The aim of the present thesis is to explore the potential of X-ray magnetic circular dichroism(XMCD) experiments on gaining new insights into Kondo and heavy fermion materials. XMCD, which is derived from X-ray absorption spectroscopy (XAS), allows probing magnetic polarization specific to the different elements in a material and to their atomic orbitals. In particular, at the Ce M4,5 edges the method is sensitive to the localized 4f level, which provides the magnetic impurity moment responsible for Kondo physics in Ce compounds. Hence, Ce M4,5 XMCD is ideally suited to investigate local magnetism in the presence of interaction of impurity and conduction electrons in such materials.
As a model material, CePt5/Pt(111) surface intermetallics were chosen for the present study. This thin-film material can be prepared by well-defined procedures involving molecular beam epitaxy. Crystalline Ordered samples are obtained by exploiting the single-crystallinity of the Pt(111) substrate. The surface character of thin films ideally matches the probing depth of soft X-ray spectroscopy in the total electron yield mode.
The XMCD and XAS experiments, taking into account dependence on temperature, angle of incidence, sample thickness and external magnetic field, revealed the presence of four relevant energy scales that influence the magnetic response:
1. The 4f level in CePt5/Pt(111) is subject to significant crystal field (CF) splitting, which leads to reorganization of the six j = 5/2 sublevels. The hexagonal symmetry of the crystal structure conserves mj as a good quantum number. The proposed CF scheme, which is derived from measurements of the paramagnetic susceptibility by XMCD as well as linear dichroism in XAS, consists of nearly degenerate |1/2> and |3/2> doublets with the |5/2> doublet excited by E5/2 = 15 ... 25 meV.
2. Single impurity Kondo interaction significantly couples the magnetic moments of the impurity and conduction electrons. A signature thereof is the f0 -> f1 contribution to Ce M4,5 XAS, the strength of which can be tuned by control of the sample thickness. This finding is in line with the observation of reduced effective 4f moments as detected by XMCD.
3. Ruderman-Kittel-Kasuya-Yosida (RKKY) interaction induces ferromagnetic correlations on the impurity lattice, which induces a positive Curie-Weiss temperature in the temperature-dependent inverse susceptibility.
4. Indications for the transition to a coherent heavy fermion state are found in the inverse susceptibility at T ~ 20 K; the ferromagnetic ground state is not observed. The fielddependence of the magnetic moment in the coherent state can be interpreted in terms of a metamagnetic transition. This allows studying basic characteristics of the renormalized band structure of a heavy fermion system by XMCD.
The disentanglement of these different contributions to the 4f magnetism not only required extensive Ce M4,5 XAS and XMCD data, but also a thorough structural characterization of the material, a fundamental study of the Ce M4,5 line shape in relation to the degree of 4f hybridization and the development of a model for the paramagnetic susceptibility.
The unit cell dimensions and sample morphology of CePt5/Pt(111) intermetallics were studied by low-energy electron diffraction (LEED) and scanning transmission electron microscopy (STEM). These experiments showed that well-defined intermetallic films form on top of the substrate. This lead to introduction of the film thickness t, measured in unit cells (u.c.), as a key feature to characterize the samples.
Systematic LEED measurements in the thickness range t ~ 1 ... 15 u.c. allowed identification of six different phases, which could be interpreted as resulting from the same crystal structure with different rotational alignments and lattice constants. An accurate determination of the surface lattice constant at t ~ 3 u.c. could be achieved by interpretation of additional superstructure spots as arising from a well-defined combination of substrate and film lattices. The thicknessdependence of the lateral lattice constant could be explained in terms of lattice relaxation.
Confirmation of the CePt5 stoichiometry and structure was performed by use of thicknessdependent XAS and a representative LEED-IV study. The results of this study indicate that the intermetallic films exhibit hexagonal CaCu5 structure over the entire range of thicknesses that were studied. The terminating layer consists purely of Pt with one additional Pt atom per unit cell compared to the bulk structure.
The line shape of Ce M4,5 spectra was analyzed with the help of full multiplet calculations.
Experimentally, characteristic variations of the line shape were observed with increasing f0 -> f1 contribution. The calculations show that these variations are not due to an admixture of j = 7/2 character to the ground state, as often stated in the literature. As alternatives, this observation can be explained by either considering an additional contribution to the spectrum or by assumption of an asymmetric lifetime profile.
The model that was developed for the inverse paramagnetic susceptibility contains the hexagonal crystal field, magnetic coupling of the impurity moments in a mean field scheme and Kondo screening. The latter is included phenomenologically by screening factors for the effective moment. Assumption of doublet-specific screening factors, which means that the degree of Kondo interaction depends on the mj character of the 4f sublevels, allows satisfactory reproduction of the experimental data.
The role of elastic interactions, particularly for the self-organized formation of periodically faceted interfaces, was investigated in this thesis for archetype organic-metal interfaces. The cantilever bending technique was applied to study the change of surface stress upon formation of the interface between 3,4,9,10-perylene-tetracarboxylic-dianhydride (PTCDA) and Ag(111). This system is known to form a chemisorptive bonding. Indeed, the sign and the coverage-dependence of the surface stress change are in agreement to models and previous measurements of chemisorptive systems in literature. While the adsorption of molecules into the large domains is associated with a negative, i.e. compressive stress change, the formation of domain boundaries in the molecular layer induces a stress change of opposite sign, increasing the surface stress. The magnitude of the surface stress change of (-0.30 +- 0.10} N/m reflects a relatively weak binding of a PTCDA molecule to each individual single silver atom. It is emphasized, however, that if normalized to the surface stress change per molecule, this value corresponds to a stress change of (-2.2 +- 0.2) eV per molecule which is in the order of the suspected binding energy of this system. Therefore, these experiments reveal elastic interactions to be of significant order of magnitude for this system class. Thereby, they add a new point of view to the understanding of these interfaces. Besides, since the results are in agreement with the well-known properties of this interface, they establish the cantilever bending technique in the field of organic-metal interfaces. The mere existence of a bending of the sample implies an interesting detail for the PTCDA/Ag(111) interface in particular. It is the first experimental evidence for a structural change in the topmost substrate layers upon adsorption of PTCDA on Ag(111). Since such a modification has significant implications for the interpretation of other experimental results, a further investigation with more quantitative structural methods appears necessary. The main focus of this work, however, was on the investigation of the formation of the long-range ordered, self-organized faceted PTCDA/Ag(10 8 7) interface. Reciprocal space maps of this interface were recorded both by spot profile analysis low energy electron diffraction (SPA-LEED) and low energy electron microscopy (LEEM) in selected area LEED mode. Complementary to the reciprocal data, also microscopic real-space LEEM data were used to characterize the morphology of this interface. Six different facet faces ((111), (532), (743), (954), (13 9 5), and (542)) were observed for the preparation path of molecular adsorption on the substrate kept at 550 K. Facet-sensitive dark-field LEEM localized these facets to grow in homogeneous areas of microscopic extensions. If the pristine mesoscopic orientation locally deviates from the average orientation, e.g. in pristine step density, locally different facet types are formed, distorting the otherwise regular mesoscopic pattern. Hence, the original mesoscopic orientation of the substrate strongly determines the degree of order of the faceted surface and the facet species formed. The temperature-dependence of the interface formation was studied in a range between 418 K and 612 K in order to learn more about the kinetics of the process. Additional steeper facets of 27° inclination with respect to the (111) surface were observed in the low temperature regime. Furthermore, using facet-sensitive dark-field LEEM, spatial and size distributions of specific facets were studied for the different temperatures. The nucleation density of the facets did not depend on temperature and can therefore be concluded not to be limited by diffusion. Moreover, the facet dimensions were statistically analyzed. The total island size of the facets follows an exponential distribution, indicating a random growth mode in absence of any mutual facet interactions. While the length distribution of the facets also follows an exponential distribution, the width distribution is peaked, reflecting the high degree of lateral order. This anisotropy is temperature-dependent and occurs starting above 478 K substrate temperature during growth. The peaked distribution indicates the presence of a long-range interaction which leads to the structural order of the self-organized grating. The origin of this long-range interaction was investigated combining three complementary in-situ methods, all providing new insights into the formation of faceted organic-metal interfaces: the cantilever bending technique, high-resolution low energy electron diffraction (SPA-LEED), and microscopy (LEEM). The cantilever bending technique was applied for the first time to a faceting system at all. Below the faceting transition temperature the surface stress change associated with the formation of the PTCDA/Ag(10 8 7) interface resembles in shape and magnitude the one observed for the reference interface PTCDA/Ag(111). But above the transition temperature the absolute surface stress change of (-0.67 +- 0.10) N/m observed for the faceted PTCDA/Ag(10 8 7) interface is considerably larger than for the previous cases. Moreover, the stress change happens in distinguishable stages with a clearly resolvable fine structure of regimes of positive and negative stress changes. These different regimes of surface stress change can be correlated to different stages of the structural phase transition observed by the structural in-situ methods. Thereby, morphological objects (i.e. the facets) are assigned to a specific stress character. Thus, domains of different stress character can be identified on the surface. These stress domains are the prerequisite to apply continuum descriptions of the self-ordering process based on elastic interactions. Hence, the results are the first experimental verification that these continuum descriptions are indeed also applicable to the whole system class of faceting organic-metal interfaces. In conclusion, the results provide strong evidence for elastic interactions being the physical origin of long-range order for this system. In addition, the clear correlation of structural phase transition and surface stress change regimes suggests surface stress to play also an important role for the kinetics of the system. Indeed, the system seems to try to limit the overall stress change during the interface formation by forming facets of positive and negative stress character. Hence, the selection of specific facets could depend on the corresponding stress character. Furthermore, the system seems willing to re-facet at high coverages in order to prevent imperfect domain boundaries which are associated with an increase of surface stress. Finally, template-assisted growth of lateral, heterorganic nanostructures has been explored. Therefore, self-assembled monolayers as a second archetype class of molecules were grown on partially covered PTCDA/Ag(10 8 7) interfaces. Indeed, using standard surface science techniques, the basic principle of this growth scheme was confirmed to be successful.
The projects presented in this thesis cover the examination of the electronic and structural properties of organic thin films at noble metal-organic interfaces. Angle-resolved photoemission spectroscopy is used as the primary investigative tool due to the connection of the emitted photoelectrons to the electronic structure of the sample. The surveyed materials are of relevance for fundamental research and practical applications on their own, but also serve as archetypes for the photoemission techniques presented throughout the four main chapters of this thesis. The techniques are therefore outlined with their adaptation to other systems in mind and a special focus on the proper description of the final state.
The most basic description of the final state that is still adequate for the evaluation of photoemission data is a plane wave. Its simplicity enables a relatively intuitive interpretation of photoemission data, since the initial and final state are related to one another by a Fourier transform and a geometric factor in this approximation. Moreover, the initial states of some systems can be reconstructed in three dimensions by combining photoemission measurements at various excitation energies. This reconstruction can even be carried out solely based on experimental data by using suitable iterative algorithms.
Since the approximation of the final state in the photoemission process by a plane wave is not valid in all instances, knowledge on the limitations of its applicability is indispensable. This can be gained by a comparison to experimental data as well as calculations with a more detailed description of the photoemission final state. One possible appraoch is based on independently emitting atoms where the coherent superposition of partial, atomic final states produces the total final state. This approach can also be used for more intricate studies on organic thin films. To this end, experimental data can be related to theoretical calculations to gain extensive insights into the structural and electronic properties of molecules in organic thin films.
Within the framework of this thesis the mechanisms of growth and reorganisation of surfaces within the first few layers were investigated that are the basis for the fabrication of high quality thin films and interfaces. Two model systems, PTCDA/Ag(111) and CdSe/ZnSe quantum dots (QD), were chosen to study such processes in detail and to demonstrate the power and improvements of the aberration corrected spectromicroscope SMART [1] simultaneously. The measurements benefit especially from the enhanced transmission of the microscope and also from its improved resolution. SMART, the first double–aberration corrected instrument of its kind [2], provided comprehensive methods (LEEM/PEEM, μ–LEED, μ–XPS) to study in–situ and in real time the surface reorganisation and to determine morphology, local structure and local chemical composition of the resulting thin film. Complementarily, a commercial AFM [3] was used ex–situ. XPEEM and μ–XPS measurements were made possible by attaching SMART to the high flux density beamline of the soft–X–ray source BESSY–II [4]. PTCDA/Ag(111) – Growth and structure of the first two layers Although PTCDA/Ag(111) is one of the most intensely studied model systems for the growth of organic semiconductor thin films, it still offers new insights into a complex growth behaviour. This study enlightens the temperature dependant influence of morphological features as small as monatomic Ag steps on the growth process of the first two layers. At low temperatures, single Ag steps act as diffusion barriers. But interdiffusion was observed already for the 2nd layer whereas domain boundaries in the 1st PTCDA–layer persist for crystallite growth in the 2nd layer. 1st layer islands are more compact and the more dendritic development of the 2nd layer indicates reduced interaction strength between 2nd and 1st layer. These findings were explained by a model consisting of structural and potential barriers. The second part of the PTCDA study reveals a variety of phases that appears only if at least two layers are deposited. Besides the six known rotational domains of the interface system PTCDA/Ag(111) [5], a further manifold of structures was discovered. It does not only show a surprising striped image contrast, but the 2nd layer also grows in an elongated way along these so–called ’ripples’. The latter show a rather large period and were found in a wide temperature range. Additionally the μ-LEED pattern of such a domain shows a new super–superstructure as well. This phase is explained by a structural model that introduces a rotated, more relaxed domain in the 2nd layer that does not exist in the first layer. Its structural parameters are similar to those of the bulk unitcells of PTCDA. The model is confirmed by the observation of two different rotational domains that grow on top of one single ’substrate’ domain in the 1st layer. The orientations of the ripple phases fit as well to the predictions of the model. The growth direction along the ripples corresponds to the short diagonal of the super–superstructure unitcell with diamond–like shape. CdSe/ZnSe – Inverse structuring by sublimation of an α-Te cap With the second model system the formation of CdSe quantum dots (QD) from strained epi-layers was investigated. In this case the structures do not form during deposition, but rather during sublimation of the so–called ‘ignition cap’. For these pilot experiments not only the process of QD formation itself was of interest, but also the portability of the preparation and the prevention of contaminations. It was found that the α-Se is well suited for capping and the last step of the QD preparation, the sublimation of the α-Te cap, needs a sufficiently high rate in rise of temperature. Subsequently the cap, the process of desorption and the final surface with the quantum structures were investigated in detail. The cap was deposited by the MBE-group in Würzburg as an amorphous Te layer but was found to contain a variety of structures. Holes, cracks, and micro–crystallites within an α-Te matrix were identified. Sublimation of the “ignition cap” was observed in real–time. Thus the discovered cap-structures could be correlated with the newly formed features as, e.g., QDs on the bare CdSe surface. Since CdSe/ZnSe QDs prefer to form in the neighbourhood of the Te μ–crystallites, Te was found to play a major role in their formation process. Different explanations as the impact of Te as a surfactant, an enhanced mobility of adatoms or as stressor nuclei are discussed. The spectromicroscopic characterisation of the CdSe surface with QDs revealed the crystallographic directions. An increased Cd signal of the film was found at positions of former holes. Several possibilities as segregation or surface termination are reviewed, that might explain this slight Cd variation. Therewith, an important step to a detailed understanding of the complex reorganisation process in coating systems could be achieved.