Refine
Has Fulltext
- yes (153)
Is part of the Bibliography
- yes (153)
Year of publication
Document Type
- Journal article (82)
- Doctoral Thesis (70)
- Preprint (1)
Keywords
- melt electrowriting (13)
- 3D printing (12)
- Knochenzement (12)
- additive manufacturing (10)
- biofabrication (9)
- 3D-Druck (8)
- Hydrogel (7)
- Magnesiumphosphate (7)
- hyaluronic acid (7)
- melt electrospinning writing (7)
Institute
- Abteilung für Funktionswerkstoffe der Medizin und der Zahnheilkunde (153) (remove)
Sonstige beteiligte Institutionen
Zelluläre Resorption 3D-gedruckter Knochenimplantate auf Basis von Calciummagnesiumphosphaten
(2023)
Für die Behandlung von Knochendefekten kritischer Größe gibt es heute eine Reihe von Therapiemöglichkeiten. Neuartige Ansätze mit Magnesiumphosphat- (MPC) und Calciummagnesiumphosphatzementen (CMPC) haben sich als echte Alternativen zu den etablierten Calciumphosphaten erwiesen.
Ziel war es, die Osteoklastogenese in vitro auf 3D-pulvergedrucktem CMPC und MPC zu induzieren und die zelluläre Resorption (zR) zu analysieren. Polystyrol (PS), Glas, β-TCP und Brushit-bildender Zement dienten als Referenzen.
Als Proben wurden Zemente der allgemeinen stöchiometrischen Summenformel CaxMg(3–x)(PO4)2 (x = 0; 0,25; 0,75; 3) verwendet, die Struvit oder Newberyit enthielten. Für die Osteoklastogenese wurden monozytenangereicherte PBMCs aus Buffy-Coat mittels dreifacher Dichtegradientenzentrifugation isoliert, auf die Prüfoberflächen ausgesät und über einen Zeitraum von 22 Tagen mit Zytokinen (M-CSF und RANKL) stimuliert. Die Interaktion der Zellen mit den Zementen bzw. PS/Glas wurde mittels TRAP-Färbung und -Aktivität, DNA- und Ionenkonzentrationen (Ca2+, Mg2+, PO43–, pH-Wert), Rasterelektronen-, Durchlicht-, Auflicht- und Fluoreszenzmikroskopie analysiert.
Auf den Struvit- und Newberyit-bildenden Zementen konnten keine für Osteoklasten typischen Riesenzellen nachgewiesen werden. Auf den Struvit-bildenden Zementen wurde deutlich mehr mononukleäre Zellen nachgewiesen wurden als auf den Newberyit-bildenden Zementen. Während die Freisetzung von Mg2+ und PO43– ausschließlich durch die chemische Degradation erfolgte, wurde Ca2+ zunächst adsorbiert und anschließend durch zR freigesetzt. Die erhöhte Ca2+-Adsorption im Vergleich zur Ca2+-Resorption führte insgesamt zu einer Calcium-Präzipitation.
Da lediglich auf β-TCP Resorptionslakunen beobachtet wurden, wird angenommen, dass auf den CMPC, MPC und Brushite-bildenden Zementen die zellvermittelte Ca2+-Freisetzung von den Präzipitaten ausging, die von Makrophagen auf den Zementen und/oder Riesenzellen auf den Wellplatten resorbiert wurden.
In this work, a toolbox was provided to create three-component polymer conjugates with a defined architecture, designed to bear different biocomponents that can interact with larger biological systems in biomacromolecular recognition experiments. The target architecture is the attachment of two biomolecule ‘arms’ to the alpha telechelic end point of a polymer and fixating the conjugate to the gold surface of SAW and SPR sensor chips with the polymer’s other omega chain end. This specific design of a conjugate will be implemented by using a strategy to yield novel double alpha as well as omega telechelic functionalized POx and the success of all cascade reaction steps leading to the final conjugation product will be proven through affinity measurements between covalently bound mannose and ConA. All reactions were performed on a low molecular model level first and then transferred to telechelic and also side chain functionalized polymer systems.
Untersuchungen zum Abbindeverhalten und der Injizierbarkeit von Magnesiumphosphat-Knochenzementen
(2018)
Ziel dieser Arbeit war die experimentelle Untersuchung von selbsthärtenden Magnesiumphosphat Zementen als Knochenersatzmaterial bezüglich der Verarbeitungsqualität, der Temperaturentwicklung beim Abbinden, der Injizierbarkeit und der mechanischen Eigenschaften. Der Schwerpunkt wurde dabei auf die Anpassung der rheologischen Eigenschaften der Zementpaste für eine minimal–invasive Applikation gelegt. Durch eine elektrische Aufladung der Partikeloberfläche von Farringtonit nach Adsorption von Citrat–Ionen und Zusatz der biokompatiblen Füllstoffe Struvit oder TiO2 für die Einstellung einer bimodalen Partikelgrößenverteilung, war es möglich, die Viskosität der Pasten zu erniedrigen und den filter–pressing−Effekt während der Injektion zu unterdrücken. Die Modifikation des Mg3(PO4)2 Pulvers und der flüssigen Phase erlaubte bei einer Verarbeitungszeit von ca. 10 min die nahezu quantitative Injektion des Zements durch eine 40 mm lange Kanüle mit einem inneren Durchmesser von ca. 800 μm. Zemente mit dem P/L–Verhältnis von 2,0 g/ml erreichten so eine Festigkeit von über 50 MPa nach 24 h Aushärtung. Obwohl die exotherme Abbindereaktion der Zemente teilweise zu einer Erwärmung auf bis zu 67 °C führte, geben literaturbekannte in vivo Studien keinen Hinweis auf Nebenwirkungen innerhalb des umliegenden Hart- bzw. Weichgewebes, was den Verdacht einer möglichen thermischen Nekrose aufgrund der exothermen Abbindereaktion ausschließt. Dies liegt eventuell auch darin begründet, dass die Temperaturmessungen in dieser Arbeit mit einer verhältnismäßig großen Menge an Zementpaste (∼15 g) durchgeführt wurden, während in vivo doch eher geringere Mengen (< 5 g) appliziert werden.
Hydrogele stehen als Material für den 3D-Biodruck zunehmend im Fokus aktueller Forschung, da sie aufgrund ihrer wasserhaltigen Struktur optimale Voraussetzungen für Anwendungen der Zellkultur aufweisen. Durch die Verarbeitung solcher Biotinten mittels additiver Fertigungstechniken der Biofabrikation erhofft man sich beschädigtes oder krankes Gewebe zu heilen oder zu ersetzen. Allerdings wird der Fortschritt in diesem Bereich durch einen Mangel an geeigneten Materialien gebremst, weshalb die Entwicklung neuer Biotinten von zentraler Bedeutung ist. Das Polymer GelAGE ist ein am Lehrstuhl für Funktionswerkstoffe der Medizin und Zahnheilkunde der Universität Würzburg synthetisiertes Hydrogelsystem. Zu diesem über eine Thiol-En Reaktion vernetzenden Material stehen systematische Untersuchungen der für die in vitro Zellkultur relevanten Eigenschaften noch aus. Das Ziel dieser Arbeit war daher die biologische Evaluation von GelAGE und der Vergleich mit der Biotinte Alginat-Gelatine.
Zu diesem Zweck wurden L929-Zellen für 7 Tage in verschiedenen Hydrogelzusammensetzungen in vitro kultiviert. Um die zytokompatiblen Eigenschaften in den verschiedenen Versuchsgruppen zu untersuchen, wurden die Proben mittels der in vitro Testverfahren Live/Dead Färbung, DNA-Assay, CCK-8-Assay und Phalloidin-Färbung analysiert.
Im Rahmen dieser Arbeit konnte ein Herstellungsprotokoll für das Material GelAGE etabliert werden, welches eine Grundlage für die Durchführung weiterer biologischer Experimente bietet. Das Resultat der biologischen Untersuchungen war, dass das Polymer GelAGE als zytokompatibel bewertet werden kann, es jedoch nicht die Qualität des Alginat-Gelatine Hydrogelsystems aufweist. Allerdings konnten die Eigenschaften der GelAGE Proben teilweise durch eine Modifikation mit Humanem Plättchenlysat verbessert werden. Des Weiteren konnten deutliche Unterschiede in der Zell-Material- Interaktion zwischen den verschiedenen GelAGE Varianten nachgewiesen werden.
Was vor einigen Jahren undenkbar erschien, könnte zukünftig möglich sein: Krankes Gewebe mit Gesundem ersetzen, das in vitro mit modernsten Biofabrikationstechniken hergestellt wird. Dabei werden bisherige Grenzen überschritten: Während lichtbasierte Biodruckverfahren wie die Zwei-Photonen-Polymerisation Auflösungen bis in den Nanometerbereich erzielen, ermöglicht der Volumetrische Biodruck (VB) den Druck zentimetergroßer Konstrukte in wenigen Sekunden. Diese Geschwindigkeiten erweisen sich unter Biodruckverfahren als konkurrenzlos und werden erreicht, da das Bioharz nicht konsekutiv, sondern zugleich vernetzt wird. Einschränkend gilt bislang nur der Mangel an geeigneten Bioharzen für den VB. Daher beschäftigt sich vorliegende Arbeit mit der Charakterisierung und Modifikation eines dafür geeigneten Bioharzes: Gelatine-Methacrylat (GelMA). Dank seiner Zusammensetzung ähnelt das etablierte Hydrogelsystem der Extratrazellularmatrix: Der Gelatine-Anteil ermöglicht Biokompatibilität und Bioaktivität durch zelladhäsive sowie degradierbare Aminosäure-Sequenzen. Zugleich können durch photovernetzbare Methacryloyl-Substituenten Konstrukte mit einer Formstabilität bei 37 °C erzeugt werden.
Zunächst wurde das Bioharz zellbiologisch charakterisiert, indem mit der embryonalen Mausfibroblasten-Zelllinie NIH-3T3 beladene GelMA-Zylinder gegossen, photopolymerisiert und kultiviert wurden. Im Verlauf einer Woche wurde die Zytokompatibilität der Gele anhand der Proliferationsfähigkeit (PicoGreen-Assay), des Metabolismus (CCK-8-Assay) und der Vitalität (Live/Dead-Assay) der Zellen beurteilt. Dabei wurden Polymerkonzentrationen von 6 – 8 % sowie GelMA-Harze zweier verschiedener Molekulargewichte verglichen. Alle hergestellten Gele erwiesen sich als zytokompatibel, 6 % ige Gele ließen im Inneren jedoch zusätzlich eine beginnende Zellspreizung zu und ein niedriges GelMA-Molekulargewicht verstärkte die gemessene Proliferation. Die sich anschließende mechanische und physikalische Charakterisierung belegte, dass höher konzentrierte Gele einen größeren E-Modul aufwiesen und damit steifer waren. Eine Modifikation der Gele mit Fibronektin beeinflusste die Zellverträglichkeit weder positiv noch negativ und die Zugabe von Kollagen war wegen Entmischungseffekten nicht bewertbar. Es liegt die Vermutung nah, dass eine weitere Reduktion der Polymerkonzentration und damit Verringerung der Gelsteifigkeit der Schlüssel für mehr Zellspreizung und -wachstum ist. Da jedoch die Druckbarkeit des Bioharzes die weitere Senkung des GelMA-Gehalts limitiert, sollten zunächst Methoden entwickelt werden, welche die Netzwerkdichte des GelMAs anderweitig herabsetzen.
In der vorliegenden Arbeit wurden unterschiedliche zementbasierte Knochenersatzmaterialien hinsichtlich ihres Potentials zur Behandlung knöcherner Defekte in vivo untersucht. Zwei verschiedene Calcium-dotierten Magnesiumphosphat Zementformulierungen (CMPC) wurden mit einem Referenzmaterial aus Calciumphosphat Zement (CPC) verglichen. Dazu wurden auf Basis von CMPC präfabrizierte, injizierbare Pasten bzw. sphärische Granulate hergestellt und anhand von orthotopen, potenziell kraftbelasteten Defekten in Kaninchenfemora getestet. Zentrales Ziel hierbei war es, herauszufinden, wie sich die Materialien in Defektsituationen mit Hartgewebekontakt biologisch verhalten und degradieren bzw. in Knochen umbauen. Nach einer Liegedauer von 6 bzw. 12 Wochen wurden die Knochenneubildung und die Degradation der Materialien mittels Histomorphometrie analysiert.
Alle Materialien waren biokompatibel und führten zur Bildung von neuem Knochen. Der CMPC-Zement zeigte im Vergleich zu CPC einen beschleunigten Abbau, während sich am Referenzmaterial mehr mineralisierter Knochen bildete. Die untersuchten Calcium-dotierten Struvit-bildenden Magnesiumphosphatzemente erwiesen sich als biokompatibel, gut resorbierbar und stellen mit ihrer Fähigkeit zur Knochenbildung ein vielversprechendes Knochenersatzmaterial dar.
A multitude of human tissues, such as bones, tendons, or muscles, are characterized by a hierarchical and highly ordered structure. In many cases, the loss of these tissues requires reconstruction using biocompatible replacement materials. In the field of bone replacement, the pore structure of the material has a crucial influence. Anisotropic porosity would have the advantage of facilitating the ingrowth of cells and newly formed blood vessels as well as the transport of nutrients.
In this thesis, scaffolds with a highly ordered and anisotropic pore structure were fabricated using unidirectional freezing.
Systematic investigations were carried out on biopolymer solutions (alginate and chitosan) to gain a deeper understanding of the freeze-structuring process. The knowledge gained was then applied to the development of anisotropically structured bone substitute materials. Here, the previously existing material platform for anisotropically structured calcium phosphates was extended to low-temperature phases such as calcium deficient hydroxyapatite (CDHA) or the secondary phosphates monetite and brushite.
After the implantation of a biomaterial, the inevitably triggered initial immune response plays a key role in the success of a graft, with immune cells such as neutrophils or macrophages being of particular importance. In this thesis, the influence of anisotropically structured alpha-TCP and CDHA scaffolds as well as their unstructured references on human monocytes/macrophages was investigated. Macrophages produced extracellular traps (ETs) due to mineral nanoparticles formed by the binding of phosphate and calcium ions to human platelet lysate. In particular, incubation of alpha-TCP samples in lysate containing cell culture medium resulted in pronounced particle formation and enhanced release of ETs.
As one kind of “smart” material, thermogelling polymers find applications in biofabrication, drug delivery and regenerative medicine. In this work, we report a thermosensitive poly(2-oxazoline)/poly(2-oxazine) based diblock copolymer comprising thermosensitive/moderately hydrophobic poly(2-N-propyl-2-oxazine) (pPrOzi) and thermosensitive/moderately hydrophilic poly(2-ethyl-2-oxazoline) (pEtOx). Hydrogels were only formed when block length exceeded certain length (≈100 repeat units). The tube inversion and rheological tests showed that the material has then a reversible sol-gel transition above 25 wt.% concentration. Rheological tests further revealed a gel strength around 3 kPa, high shear thinning property and rapid shear recovery after stress, which are highly desirable properties for extrusion based three-dimensional (3D) (bio) printing. Attributed to the rheology profile, well resolved printability and high stackability (with added laponite) was also possible. (Cryo) scanning electron microscopy exhibited a highly porous, interconnected, 3D network. The sol-state at lower temperatures (in ice bath) facilitated the homogeneous distribution of (fluorescently labelled) human adipose derived stem cells (hADSCs) in the hydrogel matrix. Post-printing live/dead assays revealed that the hADSCs encapsulated within the hydrogel remained viable (≈97%). This thermoreversible and (bio) printable hydrogel demonstrated promising properties for use in tissue engineering applications.
Despite advances in cartilage repair strategies, treatment of focal chondral lesions remains an important challenge to prevent osteoarthritis. Articular cartilage is organized into several layers and lack of zonal organization of current grafts is held responsible for insufficient biomechanical and biochemical quality of repair-tissue. The aim was to develop a zonal approach for cartilage regeneration to determine whether the outcome can be improved compared to a non-zonal strategy. Hydrogel-filled polycaprolactone (PCL)-constructs with a chondrocyte-seeded upper-layer deemed to induce hyaline cartilage and a mesenchymal stromal cell (MSC)-containing bottom-layer deemed to induce calcified cartilage were compared to chondrocyte-based non-zonal grafts in a minipig model. Grafts showed comparable hardness at implantation and did not cause visible signs of inflammation. After 6 months, X-ray microtomography (µCT)-analysis revealed significant bone-loss in both treatment groups compared to empty controls. PCL-enforcement and some hydrogel-remnants were retained in all defects, but most implants were pressed into the subchondral bone. Despite important heterogeneities, both treatments reached a significantly lower modified O’Driscoll-score compared to empty controls. Thus, PCL may have induced bone-erosion during joint loading and misplacement of grafts in vivo precluding adequate permanent orientation of zones compared to surrounding native cartilage.
Supplement-free induction of cellular differentiation and polarization solely through the topography of materials is an auspicious strategy but has so far significantly lagged behind the efficiency and intensity of media-supplementation-based protocols. Consistent with the idea that 3D structural motifs in the extracellular matrix possess immunomodulatory capacity as part of the natural healing process, it is found in this study that human-monocyte-derived macrophages show a strong M2a-like prohealing polarization when cultured on type I rat-tail collagen fibers but not on collagen I films. Therefore, it is hypothesized that highly aligned nanofibrils also of synthetic polymers, if packed into larger bundles in 3D topographical biomimetic similarity to native collagen I, would induce a localized macrophage polarization. For the automated fabrication of such bundles in a 3D printing manner, the strategy of “melt electrofibrillation” is pioneered by the integration of flow-directed polymer phase separation into melt electrowriting and subsequent selective dissolution of the matrix polymer postprocessing. This process yields nanofiber bundles with a remarkable structural similarity to native collagen I fibers, particularly for medical-grade poly(ε-caprolactone). These biomimetic fibrillar structures indeed induce a pronounced elongation of human-monocyte-derived macrophages and unprecedentedly trigger their M2-like polarization similar in efficacy as interleukin-4 treatment.
Dual setting cements composed of an in situ forming hydrogel and a reactive mineral phase combine high compressive strength of the cement with sufficient ductility and bending strength of the polymeric network. Previous studies were focused on the modification with non-degradable hydrogels based on 2-hydroxyethyl methacrylate (HEMA). Here, we describe the synthesis of suitable triblock degradable poly(ethylene glycol)-poly(lactide) (PEG-PLLA) cross-linker to improve the resorption capacity of such composites. A study with four different formulations was established. As reference, pure hydroxyapatite (HA) cements and composites with 40 wt% HEMA in the liquid cement phase were produced. Furthermore, HEMA was modified with 10 wt% of PEG-PLLA cross-linker or a test series containing only 25% cross-linker was chosen for composites with a fully degradable polymeric phase. Hence, we developed suitable systems with increased elasticity and 5-6 times higher toughn ess values in comparison to pure inorganic cement matrix. Furthermore, conversion rate from alpha-tricalcium phosphate (alpha-TCP) to HA was still about 90% for all composite formulations, whereas crystal size decreased. Based on this material development and advancement for a dual setting system, we managed to overcome the drawback of brittleness for pure calcium phosphate cements.
The aim of the work was the development of thiol-ene cross-linked hydrogels based on functionalized poly(glycidol)s (PG) and hyaluronic acid (HA) for extrusion based 3D bioprinting. Additionally, the functionalization of the synthesized PG with peptides and the suitability of these polymers for physically cross-linked gels were investigated, in a proof of principle study in order to demonstrate the versatile use of PG polymers in hydrogel development.
First, the precursor polymers of the different hydrogel systems were synthesized. For thiol-ene cross-linked hydogels, linear allyl-functionalized PG (P(AGE-co-G)) and three different thiol-(SH-)functionalized polymers, ester-containing PG-SH (PG SHec), ester-free PG-SH (PG-SHef) and HA-SH were synthesized and analysed, The degree of functionalization of these polymers was adjustable.
For physically cross-linked hydrogels, peptide-functionalized PG (P(peptide-co-G)), was synthesized through polymer analogue thiol-ene modification of P(AGE-co-G).
Subsequently, thiol-ene cross-linked hydrogels were prepared with the synthesized thiol- and allyl-functionalized polymers. Depending on the origin of the used polymers, two different systems were obtained: on the one hand synthetic hydrogels consisting of PG-SHec/ef and P(AGE-co-G) and on the other hand hybrid gels, consisting of HA-SH and P(AGE-co-G). In synthetic gels, the degradability of the gels was determined by the applied PG-SH. The use of PG-SHec resulted in hydrolytically degradable hydrogels, whereas the cross-linking with PG-SHef resulted in non-degradable gels.
The physical properties of these different hydrogel systems were determined by swelling, mechanical and diffusion studies and subsequently compared among each other. In swelling studies the differences of degradable and non-degradable synthetic hydrogels as well as the differences of synthetic compared to hybrid hydrogels were demonstrated.
Next, the stiffness and the swelling ratios (SR) of the established hydrogel systems were examined in dependency of different parameters, such as incubation time, polymer concentration and UV irradiation. In general, these measurements revealed the same trends for synthetic and hybrid hydrogels: an increased polymer concentration as well as prolonged UV irradiation led to an increased network density. Moreover, it was demonstrated that the incorporation of additional non-bound HMW HA hampered the hydrogel cross-linking resulting in gels with decreased stiffness and increased SR. This effect was strongly dependent on the amount of additional HMW HA.
The diffusion of different molecular weight fluorescein isothiocyanate-dextran (FITC-dextran) through hybrid hydrogels (with/without HMW HA) gave information about the mesh size of these gels. The smallest FITC-dextran (4 kDa) completely diffused through both hydrogel systems within the first week, whereas only 55 % of 40 kDa and 5-10 % HMW FITC-dextrans (500 kDa and 2 MDa) could diffuse through the networks.
The applicability of synthetic and hybrid hydrogels for cartilage regeneration purpose was investigated through by biological examinations. It was proven that both gels support the survival of embedded human mesenchymal stromal cells (hMSCs) (21/28 d in vitro culture), however, the chondrogenic differentiation was significantly improved in hybrid hydrogels compared to synthetic gels. The addition of non-bound HMW HA resulted in a slightly less distinct chondrogenesis.
Lastly the printability of the established hydrogel systems was examined. Therefore, the viscoelastic properties of the hydrogel solutions were adjusted by incorporation of non-bound HMW HA. Both systems could be successfully printed with high resolution and high shape fidelity.
The introduction of the double printing approach with reinforcing PCL allowed printing of hydrogel solutions with lower viscosities. As a consequence, the amount of additional HMW HA necessary for printing could be reduced allowing successful printing of hybrid hydrogel solutions with embedded cells. It was demonstrated that the integrated cells survived the printing process with high viability measured after 21 d. Moreover, by this reinforcing technique, robust hydrogel-containing constructs were fabricated.
In addition to thiol-ene cross-linked hydrogels, hydrogel cross-linking via ionic interactions was investigated with a hybrid hydrogel based on HMW HA and peptide-functionalized PG. Rheological measurements revealed an increase in the viscosity of a 2 wt.% HMW HA solution by the addition of peptide-functionalized PG. The increase in viscosity could be attributed to the ionic interactions between the positively charge PG and the negatively charge HMW HA.
In conclusion, throughout this thesis thiol-ene chemistry and PG were introduced as promising cross-linking reaction and polymer precursor for the field of biofabrication. Furthermore, the differences of hybrid and synthetic hydrogels as well as chemically and physically cross-linked hydrogels were demonstrated.
Moreover, the double printing approach was demonstrated to be a promising tool for the fabrication of robust hydrogel-containing constructs. It opens the possibility of printing hydrogels that were not printable yet, due to too low viscosities.
The aim of this thesis was the development of a multifunctional coating system for AuNPs based on thioether polymers, providing both excellent colloidal stability and a variable possibility to introduce functionalities for biological applications.
First, two thioether-polymer systems were synthesised as a systematic investigation into colloidal stabilisation efficacy. Besides commonly used monovalent poly(ethylene glycol) (PEG-SR), its structural analogue linear poly(glycidol) (PG-SR) bearing multiple statistically distributed thioether moieties along the backbone was synthesised. Additionally, respective thiol analogues (PEG-SH and PG-SH) were produced and applied as reference.
Successive modification of varyingly large AuNPs with aforementioned thiol- and thioether-polymers was performed via ligand exchange reaction on citrate stabilised AuNPs. An increased stabilisation efficacy of both thioether-polymers against biological and physiological conditions, as well as against freeze-drying compared to thiol analogues was determined.
Based on the excellent colloidal stabilisation efficacy and multi-functionalisability of thioether-PG, a plethora of functional groups, such as charged groups, hydrophilic/hydrophobic chains, as well as bio-active moieties namely diazirine and biotin was introduced to the AuNP surface. Moreover, the generic and covalent binding of diazirine-modified PG-SR with biomolecules including peptides and proteins was thoroughly demonstrated.
Lastly, diverse applicability and bioactivity of aforementioned modified particles in various studies was displayed, once more verifying the introduction of functionalities. On the one hand the electrostatic interaction of charged AuNPs with hydrogels based on hyaluronic acid was applied to tune the release kinetics of particles from three-dimensional scaffolds. On the other hand the strong complexation of siRNA onto two positively charged AuNPs was proven. The amount of siRNA payload was tuneable by varying the surface charge, ionic strength of the surrounding medium and the N/P ratio. Moreover, the biological activity and selectivity of the biotin-streptavidin conjugation was verified with respectively functionalised particles in controlled agglomeration test and in laser-triggered cell elimination experiments. In the latter, streptavidin-functionalised AuNPs resulted in excellent depletion of biotinylated cells whereas unfunctionalised control particles failed, excluding unspecific binding of these particles to the cell surface.
The focus of this thesis was to investigate how PCL and PLGA react to the heat exposure that comes with the MEW process over a defined timespan.
To assess the thermal stability of PCL during MEW over 25 d, an automated collection of fibers has been used to determine the CTS on each day of heating for three different temperatures. PCL is exceptionally stable over 25 d at 75 °C, whereas for 85 °C and 95 °C a slight upward trend during the last 10 d could be observed, which is an indication for thermal degradation. Same trend could be observed for diameter of fibers produced at a fixed collector speed. For all temperatures, CTS during the first 5 d decreased due to inhomogeneities of the melt. Physical analysis of the fibers by XRD and mechanical testing showed no significant changes.
To investigate the chemical details of the thermal durability, PCL was artificially aged over 25 d at 75 °C, 85 °C and 95 °C. Data from GPC analysis and rheology revealed that PCL is degrading steadily at all three temperatures. Combined with GC-MS analysis, two different mechanisms for degradation could be observed: random chain scission and unzipping. Additional GPC experiment using a mixture of PCL and a fluorescence labelled PCL showed that PCL was undergoing ester interchange reactions, which could explain its thermal stability.
PLGA was established successfully as material for MEW. GPC results revealed that PLGA degraded heavily in the one-hour preheating period. To reduce the processing temperature, ATEC was blended with PLGA in three mixtures. This slowed down degradation and a processing window of 6 h could be established. Mechanical testing with fibers produced with PLGA and all three blends was performed. PLGA was very brittle, whereas the blends showed an elastic behavior. This could be explained by ester interchange reactions that formed a loosely crosslinked network with ATEC.
There is a specialized niche for the electrohydrodynamic jetting of melts, from biomedical products to filtration and soft matter applications. The next frontier includes optics, microfluidics, flexible electronic devices, and soft network composites in biomaterial science and soft robotics. The recent emphasis on reproducibly direct‐writing continual molten jets has enabled a spectrum of contemporary microscale 3D objects to be fabricated. One strong suit of melt processing is the capacity for the jet to solidify rapidly into a fiber, thus fixing a particular structure into position. The ability to direct‐write complex and multiscaled architectures and structures has greatly contributed to a large number of recent studies, explicitly, toward fiber–hydrogel composites and fugitive inks, and has expanded into several biomedical applications such as cartilage, skin, periosteum, and cardiovascular tissue engineering. Following the footsteps of a publication that summarized melt electrowriting literature up to 2015, the most recent literature from then until now is reviewed to provide a continuous and comprehensive timeline that demonstrates the latest advances as well as new perspectives for this emerging technology.
The Multiweek Thermal Stability of Medical-Grade Poly(ε-caprolactone) During Melt Electrowriting
(2022)
Melt electrowriting (MEW) is a high-resolution additive manufacturing technology that places unique constraints on the processing of thermally degradable polymers. With a single nozzle, MEW operates at low throughput and in this study, medical-grade poly(ε-caprolactone) (PCL) is heated for 25 d at three different temperatures (75, 85, and 95 °C), collecting daily samples. There is an initial increase in the fiber diameter and decrease in the jet speed over the first 5 d, then the MEW process remains stable for the 75 and 85 °C groups. When the collector speed is fixed to a value at least 10% above the jet speed, the diameter remains constant for 25 d at 75 °C and only increases with time for 85 and 95 °C. Fiber fusion at increased layer height is observed for 85 and 95 °C, while the surface morphology of single fibers remain similar for all temperatures. The properties of the prints are assessed with no observable changes in the degree of crystallinity or the Young's modulus, while the yield strength decreases in later phases only for 95 °C. After the initial 5-d period, the MEW processing of PCL at 75 °C is extraordinarily stable with overall fiber diameters averaging 13.5 ± 1.0 µm over the entire 25-d period.
Calcium phosphate cement (CPC) is a well-established bone replacement material in dentistry and orthopedics. CPC mimics the physicochemical properties of natural bone and therefore shows excellent in vivo behavior. However, due to their brittleness, the application of CPC implants is limited to non-load bearing areas. Generally, the fiber-reinforcement of ceramic materials enhances fracture resistance, but simultaneously reduces the strength of the composite. Combining strong C-fiber reinforcement with a hydroxyapatite to form a CPC with a chemical modification of the fiber surface allowed us to adjust the fiber–matrix interface and consequently the fracture behavior. Thus, we could demonstrate enhanced mechanical properties of CPC in terms of bending strength and work of fracture to a strain of 5% (WOF5). Hereby, the strength increased by a factor of four from 9.2 ± 1.7 to 38.4 ± 1.7 MPa. Simultaneously, the WOF5 increased from 0.02 ± 0.004 to 2.0 ± 0.6 kJ∙m−2, when utilizing an aqua regia/CaCl2 pretreatment. The cell proliferation and activity of MG63 osteoblast-like cells as biocompatibility markers were not affected by fiber addition nor by fiber treatment. CPC reinforced with chemically activated C-fibers is a promising bone replacement material for load-bearing applications.
Melt electrowriting, a high-resolution additive manufacturing technique, is used in this study to process a magnetic polymer-based blend for the first time. Carbonyl iron (CI) particles homogenously distribute into poly(vinylidene fluoride) (PVDF) melts to result in well-defined, highly porous structures or scaffolds comprised of fibers ranging from 30 to 50 µm in diameter. This study observes that CI particle incorporation is possible up to 30 wt% without nozzle clogging, albeit that the highest concentration results in heterogeneous fiber morphologies. In contrast, the direct writing of homogeneous PVDF fibers with up to 15 wt% CI is possible. The fibers can be readily displaced using magnets at concentrations of 1 wt% and above. Combined with good viability of L929 CC1 cells using Live/Dead imaging on scaffolds for all CI concentrations indicates that these formulations have potential for the usage in stimuli-responsive applications such as 4D printing.
The bioprinting roadmap
(2020)
This bioprinting roadmap features salient advances in selected applications of the technique and highlights the status of current developments and challenges, as well as envisioned advances in science and technology, to address the challenges to the young and evolving technique. The topics covered in this roadmap encompass the broad spectrum of bioprinting; from cell expansion and novel bioink development to cell/stem cell printing, from organoid-based tissue organization to bioprinting of human-scale tissue structures, and from building cell/tissue/organ-on-a-chip to biomanufacturing of multicellular engineered living systems. The emerging application of printing-in-space and an overview of bioprinting technologies are also included in this roadmap. Due to the rapid pace of methodological advancements in bioprinting techniques and wide-ranging applications, the direction in which the field should advance is not immediately clear. This bioprinting roadmap addresses this unmet need by providing a comprehensive summary and recommendations useful to experienced researchers and newcomers to the field.
In 3D bioprinting for cartilage regeneration, bioinks that support chondrogenic development are of key importance. Growth factors covalently bound in non-printable hydrogels have been shown to effectively promote chondrogenesis. However, studies that investigate the functionality of tethered growth factors within 3D printable bioinks are still lacking. Therefore, in this study, we established a dual-stage crosslinked hyaluronic acid-based bioink that enabled covalent tethering of transforming growth factor-beta 1 (TGF-β1). Bone marrow-derived mesenchymal stromal cells (MSCs) were cultured over three weeks in vitro, and chondrogenic differentiation of MSCs within bioink constructs with tethered TGF-β1 was markedly enhanced, as compared to constructs with non-covalently incorporated TGF-β1. This was substantiated with regard to early TGF-β1 signaling, chondrogenic gene expression, qualitative and quantitative ECM deposition and distribution, and resulting construct stiffness. Furthermore, it was successfully demonstrated, in a comparative analysis of cast and printed bioinks, that covalently tethered TGF-β1 maintained its functionality after 3D printing. Taken together, the presented ink composition enabled the generation of high-quality cartilaginous tissues without the need for continuous exogenous growth factor supply and, thus, bears great potential for future investigation towards cartilage regeneration. Furthermore, growth factor tethering within bioinks, potentially leading to superior tissue development, may also be explored for other biofabrication applications.