In this paper, we present results on the first MBE growth of HgSe. The influence of the GaAs substrate temperature as well as the Hg and Se fluxes on the growth and the electrical properties has been investigated. It has been found that the growth rate is very low at substrate temperatures above 120°C. At 120°C and at lower temperatures, the growth rate is appreciably higher. The sticking coefficient of Se seems to depend inversely on the Hg/Se flux ratio. Epitaxial growth could be maintained at 70°C with Hg/Se flux ratios between lOO and ISO, and at 160°C between 280 and 450. The electron mobilities of these HgSe epilayers at room temperature decrease from a maximum value of 8.2 x 10^3 cm2 /V' s with increasing electron concentration. The concentration was found to be between 6xlO^17 and 1.6x10^19 cm- 3 at room temperature. Rocking curves from X-ray diffraction measurements of the better epilayers have a full width at half maximum of 5S0 arc sec.
The molecular beam epitaxially growth of (001) Hg\(_{1-x}\) Cd\(_z\) Te-HgTe superlattices has been systematically investigated. The well width as well as the period were determined directly by X-ray diffraction. This was accomphshed for the well width by exploiting the high reflectivity from HgTe and the low reflectivity from CdTe for the (002) Bragg reflection. Knowing the well and barrier thicknesses we have been able to set an upper limit on the aver~ge composition of the barriers, Xl, by annealing the superlattice and then measuring the composition of the. resultmg alloy. Xb was shown to decrease exponentially with decreasing barrier width. Xb is appreciably smaller m. narrow barriers due to the increased significance of interdiffusion in the Hg\(_{1-x}\)Cd\(_x\) Te/HgTe interface in narrow barriers. The experimentally determined optical absorption coefficient for these superlattices is compared WIth theoretical calculations. The absorption coefficient was determined from transmission and reflection spectra at 300, 77 and 5 K. Using the thickness and composition of the barriers and wells, and an interface width due to interdiffusion, the complex refractive index is calculated and compared with the experimental absorption coefficient. The envelope function method based on an 8 x 8 second order k . p band model was used to calculate the superlattice states. These results when inserted into Kubo's formula, yield the dynamic conductivity for interband transitions. The experimental and theoretical values for the absorption coefficient using no adjustable parameters are in good agreement for most of the investigated superlattices. Furthermore the agreement for the higher energetic interband transitions is much worse if values for the barrier composition, which are appreciably different than the experimentally determined values, are used. The infrared photoluminescence was investigated at temperatures from 4.2 to 300 K. Pronounced photoluminescence was observed for all superlattices in this temperature range.
We report the contactless determination of the conductivity, the mobility and the carrier concentration of II-VI semiconductors by means of the technique of the partially filled waveguide at a microwave frequency of 9 GHz. The samples are CdHgTe epitaxial layers, grown on CdZnTe substrates by molecular beam epitaxy. The conductivity is determined from the transmission coefficient of the sample in the partially filled waveguide. For the analysis of the experimental data, the complex transmission coefficient is calculated by a rigorous multi-mode matching procedure. By varying the conductivity of the sample, we obtain an optimum fit of the calculated data to the experimental results. Comparison with conductivity data determined by the van der Pauw method shows that our method allows to measure the conductivity with good accuracy. The behaviour of the transmission coefficient of the sample is discussed in dependence on the layer conductivity, the layer thickness and the dielectric constant of the substrate. The calculations require to consider in detail the distribution of the electromagnetic fields in the sample region. The usual assumption of a hardly disturbed TE\(_{10}\) mode cannot be used in our case. By applying a magnetic field in extraordinary Voigt configuration. galvanomagnetic measurements have been carried out which yield the mobility and thus the carrier concentration. These results are also in good agreement with van der Pauw transport measurements.
The microwave transmission and reßection is evaluated for stratified lossy dielectric segments partially filling the rectangular waveguide by the method which combines the multimode network theory with the rigorous mode matching procedure. As an example, we investigate in detail the microwave scattering properties of II-VI-epitaxial layer on a lossy dielectric substrate inserted in the rectangular waveguide. The experimental data verify the accuracy and the effectiveness of the present method. Extensive numerical results are presented to establish useful guidelines for the contactless microwave measurement of the conductivity of the epitaxiallayer.
We report on the growth of the compound semiconductor MgTe as weil as the ternary alloy Cd\(_{l-x}\)Mg, Te by molecular hcam cpitaxy. This is to our knowkdgc thc first time that this material has heen grown by any epitaxial technique. Bulk MgTe, which is hygroscopic, has a band gap of 3.0 eV and crystallizcs usually in thc wurtzite structure. Pseudomorphic films were grown on zincblende Cd Te suhstrates for a MgTe thickness helow a critical layer thickncss of approximately 500 nm. In addition, Cd\(_{l_x}\),Mg\(_x\)Te epilayers were grown with a Mg concentration between 0 and 68%, which corresponds to a band gap betwcen 1.5 and 2.5 eV at room temperature. The crystalline quality of thc layers is comparabk to CdTc thin films as long as they are fully strained. The lauice constant of zincblende MgTe is slightly smaller than that of CdTe, and the lattice mismatch is as low as O.7%. In addition highly n-type CdMgTe layers were fabricatcd by hromine doping. The tunability of the band gap as weil as the rather good laUice match with CdTc makes the matcrial interesting for optoelectronic device applications for the entire visible range.
A semiempirical model is presented that correlates the broadening of the absorption edge with both transitions below the energy gap and with transitions by the Kane band model. This model correctly fits both the absorption and luminescence spectra of narrow-gap (Hg,Cd)Te samples that have been grown by the traveling heater method as well as by molecular-beam epitaxy. The accuracy of the band-gap determination is enhanced by this model.