sowohl bei Raumtemperatur als auch bei 17 K auf einer ultraschnellen Zeitskala, d. h. innerhalb von weniger als 1 ps abläuft. Mittels transienter Lochbrennspektroskopie konnte gezeigt werden, dass die homogene Linienbreite von (6,5)-SWNTs mit 3.6 meV nur den geringsten Beitrag zur Absorptionslinienbreite liefert, während die größte Verbreiterung mit mehr als 99 % inhomogen ist. Die inhomogene Linienbreite wurde aus inkohärenten 2D-Spektren, welche durch spektrale Lochbrennexperimente bei Variation der Anregungswellenlänge erhalten werden konnten, zu \(54\pm5\)meV bestimmt. Die Dynamik der spektralen Diffusion wird mit einer Exzitonendiffusion in einer durch lokale Umgebungswechselwirkungen verursachten inhomogenen Energielandschaft entlang der Nanorohrachse erklärt. Durch zeitaufgelöste Lochbrennexperimente unter nichtresonanter Anregung konnte gezeigt werden, dass die Populationsumverteilung innerhalb dieser Energielandschaft für eine energetisch abwärts gerichtete Relaxation ein spontaner Prozess ist. Im umgekehrten Fall ist sie dagegen thermisch aktiviert. Mögliche Einflüsse von Artefakten wurden anhand von Referenzmessungen diskutiert und die Bestimmung der homogenen Linienbreite durch komplementäre CW-Lochbrennexperimente ergänzt.
Durch Monte-Carlo-Simulationen konnten erstmals Informationen über die Form der Potenzialenergielandschaft entlang einer SWNT erhalten und die Größenordnung der Plateaubreite mit nahezu konstanter Energie innerhalb der Potenziallandschaft zu 5.8-18.2nm ermittelt werden. Dies gelang durch eine Kalibrierung der Simulationszeit anhand experimenteller transienter Absorptionsspektren. Im Rahmen dieses Modells wurde darüber hinaus die Zeit für einen Sprung zu einem benachbarten Gitterplatz der Energielandschaft zu 0.1 ps bestimmt.
Inter- und intraband-Relaxationsprozesse von SWNTs wurden mittels Photolumineszenzspektroskopie untersucht. Die Ergebnisse deuten auf eine temperaturunabhängige Effizienz der internen Konversion und die photostimulierte Generierung von Löschzentren hin. Anhand temperaturabhängiger PL-Messungen, die erstmals bei Anregung des \(S_1\)-Zustands durchgeführt wurden, konnte die Energiedifferenz zwischen dem hellen und dunklen Exziton für (6,5)-SWNTs im Rahmen des Modells eines Dreiniveausystems zu \(\delta = (3.7\pm0.1)\)meV bestimmt werden. Aus der guten Übereinstimmung des temperaturabhängigen Trends der PL-Intensität unter \(S_1\)-Anregung mit in früheren Studien erhaltenen Ergebnissen unter \(S_2\)-Anregung konnte geschlussfolgert werden, dass die Effizienz der internen Konversion nicht ausgeprägt temperaturabhängig ist. Für SWNT-Gelfilme wurde unter \(S_2\)-Anregung eine deutliche Abweichung zur \(S_1\)-Anregung in Form eines Bleichens der Photolumineszenz beobachtet. Dieses Phänomen ist in der Literatur wenig diskutiert und wurde daher in leistungsabhängigen PL-Experimenten weiter untersucht. Dabei wurde für die \(S_2\)- im Vergleich zur \(S_1\)-Anregung eine stärker ausgeprägte sublineare Leistungsabhängigkeit gefunden. Die Abweichung vom linearen Zusammenhang der PL-Intensität mit der Leistung trat hier schon bei um eine Größenordnung geringeren Leistungsdichten auf als in früheren Studien und kann mit einer Exziton-Exziton-Annihilation allein nicht erklärt werden. Möglicherweise ist die Öffnung zusätzlicher Zerfallskanäle durch metastabile Löschzentren für dieses Verhalten verantwortlich. Die PL-Experimente zeigten zudem ein zeitabhängiges irreversibles Bleichen unter \(S_2\)-Anregung, welches bei 30 K stärker ausgeprägt war als bei Raumtemperatur. Dessen Abhängigkeit von der eingestrahlten Photonenzahl lässt auf eine Akkumulation von Löschzentren schließen. Daher wird eine mögliche Redoxreaktion mit Wasser, ausgelöst durch die intrinsische p-Dotierung der SWNTs, als Quelle der Löschzentren diskutiert.
Das Verzweigungsverhältnis für die Relaxation nach \(S_2\)-Anregung von SWNTs wurde in Form der relativen Quantenausbeute bestimmt und eine nahezu quantitative interne Konversion des \(S_2\)-Exzitons gefunden. Dieses Ergebnis hat eine wichtige Bedeutung für potenzielle Anwendungen von SWNTs in der Photovoltaik, da die Verluste durch die interband-Relaxation bei einer Anregung des zweiten Subband-Exzitons <3% zu sein scheinen. Die Herausforderung des Experiments wird hier durch die geringe Stokes-Verschiebung von SWNTs verursacht, die eine quantitative Trennung von PL- und Streulicht unmöglich macht. Daher wurde ein Aufbau realisiert, in dem ein großer Teil des Streulichts bereits räumlich entfernt wird und die PL unter \(S_1\)- bzw. \(S_2\)-Anregung quantifizierbar und ohne eine Annahme über Streulicht-Anteile direkt vergleichbar ist. Sowohl für SDS- als auch für Polymer-stabilisierte SWNTs wurde eine relative Quantenausbeute von \(\xi \approxeq 1\) erhalten, was eine nahezu quantitative interne Konversion von \(S_2\)- zu \(S_1\)-Exzitonen innerhalb der PL-Lebensdauer nahelegt.
Anregungsenergietransferprozesse zwischen Kohlenstoffnanoröhren in mono- und bidispersen SWNT-Netzwerkfilmen definierter Zusammensetzung wurden mittels zeitaufgelöster Polarisationsanisotropie untersucht. Dabei wurden neben einem ultraschnellen Energietransfer in weniger als 1 ps auch Hinweise auf Beiträge des \(S_2\)-Exzitons an diesem Prozess gefunden. Die Ergebnisse der Experimente mit bidispersen SWNT-Netzwerkfilmen bestätigen den auch in PLE-Spektren beobachteten energetisch abwärts gerichteten Energietransfer von SWNTs mit großer zu solchen mit kleiner Bandlücke und liefern darüber hinaus eine Zeitskala von weniger als 1 ps für diesen Prozess. Die umgekehrte Transferrichtung konnte weder aus dem \(S_1\)- noch aus dem \(S_2\)-Exziton beobachtet werden. Eine Beschleunigung der Anisotropiedynamik bei \(S_2\)- im Vergleich zu S\uu1-Anregung deutet auf einen Beitrag des \(S_2\)-Exzitons am Energietransferprozess in Konkurrenz zur internen Konversion hin. Durch Referenzexperimente mit monodispersen Netzwerkfilmen konnte eine Beteiligung von Energietransferprozessen zwischen SWNTs der gleichen Chiralität auf einer Zeitskala von 1-2ps nachgewiesen werden. Dadurch konnten Beobachtungen von zeitabhängigen Anisotropieänderungen, die einen energetisch aufwärts gerichteten Energietransfer suggerieren, mit einem intra-Spezies-Transfer erklärt werden - Hinweise auf energetisch aufwärts gerichtete EET-Prozesse wurden nicht gefunden. Eine wichtige Erkenntnis aus diesen Experimenten ist die Tatsache, dass die Überlappung von Signalbeiträgen zu einer Verfälschung der Anisotropie und damit zu fehlerhaften Interpretationen führen kann. Darüber hinaus wurde auf den Einfluss der Probenheterogenität und der Alterung von SWNT-Netzwerkfilmen hingewiesen. Diese Untersuchungen legen nahe, dass ein effizienter Exzitonentransfer in SWNT-Netzwerkfilmen auch zwischen den einzelnen Röhrensträngen erfolgen kann und es somit möglich ist, die Effizienz entsprechender Solarzellen zu verbessern.
Im letzten Teil der Arbeit wurden erstmals transiente Absorptionsexperimente im Femtosekundenbereich mit SWNTs unter \(Gate-Doping\) durchgeführt. In ersten Experimenten konnte gezeigt werden, dass analog zur chemischen Dotierung von SWNTs die Dynamik des \(S_1\)-Bleichens eines (6,5)-SWNT-Netzwerkfilms nach \(S_2\)-Anregung unter \(Gate-Doping\) eine Beschleunigung durch zusätzliche Zerfallskanäle erfährt. Die elektrochemische Bandlücke wurde für (6,5)-Nanoröhren zu 1.5 eV bestimmt. Eine Verringerung der Photoabsorptionsamplitude mit zunehmendem Potenzial lässt Vermutungen über die Natur dieses in transienten Absorptionsexperimenten beobachteten PA-Merkmals in Form der Absorption einer dotierten SWNT-Spezies zu. Diese Untersuchungen liefern erste Einblicke in die Art und Weise, wie eine elektrochemische Modifizierung von SWNTs die elektronische Bandstruktur und Ladungsträgerdynamik verändert.